JPS62289688A - Rope for yacht - Google Patents
Rope for yachtInfo
- Publication number
- JPS62289688A JPS62289688A JP61130358A JP13035886A JPS62289688A JP S62289688 A JPS62289688 A JP S62289688A JP 61130358 A JP61130358 A JP 61130358A JP 13035886 A JP13035886 A JP 13035886A JP S62289688 A JPS62289688 A JP S62289688A
- Authority
- JP
- Japan
- Prior art keywords
- fiber
- layer
- rope
- core
- aromatic polyamide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。(57) [Summary] This bulletin contains application data before electronic filing, so abstract data is not recorded.
Description
【発明の詳細な説明】
３、発明の詳細な説明
〈産業上の利用分野〉
本発明はヨツトに用いるメインロープ、スピンセールロ
ープ、ジブセールロープ等に関する。Detailed Description of the Invention 3. Detailed Description of the Invention (Field of Industrial Application) The present invention relates to a main rope, spin sail rope, jib sail rope, etc. used in a yacht.
〈従来技術〉
従来、芯繊維層に繊維を編組して多層構造とした繊維ロ
ープは公知である。たとえば、
「繊維の撚合体で構成した芯の外周に繊維を編組した中
層を設けた内層索の外周に溶融した熱溶融性樹脂の被覆
層と前記被覆層外周に熱収縮性樹脂繊維の編組を、前記
被覆層を繊維間にくい込まして収縮して外被層とした繊
維ロープ」 （特開昭５８−２０７８０６号公報）が知
られている。<Prior Art> Conventionally, fiber ropes having a multilayer structure by braiding fibers into a core fiber layer are known. For example, "an inner layer cable has a core made of twisted fibers, a middle layer made of braided fibers, a covering layer made of a melted heat-melting resin on the outer periphery of the cable, and a braided heat-shrinkable resin fiber on the outer periphery of the covering layer. , a fiber rope in which the coating layer is embedded between the fibers and then shrunk to form an outer coating layer is known (Japanese Unexamined Patent Publication No. 58-207806).
また、全芳香族ポリアミド繊維を含む繊維ロープも公知
である。 たとえば、「強度１５ｇ／ｄ以上、伸度１０
％以下の繊維と芯さや型芳香族ポリアミド繊維とを撚り
合わせ、熱融着せしめた複合１維を複数本撚り合わせま
たは編組してなることを特徴とするロープ」（特開昭５
８−３６２８６号公報）などが知られている。Fiber ropes containing wholly aromatic polyamide fibers are also known. For example, "strength 15 g/d or more, elongation 10
% or less of fibers and core-sheath type aromatic polyamide fibers, and heat-sealed them together, a plurality of composite fibers are twisted or braided.''
8-36286) and the like are known.
また、全芳香族ポリアミド繊維とポリエステル繊維とを
組合せてなる繊維ロープも公知である。たとえば、「芳
香族ポリアミド糸にて形成した芯材の外周を耐摩耗性と
耐候性とを有する繊維にて形成した被覆材にて被覆して
なることを特徴とするロープ」 （特開昭５４−１２０
７６７号公報）あるいは「それぞれ多数のストランドを
互いに交叉させながら螺旋状に巻回して筒状に編組して
なる内外両層索を有する二重編組構造のものにおいて、
上記両層索の一方の各ストランドをテトロンやナイロ
ンなど伸びの大きい繊維で形成し、他方の各ストランド
をアラミド繊維などの伸びの小さい繊維で形成し、かつ
、その他方のストランドの螺旋ピッチを一方のストラン
ドの螺旋ピッチよりも大きくしたことを特徴とする繊維
ロープ」 （特開昭５６−３７３９１号公報）などが
知られている。Furthermore, fiber ropes made of a combination of wholly aromatic polyamide fibers and polyester fibers are also known. For example, "a rope characterized in that the outer periphery of a core material made of aromatic polyamide yarn is covered with a covering material made of fibers having abrasion resistance and weather resistance" (Japanese Patent Laid-Open No. 54 -120
(No. 767 Publication) or "In a double-braided structure having both inner and outer layers formed by winding a large number of strands in a spiral shape while crossing each other and braiding them into a cylindrical shape,
Each strand on one side of the double-layered rope is made of a fiber with high elongation such as Tetron or nylon, and each strand on the other side is formed with a fiber with low elongation such as aramid fiber, and the helical pitch of the other strand is set to one side. ``A fiber rope characterized by having a helical pitch larger than the helical pitch of the strands'' (Japanese Unexamined Patent Publication No. 56-37391) is known.
