JPS60244541A - Reflective sheet - Google Patents
Reflective sheetInfo
- Publication number
- JPS60244541A JPS60244541A JP9860584A JP9860584A JPS60244541A JP S60244541 A JPS60244541 A JP S60244541A JP 9860584 A JP9860584 A JP 9860584A JP 9860584 A JP9860584 A JP 9860584A JP S60244541 A JPS60244541 A JP S60244541A
- Authority
- JP
- Japan
- Prior art keywords
- reflective sheet
- layer
- adhesive
- laminated
- fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。(57) [Summary] This bulletin contains application data before electronic filing, so abstract data is not recorded.
Description
【発明の詳細な説明】 〈産業上の利用分野〉 本発明は通気性を有する反射シートに関する。[Detailed description of the invention] <Industrial application field> The present invention relates to a breathable reflective sheet.
〈従来の技術〉
従来、光線や熱線を反射する反射性シートは例えば繊維
基材(二重合体をコーティングし、その上巡ニアルミニ
ウム等反射性の良い金属を真空蒸着法やスパッタリング
加工法じ工9積層しているものや、あるいは5〜30μ
のアルミニウム等の金属微粉末を重合体(二5〜20
wt Qk 混合して繊維製基布砿二コーティングする
方法で作られている0また、数μのガラスピーズを利用
し、前記の方法等(:エフ製造される金属層の上ζ二積
層yる方法も考、案されている。これらの方法(−よる
反射性シートの共通した欠点は通気性を有しない事で、
特(二衣服として着用した際、蒸れ感が大となり夏期に
於ける着用は非常C二不快であった。さら(二、金属微
粉末を重合体(=混合して繊維基材(:コーティングす
る方法でにその製法は容易であるが、光線や熱線の反射
性C−2しく、反射性シートとしての性能は不十分であ
る。また、ガラスピーズな使用する方法では、反射性C
二は優れるものの均−Cニガラスビーズな並べる(ユは
高度な技術を要し、出来た製品に非常C二目付の大きい
重いものであった。<Conventional technology> Conventionally, reflective sheets that reflect light and heat rays have been produced by coating a fiber base material (double composite) and then applying a highly reflective metal such as dialuminum on top of it by vacuum deposition or sputtering. 9 laminated or 5-30μ
Fine metal powder such as aluminum is mixed into a polymer (25 to 20
wt Qk is made by mixing and coating a fiber base fabric with two layers.Also, by using several micron glass beads, two layers are laminated on top of the metal layer manufactured by the above method, etc. Methods have also been considered and proposed.The common drawback of these methods (-) is that they do not have air permeability.
In particular, when worn as clothing, it caused a great stuffy feeling, making it extremely uncomfortable to wear in the summer.Furthermore, fine metal powder was mixed with a polymer (= coated with a fiber base material). Although the manufacturing method is easy, its performance as a reflective sheet is insufficient as it has a C-2 reflectivity for light and heat rays.
Although the second method is excellent, it requires a high degree of skill to arrange the glass beads evenly.
したがってその製造が容易であり、且つ光線や熱!!(
二対する優れた反射性と優れた通気性を併せて具備する
反射性シートは出現していないのが現状である。Therefore, it is easy to manufacture and does not require light or heat! ! (
At present, no reflective sheet has appeared that has both excellent reflectivity and excellent air permeability.
〈発明が解決しようとする問題点〉
本発明は光線や熱線(二対する優れた反射性と優れた通
気性を併せて具備する反射性シー)Y提供することを目
的とする。<Problems to be Solved by the Invention> An object of the present invention is to provide a reflective sheet having both excellent reflectivity and excellent air permeability for light rays and heat rays.
〈問題点を解決するための手段〉
本発明は少くとも接着剤層とその上(二積層された金属
薄層とから成る貼付物が前記接着剤層を内側C二して互
いに独立して多数、通気性ビ有するウェブ状材料の上(
二貼付されていることヲ特徴とする反射性シート(:よ
って達成される0前記ウエブ状材料とじては編物、織物
又は不織布に形成された繊m製基布を用いると好ましい
。<Means for Solving the Problems> The present invention provides a plurality of adhesives consisting of at least an adhesive layer and two laminated metal thin layers thereon, each independently of the other, with the adhesive layer on the inside C2. , on the web-like material with breathable bis(
As the web-like material, it is preferable to use a fiber base fabric formed of knitted fabric, woven fabric, or non-woven fabric.
