JPS6159645A - Air sandwich type information recording medium - Google Patents
Air sandwich type information recording mediumInfo
- Publication number
- JPS6159645A JPS6159645A JP59182013A JP18201384A JPS6159645A JP S6159645 A JPS6159645 A JP S6159645A JP 59182013 A JP59182013 A JP 59182013A JP 18201384 A JP18201384 A JP 18201384A JP S6159645 A JPS6159645 A JP S6159645A
- Authority
- JP
- Japan
- Prior art keywords
- layer
- recording medium
- information recording
- spacer
- adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
［発明の分野］
本発明は、エアーサンドイッチ構造を有する情報記録媒
体に関するものであり、さらに詳しくは未発明は、高エ
ネルギー密度のレーザービームを用いて情報の口き込み
および／または読み取りができるエアーサンドイッチ型
情報記録媒体に関するものである。DETAILED DESCRIPTION OF THE INVENTION [Field of the Invention] The present invention relates to an information recording medium having an air sandwich structure. and/or an air sandwich type information recording medium that can be read.
［９：：明の技術的ず〒景］
近年において、レーザー光等の高エネルギー密度のビー
ムを用いる情報記録媒体が開発され、実用化されている
。この情報記録媒体は光ディスクと称され、ビデオ−デ
ィスク、オーディオ・ディスク、さらには大容量静止画
像ファイルおよび大容量コンピュータ用ディスク・メモ
リーとして使用されうるちのである。[9::Technological overview of the Ming Dynasty] In recent years, information recording media that use high energy density beams such as laser light have been developed and put into practical use. This information recording medium is called an optical disk, and can be used as a video disk, an audio disk, and also as a large-capacity still image file and a large-capacity computer disk memory.
光ディスクは、基本構造としてプラスチック。The basic structure of optical discs is plastic.
ガラス等からなる円盤状の透明基板と、この上に設けら
れたＢｉ、Ｓｎ、Ｉｎ、Ｔｅ等の金属または半金属から
なる記録層とを有する。なお、記録層が設けられる側の
基板表面には通常、基板の平面性の改善、記録層との接
着力の向上あるいは光ディスクの感度の向上などの点か
ら、高分子物質からなる下塗層または中間層が設けられ
ている。It has a disk-shaped transparent substrate made of glass or the like, and a recording layer made of metal or semimetal such as Bi, Sn, In, Te, etc. provided thereon. Note that the surface of the substrate on which the recording layer is provided is usually coated with an undercoat layer or an undercoat layer made of a polymeric material in order to improve the flatness of the substrate, improve the adhesion with the recording layer, or improve the sensitivity of the optical disc. An intermediate layer is provided.
光ディスクへの情報の書き込みは、たとえばレーザービ
ームをこの光ディスクに照射することにより行なわれ、
記録層の照射部分がその光を吸収して局所的に温度上昇
する結果、物理的あるいは化学的な変化を生じてその光
学的特性を変えることにより情報が記録される。光ディ
スクからの情報の読み取りもまた。レーザービームを光
ディスクに照射することにより行なわれ、記録層の光学
的特性の変化に応じた反射光または透過光を検出するこ
とにより情報が再生される。Information is written on an optical disk by, for example, irradiating the optical disk with a laser beam.
The irradiated portion of the recording layer absorbs the light and locally increases in temperature, resulting in a physical or chemical change that changes its optical properties, thereby recording information. Also reading information from optical discs. This is performed by irradiating an optical disk with a laser beam, and information is reproduced by detecting reflected or transmitted light that corresponds to changes in the optical characteristics of the recording layer.
最近、記録層を保護するためのディスク構造として、二
枚の円盤状基板のうちの少なくとも一枚の基板上に記録
層を設け、この二枚の基板を記録層が内側に位置し、か
つ空間を形成するようにリング状内側スペーサとリング
状外側スペーサとを介して接合してなるエアーサンドイ
ンチ構造が提案されている。このような構造を有する光
ディスクでは、記録層は直接外気に接することがなく、
情報の記録、再生は基板を透過するレーザ光で行なわれ
るために、一般に記録層が物理的または化学的な損傷を
受けたり、あるいはその表面に塵埃が竹刀して情報の記
録、再生の障害となることがない。Recently, as a disk structure for protecting the recording layer, a recording layer is provided on at least one of the two disk-shaped substrates, and the recording layer is located on the inside of the two substrates, and a space is An air sandwich structure has been proposed in which a ring-shaped inner spacer and a ring-shaped outer spacer are joined together to form a ring-shaped inner spacer and a ring-shaped outer spacer. In an optical disc with such a structure, the recording layer does not come into direct contact with the outside air,
Because information is recorded and reproduced using laser light that passes through the substrate, it is common for the recording layer to be physically or chemically damaged, or for dust to accumulate on its surface, which may impede information recording or reproduction. It never becomes.
