JPS62280272A - Coating material for use to impart suede-like finish to surface of object - Google Patents
Coating material for use to impart suede-like finish to surface of objectInfo
- Publication number
- JPS62280272A JPS62280272A JP12342686A JP12342686A JPS62280272A JP S62280272 A JPS62280272 A JP S62280272A JP 12342686 A JP12342686 A JP 12342686A JP 12342686 A JP12342686 A JP 12342686A JP S62280272 A JPS62280272 A JP S62280272A
- Authority
- JP
- Japan
- Prior art keywords
- suede
- coating material
- fibers
- give
- product according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
３、発明の詳細な説明
産業上の利用分野
本発明は、コーティング材料、殊に物の表面をスェード
調にし、すぐれた外観、風合い（手触り等）を持ち、か
つ防眩性の良いものにする為のコーティング材料に関す
る。Detailed Description of the Invention 3. Detailed Description of the Invention Industrial Application Field The present invention relates to a coating material, especially a coating material that has a suede-like surface, has an excellent appearance and feel (touch, etc.), and has an excellent resistance. Concerning coating materials to provide good glare.
従来の技術
例えば合成樹脂シートの表面をスェード調にするには、
エンボス法に依ったり、短い繊維を静゛１を植毛したり
、織布若しくは不縄ｌσを合成樹脂で固め毛羽立てたり
、発泡体をスライスして毛羽立てたり、或いは細かいビ
ーズを合成樹脂の表面に塗布したりしていた。Conventional techniques For example, to make the surface of a synthetic resin sheet suede-like,
By embossing, by flocking short fibers, by hardening and fluffing woven or non-woven fabric with synthetic resin, by slicing foam and fluffing it, or by attaching fine beads to the surface of synthetic resin. It was also applied to
又１合成樹脂の表面を防眩性にするには、上記のほかに
、合成樹脂液にシリカ、炭酸マグ茅シュウム、タルク等
の無機質微粉末又はワックス類が混入されている艶消し
塗料も用いられていた。In addition to the above, in order to make the surface of synthetic resin anti-glare, a matte paint in which fine inorganic powder such as silica, magnanium carbonate, talc, or wax is mixed into the synthetic resin liquid is also used. It was getting worse.
発り１が解決しようとする問題点
しかしエンボス法によりスェード調にした合成樹脂シー
トや発泡体をスライスして毛羽立てた合成樹脂シートは
、その後成形（例えば真空成形。Problems that Origin 1 attempts to solve However, synthetic resin sheets that have been made into a suede-like appearance by the embossing method or synthetic resin sheets that have been sliced and fluffed from foam are then molded (e.g., vacuum formed).
圧空成形″Ｊ）は出来るが、外観も手触りもあまり良く
ない。Pressure molding (J) is possible, but the appearance and feel are not very good.
織布若しくは不Ｊｌｔ！布を用いたものも外観、Ｌ触り
は良いが成形には向かない。Woven fabric or non-woven fabric! Those using cloth also have a good appearance and feel, but are not suitable for molding.
又、細かいビーズを合成樹脂の表面に接着したものや、
誠維を静電気を用いて整列させ接着剤を用いて合成樹脂
表面に固定したものは、接着剤が成形時の熱に耐えられ
ず、ヒビわれしたり、また、成形するとビーズや思雄の
配夕呵にムラが出来たりする。その為、専ら成形後の製
品への使用に限られている。Also, fine beads glued to the surface of synthetic resin,
When the Sei fibers are aligned using static electricity and fixed to the synthetic resin surface using adhesive, the adhesive cannot withstand the heat during molding and may crack, or when molded, the beads and the fibers may be arranged. There may be unevenness in the evening. Therefore, its use is limited to products after molding.
さらに、艶消し塗料は防眩性がそれほど優れているとも
いえず、スクラッチも入りやすく、しかも成形時の加熱
延伸で艶変化があるため、成形前に塗布することは出来
なかった。Furthermore, matte paints cannot be said to have very good anti-glare properties, are prone to scratches, and change in gloss due to heating and stretching during molding, so they could not be applied before molding.
