JPS61151051A - Fiber reinforced cement material - Google Patents
Fiber reinforced cement materialInfo
- Publication number
- JPS61151051A JPS61151051A JP27319684A JP27319684A JPS61151051A JP S61151051 A JPS61151051 A JP S61151051A JP 27319684 A JP27319684 A JP 27319684A JP 27319684 A JP27319684 A JP 27319684A JP S61151051 A JPS61151051 A JP S61151051A
- Authority
- JP
- Japan
- Prior art keywords
- cement
- fibers
- weight
- fiber
- reinforcing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。(57) [Summary] This bulletin contains application data before electronic filing, so abstract data is not recorded.
Description
【発明の詳細な説明】
産業上の利用分野
本発明は、繊維により強化されたセメント材に関し、力
学的強度の改善されたこのセメント材は、スレート、か
わら、舗装材、床材、パイプ、壁材、デート等の建築資
材、土木資材として有用である。DETAILED DESCRIPTION OF THE INVENTION Field of Industrial Application The present invention relates to a cement material reinforced with fibers. It is useful as building materials such as timber and date, and as civil engineering materials.
従来の技術
これまでは、セメント用の一般的な補強繊維として天然
のアスベストが使われていたし、今なお最も多く用いら
れている。又、その他の補強繊維としては、ポリビニル
アルコール系繊維、ガラス繊維、炭素繊維、アラミド繊
維、アクリル系繊維等がある。Prior Art Traditionally, natural asbestos has been, and is still the most commonly used, reinforcing fiber for cement. Other reinforcing fibers include polyvinyl alcohol fibers, glass fibers, carbon fibers, aramid fibers, acrylic fibers, and the like.
発明が解決しようとする問題点
従来、セメント補強用繊維として使用されているものは
、それぞれに問題を有している。Problems to be Solved by the Invention The fibers conventionally used as cement reinforcing fibers have their own problems.
すなわち、天然のアスベストでは、ここ数年前から良質
のアスベストの産出量が不足し、アスベストは今や最も
近い将来に消尽されてしまうであろう天然資源の一つと
して挙げざるを得ない実情となっているし、公害面から
言っても、その有害性から近い将来、使用を禁止される
方向である。In other words, the production of high-quality natural asbestos has been in short supply for the past several years, and asbestos has now become one of the natural resources that will be exhausted in the near future. In terms of pollution, its use is likely to be banned in the near future due to its harmful nature.
又、ポリビニルアルコール繊維については、なるほど機
械的特性については確かに優れているが、セメントの製
造工程におけるアルカリ下での処理の際(%に高温での
処理)に著しく、その機械的特性が減殺されてしまう。Furthermore, although polyvinyl alcohol fibers certainly have excellent mechanical properties, their mechanical properties are significantly reduced during treatment under alkaline conditions (treatment at high temperatures) during the cement manufacturing process. It will be done.
更に、ガラス繊維、炭素繊維及びアラミド繊維等の公知
の繊維は、耐アルカリ性に欠けるか、そのセメントマト
リックスに対する親和性を所望通り保持するには不経済
すぎるかのいづれかである。従って、これらの繊維をセ
メント強化用に用いることは問題外である。Furthermore, known fibers such as glass fibers, carbon fibers and aramid fibers either lack alkali resistance or are too uneconomical to maintain their desired affinity for the cement matrix. Therefore, it is out of the question to use these fibers for cement reinforcement.
最後に、4リアクリロニトリル繊維に関しては、これま
でのものでは、その機械的特性、耐アルカリ性等でセメ
ント強化用としては不適であった。Finally, with regard to tetraacrylonitrile fibers, conventional ones have been unsuitable for reinforcing cement due to their mechanical properties, alkali resistance, etc.
又、最近、これらを改善したものが知られて来てはいる
が、セメントとの密着性で未だ不十分である。本発明に
おいては、機械的特性、耐アルカリ性ともにセメント強
化用として満足のいくものを用いており、又、セメント
との密着性も十分に向上したものであって、それによっ
て機械的特性の優れた繊維で補強され次セメント材を提
供しうる。In addition, although products with improved properties have recently been known, their adhesion to cement is still insufficient. In the present invention, a material with satisfactory mechanical properties and alkali resistance for reinforcing cement is used, and the adhesion with cement is also sufficiently improved. It can be reinforced with fibers to provide a sub-cement material.