光ディスクの基板としては、上述のように強化ガラス等
のガラス基板を使用することが知られている。ガラス基
板は、アクリル樹脂等のプラスチック基板と比べてディ
スクを回転させた時のバラツキの程度が小さい、表面硬
度が大きい、および形状の経時安定性が高いなどの点で
優れている。As described above, it is known to use a glass substrate such as tempered glass as a substrate for an optical disc. Glass substrates are superior to plastic substrates such as acrylic resin in that the degree of variation when rotating the disk is small, the surface hardness is high, and the shape is highly stable over time.
このガラス基板を使用する場合には感度など記録特性の
点から、特に下塗層を設けることが望まれテ１．％る。When using this glass substrate, it is particularly desirable to provide an undercoat layer from the viewpoint of recording characteristics such as sensitivity.Te1. %ru.
ガラス基板中のＮａ”、Ｋ＋、Ｃａ２＋などのアルカリ
イオンが基板表面に拡散してその上に設けられた記録層
が変質しやすいために、これらアルカリイオンの拡散を
防止する目的で、たとえば基板表面に親水性基を有する
ポリマーからなる下塗層を設けることが提案されている
（本出願人による特願昭５８−１７３６７６号）、また
、基板と記録層との間には所望の光ディスクの特性に応
じて平面性の改善、基板と記録層との接着力の改善、断
熱効果等による感度の向上などの目的で、断熱層、反射
層など各種の下塗層または中間層を設けることが行なわ
れている。Alkali ions such as Na'', K+, and Ca2+ in the glass substrate diffuse onto the substrate surface and easily deteriorate the recording layer provided thereon. Therefore, in order to prevent the diffusion of these alkali ions, for example, It has been proposed to provide an undercoat layer made of a polymer having a hydrophilic group on the substrate (Japanese Patent Application No. 173676/1989 filed by the present applicant). Depending on the situation, various undercoat layers or intermediate layers such as heat insulating layers and reflective layers are provided for the purpose of improving flatness, improving the adhesion between the substrate and the recording layer, and increasing sensitivity due to heat insulating effects. It is.
これらの下塗層および中間層は、たとえば特開昭５７−
１７２５３７号公報に開示されているように、通常は塗
布液をスピンナー等を用いて塗布することにより基板上
に形成される。従って、下塗層および中間層は基板表面
全体に一様に塗布形成されている。しかしながら、下塗
層および中間層の材料として用いられる有機物質および
無機物質の中には、ガラス基板、あるいは放射線硬化性
接着剤、エポキシ系接着剤等の接着剤とのＶ、若力が低
いものがあり、接着剤を用いて二枚の基板をスペーサを
介して接合されたエアーサンドイッチ構造の光ディスク
が満足できる接着力を有するためには、下塗層および中
間層の材料が限定されるという問題があった。These undercoat layers and intermediate layers are, for example,
As disclosed in Japanese Patent No. 172537, it is usually formed on a substrate by applying a coating liquid using a spinner or the like. Therefore, the undercoat layer and the intermediate layer are uniformly coated over the entire surface of the substrate. However, some of the organic and inorganic substances used as materials for the undercoat layer and intermediate layer have low V and youthfulness with glass substrates, or adhesives such as radiation-curable adhesives and epoxy adhesives. There is a problem in that in order for an optical disk with an air sandwich structure, in which two substrates are bonded via a spacer using an adhesive, to have a satisfactory adhesion force, the materials for the undercoat layer and the intermediate layer are limited. was there.
エアーサンドイッチ構造の密閉空間には通常は窒素ガス
等の不活性ガスが封入されて、この内部充填ガスと接す
る記録層の全屈が酸化などにより変質するのを防いでい
るが、光ディスクの接合部の接着力が弱い場合には時間
が経過するにつれて酸素、水蒸気などの外気が接合部か
ら密閉空間に侵入しやすいために、これら外気により記
ＱＨが変質して光吸収率、光反射率等の光学特性および
ピットの欠陥等の記録特性が低下する傾向にある。The sealed space of the air sandwich structure is usually filled with an inert gas such as nitrogen gas to prevent the recording layer in contact with the internal filling gas from being deteriorated due to oxidation, etc. If the adhesive strength of the QH is weak, as time passes, outside air such as oxygen and water vapor will easily enter the sealed space through the joint, and this outside air will change the quality of the QH, resulting in changes in light absorption rate, light reflectance, etc. Recording properties such as optical properties and pit defects tend to deteriorate.
［発明の要旨］
本発明は、ガラス基板とスペーサとの間の接着力が向上
したエアーサンドイッチ構造の情報記録媒体を提供する
ことをその目的とするものである。[Summary of the Invention] An object of the present invention is to provide an information recording medium with an air sandwich structure in which the adhesive strength between a glass substrate and a spacer is improved.
また１本発明は、上記接着力の向上とともに、記録特性
の経時による低下、特に感度の低下および読取り誤差の
増加を防止し、かつ光学特性の経時による低下を防止し
たエアーサンドイッチ構造の情報記録媒体を提供するこ
ともその目的とするものである。In addition, the present invention provides an information recording medium having an air sandwich structure that not only improves the adhesive strength but also prevents deterioration of recording characteristics over time, particularly a decrease in sensitivity and an increase in reading errors, and prevents deterioration of optical characteristics over time. Its purpose is also to provide.
