JPS6219786A - Timepiece dial having hologram - Google Patents
Timepiece dial having hologramInfo
- Publication number
- JPS6219786A JPS6219786A JP15874085A JP15874085A JPS6219786A JP S6219786 A JPS6219786 A JP S6219786A JP 15874085 A JP15874085 A JP 15874085A JP 15874085 A JP15874085 A JP 15874085A JP S6219786 A JPS6219786 A JP S6219786A
- Authority
- JP
- Japan
- Prior art keywords
- hologram
- layer
- resin
- dial
- resins
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
〔発明の技術分野〕
本発明は、腕時計、置時計等の時計の文字板に関し、さ
らに詳しくは、特定の樹脂によって形成されたホログラ
ムが設けられている時計文字板に関する。DETAILED DESCRIPTION OF THE INVENTION [Technical Field of the Invention] The present invention relates to a dial of a timepiece such as a wristwatch or table clock, and more particularly to a clock dial provided with a hologram formed of a specific resin.
ホログラフィ−とは、物体からの光の波面の様子を記録
再生する新しい技術であって、この技術によって作られ
たホログラム(物体からの光の波面の様子を光の干渉に
より生じた干渉縞の形で記録した材料)によれば、立体
像を再生することができしかも多重記録も可能となる。Holography is a new technology that records and reproduces the state of the wavefront of light from an object, and the hologram created by this technology (the state of the wavefront of light from an object is expressed in the form of interference fringes caused by light interference). According to the material recorded in 3D images, it is possible to reproduce a 3D image and also to perform multiple recording.
また、ホログラムの記録の一方法として干渉縞を材料表
面の凹凸模様で記録することができ、このホログラムは
大量複製が容易である。以下、この種の複製されたホロ
グラムをエンボスホログラムと呼ぶ。Further, as a method of recording a hologram, interference fringes can be recorded as an uneven pattern on the surface of a material, and this hologram can be easily reproduced in large quantities. Hereinafter, this type of replicated hologram will be referred to as an embossed hologram.
ところで、従来、時計文字板自体にホログラムを用いた
装飾を施すことは一般に行なわれてこなかった。本発明
は、この時計文字板にホログラムを設けようとするもの
であり、文字板表面にホログラムを設けることが、時計
としての機能を害さない範囲内で審美性、意匠的価値を
向上させる上で極めて効果的であるという知見に基づい
てなされたものである。By the way, in the past, it has generally not been done to decorate the clock dial itself using holograms. The present invention aims to provide a hologram on this watch dial, and it is believed that providing a hologram on the dial surface improves aesthetics and design value within the range that does not impair the function of the watch. This was done based on the knowledge that it is extremely effective.
(発明のR要)
本発明は上述した点に鑑みてなされたものであり、立体
的な視感によって審美性にすぐれ、しかも物理的、化学
的、機械的特性の向上が図られた時計文字板を提供する
ことを目的とする。(R Summary of the Invention) The present invention has been made in view of the above-mentioned points, and provides a clock character that has excellent aesthetics due to three-dimensional visibility and has improved physical, chemical, and mechanical properties. The purpose is to provide a board.
上記目的を達成するため、本発明の時計文字板は、時計
文字板基材の表面の一部または全面にホログラムが設け
られていることを特徴とする。In order to achieve the above object, the watch dial of the present invention is characterized in that a hologram is provided on a part or the entire surface of the watch dial base material.
(発明の実施例〕
以下、本発明を図面に示す具体例に基づいて詳細に説明
する。(Embodiments of the Invention) The present invention will be described in detail below based on specific examples shown in the drawings.
本発明の時計文字板に用い得るホログラムとしては、そ
の再生機能上、「反射型」であるものはいずれも適用可
能である。ここで、「反射型」とは、ホログラムに対し
その再生光源と同じ側に回折光を発生するタイプであり
「透過型」のホログラムの背面に再生光を反射させるた
めの反射層を設けたタイプのホログラムをも含むものと
する。Any hologram that can be used in the watch dial of the present invention is of a "reflection type" in terms of its reproduction function. Here, "reflection type" is a type that generates diffracted light on the same side of the hologram as the reproduction light source, and "transmission type" is a type in which a reflective layer is provided on the back of the hologram to reflect reproduction light. It also includes holograms.
