JPS60224737A - Composite aluminum alloy material having superior pitting corrosion resistance - Google Patents
Composite aluminum alloy material having superior pitting corrosion resistanceInfo
- Publication number
- JPS60224737A JPS60224737A JP8061584A JP8061584A JPS60224737A JP S60224737 A JPS60224737 A JP S60224737A JP 8061584 A JP8061584 A JP 8061584A JP 8061584 A JP8061584 A JP 8061584A JP S60224737 A JPS60224737 A JP S60224737A
- Authority
- JP
- Japan
- Prior art keywords
- aluminum alloy
- resistance
- contg
- alloy
- impurities
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【発明の詳細な説明】
［産業上の利用分野１
本発明は耐孔数性に優れたアルミニウム合金複合材に関
し、さらに詳しくは水腐蝕環境において優れた耐孔数性
を有するアルミニウム合金複合材に関する。DETAILED DESCRIPTION OF THE INVENTION [Industrial Application Field 1] The present invention relates to an aluminum alloy composite material with excellent porosity resistance, and more particularly relates to an aluminum alloy composite material with excellent porosity resistance in a water corrosion environment. .
［従来技術１
一般にアルミニウム合金は耐蝕性良好な材料として広く
知られているが、水系媒体と接触して使用される場合に
は、孔線型の腐蝕を生じて短時間で貫通腐蝕を生しる場
合があり、広く一般の水質で実際に使用されているアル
ミニウム合金は現状において殆んどない。[Prior Art 1 Aluminum alloys are generally widely known as materials with good corrosion resistance, but when used in contact with aqueous media, they suffer from hole-linear corrosion and penetrating corrosion in a short period of time. Currently, there are almost no aluminum alloys that are actually used in a wide range of general water conditions.
アルミニウム合金の耐孔数性を向−ヒさせる方法として
は、犠牲陽極層をクラッドしたアルクラッド材、例えば
、ＪＩＳ３００３合金を芯材としてＡｌ−１１１１ｔ％
Ｚｎ合金を皮材としたアルクラッド３００３が良く知ら
れているが、この場合には、アルクラッド層の消耗が天
外かったり、３００３合金芯材に接する部位の７０７２
合金層が選択的に腐蝕されることがあり、安定した耐孔
数性や防蝕スを命が得られるには至っていない。この原
因としては、例えば、７０７２合金は淡水中においては
孔線型の腐蝕を生じ、孔数が３００３合金芯材に達する
と３００３合金芯材に沿って腐蝕が横方向に進行するた
めである。従って、安定した耐孔数性を有するためには
皮材自体の耐孔数性が不可欠となる。As a method to improve the pore resistance of aluminum alloy, an Alclad material clad with a sacrificial anode layer, for example, a JIS 3003 alloy with Al-1111t% as a core material, is used.
Alclad 3003, which is made of Zn alloy as a skin material, is well known, but in this case, the Alclad layer is extremely worn out, and the 7072 layer in contact with the 3003 alloy core material is damaged.
The alloy layer may be selectively corroded, and stable pore resistance and corrosion resistance have not yet been achieved. This is because, for example, 7072 alloy undergoes hole-linear corrosion in fresh water, and when the number of holes reaches the 3003 alloy core material, corrosion progresses laterally along the 3003 alloy core material. Therefore, in order to have stable pore resistance, it is essential that the skin material itself has pore resistance.
アルミニウム合金自体の耐孔数性を向上させる方法とし
て、Ｚｎを含有させることが有効との報告があるが、不
純物として不可避的に混入してくるＦｅを極力規制し、
かつ、混入したＦｅは何等かの方法により有効カソード
としての作用を抑制しなければＺｎを含有させても有効
な耐孔数性を得ることはできない。また、長期にわたり
有効な耐孔数性を保有させるには、それ自体の耐蝕性（
溶出速度）も向上させなければならない。It has been reported that incorporating Zn is an effective way to improve the pore resistance of the aluminum alloy itself, but it is necessary to limit Fe, which inevitably enters as an impurity, as much as possible.
Moreover, unless the effect of the mixed Fe as an effective cathode is suppressed by some method, effective pore resistance cannot be obtained even if Zn is included. In addition, in order to maintain effective pore resistance over a long period of time, it is necessary to have its own corrosion resistance (
elution rate) must also be improved.