以下本発明の反射性7−トの具体的構成を順ビ追って説
明するっ
第1図および第2図に本発明の反射シートの一実施例を
示し、第1図は断面図、第2図は平面図である。第1図
(二足すよう(二繊維製基布1の上に接着剤層2、金属
薄層3、および重合体層4が順次積層されて複数の貼付
物5が形成されている0この複数の貼付物5は第1図お
よび第2図で明らかf二足さ3る工う(二相互に独立し
て繊維製基布1上に貼付されている。なお第1図および
第2図(二足した実施PJCおいてに貼付物5の最外側
(二重合体層4が積層されているが、これは金属薄層3
の耐久性増強のためし設けられたもので、あって、本発
明の反射シートとしては必ずしも必須の構成ではない。The specific structure of the reflective sheet of the present invention will be explained in order below. An embodiment of the reflective sheet of the present invention is shown in FIGS. 1 and 2, and FIG. 1 is a cross-sectional view, and FIG. is a plan view. FIG. 1 (2) A plurality of adhesives 5 are formed by sequentially laminating an adhesive layer 2, a thin metal layer 3, and a polymer layer 4 on a base fabric 1 made of two fibers. It is clear in FIGS. 1 and 2 that the attached material 5 is attached to the fiber base fabric 1 independently from each other. In the combined implementation PJC, the outermost side of the patch 5 (the double composite layer 4 is laminated, but this is the metal thin layer 3
This is provided for the purpose of enhancing the durability of the reflective sheet, and is not necessarily an essential configuration for the reflective sheet of the present invention.
又第1図および第2図C二足した実施例では通気性を有
するウェブ状材料として線維製基布が例示されているが
、必ずしも繊維製基布に限定されるものではなく、例え
ば多孔性フィルム等通気性のあるフィルム状材料であっ
てもよい0たソし本発明による反射シートの主要な用途
である衣料用の場合(二に繊維製基布な用いることが好
ましい。In addition, in the combined examples of FIGS. 1 and 2C, a fiber base fabric is illustrated as an air permeable web-like material, but this is not necessarily limited to fiber base fabrics, and for example, porous In the case of clothing, which is the main application of the reflective sheet according to the present invention, it is preferable to use a fiber base fabric.
本発明の反射性シート(二おける繊維凝基布とにポリエ
ステル、ナイロン−6、ナイロン−66アクリル等のけ
成繊維あるいdアセテート等の半盆成繊維、キュプラ、
レーヨン等の再成繊維さら【二、木綿、麻、羊毛等の天
然繊維を一種又は二種以上使用した編物、織物、不織布
でその組織、目付、厚み は特Cユ限定されないが、吸
水性、あるいは吸湿性1−優れ、通気性が大であるIA
維M基布が好ましい。The reflective sheet of the present invention (with a fiber agglomerated fabric in two layers, synthetic fibers such as polyester, nylon-6, nylon-66 acrylic, or half-basin synthetic fibers such as d-acetate, cupro,
Regenerated fibers such as rayon (2) Knitted fabrics, woven fabrics, and non-woven fabrics using one or more types of natural fibers such as cotton, linen, and wool, whose structure, basis weight, and thickness are not particularly limited, but include water absorbency, Or hygroscopicity 1 - IA with excellent moisture absorption and high breathability
A fiber M base fabric is preferred.
本発明の反射シー)における接着剤層とは、ポリウレタ
ン系、ポリアミド系、ポリエステル系、ポリ塩化ビニル
系、ポリビニルアルコール系、ゴム系、シアノアクリレ
ート系、などの重合体で、好ましくはポリアミド系、ポ
リエステル系の接着剤で低融点のものが適L7ておジ、
その樹脂量については5〜4011/rI?が好ましく
、更じl−[7〜15findがエフ好ましい。The adhesive layer in the reflective sheet of the present invention is a polymer such as polyurethane, polyamide, polyester, polyvinyl chloride, polyvinyl alcohol, rubber, or cyanoacrylate, preferably polyamide or polyester. A type of adhesive with a low melting point is suitable for L7.
The amount of resin is 5~4011/rI? is preferable, and 1-[7 to 15find is more preferable.
