JPS60245675A - Antistatic paint - Google Patents

Abstract

PURPOSE:To provide the titled paint which gives a coating film having excellent antistatic performance, wear resistance transparency, etc. by mixing a paint binder consisting of a specified methacrylic copolymer and a polyisocyanate with an electrically conductive powder mainly composed of tin oxide. CONSTITUTION:100-350pts.wt. electrically conductive powder having a particle size of 0.2mum or below and surface resistivity of 10<8>OMEGA/in<2> or below, mainly composed of tin oxide contg. optionally a small quantity of Sb is blended with 100pts.wt. paint binder obtd. by mixing a polyisocyanate contg. at least two isocyanate groups per molecule (e.g. tolylene diisocyanate) and optionally a crosslinking accelerator such as an amine with 100pts.wt. copolymer obtd. by copolymerizing 70-98mol% of methyl methacrylate and 2-25mol% of an active hydrogen-contg. vinyl monomer of formula I or II (wherein R1, R2 are each H, CH3; n is 2, 3; m is 1-10; l is 2-9).

Description

【発明の詳細な説明】 ｌ）産業上の利用分野 本発明は帯電防止用塗料、特に帯電防止機能と透明性を
有し、しかも耐摩耗性、耐薬品性に優れた塗膜を彩成し
うる塗料に関する。[Detailed Description of the Invention] l) Industrial Field of Application The present invention is directed to antistatic coatings, particularly for forming coatings that have antistatic function and transparency, and have excellent abrasion resistance and chemical resistance. Regarding Uru paint.

２）従来技術 帯電防止性を必要とする合成樹脂製建材、シート及び容
器等の部材には、従来、カーボン粉末や金属粉床入し塗
料でコーティングしたり、あるいはカーボン粉末や金属
繊維などを樹脂に練り込んで成形することが行なわれて
いる。しかし、これらの従来法では塗膜又は成形品自体
が着色しているため不透明であり、内容物を透視するこ
とができない。2) Prior art Synthetic resin building materials, sheets, containers, and other components that require antistatic properties have traditionally been coated with paint containing carbon powder or metal powder, or coated with carbon powder or metal fibers in resin. The process is to knead it into a mold. However, in these conventional methods, the coating film or molded product itself is colored and is therefore opaque, making it impossible to see through the contents.

特開昭５７　８５８６６号公報には、透明でかつ帯電防
止機能を有する塗料が開示されている。この塗料は酸化
錫を主成分きする粒Ｐｋ（１２μｍ以下の導電性粉末を
含有してなるが、導電性微粉末を高度に分散させるこ七
が困難であり、従って、樹脂部材にコーティングして得
られる塗膜は透明性および帯電防止機能を安定に発現さ
せることが臀しい。JP-A-57-85866 discloses a paint that is transparent and has an antistatic function. This paint contains conductive powder Pk (12 μm or less) whose main component is tin oxide, but it is difficult to disperse the conductive fine powder to a high degree, so it is necessary to coat the resin member. It is important that the resulting coating film stably exhibits transparency and antistatic function.

３）発明の目的 本発明の目的は、透１η性と帯電防１ヒ作用に優れ、且
つ高い硬度を有し耐摩耗性、耐薬品性に優れた塗膜を形
成し得る塗料を提供することにある。3) Purpose of the Invention The purpose of the present invention is to provide a paint that has excellent permeability and antistatic properties, and is capable of forming a coating film with high hardness and excellent abrasion resistance and chemical resistance. It is in.

４）発明の構成 本発明の要旨はメタクリル酸メチル単量体７０〜９８モ
ル％及び活性水素含有ビニル単量体２〜２５モル％を含
む共重合体１００重景前置ポリインシアネート１〜２５
重量部が添加されてなる塗料バイングー１００重量部傾
対し、酸化錫を主成分とする粒径０．２μｍ以下の導電
性粉末が１００〜３５０重量部の割合で含有されてなる
ことを特徴さする帯電防止用塗料に存する。4) Structure of the Invention The gist of the present invention is a copolymer containing 70 to 98 mol% of methyl methacrylate monomer and 2 to 25 mol% of an active hydrogen-containing vinyl monomer.
100 parts by weight of a coating material containing 100 parts by weight of a conductive powder containing tin oxide as a main component and having a particle size of 0.2 μm or less in a proportion of 100 to 350 parts by weight. Exists in antistatic paints.

