JPS59176330A - Laminated film - Google Patents

Abstract

PURPOSE:A laminated film excellent in both surface smoothness and easy slidability and suitable as a base for magnetic recording media, etc., prepared by laminating the surface of a base film layer with a continuous layer containing a fluorine compound so that the surface roughness may fall within a specified range. CONSTITUTION:The purpose laminated film is prepared by providing at least one of the surfaces of a base film comprising polyethylene terephthalate or the like with a continuous layer comprising a fluorine compound or with a continuous layer comprising a mixture of a fluorine compound and a high-molecular solid (e.g., epoxy resin) by means of painting or the like so that the surface roughness (Ra) on the side of the continuous layer containing the fluorine compound may be 0.015-0.005mu. The fluorine compounds include, for example, tetrafluoroethylene wax and polychlorofluoroethylene. When the produced laminated film is used in a magnetic recording medium, a magnetic layer is further formed on its surface.

Description

【発明の詳細な説明】 〔産業上の利用分野〕 本発明は２表面の平滑性と易滑性が共に優れた積層フィ
ルムに関するものである。DETAILED DESCRIPTION OF THE INVENTION [Industrial Field of Application] The present invention relates to a laminated film having excellent smoothness and slipperiness on two surfaces.

〔従来技術〕[Prior art]

近年、磁気記録媒体ベース、コンデンザーベース、グラ
フィックベースおよび包装ベースなどの用途に、プラス
チックフィルムの需要が急伸している。それらの用途で
は共通して小型軽量化が要望され、同時に、精度が厳し
くなっている。このことは、たとえば、磁気記録の分野
では、ビデオレコーダーの小型化・軽量化や、ビデオテ
ープの長時間記録化１品密度記録化という技術革新の志
向となっている。この志向に即して、磁気記録媒体は薄
く、かつ高密度記録する必要があり、それを実現するた
めには、ベースフィルムと磁性層の厚みは共に薄く、か
つ磁性層表面は平滑であることが望１しくなる。ところ
が、磁性層の厚みが薄くなるとベースフィルムの表面状
態は磁性層表面の状態に影響を及ぼす度合が強まる。従
って磁性層表面を平滑にするにはベースフィルム表面の
平滑性が必要となる。In recent years, demand for plastic films has been rapidly increasing for applications such as magnetic recording media bases, condenser bases, graphic bases, and packaging bases. In these applications, there is a common demand for smaller size and lighter weight, and at the same time, accuracy is becoming stricter. For example, in the field of magnetic recording, this has led to technological innovations such as miniaturization and weight reduction of video recorders, long-duration recording of video tapes, and single-item density recording. In line with this trend, magnetic recording media must be thin and capable of high-density recording, and in order to achieve this, both the base film and the magnetic layer must be thin and the surface of the magnetic layer must be smooth. becomes more desirable. However, as the thickness of the magnetic layer becomes thinner, the surface condition of the base film has a stronger influence on the surface condition of the magnetic layer. Therefore, in order to make the surface of the magnetic layer smooth, it is necessary that the surface of the base film be smooth.

一方、磁気記録媒体を製造する際にはベースフィルムの
表面の滑り性か必要となる。このベースフィルムの滑り
性は、磁気記録媒体となした後の使用時の走行性にも直
結する。以上のように、ベースフィルムとしては平滑性
と易滑性が共に優れた表面のものが待望されているが１
元来、平滑性と易滑性は相反関係にあり２両特性を同時
に満足できるフィルムはなかなか見当らない。このよう
な非常に平滑で、かつ非常に滑シ件の良いフィルムを得
るために従来から種々の検討がなされてきた。たとえは
、微細粒子を添加したフィルムや。On the other hand, when manufacturing magnetic recording media, the surface of the base film needs to have slipperiness. The slipperiness of this base film is directly related to the runnability during use after it is made into a magnetic recording medium. As mentioned above, there is a long-awaited base film with a surface that has both excellent smoothness and slipperiness.
Originally, smoothness and ease of sliding are in a contradictory relationship, and it is difficult to find a film that can satisfy both properties at the same time. Various studies have been made in the past in order to obtain such a film that is extremely smooth and has excellent gliding properties. An example is a film containing fine particles.