一方一般に市販されているヨツト用ロープには、通常ポ
リエステル、ナイロン、ビニロンなどが用いられ、最外
層は長繊維糸で構成されている。そのため従来のヨツト
用ロープには下記の如き問題点があった。On the other hand, commercially available yacht ropes are usually made of polyester, nylon, vinylon, etc., and the outermost layer is made of long fiber yarn. Therefore, conventional yacht ropes have the following problems.
（１）ヨツトセールが風圧を受けたとき、その応力のた
め伸びを生じヨツトセールの形態寸法安定性が損なわれ
る。(1) When a sailboat is subjected to wind pressure, the stress causes it to elongate, impairing the dimensional stability of the sailboat.
（２）モジユラスが低いため耐久性が低い。(2) Durability is low due to low modulus.
（３）ロープの最外層が長繊維で編組されているためロ
ープ表面が滑りやすい。(3) Since the outermost layer of the rope is braided with long fibers, the rope surface is slippery.
〈発明の目的〉
本発明は従来技術におけるかかる問題点を解決するため
になされたものである。すなわち本発明は、＜１）芯繊
維層に繊維を編組した被覆層を設けてなる繊維ロープに
おいて、少な（とも１層が全芳香族ポリアミド繊維を含
み、かつ最外層がポリエステルタスラン加工糸からなる
ことを特徴とするヨツト用ロープ
（２）芯繊維層が全芳香族ポリアミドｍ維である特許請
求の範囲第（１）項に記載のヨツト用ロープ（３）全芳
香族ポリアミド繊維が樹脂で被覆されてなる特許請求の
範囲第（２）項に記載のヨツト用ロープ（４）芯繊維層
がポリエステル長繊維有撚糸である特許請求の範囲第（
１）項に記載のヨツト用ロープ（５）芯繊維層がポリエ
ステル長繊維無撚糸である特許請求の範囲第（１）項に
記載のヨツト用ロープ（６）ポリエステル長繊維からな
る芯層に全芳香族ポリアミド繊維を編組した中層を設け
、該中層にポリエステルタスラン加工糸を編組した最外
層を設けてなる特許請求の範囲第（１）項に記載のヨツ
ト用ロープ
（７）太い部分と細い部分とを有する繊維ロープであっ
て太い部分の芯層はポリエステル長繊維糸と全芳香族ポ
リアミド繊維とで構成され、細い部分の芯層は全芳香族
ポリアミド繊維で構成され、それぞれの層にポリエステ
ルタスラン加工糸を編組した最外層を設けてなる特許請
求の範囲第（１）項に記載のヨツト用ロープ
ここに全芳香族ポリアミドとは、主としてボリバ本発明
のヨツト用ロープは２以上の層からなるロープにおいて
少なくとも１層が全芳香族ポリアミド繊維を含むもので
ある。全芳香族ポリアミド繊維を含む層は芯層であって
もよく芯層と最外層との間の中間層であってもよい。最
外層はポリエステルタスラン加工糸からなるものである
。ポリエステルタスラン加工糸はいわゆる２−フィード
タスラン加工糸であり、比較的太デニールのポリエステ
ル系を芯糸とし、該芯糸よりも細デニールのポリエステ
ル糸を被覆糸（カバーリング糸）としたものである。被
覆系は芯糸の周囲に捲回して多数の細かなループを形成
している。<Object of the Invention> The present invention has been made in order to solve such problems in the prior art. That is, the present invention provides <1) a fiber rope in which a core fiber layer is provided with a covering layer of braided fibers; (2) A rope for yachting according to claim (1), wherein the core fiber layer is a fully aromatic polyamide fiber (3) The fully aromatic polyamide fiber is coated with a resin. The yacht rope (4) according to claim 2, wherein the core fiber layer is made of polyester long fiber twisted yarn.
The rope for yachting according to claim 1) (5) The core fiber layer is made of polyester long fiber non-twisted yarn. A rope for yachting (7) according to claim (1), comprising a middle layer made of braided aromatic polyamide fibers, and an outermost layer made of braided polyester Taslan thread in the middle layer. The core layer of the thick part is composed of polyester long fiber yarn and wholly aromatic polyamide fiber, the core layer of the thin part is composed of wholly aromatic polyamide fiber, and each layer is made of polyester taslan. A yachting rope according to claim (1), which comprises an outermost layer of braided processed yarn.The yachting rope of the present invention is composed of two or more layers. At least one layer of the rope contains wholly aromatic polyamide fibers. The layer containing wholly aromatic polyamide fibers may be a core layer or an intermediate layer between the core layer and the outermost layer. The outermost layer is made of polyester taslan textured yarn. Polyester taslan processed yarn is a so-called 2-feed taslan processed yarn, in which a relatively thick denier polyester yarn is used as the core yarn, and a polyester yarn with a finer denier than the core yarn is used as the covering yarn (covering yarn). . The covering system is wound around the core yarn to form a large number of fine loops.
