JPS5928305A - Inductance element and manufacture thereof - Google Patents
Inductance element and manufacture thereofInfo
- Publication number
- JPS5928305A JPS5928305A JP13893082A JP13893082A JPS5928305A JP S5928305 A JPS5928305 A JP S5928305A JP 13893082 A JP13893082 A JP 13893082A JP 13893082 A JP13893082 A JP 13893082A JP S5928305 A JPS5928305 A JP S5928305A
- Authority
- JP
- Japan
- Prior art keywords
- magnetic
- layer
- inductance element
- patterns
- pattern
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
本発明は、インダクタンス素子とその製造方法に係るも
ので、特に、磁性体と導体を積層することによって周回
するコイルパターンを具えたインダクタンス素子とその
製造方法に関するものである。DETAILED DESCRIPTION OF THE INVENTION The present invention relates to an inductance element and a method of manufacturing the same, and particularly relates to an inductance element having a coil pattern that circulates by laminating a magnetic material and a conductor, and a method of manufacturing the same. .
インダクタンス素子は、導電性線材をコイル状に巻回し
たものが古くから用いられているが、インダクタンスを
上げるためにフェライトのコアなどの磁芯を併せて用い
ている。しかし、電子回路の小形化に伴って電子部品の
小形化の要求も高まっており、インダクタンス素子もそ
の例外ではなイｅ５
い。インダクタンス素子の小形筆他の素子と較べると遅
れているが、大別すると二つの方向で開発が進められて
いる。一つは、基本的には従来のインダクタンス素子の
寸法形状を小さくするものであり、もう一つは印刷方式
等によって固体化するものである。Inductance elements have long been used as coiled conductive wires, but in order to increase inductance, magnetic cores such as ferrite cores are also used. However, with the miniaturization of electronic circuits, the demand for miniaturization of electronic components has also increased, and inductance elements are no exception. Compact inductance elements Although they are behind compared to other elements, development is proceeding in two main directions. One is basically to reduce the size and shape of a conventional inductance element, and the other is to solidify it by a printing method or the like.
印刷方式たよるインダクタンス素子にも様々なタイプが
あるが、インダクタンス値を高くシ、シかも機械的な強
度を高くするために１、絶縁層の上に円弧状のコイル形
成用金属パターンを印刷し、その一端を残してその上に
絶縁層を印刷し、次に乞
金属パターンが端部を接続して形成し、これを繰返して
形成されるものが注目を浴びている。これによって、絶
縁体中に周回するパターンによってコイルを形成するも
のである。印刷する層の数を適宜選択することによって
所望のインダクタンス値を得ることができる。絶縁層を
磁性体で形成す石ことによって、インダクタンス値を上
げることも考えられている。There are various types of inductance elements depending on the printing method, but in order to increase the inductance value and mechanical strength, 1. An arc-shaped metal pattern for forming a coil is printed on the insulating layer. , a method in which an insulating layer is printed on the insulating layer leaving one end intact, and then a metal pattern is formed by connecting the ends, and this process is repeated is attracting attention. Thereby, a coil is formed by a pattern circulating in the insulator. A desired inductance value can be obtained by appropriately selecting the number of printed layers. It is also being considered to increase the inductance value by forming the insulating layer with a magnetic material.
本発明は、上記のような、印刷によって周回導電パター
ンが形成されるインダクタンス素子とその製造方法に関
する本のである。The present invention is a book relating to an inductance element in which a circular conductive pattern is formed by printing, as described above, and a method for manufacturing the same.
印刷によって周回導電パターンを形成するインダクタン
ス素子は、導電パターンの周囲は絶縁体でなければなら
ず、また、インダクタンス値を上げるためには磁性体で
あることが望ましい。そこで１．一般には、導電パター
ンと絶縁性の磁性体層を交互に印刷するものが多く用い
られている。このようにして形成されたインダクタンス
素子において、隣り合う導電パターンの間には磁性体層
が存在することになる。また、電流の向きも同じとなる
ので、部分断面正面図である第１図に示したように、そ
れぞれの導体パターン１１の周囲に同じ向きに磁力ｍ１
２が発生することになる。したパ
かって、二つの導電−ターン１１の間では磁力線の向き
が逆となるので、磁気抵抗が増すことになる。これが、
インダクタンス素子のＱ値の劣化をひき起こす原因どな
っている。In an inductance element that forms a circulating conductive pattern by printing, the area around the conductive pattern must be an insulator, and in order to increase the inductance value, it is preferably a magnetic material. So 1. In general, those in which conductive patterns and insulating magnetic layers are alternately printed are often used. In the inductance element formed in this manner, a magnetic layer exists between adjacent conductive patterns. Also, since the direction of the current is the same, as shown in FIG.