上記共重合体及びポリイソシアネートは本発明塗料にお
けるパイングーとして用いられるものであり、共重合体
は、通常の重合法、例えば溶液重合法・乳化重合法・懸
濁重合法・塊状重合法等による上記各単量体の共重合体
であることが多いが、共重合体のケシ化物であってもよ
い、 本発明塗料により形成される塗膜が優れた透明性並びに
硬度を有する為には、上記共重合体中にメタクリル酸メ
チル単景体が７０〜９８モル％含有されていることを必
要とする。The above-mentioned copolymer and polyisocyanate are used as the paint in the coating composition of the present invention, and the copolymer can be prepared by the above-mentioned polymerization method using a conventional polymerization method, such as solution polymerization method, emulsion polymerization method, suspension polymerization method, or bulk polymerization method. It is often a copolymer of each monomer, but it may also be a pycnic copolymer. In order for the coating film formed by the coating of the present invention to have excellent transparency and hardness, the above It is necessary that the copolymer contains 70 to 98 mol% of methyl methacrylate monomer.

又、１ｉｆｉ記活性水活性水素含有ビニル単量ポリイソ
シアネートのインシアネート基と反応する水素を含有す
るものであり、その具体例としては、ヒドロキシエチル
（メタ）アクリレート（これはヒドロキシエチルアクリ
レートとヒドロキシエチルメタクリレート６両方を表わ
す。以下同じ。）、ヒドロキシプロピル（メタ）アクリ
レート、ヒドロキシエチル（メタ）アクリレート、ヒド
ロキシオクチル（メタ）アクリレート、ヒドロキシ２エ
チルヘキシル（メタ）アクリレート等の一般式 ％式％ ） 又はメチル基、ｍけ１〜１ｏの整数を表わす。）で表わ
されるヒドロキシ（メタ）アクリレート：トリエチレン
グリコールモノ（メタ）アクリレート、テトラエチレン
グリコールモノ（メタ）アクリレート、ペンタエチレン
グリコールモノ（メタ）アクリレート、ヘキサメチレン
グリコールモノ（メタ）アクリレート、ヘプタエチレン
グリフールモノ（メタ）アクリレート等の一２　０ 又はメチル基、ｎけ２又は３．１Ｖｉ２〜９の整数を表
わす。）、で表わされるポリアルキレングリコールモノ
（メタ）アクリレート：アクリル酸、メタクリル酸、（
無水）マレイン酸等のビニル重合性カルボン酸が挙げら
れ、ｙｉＫビニルアルコールが包含される。In addition, it contains hydrogen that reacts with the incyanate group of the vinyl monomeric polyisocyanate containing active water active hydrogen, and specific examples thereof include hydroxyethyl (meth)acrylate (this includes hydroxyethyl acrylate and hydroxyethyl acrylate). methacrylate 6 (the same applies hereinafter), hydroxypropyl (meth)acrylate, hydroxyethyl (meth)acrylate, hydroxyoctyl (meth)acrylate, hydroxy2ethylhexyl (meth)acrylate, etc. (%) or methyl group , m represents an integer from 1 to 1o. ) Hydroxy(meth)acrylates represented by: triethylene glycol mono(meth)acrylate, tetraethylene glycol mono(meth)acrylate, pentaethylene glycol mono(meth)acrylate, hexamethylene glycol mono(meth)acrylate, heptaethylene glycol Represents one (20) or a methyl group such as mono(meth)acrylate, n (n) two or an integer from 3.1Vi2 to 9. ), polyalkylene glycol mono(meth)acrylate: acrylic acid, methacrylic acid, (
(anhydride) vinyl polymerizable carboxylic acids such as maleic acid, including yiK vinyl alcohol.