本発明の反射シート(二おける金属薄層の金属とに光線
および熱線反射性(二重れるアルミニウム、銀、ニッケ
ル、マグネシウム、などが好ましく、中でもコストが安
く、積層の容易なアルミニウムがエフ好ましい0金属薄
層の厚み(二ついては特(:限定されないが、100〜
5oooXが好ましく、さら(二300−100OAが
より好ましい。The reflective sheet of the present invention (aluminum, silver, nickel, magnesium, etc., which have double metal thin metal layers) is preferable, and among them, aluminum is preferable because it is cheap and easy to layer. The thickness of the metal thin layer (not limited to 100~
5oooX is preferred, and 2300-100OA is more preferred.
本発明の反射シートでは、金属薄層の耐久性を増丁為C
:金属薄層の上(二重合体層を積層するのがより好まし
いが、ここでいう重合体層とは、ポリアクリル系重合体
、ポリフッ素系重合体、ぺびポリウレタン系重合体を一
種または二種以上を主体とするものでおる。重合体層の
厚みについては3〜50μが好ましく、さら(:5〜2
0μがより好ましい0厚みが3μ未満では重合体層の強
力が弱く、耐久性(二劣ジ、50μより厚くなると透明
度が悪くなり金属薄層の反射性能が低下しがちとなる為
である。In the reflective sheet of the present invention, the durability of the thin metal layer is increased.
: On top of the metal thin layer (it is more preferable to laminate a double polymer layer, but the polymer layer here refers to one or more polyacrylic polymers, polyfluorine polymers, PEB polyurethane polymers, etc.) The thickness of the polymer layer is preferably 3 to 50μ, and furthermore (:5 to 2μ).
If the thickness is less than 3 μm, the strength of the polymer layer will be weak, and the durability will be poor.
本発明の反射性シートの貼付物は、ウェブ状材料6二接
着剤層、金属薄層、さらに好ましくは重合体層が点状(
二順次積層されて形成されるが、接着剤層、金属薄層、
さらには重合体層がウェブ状材料(二重める面積は、3
0〜90鳴が好ましく、さらC二は50〜70%がより
好ましい。30%Lジ少なくなると反射性に乏しくなり
反射性シートとして性能発揮出来ない。また、通気性C
二ついてはg cc / ssc /−以上が好ましく
、30 cc /sec / cdlDA上がより好ま
しい。通気性がB cc i sec /ltAよす少
ないと、例えば衣服内の湿度が高くなり、蒸れ感、ある
いは発汗現象が生じ易い為である。The reflective sheet paste of the present invention includes a web-like material 6, an adhesive layer, a thin metal layer, and more preferably a polymer layer in the form of dots (
It is formed by laminating two layers in sequence, including an adhesive layer, a thin metal layer,
Furthermore, the polymer layer is a web-like material (the double area is 3
0 to 90% is preferable, and C2 is more preferably 50 to 70%. If the L di is reduced by 30%, the reflective properties will be poor and the reflective sheet will not be able to exhibit its performance. In addition, breathability C
Regarding the second, gcc/ssc/- or more is preferable, and 30 cc/sec/cdlDA or more is more preferable. This is because if the air permeability is less than B cc i sec /ltA, the humidity inside the clothes will be high, and a stuffy feeling or sweating phenomenon will easily occur.
また貼付物の形状(二ついては特に限定されず、円、楕
円などの円型、三角、四角などの角型、あるいに星型な
と任意でそれぞれ独立した形状であれば良く、その大き
さについてに%i’ニー限定はないが長径が0.3〜2
0.0mm程度のものを選定すると好ましい。なお、独
立した形状でなく連続した横縞状、あるいは経編状など
とすれば、反射性シー −トの風合が硬くなり、緯方向
と経方向の曲げ硬さも変わり例えば衣服とする際には適
さない。従ってそれぞれ独立した形状とすれば、風合も
柔らかく、均一な曲げ硬さを有する反射性シートが得ら
れる。In addition, the shape of the adhesive (the two are not particularly limited, but may be any independent shape such as a circle such as a circle or an ellipse, a square shape such as a triangle or square, or a star shape, and the size) There is no limitation on %i' knee, but the major axis is 0.3 to 2.
It is preferable to select one with a diameter of about 0.0 mm. Note that if the reflective sheet is made into a continuous horizontal striped shape or a warp knitted shape instead of an independent shape, the texture of the reflective sheet will become harder, and the bending stiffness in the weft and warp directions will also change. Not suitable. Therefore, if they are formed into independent shapes, a reflective sheet with a soft texture and uniform bending hardness can be obtained.