2 will occur. As a result, the direction of the lines of magnetic force becomes opposite between the two conductive turns 11, so that the magnetic resistance increases. This is,
This is the cause of deterioration of the Q value of the inductance element.
本発明は、上記の問題を解決して、磁気抵抗を減少させ
て高いＱ値の得られるインダクタンス装置を提供するこ
とを目的とする。An object of the present invention is to solve the above problems and provide an inductance device that can reduce magnetic resistance and obtain a high Q value.
本発明は、導電パターンの間には非磁性体の層を介在さ
せることによって、上記の目的を達成するものである。The present invention achieves the above object by interposing a nonmagnetic layer between conductive patterns.
以下、図面に従って、本発明の実施例につき、説明する
。Embodiments of the present invention will be described below with reference to the drawings.
第１・図は、本発明によるインダクタンス素子の一例の
正面断面図を示す。フェライトから成る磁性体１３中に
、銀／パラジウムの導体パターン１４が形成され、この
導体パターン１４は周回するコイルパターンを形成して
いる。導体パターン１４０間には非磁性体の絶縁層１５
を具えている。絶織
線層１５は、アルミナ、ステアタイト、二ＪＢ化シリコ
ンなどの非磁性体で形成されており、これらの非磁性体
は誘電率を低くしておくことが望ましい。FIG. 1 shows a front sectional view of an example of an inductance element according to the present invention. A conductor pattern 14 of silver/palladium is formed in a magnetic body 13 made of ferrite, and this conductor pattern 14 forms a rotating coil pattern. A non-magnetic insulating layer 15 is provided between the conductor patterns 140.
It is equipped with The woven wire layer 15 is formed of a nonmagnetic material such as alumina, steatite, and di-JB silicon, and these nonmagnetic materials preferably have a low dielectric constant.
第３図は、本発明によるインダクタンス素子の製造方法
の一例を示す正面断面図である。基体１６上に粉末をメ
チルセルロース、ブチラール樹脂等のバインダー及び溶
剤で練ってペースト状にしたフェライト１７を印刷する
（ハ。このとき、導電パターンを後に形成する部分を除
いた他の部分にフェライト１７を印刷する。とれによっ
て、導電パターンを印刷する領域は、フェライト１７に
よって形成された溝の部分となる。FIG. 3 is a front sectional view showing an example of the method for manufacturing an inductance element according to the present invention. Ferrite 17 is printed on the substrate 16 by kneading the powder with a binder such as methylcellulose or butyral resin and a solvent to form a paste (c. At this time, ferrite 17 is printed on the other parts except for the part where the conductive pattern will be formed later). Print.Due to the cracking, the area where the conductive pattern is printed becomes the groove portion formed by the ferrite 17.
次に、銀−パラジウム合金とバインダーと溶剤からなる
ペースト状の導体１８を印刷する。この印刷は二段階に
分けて行なうと良く、先ず、フェライト１７によって形
成された溝の部分を埋めるように印刷し、更にそれと同
じパターンで同程度の厚さ印刷して、フェライト１７の
厚さの２倍程度と在るようにする（Ｂ）。とれによって
、焼結によって導体１８が収縮し、ても十分な厚さの導
電周回パターンが形成されるようにするものである。Next, a paste-like conductor 18 made of a silver-palladium alloy, a binder, and a solvent is printed. It is best to carry out this printing in two stages. First, print to fill the grooves formed by the ferrite 17, and then print with the same pattern to a similar thickness to match the thickness of the ferrite 17. Make sure it is about twice the size (B). Even if the conductor 18 shrinks due to sintering due to the cracking, a conductive circuit pattern with a sufficient thickness can be formed.
導体１８を印刷した後に、再びフェライト１９を印刷す
るが、この場合にも、二回重ねて印刷するようにして厚
みを大きくしておく（Ｃ）。これによって、再びフェラ
イト１９によって溝が形成された形となる。After printing the conductor 18, the ferrite 19 is printed again, but in this case as well, the thickness is increased by printing twice overlappingly (C). As a result, a groove is again formed by the ferrite 19.
導体１８上のフェライト１９で囲まれｆｃ溝の部分にア
ルミナ等の粉末ペーストから成る非磁性体２０を印刷す
る（Ｄ）。この非磁性体２００表面とフェライト１９の
表面が同一の表面となるように形成する。A non-magnetic material 20 made of powder paste such as alumina is printed in the fc groove surrounded by the ferrite 19 on the conductor 18 (D). The surface of the nonmagnetic material 200 and the surface of the ferrite 19 are formed to be the same surface.