問題点を解決するための手段
本発明によれば繊維により強化されたセメント材が提供
されるのであって、このセメント材は、強化繊維として
、メタクリコニトリル2.5乃至30重量%、アクリロ
ニトリルと共重合可能なビニルモノマー5乃至0重量%
とアクリロニトリルからなるアクリル系繊維を含有する
ことを特徴とする。Means for Solving the Problems According to the present invention, a cement material reinforced with fibers is provided, and this cement material contains 2.5 to 30% by weight of methacriconitrile, acrylonitrile and 5 to 0% by weight of copolymerizable vinyl monomer
It is characterized by containing acrylic fibers consisting of and acrylonitrile.
セメント材は一般的に伸度が低く、初期弾性率は高いが
、じん性に乏しい。すなわち、荷重が作用することによ
り、一旦ヒピが入ると同時にしん性がないために割れの
現象を起す。この問題点を解決するために、これまでの
経緯としては、セメント材に、各種の無機、有機高分子
粘体、天然鉱物(アスベスト)、有機繊維、無機繊維な
どを補強材として導入し、セメントの強度及びじん性を
向上させて来友。特に、天然鉱物であるアスベストは、
その機械的性質及び価格面からセメント補強材として主
に使用されて来た。しかしながら、今日、アスベストは
公害問題から、その使用がかなり規制されつつある。Cement materials generally have low elongation and high initial modulus, but poor toughness. In other words, when a load is applied, once cracks occur, cracking occurs due to the lack of toughness. In order to solve this problem, various inorganic and organic polymer viscosity, natural minerals (asbestos), organic fibers, inorganic fibers, etc. have been introduced into cement materials as reinforcing materials. Comes with improved strength and toughness. In particular, asbestos, a natural mineral,
Due to its mechanical properties and cost, it has been mainly used as a cement reinforcement material. However, today, the use of asbestos is being heavily regulated due to pollution problems.
補強材として今日、話題にあがっているのが各種有機繊
維である。中でもビニロン(ポリビニルアルコール繊維
)は、その優れた機械的性質、耐アルカリ性などから、
セメント補強材として用いられて来ている。しかしなが
ら、ビニロンにも短所があり、セメント材を硬化する際
に行なう養生の温度に限界がある。すなわち、110℃
以上の温度でビニロン強化セメント材を養生すると、ビ
ニロン繊維の劣化が生じ、補強材としての役目を果さず
、セメント材の機械的性質は何ら向上しないことになる
。しかるに、高温度での養生はセメント材の生産性を向
上させる点で重要である。Various organic fibers are currently being talked about as reinforcing materials. Among them, vinylon (polyvinyl alcohol fiber) is highly valued due to its excellent mechanical properties and alkali resistance.
It has been used as a cement reinforcing material. However, vinylon also has disadvantages, and there is a limit to the temperature at which it can be cured when curing the cement material. That is, 110℃
If vinylon-reinforced cement material is cured at temperatures above, the vinylon fibers will deteriorate and will not function as a reinforcing material, resulting in no improvement in the mechanical properties of the cement material. However, curing at high temperatures is important in improving the productivity of cement materials.
そこで、セメント材の機械的強度及びじん性を向上し、
高温養生においても耐えられる補強材を鋭意検討した結
果、アクリル系繊維を補強材として用いたセメント材は
、そのじん性及び機械的強度が向上することがわかった
。これまで知られているアクリル系繊維では機械的強度
及び耐アルカリ性が低く補強繊維には適していない。又
、これらを改善したアクリル系繊維が最近知られて来て
はいるが、未だセメントとの密着性−1i不十分である
。本発明のセメント複合材に用いられているアクリル系
繊維は根域的強度及び耐アルカリ性が優れており、セメ
ントとの密着性も向上されたものである。Therefore, we improved the mechanical strength and toughness of cement materials,
As a result of intensive research into reinforcing materials that can withstand high-temperature curing, it was found that cement materials using acrylic fibers as reinforcing materials have improved toughness and mechanical strength. Acrylic fibers known so far have low mechanical strength and alkali resistance and are not suitable as reinforcing fibers. In addition, although acrylic fibers with improved properties have recently become known, their adhesion to cement -1i is still insufficient. The acrylic fibers used in the cement composite material of the present invention have excellent root zone strength and alkali resistance, and have improved adhesion to cement.