本発明の反射性シートでは、ウェブ状材料(二接着剤層
、金属薄層、さらC:好ましくは重合体層を独立した形
状で順次積層して貼付物を形成するがその翼体的方法の
1例として以下Cユ示す工程がある。勿論本発明の反射
性シートの製造方法はこれ(二限定されるものではない
。In the reflective sheet of the present invention, a web-like material (two adhesive layers, a thin metal layer, and a polymer layer, preferably a polymer layer) are sequentially laminated in an independent form to form an adhesive. One example is the process shown below.Of course, the method for manufacturing the reflective sheet of the present invention is not limited to this.
第1工程
離型層、つまり離型紙またげポリエステル、ポリプロピ
レン等のフィルムCニシリコン処理したもの等1:、l
!重合体、ナイフコーター、ロールコータ−など(ニエ
クコーティングする。1st step Release layer, that is, film covered with release paper, polyester, polypropylene, etc. treated with silicone, etc. 1:, l
! Coating with polymer, knife coater, roll coater, etc.
第2工程
第1工程で製造したものを十分乾燥後、真空蒸着機また
はスパッタリング加工機へ投入し、金属、例えばアルミ
ニウムを積層加工する。Second Step After sufficiently drying the product manufactured in the first step, it is put into a vacuum evaporation machine or a sputtering machine, and a metal such as aluminum is laminated thereon.
第3工程
繊維製基布ζ:低融点の接着剤を点状にグラビアロール
などを使用して塗布する。Third step fiber base fabric ζ: A low melting point adhesive is applied in dots using a gravure roll or the like.
第4工程
第2工程で製造出来た金属薄層が積層されたシート状物
と、第3工程で製造した繊維製基布C二低融点接着剤を
塗布した物とを貼り合わせ、熱プレスによV繊維基剤と
金属薄層を接着する。4th step: The sheet-like material produced in the 2nd step, in which the thin metal layers are laminated, is pasted together with the fiber base fabric C2 produced in the 3rd step, coated with a low melting point adhesive, and then heated in a hot press. Adhere the V-fiber base and the thin metal layer.
第5工程
第4工程で製造出来た繊維製基布、接着剤、金属薄層、
重合体層、離型層と順次積層されたシート状物のIIJ
!型層、及び接着剤の塗布されていない部分の重合体層
を剥離する。5th process The fiber base fabric, adhesive, metal thin layer produced in the 4th process,
IIJ of a sheet-like product in which a polymer layer and a release layer are sequentially laminated
! Peel off the mold layer and the polymer layer in the areas not coated with adhesive.
以上の様な工程により、繊維製基布(二接着剤層、金属
薄層、重合体層が順次積層され且つ独立して配置された
貼付物を有する反射性シートが製造出来る。なお、金属
薄層の強い耐久性を必要としない時は第1工程を省略す
る事が可能である。また、第5工程で離型層及び接着剤
の塗布されていない部分の重合体層のみを剥離するC二
は、■離型層と重合体層との接着強力、■重合体層の破
断強力、■重合体層と金属薄層との接着強力、■金属薄
層と接着剤との接着強力、■接着剤と繊維製基布との接
着強力、以上のa ”−e間の強力関係を適切(二選定
することが重要であり、本発明の反射性シートを製造す
るC−は次のような強力関係が望ましい。Through the above process, a reflective sheet having a fiber base fabric (two adhesive layers, a metal thin layer, and a polymer layer are successively laminated and independently arranged adhesives) can be manufactured. If strong durability of the layer is not required, the first step can be omitted.Also, in the fifth step, only the part of the polymer layer that is not coated with the release layer or adhesive can be removed. The second is ■ strong adhesion between the release layer and the polymer layer, ■ breaking strength of the polymer layer, ■ strong adhesion between the polymer layer and the thin metal layer, ■ strong adhesion between the thin metal layer and the adhesive, and ■ It is important to appropriately select the adhesion strength between the adhesive and the fiber base fabric, and the strength relationship between a'' and e above. Strong relationships are desirable.
a>b 、b<c 、a<c 、a<d 、age〈実
施例〉
次C:本発明による反射シートの実施例の数的を説明す
る。尚実施例に記載した特性の定義及び測定方法を以下
(−示す。a>b, b<c, a<c, a<d, age <Example> Next C: Numerical explanation of an example of the reflective sheet according to the present invention. The definitions and measurement methods of the characteristics described in the examples are shown below.