易滑表面層と平滑表面層とからなる複合フィルム。A composite film consisting of a slippery surface layer and a smooth surface layer.

さらに、架橋性シリコーンやワックスを表面塗布した積
層フィルムなどが知られ、磁気テープベースフィルムな
どに使用されている。Furthermore, laminated films whose surfaces are coated with crosslinkable silicone or wax are known and are used in magnetic tape base films and the like.

しかし、かかる従来のフィルムには、平滑性を満足せし
めようとすれば易滑性が犠牲になり、逆に易滑性を満足
せしめようとすれは、平滑性が犠牲になるという欠点が
ある。捷だ、易滑層と平’１４層と力・らなる複合フィ
ルムでは、製品として巻いた後、易滑層の表面突起か平
滑層側の表面に転写するため、せっかくの平滑層側の平
滑性か損われてしまう欠点か付随する。However, such conventional films have the drawback that smoothness is sacrificed when smoothness is desired, and smoothness is sacrificed when smoothness is desired. In a composite film consisting of a smooth layer, a flat layer, and a flat layer, after being rolled as a product, the surface protrusions of the easy layer are transferred to the surface of the smooth layer, so the smoothness of the smooth layer is Accompanied by flaws that impair gender.

〔発明の目的〕[Purpose of the invention]

本発明の目的は、上記欠点を解消せしめ、平滑性と易滑
性とが共に優れた積層フィルムを提供すること、加えて
、易滑性の耐久性、耐摩耗性に優れた積層フィルムを提
供するものである。The purpose of the present invention is to eliminate the above-mentioned drawbacks and provide a laminated film that is excellent in both smoothness and easy sliding properties.In addition, it is an object of the present invention to provide a laminated film that has excellent slipping properties, durability, and abrasion resistance. It is something to do.

〔発明の構成〕[Structure of the invention]

本発明は上記目的を達成するため１次の構成。 The present invention has a primary configuration to achieve the above object.

すなわち、孔体フィルム層の少なくとも片面に。That is, on at least one side of the porous film layer.

フッ素系化合物を含む連続層が積層されてなる積層フィ
ルムであり、フッ素系化合物が積層された側の表面の表
面粗さくＲａ）が、　　０．０１５〜０．００５　／。It is a laminated film formed by laminating continuous layers containing a fluorine-based compound, and the surface roughness (Ra) of the side on which the fluorine-based compound is laminated is 0.015 to 0.005/.

テｈ　ル積層フィルムを特徴とするものである。It is characterized by a multilayer film.

本発明における基体フィルムとは、フィルム状をしたも
のであれば特に限定されるものではなく熱可塑性樹脂、
熱硬化性樹脂などから広く選択し得る。たとえばポリエ
ステル、ポリオレフィン。The base film in the present invention is not particularly limited as long as it is in the form of a film, such as thermoplastic resin,
It can be selected from a wide range of thermosetting resins. For example, polyester and polyolefin.

セルロースアセテート、ポリ塩化ビニル、ポリイミド、
ポリカーボン、ポリイミドアミド、ポリフェニレンスル
フィドなどが挙げられる。浴融押出製膜か可能という理
由からは、熱可塑性樹脂が好ましい。さらに、フィルム
の機械的強度、剛性。Cellulose acetate, polyvinyl chloride, polyimide,
Examples include polycarbon, polyimide amide, and polyphenylene sulfide. Thermoplastic resins are preferred because they allow bath-melt extrusion film formation. Additionally, the mechanical strength and rigidity of the film.

寸法安定性、耐熱性などの物性を総合して良いという理
由からポリエステルが好ましい。ポリエステルは１例え
ば、飽和線状ポリエステルを主体とするものが挙げられ
、ポリエチレンテレフタレート、ポリエチレン２．６−
ナフタリンジカルボキシレート、ポリエチレン−ｐ−オ
キシベンゾエート。Polyester is preferred because it has good overall physical properties such as dimensional stability and heat resistance. Examples of polyesters include those mainly composed of saturated linear polyesters, such as polyethylene terephthalate, polyethylene 2.6-
Naphthalene dicarboxylate, polyethylene-p-oxybenzoate.

