JPS6170701A - Multipolar resin magnet - Google Patents
Multipolar resin magnetInfo
- Publication number
- JPS6170701A JPS6170701A JP19183084A JP19183084A JPS6170701A JP S6170701 A JPS6170701 A JP S6170701A JP 19183084 A JP19183084 A JP 19183084A JP 19183084 A JP19183084 A JP 19183084A JP S6170701 A JPS6170701 A JP S6170701A
- Authority
- JP
- Japan
- Prior art keywords
- magnet
- resin magnet
- resin
- multipolar
- fixed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
〔産業上の利用分野〕
本発明は円筒状の多極性磁石として用いうる樹脂磁石構
成体に関するものである。DETAILED DESCRIPTION OF THE INVENTION [Field of Industrial Application] The present invention relates to a resin magnet structure that can be used as a cylindrical multipolar magnet.
円筒状の多極性磁石は、自転車、オートバイ等の小型発
電機のローターとして、あるいは複写機の静電現像用ロ
ール等に使用されている。Cylindrical multipolar magnets are used as rotors in small generators for bicycles, motorcycles, etc., or in electrostatic developing rolls in copying machines.
従来、このような用途−には円筒状の多極性磁石は焼結
磁石極のものが用いられていたが、近年加工性が良好で
あることあるいは軽量であることなどの理由から樹脂に
磁性粉末を添加したいわゆる樹脂磁石性のものが開発さ
れるに到っている。Traditionally, cylindrical multipolar magnets with sintered magnetic poles were used for such applications, but in recent years magnetic powder has been used in resin for reasons such as good processability and light weight. So-called resin magnets have been developed.
ところで、この樹脂磁石製の円筒状多極性磁石としては
、（ｌ）樹脂磁石材料を円筒状に成形すると同時に多極
着磁したもの（例えば、特開昭５７−１３０４０７号公
報） 、（２）断面が扇状の樹脂磁石ネ。By the way, this cylindrical multipolar magnet made of a resin magnet includes (l) one in which a resin magnet material is molded into a cylindrical shape and simultaneously multipolar magnetized (e.g., Japanese Patent Application Laid-Open No. 130407/1982); (2) A resin magnet with a fan-shaped cross section.
をシャフト軸に貼合せたもの、（３）シートの樹脂磁石
をシャフト軸に巻き付け、必要極数になるように切り欠
いたもの、あるいは（４）板状樹脂磁石をシャフト軸に
取りつけたアルミブロック又は樹脂成形物に固定したも
のなどが知られている。(3) a sheet of resin magnet wrapped around the shaft and cut out to the required number of poles, or (4) an aluminum block with a plate-shaped resin magnet attached to the shaft. Or, those fixed to resin moldings are known.
（１）〜（３）のものでは、円筒状磁石が全て樹脂磁石
であるため、樹脂磁石とはいえ全体が重くなってしまう
という欠点がある。更に（１）のものにおいては製造時
に多極着磁せねばならず、また、製造後のひけがあるた
め仕上げ加工が不可欠であるという問題もある。（３）
のちのではシート状融石金切り欠いているため、磁力が
弱く、かつ、強い磁力の必要を強く着磁できないという
欠点がある。In the case of (1) to (3), all the cylindrical magnets are resin magnets, so there is a drawback that the whole is heavy even though it is a resin magnet. Furthermore, in the case of (1), multi-pole magnetization must be performed during manufacturing, and there is also a problem that finishing is essential due to the presence of sink marks after manufacturing. (3)
Later, because the sheet-shaped molten metal was notched, the magnetic force was weak, and the disadvantage was that it could not be strongly magnetized even though a strong magnetic force was required.
（４）のものでは、磁石部分が（１）〜（３）に比べ小
さくて良好であり、かつ、各々磁極の強さを変えること
ができ好ましいのであるが、板状の樹脂磁石はシャフト
軸に取りつけたアルミブロックあるいは樹脂成形体に全
体が保持されるべく固定されており、ｍｒ：ｉとしては
（１）〜（３）とあまり変らない結果となりでいる。In (4), the magnet part is smaller than in (1) to (3), which is preferable, and the strength of each magnetic pole can be changed, but the plate-shaped resin magnet is suitable for the shaft axis. The entire structure is fixed to an aluminum block or a resin molded body attached to the frame, and the mr:i results are not much different from (1) to (3).