0通気性 JIS Ll、096
◎着用感
反射性シートで丸首長袖ブルゾンを縫製し、このブルゾ
ンを綿半袖シャツの上に着用した。ボトムは綿ブリーフ
の上(二綿長ズボンを着用した状態で、30℃ 60%
RHの温湿度下、正面から2@/secの風を受けるよ
うにして30分間立位て着用感を評価した。0 Breathability JIS Ll, 096 ◎ Wearing feeling A round long-sleeved blouson was sewn from a reflective sheet, and this blouson was worn over a cotton short-sleeved shirt. The bottom is over cotton briefs (with two cotton long pants, 30℃ 60%
The wearing feeling was evaluated in a standing position for 30 minutes under RH temperature and humidity with wind blowing at 2@/sec from the front.
◎耐洗濯性
金属薄層の耐久性を洗濯試験で行ない、金属薄層の輝度
低下を視覚判定した。なお洗濯条件は次の通りで、結果
の記号は次の意味を表わす。◎ Washing resistance The durability of the thin metal layer was tested in a washing test, and the reduction in brightness of the thin metal layer was visually judged. The washing conditions are as follows, and the symbols in the results have the following meanings.
洗濯条件
沿 比・・・・・・50:1
洗 剤・・・・・・弱アルカリ性洗剤2g/II時 間
・・・・・・本洗い5分、丁すぎ1o分洗濯機・・・・
・・反転式強水流洗濯根回 数・・・・・・30回繰り
返し
記号の意味
○・・・・・・輝度低下はとんどない
△・・・・・・輝度低下やや見られる
×・・・・・・ I 著しい
実施例1,2.3および4と比較列
それぞれ下記条件で4種類の反射シート(実施例1,2
.3お工び4)を作った。Washing conditions Ratio: 50:1 Detergent: Weak alkaline detergent 2g/II time: 5 minutes of main washing, 1 hour washing machine...
・・Reversal type strong water washing Number of times ・・ 30 times Repeated meaning of the symbol ○ ・ ・ ・ ・ ・ ・ ・ ・ ・ ・ ・ ・ ・ ・ ・ ・ ・ ・ ・ ・ ・ ・ ・ ・ ・ ・ ・ ・ ・ ・ ・ ・ ・ ・・・・・・・ I. Four types of reflective sheets (Examples 1, 2.
.. 3) I made 4).
0実施例10反射シートの製造条件
離型紙にポリアクリルニトリル90wt%、ポリウレタ
ン10wt%の割合で混合した溶液をコマティングし、
乾式凝固した0この重合体層の膜厚は10μでこの上1
ニアルミニウムを真空蒸着法(ユより500Aの膜厚で
積層した。次(:、ナイロン−66トリコツト(組織ハ
ーフ)(二融点94℃のポリアミド樹脂を長径0.8鵬
のほぼ円型の樹脂点がトリコットの生地面積の75俤を
占めるようほぼ均一(−散布した。更蔦:こうして製造
した繊維製基布(トリコット)(ユ接着剤層を積層した
ものと、離型紙≦二重合体層と金属薄層ン積層したもの
とを温度140℃、ルス圧力30(1/−の条件で接着
後、離型紙と接着剤層のない部分の重合体層を剥離し、
反射性シートを製造した。0 Example 10 Manufacturing conditions of reflective sheet A solution of 90 wt% polyacrylonitrile and 10 wt% polyurethane was coated on release paper,
The film thickness of this dry coagulated polymer layer is 10μ, and
Nialuminum was laminated to a film thickness of 500A using a vacuum evaporation method. was dispersed almost uniformly (-) so as to occupy 75 circles of the tricot fabric area. After adhering the laminated metal thin layers at a temperature of 140°C and a Lux pressure of 30 (1/-), peel off the release paper and the polymer layer where there is no adhesive layer,
A reflective sheet was manufactured.
O実施例2の反射シートの製造条件
実施例1と同一条件で、たyし重合体層を設けない点の
み異る反射シートを製造した。Manufacturing conditions for reflective sheet in Example 2 A reflective sheet was manufactured under the same conditions as in Example 1, except that no polymer layer was provided.