［発明が解決しようとする問題点１
本発明は上記に説明したアルミニウム合金の耐孔数性に
ついての知見からなされたものであり、即ち、それ自体
が耐孔数性に優れ相対的に卑な電位を有するアルミニウ
ム合金を皮材とし、また、それ自体耐孔数性に優れ相対
的に責な電位を有するアルミニウム合金を芯材とした、
一般の水質下においても充分な耐孔数性が得られ、がっ
、多目的用途の耐孔数性に優れたアルミニウム合金複合
材を提供するものである。[Problem to be solved by the invention 1 The present invention was made based on the knowledge of the porosity resistance of the aluminum alloy explained above. The skin material is made of an aluminum alloy that has a potential, and the core material is an aluminum alloy that itself has excellent pore resistance and has a relatively negative potential.
The present invention provides an aluminum alloy composite material that has sufficient pore resistance even under normal water conditions and has excellent pore resistance for multipurpose applications.
１問題点を解決するための手段１
本発明に係る耐孔数性に優れたアルミニウム合金複合材
は、
（１） Ｚｎ ０．１−１．Ｏｕ＋１％、Ｍｎ ０．０
５−０．３＋ｕ１％を含有し、かつ、
Ｍ＋＋／Ｆｅ＝ １．５以上
である、残部Ａ１および不純物からなるアルミニウム合
金を皮材とし、
Ｍｎ ０．５−１．５ｗｔ％、Ｃｒ Ｏ，０５−０，５
ｗＬ％を含有し、かつ、
Ｍｎ／Ｆｅ＝５以上
である残部Ａ１および不純物からなるアルミニウム合金
を芯材とすることを特徴とする耐孔数性に優れたアルミ
ニウム合金複合材を第１の発明とし、（２） Ｚｎ Ｏ
，１４，０ｗｔ％、Ｍ ｎ ０．０５−０．３ｗｔ％を
含有し、ｈす、
Ｍ＋＋／ Ｆｃ−１，５以上
である、残部Ａ１および不純物からなるアルミニウム合
金を皮材とし、
Ｍｎ ０．５−１．５ｗｔ％、Ｃｒ Ｏ，０５−０，５
ｗｔ％を含有し、さらに、
Ｃｕ Ｏ，３ＩＩｌｔ％以下、ＭＢ Ｏ，２−２，５ｗ
ｔ％の１種または２種を含有し、がっ、
Ｍｎ／Ｆｅ＝５以上
である残部Ａ１および不純物からなるアルミニウム合金
を芯材とすることを特徴とする耐孔数性に優れたアルミ
ニウム合金複合材を第２の発明とし、（３） Ｚｎ０．
１−１．０ｗｔ％、Ｍｎ Ｏ，０５−０，３ｗｔ％、Ｍ
ｇ０．２〜２．５ｗｔ％
を含有し、かつ、
Ｍｎ／Ｆｅ＝ １．５以上
である、残部Ａ１および不純物からなるアルミニウム合
金を皮材とし、
Ｍｎ ０．５〜１．５ｗｔ％、Ｃｒ Ｏ，０５−０，５
ｗｔ％を含有し、かつ、
Ｍｎ／Ｆｅ＝５以上
である残部Ａ１および不純物からなるアルミニウム合金
を芯材とすることを特徴とする耐孔数性に優れたアルミ
ニウム合金複合材を第３の発明とし、（４） Ｚｎ Ｏ
，１−］、Ｏｗ１％、Ｍｎ ０．０５−０．３ｗｔ％、
Ｍｇ０．２〜２．５ｗｔ％
を含有し、かつ、
Ｍｎ／Ｆｅ＝ １．５以上
である、残部ＡＩおよび不純物からなるアルミニウム合
金を皮材とし、
Ｍｎ Ｏ，５−１，５ｗＬ％、 Ｃｒ Ｏ，０５−０，
５ｗｔ％を含有し、さらに、
Ｃｕ Ｏ，３ｗｔ％以下、Ｍｇ０．２−２．５ｗｔ％の
１種または２種を含有し、がっ、
Ｍｎ／Ｆｅ＝ ５以上
である残部Ａ１および不純物あらなるアルミニウム合金
を芯材とすることを特徴とする耐孔数性に優れたアルミ
ニウム合金複合材を第４の発明とする４つの発明よりな
るものである。1 Means for Solving Problem 1 The aluminum alloy composite material having excellent pore resistance according to the present invention has: (1) Zn 0.1-1. Ou+1%, Mn 0.0
The skin material is an aluminum alloy containing 5-0.3+u1% and M++/Fe=1.5 or more, the balance A1 and impurities, Mn 0.5-1.5wt%, CrO,05 -0,5
A first invention provides an aluminum alloy composite material having excellent pore resistance, characterized in that the core material is an aluminum alloy containing wL% and consisting of the balance A1 with Mn/Fe = 5 or more and impurities. (2) ZnO
, 14.0wt%, Mn 0.05-0.3wt%, h, M++/Fc-1.5 or more, the balance A1 and impurities, the aluminum alloy is used as the skin material, Mn 0.0. 5-1.5wt%, CrO,05-0,5
wt% and further contains CuO,3IIlt% or less, MBO,2-2,5w
An aluminum alloy with excellent pore resistance, characterized in that the core material is an aluminum alloy containing one or two types of t%, the remainder A1 having Mn/Fe = 5 or more, and impurities. A second invention is a composite material, (3) Zn0.