ポリブチレンテレフタレート、ポリヘキンレンテレフタ
レート、ポリエチレンビス−ａ、β＋２−クロルフェノ
キシ÷エタン−４，４′−ジカルボキシレートナトが代
表例である。なお・、ホモポリエステルでもコポリエス
テルでもよい。さらにポリエステルのうちでもポリエチ
レンテレフタレートは」二記フィルム物性の総合バラン
スがよいことや。Typical examples include polybutylene terephthalate, polyhexene terephthalate, polyethylene bis-a, and β+2-chlorophenoxy÷ethane-4,4'-dicarboxylate. Note that homopolyester or copolyester may be used. Furthermore, among polyesters, polyethylene terephthalate has a good overall balance of film properties.

原料が容易に安く入手可能という理由で、最も好ましい
。Most preferred because the raw materials are readily available and cheap.

なお、必要に応じて２種以上の樹脂の混合、たとえ（は
、ポリエチレンテレフタレートにポリブチレンテレフタ
レートを１０〜９　Ｑ　重量バーセント混合してもよい
。また、基体フィルム層には、平均粒径が１０μ、好寸
しくけ５μ以上の粒子が含まれないことが望ましい。If necessary, two or more resins may be mixed, for example, polyethylene terephthalate and polybutylene terephthalate may be mixed at a weight percentage of 10 to 9 Q. In addition, the base film layer may have an average particle size of 10 μm. It is preferable that particles with a size of 5 microns or more are not included.

基体フィルムの配向状態は特に限定されず、無配向、−
軸配向、二軸配向のいずれでもよいが。The orientation state of the base film is not particularly limited, and may be non-oriented, -
Either axial orientation or biaxial orientation may be used.

機械的強度や寸法安定性や剛性の点で２軸配向状態のも
のが望ましい。In terms of mechanical strength, dimensional stability, and rigidity, biaxially oriented materials are desirable.

基体フィルムの表面粗さくＲａ）は、０．００２〜００
５０μ、好ましくは０．００３〜０．０４０μが望まし
い。The surface roughness (Ra) of the base film is 0.002 to 0.00
50μ, preferably 0.003 to 0.040μ is desirable.

また、基体フィルムの厚みは、３〜１００μ。Moreover, the thickness of the base film is 3 to 100 μm.

好ましくは４〜８０μが望ましい。Preferably 4 to 80μ is desirable.

本発明に用いられるフッ素系化合物は特に限定されるも
のではなく、含フツ素オリゴマ、含フツ素ポリマから選
択される。含フツ素オリゴマとしては、フッ素油、テト
ラフルオロエチレンワックス、含フツ素アルコール、ベ
ルフルオルアルキルヨーシトなどのフルオロオレフィン
テロマーや。The fluorine-based compound used in the present invention is not particularly limited, and is selected from fluorine-containing oligomers and fluorine-containing polymers. Examples of the fluorine-containing oligomer include fluorine oil, tetrafluoroethylene wax, fluorine-containing alcohol, and fluoroolefin telomer such as perfluoroalkyl iosite.

ペルフルオロポリエーテルやペルフルオロオレフィンオ
リコマなどが代表例であり、その他、それらの酸塩、ベ
タイン、エチレンオキシド付加物。Typical examples include perfluoropolyether and perfluoroolefin olicoma, as well as their acid salts, betaine, and ethylene oxide adducts.

エステル、シリコーンを化学結合させたものなどが挙け
られる。また、含フツ素ポリマとしては。Examples include chemically bonded esters and silicones. Also, as a fluorine-containing polymer.

ポリテトラフルオロエチレン、ポリへキサフルオロプロ
ピレン、ポリトリクロロフルオロエチレン。Polytetrafluoroethylene, polyhexafluoropropylene, polytrichlorofluoroethylene.

ポリ塩化ビニリデン、フッ素化合物とシロキサン化合物
の共重合体などが代表例である。Representative examples include polyvinylidene chloride and copolymers of fluorine compounds and siloxane compounds.