芯繊維層に全芳香族ポリアミド繊維を用いる場合、該繊
維を樹脂で被覆してもよいっこの場合、被覆樹脂は特に
限定されないが、ポリアミド、ポリアミド共重合体、ポ
リエステノベポリエステル共重合体、ポリエチレン、ポ
リプロピレンの如きポリオレフィン、ビニル系ポリマー
、ゴム、ポリウレタンなどのエラストマー等を用いるこ
とができる。When wholly aromatic polyamide fiber is used for the core fiber layer, the fiber may be coated with a resin. In this case, the coating resin is not particularly limited, but may include polyamide, polyamide copolymer, polyester copolymer, polyethylene, etc. , polyolefins such as polypropylene, vinyl polymers, rubbers, elastomers such as polyurethane, etc. can be used.
また全芳香族ポリアミド繊維の代わりにポリエステル長
繊維系を芯繊維層として用い、全芳香族ポリアミド繊維
を中間層として用いてもよい。この場合ポリエステル長
繊維糸は、有撚糸を用いてもよく、無撚糸を用いてもよ
い。またヨツト用ロープの場合、太い部分と細い部分と
を有する繊維ロープが使用されることがあるが、本発明
においては、かかる形状のヨツト用ロープは下記のごと
く構成するのが好ましい。 すなわち、太い部分におけ
る芯繊維層は全芳香族ポリアミド繊維とポリエステル長
繊維とで構成し、細い部分における芯繊維層は同じ全芳
香族ポリアミド繊維で構成し、それぞれの最外層として
はポリエステルタスラン加工糸を編組した繊維層を設け
る。Further, instead of wholly aromatic polyamide fibers, polyester long fibers may be used as the core fiber layer, and wholly aromatic polyamide fibers may be used as the intermediate layer. In this case, the polyester long fiber yarn may be a twisted yarn or a non-twisted yarn. Further, in the case of a yachting rope, a fiber rope having a thick portion and a thin portion is sometimes used, and in the present invention, it is preferable that the yachting rope having such a shape is constructed as follows. That is, the core fiber layer in the thick part is composed of wholly aromatic polyamide fibers and polyester long fibers, the core fiber layer in the thin part is composed of the same wholly aromatic polyamide fiber, and the outermost layer of each is made of polyester Taslan processed yarn. A fiber layer is provided by braiding the fibers.
〈発明の効果〉 本発明のヨツト用ロープは下記の効果を有する。<Effect of the invention> The yacht rope of the present invention has the following effects.
（１）セーリング中にヨツトセールが風圧を受けたとき
その応力によって伸びを生じることがない。(1) When the yacht sail is subjected to wind pressure during sailing, the stress does not cause elongation.
（２）ヨツトセールに永久歪みを生じ、形態寸法安定性
が損なわれるということがない。すなわち耐久性が高い
。(2) There is no possibility of permanent distortion occurring in the yacht sail and loss of dimensional stability. In other words, it has high durability.
（３）ヨツト用ロープの表面が滑り難いのでヨツト用ロ
ープを操作するときの取扱性（Ｈａｎｄｌｉｎｇ性）が
良好である。(3) Since the surface of the yachting rope is hard to slip, the handling property when operating the yachting rope is good.
く実 施 例〉
以下、実施例により本発明のヨツト用ロープの製造方法
を具体的に説明する。なお実施例においてロープの強伸
度、耐久性は下記の方法に従って測定した。EXAMPLES Hereinafter, the method for manufacturing a yacht rope of the present invention will be specifically explained using examples. In the examples, the strength and elongation and durability of the ropes were measured according to the following methods.
強伸度 ＪＩＳ−Ｌ−２７０７−１９８４の方法に従った。Strong elongation The method of JIS-L-2707-1984 was followed.
試験機は定速伸長型引張試験機（Ｉ ｎ５ｔｒｏｎ ）
、引張速度： ５ｃｍ／ｍｉｎ 、試料有効長：１８０
ｃｍ耐久性（摩耗）
外洋型ヨツトに取付け、長期間使用したときの乗組員の
感触（取扱性）および使用後のロープ表面観察によって
判定した。The testing machine is a constant speed extension type tensile testing machine (In5tron).