具体的なホログラムの種類としては、イメージホログラ
ム、レインボーホログラム、リップマンホログラム、ホ
ログラフィックステレオグラム、回折格子等が広く適用
され得る。As specific types of holograms, image holograms, rainbow holograms, Lippmann holograms, holographic stereograms, diffraction gratings, etc. can be widely applied.
ホログラムを材料別に大別すると、「感光材料型」と「
エンボス複製型」の2タイプに分けられ、後者は本発明
に利用しうる。リップマンホログラム以外の「感光材料
型」のホログラムは再生機能上は透過型であるので前述
したように背面に反射層を伴う。また、「感光材料型」
でリップマンホログラムのタイプは、そのまま用いるこ
とができる。また、「エンボス複製型」で材料として透
明樹脂を用いたものは透過型であり背面に反射層を形成
して適用することができるが、レリーフ面にレリーフ形
状に従う反射層を、たとえば真空蒸着法等により設は反
射型ホログラムとしてそのまま利用することができる。When holograms are roughly classified by material, there are two types: “photosensitive material type” and “
There are two types: the embossed reproduction type, and the latter can be used in the present invention. Since "photosensitive material type" holograms other than Lippmann holograms are transmission type in terms of reproduction function, they are accompanied by a reflective layer on the back surface as described above. In addition, “photosensitive material type”
The Lippmann hologram type can be used as is. In addition, the "embossed duplication type" that uses transparent resin as a material is a transmissive type and can be applied by forming a reflective layer on the back surface, but it is also possible to apply a reflective layer that follows the relief shape on the relief surface using, for example, vacuum evaporation. The structure can be used as is as a reflection hologram.
第1図に示す時計文字板1は、エンボスホログラムを用
いて時計文字板基材2上に、接着剤層3を介して、反射
性金属簿膜層4ならびにホログラム層5が偵庖されてい
る。A watch dial 1 shown in FIG. 1 has a reflective metal film layer 4 and a hologram layer 5 formed on a watch dial base material 2 via an adhesive layer 3 using an embossed hologram. .
第2図に示す時計文字板1は、ホログラム層5の微小な
凹凸形状の表面に反射性金属薄膜層4を積層した場合の
例である。The clock dial 1 shown in FIG. 2 is an example in which a reflective metal thin film layer 4 is laminated on the surface of the hologram layer 5 having minute irregularities.
第3図に示す時計文字板1は、反射性金属層10の表面
にホログラム層5を設けた場合の例であり、ホログラム
の凹凸形状は表面に露出した構成となっている。The clock dial 1 shown in FIG. 3 is an example in which a hologram layer 5 is provided on the surface of a reflective metal layer 10, and the uneven shape of the hologram is exposed on the surface.
上記第2図の構造においては、表面の凹凸形状が露出し
ているので、表面の損傷を防止する上で、表面に保m層
を設けることが好ましい。 以下、各構成材料について
、さらに詳細に説明する。In the structure shown in FIG. 2 above, since the uneven shape of the surface is exposed, it is preferable to provide a heat-retaining layer on the surface to prevent damage to the surface. Each constituent material will be explained in more detail below.
11又ヱwmu
時計文字板基材2としては、従来、時計文字板用材料と
して用いられている金属、プラスチックス、セラミック
スなどの材料がすべて用いられ得る。As the watch dial base material 2, all materials conventionally used as watch dial materials such as metals, plastics, and ceramics can be used.
これら時計文字板基材には、図示はされていないが、文
字板としての機能上必要な、針の回転軸用孔、文字、数
字などが形成されている。Although not shown in the drawings, these timepiece dial base materials are formed with holes for the rotating shaft of the hands, letters, numbers, etc. that are necessary for the function of the dial.
ホログラムは、これら時計文字ffi !2材の全面ま
たは一部(たとえば、数字、目@等)に設けることがで
きる。The holograms are these clock letters ffi! It can be provided on the entire surface or a part (for example, numbers, eyes, etc.) of the second material.
色且グユA1
ホログラム層5は、ホログラム用感光材料またはエンボ
スホログラム形成材料からなる。Color and Gray A1 The hologram layer 5 is made of a hologram photosensitive material or an embossed hologram forming material.
ホログラム層5の厚みは、文字板の大きさ、ホログラム
の種類によって適宜選択されつるが、通常、0.1〜5
0μm、望ましくは0.5〜5μmであることが好まし
い。The thickness of the hologram layer 5 is appropriately selected depending on the size of the dial and the type of hologram, but is usually 0.1 to 5.