即ち、従来の円筒状多極性樹脂磁石として軽量で充分な
性能を有したものがないのが実情である。That is, the reality is that there is no conventional cylindrical multipolar resin magnet that is lightweight and has sufficient performance.
本発明の目的は、軽量で充分な性能を有した円筒状樹脂
磁石を提供することにある。An object of the present invention is to provide a cylindrical resin magnet that is lightweight and has sufficient performance.
本発明者らは、上記目的を達成するため鋭意検討し、板
状樹脂磁石を用い、その固定材料として特定の構造を有
したものを用いるならば、良好な結果が得られることを
見出し、遂に本発明を完成するに到った。In order to achieve the above object, the present inventors made extensive studies and found that good results could be obtained by using a plate-shaped resin magnet and a material with a specific structure as its fixing material. The present invention has now been completed.
即ち、本発明は板状の樹脂磁石の少なくとも両端部をシ
ャフトに固定された該樹脂磁石を固定できる構造を有し
た支持部品に固定してなることを特徴とする多極性樹脂
磁石である。That is, the present invention is a multipolar resin magnet characterized in that at least both ends of a plate-shaped resin magnet are fixed to a support component having a structure capable of fixing the resin magnet fixed to a shaft.
本発明の板状樹脂磁石は通常、異方性樹脂磁石成型物で
あり、磁場配向射出成型、磁場配向押し出し成型又は、
磁場配向圧縮成形により樹脂磁石材料を用いて成型する
ことが出来る。The plate-shaped resin magnet of the present invention is usually an anisotropic resin magnet molded product, and is formed by magnetic field oriented injection molding, magnetic field oriented extrusion molding, or
It can be molded using a resin magnet material by magnetic field oriented compression molding.
本発明に用いられる樹脂磁石材料は、磁性体粉末を樹脂
で結合させたものである。The resin magnet material used in the present invention is made by bonding magnetic powder with resin.
磁性体粉末としては、代表的なものとしてバリウム・７
エライト、ストロンチウム・フェライト）サマリウム・
コバルト、その他の磁石合金等が用いられる。A typical example of magnetic powder is barium 7.
elite, strontium ferrite) samarium
Cobalt, other magnetic alloys, etc. are used.
又、代表的な樹脂としては、ナイロン、ポリプロピレン
、ポリ塩化ビニール、塩素化ポリエチレンの他、合成ゴ
ム等の熱可塑性樹脂又は、エポキシ等の熱硬化性樹脂が
用いられる。Typical resins include nylon, polypropylene, polyvinyl chloride, chlorinated polyethylene, thermoplastic resins such as synthetic rubber, and thermosetting resins such as epoxy.
支持部品としては、射出成型により製造した樹脂部品又
は、鍛造により製造した金属部品が用いられる。樹脂部
品°としては、ナイロン、ポリカーボネー）、ＡＢＳ、
ポリエーテル樹脂が用いられる。樹脂磁石の重量が大き
い場合又は、回転速度等の使用条件により、部品として
温性が必要な場合には、ガラス・７アイバー入りの樹脂
を用いる。As the support component, a resin component manufactured by injection molding or a metal component manufactured by forging is used. Resin parts include nylon, polycarbonate), ABS,
Polyether resin is used. When the weight of the resin magnet is large, or when the component needs to be warm due to operating conditions such as rotation speed, a resin containing glass and 7-eye bars is used.
支持部品として特に寸法精度が要求される場合には、ア
ルミニウム、亜鉛、真ちゅう等の鍛造部品を用いる。シ
ャフトとしては、鉄、ステンレス、アルミ等の金属が一
般的に用いられる。If dimensional accuracy is particularly required for the supporting parts, forged parts of aluminum, zinc, brass, etc. are used. Metals such as iron, stainless steel, and aluminum are generally used for the shaft.
板状樹脂磁石と支持部品、支持部品とシャフトの固定に
は通常、接着剤又は、熱融着が用いられる。もちろんは
め込み式のものであってもかまわない。樹脂磁石を強力
に接着させるものとしては、エポキシ系又は、アクリル
系の接着剤が用いられる０
本発明の多極性樹脂磁石の一般的な製造方法は、次の如
くである。Adhesive or heat fusion is usually used to fix the plate-shaped resin magnet and the support component, and the support component and the shaft. Of course, it may be a built-in type. Epoxy or acrylic adhesives are used to strongly adhere the resin magnets. A general method for manufacturing the multipolar resin magnet of the present invention is as follows.
