JPS61258747A - Mold release treating base body - Google Patents
Mold release treating base bodyInfo
- Publication number
- JPS61258747A JPS61258747A JP10012385A JP10012385A JPS61258747A JP S61258747 A JPS61258747 A JP S61258747A JP 10012385 A JP10012385 A JP 10012385A JP 10012385 A JP10012385 A JP 10012385A JP S61258747 A JPS61258747 A JP S61258747A
- Authority
- JP
- Japan
- Prior art keywords
- release
- mold release
- back surfaces
- base body
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。(57) [Summary] This bulletin contains application data before electronic filing, so abstract data is not recorded.
Description
【発明の詳細な説明】
産業上の利用分野
本発明は、表裏面におけるシリコーン系の離形皮膜の架
橋密度を相違させて表裏面における剥離力のバランスを
よくした離形処理基体に関するものである。DETAILED DESCRIPTION OF THE INVENTION Field of Industrial Application The present invention relates to a release-treated substrate in which the crosslinking densities of silicone-based release films on the front and back surfaces are different to better balance the release force on the front and back surfaces. .
従来の技術及び問題点
薄葉基材の表裏面にシリコーン系離形処理剤からなる皮
膜を有する例えば粘着テープにおける剥離紙等の離形処
理基体の用途の多様化に伴って、従来の表裏面における
剥離力が実質的に同じ1タイプのものでは充分にその用
途に対応できないという問題が発生している。粘着テー
プを高速度で巻戻す際に剥離紙の背面側に粘着剤層が残
存する現象やテープ基材と剥離紙との間で剥がれたシす
る現象などがその例である。Prior Art and Problems With the diversification of uses for release treated substrates, such as release paper in adhesive tapes, which have films made of silicone release agents on the front and back sides of thin substrates, conventional A problem has arisen in that one type of material having substantially the same peeling force is not sufficient for the intended use. Examples include the phenomenon in which the adhesive layer remains on the back side of the release paper when the adhesive tape is rewound at high speed, and the phenomenon in which the adhesive layer peels off between the tape base material and the release paper.
問題点を解決するための手段
本発明者らは、軽剥離から1剥離に及ぶ剥離力めるいは
剥離速度に応じた剥離バランスのコントロール化などの
要求に応じつつ、と記の問題が克服された離形処理基体
を開発するために鋭意研究を重ねた結果、シリコーン系
離形処理剤の硬化皮膜における架橋密度とその剥離力の
速度依存性とに因果性があるという新たな知見をみいだ
した。Means for Solving the Problems The present inventors have overcome the problems described in the following while responding to demands such as control of peeling force ranging from light peeling to one peeling and peeling balance according to peeling speed. As a result of intensive research to develop a mold release treatment substrate, we discovered a new finding that there is a causal relationship between the crosslinking density in the cured film of silicone mold release agents and the speed dependence of the peeling force. did.
本発明はこの新知見に基°づいてなしたものである。The present invention was made based on this new knowledge.
すなわち、本発明は、薄葉基材の表裏面にシリコーン系
離形処理剤からなる皮膜を有する基体において、表裏面
における前記皮膜の架橋密度が異なることを特徴とする
離形処理基体を提供するものである。That is, the present invention provides a mold release treated substrate having a film made of a silicone mold release agent on the front and back surfaces of a thin base material, characterized in that the crosslinking density of the film on the front and back surfaces is different. It is.
本発明において用いられる薄葉基材としては、紙、プラ
スチック、金属箔等の単層物、積層物などからなシ厚さ
が通常0.01〜11111のものをその代表例として
あげることができる。Typical examples of the thin substrate used in the present invention include paper, plastic, metal foil and other single-layer and laminate materials having a thickness of usually 0.01 to 11111 mm.
また、シリコーン系離形処理剤としては市販のポリジメ
チルシロキサン系離形処理剤などで代表されるシリコー
ン系硬化皮膜形成性のものをあげることができる。もち
ろん、プラスチック、ゴム等の剥離力調整剤や充填剤な
どを含有するものなどであってもよい。Further, as the silicone mold release agent, there may be mentioned a cured silicone film-forming agent such as a commercially available polydimethylsiloxane mold release agent. Of course, it may also be made of plastic, rubber, or the like containing a release force adjusting agent, filler, or the like.