上記フッ素系化合物のうち９本発明に好ましいのは、含
フツ素オリゴマである。その理由は、含フツ素オリゴマ
は液状あるいは固体状でも均一微細化しやすいため９本
発明フィルムとなした時のフィルムの平滑性が良くなり
、また、含フツ素ポリマにくらべて、基体フィルムの樹
脂との親和力・接着力を強くできるからである。同じく
親和力。Among the above-mentioned fluorine-based compounds, nine preferred in the present invention are fluorine-containing oligomers. The reason for this is that fluorine-containing oligomers can be easily made uniform and fine even in liquid or solid form, so that when formed into the film of the present invention, the film has better smoothness. This is because it can strengthen the affinity and adhesion with. Similarly affinity.

接着力の点で、含フツ素ポリマのうちでは、ポリ塩化ビ
ニリチンやポリクロロフルオロエチレンのような有極１
住営フツ素ポリマの方か、ポリエトラフルオロエチレン
のような無極性含フツ素ポリマよりも好ましい。In terms of adhesive strength, among fluorine-containing polymers, there are
Fluorinated polymers are preferred over non-polar fluorinated polymers such as polyetrafluoroethylene.

上記含フツ素オリコマのうちで特に本発明に好ましいの
は、炭素数か１〜ろ０のペルフルオロアルキル基を有す
る単量体もしく　（ｒｉ重合体からなるものである。ペ
ルフルオロアルキル基”　ｒｌ’２ｎ＋、）の炭素数Ｉ
〕の範囲は、１〜３０．打型しくに６〜３０、さらに好
ましくは６〜３０にすると、ペルフルオロアルキルの末
端−ＣＦ、基が整然とフィルム表面に配列され、その結
果として、臨界表面張力（表面自由エネルギー）の低い
表面が形ｌ戊される。壕だ、炭素数ｎが５０を越えると
。単量体もしくは重合体としての粒子径が大きくなりす
ぎて積層フィルムとなした時の連続層側表面の平滑性が
損われることがある。ここで述べているペルフルオロア
ルキル基を有する単量体もしくは重合体は、その分子構
造式に、ペルフルオロアルキル基以外に、カルボキシル
基、カルボニル基、アルデヒド基、アミ７基、イミノ基
、スルホン基、アクリル基、メタクリル基々どの官能基
を一種以上有することか、基体フィルムとの親和力・接
着力を増すためと、積層する時の分散媒（水や有機溶媒
など）への相溶性を高めるだめの両方に有利であり、そ
のことは１本発明フィルムの積層界面の接着力を上げ、
かつ、積層表面の平滑性を得る点に有利となる。Among the above-mentioned fluorine-containing oricomers, particularly preferred for the present invention are monomers or (ri polymers) having a perfluoroalkyl group having 1 to 0 carbon atoms.Perfluoroalkyl group "rl' 2n+,) carbon number I
] range is 1 to 30. When the mold is set to 6 to 30, more preferably 6 to 30, the terminal -CF groups of perfluoroalkyl are arranged in an orderly manner on the film surface, and as a result, a surface with low critical surface tension (surface free energy) is formed. I will be blown away. It's a moat when the carbon number n exceeds 50. If the particle size of the monomer or polymer becomes too large, the smoothness of the surface of the continuous layer when formed into a laminated film may be impaired. The monomers or polymers having a perfluoroalkyl group mentioned here include, in addition to the perfluoroalkyl group, a carboxyl group, a carbonyl group, an aldehyde group, an amine group, an imino group, a sulfone group, an acrylic group, and It is important to have one or more types of functional groups, such as methacrylate groups and methacrylic groups, both to increase affinity and adhesive strength with the base film, and to increase compatibility with dispersion media (water, organic solvents, etc.) during lamination. This is advantageous in that it increases the adhesive strength at the laminated interface of the film of the present invention,
Moreover, it is advantageous in obtaining smoothness of the laminated surface.

