JPS6097531A - Display device - Google Patents

Abstract

PURPOSE:To obtain a display device which can perform displays of high quality and in which any development of warps or cracks is prevented by maintaining the accuracy of the assembly by providing each case with an area to be fused by welding. CONSTITUTION:After a low melting crystalline glass powder 7 is applied between a glass front case 1 and a metallic plate 2, sintering is performed in an electric furnace to fix these members together. In a similar manner, after the low melting crystalline glass powder 7 is applied between a metallic plate 4, a glass frame 3, lead wires 6 made of 42-6 alloy and a glass back plate 5, sintering is performed to fix these members together. Next, an electrode structure is installed in the back base before the electrode terminals are connected to the lead wires 6. Then the front case 1 is placed over the back case before the metallic plates 2 and 4 are welded together by applying a laser beam to their peripheries. After the fusing is completed, exhaustion and backing are performed before sealing is performed at room temperature.

Description

【発明の詳細な説明】 産業上の利用分野 本発明は、表示装置に関するものである。[Detailed description of the invention] Industrial applications The present invention relates to a display device.

従来例の構成とその問題点 従来、プラズマディスプレイ或は螢光表示管等の表示装
置の封着は、粉末ガラスを表容器と裏容器との接合部に
塗布して、４５０’Ｃ〜５００°Ｃ近くに昇温させ封着
を行ってきた。その為に、表示装置内で構成されている
電極、ガラス等の絶縁物などが昇温、降温のサイクルを
通じて、膨張収縮をくり返し、膨張係数の差異、温度分
布の不均一等で構成物の組立が大巾にずれたり、或は、
割れやそり等が発生し、高品位な表示を得ることが極め
て困難な問題点があった。特に、４ｏＯ°Ｃ〜ｓｏｏ”
Ｃにて、粉末ガラスがやや軟化したり、或は、ガラス板
等の変形が一部発生したりすることにその原因がある。Conventional structure and its problems Traditionally, display devices such as plasma displays or fluorescent display tubes were sealed by applying powdered glass to the joint between the front container and the back container, and heating at 450'C to 500°C. Sealing was performed by raising the temperature to near C. For this reason, the electrodes, glass, and other insulating materials that make up the display device expand and contract repeatedly through cycles of temperature rise and fall, and due to differences in expansion coefficients, uneven temperature distribution, etc. deviates from the width, or
There were problems such as cracking and warping, making it extremely difficult to obtain a high-quality display. In particular, 4oO°C ~ soo”
In case C, the cause is that the powdered glass becomes slightly softened or that the glass plate or the like partially deforms.

発明の目的 本発明は、前記従来の欠点を除去するものであり、容器
が溶接により封着される部分を有することにより、組立
精度を維持し、そり、割れ等の発生を防止して高品位な
表示が出来得る表示装置を提供することを目的とするも
のである。さらに他の目的は、より簡便な構成にて安価
に作られる表示装置を提供することを目的とするもので
ある。Purpose of the Invention The present invention eliminates the above-mentioned drawbacks of the conventional art.The container has a part that is sealed by welding, thereby maintaining assembly precision and preventing warping, cracking, etc., and achieving high quality. The object of the present invention is to provide a display device that can display images of various types. Still another object is to provide a display device that can be manufactured at low cost with a simpler configuration.

発明の構成 本発明は、電極構体を収納する容器が溶接手段により封
着されている部分を有するものである。Structure of the Invention According to the present invention, a container housing an electrode assembly has a portion sealed by welding means.

この構成によれば、封着温度を大巾に引き下げられ、こ
れにより、前記表示装置内の温度上昇に伴う電極構体の
位置ずれ、そり２割れ等を低減させることができ、より
高品位な表示を行うことができるものである。According to this configuration, the sealing temperature can be significantly lowered, thereby making it possible to reduce misalignment of the electrode structure, warping, cracking, etc. caused by temperature rise within the display device, and thereby achieving higher quality display. It is something that can be done.

さらに本発明は前記封着されている部分を金属にするこ
とにより、より確実な溶接を行うことができ、製品の歩
留りを大巾に引き上げ、安価に作ることができる。Further, in the present invention, by making the sealed portions metal, more reliable welding can be performed, the yield of the product can be greatly increased, and the product can be manufactured at low cost.