1-1.0wt%, MnO, 05-0.3wt%, M
The skin material is an aluminum alloy consisting of the balance A1 and impurities, containing 0.2 to 2.5 wt% of Mn and Mn/Fe = 1.5 or more, 0.5 to 1.5 wt% of Mn, CrO ,05-0,5
A third invention provides an aluminum alloy composite material having excellent porosity resistance, characterized in that the core material is an aluminum alloy comprising a balance A1 of Mn/Fe=5 or more and impurities. (4) ZnO
,1-], Ow1%, Mn 0.05-0.3wt%,
The skin material is an aluminum alloy containing 0.2 to 2.5 wt% Mg and Mn/Fe = 1.5 or more, the balance being AI and impurities, MnO, 5-1.5wL%, CrO ,05-0,
5wt%, and further contains one or two of CuO, 3wt% or less, Mg0.2-2.5wt%, the remainder A1 having Mn/Fe=5 or more, and impurities. This invention consists of four inventions, with the fourth invention being an aluminum alloy composite material with excellent pore resistance characterized by using an aluminum alloy as a core material.
本発明に係る耐孔数性に優れたアルミニウム合金複合材
について以下詳細に説明する。The aluminum alloy composite material with excellent pore resistance according to the present invention will be described in detail below.
先ず、本発明に係る耐孔数性に優れたアルミニウム合金
複合材における皮材の含有成分および成分割合について
説明する。First, the components and component ratios of the skin material in the aluminum alloy composite material with excellent pore resistance according to the present invention will be explained.
１＋＋はアルミニウム合金の電位を卑に移行させる元素
であり、同時にアルミニウム合金表面の自然酸化皮膜を
付安定に腰腐蝕形態を孔数型から全面腐蝕型にかえる作
用があり、Ｚｎ含有量を増加させると電位は卑に移行し
、腐蝕形態も全面腐蝕型となるが、含有量が多くなり過
ぎると自己腐蝕速度が増大する。従って、Ｚｎ含有量は
自己腐蝕速度を増大させることがなく、腐蝕形態を改善
する範囲として０．１〜１，０ｗ１％とする。1++ is an element that shifts the potential of the aluminum alloy to a base state, and at the same time has the effect of stabilizing the natural oxide film on the surface of the aluminum alloy, changing the form of corrosion from the pore type to the full surface corrosion type, and increases the Zn content. The potential shifts to less noble and the corrosion form becomes full surface corrosion, but if the content becomes too large, the rate of self-corrosion increases. Therefore, the Zn content is set to 0.1 to 1.0w1%, which does not increase the self-corrosion rate and improves the corrosion morphology.