本発明は、成形前でも成形後でも表向を防眩性が優れ外
観も丁触りも良いスェード調にすることができるコーテ
ィング材料を提供することを目的としている。An object of the present invention is to provide a coating material that can give a suede-like surface with excellent anti-glare properties and a good appearance and feel both before and after molding.
問題点を解決する為のＬ段
本発明のコーティング材料には、繊維が混入されており
、これをスェード調にすべき表面に塗り乾燥後、場合に
より毛羽立てを行うものである。L stage to solve the problem The coating material of the present invention contains fibers, which are applied to the surface to be suede-like, dried, and then fluffed if necessary.
本発明のコーティング材料は、例えばアクリル樹脂、塩
化ビニル樹脂、ウレタン樹脂、ポリエステル樹脂、ポリ
アミド樹脂、或いはこれらの混合物を基材とするが、種
類や性状は塗布すべき而の材質や、後に成形される場合
には成形時の伸度等も考慮して決められる。これ以外の
合成樹脂又は合成樹脂以外のもの（例えば天然樹脂）を
基材としたものや、これらとＬ記樹脂等とを組合わせた
ものでも良い。The coating material of the present invention is based on, for example, acrylic resin, vinyl chloride resin, urethane resin, polyester resin, polyamide resin, or a mixture thereof, but the type and properties may vary depending on the material to be coated or the material to be molded later. In the case of molding, the elongation during molding is also taken into consideration. It is also possible to use other synthetic resins or materials other than synthetic resins (for example, natural resins) as a base material, or combinations of these and L resins.
コーティング材料には、必要に応じて有色顔料を入れ塗
料のかたちにしたり、シリカの如き艶消し助剤や１体質
顔料、安定剤、可塑剤、充Ｉｒｉ〜１等の補助剤を入れ
てもよい。If necessary, the coating material may contain colored pigments to form a paint, or may contain auxiliary agents such as matting aids such as silica, unibody pigments, stabilizers, plasticizers, and fillers. .
基材は水または有機溶剤及び助剤など、それぞれの基材
に適切な溶剤、助剤で溶解されていることもできる。The substrates can also be dissolved in water or with solvents and auxiliaries appropriate for the respective substrates, such as organic solvents and auxiliaries.
混入される１８ ｍの長さ及び太さは、出来上がりのス
ェード調の外観及びト触り及び塗布方法にょり異なるが
、一般には長さ３ｆｆｉ国以下、好ましくはｌｌｌ１１
以下、太さは３００デニール以下、好ましくは１０デニ
ール以下である。The length and thickness of the 18 m mixed in will vary depending on the finished suede-like appearance and feel and application method, but generally the length is 3ffi or less, preferably lll11.
Hereinafter, the thickness is 300 deniers or less, preferably 10 deniers or less.
例えば、リバースロールコータ−法で塗布する場合 太さ １．０〜１０．０ デニール 長さ ０．５〜２ ■ が好ましい。For example, when applying with reverse roll coater method Thickness 1.0-10.0 denier Length 0.5-2 ■ is preferred.
ＦＲ雄の址は基材 １００屯量部に対して ３００重着
部以ｒ、好ましくは基材１００重着部に対して２５〜１
００１六部が良い。The weight of FR male is 300 parts or more per 100 parts of base material, preferably 25 to 1 part per 100 parts of base material.
0016 parts is good.
繊維の材質は１例えばナイロン、ビニロン、ポリエステ
ル等の合成繊維であることができるが、これ以外の合し
＆繊維或いは合成樹脂以外のものでも良い、ｍｍは必要
に応じて着色しても良い。The material of the fibers can be synthetic fibers such as nylon, vinylon, polyester, etc., but it may also be other combinations and fibers or materials other than synthetic resins.The fibers may be colored if necessary.
塗布する表面は、成形前のシート状の合成樹脂でも、成
形後の合成樹脂でも、或いは合成樹脂以外の木、金属、
ガラス、磁器等何んでも良く、又その形状も問わない。The surface to be coated may be sheet-like synthetic resin before molding, synthetic resin after molding, or wood, metal, or other material other than synthetic resin.
It can be made of glass, porcelain, etc., and its shape does not matter.