実施例の説明 第１図は本発明の一実施例における表示装置の容器の組
立概観図を示すものである。第２図ａは、第１図の断面
図、第２図すは第２図ａのＡ部の拡大図を示すものであ
る。これらの図において１は表示装置の氷容器、２は氷
容器１に接着された金属板、３は容器の一要素を構成す
る枠体、４は枠体３に接着された金属板、６は枠体３と
共に裏容器を構成する一要素としての裏板、６は容器内
の電極構体からの電極を引出す為のリード線である。DESCRIPTION OF THE EMBODIMENTS FIG. 1 shows an assembled overview of a display device container in an embodiment of the present invention. FIG. 2a is a sectional view of FIG. 1, and FIG. 2 is an enlarged view of section A in FIG. 2a. In these figures, 1 is an ice container of a display device, 2 is a metal plate glued to the ice container 1, 3 is a frame constituting one element of the container, 4 is a metal plate glued to the frame 3, and 6 is a metal plate glued to the ice container 1. A back plate 6, which is an element constituting the back container together with the frame 3, is a lead wire for drawing out the electrode from the electrode assembly inside the container.

また、第２図に示されている７は封着用粉末ガラスであ
る。８はこの実施例での溶接にて封着される部分である
〇 前記容器のより具体的な製造方法を説明する。Moreover, 7 shown in FIG. 2 is powder glass for sealing. 8 is the part sealed by welding in this embodiment. A more specific method of manufacturing the container will be explained.

容器の材料としては、一般によく用いられているガラス
を用い、金属板の４２−６合金（４２％Ｎ１ｔ６％Ｃｒ
、残りＦｅ）と膨張係数が殆んど同一になる様な材質か
ら作られている０例えば、商品化されている螢光表示管
、プラズマディスプレイ等に用いられるものとほぼ同じ
である。あらかじめ、ガラスで出来た外周が２５０　ｍ
ｘ　Ｘ　２００　ｍの大きさで板厚１５叫の氷容器１と
、板厚２００μｍの４２−６合金板をエツチング等で加
工して、内の９寸法が２３０ｍ＋ｎ　Ｘ　１７０ｗｎ、
外周が２８０１１＋ｌｌＸ２４３０ｍｍになる様に中を
取り除いた金属板２との間に低溶融結晶性粉末ガラス７
を塗布して、電気炉等で、４５０’Ｃ位に焼成を行うこ
とにより、氷容器１と金属板２とが接着される。同様に
しで、金属板４とガラス枠体３および、４２−６合金製
のり−ド線６、ガラス製裏板６を低溶融結晶性粉末ガラ
ス７を介して焼成を行うことにより、金属板４．ガラス
枠体３．リード線６．裏板６が接着される。このように
して表示装置の容器として氷容器と裏容器とが準備でき
る。The material for the container is glass, which is commonly used, and a metal plate of 42-6 alloy (42%N1t6%Cr).
For example, it is made of a material whose expansion coefficient is almost the same as that of the remaining Fe), and is almost the same as that used in commercially available fluorescent display tubes, plasma displays, etc. In advance, the outer circumference made of glass is 250 m.
An ice container 1 with a size of x
A low-melting crystalline powder glass 7 is placed between the metal plate 2 whose inside is removed so that the outer circumference is 28011 + 11 x 2430 mm.
The ice container 1 and the metal plate 2 are bonded together by applying and firing the ice container to about 450'C in an electric furnace or the like. Similarly, by firing the metal plate 4, the glass frame 3, the 42-6 alloy glue wire 6, and the glass back plate 6 through the low-melting crystalline powder glass 7, the metal plate 4 ．． Glass frame 3. Lead wire 6. The back plate 6 is adhered. In this way, an ice container and a back container can be prepared as containers for the display device.

次に、前記容器に収納される電極構体についてその基本
的構成の要部分解斜視図である第３図を用いて説明する
。Next, the electrode structure housed in the container will be described with reference to FIG. 3, which is an exploded perspective view of essential parts of its basic configuration.