本発明では１以上に述べたフッ素系化合物を少なくとも
１種類選択して用いればよいが、２種類以上を適当に組
合せて用いても差支えない。In the present invention, at least one of the above-mentioned fluorine compounds may be selected and used, but two or more may be used in an appropriate combination.

本発明のフッ素系化合物を含む連続層とは、上記のフッ
素系化合物そのものの層、または、その化合物と次に述
べる高分子固体とが混合された層である。The continuous layer containing the fluorine-based compound of the present invention is a layer of the above-mentioned fluorine-based compound itself, or a layer in which the compound and the polymer solid described below are mixed.

なお、高分子固体を混合すると９本発明フィルムの易滑
性の耐久性、剛摩耗性などが向上するのに役立つ。ここ
で言う［易滑性の耐久性が向上］とは、フィルムを長時
間繰返し金属固定ガイドに走行させて摩擦させた後も滑
り性が悪化（摩擦係数か大きくなる）しないことであシ
、「耐摩耗性が向」二」とは、やはりフィルムを長時間
繰反し摩擦させた後も、滑り性を伺与させるに用いフッ
素系化合物がフィルムから脱落しにくいということであ
る。Incidentally, the mixing of polymeric solids helps to improve the slipperiness, durability, hard abrasion resistance, etc. of the film of the present invention. Here, ``improved durability of slipperiness'' means that the slipperiness does not deteriorate (the coefficient of friction does not increase) even after the film is repeatedly run against a fixed metal guide for a long period of time to cause friction. ``Good abrasion resistance'' means that the fluorine-based compound used to impart slipperiness is difficult to fall off from the film even after the film is repeatedly rubbed for a long period of time.

高分子固体の種類は特に限定されないが、フッ素系化合
物とも基体フィルムとも親和力が良い熱可塑性樹脂、熱
硬化性樹脂１反応性樹脂などの中から選ばれ、たとえは
、ニカワ、カセインなどの天然水浴性高分子、ポリビニ
ルアルコール、メチルセルロースおよびセルロース誘４
　体、　尿素１ｆｆｌｌ　脂やメラミン樹脂などの合成
水溶性高分子、ポリエステルエーテルなどの水溶性ホリ
エステル、ポリエチレンテレフタレート、ポリフ゛チレ
ンテンフクレート、ポリアクリル酸エステル　、％　ｌ
ノメタク１ノル酸エステルなどのポリエステル、ポ１ナ
アクＩＪ口ニトリル、ポリアミド、ポリビニルフ゛チラ
ール。The type of polymer solid is not particularly limited, but it is selected from thermoplastic resins, thermosetting resins, and reactive resins that have good affinity with both fluorine compounds and the base film.For example, natural water baths such as glue and casein are used. Polymer, polyvinyl alcohol, methyl cellulose and cellulose
Synthetic water-soluble polymers such as fat and melamine resin, water-soluble polyesters such as polyester ether, polyethylene terephthalate, polyethylene terephthalate, polyacrylic acid ester, % l
Polyester such as Nometac 1-Noric acid ester, Polyester, Polyamide, Polyvinyl nitrile.

ポリフッ化ビニル、ポリ塩化ビニル、ポリ塩化ビニリチ
ン、ポリスチレ／、ポリ酢酸ビニル、ポ１ノブタシエン
、ポリウレタン、ポリクロロフ０レン。Polyvinyl fluoride, polyvinyl chloride, polyvinyritine chloride, polystyrene/, polyvinyl acetate, polybutadiene, polyurethane, polychlorofluorene.

フェノール樹脂、アルキッド樹脂、エポキシ樹脂。Phenolic resin, alkyd resin, epoxy resin.

架橋性シリコーン樹脂など、および９以上の共重合体、
および、それらの混合物である。その中でもフッ素化合
物および基体フィルムとの親オロカの点で、基体フィル
ムにポリエステルを用いる場合は、該高分子固体として
、コポリエステルエーテルやエポキシ樹脂が好ましい。crosslinkable silicone resin, etc., and copolymers of 9 or more,
and mixtures thereof. Among these, copolyester ethers and epoxy resins are preferred as the polymer solid when polyester is used for the base film in terms of affinity with fluorine compounds and the base film.