この補強材として用いられるアクリル系繊維についてさ
らに詳しく記述する。該アクリル系繊維はメタクリコニ
トリル2.5乃至30重量%(好ましくは10〜20重
量q6)、アクリロニトリルと共重合可能なビニルモノ
マー5乃至0重量%とアクリロニトリルから構成されて
いる。メタクリロニトリルが2.5重量%未満の場合は
耐アルカリ性に劣化、セメント内(アルカリ雰囲気下)
において繊維の機械的特性の劣化がおこるとともにセメ
ントと混練時における繊維のフィブリル化が起りにくく
なり、セメントとの密着性が低下し、目標とするセメン
ト材は得られない。又、メタクリロニトリルが30重量
%より大きい場合は、繊維自体の機械的特性の向上が望
めず、その結果、機械的特性の向上したセメント複合体
は得られない。The acrylic fiber used as this reinforcing material will be described in more detail. The acrylic fibers are composed of 2.5 to 30% by weight of methacriconitrile (preferably 10 to 20% by weight q6), 5 to 0% by weight of a vinyl monomer copolymerizable with acrylonitrile, and acrylonitrile. If methacrylonitrile is less than 2.5% by weight, alkali resistance deteriorates, inside cement (under alkaline atmosphere)
In addition, the mechanical properties of the fibers deteriorate, and fibrillation of the fibers during kneading with cement becomes difficult to occur, resulting in a decrease in adhesion with cement, making it impossible to obtain the desired cement material. Furthermore, if the methacrylonitrile content is greater than 30% by weight, no improvement in the mechanical properties of the fibers themselves can be expected, and as a result, a cement composite with improved mechanical properties cannot be obtained.
このような組成を持つアクリロニトリル系重合体は通常
の水系懸濁重合あるいは有機溶剤による溶液重合によっ
て得られる。アクリロニトリルと共重合可能なビニルモ
ノマーとしては、アクリル酸メチル、メタクリル酸メチ
ル、アクリルアミド、メタクリルアミド、イタコン酸、
マレイミド、アリルアルコール、メタリルアミン、β−
ヒドロキシエチルメタクリレート、β−アミノエチルメ
タクリレート、アクリル酸等があるけれども、これに限
定されるものではない。Acrylonitrile polymers having such a composition can be obtained by conventional aqueous suspension polymerization or solution polymerization using an organic solvent. Vinyl monomers copolymerizable with acrylonitrile include methyl acrylate, methyl methacrylate, acrylamide, methacrylamide, itaconic acid,
maleimide, allyl alcohol, methallylamine, β-
Examples include, but are not limited to, hydroxyethyl methacrylate, β-aminoethyl methacrylate, and acrylic acid.
かくして得られたアクリル系重合体は、ジメチルホルム
アミド、ジメチルアセトアミド、ツメチルスルホアミド
等の有機溶剤、硝酸、硫酸、チオシアン酸ナトリウム(
ロダン塩)、塩化亜鉛水溶液等の無機溶剤に溶解して紡
糸原液とする。この紡糸原液を乾式あるいは湿式の紡糸
法により紡出し、凝固させた後、溶剤延伸を施こし水洗
する。The acrylic polymer thus obtained can be treated with organic solvents such as dimethylformamide, dimethylacetamide, and trimethylsulfamide, nitric acid, sulfuric acid, and sodium thiocyanate (
Rodan salt), dissolved in an inorganic solvent such as an aqueous zinc chloride solution to prepare a spinning stock solution. This spinning stock solution is spun using a dry or wet spinning method, solidified, and then subjected to solvent stretching and washing with water.