これらの具体例の内、ヒドロキシエチル（メタ）アクリ
レート、ヒドロキシプロピル（メタ）アクリレート、ヒ
ドロキシメチル（メタ）アクリレート等が特に好＊に用
いられる。そして上記共重合体中に用いられる活性水素
・含有ビニル単量体の量は、少な過ぎるとポリイソシア
ネートとの反応による共重合体の網状化が達成されない
為、耐摩耗性の優れた塗膜を得ることが困難であり、又
、メタクリル酸メチルと相俟った導電性粉末の優れた分
散性が発現されない為、塗膜の透明性が低下することと
なる。一方使用量が多過ぎると耐水性や耐薬品性が低Ｆ
する。Among these specific examples, hydroxyethyl (meth)acrylate, hydroxypropyl (meth)acrylate, hydroxymethyl (meth)acrylate, etc. are particularly preferably used. If the amount of active hydrogen/containing vinyl monomer used in the above copolymer is too small, the copolymer will not form a network due to the reaction with the polyisocyanate. It is difficult to obtain, and the excellent dispersibility of the conductive powder in combination with methyl methacrylate is not achieved, resulting in a decrease in the transparency of the coating film. On the other hand, if too much is used, water resistance and chemical resistance will be low.
do.

従って、活性水素含有ビニル単量体は上記共重合体中に
２〜２５モル％含有される。Therefore, the active hydrogen-containing vinyl monomer is contained in the copolymer in an amount of 2 to 25 mol %.

上記共重合体には、メタクリル酸メチル及び活性水素含
有ビニル単量体の他に、更（てその他のビニル単量体が
含有されてもよい。その具体例としてはスチレン、ビニ
ルトルエン等の芳香族ビニル化合物、炭素数ｌ〜８のア
ルキル基を有スる、（メタ）アクリル酸アルキルエステ
ル（メタクリル酸メチルを除り）、（メタ）アクリル酸
ドデシル、（メタ）アクリル酸オクタデシル、酢酸ビニ
ル、塩化ビニル等が挙げられる。In addition to methyl methacrylate and the active hydrogen-containing vinyl monomer, the above copolymer may also contain other vinyl monomers. Specific examples thereof include aromatic aromatics such as styrene and vinyltoluene. Group vinyl compounds, (meth)acrylic acid alkyl esters (excluding methyl methacrylate), having an alkyl group having 1 to 8 carbon atoms, dodecyl (meth)acrylate, octadecyl (meth)acrylate, vinyl acetate, Examples include vinyl chloride.

これらは、二種以上用いられてもよりが、共重合体中に
２８モル％以下の範囲で使用される。Two or more of these may be used in the copolymer in an amount of 28 mol% or less.

本発明に用いられるポリイソシアネートとは１分子中に
２個以上のインシアネート基を有するイソシアネート化
合物を言い、共重合体中の前記活性水素含有−ビニル単
量体と反応して架橋を進行せしめる作用を有し、その具
体例としては、エチレンジイソシアネート、ヘキサメチ
レンジイソシアネート、トリレンジイソシアネート、ナ
フチレン−１，５−ジイソシアネート、ジフェニルメタ
ンジイソシアネート、ジアニシジンジイソシアネート、
トリフェニルメタントリイソシアネート、ポリメチレン
ボリフェニルイソシアネート、及びトリメチロールプロ
パン１モルとトリレンジイソシアネート３モルとの反応
物（例えば日本ポリフレクン工業社より「コロネートし
」として市販されている。）等が挙げられる。ポリイソ
シアネートの上記共重合体への添加ｆｌＦ′！、、共重
合体中に含まれる活性水素含有単量体の割合やポリイソ
シアネートの有するインシアネート基の数等によって適
宜選択されるが、少な過ぎると共重合体の架橋反応が不
充分となり、多過ぎると得られる塗膜が脆くなるので、
共重合体１００重量部に対して１〜２５重量部とされる
。The polyisocyanate used in the present invention refers to an isocyanate compound having two or more incyanate groups in one molecule, and has the effect of reacting with the active hydrogen-containing vinyl monomer in the copolymer to promote crosslinking. Specific examples include ethylene diisocyanate, hexamethylene diisocyanate, tolylene diisocyanate, naphthylene-1,5-diisocyanate, diphenylmethane diisocyanate, dianisidine diisocyanate,
Examples include triphenylmethane triisocyanate, polymethylene polyphenyl isocyanate, and a reaction product of 1 mol of trimethylolpropane and 3 mol of tolylene diisocyanate (for example, commercially available as "Coronate" from Nippon Polyflexen Industries Co., Ltd.). . Addition of polyisocyanate to the above copolymer flF'! , is selected depending on the proportion of the active hydrogen-containing monomer contained in the copolymer, the number of incyanate groups in the polyisocyanate, etc., but if it is too small, the crosslinking reaction of the copolymer will be insufficient, If too much, the resulting coating will become brittle, so
The amount is 1 to 25 parts by weight per 100 parts by weight of the copolymer.

