JPS59225948A - Elastomer coated cloth joined body - Google Patents
Elastomer coated cloth joined bodyInfo
- Publication number
- JPS59225948A JPS59225948A JP58099510A JP9951083A JPS59225948A JP S59225948 A JPS59225948 A JP S59225948A JP 58099510 A JP58099510 A JP 58099510A JP 9951083 A JP9951083 A JP 9951083A JP S59225948 A JPS59225948 A JP S59225948A
- Authority
- JP
- Japan
- Prior art keywords
- elastomer
- coated
- silicone
- fabric
- cloth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。(57) [Summary] This bulletin contains application data before electronic filing, so abstract data is not recorded.
Description
【発明の詳細な説明】
本発明は、エラストマー被覆布接合体に関するものであ
る。DETAILED DESCRIPTION OF THE INVENTION The present invention relates to an elastomer-coated fabric assembly.
エラストマー被覆布は、従来から防水布、ダイビングス
ーツ、ベルト、防火カーテンなどとして使用されている
が、最近は競技場、体育館、屋外レストラン等の屋根材
として使用することが提案されている。Elastomer-coated fabrics have traditionally been used as waterproof fabrics, diving suits, belts, fire curtains, etc., but recently it has been proposed to be used as roofing materials for stadiums, gymnasiums, outdoor restaurants, etc.
エラストマー被覆布は、製造技術上あまり大面積なもの
を製造することは困ｆｆ１ｔである。しかし、エラスト
マー被覆布を建造物の屋根替りに使用するときや、大規
模なテント材料として使用するときは大面積を必要とす
るので、工場で製造した比較的小面積のものを多数接合
することが必要となる。Due to manufacturing technology, it is difficult to manufacture elastomer-covered cloth with a large area. However, when using elastomer-covered fabric as a roof for a building or as a material for a large-scale tent, a large area is required, so it is necessary to join together a large number of relatively small-area fabrics manufactured in a factory. Is required.
布と布を接合するときは、布の端部同士を積層して縫製
する方法が一般的である。小面積の重接合体を目的とす
る場合は、こうした接合方法で通常十分である。しかし
、建造物の屋根替りに使用したり、大規模なテント材料
のような大面積の重接合体を目的とする場合は、布の端
部同士を積層して縫製するだけでは強度的にも水密性の
点でも問題がある。重力や風圧に起因する引張応力が縫
糸周辺部に集中して、該周辺部が破壊されやすくなった
り、該積層部分の隙間を通して雨水や風塵が侵入するか
らである。When joining cloth to cloth, it is common to laminate the ends of the cloths and sew them together. If a small-area heavy conjugate is desired, this joining method is usually sufficient. However, if the purpose is to use it as a roof for a building or to make a large-area heavy joint such as a large-scale tent material, simply laminating the ends of the cloth and sewing them together is insufficient for strength. There is also a problem with watertightness. This is because tensile stress caused by gravity and wind pressure concentrates around the sewing thread, making the surrounding area more likely to be destroyed, and rainwater and wind dust entering through gaps in the laminated portion.
本発明の目的は上述の問題に鑑み、強力で且つ水密性、
気密性よく接合されたエラストマー被覆布接合体を提供
せんとすることにある。In view of the above-mentioned problems, the object of the present invention is to provide a strong, watertight,
It is an object of the present invention to provide an elastomer-coated fabric bonded body that is bonded with good airtightness.
上記目的を達成する本発明によるエラストマー被覆布接
合体は、互いに隣接するエラストマー被覆布の端部同士
を、両端部の間に感圧接着剤を介在させて積層接着し、
−力のエラストマー被覆布の前記積層部分と他方のエラ
ストマー被覆布の非積層部分との両面に芦るように粘着
テープを貼着させたことを特徴とするものである。An elastomer-coated fabric bonded body according to the present invention that achieves the above object includes laminating and bonding the ends of adjacent elastomer-covered fabrics with a pressure-sensitive adhesive interposed between the two ends,
- Adhesive tapes are affixed to both surfaces of the laminated portion of the elastomer-coated fabric and the non-laminated portion of the other elastomer-coated fabric.
本発明において使用するエラストマー被覆布は、エラス
トマーが布を被覆しており、かつエラストマーと布とが
一体化したものであれば特に限定されるものではない。The elastomer-coated cloth used in the present invention is not particularly limited as long as the elastomer covers the cloth and the elastomer and the cloth are integrated.