第３図において、２０は線状熱陰極であって１０〜２０
μφのタングステン線に酸化物陰極材料が塗着されてい
る。２１はコの字形又はＵ字形の隔壁電極であって、各
線状熱陰極前方側を除く周囲を覆うように配置されてお
り、電子ビームを取り出すだめの電極２２と対向し、前
記電極２２に設けられた貫通孔２２ａに高密度の電子ビ
ームが流入するように構成されている。電子ビームを取
り出すための電極２２に穿設される一連の貫通孔２２ａ
は各線状熱陰極に対向して平行に穿設されている。In FIG. 3, 20 is a linear hot cathode, and 10 to 20
An oxide cathode material is applied to a μφ tungsten wire. Reference numeral 21 denotes a U-shaped or U-shaped partition wall electrode, which is arranged so as to cover the periphery of each linear hot cathode except for the front side, and is opposed to the electrode 22 from which the electron beam is taken out. The structure is such that a high-density electron beam flows into the through hole 22a. A series of through holes 22a formed in the electrode 22 for extracting the electron beam
are perforated in parallel and opposite to each linear hot cathode.

２３は複数本の短冊状の電極であって、前記電極２２に
穿されている貫通孔２１ａと同軸に貫通孔２３ａが穿設
されている。電極２４および２５は電子ビームを成形す
るための電極であって前記電極２２および２３に穿設さ
れた貫通孔２２ａおよび２３ａと同軸に貫通孔２４ａお
よび２５ａが穿設されている。電極２ｅけ２θ′と一対
をなして垂直偏向のだめの電極を構成している。同様に
２７および２７′は水平方向の偏向のための電極である
。電極２８は格子状の電極であって電子ビームを加速す
るための電極２９に印加する高電圧の影響が偏向するた
めの電＆２７，２７′に悪影響を及ぼさないための電界
じゃへい用の電極である。23 is a plurality of strip-shaped electrodes, and a through hole 23a is formed coaxially with the through hole 21a formed in the electrode 22. The electrodes 24 and 25 are electrodes for shaping an electron beam, and through holes 24a and 25a are formed coaxially with the through holes 22a and 23a formed in the electrodes 22 and 23. It forms a pair with electrode 2e and 2θ' to form a vertical deflection stopper electrode. Similarly, 27 and 27' are electrodes for horizontal deflection. The electrode 28 is a lattice-shaped electrode, and is an electrode for blocking an electric field so that the influence of the high voltage applied to the electrode 29 for accelerating the electron beam does not have an adverse effect on the electrons &27, 27' for deflection. be.

３１は透明なガラス基板であって、表面に電子ビームの
衝突によって発光する螢光体層３０が塗着されており、
その表面にアルミ薄膜２９が蒸着されており、加速電極
と同時に表示面を構成しているＱ 前記電極構体の各電極の部品精度、および各電極間の組
立精度は、それぞれ部分的に異っているが、約δμｒ→
声ｏμｍ位の範囲に入っている。31 is a transparent glass substrate, on the surface of which is coated a phosphor layer 30 that emits light upon collision with an electron beam;
A thin aluminum film 29 is vapor-deposited on its surface, and forms the display surface at the same time as the accelerating electrode. However, about δμr→
The voice is within the range of 0 μm.

そして、各電極間の固定には、溶接、粉末ガラス。And welding and powder glass are used to fix between each electrode.

ネジ等が用いられている。また電極としては、４２−６
合金板、ＳＵＳ、マコールガラス、セラミック、ガラス
板等が用いられている。Screws etc. are used. Also, as an electrode, 42-6
Alloy plates, SUS, Macor glass, ceramics, glass plates, etc. are used.