塗布は、場合により塗布すべき表面を予め処理してから
、コーチづング材料をそのまま、溶剤などに溶解されて
いない場合には１水または有機溶剤及び助剤など、それ
ぞれの基材に適切な溶剤。Application may be carried out by pre-treating the surface to be coated, and then using the coating material as is or, if not dissolved in a solvent, in a suitable solution for each substrate, such as 1 water or an organic solvent and an auxiliary agent. solvent.
助剤で溶解したり、希釈して刷毛、或いはリバースロー
ルコータ−を用いて若しくはその他の’Ｉｘ Ａｘ方法
で行うことが出来る。It can be applied by dissolving or diluting with an auxiliary agent and using a brush or reverse roll coater, or by other 'Ix Ax methods.
塗７σ礒は、塗布する個所及び表［ｎｌの材質等で異な
るが、例えば、溶剤で溶解する前の状態でｌモ方メート
ル当り数十ｇ７″７全数百ｇ、好ましくは、２０〜ｔｏ
ｏ ｌであることができる。必要により、プラ・イマー
等を塗ってからコーティング材料ヲ塗っても良い。The amount of coating 7σ varies depending on the area to be applied and the material of the material, but for example, before dissolving with a solvent, the amount is several tens of grams per meter, preferably several hundred grams.
It can be o l. If necessary, the coating material may be applied after applying a primer or primer.
乾燥方法は、自然乾燥でも、加熱乾燥でも如何なる方法
でも良い、乾爆後、ざらに毛羽ｔてを施すと、外観、風
合いがさらに良くなる。The drying method may be natural drying or heat drying, or any other method.If the material is fluffed after dry blasting, the appearance and texture will be even better.
毛朋党ては、針ＡＪ、サントペーパー等、塗布された表
面の形状及び犬ぎさに応じて適宜の方法を用いうる。An appropriate method can be used depending on the shape and hardness of the coated surface, such as needle AJ or sandpaper.
実施例 Ｉ
ＰＶＣ（ＶＹＨＨ）１１ ｌ ＯＯＭＥＫ（メチ
ｈｚチｈケトン） １５０トルエン
１５０
ＤＯＰ（ジすクナルプタレート）ｌＯ
顔料 （Δ−４シブラック）
５安定剤（Ｃｄ−Ｂａ ） ３
ビニロン短繊維？）２５
１〉ユニオンカーバイト 社’ＪＪ 塩化ヒニル樹
脂７１ ：ｊＱデニール、 １．０ ｍ箇溶解条件
オートクレーブ中で７０°Ｃ４時間加温し溶解、分散さ
せた。Example I PVC (VYHH) 11 l OOMEK (methyhzthihketone) 150 toluene
150 DOP (dicunal ptalate) lO pigment (Δ-4 siblack)
5 Stabilizer (Cd-Ba) 3
Vinylon staple fiber? )25 1>Union Carbide Co.'JJ Hinyl Chloride Resin 71: jQ denier, 1.0 m dissolution conditions Dissolved and dispersed by heating at 70°C for 4 hours in an autoclave.
」１記のコーティング材料を、厚さｌ １１ｍの軟質Ｐ
ｖＣシートに、リバースロールローターで塗布した。１
３０℃で３分間加熱して乾燥した結果、スェード調のシ
ートが得られた。このシートを１通常のごとく成形した
が、ヒビわれたり、ムラになったりすることもなく、外
観、−ト触りとも良（ｌｒであった。また、このソート
をサントペーパーでｔ朋党てしたら、外観、風合いとも
さらに良好なスェード調のソートが得られた。”The coating material described in item 1 was coated with a soft P coated with a thickness of
It was applied to the vC sheet using a reverse roll rotor. 1
As a result of heating and drying at 30° C. for 3 minutes, a suede-like sheet was obtained. This sheet was molded as usual, but there were no cracks or unevenness, and the appearance and feel were good. A suede-like sorting with even better appearance and texture was obtained.