エラストマー被覆布を構成するエラストマーとしては、
天然ゴム。The elastomers that make up the elastomer-covered fabric include:
natural rubber.
合成ゴム、熱可塑性エラストマーのいずれでもよい。合
成ゴムとしては、ＳＢＲ，ＮＢＲ，ＥＰＲ，ＥＰＤＭ、
クロロプレンゴム、アクリルゴム、シリコーンゴム等
が適用可能である。屋外で使用される大面積の接合体を
目的とする場合は、上記合成ゴム、特にシリコーンゴム
が好ましい。このシリコーンゴムとしては、有機過酸化
物加硫型、付加反応硬化型及び室温硬化型が適用できる
。またこのシリコーンゴムは、その表面にシリコーンレ
ジンの薄層を積層一体化したものであってもよい。Either synthetic rubber or thermoplastic elastomer may be used. Synthetic rubbers include SBR, NBR, EPR, EPDM,
Chloroprene rubber, acrylic rubber, silicone rubber, etc. are applicable. When the purpose is a large-area bonded body to be used outdoors, the above-mentioned synthetic rubbers, particularly silicone rubbers, are preferred. As this silicone rubber, organic peroxide vulcanization type, addition reaction curing type and room temperature curing type can be applied. The silicone rubber may also have a thin layer of silicone resin laminated on its surface.
エラストマー被覆布を構成する布としては、織物１編物
、不織布、網及びそれらの積層品のいずれでもよい。こ
れらを構成する繊維としては、天然繊維、半合成繊維２
合成繊維及び無機繊維が使用できる。屋外で使用される
大面積の接合体を目的とする場合は、耐候性のすぐれた
合成繊維布、例えばポリエステル繊維織物、あるいは無
機繊維布、例えばガラス繊維布、金属繊維布が好ましい
。また、体育館、競技場、テニスコート、屋外レストラ
ンなどの外装材料であって自然光の活用を目的とする場
合、即ち空気膜構造物用の膜を目的とする場合は、光透
過性の大きな繊維を使用した布や、繊維の目付の小さい
空隙を有する織組織又は編組織にした布が好ましい。The fabric constituting the elastomer-coated fabric may be any of a woven fabric, a nonwoven fabric, a net, and a laminate thereof. The fibers that make up these include natural fibers, semi-synthetic fibers2
Synthetic and inorganic fibers can be used. When a large-area bonded body to be used outdoors is intended, synthetic fiber cloth with excellent weather resistance, such as polyester fiber cloth, or inorganic fiber cloth, such as glass fiber cloth or metal fiber cloth, is preferable. In addition, when the purpose is to utilize natural light as an exterior material for gymnasiums, stadiums, tennis courts, outdoor restaurants, etc., in other words, when the purpose is to use membranes for air membrane structures, fibers with large light transmittance are used. It is preferable to use a woven fabric or a knitted fabric having small voids and a fiber basis weight.
エラストマー被覆布の形状、厚み、大きさく面積）は特
に限定されるせのではないが、平面形状としては正方形
、長方形、三角形１台形などが適用可能であり、厚みと
しては、０．１〜５ｍｍが好ましい。また、適用可能な
平面の大きさとしては１００ａｌｌ〜５０ｎ（が好まし
い。The shape, thickness, size and area of the elastomer-coated cloth are not particularly limited, but square, rectangular, trapezoidal triangles, etc. are applicable as the planar shape, and the thickness is 0.1 to 5 mm. is preferred. Further, the applicable plane size is preferably 100all to 50n.
粘着テープは、テープ片面に粘着剤を積層したものであ
る。基材となるテープとしてはプラスチックフィルムテ
ープ、例えばポリテトラフルオロエチレンフィルムテー
プ、ポリエステルフィルムテープ、ポリプロピレンフィ
ルムテープ、フェス含浸布テープ、例えばシリコーンワ
ニス含浸ガラス布テープ、円ラストマー被覆布テープ、
例えばシリコーンエラストマー被覆ガラス布テープなど
が好適である。屋外で使用される大面積の重接合体を目
的とする場合は、シリコーン粘着剤を使用したポリテト
ラフルオロエチレンフィルムチーブ、又はシリコーン硬
化体被覆熱ｔａ繊維布テープが好ましい。Adhesive tape has an adhesive layered on one side of the tape. The base material tapes include plastic film tapes such as polytetrafluoroethylene film tapes, polyester film tapes, polypropylene film tapes, festival-impregnated cloth tapes such as silicone varnish-impregnated glass cloth tapes, circular elastomer-coated cloth tapes,
For example, a glass cloth tape coated with a silicone elastomer is suitable. When the purpose is a large-area heavy bonded body to be used outdoors, a polytetrafluoroethylene film film using a silicone adhesive or a thermal TA fiber cloth tape coated with a silicone cured material is preferable.