上記の目的は、二枚の円盤状ガラス基板がリング状内側
スペーサとリング状外側スペーサとを介して接着剤によ
り接合され、かつ少なくともその一方の基板の内側表面
に下塗層および／または中間層を介してレーザーによる
情報の書き込みおよび／または読み取りが可能な記録層
が設けられてなるエアーサンドイッチ構造の情報記録媒
体において、該ガラス基板のスペーサと接合される部分
には下塗層、中１８１層および記録層が設けられていな
いことを特徴とする本発明の情報記録媒体による達成す
ることができる。The above object is to bond two disk-shaped glass substrates with an adhesive via a ring-shaped inner spacer and a ring-shaped outer spacer, and to coat the inner surface of at least one of the substrates with an undercoat layer and/or an intermediate layer. In an information recording medium having an air sandwich structure, which is provided with a recording layer on which information can be written and/or read by a laser via the glass substrate, a portion of the glass substrate to be bonded to the spacer is provided with an undercoat layer, a middle 181 layer. This can be achieved by the information recording medium of the present invention, which is characterized in that it is not provided with a recording layer.
［発明の構成］
本発明は、ガラス基板上に下塗層および／または中間層
を有するエアーサンドイッチ構造の情報記録媒体におい
て、ガラス基板のスペーサと接合される部分には下塗層
および中ＩＪＩ層を設けないで、基板とスペーサとを接
着剤を用いて直接に接着することにより、記録特性およ
び光学特性の向上を実現するものである。[Structure of the Invention] The present invention provides an information recording medium having an air sandwich structure having an undercoat layer and/or an intermediate layer on a glass substrate. By directly bonding the substrate and the spacer using an adhesive without providing a spacer, recording characteristics and optical characteristics can be improved.
エアーサンドイッチ構造の情報記録媒体は一般に、記録
層の設けられた二枚の円盤状ガラス基板をリング状内側
スペーサとリング状外側スペーサとを介して接着剤で接
合することにより製造される。記録媒体の基板と記録層
との間に下塗層、中間層など各種の層を設ける場合に、
これら各層は通常は塗布液をスピンナー等を用いて基板
上に塗布することにより形成され、基板の表面−面に均
一に塗布形成される。従って、従来においては基板とス
ペーサとの接合は必然的に下塗層、中１１１１ｆｆを介
して接着することにより行なわれていたが。An air sandwich structure information recording medium is generally manufactured by bonding two disc-shaped glass substrates provided with recording layers with an adhesive via a ring-shaped inner spacer and a ring-shaped outer spacer. When providing various layers such as an undercoat layer and an intermediate layer between the substrate of the recording medium and the recording layer,
Each of these layers is usually formed by applying a coating liquid onto the substrate using a spinner or the like, and is uniformly applied to the surface of the substrate. Therefore, in the past, the substrate and the spacer were necessarily bonded together through an undercoat layer, 1111ff.
本発明においては該下塗層、中間層を基板上に形成する
に際して基板の接合部分にはこれら各層を設けないで基
板表面を露出させておき、直接に基板とスペーサとを接
着剤で接着する。このようにすることにより、従来の下
塗層および／または中間層を介して接着した場合よりも
基板とスペーサとの接着力を顕著に高めることができる
。In the present invention, when forming the undercoat layer and the intermediate layer on the substrate, these layers are not provided at the joint portion of the substrate, the surface of the substrate is exposed, and the substrate and spacer are directly bonded with an adhesive. . By doing so, the adhesive strength between the substrate and the spacer can be significantly increased compared to the conventional case of adhesion via an undercoat layer and/or intermediate layer.
そして、この接着耐久性の向上によって、接合部から酸
素、水蒸気などの外気が侵入することにより生じる記ｊ
ａ層の変質劣化を防止することができる。従って、ガラ
ス基板の表面全体に下塗層および／または中間層を設け
た場合、すなわち下塗層および／または中ＩＩＩ Ｗを
介して基板とスペーサとを接合した場合よりも、感度お
よび読取り誤差などの記録特性および反射率などの光学
特性の経時による低下をｆｌ著に防ぐことができる。This improvement in adhesive durability also reduces the risk of damage caused by outside air such as oxygen and water vapor entering through the joint.
It is possible to prevent alteration and deterioration of the a-layer. Therefore, the sensitivity and reading error are lower than when the undercoat layer and/or the intermediate layer is provided on the entire surface of the glass substrate, that is, when the substrate and the spacer are bonded through the undercoat layer and/or the intermediate layer. Deterioration of optical properties such as recording properties and reflectance over time can be significantly prevented.