It is preferably 0 μm, preferably 0.5 to 5 μm.
本発明にはエンボスホログラムが遺しており、このエン
ボスホログラム層用の樹脂は、ホログラムの成形(複製
)時には熱成形可能であり、ホログラム成形後つまり加
工時には、加工の際の熱圧力、接着剤中の溶剤に耐える
だけの耐性を有することが必要である。このような樹脂
としては、いわゆる紫外線硬化樹脂、電子線硬化樹脂、
熱硬化、自然硬化型の反応性の樹脂などが用いられうる
。The present invention has an embossed hologram, and the resin for this embossed hologram layer can be thermoformed when molding (duplicating) the hologram. It is necessary to have sufficient resistance to withstand solvents. Such resins include so-called ultraviolet curing resins, electron beam curing resins,
A thermosetting or naturally curing reactive resin may be used.
特に生産性を考慮した場合、紫外線もしくは電子線で硬
化する樹脂が適している。Especially when considering productivity, resins that are cured by ultraviolet rays or electron beams are suitable.
具体的には、たとえばメチルメタクリレート、メチルア
クリレート、エチルアクリレート、エチルメタクリレー
ト、プロピルアクリレート、プロピルメタクリレート、
ブチルアクリレート、ブチルメタクリレート、イソブチ
ルアクリレート、イソブチルメタクリレート、t−ブチ
ルアクリレート、t−ブチルメタクリレート、イソアミ
ルアクリレート、イソアミルメタクリレート、シクロへ
キシルアクリレート、シクロへキシルメタクリレート、
2−エチルへキシルアクリレート、2−エチルへキシル
メタクリレート、エチレングリコールジアクリレート、
エチレングリコールジメタクリレート、ポリエチレング
リコールジアクリレート、ポリエチレングリコールジメ
タクリレート、ヘキサンジオールジアクリレート、ヘキ
サンジオールジメタクリレート、トリメチロールプロパ
ントリアクリレート、トリメチロールプロパントリメタ
クリレート、1−リメチロールプロパンジアクリレート
、トリメチロールプロパンジメタクリレート、ペンタエ
リスリトールテトラアクリレート、ペンタエリスリトー
ルテトラメタクリレート、ペンタエリスリトールトリア
クリレート、ペンタエリスリトールトリメタクリレート
、ジペンタエリスリトールへキサアクリレート、ジペン
タエリスリトールへキサメタクリレート、エチレングリ
コールジグリシジルエーテルジアクリレート、エチレン
グリコールジグリシジルエーテルジメタクリレート、ポ
リエチレングリコールジグリシジルエーテルジアクリレ
ート、ポリエチレングリコールジグリシジルエーテルジ
メタクリレート、プロピレングリコールジグリシジルエ
ーテルジアクリレート、プロピレングリコールジグリシ
ジルエーテルジメタクリレート、ポリプロピレングリコ
ールジグリシジルエーテルジアクリレート、ポリプロピ
レングリコールジグリシジルエーテルジメタクリレート
、ソルビトールテトラグリシジルエーテルテトラアクリ
レート、ソルビトールテトラグリシジルエーテルテトラ
メタクリレート、などのラ jジカル重合性不
飽和基を有する単量体が用いられうる。Specifically, for example, methyl methacrylate, methyl acrylate, ethyl acrylate, ethyl methacrylate, propyl acrylate, propyl methacrylate,
Butyl acrylate, butyl methacrylate, isobutyl acrylate, isobutyl methacrylate, t-butyl acrylate, t-butyl methacrylate, isoamyl acrylate, isoamyl methacrylate, cyclohexyl acrylate, cyclohexyl methacrylate,
2-ethylhexyl acrylate, 2-ethylhexyl methacrylate, ethylene glycol diacrylate,
Ethylene glycol dimethacrylate, polyethylene glycol diacrylate, polyethylene glycol dimethacrylate, hexanediol diacrylate, hexanediol dimethacrylate, trimethylolpropane triacrylate, trimethylolpropane trimethacrylate, 1-rimethylolpropane diacrylate, trimethylolpropane dimethacrylate , pentaerythritol tetraacrylate, pentaerythritol tetramethacrylate, pentaerythritol triacrylate, pentaerythritol trimethacrylate, dipentaerythritol hexaacrylate, dipentaerythritol hexamethacrylate, ethylene glycol diglycidyl ether diacrylate, ethylene glycol diglycidyl ether dimethacrylate , polyethylene glycol diglycidyl ether diacrylate, polyethylene glycol diglycidyl ether dimethacrylate, propylene glycol diglycidyl ether diacrylate, propylene glycol diglycidyl ether dimethacrylate, polypropylene glycol diglycidyl ether diacrylate, polypropylene glycol diglycidyl ether dimethacrylate, sorbitol Monomers having radically polymerizable unsaturated groups such as tetraglycidyl ether tetraacrylate and sorbitol tetraglycidyl ether tetramethacrylate can be used.