粘着テープを構成する粘着剤としては、粘着力が強いも
のが好ましく、ゴム系粘着剤、ビニル系粘着剤、アクリ
ル系粘着剤、シリコーン系粘着剤が好ましい。特に、屋
外で使用される大面積の接合体を目的とする場合は、シ
リコーン系粘着剤が好ましい。The adhesive constituting the adhesive tape is preferably one with strong adhesive strength, and rubber-based adhesives, vinyl-based adhesives, acrylic-based adhesives, and silicone-based adhesives are preferred. In particular, silicone-based adhesives are preferred when the purpose is a large-area bonded body to be used outdoors.
エラス１−マー被覆布の端部同士の間に介在させる感圧
接着剤としては、非硬化型、硬化型のいずれでもよいが
、好ましくは硬化型が望ましい。また無溶剤型、溶液型
、ホットメルト型のいずれでもよい。このような感圧接
着剤としては、接着力の強いビニル系感圧接着剤、ゴム
系感圧接着剤、アクリル系感圧接着剤、シリコーン系感
圧接着剤が好ましい。特に屋外で使用される大面積の接
合体を目的とする場合は、シリコーン系感圧接着剤が好
適である。The pressure-sensitive adhesive interposed between the ends of the elastomer-coated fabric may be either a non-curing type or a curable type, but a curable type is preferred. Moreover, any of solvent-free type, solution type, and hot melt type may be used. As such a pressure-sensitive adhesive, a vinyl-based pressure-sensitive adhesive, a rubber-based pressure-sensitive adhesive, an acrylic-based pressure-sensitive adhesive, or a silicone-based pressure-sensitive adhesive, which have strong adhesive strength, are preferable. Particularly when the purpose is a large-area bonded body to be used outdoors, silicone-based pressure-sensitive adhesives are suitable.
以下、本発明のエラストマー被覆布接合体を図に示す実
施例により説明する。DESCRIPTION OF THE PREFERRED EMBODIMENTS The elastomer-coated fabric assembly of the present invention will be explained below using examples shown in the drawings.
第１図及び第２図に示す本発明のエラストマー被覆接合
体において、１は一方のエラストマー被覆布、２は他方
のエラストマー被覆布である。両エラストマー被覆布１
．２とも、上述したように編織物等からなる布１ａ、２
ａを内部に有し、その外側をエラストマー１ｂ、２ｂで
被覆され、非通気性のシートを構成している。In the elastomer-coated assembly of the present invention shown in FIGS. 1 and 2, 1 is one elastomer-coated fabric, and 2 is the other elastomer-coated fabric. Both elastomer coated fabrics 1
．． Both of the cloths 1a and 2 are made of knitted fabric or the like as described above.
a inside, and the outside thereof is covered with elastomers 1b and 2b, forming a non-breathable sheet.
このエラストマー被覆布１，２ばそれぞれの端部同士を
、その間に感圧接着剤３を介在させて互いに積層接着さ
れている。このように端部同士が互いに積層かつ接着さ
れた部分において、エラストマー被覆布１例の積層部分
の表面と、エラストマー被覆布２側の非積層部分の表面
との間に跨るように、粘着テープ４が貼着している。同
様に、反対側の面に対しても、粘着テープ５がエラスト
マー被覆布２側の積層部分の表面とエラストマー被覆布
１側の非積層部分の表面との間に跨るように貼着されて
いる。この粘着テープ４．５は、それぞれテープ基材４
ａ。The end portions of the elastomer coated cloths 1 and 2 are laminated and bonded to each other with a pressure sensitive adhesive 3 interposed therebetween. At the portion where the end portions are laminated and adhered to each other in this way, apply the adhesive tape 4 so as to span between the surface of the laminated portion of one example of the elastomer-coated fabric and the surface of the non-laminated portion on the elastomer-coated fabric 2 side. is attached. Similarly, on the opposite side, an adhesive tape 5 is attached so as to span between the surface of the laminated portion on the elastomer-covered fabric 2 side and the surface of the non-laminated portion on the elastomer-covered fabric 1 side. . This adhesive tape 4.5 has a tape base material 4.
a.