そして、本発明の離形処理基体は、薄葉基材の表裏面に
シリコーン系離形処理剤からなる皮膜を、それらの架橋
密度が異なるよう(、好ましくは10%以上の架橋密度
差となるように設けたものである◇これにより離形処理
基体の表裏面における剥離力の速度依存性に差異が生じ
ることとなる。一般にその剥離力の速度依存性は、架橋
密度が高くなるほど小さくなる傾向にある。なお、該皮
膜の形戊厚さとしては特に限定はなく、従来と同様の厚
さで本発明の目的を達成しうる。具体的には0.1〜1
100)tの厚さが一般的で委る。The release-treated substrate of the present invention is produced by applying a film made of a silicone-based release agent to the front and back surfaces of a thin substrate so that the crosslinking densities thereof are different (preferably, the difference in crosslinking density is 10% or more). ◇This causes a difference in the speed dependence of the peeling force on the front and back surfaces of the release-treated substrate.Generally, the speed dependence of the peeling force tends to decrease as the crosslinking density increases. The thickness of the film is not particularly limited, and the object of the present invention can be achieved with the same thickness as in the past.Specifically, the thickness is 0.1 to 1.
100) Thickness of t is common.
発明の効果
本発明によれば、表裏面におけるシリコーン系の離形皮
膜の架橋密度を相違させたので、その表裏面における剥
離力の速度依存性が異なる離形処理基体を得ることがで
きる。その結果、用途に対応した表裏面における剥離力
のバランスを有する離形処理基体の形成が可能となシ、
剥離紙の背面側に粘着剤層が残存すること、テープ基材
と剥離紙との間で剥れることなどを有効に防止すること
ができる。Effects of the Invention According to the present invention, since the crosslinking densities of the silicone release coatings on the front and back surfaces are different, it is possible to obtain a release-treated substrate in which the speed dependence of the peeling force on the front and back surfaces is different. As a result, it is possible to form a release-treated substrate that has a balance of peeling force on the front and back surfaces that corresponds to the application.
It is possible to effectively prevent the adhesive layer from remaining on the back side of the release paper and from peeling between the tape base material and the release paper.
実施例
? 0 f/rr?の晒しクラフト紙の片面にポリジメ
チルシロキサン系離形処理剤の塗布加熱処理層からなる
厚さ1)tm、架橋密度5X10 mol/fの硬化
皮膜を、他面に前記と同系の処理剤の塗布加熱処理層か
らなる厚さ1)1m、架橋密度0.IX No mo
l、/gの硬化皮膜を設けて剥離紙を得た。Example? 0 f/rr? Apply a polydimethylsiloxane-based mold release treatment agent on one side of bleached kraft paper. Apply a cured film consisting of a heat-treated layer with a thickness of 1) tm and a crosslinking density of 5 x 10 mol/f, and apply the same type of treatment agent as above on the other side. Thickness of heat-treated layer: 1) 1 m, crosslinking density: 0. IX No mo
A release paper was obtained by providing a cured film of 1,/g.
この剥離紙における低架橋密度側の硬化皮膜上に天然ゴ
ム系感圧接着剤を乾燥後の厚みが0.06nどなるよう
に塗布して乾燥させ、これをロール状に回巻した。つい
で、その回巻物を3〜100m/分の速度で巻戻したと
ころ良好な巻戻し性を示し、テープと剥離紙との間の分
離は生じなかったO
ちなみに、両面に架橋密度が0. I X 10 m
ol/ fの硬化皮膜を設けたほかは実施例に準じて得
た感圧接着テープの回巻物の同条件での巻戻し試験では
、テープと剥離紙との間で分離が生じた。A natural rubber-based pressure-sensitive adhesive was applied onto the cured film on the low crosslinking density side of the release paper so that the thickness after drying was 0.06 nm, dried, and then wound into a roll. Then, when the rolled material was unwound at a speed of 3 to 100 m/min, it showed good unwinding properties, and no separation occurred between the tape and the release paper. I x 10m
In an unwinding test under the same conditions of a roll of pressure-sensitive adhesive tape obtained according to the example except that a hardened film of ol/f was provided, separation occurred between the tape and the release paper.
Claims (1)
る皮膜を有する基体において、表裏面における前記皮膜
の架橋密度が異なることを特徴とする離形処理基体。 2、架橋密度の差が10%以上である特許請求の範囲第
1項記載の基体。[Scope of Claims] 1. A mold release treated substrate having a film made of a silicone mold release agent on the front and back surfaces of a thin base material, characterized in that the crosslinking density of the film on the front and back surfaces is different. 2. The substrate according to claim 1, wherein the difference in crosslink density is 10% or more.