本発明塗料においては前記共重合体に上記ポリイソシア
ネート及び必要によりアミン等の架橋促進剤が添加され
てパイングーとして用いられる。In the coating material of the present invention, the above-mentioned polyisocyanate and, if necessary, a crosslinking accelerator such as an amine are added to the above-mentioned copolymer and used as paint.

本発明塗料に用いられる導電性粉末は、酸化錫を主成分
として含有するものであり、導電性をより高める為をで
、例えば少量のアンチモンが含有されていてもよいが、
透明な塗膜を形成する為にその粒径け０．２μｍ以下、
好ましくけαＩＰｍ以下七される。良好な帯電防止能を
有するＫは、表面固有抵抗率が１０８Ω／口以下である
こさが望ましく、その為ＫＭ導電性粉末のＮは前記バイ
ングー１００重量部に対し１００重量部以上が必要であ
り、好ましくけ１２０重量部以上とされる。又、導電性
粉末の量が多過ぎると分散が不良となって塗膜の透明性
及び平滑性が低下するので前記パイングー１００重量部
に対し３５０重量部以下、好ましくＶｉ３００重景部以
重量範囲で用いられる。The conductive powder used in the paint of the present invention contains tin oxide as a main component, and may contain a small amount of antimony, for example, in order to further increase the conductivity.
In order to form a transparent coating, the particle size is 0.2 μm or less,
Preferably αIPm or less. K, which has good antistatic ability, desirably has a specific surface resistivity of 10 8 Ω/mouth or less. Therefore, the amount of N in the KM conductive powder is required to be 100 parts by weight or more per 100 parts by weight of the above-mentioned baingu. It is preferably 120 parts by weight or more. Furthermore, if the amount of the conductive powder is too large, the dispersion will be poor and the transparency and smoothness of the coating film will be reduced. used.

塗料の調整は、例えば、前記共重合体を有機溶剤に溶解
し次いで酸化錫を主成分とする上記導電性粉末を混合し
、更にポリイソシアネートを加え、必要ならば架橋促進
剤の添加、加熱等の処理を経て行なわれる１、 ル 使用さえ３る溶剤は上記共重合体パイングーを溶解し得
るものであれば何ら特定されず、代表例としてはメチル
エチルケトン、シクロヘキサノン、トルエン、酢酸エチ
ル、エチレングリコールモノメチルエーテル、エチレン
クリコールモノエチルエーテル等が挙げられ、これらけ
適宜混合して用いてもよい。又、導電性粉末を塗料中に
充分分散させるために塗料の分散や配合に通常用いられ
る機器、例えばサンドミル、ボールミル、高速回転攪拌
装置、三木ロールなどが使用され得る。この粉末の分散
をより高めるために、シランカップリング剤、チタネー
トカップリング剤、界面活性剤、オレイン酸、レシチン
などの分散助剤も併用され得る。更に、塗膜の耐久性を
高める為に、紫外線吸収剤、安定剤等を併用してもよい
。Preparation of the paint can be carried out, for example, by dissolving the copolymer in an organic solvent, mixing the conductive powder containing tin oxide as a main component, adding polyisocyanate, adding a crosslinking accelerator if necessary, heating, etc. The solvent used in this process is not specified as long as it can dissolve the above copolymer, and typical examples include methyl ethyl ketone, cyclohexanone, toluene, ethyl acetate, and ethylene glycol monomethyl ether. , ethylene glycol monoethyl ether, etc., and these may be used by appropriately mixing them. Further, in order to sufficiently disperse the conductive powder in the coating material, equipment commonly used for dispersing and blending coating materials, such as a sand mill, a ball mill, a high-speed rotating stirring device, a Miki roll, etc., may be used. In order to further enhance the dispersion of this powder, dispersion aids such as silane coupling agents, titanate coupling agents, surfactants, oleic acid, and lecithin may also be used. Furthermore, in order to increase the durability of the coating film, ultraviolet absorbers, stabilizers, etc. may be used in combination.