５ａの片面に粘着剤４ｂ、５ｂを塗布して構成され、こ
の粘着剤４ｂ、５ｂ側を上記エラス１−マー被覆布１．
２の表面に貼着させている。5a is coated with adhesives 4b and 5b, and the adhesives 4b and 5b side is coated with the elastomer-coated cloth 1.
It is attached to the surface of 2.
勿論、上述した粘着テープは、用途により両エラストマ
ー被覆布１，２の片面だけでもよいが、特に屋外用途の
ように大面積にして使用する場合は、接合強度、接合安
定性あるいは水蜜性、気密性の向上等の点から上記実施
例のように表裏両面に貼着するようにすることが好まし
い。Of course, the above-mentioned adhesive tape may be used on only one side of both elastomer-covered fabrics 1 and 2 depending on the application, but especially when used over a large area such as outdoors, it may be necessary to From the viewpoint of improving properties, etc., it is preferable to attach it to both the front and back surfaces as in the above embodiment.
また、上述の実施例は、隣接する１枚づつのエラストマ
ー被覆布同士を接合したものであるが、建造物の屋根や
大規模なテント材料などを製作するときは、複数枚づづ
のエラストマー被覆布の端部同士を同時を交互に積層し
て上記構成を繰り返すようにしてもよい。また、エラス
トマー被覆布の端部を鉤状に折り返し、双方の鉤状折り
返し部を互いに引っ掛は合う状態で積層させてもよい。In addition, in the above embodiment, adjacent pieces of elastomer-coated fabric are joined together, but when manufacturing roofs of buildings or large-scale tent materials, multiple pieces of elastomer-covered fabric are bonded together. The above structure may be repeated by simultaneously and alternately laminating the end portions of each other. Alternatively, the ends of the elastomer-covered fabric may be folded back into a hook shape, and the two hook-shaped folded portions may be stacked together in a state where they are hooked onto each other.
上述したエラストマー被覆布接合体は、互いに隣接する
エラストマー被覆布の端部同士を、その端部同士の間に
感圧接着剤を介在させて積層接着するため、縫糸による
縫合等の面倒な作業をすることなく強力な結合を行うこ
とができる上、さらに縫合だけでは得られない両エラス
トマー被覆布間の雨水や風即に対するシール性をも得る
ことができる。このように強固な結合とシールとがなさ
れている上に、さらに一方のエラストマー被覆布の結合
部分と他方のエラストマー被覆布の非結合部分とを跨ぐ
ように粘着テープが貼着されているため、結合力とシー
ル性とは一層向上する。そのため仮に粘着テープが剥離
しても、水密性や気密性を維持することができる。The above-mentioned elastomer-coated fabric bonded body is constructed by laminating and adhering the ends of adjacent elastomer-coated fabrics to each other with a pressure-sensitive adhesive interposed between the ends, which eliminates the need for troublesome work such as sewing with sewing thread. In addition to being able to form a strong bond without causing any damage, it is also possible to obtain sealing properties against rainwater and wind between the two elastomer-covered fabrics that cannot be obtained by sewing alone. In addition to the strong bonding and sealing, an adhesive tape is attached across the bonded portion of one elastomer-coated fabric and the unbonded portion of the other elastomer-coated fabric, so Bonding strength and sealing properties are further improved. Therefore, even if the adhesive tape peels off, watertightness and airtightness can be maintained.
以下、具体的な実施例により説明する。This will be explained below using specific examples.
実施例１ 手織ガラスｍ維（幅１．Ｏｍ、長さ５．０ｍ。Example 1 Hand-woven glass m-fiber (width 1.0m, length 5.0m.
厚さ０．３５ｍｍ＋ ガラスコードｆ１１．Ｏｍｍ／本
。Thickness 0.35mm + glass cord f11. Omm/book.