本発明の情報記録媒体は、第１図に示すような外成形状
を有し、たとえば第２図に示すような構成をとるもので
ある。すなわち、二枚の円盤状ガラス基板１ａ、ｌｂ上
にはそれぞれ下塗Ｗ ２ ａ、２ｂおよび記録層３ａ、
３ｂが設けられ１両基板１ａ、１ｂは直接に接着剤層４
ａ、４ｂを介してリング状外側スペーサ５およびリング
状内側スペーサ６を挟んで接合されている。The information recording medium of the present invention has an externally formed shape as shown in FIG. 1, and has a configuration as shown in FIG. 2, for example. That is, on the two disk-shaped glass substrates 1a and lb, the undercoat W 2 a and 2b and the recording layer 3a,
3b is provided, and both substrates 1a and 1b are directly connected to the adhesive layer 4.
They are joined with a ring-shaped outer spacer 5 and a ring-shaped inner spacer 6 interposed therebetween via a and 4b.
なお、第２図に示した情報記録媒体は本発明に従う記Ｑ
媒体の一構成例であり、本発明の記録媒体は上記の構成
に限定されるものではない。Note that the information recording medium shown in FIG.
This is one configuration example of a medium, and the recording medium of the present invention is not limited to the above configuration.
次に、本発明の情報記録媒体は、たとえば、以下のよう
な方法により製造することができる。Next, the information recording medium of the present invention can be manufactured, for example, by the following method.
本発明において使用する基板は、寸度安定性。The substrate used in the present invention has dimensional stability.
透ＩＪＩ性および平面性の点から、強化ガラス等に代表
されるガラスノ、（板である。From the point of view of transparency and flatness, glass sheets, such as tempered glass, are used.
記録層が設けられる側の表面には、平面性の改善、記録
層との接看力の向上、断熱効果による感度の向上および
記録層の変質の防止などの目的で、下塗層および／また
は中間層が設けられていてもよい、下塗層（または中間
層）の材料としては、たとえば、ポリメチルメタクリレ
ート、アクリル酸嗜メタクリル酸共重合体、スチレン・
無水マレイン酸共重合体、ポリビニルアルコール、Ｎ−
メチロールアクリルアミド、スチレン−スルホン酸共重
合体、スチレン・ビニルトルエン共重合体、１Ｅ化ポリ
エチレン、クロルスルホン化ポリエチレン、ニトロセル
ロース、ポリ塩化ビニル、ポリエステル、ポリイミド、
酢酸ビニル・塩化ビニル共重合体、エチレン・酢酸ビニ
ル共正合体。The surface on which the recording layer is provided is coated with an undercoat layer and/or for the purpose of improving flatness, improving the contact force with the recording layer, improving sensitivity due to the heat insulation effect, and preventing deterioration of the recording layer. Examples of materials for the undercoat layer (or intermediate layer), which may include an intermediate layer, include polymethyl methacrylate, acrylic acid-methacrylic acid copolymer, styrene.
Maleic anhydride copolymer, polyvinyl alcohol, N-
Methyloracrylamide, styrene-sulfonic acid copolymer, styrene-vinyltoluene copolymer, 1E polyethylene, chlorosulfonated polyethylene, nitrocellulose, polyvinyl chloride, polyester, polyimide,
Vinyl acetate/vinyl chloride copolymer, ethylene/vinyl acetate copolymer.
ポリエチレン、ポリプロピレン、ポリカーボネートなど
の高分子物質を挙げることができる。Examples include polymeric substances such as polyethylene, polypropylene, and polycarbonate.
特に本発明のガラス基板を右する情報記録媒体において
は、前記特願昭５８−１７３６７６号明細書に記載され
ているように、基板から遊蕩するアルカリ金１市イオン
、アルカリ土類金属イオンによる記録層への悪影響を防
止する目的で、スチレン・無水マレイン酸共重合体など
の親水性基および／または無水マレイン酸基を有するポ
リマーからなる下塗層が設けられているのが望ましい。In particular, in the information recording medium using the glass substrate of the present invention, as described in the above-mentioned Japanese Patent Application No. 173676/1987, recording is caused by alkali gold ions and alkaline earth metal ions floating from the substrate. In order to prevent an adverse effect on the layer, it is desirable to provide an undercoat layer made of a polymer having a hydrophilic group and/or a maleic anhydride group, such as a styrene/maleic anhydride copolymer.
本発明の特徴的な要件である下塗層（または中間層）の
形成は、以下のようして行なうことができる。まず、上
記高分子物質を適当な溶剤に溶解または分散させて塗布
液を調製する０次に、この塗布液をスピンコード、ディ
ップコート、エクストルージョンコートなどの通常の塗
布方法で円盤状基板の表面全体に塗布して塗膜を設けた
のち、直ちにスペーサとの接合部分の塗膜、すなわち基
板の外周および内周に沿った一定幅の塗膜を適当な溶剤
を用いで布等で拭き取り、そののちに塗膜を乾燥させる
。または、塗膜の乾燥後に接合部分の下塗層の除去を行
なってもよい。Formation of the undercoat layer (or intermediate layer), which is a characteristic requirement of the present invention, can be performed as follows. First, a coating solution is prepared by dissolving or dispersing the above-mentioned polymeric substance in an appropriate solvent.Next, this coating solution is applied to the surface of a disc-shaped substrate by a conventional coating method such as spin cord, dip coating, or extrusion coating. After coating the entire surface to form a coating film, immediately wipe off the coating film on the joint part with the spacer, that is, the coating film of a certain width along the outer and inner peripheries of the board, with a cloth etc. using an appropriate solvent. Afterward, let the paint film dry. Alternatively, the undercoat layer at the joint portion may be removed after the coating film has dried.