さらに本発明に33いては、熱成形性を有する紫外線ま
たは電子線硬化樹脂を用いることができる。Furthermore, according to the present invention, an ultraviolet or electron beam curing resin having thermoformability can be used.
このような樹脂としては、以下の化合物■〜■を重合も
しくは共重合させた重合体に対し、゛後述する方法(イ
)〜(ニ)によりラジカル性不飽和基を導入したものが
用いられる。As such a resin, a polymer obtained by polymerizing or copolymerizing the following compounds (1) to (4) and introducing radically unsaturated groups by methods (a) to (d) described below is used.
■ 水酸基を有する単量体二N−メチ0−ルアクリルア
ミド、2−ヒドロキシエチルアクリレート、2−ヒドロ
キシエチルメタクリレート、2−ヒドロキシプロピルア
クリレート、2−ヒドロキシプロピルメタクリレート、
2−ヒドロキシブチルアクリレート、2−ヒドロキシエ
チルアクリレート、2−ヒドロキシ、3−フェノキシプ
ロビルメタクリレート、2−ヒドロキシ、3−フェノキ
シプロピルアクリレートなど。■ Monomers having a hydroxyl group 2N-methyl0-yacrylamide, 2-hydroxyethyl acrylate, 2-hydroxyethyl methacrylate, 2-hydroxypropyl acrylate, 2-hydroxypropyl methacrylate,
2-hydroxybutyl acrylate, 2-hydroxyethyl acrylate, 2-hydroxy, 3-phenoxypropyl methacrylate, 2-hydroxy, 3-phenoxypropyl acrylate, etc.
■ カルボキシル基を有する単量体ニアクリル酸、メタ
クリル酸、アクリロイルオキシエチルモノサクシネート
など。■ Monomers with carboxyl groups such as nialic acid, methacrylic acid, acryloyloxyethyl monosuccinate, etc.
■ エポキシ基を有する単量体ニゲリシジルメタクリレ
ートなど。■ Monomers such as nigericidyl methacrylate having epoxy groups.
■ アジリジニル基を有する単吊体:2−7ジリジニル
エチルメタクリレート、2−アジリジニルプロピオン酸
アリルなと。(2) Monohanging bodies having an aziridinyl group: 2-7 ziridinylethyl methacrylate, allyl 2-aziridinylpropionate, etc.
■ アミノ基を有する単量体ニアクリルアミド、メタク
リルアミド、ダイアセトンアクリルアミド、ジメチルア
ミノエチルメタクリレート、ジエチルアミノエチルメタ
クリレートなど。■ Monomers containing amino groups such as niacrylamide, methacrylamide, diacetone acrylamide, dimethylaminoethyl methacrylate, diethylaminoethyl methacrylate, etc.
■ スルフォン基を有する単ω体=2−アクリルアミド
ー2−メチルプロパンスルフォン酸など。■ Mono-omega substance having a sulfone group = 2-acrylamide 2-methylpropanesulfonic acid, etc.
■′イソシアネート基を有する単吊体:2.4−トルエ
ンジイソシアネートと2−ヒドロキシエチルアクリレー
トの1モル対1モル付加物などのジイソシアネートと活
性水素を有するラジアル重合性単量体の付加物など。(2) Monohanging body having an isocyanate group: an adduct of a diisocyanate and a radially polymerizable monomer having active hydrogen, such as a 1 mol to 1 mol adduct of 2.4-toluene diisocyanate and 2-hydroxyethyl acrylate.