磁場配向により製造した板状の樹脂磁石を脱磁する。予
め、シャフトに固定した支持部品に板状の樹脂磁石を固
着する。多極に着磁させる為には、単一の着磁ヨークを
用いて順次各欄に必要な磁束密度を着磁させるか、又は
円筒状の着磁ヨークを用いて各欄に必要な磁束密度に着
磁させる。各欄の磁束密度が異なる場合には、各欄の着
磁条件を変えることにより多極をつくるか、又は板状の
樹脂磁石の材料を選択することにより、同じ着磁条件で
も各欄の磁束密度を変えることができる。A plate-shaped resin magnet manufactured by magnetic field orientation is demagnetized. In advance, a plate-shaped resin magnet is fixed to a support component fixed to the shaft. To magnetize multiple poles, use a single magnetizing yoke to sequentially magnetize each column to the required magnetic flux density, or use a cylindrical magnetizing yoke to magnetize each column to the required magnetic flux density. magnetize it. If the magnetic flux density of each column is different, you can create multiple poles by changing the magnetization conditions of each column, or by selecting the material of the plate-shaped resin magnet, the magnetic flux density of each column can be changed even under the same magnetization conditions. Density can be changed.
以下、図面により本発明を説明する。The present invention will be explained below with reference to the drawings.
第１図は４極の磁石の正面図であり、第２図はその側面
図である。板状樹脂磁石１〜４はシャフト軸５両端ちか
くに取りつけられた支持部品６゜７により固定されてい
る。FIG. 1 is a front view of a four-pole magnet, and FIG. 2 is a side view thereof. The plate-shaped resin magnets 1 to 4 are fixed by support parts 6.about.7 attached to both ends of the shaft shaft 5.
板状樹脂磁石が大きくて、両端の固定だけで不足する場
合は、支持部品を増やして固定すればよい。If the plate-shaped resin magnet is large and it is insufficient to fix both ends, it is sufficient to increase the number of supporting parts and fix it.
また、更に極数が多く必要な場合は、例えば６極のもの
では第３図に示すように、支持部品の切欠きを必要な数
にしたものを用いその部分に板状樹脂磁石９〜１４を固
定する。If an even larger number of poles is required, for example, in the case of a 6-pole type, as shown in Figure 3, the supporting part should have the necessary number of notches, and plate-shaped resin magnets 9 to 14 should be placed in that part. to be fixed.
なお、固定された板状磁石はＮ極とＳ極が交互になるよ
うに着磁されている。Note that the fixed plate-shaped magnet is magnetized so that north poles and south poles alternate.
以下、実施例により本発明を説明する。 The present invention will be explained below with reference to Examples.
実施例１
スートロンチウム・フェライト８９重皿％であるフェラ
イト−ナイロンのコンパウンドを磁場配向射出成形機に
より、厚み４ ｍ 、高さ１２闘、巾３００ｊｕｌ＋で
、かつ、一方の頂部に半径１９謁のＲをつけた板状樹脂
磁石を得た。Example 1 A ferrite-nylon compound containing 89% sootrontium ferrite was molded using a magnetically oriented injection molding machine to form a mold with a thickness of 4 m, a height of 12 mm, a width of 300 mm, and a radius of 19 mm on one top. A plate-shaped resin magnet with R attached thereto was obtained.
一方、ＡＢＳ樹脂を用い、直径２４ｍＩＩ、厚み３闘で
、シャフト軸はめ込み部穴直径８日および板状樹脂磁石
はめ込み部（巾４鰭×深さ５闘の切欠、４ケ所）を有す
る支持部品を射出成形により製造した。On the other hand, the support part is made of ABS resin, has a diameter of 24 mII, a thickness of 3 mm, a hole diameter of 8 mm for the shaft fitting part, and a plate-shaped resin magnet fitting part (4 fins wide x 5 deep notches, 4 places). Manufactured by injection molding.
ステンレス製のシャフト（径８ＩＩＩｓ）に支持部品を
２個取りつけ、その支持部品に脱磁した板状樹脂磁石４
個を接着固定した。なお、接着にはエポキシ系接着剤を
用いた。このものを４極の着磁ヨークを用いて着磁し、
多極の磁束密度１２００Ｇの４極樹脂磁石を得た。Two supporting parts are attached to a stainless steel shaft (diameter 8IIIs), and a demagnetized plate-shaped resin magnet 4 is attached to the supporting parts.