あるいは、予め基板のスペーサとの接合部分をテープ等
で覆っておいて上記と同様にして塗布液を塗布、乾燥し
たのち覆いを取りはずしてもよい、あるいはまた、塗布
液をスクリーン印刷法により基板表面の特定部分にのみ
塗布してもよい。Alternatively, the joint portion of the substrate with the spacer may be covered with tape or the like in advance, and the coating liquid may be applied in the same manner as above, and the cover may be removed after drying.Alternatively, the coating liquid may be applied to the substrate surface by screen printing. It may be applied only to specific areas.
このようにして、基板の記録層が設けられる側の接合部
分以外の表面、言い換えれば記録層が設けられる部分の
みに、下塗層（または中間層）を形成することができる
。また、下塗層および／または中間層を複数層形成する
場合には上記操作を繰り返すことにより、基板の接合部
分は基板表面が露出した状態とすることができる。下塗
層（または中間層）の層厚は一般に０．Ｏｌ乃至２０ｐ
ｍであり、好ましくは０．１乃至１０ｐｍである。In this way, the undercoat layer (or intermediate layer) can be formed only on the surface of the substrate other than the joint portion on the side where the recording layer is provided, in other words, only on the portion where the recording layer is provided. Furthermore, when forming a plurality of undercoat layers and/or intermediate layers, by repeating the above operations, the surfaces of the substrates can be exposed at the bonding portions of the substrates. The layer thickness of the undercoat layer (or intermediate layer) is generally 0. Ol~20p
m, preferably 0.1 to 10 pm.
次に、下塗層および／または中間層上には記録層が設け
られる。Next, a recording layer is provided on the undercoat layer and/or the intermediate layer.
記録層に用いられる材料の例としては、Ｔｅ、Ｚｎ、Ｉ
ｎ、Ｓｎ、Ｚｒ、Ａｎ、Ｃｕ、Ｇｅ等の金属；Ｂｉ、Ａ
ｓ、Ｓｂ等の半金属；Ｇｅ、Ｓｉ等の半導体；およびこ
れらの合金またはこれらの組合せを挙げることができる
。また、これらの金属または半金属の硫化物、酸化物、
ホウ化物、ケイ素化合物、炭化物および窒化物等の化合
物；およびこれらの化合物と金属との混合物も記Ｑ層に
用いることができる。Examples of materials used for the recording layer include Te, Zn, I
Metals such as n, Sn, Zr, An, Cu, Ge; Bi, A
Metalloids such as S and Sb; semiconductors such as Ge and Si; and alloys thereof or combinations thereof. In addition, sulfides, oxides of these metals or metalloids,
Compounds such as borides, silicon compounds, carbides, and nitrides; and mixtures of these compounds and metals can also be used in the Q layer.
記録層は、上記材料を蒸着、スパッタリング、イオンブ
レーティングなどの方法により下ｍｆｆ（および／また
は中間層）を介して形成することができる。記ｊｉ層は
単層またはｍｚでもよいが。The recording layer can be formed using the above-mentioned materials via the lower mff (and/or the intermediate layer) by a method such as vapor deposition, sputtering, or ion blasting. The ji layer may be a single layer or a mz layer.
その層厚は光情＋＆記録に要求される光学濃度の点から
一般に１００乃至５５００″人の範囲である。The layer thickness is generally in the range of 100 to 5,500 inches in view of the optical density required for optical performance and recording.
記録層は二枚の基板両方に設けられていてもよいし、あ
るいは片方のみに設けられていてもよい。The recording layer may be provided on both of the two substrates, or may be provided on only one of the substrates.
なお、基板の記録層が設けられる側とは反対側の表面に
は、耐傷性、防湿性などを高めるために、たとえば二酸
化ケイ素、酸化スズ、弗化マグネシウムなどの無機物質
からなる薄膜が真空革着、スパッタリング等により設け
られていてもよい。In addition, a thin film made of an inorganic substance such as silicon dioxide, tin oxide, or magnesium fluoride is coated with vacuum leather on the surface of the substrate opposite to the side on which the recording layer is provided, in order to improve scratch resistance and moisture resistance. It may be provided by deposition, sputtering, or the like.