■ さらに、上記の共重合体のガラス転移点を調節した
り、硬化膜・の物性を調節したりするために、上記の化
合物と、この化合物と共重合可能な以下のような単量体
とを共重合させることができる。このような共重合可能
な1m体としては、たとえばメチルアクリレート、メチ
ルアクリレート、エチルアクリレート、エチルメタクリ
レート、プロピルアクリレート、プロピルメタクリレー
ト、ブチルアクリレート、ブチルメタクリレート、イソ
ブチルアクリレート、イソブチルメタクリレート、t−
ブチルアクリレート、t−ブチルメタクリレート、イソ
アミルアクリレート、イソアミルメタクリレート、シク
ロへキシルアクリレート、シクロへキシルメタクリレー
ト、2〜エチルへキシルアクリレート、2−エチルへキ
シルメタクリレートなどが挙げられる。■ Furthermore, in order to adjust the glass transition point of the above copolymer and the physical properties of the cured film, the above compound and the following monomers that can be copolymerized with this compound are combined. can be copolymerized. Examples of such copolymerizable 1m bodies include methyl acrylate, methyl acrylate, ethyl acrylate, ethyl methacrylate, propyl acrylate, propyl methacrylate, butyl acrylate, butyl methacrylate, isobutyl acrylate, isobutyl methacrylate, t-
Examples include butyl acrylate, t-butyl methacrylate, isoamyl acrylate, isoamyl methacrylate, cyclohexyl acrylate, cyclohexyl methacrylate, 2-ethylhexyl acrylate, 2-ethylhexyl methacrylate, and the like.
次に上述のようにして得られた重合体を以下に述べる方
法(イ)〜(ニ)により反応させ、ラジカル重合性不飽
和基を導入することによって、紫外線もしくは電子線硬
化樹脂が得られる。Next, the polymer obtained as described above is reacted by methods (a) to (d) described below to introduce a radically polymerizable unsaturated group, thereby obtaining an ultraviolet ray or electron beam curable resin.
(イ) 水酸基を有する単量体の重合体または共重合体
の場合には、アクリル酸、メタクリル酸などのカルボキ
シル基を有する単量体などを縮合反応させる。(a) In the case of a polymer or copolymer of a monomer having a hydroxyl group, a monomer having a carboxyl group such as acrylic acid or methacrylic acid is subjected to a condensation reaction.
(ロ) カルボキシル基、スルフォン基を有する単量体
の重合体または共重合体の場合には、前述の水酸基を有
する単量体を縮合反応させる。(b) In the case of a polymer or copolymer of monomers having a carboxyl group or a sulfone group, the monomers having the aforementioned hydroxyl group are subjected to a condensation reaction.
(ハ) エポキシ基、イソシアネート基あるいはアジリ
ジニル基を有する単m体の重合体または共重合体の場合
には、前述の水l@i基を有する単量体もしくはカルボ
キシル基を有する単量体を付加反応させる。(c) In the case of a monomer polymer or copolymer having an epoxy group, an isocyanate group, or an aziridinyl group, the above-mentioned monomer having a water l@i group or a monomer having a carboxyl group is added. Make it react.
(ニ) 水酸基あるいはカルボキシル基を有する単量体
の重合体または共重合体の場合には、エポキシ基を有す
る単量体あるいはアジリジニル基を有する単量体あるい
はジインシアネート化合物と水III含有アクリル酸エ
ステル単量体の1対1モルの付加物を付加反応させても
良い。(d) In the case of a polymer or copolymer of a monomer having a hydroxyl group or a carboxyl group, a monomer having an epoxy group or a monomer having an aziridinyl group or a diincyanate compound and a water III-containing acrylic ester An addition reaction may be carried out using a 1:1 mole adduct of monomers.
またさらに、前述の単量体と、上記の熱成形性の紫外線
または電子線硬化樹脂とを混合して用いることもできる
。Furthermore, the above-mentioned monomer and the above-mentioned thermoformable ultraviolet ray or electron beam curable resin can be mixed and used.
また、上記のものは電子線により十分に硬化可能である
が、紫外線照射で硬化させる場合には、増感剤としてベ
ンゾキノン、ベンゾイン、ベンゾインメチルエーテル、
などのベンゾインエーテル類、ハロゲン化アセトフェノ
ン類、ビアセチル類などの紫外線照射によりラジカルを
発生するものも用いることができる。Furthermore, although the above materials can be sufficiently cured by electron beams, when curing by ultraviolet irradiation, benzoquinone, benzoin, benzoin methyl ether, benzoquinone, benzoin, benzoin methyl ether,
Those that generate radicals when irradiated with ultraviolet light, such as benzoin ethers, halogenated acetophenones, and biacetyls, can also be used.