〇実施例30反射シートの製造条件
実施例1で得られた離型紙(−重合体層゛、金属薄層を
積層したものとアクリル50%、キュプラ50優の混紡
糸使いのニット(組織スムース)に、融点105℃のポ
リエステル樹脂を、長径1.3 amのはは円型の樹脂
点ηぐニット生地の表面積の70%を占める工うC:は
ぼ均一(−散布したものとを、温度140℃、プレス圧
力300.9/c1dの条件で接着した。しかる後離型
紙と接着剤の付着していない部分の重合体を剥離して反
射性シートを製造した0
0実施例40反射シートの製造条件
離型紙Cニボリ弗化ビニリチン70wt5ポリウレタン
30wt%の割合で混合した溶液をコーティングし、乾
式凝固した。膜厚は10μでこの上Cニアルミニウムを
真空蒸着法(ニエり40OAの膜厚で積層した。次(;
キュグラ織物(組織平織物)C融点94℃のポリアミド
樹脂を長径2.5柵の11は円型の樹脂点が、生地表面
積の60%を占めるようはは均−C−散布1.た。さら
(;繊維基材(−接着剤を積層したものと、重合体層(
−金属薄層を積層したものとを、温度140℃、プレス
圧力300.9/cfflの条件で接着後、離型紙と接
着剤層の塗布されていない部分の重合体層とを剥離し、
反射性シートとした。〇Example 30 Manufacturing conditions for reflective sheet Release paper obtained in Example 1 (-polymer layer, laminated metal thin layer, knit using blended yarn of 50% acrylic and 50% cupro (smooth structure)) A polyester resin with a melting point of 105°C is applied to a circular resin point with a major axis of 1.3 am, which occupies 70% of the surface area of the knit fabric. Adhesion was carried out under the conditions of 140°C and a press pressure of 300.9/c1d.Then, the release paper and the polymer in the areas to which the adhesive was not attached were peeled off to produce a reflective sheet.00Example 40 Reflective sheet Manufacturing conditions Release paper C Nibolyvinyritine fluoride 70wt5 Polyurethane was coated with a mixed solution of 30wt% and dry coagulated.The film thickness was 10μ, and on top of this, Cnialuminum was laminated by vacuum evaporation method (with a film thickness of 40OA). I did.Next(;
Cuglar fabric (textured plain fabric) C polyamide resin with a melting point of 94°C is uniformly dispersed so that the circular resin points 11 on the long diameter 2.5 fence occupy 60% of the fabric surface area.1. Ta. Furthermore, fiber base material (-adhesive layer) and polymer layer (
- After adhering the laminated metal thin layer at a temperature of 140°C and a press pressure of 300.9/cffl, peeling off the release paper and the polymer layer on the part where the adhesive layer is not applied,
It was made into a reflective sheet.
又比較例として実施例1と同一条件で、たyし繊維製基
布C二接着剤層、金属薄層、重合体層を全面じ積層した
ものを用意した。In addition, as a comparative example, a material was prepared under the same conditions as in Example 1, in which two adhesive layers, a thin metal layer, and a polymer layer were laminated over the entire surface of the base fabric C made of tungsten fiber.
各実施例および比較例の反射性シートの通気性、着用感
および耐洗濯性を評価し、その結果を第1表(二示す。The breathability, wearing comfort, and washing resistance of the reflective sheets of each Example and Comparative Example were evaluated, and the results are shown in Table 1 (2).
以下余白 第1表 。Margin below Table 1.
第1表に示す工うC−1比較し1は通気性がなく着用感
も不快である。それζ:対し本発明の反射シートで縫製
された衣服では、通気性(二重れ着用感も快適であった
。また、重合体層を積層しであるもの妹、金属薄層を保
護し、耐洗糊性(二重れている。Compared to C-1 shown in Table 1, C-1 has no breathability and is uncomfortable to wear. On the other hand, clothes sewn with the reflective sheet of the present invention were breathable (and comfortable to wear double-layered).In addition, the laminated polymer layer protects the thin metal layer. Washing and starch resistance (double layered).