次に、下塗層および／または中間層、および記録層の形
成された二枚のガラス基板を記録層を内側にして、スペ
ーサを介して接合する。接合は、接着剤を用いてリング
状外側スペーサおよびリング状内側スペーサと二枚の基
板とを窒素ガス等の不活性ガス雰囲気下で貼り合わせる
ことにより行なわれる９本発明において、基板の接合部
分には下塗層および／または中間層、さらには記録層が
一切設けられていないから、ガラス基板とスペーサとは
接着剤により直接に接着される。Next, the two glass substrates on which the undercoat layer and/or intermediate layer and the recording layer have been formed are joined together with the recording layer on the inside via a spacer. Bonding is performed by bonding the ring-shaped outer spacer and ring-shaped inner spacer to the two substrates using an adhesive in an inert gas atmosphere such as nitrogen gas. Since no undercoat layer and/or intermediate layer, and even no recording layer are provided, the glass substrate and the spacer are directly bonded to each other with an adhesive.
スペーサには、公知のアルミニウム等の金属製のスペー
サおよびアセタール樹脂等の合Ｊ＆樹脂製のスペーサな
どを使用することができるが、耐久性の点から特に好ま
しいものは陽極酸化処理（アルマイト処理）を施された
金属アルミニウム製スペーサである。As the spacer, known spacers made of metal such as aluminum and spacers made of composite resin such as acetal resin can be used, but from the viewpoint of durability, anodizing treatment (alumite treatment) is particularly preferable. It is a spacer made of metal aluminum.
接合には公知の各種の接着剤を用いることができ、その
例としてはエポキシ系接若剤、放射線硬化性接着剤を挙
げることができる。耐久性の点から、紫外線、電子線な
どの照射により硬化する放射線硬化性接着剤が好ましい
、その例としては。Various known adhesives can be used for bonding, examples of which include epoxy adhesives and radiation-curable adhesives. From the viewpoint of durability, radiation-curable adhesives that are cured by irradiation with ultraviolet rays, electron beams, etc. are preferred, as examples.
（メタ）アクリル酸、（メタ）アクリル酸エステル、
（メタ）アクリルアミド、アクリロニトリルおよびこれ
らの誘導体；多価アルコールの（メタ）アクリル酸エス
テル；およびこれらの混合物を挙げることができる。(meth)acrylic acid, (meth)acrylic ester,
Mention may be made of (meth)acrylamide, acrylonitrile and derivatives thereof; (meth)acrylic acid esters of polyhydric alcohols; and mixtures thereof.
なお、上記放射線硬化性接着剤中には増感剤（ラジカル
発生のだめの重合開始剤）が添加されていてもよい、そ
のような目的に用いられる増感剤の例としては、ヘンジ
インアルキルエーテル、ペンジルケクール、７セタール
類、アセトフェノ７話導体、ベンゾフェノン訝導体、キ
サントン訪導体、チオキサントン誘導体、アントラキ／
ノ誘導体、ベンズアルデヒド誘導体などを挙げることが
できる。これらの増感剤は単独でも、あるいは適宜組合
わせても使用することができる。A sensitizer (polymerization initiator to prevent radical generation) may be added to the radiation-curable adhesive. Examples of sensitizers used for such purposes include hengeyne alkyl ether. , penzilkecool, 7 setals, acetophenol 7 conductors, benzophenone conductors, xanthone conductors, thioxanthone derivatives, anthracite/
and benzaldehyde derivatives. These sensitizers can be used alone or in appropriate combinations.
また、基板とスペーサとの接着を強化するために上記ｍ
Ｅ剤と共にシランカップリング剤を使用してもよい。In addition, in order to strengthen the adhesion between the substrate and the spacer,
A silane coupling agent may be used with the E agent.
次に本発明の実施例および比較例を記載する。Next, Examples and Comparative Examples of the present invention will be described.
ただし、これらの各個は本発明を制限するものでない。However, each of these does not limit the present invention.
［実施例］
二枚の円盤状ガラス基板（外径：３０５ｍｍ、内径：３
５ｍｍ、厚さ：１．３ｍｍ）の片面全体に、２％のスチ
レン惨無水マレイン酸共重合体溶液（メチルエチルケト
ンとメチルセロソルブアセテートの１＝１（容積比）溶
液）を１１０００ｒｐの回転数のスピンナーを用いて塗
布したのち、１２０°Ｃの温度で５分間塗膜を乾燥させ
て乾燥膜厚が０．２４ｍの下塗層を形成した。[Example] Two disc-shaped glass substrates (outer diameter: 305 mm, inner diameter: 3
A 2% styrene-maleic anhydride copolymer solution (a 1=1 (volume ratio) solution of methyl ethyl ketone and methyl cellosolve acetate) was applied to one side of a 5 mm, thickness: 1.3 mm) using a spinner rotating at 11,000 rpm. After coating using the same method, the coating film was dried at a temperature of 120° C. for 5 minutes to form an undercoat layer having a dry film thickness of 0.24 m.