艮肚i皇星1旦1
反射性金属薄膜層4は、ホログラム層5に反射性を与え
るためのものであって、Qr、Ti、Fe、Go、Ni
、CI、AQ、Au、Ge1Al、Mg、Sb、Pb、
Pd、Cd、8 i。The reflective metal thin film layer 4 is for imparting reflectivity to the hologram layer 5, and is made of Qr, Ti, Fe, Go, Ni.
, CI, AQ, Au, Ge1Al, Mg, Sb, Pb,
Pd, Cd, 8i.
5nSSe、In、Ga、Rhなどの金属およびその酸
化物、窒化物などを単独もしくは2s以上組合せて用い
て形成される。これらの金属のうちAI、CCrlN1
1A、Auなどが特に好ましい。It is formed using metals such as 5nSSe, In, Ga, Rh, and their oxides, nitrides, etc. alone or in combination for 2s or more. Among these metals, AI, CCrlN1
1A, Au, etc. are particularly preferred.
この反射性金属薄膜層4の膜層は、10〜10.000
人望ましくは200〜2000人であることが好ましい
。The thickness of this reflective metal thin film layer 4 is 10 to 10,000.
The number of people is preferably 200 to 2000 people.
この反射性金RWIrmm4は必ずしもなくてもよい場
合があるが、存在することが好ましい。Although this reflective gold RWIrmm4 may not necessarily be present, it is preferable that it be present.
11亙1
接着剤層3は、ホログラム層5および反射性金1Eal
l!!4を時計文字板基材2上に接着させる役割を果し
ている。接着剤層としては、アクリル系樹脂、ビニル系
樹脂、ポリエステル系樹脂、ウレタン系樹脂、アミド系
樹脂、エポキシ系樹脂などの従来接着剤層として既知の
ものが広く使用できる。この接着剤層の膜厚は、0.1
〜50μm。11-1 Adhesive layer 3 includes hologram layer 5 and reflective gold 1Eal
l! ! 4 onto the watch dial base material 2. As the adhesive layer, a wide variety of conventional adhesive layers such as acrylic resin, vinyl resin, polyester resin, urethane resin, amide resin, and epoxy resin can be used. The thickness of this adhesive layer is 0.1
~50μm.
望ま・しくは0.5〜10μmであることが好ましい。The thickness is desirably 0.5 to 10 μm.
なお、前記反射性台RN膜層4と接着剤層3との間には
、両者の接着性を高めるためにアンカ一層(図示せず)
を設けることもできる。Note that an anchor layer (not shown) is provided between the reflective stand RN film layer 4 and the adhesive layer 3 in order to improve the adhesion between the two.
It is also possible to provide
製造方法
次に、本発明に係るホログラム付き時計文字板の製造方
法について説明する。Manufacturing Method Next, a method for manufacturing the hologram-equipped timepiece dial according to the present invention will be described.
時計文字板基材にホログラムを設ける方法としては、接
着、粘着、W1着などの適宜な公知の貼着手段が用いら
れ得る他、転写法が好ましく用いられる。As a method for providing the hologram on the watch dial base material, any suitable known attachment means such as adhesion, adhesion, and W1 attachment may be used, and a transfer method is preferably used.
以下、この転写法によって第1図に示す時計文字板を製
造する場合の例について説明する。An example of manufacturing the timepiece dial shown in FIG. 1 using this transfer method will be described below.
まず、ホログラム付き時計文字板を製造するに先立って
、第4図に示すようなホログラム転写シート6を作成す
る。このホログラム転写シート6を作成するには、まず
ホログラム転写シート基材7上に、必要に応じて剥11
層8およびオーバープリント層9を介して、熱成形性を
有する紫外線または電子線硬化樹脂5あるいは熱成形性
を有する熱硬化樹脂5を設けて、ホログラム形成用フィ
ルムを形成する。上記樹脂のうち、特に硬化前に常温で
固体であり熱成形性を有する紫外線または電子線硬化樹
脂が好ましい。First, before manufacturing a hologram-equipped watch dial, a hologram transfer sheet 6 as shown in FIG. 4 is created. In order to create this hologram transfer sheet 6, first, a peeling film 11 is placed on the hologram transfer sheet base material 7 as needed.