ガラスコード数５．５本／ｃｍ−旭グラスファイバー株
式会社製、グラスロン・クロスＭＧ３０００−ＩＮＨ・
３０）の両面に、透明な付加反応硬化型液状シリコーン
ゴム（トーレ・シリコーン株式会社製、５Ｅ６７０５）
を含浸、被覆し加熱硬化させて得られたシリコーンゴム
被覆ガラス布（全厚０．７５ｍｍ）２枚を用意した。Number of glass cords 5.5/cm-manufactured by Asahi Glass Fiber Co., Ltd., Glasslon Cross MG3000-INH.
30) Transparent addition reaction curing liquid silicone rubber (manufactured by Toray Silicone Co., Ltd., 5E6705)
Two sheets of silicone rubber-coated glass cloth (total thickness 0.75 mm) obtained by impregnating, coating, and heating and curing were prepared.
一方の布の５．０ｍ長の一端の奥行き５ｃｍの部分にシ
リコーン系感圧接着剤（１・−レ・シリコーン株式会社
製、５Ｈ４２８０固形分６０重量％）を最終厚さが８０
〜１００μになるように均一に塗布し、室温で３０分以
上風乾した後、他方の布の５．Ｏｍ長の一端の奥行き５
ｃｍの部分を積層し、その積層部分上に重量的２．５ｋ
ｇのハンドローラを往復させた。両方の布はよく密着接
合していて、人力で反対方向に引っ張ってもずれること
ばなかった。Apply silicone pressure-sensitive adhesive (manufactured by 1.-Le Silicone Co., Ltd., 5H4280 solid content 60% by weight) to a 5cm deep part of one end of the 5.0m length of one piece of cloth until the final thickness is 80%.
After applying it evenly to a thickness of ~100μ and air-drying it for at least 30 minutes at room temperature, apply 5. to the other cloth. Depth of one end of Om length 5
cm part is laminated, and a weight of 2.5 kg is placed on the laminated part.
The hand roller of g was reciprocated. Both fabrics were well bonded and did not shift even when manually pulled in opposite directions.
次いで、積層部分の片面側に、この積層部分を挾み隣接
する布の非積層部分表面に３ＣＩＩ１幅延長して跨り、
また上記積層部分と同一面の右側面には１ｃｌＩ１幅で
互いに反対側に延長させるようにして、シリコーン系感
圧接着剤（トーμ・シリコーン株式会社製、５Ｈ４２８
０）をポリテトラフルオロエチレンフィルムテープの片
面に積層した粘着テープ（ＳＩ（４２８０層の厚さ２０
μ、ポリテトラフルオロエチレンフィルムテープの厚さ
５０μ１幅６．０ｃｍ）を、感圧接着剤がシリコーンゴ
ム被覆ガラス繊維布に接するようにして貼着した。また
、同じ粘着テープを上記積層部分の反対側の面に対して
も、同様の方法で貼着した。Next, on one side of the laminated part, sandwich this laminated part and extend 3 CII 1 width over the surface of the non-laminated part of the adjacent cloth, straddling it,
In addition, on the right side of the same surface as the laminated part, a silicone pressure sensitive adhesive (5H428 manufactured by Tomu Silicone Co., Ltd., manufactured by Tomu Silicone Co., Ltd.,
0) laminated on one side of a polytetrafluoroethylene film tape (SI (4280 layer thickness 20
A polytetrafluoroethylene film tape having a thickness of 50 μm and a width of 6.0 cm) was attached so that the pressure-sensitive adhesive was in contact with the silicone rubber-coated glass fiber cloth. Further, the same adhesive tape was applied to the opposite side of the laminated portion in the same manner.
かくして得られたシリコーンゴム被覆ガラス繊布接合体
は透光性があり、かつ両シリコーンゴム被覆ガラス布が
強固に接合しており、接合部分上に水を噴射しても裏側
に通過することがなく、屋外暴露しても変化がなかった
。The thus obtained silicone rubber-coated glass fiber bonded body is translucent, and both silicone rubber-coated glass fabrics are firmly bonded, so that even if water is sprayed onto the bonded portion, it will not pass through to the back side. There was no change even after outdoor exposure.
比較例として、縫合だけしたもの及び粘着テープで貼り
合せただけのものを作った。縫合だけしたものは接合部
分を蛇行させながらその上に水を噴射したところ、裏側
に水が透過した。As comparative examples, we made one that was only sewn together and one that was just pasted together with adhesive tape. When we sprayed water on the joints with only sutures in a meandering manner, the water penetrated to the back side.