この下塗層の上に、２％のポリンチルメタクリレート溶
液（トルエンとメチルセロソルブの４＝１（容積比）溶
液）を同様にしてスピンナーを用いて塗布したのち乾燥
して、乾燥膜厚が０．２ＡＬｍの断ａＦ！：を形成した
１次いで、基板の外周に沿った７、５ｍ出の幅の領域お
よび基板の内周に沿った７２．５ｍｍの幅の領域の下塗
層および断熱層をメチルエチルケトンを用いて拭き取る
ことにより除去した。On top of this undercoat layer, a 2% polytyl methacrylate solution (a 4=1 (volume ratio) solution of toluene and methyl cellosolve) was similarly applied using a spinner, and then dried until the dry film thickness was 0. .2ALm's break aF! : Next, the undercoat layer and the heat insulation layer in a 7.5 m wide area along the outer circumference of the substrate and a 72.5 mm wide area along the inner circumference of the substrate are wiped off using methyl ethyl ketone. It was removed by
次に、断熱層表面にＩｎとＧａｓとを１：１（Ｉｎ：Ｇ
ｅＳ、容積比）の比率で共蒸着させて、厚さ３００人の
記録層を形成した。Next, In and Gas were added to the surface of the heat insulating layer at a ratio of 1:1 (In:G
eS, volume ratio) to form a recording layer with a thickness of 300 nm.
リング状のアルマイト処理された外側Ａｎスペーサ（外
径：３０５ｍｍ、内径：２９５ｍｍ）および内側Ａ文ス
ペーサ（外径：１６０ｍｍ、内径：３５ｍｍ）の各接着
面に、シランカップリング剤を設けたのち、転写印刷法
により下記組成の紫外線硬化性接着剤からなる層を５０
Ｉｊ、ｍの厚さで設けた。After applying a silane coupling agent to each adhesive surface of the ring-shaped anodized outer An spacer (outer diameter: 305 mm, inner diameter: 295 mm) and inner A spacer (outer diameter: 160 mm, inner diameter: 35 mm), 50 layers of ultraviolet curable adhesive having the following composition were formed using a transfer printing method.
It was provided with a thickness of Ij, m.
７ ′ １「
けられたＡ文スペーサとを、記録層を内側にして窒；ド
ガス雰囲気下で接着したのち、ｌｋｗの高圧水銀灯２台
を用いて５０ｃｍの距離から両面同時に紫外線を２分９
間照射した。7' 1 "After bonding the cut A spacer with the recording layer inside in a nitrogen gas atmosphere, both sides were exposed to ultraviolet light for 2 minutes at the same time from a distance of 50 cm using two LKW high pressure mercury lamps.
Irradiated for a while.
このようにして、第３図に示すような情報記録媒体を製
造した。ただし、ｆｊＳ３図の部分断面図において、ｌ
ａ、ｌｂ：基板、２ａ、２ｂ：下塗層、３ａ、３ｂ：記
録層、４ａ、４ｂ：接着剤層。In this way, an information recording medium as shown in FIG. 3 was manufactured. However, in the partial cross-sectional view of figure fjS3, l
a, lb: substrate, 2a, 2b: undercoat layer, 3a, 3b: recording layer, 4a, 4b: adhesive layer.
５：外側スペーサ、６：内側スペーサ、７ａ。5: outer spacer, 6: inner spacer, 7a.
７ｂ；断ａ暦である。7b; It is a broken calendar.
［比較例］
実施例において、基板上に下塗層および断８層を設けた
のちこの下塗層および断熱層の一部をメチルエチルケト
ンで拭き取らなかったこと以外は、実施例の方法と同様
の操作を行なうことにより、情報記録媒体を製造した。[Comparative Example] The same method as in the example was used, except that after providing the undercoat layer and the 8 layers on the substrate, a part of the undercoat layer and the heat insulation layer was not wiped off with methyl ethyl ketone. By performing the operations, an information recording medium was manufactured.
従って、下塗層および断熱層を介して基板とＡ文スペー
サとが接着された。Therefore, the substrate and the A-shaped spacer were bonded through the undercoat layer and the heat insulating layer.
次に、得られた各情報記録媒体について接着性試験によ
り評価した。Next, each of the obtained information recording media was evaluated by an adhesion test.
情報記録媒体を温度６０℃、湿度９０％ＲＨの恒温槽中
で３０日間放置後、該情報記録媒体を断面凸型のスピン
ドル（突出部の直径：３５ｍｍ）に載せて一方を固定し
、他方を３ｍｍ下方へ変形させた。このとき、ガラス基
板と接着剤層とが剥離するか否かを観察し、全く剥離し
ない場合を接着性良好、少しでも！ｌＩ類する場合を接
着性不良として評価を行なった。After leaving the information recording medium in a constant temperature bath at a temperature of 60°C and a humidity of 90% RH for 30 days, the information recording medium was placed on a spindle with a convex cross section (diameter of the protrusion: 35 mm), one side was fixed, and the other side was It was deformed 3mm downward. At this time, observe whether the glass substrate and the adhesive layer peel off or not. If they do not peel off at all, the adhesion is good, even a little! Cases of Class II were evaluated as poor adhesion.
得られた結果を第１表に示す。The results obtained are shown in Table 1.