A thermoformable ultraviolet or electron beam curing resin 5 or a thermoformable thermosetting resin 5 is provided via the layer 8 and the overprint layer 9 to form a hologram forming film. Among the above-mentioned resins, particularly preferred are ultraviolet or electron beam-curable resins that are solid at room temperature before curing and have thermoformability.
次いで、得られたホログラム形成用フィルムと凹凸模様
が形成されたホログラム原版とを、該フィルムの樹脂層
がホログラム原版に接するようにして加熱圧接させ前記
樹脂表面に凹凸模様を形成しつつ、またはその後紫外線
または電子線を照射するか熱をさらに加えて前記樹脂を
硬化させモる。Next, the obtained hologram forming film and the hologram original plate on which the uneven pattern has been formed are heated and pressed so that the resin layer of the film is in contact with the hologram original plate, while forming the uneven pattern on the resin surface, or after that. The resin is cured by irradiation with ultraviolet rays or electron beams, or by further applying heat.
ホログラム原版とホログラム形成用フィルムとを加熱圧
接するに際しては、加熱ロールなどの加熱圧接手段を用
いることができ、この際加熱ロールの温度は、用いられ
るべき樹脂の種類ベースフィルムの材料、厚みなどによ
って大きく変化するが、一般的には、100〜200℃
であることが適当である。また、ホログラム原版とホロ
グラム形成用フィルムとは0.18g/ci以上、望ま
しくは1 Kg / ci以上の圧力下に圧接すること
が好ましい。When heat-pressing the hologram original plate and the hologram-forming film, a heat-pressing means such as a heating roll can be used, and the temperature of the heating roll depends on the type of resin to be used, the material of the base film, the thickness, etc. Although it varies greatly, generally 100-200℃
It is appropriate that Further, it is preferable that the hologram original plate and the hologram forming film are pressed together under a pressure of 0.18 g/ci or more, preferably 1 Kg/ci or more.
この際に、紫外線または電子線を照射しても良い。また
ホログラム原版のホログラムの凹凸を成形したフィルム
を版より剥離した後に再度照射しでも良く、照射強度は
樹脂を十分に硬化させることが好ましい。紫外線、電子
線の照射は、使用する樹脂に応じて適宜法めることが必
要である。At this time, ultraviolet rays or electron beams may be irradiated. Further, the irradiation may be performed again after the film formed with the hologram irregularities of the hologram original plate is peeled from the plate, and the irradiation intensity is preferably set to sufficiently harden the resin. Irradiation with ultraviolet rays and electron beams needs to be controlled appropriately depending on the resin used.
次に、反射性金属薄膜層4を被着させる。この反射性金
属薄膜層は、スパッタリング法、イオンブレーティング
法、真空蒸着法などによってホログラム原版に設けるこ
とができる。Next, a reflective metal thin film layer 4 is applied. This reflective metal thin film layer can be provided on the hologram master by a sputtering method, an ion blating method, a vacuum evaporation method, or the like.
次いで、この反射性金属薄膜層4上に、必要に応じてア
ンカ一層を設けた後に、接着剤層3を塗 ”布法
などにより設けると、ホログラム転写シートが得られる
。Next, if necessary, an anchor layer is provided on this reflective metal thin film layer 4, and then an adhesive layer 3 is provided by a coating method or the like to obtain a hologram transfer sheet.
なお、従来用いられてきた種類の紫外線硬化樹脂および
電子線硬化樹脂は、一般に液体状態であるため、基材フ
ィルム上に塗布した場合に著しくべたつき、したがって
基材フィルム上に従来の紫外線または電子線硬化樹脂を
塗布してなるホログラム形成用フィルムは巻取って保管
することができず、ホログラム原版と接触する直前に基
材フィルム上にいちいち紫外線硬化樹脂を塗布してホロ
グラム形成用フィルムを形成しなければならないという
問題点があったが、上記のようなホログラム形成用フィ
ルムは、特定の樹脂により形成されているため、べとつ
くことがなく、巻取って保管することができるという利
点を有している。It should be noted that the types of ultraviolet curable resins and electron beam curable resins that have been used conventionally are generally in a liquid state and are extremely sticky when applied onto a base film. A hologram-forming film coated with a cured resin cannot be rolled up and stored, and a hologram-forming film must be formed by coating the base film with UV-curable resin one by one immediately before contacting the hologram master. However, since the above-mentioned hologram-forming film is made of a specific resin, it does not become sticky and has the advantage of being able to be rolled up and stored. .