The pieces were glued and fixed. Note that epoxy adhesive was used for bonding. This is magnetized using a 4-pole magnetizing yoke,
A four-pole resin magnet with a multipolar magnetic flux density of 1200G was obtained.
此のようにして製造した４極の樹脂磁石は、非磁性のス
リーブ内に入れて複写機専用マグネ、トロールとして使
用され、径３８龍、長さ３００鱈の４極の円筒状樹脂磁
石部品と同じ性能を示した。The 4-pole resin magnet manufactured in this way is placed in a non-magnetic sleeve and used as a special magnet for copying machines and as a trolley, and is used as a 4-pole cylindrical resin magnet component with a diameter of 38 mm and a length of 300 mm. showed the same performance.
本磁石の樹脂磁石自体の重量は２１３りであり、もし円
筒状にすれば、樹脂磁石の重量は１２００ｇとなるので
、大幅に軽量化されている。The weight of the resin magnet itself of this magnet is 213 g, and if it were made into a cylindrical shape, the weight of the resin magnet would be 1200 g, which is a significant reduction in weight.
実施例２
板状の樹脂磁石として、５つはストロンチウム・フェラ
イト８７重量％であるものを用い、もう１つは実施例１
と同じものを用い、実施例１と同様にして６極の樹脂磁
石を製造した。Example 2 As plate-shaped resin magnets, five were made of 87% by weight of strontium ferrite, and the other was made of Example 1.
A six-pole resin magnet was manufactured in the same manner as in Example 1 using the same material.
なお、６極の着磁ヨークにより着磁したのであるが、１
つが１２００Ｇとなり、他は９００Ｇとなった０
此のようにして製造した６極の樹脂磁石は、非磁性のス
リーブ内に入れて複写機用マグネットロールとして使用
され、径３８鱈、長さ３００謔の６極の円筒状焼結磁石
と同じ性能を示した。本磁石部品の樹脂磁石の重量は３
２０９であるが円筒状焼結磁石は１６００ｇであるので
、著しく軽量化される。In addition, although magnetization was performed using a six-pole magnetizing yoke, 1
The 6-pole resin magnet manufactured in this way was placed in a non-magnetic sleeve and used as a magnet roll for a copying machine, with a diameter of 38 mm and a length of 300 g. It showed the same performance as a six-pole cylindrical sintered magnet. The weight of the resin magnet of this magnet part is 3
209, but the cylindrical sintered magnet weighs 1600 g, so it is significantly lighter.
本発明の樹脂磁石は、きわめて軽重量であるにもかかわ
らず、従来の円筒状多極磁石と同様に用いうるものであ
る。Although the resin magnet of the present invention is extremely light in weight, it can be used in the same manner as conventional cylindrical multipolar magnets.
また、各磁極の強さは、磁性材料あるいはその使用量を
かえたり、板状にした樹脂磁石の大きさを変えることに
より変えられるというメリットもある。Another advantage is that the strength of each magnetic pole can be changed by changing the magnetic material or the amount used, or by changing the size of the plate-shaped resin magnet.
更に、寸法精度が従来のものに比べ格段に良好である。Furthermore, the dimensional accuracy is much better than conventional ones.
第１図は本発明の１実施例である４極のものの正面図で
あり、第２図は同じく側面図である。また第３図は他の
実施例（６極のもの）の側面図である。
図において、１〜４，９〜１４は板状樹脂磁石、５はシ
ャフト軸、６〜８は支持部品である。また、Ｎ１〜Ｎ３
はＮ極を、８１〜Ｓ３はＳ極を示す。
特許出願人 三井東圧化学株式会社
第１図
第２図 第３図FIG. 1 is a front view of a four-pole device according to an embodiment of the present invention, and FIG. 2 is a side view of the same. FIG. 3 is a side view of another embodiment (six poles). In the figure, numerals 1 to 4 and 9 to 14 are plate-shaped resin magnets, 5 is a shaft axis, and 6 to 8 are supporting parts. Also, N1 to N3
indicates the north pole, and 81 to S3 indicate the south pole. Patent applicant Mitsui Toatsu Chemical Co., Ltd. Figure 1 Figure 2 Figure 3
Claims (1)
定された該樹脂磁石を固定できる構造を有した支持部品
に固定してなることを特徴とする多極性樹脂磁石1) A multipolar resin magnet, characterized in that at least both ends of a plate-shaped resin magnet are fixed to a support component having a structure capable of fixing the resin magnet fixed to a shaft.