このようにして調製された本発明の帯電防止用塗料はス
プレー法、ロールコーク−法、ブローコーター法、バー
コード法、ドクターグレード法、ディッピング法などの
一般的な塗布方法により塗布されるべき対象物に塗布さ
れる。The antistatic paint of the present invention thus prepared is to be applied to a target by a general coating method such as a spray method, a roll coke method, a blow coater method, a bar code method, a doctor grade method, or a dipping method. applied to things.

５）発明の効果 本発明の帯電防止用塗料は、高度に透明性を有しかつ優
れた帯電防止効果を発揮する塗膜を形成しつる。その塗
膜は、硬度１強度および耐擦過性、耐摩耗性、耐薬品性
においても著しく優れている。5) Effects of the Invention The antistatic paint of the present invention forms a coating film that is highly transparent and exhibits an excellent antistatic effect. The coating film is also extremely excellent in hardness 1 strength, scratch resistance, abrasion resistance, and chemical resistance.

６）実施例 塗膜の各物性値の測定は以下の方法によった。6) Examples Each physical property value of the coating film was measured by the following method.

（１）　表面固有抵抗率・・・ＡＳＴＭＤ２５７に準拠
して行った。(1) Surface specific resistivity: Conducted in accordance with ASTM D257.

（２）　全光線透過率・・・・・・ＡＳＴＭＤ１００３
に準拠して行った。(2) Total light transmittance...ASTMD1003
This was done in accordance with the.

（８）　ヘーズ値・・・・・・・・・・・・ＡＳＴＭＤ
１００３に準拠して行った。(8) Haze value・・・・・・・・・ASTMD
1003.

（４）　鉛筆硬度・・・・・・・・・・・・ＪＩＳＫ５
４０１に準拠して行った。(4) Pencil hardness...JISK5
401.

実施例１ 囚　共重合体の合成 冷却管、攪拌機、滴下ロートを備えたセ・！ラブルフラ
スコにトルエン２５００ｙを仕込ミ、窒素ガス気流下で
トルエンの沸点１１０℃まで昇温させた。他方、メタク
リル酸メチル１１２５ｐ（１３，０７モル）、β−ヒド
ロキシエチルメメタリレー）　１２５　ｙ（０，９６モ
ル）そして重合開始剤アゾビスイソブチロニトリル５ｙ
の混合液を調製し、これを滴下ロフトに仕込んでおいた
。フラスコ内のトルエンの温度が１１０℃になった後、
これに滴下ロフトからモノマーと重合開始剤との混合液
を２時間かけて滴下し重合させた。そして、フラスコ内
温度を９０℃にした。次いで、アゾピスイソゾチロニト
リル５２をトルエン２００１ｉＦＫ溶解した液を滴下ロ
フトに仕込み、これを上記フラスコ内へ２時間かけて滴
下した。滴下完ｒ後さらに９０℃で２時間重合を継続し
た。得られた共重合体の重量平均分子量は４５．　ＯＯ
Ｏであり、重合率１１９９％であった。Example 1 Synthesis of copolymer A cell equipped with a cooling tube, a stirrer, and a dropping funnel! A rubble flask was charged with 2,500 y of toluene, and the temperature was raised to the boiling point of toluene, 110° C., under a nitrogen gas flow. On the other hand, methyl methacrylate 1125p (13,07 mol), β-hydroxyethylmethacrylate 125y (0,96 mol) and the polymerization initiator azobisisobutyronitrile 5y
A mixed solution was prepared and placed in the dropping loft. After the temperature of toluene in the flask reached 110℃,
A mixed solution of a monomer and a polymerization initiator was added dropwise to this from a dropping loft over a period of 2 hours to cause polymerization. Then, the temperature inside the flask was set to 90°C. Next, a solution obtained by dissolving azopisisozotyronitrile 52 in toluene 2001iFK was charged into the dropping loft, and this was dropped into the flask over a period of 2 hours. After the dropwise addition was completed, polymerization was continued at 90° C. for 2 hours. The weight average molecular weight of the obtained copolymer was 45. OO
The polymerization rate was 1199%.