実施例 ２
アクリル樹脂１１ １００
ＭＥＫ １５０
トルエン １５０
シリカ １０
顔料 （カーボンブラック）
５ビニロン短繊維２）２５
１）ＭＭＡ−ＥＡ共重合体、分子は ８万（７０：３０
）
７１２．０デニール、 １．０１１ｎ溶解条件
オートクレーブ中で８０℃ ６時間加温し溶解、分散さ
せた。Example 2 Acrylic resin 11 100 MEK 150 Toluene 150 Silica 10 Pigment (carbon black)
5 Vinylon staple fiber 2) 25 1) MMA-EA copolymer, molecule is 80,000 (70:30)
) 712.0 denier, 1.011n dissolution conditions: Dissolved and dispersed by heating in an autoclave at 80°C for 6 hours.
Ｌ記のコーティング材料を、厚さ１ＩＩ１１の軟質ＰＶ
Ｃシートに、す／゛・−スロールローターで塗１１した
。１３０°Ｃで３分間加熱して乾燥した結果、スェード
調のソートが得られた。このシートを５通常のこと〈成
形したが、ヒビわれたり、ムラになったりすることもな
く、外観、手触りとも良好であった。また、このシート
をサンドペーパーテ且朋党てしたら、外観、風合いとも
さらに良好なスェード調のシートが得られた。The coating material listed in L is coated with soft PV having a thickness of 1II11.
Coating was carried out on C sheet using a S/゛・-throttle rotor. As a result of drying by heating at 130°C for 3 minutes, a suede-like sort was obtained. This sheet was molded in the usual way, but it did not crack or become uneven, and had a good appearance and feel. Furthermore, when this sheet was sandpapered, a suede-like sheet with even better appearance and texture was obtained.
従来品
ＰＶＣ（ＶＹＨＨ） ６０アクリル樹脂（
ＭＭＡ−ＥＡ） ４０ＭＥＫ
１５０トルエン １５０
シリカ ３０
顔料 （ｈ−５シブラツク）
５溶解条件
オートクレーブ中で８０℃ ６時間加温し溶解、分散さ
せた。Conventional product PVC (VYHH) 60 Acrylic resin (
MMA-EA) 40MEK
150 Toluene 150 Silica 30 Pigment (h-5 Shibrak)
5. Dissolution Conditions The mixture was heated in an autoclave at 80° C. for 6 hours to dissolve and disperse.
上−記のコーディング材料を、厚さｌ ｍｍの軟質Ｐｖ
Ｃシートに、リバースロールローターで塗！■１した。The above-mentioned coating material is coated with a soft Pv having a thickness of l mm.
Paint on C sheet with a reverse roll rotor! ■I did 1.
１３０℃で３分間加熱して乾燥した。It was dried by heating at 130° C. for 3 minutes.
実施例１．２のものと、従来品との防眩性を反射率で比
較測定し、次の結果を得た。The anti-glare properties of Example 1.2 and the conventional product were compared and measured in terms of reflectance, and the following results were obtained.
ｄａｘメ−ｑ−角度 実施例 従来品（投光
）（受光）ｌ ２
７０ ８０ ０．３ Ｑ、４
４．５Ｇｏ ８０ ０
．１ ０．２ ３．５５０ ［
１００，００，０２，０４０ｉ３０ ０．０
０．０ ０．５３０ ［１
００，００，００，２２０６００，００，００，０
測定）Ｉｌｌ Ｇｌａｓｓ Ｍｅｔｅｒ ＴＣニー１
０８０ （東京主色製）発明の効果
本発明のコーティング材料は、成形萌のシート状の合成
樹脂でも、成形後の合成樹脂でも、或いは合成樹脂以外
の木、全屈、ガラス、磁器笠何んでもその表面をスェー
ド調にするのに用いることができ、出来たスェード調表
面は、防眩性、外観、手触りがきわめて良好で、成形し
てもヒビわれたり、ムラになったりすることもないきわ
めて優れたものである。dax me-q-angle Example Conventional product (light emission) (light reception) l 2 70 80 0.3 Q, 4
4.5 Go 80 0
．． 1 0.2 3.550 [
100,00,02,040i30 0.0
0.0 0.530 [1
00,00,00,220600,00,00,0 Measurement) Ill Glass Meter TC knee 1
080 (Manufactured by Tokyo Shushoku) Effects of the Invention The coating material of the present invention can be applied to sheet-shaped synthetic resin in molded form, synthetic resin after molding, or wood, full-length, glass, porcelain shade, etc. other than synthetic resin. However, it can be used to create a suede-like surface, and the resulting suede-like surface has excellent anti-glare properties, appearance, and feel, and does not crack or become uneven even when molded. It is extremely excellent.