粘着テープで貼り合せただけのものは、両ガラス繊維布
を反対方向に強く引っ張ると剥がれてしまった。The one that was simply attached with adhesive tape came off when both glass fiber cloths were pulled strongly in opposite directions.
実施例２
実施例１の感圧接着剤５Ｈ４２８０の代りにシリコーン
系感圧接着剤（トーμ・シリコーン株式会社製、試作品
ＤＸ３８−０５２．固形分６０重量％）を使用し、室温
に１２時間放置して硬化接着させた他は、実施例１と同
様とした。Example 2 A silicone-based pressure-sensitive adhesive (prototype DX38-052, manufactured by Tou Silicone Co., Ltd., solid content 60% by weight) was used in place of the pressure-sensitive adhesive 5H4280 in Example 1, and the adhesive was left at room temperature for 12 hours. The procedure was the same as in Example 1 except that it was allowed to stand for curing and adhesion.
積層部分を感圧接着材で接着させただけの縫合前の中間
状態の両市はよく接着しており、両市を人力で引っ張っ
てもずれたり、剥がれたりすることはなかった。また、
粘着テープを貼着した後の接合体は、その結合部分の上
に水を蛇行させながら噴射しても裏側に透過することが
なく、屋外暴露しても変化がなかった。In the intermediate state before suturing, in which the laminated parts were simply glued together with a pressure-sensitive adhesive, the two sheets were well adhered, and even when the two sheets were pulled manually, they did not shift or peel. Also,
After the adhesive tape was attached, water did not penetrate to the back side even when water was sprayed onto the bonded part in a meandering manner, and there was no change even when exposed outdoors.
第１図は本発明によるエラストマー被覆布接合体の要部
斜視図、第２図は第１図のｎ−ｎ矢視断面図である。
■、２・・エラストマー被覆布、 ３・・感圧接着剤、
４，５・・粘着テープ。
代理人 弁理士 小 川 信 −
弁理士 野 口 賢 照
弁理士斎下和彦FIG. 1 is a perspective view of a main part of an elastomer-coated fabric assembly according to the present invention, and FIG. 2 is a sectional view taken along the line nn in FIG. 1. ■, 2...Elastomer coated cloth, 3...Pressure sensitive adhesive,
4,5... Adhesive tape. Agent: Patent Attorney Shin Ogawa − Patent Attorney Ken Noguchi Teru Patent Attorney Kazuhiko Saishita
Claims (5)
士を、両端部の間に感圧接着剤を介在させて積層接着し
、一方のエラストマー被覆布の前記積層部分と他方のエ
ラストマー被覆布の非積層部分との両面に跨るように粘
着テープを貼着させたことを特徴とするエラストマー被
覆布接合体。(1) Ends of adjacent elastomer-coated fabrics are laminated and adhered to each other with a pressure-sensitive adhesive interposed between both ends, and the laminated portion of one elastomer-coated fabric and the other elastomer-coated fabric are not laminated. 1. An elastomer-coated fabric bonded body characterized by having adhesive tape adhered so as to span both sides of the part.
覆したガラス繊維布又はシリコーンゴムを被覆した金属
繊維布である特許請求の範囲第１項記載のエラストマー
被覆布接合体。(2) The elastomer-coated cloth assembly according to claim 1, wherein the elastomer-coated cloth is a glass fiber cloth coated with silicone rubber or a metal fiber cloth coated with silicone rubber.
被覆布の表裏両側面に貼着されている特許請求の範囲第
１項記載のエラストマー被覆布接合体。(3) The elastomer-coated fabric assembly according to claim 1, wherein adhesive tapes are attached to both the front and back sides of the elastomer-coated fabrics that are laminated and adhered to each other.
トラフルオロエチレンフィルムテープ又はシリコーン硬
化体被覆無機繊維布テープである特許請求の範囲第１項
記載のエラストマー被覆布接合体。(4) The elastomer-coated fabric assembly according to claim 1, wherein the adhesive tape is a polytetrafluoroethylene film tape coated with a silicone adhesive or an inorganic fiber fabric tape coated with a cured silicone.
系又はシリコーン系の感圧接着剤である特許請求の範囲
第１項記載のエラストマー被覆布接合体。(5) The elastomer-coated fabric bonded article according to claim 1, wherein the pressure-sensitive adhesive is a vinyl-based, rubber-based, acrylic-based, or silicone-based pressure-sensitive adhesive.