次に上記のような構成を有するホログラム転写シート6
と時計文字板基材2とを、ホログラム転写シートの接着
剤層3と時計文字板基材とが接するようにして加熱圧接
すると、ホログラム転写シートのホログラム層5および
反射性金属薄膜層4が時計文字板基材2上に転写されて
、本発明に係るホログラム付き時計文字板が得られる。Next, a hologram transfer sheet 6 having the above configuration
and the watch dial base material 2 are heat-pressed so that the adhesive layer 3 of the hologram transfer sheet and the watch dial base material are in contact with each other, the hologram layer 5 and the reflective metal thin film layer 4 of the hologram transfer sheet are bonded to the watch dial base material 2. It is transferred onto the dial base material 2 to obtain a hologram-equipped watch dial according to the present invention.
ホログラム転写シート6と時計文字板基材2とは、10
0〜200℃の温度で5〜50にび/cdの圧力下で加
熱圧接されることが好ましい。The hologram transfer sheet 6 and the clock dial base material 2 are 10
It is preferable to carry out heat-pressure welding at a temperature of 0 to 200°C and a pressure of 5 to 50 m/cd.
本発明に係る時計文字板は、その表面にホログラムが設
けられているので、以下のような効果が得られる。Since the timepiece dial plate according to the present invention has a hologram on its surface, the following effects can be obtained.
(イ) 文字板に立体的な視感が生じ、審美性、装飾性
が一層向上する。(b) A three-dimensional visual appearance is created on the dial, further improving aesthetics and decorativeness.
(ロ) 耐熱性にすぐれたホログラム層を設けるように
したので、ホログラム貼着時に熱をかけ 。(b) Since a hologram layer with excellent heat resistance is provided, heat is not applied when pasting the hologram.
て形成することができる。It can be formed by
(ハ) 表面硬度が高く、傷つきにくい時計文字板が得
られる。(c) A watch dial with high surface hardness and scratch resistance can be obtained.
第1図〜第3図は、本発明に係るホログラム付き時計文
字板の断面図であり、第4図は本発明の時計文字板を製
造するに際して用いられるホログ □ラム転写シ
ートの断面図である。
1・・・ホログラム付き時計文字板、2・・・時計文字
板基材、3・・・接着剤層、4・・・反射性金属薄膜層
、5・・・ホログラム層、6・・・ホログラム転写シー
ト、7・・・ホログラム転写シート基材、8・・・剥離
層、9・・・オーバープリント層、10・・・反射性金
属層。
出願人代理人 佐 藤 −雄
色2 図
工
色3 口Figures 1 to 3 are cross-sectional views of a watch dial with a hologram according to the present invention, and Figure 4 is a cross-sectional view of a hologram transfer sheet used in manufacturing the watch dial of the present invention. . DESCRIPTION OF SYMBOLS 1... Watch dial with hologram, 2... Watch dial base material, 3... Adhesive layer, 4... Reflective metal thin film layer, 5... Hologram layer, 6... Hologram Transfer sheet, 7... Hologram transfer sheet base material, 8... Peeling layer, 9... Overprint layer, 10... Reflective metal layer. Applicant's agent Sato - Osiro 2 Zukoiro 3 Kuchi
Claims (1)
ムが設けられていることを特徴とする、ホログラム付時
計文字板。 2、前記ホログラムが、熱成形性を有する紫外線硬化樹
脂、電子線硬化樹脂または熱硬化樹脂を用いて形成され
た、特許請求の範囲第1項に記載の時計文字板。 3、前記紫外線硬化樹脂、電子線硬化樹脂または熱硬化
樹脂は、硬化前の状態が常温で固体であり、熱成形性を
有するものである、特許請求の範囲第2項に記載の時計
文字板。[Scope of Claims] 1. A timepiece dial plate with a hologram, characterized in that a hologram is provided on a part or the entire surface of a watch dial base material. 2. The clock dial according to claim 1, wherein the hologram is formed using an ultraviolet curable resin, an electron beam curable resin, or a thermosetting resin that has thermoformability. 3. The watch dial according to claim 2, wherein the ultraviolet curable resin, electron beam curable resin, or thermosetting resin is solid at room temperature before curing and has thermoformability. .