Ｍｕは不純物として不可避的に含有されてくるＡ１６（
ＭｎＦｅ）化合物を固定するので耐孔数性に有効な元素
であり、不純物として含まれるＦｅはＡＩ＝Ｆｅおよび
Ａｌ６Ｆｅとして晶出し、アルミニウム合金に対してカ
ッディックに作用し、その近傍が孔数の核となり耐孔数
性を著しく阻害し、また、アルミニウム合金中にＭｎが
含有されているとＡ１６（ＭｎＦｅ）のＡ１に対する有
効カソードとしての作用はＭｎ／Ｆｅの比により大きく
異なり、Ｍｎ／Ｆｅの比が１．５以上になれば有効カソ
ードとしての作用が着しく抑制される。そして、Ｍｎ含
有量が０，０５ｗｔ％未満では不可避的に混入してくる
Ｆｅの有効カソードとしの作用を充分に抑することがで
きず、また、０．３ｗｔ％を越えて含有されると晶出物
の増大を招き、耐孔数性を向上させることはできない。Mu is unavoidably contained as an impurity in A16 (
It is an effective element for pore resistance because it fixes MnFe) compounds, and Fe contained as an impurity crystallizes as AI=Fe and Al6Fe, which acts caddishly on the aluminum alloy, and its vicinity increases the number of pores. If Mn is contained in the aluminum alloy, the effectiveness of A16 (MnFe) as an effective cathode for A1 will vary greatly depending on the Mn/Fe ratio; When the ratio is 1.5 or more, the effect as an effective cathode is severely suppressed. If the Mn content is less than 0.05 wt%, it will not be possible to sufficiently suppress the effect of Fe, which is inevitably mixed in, as an effective cathode, and if the Mn content exceeds 0.3 wt%, crystallization will occur. This results in an increase in extrusions and makes it impossible to improve the resistance to the number of holes.
さらに、ＭｎはＡ１中に固溶しアルミニウム合金の電位
を貴に移行させ、腐蝕形態を全面腐蝕型とするために必
要なＺｎ含有量が増大し、その結果、耐孔数性が改善す
れば自己腐蝕速度が増大する。従って、Ｍｎ含有量は０
．０５〜０．３ｗｔ％とじ、かつ、Ｍｎ／Ｆｅ＝ １．
５以上とする。Furthermore, Mn dissolves in A1 and shifts the potential of the aluminum alloy to a more noble state, increasing the Zn content necessary to make the corrosion form all-over corrosion, and as a result, the pore resistance improves. Self-corrosion rate increases. Therefore, the Mn content is 0
．． 05 to 0.3 wt%, and Mn/Fe=1.
5 or more.
ＭＢは耐孔数性を低下させずに強度を向上させる元素で
あり、含有量が０．２社％未満では強度向上成分として
有効ではなく、また、２．５Ｉｌｌｔ％を越えて含有さ
れると加工、熱処理等の条件によってはＮ旬Ｚｎ、およ
びｊ＼１５Ｍ８を析出し、腐蝕性を低下させる。従って
、へ旬含有量は０．２〜２．５Ｉｌｌ１％とする。MB is an element that improves strength without reducing porosity resistance, and if the content is less than 0.2%, it is not effective as a strength-improving component, and if it is contained in excess of 2.5%. Depending on processing, heat treatment, and other conditions, N-Zn and J\15M8 may precipitate, reducing corrosivity. Therefore, the hemlock content is set to 0.2 to 2.5 Ill1%.
次に、本発明に係る耐孔数性に優れたアルミニウム合金
複合相における芯材の含有成分および成分割合について
説明する。Next, the components and component ratios of the core material in the aluminum alloy composite phase having excellent pore resistance according to the present invention will be explained.
Ｍｎは不純物のＦｅの有効カソードとしての作用を抑制
するの元素であり、アルミニウム合金中にＺｎが含まれ
る場合にはＺｎの効果によりＭｎ／Ｆｅ比は１．５以上
で、Ｍｎ含有量も０．０５〜０．３で最を良好な耐孔数
性が得られるが、Ｚｎを含まない場合は、Ｆｅの有効カ
ソードとしての作用を効果的に抑制するためには、Ｍｎ
／Ｆｅ比を５以上にすることが必要であり、同時に相対
的に責な電位をアルミニウム合金に付与するにはＭｎ含
有量が０．５ｗｔ％未満ではこのような効果を得ること
ができず、また、Ｍｎ含有量が１，５ｗｔ％を越えて含
有されるとＡｌ６Ｍｎの晶出物が多数生じ、加工性を低
下させ、そして、Ｍｎ量、ｔＡｌ中に固溶した場合にの
みアルミニウム合金の電位を貴に移行させるものである
が、１．５ｕ＋ｔ％を越えて含まれても固溶するＭｎ量
には限りがあるので電位を向上させる効果は飽和してし
まう。従って、相対的に責な電位を有し、耐孔数性に優
れ、かつ、加工性を低下させないＭｎ含有量は０．５−
１．５ｗｔ％とする。Mn is an element that suppresses the effect of impurity Fe as an effective cathode, and when Zn is included in the aluminum alloy, the Mn/Fe ratio is 1.5 or more due to the effect of Zn, and the Mn content is also 0. A value of .05 to 0.3 provides the best pore resistance, but when Zn is not included, in order to effectively suppress the effect of Fe as an effective cathode, Mn
/Fe ratio is required to be 5 or more, and at the same time, in order to impart a relatively negative potential to the aluminum alloy, such an effect cannot be obtained if the Mn content is less than 0.5 wt%, Furthermore, if the Mn content exceeds 1.5 wt%, many Al6Mn crystals will be produced, reducing workability. However, even if the Mn content exceeds 1.5u+t%, the amount of Mn dissolved in solid solution is limited, so the effect of improving the potential becomes saturated. Therefore, the Mn content that has a relatively negative potential, excellent pore resistance, and does not reduce workability is 0.5-
It is set to 1.5 wt%.