この実施例では第３図の電極構体は電極組立後容器に入
れて、２００″Ｃ〜３５０″Ｃ程度以下に抑えることが
可能になった為、組立精度のずれや、部品のそり２割れ
を極力小さく、少くすることができるようになり、高品
位な表示を得ることができる。また、レーザ光線により
、表容器と裏容器とを金属板を介さずに溶接する場合は
、溶接部分を極めて滑らかに平坦性よく表面を仕上げ、
かつ溶接部の位置決めを正確に行った後、レーザ光線を
レンズ系にて、溶接部前後で最小スポット径が得られる
様に調整して、直接的にガラス溶接を行うＯ 前記実施例の様に、金属板を用いて溶接を行うと、溶接
部の変形が容易になり溶接の仕方或は位置等の制約がな
く、シかも、溶接法としても、レーザ光線のみならず、
ガス溶接、電気溶接、イオン、電子ビーム溶接、光ビー
ム溶接等、溶接装置前記電極構体を前記裏容器内に設置
し、各電極端子をリード線６と接続した後、表容器を配
置し金属板２，４の周辺部にレーザ光線をあてて、溶接
を縁に沿って行っていく。このレーザビーム溶接装置と
しては、炭酸ガスレーザ装置或はＹＡＧレーザ装置等何
れでもよい。この浴接による封着後、排気装置と前記表
示装置の容器とを接続し、排気し、電気炉等で２００°
Ｃ〜３５０″Ｃ程度に昇温し来る様になる。In this example, the electrode structure shown in Fig. 3 can be placed in a container after the electrode assembly, and the temperature can be kept below about 200"C to 350"C, which prevents deviations in assembly accuracy and warping of parts. It is now possible to make the display as small and as small as possible, and a high-quality display can be obtained. In addition, when welding the front and back containers using a laser beam without using a metal plate, the surface of the welded area is extremely smooth and flat, and
After accurately positioning the welding area, the laser beam is adjusted with a lens system so that the minimum spot diameter is obtained before and after the welding area, and glass welding is performed directly. When welding is performed using metal plates, the welded part easily deforms, and there are no restrictions on the welding method or position.
Welding equipment such as gas welding, electric welding, ion beam welding, electron beam welding, light beam welding, etc. After the electrode assembly is installed in the back container and each electrode terminal is connected to the lead wire 6, the front container is placed and a metal plate is placed. A laser beam is applied to the periphery of parts 2 and 4, and welding is performed along the edges. This laser beam welding device may be a carbon dioxide laser device, a YAG laser device, or the like. After sealing by this bath welding, the exhaust device and the display device container are connected, evacuated, and heated to 200° in an electric furnace or the like.
The temperature will start to rise to around 350"C.

また、ビーム溶接にては、極めて小さくビームを絞る事
が可能でかつ連続的に溶接できるため、精度よく確実に
出来る効果がある。In addition, in beam welding, the beam can be narrowed down to an extremely small size and welding can be performed continuously, which has the effect of ensuring accurate and reliable welding.

発明の効果 本発明の表示装置は、電極構体を収納する容器が溶接に
より封着される部分をゼすることによりより高品位な表
示をすることができ、その実用的効果は大きい。さらに
、前記封着される部分が金属で構成することにより、よ
り安価に表示装置を提供することができる０Effects of the Invention The display device of the present invention can provide a higher quality display by eliminating the portion where the container housing the electrode assembly is sealed by welding, and its practical effects are significant. Furthermore, since the sealed portion is made of metal, the display device can be provided at a lower cost.

【図面の簡単な説明】[Brief explanation of the drawing]

第１図は、本発明の一実施例における表示装置の容器の
分解斜視図、第２図ａは、第１図の断面崗、第２図すは
第２図ａのＡ部の拡大図、第３図は同容器に収納する電
極構体の分解斜視図である。 １・・・・・・表示装置の表容器、２・・・・・・金属
板、３・・・・・・裏容器の一要素を構成する枠体、４
・・・・・・金属板、６・・・・・・裏容器の一要素を
構成する裏板。FIG. 1 is an exploded perspective view of a container of a display device according to an embodiment of the present invention, FIG. 2 a is a cross-sectional view of FIG. 1, and FIG. 2 is an enlarged view of part A of FIG. FIG. 3 is an exploded perspective view of the electrode assembly housed in the same container. DESCRIPTION OF SYMBOLS 1... Front container of display device, 2... Metal plate, 3... Frame constituting one element of back container, 4
...Metal plate, 6... Back plate constituting one element of the back container.

Claims (1)

【特許請求の範囲】[Claims] （１）　電極構体を収納する容器が溶接手段にて封着さ
れている部分を有することを特徴とする表示装置。 （坤　容器の溶接手段にて封着されている部分が、金属
で構成されていることを特徴とする特許請求の範囲第１
項記載の表示装置。 （→　溶接手段として、レーザ光線等の光ビーム。 電子ビーム、イオンビーム等のビーム溶接手段を用いる
ことを特徴とする特許請求の範囲第１項記載の表示装置
。(1) A display device characterized in that a container housing an electrode assembly has a portion sealed by welding means. (Kon) Claim 1, characterized in that the portion of the container sealed by the welding means is made of metal.
Display device as described in section. (→ The welding means is a light beam such as a laser beam.) The display device according to claim 1, wherein a beam welding means such as an electron beam or an ion beam is used.