〈発明の効果〉
本発明の反射性シー1:前述の↓う(二構成され−てい
るので、金属薄層側を外側C−シて衣Kw縫製丁れば、
太陽などの熱線を受ける場合、その熱線は金属薄層で大
部分反射され、熱線にほとんど人体に影響しない。つ′
iり熱線(二よる体温上昇は最小成じ抑えられ、俸温上
昇4二↓る発汗現象も少なく、エネルギーロスが小さく
なる。また、自動車やバインのライトが衣@−二照射さ
れた場合(二に、ライトの元が金属薄層により反射され
、光源つまり自動車やバインの付近へ元が多く戻る。従
って特に夜間本発明反射性シートからなる衣服を着用す
れば、自動車やバインの運転者へ自分の位置を視認させ
る安全な衣服となる。さら(−1金Ik薄層が積層され
ている部分に通気性を有しないが、金属薄層が積層され
ていない部分は通気性を南する為、衣服内の湿気は通気
性を有する部分から衣服外へ透湿し、夏期(二本発明の
反射性シートで縫製された衣服t・着用した場合でも熱
線、あるいに光線を反射し、かつ、涼しく蒸れない衣服
となる。<Effects of the Invention> Reflective sheet 1 of the present invention: As described above, it is composed of two parts, so if you put the thin metal layer side on the outside and sew the garment,
When exposed to heat rays from the sun, most of the heat rays are reflected by the thin metal layer and have little effect on the human body. tsu'
The rise in body temperature caused by heat rays (2) is minimized, the sweating phenomenon that causes a rise in temperature is reduced, and the energy loss is reduced.Also, when the lights of a car or a vine are irradiated with clothes ( Second, the source of the light is reflected by the thin metal layer, and a large amount of the source of light returns to the vicinity of the light source, that is, the car or van.Therefore, if you wear clothing made of the reflective sheet of the present invention, especially at night, it will be difficult for the driver of the car or van to It is a safe garment that allows you to see your position.Furthermore, the part where the gold Ik thin layer is laminated has no breathability, but the part where the metal thin layer is not laminated has poor breathability. Moisture inside the clothes permeates through the breathable parts to the outside of the clothes, and in summer (2) Clothes sewn with the reflective sheet of the present invention reflect heat rays and light rays even when worn. , resulting in clothes that stay cool and don't get stuffy.
また、金属薄層の上(二重合体層を積層したものは、金
属薄層の耐久性が同上し、洗曜や離粍ζ二強い反射性シ
ートとなる。In addition, when a double composite layer is laminated on top of a thin metal layer, the thin metal layer has the same durability and becomes a reflective sheet that is resistant to peeling and peeling.
なお本発明の反射性シートは前述の衣料用途以外、丁な
わち光線又は熱線に対1−る反射性と通気性を必要とす
る農業用途又は資拐用途等に用いられた場合(ユも優れ
た件能を示す。In addition to the above-mentioned clothing applications, the reflective sheet of the present invention may also be used for agricultural applications or burglary applications that require good reflectivity against light or heat rays and breathability. Indicates the ability to perform.
第1図は本発明の反射シートの一実施例を示す断面図で
あり、第2図は第1図に示した実施例の平面図である。
1・・・・・・繊IIM基布、2・・・・・・接着剤層
、3・・・・・・金属薄層、4・・・・・・重合体層、
5・・・・・・貼付物。
特許出願人
旭化成工業株式会社
特許出願代理人
弁理士 青 木 朗
弁理士 西 舘 和 之
弁理士 山 口 昭 之
弁理士 西 山 雅 也FIG. 1 is a sectional view showing an embodiment of the reflective sheet of the present invention, and FIG. 2 is a plan view of the embodiment shown in FIG. DESCRIPTION OF SYMBOLS 1... Fiber IIM base fabric, 2... Adhesive layer, 3... Thin metal layer, 4... Polymer layer,
5... Paste. Patent applicant: Asahi Kasei Kogyo Co., Ltd. Patent agent: Akira Aoki, patent attorney Kazuyuki Nishidate, patent attorney Akira Yamaguchi, patent attorney Masaya Nishiyama
Claims (1)
とから成る貼付物が前記接着剤層を内側(−して互い(
−独立して多数、通気性を有するウェブ状材料の上口貼
付されていることを特徴とする反射性シート。 2、前記通気性を有するウェブ状材料が編物、織物又は
不織布(二形成された繊維製基布である特許請求の範囲
第1項記載の反射性シート。[Claims] 1. A patch consisting of at least an adhesive layer and two laminated thin metal layers thereon, with the adhesive layer inside (-) and each other (
- A reflective sheet characterized in that a plurality of air permeable web-like materials are independently attached to the top of the sheet. 2. The reflective sheet according to claim 1, wherein the breathable web-like material is a knitted fabric, a woven fabric, or a nonwoven fabric (a fabric made of fibers).