ＣｒはＭｎと同様な効果を有するが、含有量が０．０５
＋ｕｔ％未満では有効ではなく、また、０．５ｕ＋ｔ％
を越えて含有されると巨大化合物が生成し、加工性を低
下させる。さらに、ＣｒはＭｎと共に含有されることに
より熱処理等の再結晶時の結晶粒粗大化防止に有効であ
る。従って、Ｃｒ含有量は０．０５〜０．５＋ｕｔ％と
する。Cr has the same effect as Mn, but the content is 0.05
It is not effective below +ut%, and 0.5u+t%
If the content exceeds 100%, giant compounds will be formed and processability will be reduced. Further, when Cr is contained together with Mn, it is effective in preventing coarsening of crystal grains during recrystallization such as heat treatment. Therefore, the Cr content is set to 0.05 to 0.5+ut%.
Ｃｕはアルミニウム合金の電位を貴に移行させる効果と
結晶粒の粗大化を防止するのに有効であり、０．３ｕ＋
Ｌ％を越える含有量では通常の熱処理では耐蝕性を低下
させるので好ましくない。従って、Ｃｕ含有量は０．３
＋ｕｔ％以下する。Cu is effective in shifting the potential of aluminum alloy to a nobler state and preventing coarsening of crystal grains, and is effective at 0.3u+
If the content exceeds L%, it is not preferable because the corrosion resistance decreases in normal heat treatment. Therefore, the Cu content is 0.3
+ut% or less.
Ｍｇは耐蝕性を低下させることなく強度を向上させる元
素であり、アルミニウム合金の耐蝕性を招来せず、強度
向上が図れるＭ８含有量は、０．２〜２．５ｕ＋ｔ％と
する。Mg is an element that improves strength without reducing corrosion resistance, and the M8 content that can improve strength without impairing the corrosion resistance of aluminum alloys is 0.2 to 2.5 u+t%.
そして、上記に説明したように、本発明に係る耐孔数性
に優れたアルミニウム合金複合材においては、皮材自体
が耐孔数性を有するのに加えてそれ自対耐孔数性を持つ
芯材を陰極防蝕するため、耐孔数性は著しく向上し、さ
らに、通常の加工、熱処理を行なってから使用する場合
にはより着しい効果を奏するものである。As explained above, in the aluminum alloy composite material with excellent porosity resistance according to the present invention, in addition to the skin material itself having porosity resistance, it also has porosity resistance to itself. Since the core material is cathodic-protected, the pore resistance is significantly improved, and furthermore, when used after normal processing and heat treatment, even better effects are produced.
［実施例１
本発明に係る耐孔数性に優れたアルミニウム合金複合材
の実施例を説明する。[Example 1] An example of an aluminum alloy composite material with excellent pore count resistance according to the present invention will be described.
実施例１
第１表に示す含有成分および成分割合のアルミニウム合
金を溶製して鋳造し、０．６ｍｎｔのアルミニウム合金
圧延板を作成し、最終熱処理として３６０’ＣＸ１時間
の焼鈍を施して供試材とした。Example 1 An aluminum alloy having the ingredients and proportions shown in Table 1 was melted and cast to create a 0.6 mnt aluminum alloy rolled plate, which was then annealed at 360'C for 1 hour as a final heat treatment and tested. It was used as a material.
これらの供試材を水道水（ｉｔ／ｍｉｎオーバー７０−
）に６ケ月浸漬した。その後腐蝕生成物を除去し、重量
法による腐蝕速度の測定と表面からの顕微鏡焦点深度法
による孔数深さを測定した。These test materials were soaked in tap water (it/min over 70-
) for 6 months. Thereafter, the corrosion products were removed, and the corrosion rate was measured using a gravimetric method, and the depth of the pores was measured using a microscope depth of focus method from the surface.