上記のような工程を繰り返して導体パターンを接続しな
がら層を重ねて周回導電パターンを形成する。導体間は
非磁性体で、中心部と周囲は磁性体でそれぞれ構成され
たコイルが得られることになる。The above steps are repeated to connect the conductive patterns and stack the layers to form a circular conductive pattern. A coil is obtained in which the space between the conductors is made of non-magnetic material, and the center and periphery are made of magnetic material.
本発明によれば、積層された導体の間が非磁性体の絶縁
物で形成されているので、磁気回路はフェライトなどの
磁性材内に形成されるようになり導体間の部分には形成
されにくくなる。したがって、導体の磁気抵抗が減少す
るので、周回する導体パターンの抵抗も小さくなり、Ｑ
の値を向上させることができる。According to the present invention, since the space between the laminated conductors is formed of a non-magnetic insulator, the magnetic circuit is formed in the magnetic material such as ferrite, and is not formed between the conductors. It becomes difficult. Therefore, since the magnetic resistance of the conductor decreases, the resistance of the circulating conductor pattern also decreases, and the Q
can improve the value of
また、フェライトなどの磁性体、導体、非磁性体を重ね
て印刷する際に、導体の厚みを十分大きくしたり、確実
に非磁性体を導体゛の上に印刷できるので、製造上の歩
留も向上し、極めて信頼性の高いインダクタンス素子が
得られる。In addition, when printing magnetic materials such as ferrite, conductors, and non-magnetic materials in layers, the thickness of the conductor can be made sufficiently large, and the non-magnetic material can be reliably printed on top of the conductor, improving manufacturing yield. The inductance element is also improved, and an extremely reliable inductance element can be obtained.
前記のように、非磁性体として誘電率の低い物質を用い
れば、導体間の容量も減少させることができるので有利
である。As mentioned above, it is advantageous to use a material with a low dielectric constant as the non-magnetic material because it can also reduce the capacitance between conductors.
第１図は従来のインダクタンス素子の部分正面断面図、
第２図は本発明如よるインダクタンス素子の一例の正面
断面図を示す。また、第３図は本を示す正面断面図であ
る。
１３．１７．１９・・・・・・磁性体。
１４．１８・・・・・・導体。
１５．２０・・・・・・非磁性体
特許出願人
東光株式会社
第 １ 旧
第 ２ 記
第 ３ 図Figure 1 is a partial front sectional view of a conventional inductance element.
FIG. 2 shows a front sectional view of an example of an inductance element according to the present invention. Moreover, FIG. 3 is a front sectional view showing the book. 13.17.19...Magnetic material. 14.18... Conductor. 15.20...Non-magnetic material patent applicant Toko Co., Ltd. No. 1 Old No. 2 No. 3 Figure 3
Claims (2)
れて、絶縁層間を一周′回してコイルパターンが形成さ
れたインダクタンス素子において、周回する導電層間に
非磁性体の絶縁層を具え、その他の絶縁層が磁性体から
成ることを特徴とするインダクタンス素子。(1) In an inductance element in which a conductive layer and an insulating layer are sequentially formed by a printing method, and a coil pattern is formed by making one circuit between the insulating layers, an insulating layer of a non-magnetic material is provided between the circulating conductive layers, and other An inductance element characterized in that an insulating layer is made of a magnetic material.
を印刷し、該磁性体層によって形成てれる溝に導電層を
印刷して更に同じパターンで導電層を形成し、該導電層
によって形成される溝に磁性体層を印刷して更に同じパ
ターンで磁性体層を形成し、該磁性体層によって形成さ
れる溝に非磁性体の絶縁層を形成し、この工程を反復す
ることによって周回するコイルパターンを得ることを特
徴とする特許請求の範囲第１項記載のインダクタンス素
子の製造方法。(2) Print a magnetic layer on the substrate excluding the printed pattern of the conductive layer, print a conductive layer in the grooves formed by the magnetic layer, further form a conductive layer with the same pattern, and then print the conductive layer in the grooves formed by the magnetic layer. Print a magnetic layer in the grooves formed by the magnetic layer, further form a magnetic layer in the same pattern, form a non-magnetic insulating layer in the grooves formed by the magnetic layer, and repeat this process. 2. The method of manufacturing an inductance element according to claim 1, wherein a circulating coil pattern is obtained.