, tensile speed: 5 cm/min, sample effective length: 180
cm Durability (Abrasion) The rope was attached to an ocean-going yacht and evaluated based on the feel of the rope (handlability) when used for a long period of time and observation of the rope surface after use.
実施例１
まず下記の条件でポリエステルタスラン加工糸を作成し
た。Example 1 First, a polyester Taslan processed yarn was created under the following conditions.
（１＆［Ａ：総繊度１５００デニール、２５０フイラメ
ントのポリエチレンテレフタレート繊維
供給繊維Ｂ：総繊度２５０デニニル、４８フイラメント
のポリエチレンテレフタレート繊維
タスラン加工速度 ： ４７ｍｍ／ｍｉｎオーバーフィ
ード率：繊維Ａに対し＋３０％で繊維Ｂを供給
圧空圧 ： ６．Ｏｋｇ／ｃｍ”
ドラフト ：０．３ ％
得られたタスラン加工糸は見掛は繊度が１９００デニー
ル、強度は７．５ｇ／ｄ、伸度は１７％であった。(1 & [A: Polyethylene terephthalate fiber with a total fineness of 1500 denier and 250 filaments Supply fiber B: Polyethylene terephthalate fiber with a total fineness of 250 denier and 48 filaments Taslan processing speed: 47 mm/min Overfeed rate: +30% for fiber A Supply pressure of B Pneumatic pressure: 6.Okg/cm" Draft: 0.3% The obtained Taslan processed yarn had an apparent fineness of 1900 denier, a strength of 7.5 g/d, and an elongation of 17%.
つぎに総繊度１５００デニーノベ２５０ フィラメント
（強度９．５ｇ／ｄ、伸度１２％）のポリエチレンテレ
フタレート繊維を芯繊維層とし、これに１５００デニー
ル、１０００フイラメントの全芳香族ポリアミ■
ド繊維テクノーラ（奇人■製二強度２５ｇ／ｄ。Next, polyethylene terephthalate fiber with a total fineness of 1500 denier 250 filaments (strength 9.5 g/d, elongation 12%) is used as the core fiber layer, and this is coated with a fully aromatic polyamide fiber of 1500 denier and 1000 filaments. Durability: 25g/d.
伸度４．４％）を編組して中繊維層とし、最外層として
前記のタスラン加工糸を編組して直径１２ｍｍのヨツト
用ロープを作成した。得られたロープの強伸度、実地に
使用したときのロープ表面の摩耗耐久性についての評価
結果を第１表に示した。A rope for yachting with a diameter of 12 mm was prepared by braiding the yarn (with an elongation of 4.4%) to form the middle fiber layer, and the above-mentioned Taslan processed yarn as the outermost layer. Table 1 shows the evaluation results for the strength and elongation of the obtained rope and the abrasion durability of the rope surface when used in actual use.
実施例２
芯繊維として実施例１で用いた全芳香族ポリアミド繊維
にポリウレタン樹脂加工を施したものを用い、これに実
施例１のタスラン加工糸を編組して最外層として、直径
１２ｍｍのヨツト用ロープを作成した。ロープ物性等に
ついての評価結果を第１表に示した。Example 2 The fully aromatic polyamide fiber used in Example 1 treated with polyurethane resin was used as the core fiber, and the Taslan processed yarn of Example 1 was braided into it to form the outermost layer. Created a rope. Table 1 shows the evaluation results regarding the physical properties of the rope.
実施例３
太い部分と細い部分とを有するヨツト用ロープにおいて
、太い部分の芯繊維として１０００デニーノぺ１９２
フィラメントのポリエチレンテレフタレート長繊維と実
施例１で用いた全方＠族ポリアミド繊維とからなる混合
繊維を用い、細い部分の芯繊維として同様に実施例１で
用いた全芳香族ポリアミド繊維のみを用いた。 太い部
分と細い部分とを有するこの芯繊維層にやはり実施例１
で用いたタスラン加工糸を編組して太い部分の直径が３
ｍｍ、細い部分の直径が３＋ｎ＋ｎのヨツト用ロープを
得た。Example 3 In a yacht rope having a thick part and a thin part, 1000 Deninope 192 was used as the core fiber of the thick part.
A mixed fiber consisting of the polyethylene terephthalate long fibers of the filament and the wholly @ group polyamide fiber used in Example 1 was used, and only the wholly aromatic polyamide fiber similarly used in Example 1 was used as the core fiber of the thin part. . In this core fiber layer having a thick portion and a thin portion, Example 1 was also applied.