その結果を第２表に示す通り、本発明に係る耐孔数性に
優れたアルミニウム合金複合材の皮材および芯材は何れ
も良好な耐蝕性、耐孔数性を有していることがわかる。As shown in Table 2, the results show that both the skin and core materials of the aluminum alloy composite material with excellent pore resistance according to the present invention have good corrosion resistance and pore resistance. Recognize.
即ち、Ｎｏ、１〜Ｎｏ、６が本発明に係る耐孔数性に優
れたアルミニウム合金複合相の皮材であって、耐孔数性
に優れ、かつ、相対的に卑な電位を有するアルミニウム
合金であり、皮材として好ましいものであり、また、Ｎ
ｏ、７〜Ｎｏ、１１は同しく芯材であり、耐孔数性に優
れ、かつ、相対的に貴な電位を有するアルミニウム合金
であり、芯材として好ましいものである。なお、Ｎｏ、
］７〜Ｎｏ、２２は比較材である。That is, No. 1 to No. 6 are aluminum alloy composite phase skin materials having excellent pore resistance according to the present invention, and are aluminum having excellent pore resistance and a relatively base potential. It is an alloy and is preferable as a skin material, and also contains N
Nos. o, 7 to 11 are core materials, and are aluminum alloys that have excellent pore resistance and a relatively noble potential, and are preferable as core materials. In addition, No,
] 7 to No. 22 are comparative materials.
実施例２
第２表に示すように、Ｎｏ、４８−Ｎｏ、５３およびＮ
ｏ、６ｆ）〜Ｎｏ、６３のアルミニウム合金複合材（板
厚０．ｈｉｔ、両面複合材、複合率各１０％）を作成し
、３６（１’ｃＸ１時間の熱処理を施しと供試材とした
。Example 2 As shown in Table 2, No., 48-No., 53 and N.
No. o, 6f) to No. 63 aluminum alloy composites (plate thickness 0.hit, double-sided composite material, composite ratio each 10%) were created and heat treated for 36 (1'c x 1 hour) and used as test materials. .
この供試材をｌ （１１１１１１１１のＣｕ”イオンを
含むＡＳＴＭ水（ＣＩ、ＳＯｌ、ＨＣ０３、各１０１０
０ｐｐ中で８０℃×８時間、）ＲＴＸ１６時間の温度サ
イクルで６ケ月間腐蝕試験を実施した。This test material was washed with ASTM water (CI, SOI, HC03, each containing 1010 Cu" ions)
Corrosion tests were carried out for 6 months under a temperature cycle of 80° C. x 8 hours in 0pp, and 16 hours of RTX.
その結果を第２表に示すが、本発明に係る耐孔数性に優
れたアルミニウム合金複合材が比較材に比べて格段に優
れた耐蝕性および耐孔数性を有していることがわかる。The results are shown in Table 2, and it can be seen that the aluminum alloy composite material with excellent pore resistance according to the present invention has significantly superior corrosion resistance and pore resistance compared to comparative materials. .
［発明の効果１
以上説明したように、本発明に係る耐孔数性に優れたア
ルミニウム合金複合材は、耐孔数性に優れており、かつ
、相対的に電位が卑である皮材と耐孔数性に優れており
、かつ、電位が相対的に貴である芯材とより構成されて
いるが呟皮材により芯材が陰極防蝕されるから、耐孔数
性は著しく優れているという効果がある。[Effect of the invention 1 As explained above, the aluminum alloy composite material with excellent pore resistance according to the present invention has excellent pore resistance and has a relatively base potential. It has excellent pore resistance and is composed of a core material with a relatively noble potential, but since the core material is cathodically protected by the skin material, it has extremely high pore resistance. There is an effect.
Claims (3)
−０．３ｕ＋ｔ％を含有し、かつ、 Ｍｎ／Ｆｅ＝ １．５以上 である、残部ＡＩおよび不純物からなるアルミニウム合
金を皮材とし、 Ｍｕ ０．５−］、５ｕ＋１％、Ｃｒ Ｏ，０５−０，
５１１ｔ％を含有し、かつ、 Ｍｎ／Ｆｅ＝ ５以上 である、残部Ａ１および不純物からなるアルミニウム合
金を芯材とすることを特徴とする耐孔蝕性に優れたアル
ミニウム合金複合材。(1) ZnO, 1-1,0wt%, Mn 0.05
-0.3u+t% and Mn/Fe=1.5 or more, the balance is AI and impurities, the aluminum alloy is used as a skin material, Mu 0.5-], 5u+1%, CrO, 05- 0,
An aluminum alloy composite material having excellent pitting resistance, characterized in that the core material is an aluminum alloy containing 511 t% and Mn/Fe=5 or more, the balance A1 and impurities.