水洗後は沸水、グリセリン、水蒸気等の媒体によf)延
伸せしめる。紡出からの総延伸倍率は9〜20倍で、好
ましくは11倍から16倍である。After washing with water, f) stretching is performed using a medium such as boiling water, glycerin, or steam. The total stretching ratio from spinning is 9 to 20 times, preferably 11 to 16 times.
9倍未満であると目標とする機械的強度は得られず、2
0倍より大きいと延伸不能となり、糸切れが多発する。If it is less than 9 times, the target mechanical strength cannot be obtained, and 2
If it is larger than 0 times, stretching becomes impossible and yarn breakage occurs frequently.
かくして得られた延伸糸は乾燥機にて足長もしくは緊張
下で乾燥緻密化を行なった後、再度、乾熱あるいは湿熱
下で延伸する。延伸比は1.1から1.4倍であって、
1.1倍未満であると目標とする機械的物性は得難く、
1.4倍より大きいと糸切れが多発し、均一な繊維は得
られない。The thus obtained drawn yarn is dried and densified in a dryer under full length or tension, and then drawn again under dry heat or moist heat. The stretching ratio is 1.1 to 1.4 times,
If it is less than 1.1 times, it is difficult to obtain the target mechanical properties.
If it is larger than 1.4 times, thread breakage occurs frequently and uniform fibers cannot be obtained.
再延伸を施した繊維は最後に熱セットに付される。熱セ
ットを施さないと、セメントに混合した際アルカリ液に
より収縮を起し、機械的性質が劣化し、補強繊維として
の役目を果さなくなる。以上の製造工程によって得られ
たアクリル系繊維の単繊維強度は611/ci以上であ
り、初期弾性率は850kg/a2以上と高強度でかつ
高弾性率を有し、セメントとの密着性がよく、耐アルカ
リ性の優れたアクリル系繊維である。該繊維をポルトラ
ンドセメント炉液(アルカリ液:pH=12)により8
0Cで8時間処理した後の強度の保持率はいづれも85
チ以上と優れており、セメント補強材としては遜色ない
。The redrawn fibers are finally heat set. If it is not heat-set, it will shrink due to the alkaline solution when mixed with cement, its mechanical properties will deteriorate, and it will no longer function as a reinforcing fiber. The single fiber strength of the acrylic fiber obtained through the above manufacturing process is 611/ci or more, the initial elastic modulus is 850 kg/a2 or more, which is high strength and high elastic modulus, and has good adhesion to cement. , an acrylic fiber with excellent alkali resistance. The fibers were mixed with Portland cement furnace solution (alkaline solution: pH=12).
The strength retention rate after 8 hours of treatment at 0C was 85.
It is superior in quality and is comparable as a cement reinforcing material.
本発明で用いるメタクリロニトリルを成分として含有し
ているアクリル系繊維の物性及びセメント戸液で処理(
80℃×8時間)した後の繊維物性を表1及び表2に記
載する。Physical properties of acrylic fiber containing methacrylonitrile used in the present invention and treatment with cement solution (
Tables 1 and 2 show the fiber properties after heating at 80°C for 8 hours.
又、本発明のセメント材に用いるメタクリロニトリルを
含有するアクリル系繊維は、セメントとの混線時におい
てフィブリル化を起しやすい性質を有している。その理
由は定かではないが、メタクリロニトリルを含有するこ
とによってアクリル系繊維内の結晶性に変化がみられ、
もろくなる傾向になるからであると考えられる。このフ
ィブリル化を起すことによって補強繊維とセメントとの
密着性が増大し、セメント材の機械的強度が増す″
ものと考えられる。したがって、従来のアクリル系繊維
、あるいは最近知られている機械的物性・耐アルカリ性
の向上したアクリル系繊維を含有したセメント材に比べ
てもその機械的物性は優れている。Furthermore, the acrylic fiber containing methacrylonitrile used in the cement material of the present invention has a property of being easily fibrillated when mixed with cement. The reason for this is not clear, but the inclusion of methacrylonitrile changes the crystallinity within the acrylic fiber.
This is thought to be because it tends to become brittle. This fibrillation increases the adhesion between reinforcing fibers and cement, increasing the mechanical strength of the cement material.
considered to be a thing. Therefore, its mechanical properties are superior compared to conventional acrylic fibers or cement materials containing recently known acrylic fibers with improved mechanical properties and alkali resistance.
又、本発明のセメント材に用いる繊維の太さは、好まし
くは、0.5d〜10.Odであって、セメント補強材
として用いる時は、好ましくは3m〜20mの長さに切
断して用いる。長さが3mより短かい場合は補強材とし
ての効果に寄与することが少なく、長さが20震より長
い場合は繊維がセメントに混練される際にややもすると
玉状にナクがちで補強効果は減少する。該繊維は高温ア
ルカリ雰囲気下においてもその物性を十分に保持するこ
とが可能であり、セメント材としての曲げ強度及びじん
性を大幅に向上させる。又、セメント材のひび割れ発生
後の曲げ強度において、耐折力の増加を示し、ひび割れ
発生後の最高荷重時の歪は大きな値を示す。すなわち、
ひび割れ発生後の最高荷重時の歪の大きさの増加がタフ
ネスを向上させ靭性(じん性)の向上につながり、曲げ
強度の向上と高エネルギー吸収能を与えることとなる。Further, the thickness of the fibers used in the cement material of the present invention is preferably 0.5d to 10.5d. When used as a cement reinforcing material, it is preferably cut into lengths of 3 m to 20 m. If the length is shorter than 3 m, it will not contribute much to the effect as a reinforcing material, and if the length is longer than 20 tremors, the fibers tend to bead-like when mixed into cement and have no reinforcing effect. decreases. The fibers can sufficiently maintain their physical properties even in a high-temperature alkaline atmosphere, and greatly improve the bending strength and toughness of cement materials. In addition, the bending strength of the cement material after cracking shows an increase in rupture strength, and the strain at the highest load after cracking shows a large value. That is,
An increase in the amount of strain at the highest load after cracking improves toughness, leading to improved toughness, which provides improved bending strength and high energy absorption ability.
該繊維は、単独又は鋼繊維、耐アルカIJ ffラス繊
維、ホlJヒニルアルコール、アスベストパルプ、及び
ポリエチレン、ナイロン等の他の有機合成繊維とも混合
使用が出来る。セメントは通常の水硬性セメントであり
、通常のポルトランドセメントで普通ポルトランドセメ
ント、早強ポルトランドセメント、耐硫酸塩ポルトラン
ドセメント、白色ポルトランドセメントが用いられる。The fibers can be used alone or mixed with other organic synthetic fibers such as steel fibers, alkali-resistant IJ ff fibers, HolJ vinyl alcohol, asbestos pulp, and polyethylene and nylon. The cement is an ordinary hydraulic cement, and ordinary Portland cement, early-strength Portland cement, sulfate-resistant Portland cement, and white Portland cement are used.
混合セメントも限定するものでなく、高炉セメン・ト、
シリカセメント、フライアッシーセメントも利用出来、
その他アルミナセメント、膨張セメント、超早強セメン
トも利用できる。又、混和剤として流動化剤、減水剤、
増粘剤、保水剤、撥水剤を混合利用することも可能であ
る。セメントに対する該繊維の含有率は、好ましくは0
.5重量%から10重量%である。Mixed cement is also not limited to blast furnace cement,
Silica cement and fly-assy cement can also be used.
In addition, alumina cement, expansive cement, and ultra-early strength cement can also be used. In addition, as admixtures, fluidizing agents, water reducing agents,
It is also possible to use a mixture of thickeners, water retention agents, and water repellents. The content of the fibers in cement is preferably 0.
.. It is 5% to 10% by weight.
セメントに該繊維を混和する際、該繊維はセメントとの
親和性が良好であり、分散性についても特に大きな問題
はない。又、抄造法でセメント材を製造する際も、セメ
ントとの親和性が良いため、該繊維のセメントからの脱
落はほとんど起らない。When the fibers are mixed with cement, the fibers have good affinity with the cement, and there are no particular problems with dispersibility. Furthermore, when producing cement material by the papermaking method, the fibers hardly fall off from the cement because of their good affinity with cement.
かくして造られたセメント材の用途としては、スレート
材、屋根材、タイル等があり、具体的な製品としてはノ
4イグ(下水管)、住宅外装(壁、防音材)、かわら、
植木鉢等がある。特に、かわらや住宅外装で用いる場合
は、本発明のセメント材は、曲げ強度、靭性が向上して
いることから、使用時はもちろん施行時においても作業
性の向上がみられる。特に、手作業においては、釘打ち
性、/4ンチング性、裁断においてひびが入りにくい性
質がある。The cement materials produced in this way can be used for slate materials, roofing materials, tiles, etc., and specific products include sewer pipes, housing exteriors (walls, soundproofing materials), tiles, etc.
There are flower pots etc. In particular, when used for roofing or housing exteriors, the cement material of the present invention has improved bending strength and toughness, so it can be seen to improve workability not only during use but also during construction. In particular, it has the property of not being easily cracked during nailing, quarter-inching, and cutting when used manually.
実施例 以下に、本発明のセメント材の実施例を示す。Example Examples of the cement material of the present invention are shown below.
実施例1
メタクリロニトリルを1.5重量%、2.5重量%、1
0重量%、20重量%、30重量%、35重量%とアク
リロニトリルをそれぞれ98.5重量%、97.5重量
%、90重量%、80重量%、70重量%、65重量%
採り、水系懸濁重合法によって重合し6種類の共重合体
を得た。これらの共重合体をそれぞれ68%硝酸水溶液
に溶解し、紡糸原液とした後、これらの紡糸原液を湿式
紡糸法によって稀硝醗水溶液中で凝固せしめ、溶剤延伸
、製水延伸、蒸気延伸で総延伸倍率16倍の繊維を得た
。熱セットにより繊維自身の固定を行ない、各繊維を6
■にカットし念。Example 1 Methacrylonitrile 1.5% by weight, 2.5% by weight, 1
0% by weight, 20% by weight, 30% by weight, 35% by weight and acrylonitrile by 98.5% by weight, 97.5% by weight, 90% by weight, 80% by weight, 70% by weight, 65% by weight, respectively.
The copolymers were collected and polymerized by an aqueous suspension polymerization method to obtain six types of copolymers. Each of these copolymers was dissolved in a 68% nitric acid aqueous solution to obtain a spinning stock solution, and then these spinning stock solutions were coagulated in a dilute aqueous solution of nitric acid by a wet spinning method. A fiber with a stretching ratio of 16 times was obtained. The fibers themselves are fixed by heat setting, and each fiber is
Please cut to ■.
上記繊維35部に減水剤(ナフチルスルホン酸ソーダ)
を含浸させる。十分に含浸させた後、余剰の減水剤を絞
り出す。あらかじめセメント(早強ポルトランドセメン
ト):水を3000部ニア50部の割合で混練したもの
に、上記減水剤付着繊維を十分混合分散させる。このも
のを成形金型(15cIn長X4CM巾X1.5m厚)
に流し込み、成形体とする。この成形体を80℃湿空中
で養生し、繊維含有セメント材とした。該セメント材の
物性を次頁の表3に示す。セメント材サンプルの寸法は
、15crn(長さ) X 4.m (幅)Xl、7c
rIt(厚さ)であり、ス・母ン長はlO儒である。Water reducing agent (sodium naphthylsulfonate) added to 35 parts of the above fiber.
Impregnate. After sufficient impregnation, squeeze out excess water reducing agent. Cement (early strength Portland cement): The water reducing agent-attached fibers are thoroughly mixed and dispersed in a mixture of 3,000 parts and 50 parts of water. Use this as a mold (15cIn length x 4CM width x 1.5m thickness)
The mixture is poured into a molded body. This molded body was cured in a humid atmosphere at 80°C to obtain a fiber-containing cement material. The physical properties of the cement material are shown in Table 3 on the next page. The dimensions of the cement material sample are 15 crn (length) x 4. m (width) Xl, 7c
It is rIt (thickness), and its length is IO.
尚、曲げ強度の測定はインストロンTT−OMt−用い
次。又、試験片に対する試験は、7日間硬化さ51後′
行7°1・ 以下余白実施例2
メタクリロニトリルを2.5重量%、10重量%、20
重量%、30重量%、アクリル酸メチルをそれぞれに2
重量%、及びアクリロニトリルをそれぞれ95.5重量
%、88重量%、78重量%、68重量%の組成をもつ
アクリ々糸繊維を実施例1と同様な方法で作成し6wa
に力、トする。簡易抄造装置を用いて試験片を作成する
が、先は上記繊維30部に、それぞれノ’?ルグ80部
、セメント(早強ポルトランドセメント)1000部及
び水2500St−セメントミキサーで15分間混合し
た。この混合物を簡易抄造装置を用い厚さ6簡の板を作
成した(抄造時、サクシ、ン圧200〜300mHgで
行ない、その後は50 kg/crn’で10分間加圧
、その後80℃で養生)。The bending strength was measured using Instron TT-OMt-. In addition, tests on test pieces were conducted after 7 days of curing.
Row 7° 1・ Below margin Example 2 Methacrylonitrile 2.5% by weight, 10% by weight, 20
2% by weight, 30% by weight, and 2% by weight of methyl acrylate, respectively.
Acrylic yarn fibers having compositions of 95.5% by weight, 88% by weight, 78% by weight, and 68% by weight of acrylonitrile, respectively, were prepared in the same manner as in Example 1.
To force, to. A test piece is prepared using a simple paper-making device, and 30 parts of the above-mentioned fibers are each coated with a sample. 80 parts of cement, 1000 parts of cement (early strength Portland cement) and 2500 St of water were mixed for 15 minutes in a cement mixer. A board with a thickness of 6 sheets was made from this mixture using a simple paper-making device (during paper-making, a saccharging pressure of 200 to 300 mHg was applied, and then a pressure of 50 kg/crn' was applied for 10 minutes, followed by curing at 80°C). .
以上により作成した4種類の試験片の曲げ強度及び歪を
測定した。該セメント材の測定結果を次頁の表4に示す
。セメント材サンプルの寸法は、25 cm (長さ)
X 5 cm (幅)xi、5crIt(厚さ)で実
施例3
メタクリコニトリル10重量%とアクリロニトリル90
重量係からなる本発明セメント材に用いているアクリル
系繊維(A)、従来から知られている衣料用アクリル系
繊維(B)、機械的物性及び耐アルカリ性の優れたアク
リル系繊維(C)、及びセメント補強用に使用されてい
るビニロンCD)、のそれぞれを実施例1の方法でセメ
ント複合体とする。これらのセメント複合体を養生する
際に、養生温度を800.110℃、140℃と変えて
、それぞれの複合体を8時間処理した。以上により作成
されたセメント複合体の物性及び繊維自体の物性を表5
に示す。尚、試験片に対する測定は、7日間硬化させ友
後に行なった。The bending strength and strain of the four types of test specimens prepared above were measured. The measurement results for the cement material are shown in Table 4 on the next page. The dimensions of the cement material sample are 25 cm (length)
Example 3: 10% by weight of methacriconitrile and 90% by weight of acrylonitrile
Acrylic fiber used in the cement material of the present invention consisting of a weight factor (A), a conventionally known acrylic fiber for clothing (B), an acrylic fiber with excellent mechanical properties and alkali resistance (C), and Vinylon CD, which is used for cement reinforcement, are each made into a cement composite by the method of Example 1. When curing these cement composites, the curing temperature was changed to 800°C, 110°C and 140°C, and each composite was treated for 8 hours. Table 5 shows the physical properties of the cement composite prepared above and the physical properties of the fiber itself.
Shown below. The test pieces were measured after being cured for 7 days.
Claims (1)
0重量%、アクリロニトリルと共重合可能なビニルモノ
マー5乃至0重量%とアクリロニトリルからなるアクリ
ル系繊維を含有することを特徴とする、繊維により強化
されたセメント材。1. Methacrylonitrile 2.5 to 3 as reinforcing fiber
1. A fiber-reinforced cement material characterized by containing acrylic fibers consisting of 0% by weight, 5 to 0% by weight of a vinyl monomer copolymerizable with acrylonitrile, and acrylonitrile.