The diameter of the thick part is 3 by braiding the Taslan processed yarn used in
A sailing rope having a diameter of 3+n+n at the thinner part was obtained.
得られたロープは、表面が滑り難く感触も柔らかく取扱
性が良好であった。The obtained rope had a non-slip surface, a soft feel and good handling properties.
比較例１
芯繊維として１０００デニーノペ１９２ フィラメント
、無撚のポリエチレンテレフタレート繊維（強度９．０
ｇ／ｄ 、伸度１３％）を用い、これに最外層繊維とし
て綿番手３番のポリエチレンテレフタレート紡績糸を編
組して１２ｍｍのヨツト用ロープを作成した。Comparative Example 1 Core fiber: 1000 Deny Nope 192 filament, untwisted polyethylene terephthalate fiber (strength: 9.0
g/d, elongation 13%), and a polyethylene terephthalate spun yarn of cotton count No. 3 was braided thereto as the outermost fiber to prepare a 12 mm yacht rope.
得られたロープの物性等の評価結果を第１表に示した。Table 1 shows the evaluation results of the physical properties of the rope obtained.
比較例２
太い部分と細い部分とを有するヨツト用ロープにおいて
太い部分の芯繊維として直径３ｍｍのステンレスワイヤ
ーロープと１０００デニーノペ１９２ フィラメントの
ポリエチレンテレフタレート長繊維糸（強度９．０ ｇ
／ｄ 、伸度１３％）とを引揃した混合繊維を用い、細
い部分の芯繊維として上記のステンレスワイヤーロープ
のみを用いた。Comparative Example 2 In a sailboat rope having a thick part and a thin part, a stainless steel wire rope with a diameter of 3 mm and a polyethylene terephthalate long fiber yarn of 1000 Deny Nope 192 filament (strength 9.0 g) were used as the core fiber of the thick part.
/d, elongation 13%) were used, and only the above-mentioned stainless steel wire rope was used as the core fiber in the thin part.
これに綿番手３番のポリエチレンテレフタレート紡績糸
を編組して太い部分の直径が３ｍｍ、細い部分の直径が
３ｍｍのヨツト用ロープを得た。得られたロープは表面
が滑りやすく感触は硬く、取扱性が劣っていた。This was braided with polyethylene terephthalate spun yarn of cotton count No. 3 to obtain a sailing rope having a diameter of 3 mm at the thick part and 3 mm at the thin part. The resulting rope had a slippery surface, a hard feel, and poor handling properties.
Claims (7)
維ロープにおいて、少なくとも１層が全芳香族ポリアミ
ド繊維を含み、かつ最外層がポリエステルタスラン加工
糸からなることを特徴とするヨット用ロープ(1) A fiber rope for yachts comprising a core fiber layer and a covering layer made of braided fibers, in which at least one layer contains fully aromatic polyamide fibers, and the outermost layer is made of polyester Taslan processed yarn. rope
求のの範囲第（１）項に記載のヨット用ロープ(2) The yacht rope according to claim (1), wherein the core fiber layer is a wholly aromatic polyamide fiber.
特許請求の範囲第（２）項に記載のヨット用ロープ(3) A yacht rope according to claim (2), which is made of fully aromatic polyamide fibers coated with resin.
請求の範囲第（１）項に記載のヨット用ロープ(4) A yacht rope according to claim (1), wherein the core fiber layer is a polyester long fiber twisted yarn.
請求の範囲第（１）項に記載のヨット用ロープ(5) The yacht rope according to claim (1), wherein the core fiber layer is polyester long fiber non-twisted yarn.
アミド繊維を編組した中層を設け、該中層にポリエステ
ルタスラン加工糸を編組した最外層を設けてなる特許請
求の範囲第（１）項に記載のヨット用ロープ(6) A core layer made of long polyester fibers is provided with a middle layer made of braided wholly aromatic polyamide fibers, and the middle layer is provided with an outermost layer made of braided polyester Taslan processed yarn. yacht rope
て、太い部分の芯層はポリエステル長繊維糸と全芳香族
ポリアミド繊維とで構成され、細い部分の芯層は全芳香
族ポリアミド繊維で構成され、それぞれの層にポリエス
テルタスラン加工糸を編組した最外層を設けてなる特許
請求の範囲第（１）項に記載のヨット用ロープ(7) A fiber rope having a thick part and a thin part, where the core layer of the thick part is composed of polyester long fiber yarn and wholly aromatic polyamide fibers, and the core layer of the thin part is composed of wholly aromatic polyamide fibers. A yacht rope according to claim (1), wherein each layer has an outermost layer made of braided polyester Taslan thread.