（９）　塗料の調製 囚で合成した共重合体溶液９７ｙ１メチルエチルケトン
３２ｙ、）ルエン４８ｙおよび粒径へ１μｍ以下のアン
チモン含有酸化第二錫粉末（三菱金属製、Ｔ−１）６８
ｙをボールミル傾仕い 込んで分散させ、次ヂでポリイソシアネート（日本ポリ
フレタン工業製、コロネートＬ）３Ｆを添加し更に分散
させて目的の塗料を調製した。(9) Copolymer solution synthesized in the preparation of paint 97y1 methyl ethyl ketone 32y) Luene 48y and antimony-containing tin oxide powder with a particle size of 1 μm or less (manufactured by Mitsubishi Metals, T-1) 68
Then, polyisocyanate (Coronate L, manufactured by Nippon Polyurethane Industries) 3F was added and further dispersed to prepare the desired coating material.

（Ｃ）　塗膜の作成及び性能評価 厚さ３ｆｉの透明塩化ビニルプレート上に厚さ１μｍＫ
なるように上記塗料を塗布し、溶剤を乾燥した。得られ
た塗膜の表面固有抵抗率、全光線透過率、ヘーズ値およ
び鉛筆硬度の測定結果を第１表に示した。(C) Preparation of coating film and performance evaluation
The above paint was applied and the solvent was dried. Table 1 shows the measurement results of the surface resistivity, total light transmittance, haze value, and pencil hardness of the resulting coating film.

又、塗膜を室温にて第２表に示す各薬品及び市販の液状
洗剤（罷工石鹸社製、マイペット）に２４時間浸漬した
後に上記と同様の物性値を測定し、その結果を第２表に
示した。In addition, after immersing the coating film at room temperature in each of the chemicals listed in Table 2 and a commercially available liquid detergent (manufactured by Hito Soap Co., Ltd., Mypet) for 24 hours, the same physical property values as above were measured, and the results were reported in the second table. Shown in the table.

実施例２ 実施例１においてβ−ヒドロキシエチルメメタＩＪ　Ｌ
／−ト１２５ｙを用いる代りに１　ヒドロキシプロピル
アクリレート１２５　ｐ　（０，８６８モル）を用いた
以外は実施例１と同様にして共重合体を合成し、塗料を
調整し、塗膜の性能を評価した。結果は第１表、第２表
の通りであった。Example 2 In Example 1, β-hydroxyethyl memetha IJ L
A copolymer was synthesized in the same manner as in Example 1 except that 1 hydroxypropyl acrylate 125 p (0,868 mol) was used instead of 125y, a paint was prepared, and the performance of the coating film was evaluated. did. The results are shown in Tables 1 and 2.