Claims (14)
る為に用いられるコーティング材料(1) Coating material mixed with fibers and used to make the surface of objects look like suede
載の物の表面をスエード調にする為に用いられるコーテ
ィング材料。(2) A coating material used to give a suede-like surface to a product according to claim 1, wherein the base material is a synthetic resin.
ン樹脂、ポリエステル樹脂、ポリアミド樹脂、或いはこ
れらの混合物である、特許請求の範囲第２項記載の物の
表面をスエード調にする為に用いられるコーティング材
料。(3) Used to give a suede-like surface to the product according to claim 2, wherein the base material is acrylic resin, vinyl chloride resin, urethane resin, polyester resin, polyamide resin, or a mixture thereof. coating material.
囲第１項記載の物の表面をスエード調にする為に用いら
れるコーティング材料。(4) A coating material used to give a suede-like surface to a product according to claim 1, wherein the base material is other than a synthetic resin.
化ビニル樹脂、ウレタン樹脂、ポリエステル樹脂、ポリ
アミド樹脂、或いはこれらの混合物とを組合わせもので
ある、特許請求の範囲第１項記載の物の表面をスエード
調にする為に用いられるコーティング材料。(5) The base material according to claim 1, wherein the base material is a combination of a material other than a synthetic resin and an acrylic resin, a vinyl chloride resin, a urethane resin, a polyester resin, a polyamide resin, or a mixture thereof. A coating material used to make the surface of objects look like suede.
の物の表面をスエード調にする為に用いられるコーティ
ング材料。(6) A coating material used to give a suede-like surface to a product according to claim 1, wherein the fibers are short fibers.
６項記載の物の表面をスエード調にする為に用いられる
コーティング材料。(7) A coating material used to give a suede-like surface to a product according to claim 1 or 6, wherein the fibers are synthetic fibers.
囲第１又は６項記載の物の表面をスエード調にする為に
用いられるコーティング材料。(8) A coating material used to give a suede-like surface to a product according to claim 1 or 6, wherein the fibers are fibers other than synthetic fibers.
下である、特許請求の範囲第１又は６〜８項のいずれか
一つに記載の物の表面をスエード調にする為に用いられ
るコーティング材料。(9) Used to give a suede-like surface to the product according to any one of claims 1 or 6 to 8, wherein the fibers have a length of 3 mm or less and a thickness of 300 denier or less. coating material.
下である、特許請求の範囲第９項記載の物の表面をスエ
ード調にする為に用いられるコーティング材料。(10) A coating material used to give a suede-like surface to a product according to claim 9, wherein the fibers have a length of 1 mm or less and a thickness of 10 denier or less.
量部以下である、特許請求の範囲第１項記載の物の表面
をスエード調にする為に用いられるコーティング材料。(11) A coating material used to give a suede-like surface to a product according to claim 1, wherein the amount of fiber is 300 parts by weight or less based on 100 parts by weight of the base material.
００重量部である、特許請求の範囲第１項記載の物の表
面をスエード調にする為に用いられるコーティング材料
。(12) The amount of fiber is 25 to 1 per 100 parts by weight of the base material.
00 parts by weight of a coating material used for making the surface of the article according to claim 1 suede-like.
補助剤を混入してなる、特許請求の範囲第１項記載の物
の表面をスエード調にする為に用いられるコーティング
材料。(13) A coating material used to make the surface of the article described in claim 1 suede-like, which is made by mixing auxiliary agents such as pigments, stabilizers, plasticizers, and fillers in addition to fibers. .
いる、特許請求の範囲第１項記載の物の表面をスエード
調にする為に用いられるコーティング材料。(14) A coating material used to give a suede-like surface to a product according to claim 1, wherein the base material is dissolved in water or an organic solvent and an auxiliary agent.