第１表
接着性
実施例 良好
比較例 不良
第１表に示された結果から明らかなように１本発明に従
う情報記録媒体（実施例）は接着剤層との接看面がガラ
ス基板であるために、下塗層および断熱層を介して接着
された従来の情報記録媒体（比較例）と比較して、接着
性が大幅に改良されていた。Table 1 Adhesiveness Example Good Comparative Example Bad As is clear from the results shown in Table 1, the information recording medium according to the present invention (Example) has a glass substrate as the contact surface with the adhesive layer. In addition, the adhesion was significantly improved compared to a conventional information recording medium (comparative example) that was adhered via an undercoat layer and a heat insulating layer.
第１図は１本発明のエアーサンドイッチ構造の情報記録
媒体を模式的に示す斜視図である。
第２図は、第１図のｘ−Ｘ線に沿った断面図であり、本
発明のエアーサンドイッチ型情報記録媒体の一実施態様
を示す図である。
第３図は、本発明のエアーサンドイッチ型情報記録媒体
の別の実施態様を示す部分断面図である。
ｌａ、ｌｂ：基板、２ａ、２ｂ：下塗層。
３ａ、３ｂ：記録層、４ａ 、 ４ｂ ：接着剤層、５
、外側スペーサ、６：内側スペーサ、７ａ 、 ７ｂ
：断熱層
特許出願人 富士写真フィルム株式会社代 理 人
弁理士 柳 川 泰 男第１図
第２図
第３図FIG. 1 is a perspective view schematically showing an information recording medium having an air sandwich structure according to the present invention. FIG. 2 is a sectional view taken along the line xx in FIG. 1, and is a diagram showing one embodiment of the air sandwich type information recording medium of the present invention. FIG. 3 is a partial sectional view showing another embodiment of the air sandwich type information recording medium of the present invention. la, lb: substrate, 2a, 2b: undercoat layer. 3a, 3b: recording layer, 4a, 4b: adhesive layer, 5
, outer spacer, 6: inner spacer, 7a, 7b
:Thermal Insulation Layer Patent Applicant Fuji Photo Film Co., Ltd. Representative Patent Attorney Yasushi Yanagawa Figure 1 Figure 2 Figure 3
Claims (1)
リング状外側スペーサとを介して接着剤により接合され
、かつ少なくともその一方の基板の内側表面に下塗層お
よび／または中間層を介してレーザーによる情報の書き
込みおよび／または読み取りが可能な記録層が設けられ
てなるエアーサンドイッチ構造の情報記録媒体において
、該ガラス基板のスペーサと接合される部分には下塗層
、中間層および記録層が設けられていないことを特徴と
する情報記録媒体。 ２、上記接着剤が放射線硬化性接着剤であることを特徴
とする特許請求の範囲第１項記載の情報記録媒体。 ３、上記接着剤がエポキシ系接着剤であることを特徴と
する特許請求の範囲第１項記載の情報記録媒体。 ４、上記スペーサが陽極酸化処理を施された金属アルミ
ニウムからなることを特徴とする特許請求の範囲第１項
記載の情報記録媒体。 ５、上記下塗層が親水性基および／または無水マレイン
酸基を有するポリマーであることを特徴とする特許請求
の範囲第１項記載の情報記録媒体。 ６、上記下塗層がスチレン・無水マレイン酸共重合体か
らなることを特徴とする特許請求の範囲第５項記載の情
報記録媒体。 ７、上記中間層が高分子物質からなる断熱層であること
を特徴とする特許請求の範囲第１項記載の情報記録媒体
。 ８、上記断熱層がポリアルキル（メタ）アクリレート系
樹脂および／またはセルロース誘導体からなることを特
徴とする特許請求の範囲第７項記載の情報記録媒体。[Claims] 1. Two disc-shaped glass substrates are bonded together with an adhesive via a ring-shaped inner spacer and a ring-shaped outer spacer, and an undercoat layer and/or an undercoat layer is provided on the inner surface of at least one of the substrates. Alternatively, in an air sandwich structure information recording medium provided with a recording layer on which information can be written and/or read by a laser via an intermediate layer, the portion of the glass substrate to be bonded to the spacer has an undercoat layer; An information recording medium characterized in that an intermediate layer and a recording layer are not provided. 2. The information recording medium according to claim 1, wherein the adhesive is a radiation-curable adhesive. 3. The information recording medium according to claim 1, wherein the adhesive is an epoxy adhesive. 4. The information recording medium according to claim 1, wherein the spacer is made of metal aluminum subjected to anodizing treatment. 5. The information recording medium according to claim 1, wherein the undercoat layer is a polymer having a hydrophilic group and/or a maleic anhydride group. 6. The information recording medium according to claim 5, wherein the undercoat layer is made of a styrene/maleic anhydride copolymer. 7. The information recording medium according to claim 1, wherein the intermediate layer is a heat insulating layer made of a polymeric substance. 8. The information recording medium according to claim 7, wherein the heat insulating layer is made of a polyalkyl (meth)acrylate resin and/or a cellulose derivative.