実施例３ 実施例Ｉにおいてβ−ヒドロキシエチルメタクリし・−
ト１２５ｙを用いる代りにヒドロキシブチルアクリレー
ト１２５ｙ（α７９１モル）を用いた以外は実施例１と
同様にして共重合体を合成し、塗料を調整し、塗膜の性
能を評価した。結果は第１表、＠２表の通りであった。Example 3 In Example I, β-hydroxyethyl methacrylate
A copolymer was synthesized in the same manner as in Example 1 except that hydroxybutyl acrylate 125y (α791 mol) was used instead of 125y, a coating material was prepared, and the performance of the coating film was evaluated. The results were as shown in Table 1 and @Table 2.

比較例１ 実施例１のＡにて合成した共重合体溶液１００Ｆ、）ル
エン４８ハメチルエチルケトン３２２及び導電性粉末Ｔ
−１６８ｙからなる塗料を調整し、実施例１と同様にし
て塗膜の性能を評価した。結果は第１表、第２表の通り
てあった。Comparative Example 1 Copolymer solution 100F synthesized in Example 1 A, ) 48 methyl ethyl ketone 322 and conductive powder T
A paint consisting of -168y was prepared, and the performance of the paint film was evaluated in the same manner as in Example 1. The results are shown in Tables 1 and 2.

比較例２ 熱可塑性ポリエステル３０ｙ（東洋紡績社製、パイロン
２００）をｌルエン１２８ｙと／ｆルエチルケトン３２
２との混合液に溶解し、導電性粉末Ｔ−１６８９を添加
分散して塗料を調整した。実施例１と同様にして塗膜の
性能を評価した結果＃−ｉ第１表及び第２表の通りであ
った。Comparative Example 2 Thermoplastic polyester 30y (manufactured by Toyobo Co., Ltd., Pylon 200) was mixed with 128y of luene and 32y of /f ethyl ketone.
2 and conductive powder T-1689 was added and dispersed therein to prepare a paint. The performance of the coating film was evaluated in the same manner as in Example 1, and the results were as shown in Tables 1 and 2 of #-i.

以下余白 第１表 以下余白 第　２　表 注１）各測定値の単位Ｆ′ｉ第１第１同七同ある。Margin below Table 1 Margin below Table 2 Note 1) The unit of each measurement value is F'i.

注２）米は塗膜が剥離したことを表わす。Note 2) Rice indicates that the paint film has peeled off.

特許出願人 積水化学工業株式会社 代表者　藤　沼　基　利patent applicant Sekisui Chemical Co., Ltd. Representative: Mototoshi Fujinuma

Claims (1)

【特許請求の範囲】 Ｌ　メククリル酸メチル単量体７０〜９８モル％及び活
性水素含有ビニル単量体２〜２５モル％を含む共重合体
１００重量部にポリイソシアネート１〜２５重量部が添
加されてなる塗料バイングー１００重量部忙対し、酸化
錫を主成分とする粒径０．２　ｐ　ｑ以下の導電性粉末
がｉｏｏ〜３５０重量部の割合で含有されてなることを
特徴とする帯電防止用塗料。 区　活性水素含有ビニル単量体が一般式％式％（１ 素又はメチル基、ｍけ１〜１０の整数を表わす。）で表
わされるものである第１項記載の帯電防止Ｒ，０ 又はメチル基、ｎけ２又け３，１Ｆｉ２〜９の寮歌を表
わす。） で表わされるものである第１項記載の帯電防止用塗料。[Scope of Claims] 1 to 25 parts by weight of a polyisocyanate is added to 100 parts by weight of a copolymer containing 70 to 98 mol% of L methyl meccrylate monomer and 2 to 25 mol% of an active hydrogen-containing vinyl monomer. An antistatic agent characterized by containing 100 parts by weight of a paint made of paint, and 100 parts by weight of conductive powder containing tin oxide as a main component and having a particle size of 0.2 pq or less. paint. The antistatic R,0 or methyl compound according to item 1, wherein the active hydrogen-containing vinyl monomer is represented by the general formula % (1 element or methyl group, where m represents an integer from 1 to 10). Represents the dormitory songs of Ki, n, 2, 3, 1, Fi 2 to 9. ) The antistatic paint according to item 1, which is represented by: