JPS61133504A - Colored crosslinked polyethylene insulated wire - Google Patents
Colored crosslinked polyethylene insulated wireInfo
- Publication number
- JPS61133504A JPS61133504A JP25448884A JP25448884A JPS61133504A JP S61133504 A JPS61133504 A JP S61133504A JP 25448884 A JP25448884 A JP 25448884A JP 25448884 A JP25448884 A JP 25448884A JP S61133504 A JPS61133504 A JP S61133504A
- Authority
- JP
- Japan
- Prior art keywords
- crosslinked polyethylene
- colored
- insulated wire
- polyethylene insulated
- colored crosslinked
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。(57) [Summary] This bulletin contains application data before electronic filing, so abstract data is not recorded.
Description
【発明の詳細な説明】
〔発明の技術分野〕
本発明は着色を施した架橋ポリエチレンケーブルに関す
るイ)のである。DETAILED DESCRIPTION OF THE INVENTION [Technical Field of the Invention] The present invention relates to a colored crosslinked polyethylene cable.
色刷のために青色に着色分節した架橋ポリエチレン絶縁
型、線は、顔料とL7て46色性のよいシアンブルー、
フタロシアンブルーナトのシアンブルー系顔料が使用さ
れている。Segmented cross-linked polyethylene insulated type colored blue for color printing, wires are cyan blue with good pigment and L7 color,
Phthalocyan Bluenato cyan blue pigment is used.
トコロカ、シアンブルー系顔料音用いた架橋ポリエチレ
ン絶縁電線は、使用時において短絡事故などが発生した
場合、過電流が流れて絶縁体が損傷に受けるとし1う問
題があった。Cross-linked polyethylene insulated wires using Tokoroka and cyan blue pigments have a problem in that if a short circuit or the like occurs during use, an overcurrent will flow and the insulator will be damaged.
この原因は、架橋ポリエチレンにシアンブルー系顔料を
含有させると、常温(例えば20°C)では機械的(!
l’Wに引張り)強度が充分であるものの高温(例えば
200°C)にさらされると強度が著しく低下するため
と跨えられ、従って短絡事故等が起きた場合に過電流に
より導体近1カの絶縁体は200°C近くまで昇温する
可能性があり、その為、損傷を受けるものと思われる。The reason for this is that when cross-linked polyethylene contains a cyan blue pigment, it becomes mechanical (!
Although the strength is sufficient (tensile to l'W), the strength decreases significantly when exposed to high temperatures (e.g. 200°C). Insulators can be heated to temperatures close to 200°C and are therefore likely to be damaged.
架橋ポリエチレンの高温にJ・・ける機械的強度に−1
−げる方法として、架橋剤の添加1迂全増すという方法
もあるが、押出加−ロ寺にスコーチを起しやすいという
問題がある。その池、補強用として充填剤全添加する方
法もあるが、この方法は押出加工時にトルクが1−昇す
るなど、加工性を芹しく低「・も
することQでなり必ずしも望しいイ、のではない。Mechanical strength of cross-linked polyethylene at high temperatures: -1
As a method of increasing the amount of crosslinking agent, there is a method of increasing the amount of crosslinking agent once or completely, but this method has the problem that scorch is likely to occur during extrusion. There is also a method of adding all the filler for reinforcement, but this method causes a 1-increase in torque during extrusion processing, significantly lowers the processability, and is not necessarily desirable. isn't it.
本発明は、−I−記の点(・こ鑑みて為されたもので、
青色顔料としてAlC10りけ(″、0全0全含機rヒ
合物を用いて着色された架橋ポリエチレンを絶縁体とす
るにJ:す、高温における機械的強度が損われず、過電
流による絶縁体の損傷の無い着色架橋ポリエチレン絶縁
電線全提供するものである。The present invention has been made in view of the points mentioned in -I-.
The insulator is made of cross-linked polyethylene colored with AlC10 as a blue pigment. The present invention provides colored cross-linked polyethylene insulated wires with no damage to the insulation.
〔発明の貝−f・1ζ的説明〕
本発明において導体の外方に設けられる架橋ポリエチレ
ン絶縁体は、ポリエチレンにジクミルパーオキザイド等
の過酸化物全添加し、更にAe若しくはCo全含む無機
青色顔料を添加し、加熱架橋して成るものである。[F.1ζ Description of the Invention] In the present invention, the crosslinked polyethylene insulator provided outside the conductor is made of polyethylene with a total addition of peroxide such as dicumyl peroxide, and an inorganic material containing all of Ae or Co. It is made by adding a blue pigment and crosslinking it by heating.
Al若しくはCo f含む無機青色顔料としては、例え
ば、ケイ酸アルミニウムソーダ(群青)、アルミニウム
酸コバルl−(コバル+−フルー)、スズ酸コバルl−
などが挙げられる。Al 若しくはC。Inorganic blue pigments containing Al or Co f include, for example, aluminum soda silicate (ulmarine blue), cobal aluminate l- (cobal+-flu), cobal stannate l-
Examples include. Al or C.
を含む無機化合物の添加量は、特に限定されないが、0
01〜0,5型槽%で十分に着色し得る。The amount of the inorganic compound added is not particularly limited, but
01 to 0.5 type tank% can provide sufficient coloring.
本発明に係る架橋ポリエチレン絶縁体は、上記無機青色
顔料により着色されたものであるから、シアンブルー系
顔料音用いて着色された絶縁体に比べ、高温における機
械的強度の著しい低下もなく、又架橋剤に増量したり、
充填剤全添加したりすることによりDnT性が損われる
こともない。Since the crosslinked polyethylene insulator according to the present invention is colored with the above-mentioned inorganic blue pigment, there is no significant decrease in mechanical strength at high temperatures compared to an insulator colored with cyan blue pigment. Increase the amount of crosslinking agent,
DnT properties are not impaired by adding all the filler.
尚、本発明にj・・いて、絶縁体に老化防止剤等を適量
添加I〜ても本発明の効果は損われることはない。Incidentally, even if an appropriate amount of an antiaging agent or the like is added to the insulator according to the present invention, the effects of the present invention will not be impaired.
本発明の1−記効果を確認するため、第1表に示す種々
顔料Qでより着色せしめた架橋ポリエチレン絶縁電線を
作成し、それら絶縁体について200°Cで10分間加
熱した後の引張り強度に測定した。In order to confirm the effect described in item 1- of the present invention, cross-linked polyethylene insulated wires colored with various pigments Q shown in Table 1 were prepared, and the tensile strength of these insulators after heating at 200°C for 10 minutes was It was measured.
その結果に第1表に併記する。The results are also listed in Table 1.
実施例1及び2は、比較例2及び3の様に押出時にスコ
ーチが発生することがす<、比較例4.の様に200°
C&でおける引張り強度が低くない。In Examples 1 and 2, scorch may occur during extrusion as in Comparative Examples 2 and 3, and in Comparative Example 4. 200° like
The tensile strength in C& is not low.
尚、比較例及び実施例の絶縁電線は100mm5qの導
体に絶縁体k 1.2 mm厚に施したものに加熱架橋
したものである。The insulated wires of Comparative Examples and Examples were obtained by heating and crosslinking a 100 mm 5 q conductor coated with an insulator k 1.2 mm thick.
Claims (1)
顔料を用いて着色された架橋ポリエチレン絶縁体を設け
て成る着色架橋ポリエチレン絶縁電線。(1) A colored crosslinked polyethylene insulated wire comprising a crosslinked polyethylene insulator colored with an inorganic blue pigment containing Al or Co on the outside of a conductor.