０．３ｕ＋ｔ％を含有し、かつ、 Ｍｎ／Ｆｅ＝ １．５以上 である、残部Ａ１および不純物からなるアルミニウム合
金を皮材とし、 Ｍｎ Ｏ，５−］、５Ｉｌｔ％、Ｃｒ Ｏ，０５−０，
５ｗｔ％を含有し、さらに、 Ｃｕ ０．３ｗｔ％以下、Ｍｇ Ｏ，２−２，５ａ＋ｔ
％の１種または２種を含有し、かつ、 Ｍｎ／Ｆｅ＝５以上 である、残部Ａ１および不純物からなるアルミニウム合
金を芯材とすることを特徴とする耐孔蝕性に優れたアル
ミニウム合金複合材。(2) ZnO, ] ~1. OwL%, Mn 0.05~
An aluminum alloy containing 0.3u+t% and Mn/Fe=1.5 or more, the balance A1 and impurities is used as the skin material, MnO,5-], 5Ilt%, CrO,05-0 ，
5 wt%, further Cu 0.3 wt% or less, Mg O,2-2,5a+t
An aluminum alloy composite with excellent pitting resistance, characterized in that the core material is an aluminum alloy containing one or two of Mn/Fe=5 or more, the balance A1 and impurities. Material.
−０．３ｗｔ％、Ｍｇ０．２〜２．５ｗ１％ を含有し、かつ、 Ｍｎ／Ｆｅ＝ １．５以上 である、残部ＡＩおよび不純物からなるアルミニウム合
金を皮材とし、 Ｍｎ ０．５〜１，５ｗｔ％、Ｃｒ Ｏ，０５−０，５
ｗｔ％を含有し、かつ、 Ｍｎ／Ｆｅ＝５以上 である、残部Ａ１および不純物からなるアルミニウム合
金を芯材とすることを特徴とする耐孔蝕性に優れたアル
ミニウム合金複合材。 （＝１ ） Ｚｎ Ｏ，］ ・−１，Ｏｕ＋ｔ％、Ｍｎ
Ｏ，０５−０，３＋ｕｔ％、ＭＢｏ、２へ２．５１％ を含有し、かつ、 Ｍｎ／Ｆｅ＝ １．５以上 である、残部Ａ１および不純物からなるアルミニウム合
金を皮材とし、 Ｍｎ ０．５−１，５ｕ＋ｔ％、Ｃｒ０．０５〜０．５
１１１ｔ％を含有し、さらに、 Ｃｕ０．３田Ｌ％以下、Ｍ２Ｏ，２〜２．５＋ｕｔ％の
１種または２種を含有しかつ、 Ｍｎ／Ｆｅ＝ ５以上 である、残部Ａ１および不純物あらなるアルミニウム合
金を芯材とすることを特徴とする耐孔数性に優れたアル
ミニウム合金複合材。(3) Zn0.1-1.01llt%, Mn 0.05
-0.3wt%, Mg0.2~2.5w1%, and Mn/Fe=1.5 or more, the balance consisting of AI and impurities is used as a skin material, and Mn 0.5~1 ,5wt%,CrO,05-0,5
An aluminum alloy composite material having excellent pitting resistance, characterized in that the core material is an aluminum alloy consisting of the balance A1 and impurities, which contains Mn/Fe=5 or more and has a Mn/Fe ratio of 5 or more. (=1) Zn O, ] ・-1, Ou+t%, Mn
The skin material is an aluminum alloy containing 2.51% of O,05-0,3+ut%, MBo,2 and Mn/Fe=1.5 or more, the balance A1 and impurities, and Mn0. 5-1,5u+t%, Cr0.05-0.5
111t%, further contains Cu0.3% or less, one or two of M2O, 2 to 2.5+ut%, and Mn/Fe=5 or more, the balance consisting of A1 and impurities. An aluminum alloy composite material with excellent pore resistance that uses aluminum alloy as its core material.