コポリエステルエーテル（、ま、フィルムとなしたあと
連続層側表面に磁性層（たとえば１強磁性金属薄膜）を
設ける場合該磁性層と連続層との接着性が向上させる効
果７５王大きく、また、エポキシ樹脂は滑シ件の耐久性
を向上させる効果が太きい。また、コポリエステルエー
テルとしては・以下の組成のものが有用である。When a magnetic layer (for example, a ferromagnetic metal thin film) is provided on the surface of the continuous layer side after the copolyester ether is formed into a film, the adhesion between the magnetic layer and the continuous layer is greatly improved. Epoxy resins have a great effect on improving the durability of lubrication surfaces. Also, as copolyester ethers, those with the following compositions are useful.

まず、酸成分としては、芳香族ジカルボン酸および非力
６族カルボン酸２Ｌ・よび−そ、ｌＬシのＳＣステル形
成性誘導体ジカルボン酸が挙げられ、それらの酸のうち
で芳香族ジカルボン酸が全シカルホン酸成分に対し６０
モル係以上占めることか打型しく。First, as acid components, there are aromatic dicarboxylic acids and dicarboxylic acids that are SC ester-forming derivatives of non-strength group 6 carboxylic acids 2L and 1L, and among these acids, aromatic dicarboxylic acids are 60 for acid components
It is important to occupy more than one person in charge of the mall.

その範囲で数種のジカルボン酸を併用してもよい。Several types of dicarboxylic acids may be used in combination within this range.

具体的な酸成分の例は、芳香族ジカルボン酸としては、
テレフタル酸、イソフタル酸、フタル酸。Specific examples of acid components include aromatic dicarboxylic acids such as
Terephthalic acid, isophthalic acid, phthalic acid.

２．５−ジメチルテレンタル酸、１１４−ナフタレンジ
カルボン酸、２，６−ナフタレンジカルボン酸。2,5-dimethylterental acid, 114-naphthalene dicarboxylic acid, 2,6-naphthalene dicarboxylic acid.

ビフェニルジカルボン［，１，２−ビス（フェノキシ）
エタン−ｐ＋ｐ’−ジカルボン酸およびそれらのエステ
ル形成性誘導体ジカルボン酸かあり、非芳香族ジカルボ
ン酸としては、蓚酸、マロン酸。biphenyl dicarbonate [,1,2-bis(phenoxy)]
Ethane-p+p'-dicarboxylic acid and their ester-forming derivative dicarboxylic acids include oxalic acid and malonic acid as non-aromatic dicarboxylic acids.

コハク酸、クルタール酸、アジピン酸、セハンン酸、１
．２−シクロヘキザンシカルボン酸、１．４−シクロヘ
キサンジカルボン酸およびそレラノエステル形成性誘導
体ジカルボン酸がある。Succinic acid, cultaric acid, adipic acid, sehanic acid, 1
．． These include 2-cyclohexanedicarboxylic acid, 1,4-cyclohexanedicarboxylic acid, and itsleranoester-forming derivative dicarboxylic acids.

ここで言うエステル形成性誘導体ジカルボン酸としては
、エステル形成性スルホン酸アルカリ金属塩化合物が代
表であシ、たとえば、スルホテレンタル酸、５−スルホ
イソフタル酸、４−スルホフタル酸、４−スルホナフタ
レン−２，７−ジカルポン７１．２−スルホ−１，４−
ビス＋ヒドロキンエトキシ＋ベンゼンなどのスルホン酸
部分のアルカリ金属塩などがあり、５−スルホイソフタ
ル酸。The ester-forming derivative dicarboxylic acids mentioned here are typically ester-forming sulfonic acid alkali metal salt compounds, such as sulfoterentalic acid, 5-sulfoisophthalic acid, 4-sulfophthalic acid, 4-sulfonaphthalene- 2,7-dicarpone 71.2-sulfo-1,4-
There are alkali metal salts of the sulfonic acid moiety such as bis + hydroquine ethoxy + benzene, and 5-sulfoisophthalic acid.

スルホテレフタル酸のナトリウム塩が好ましく使用され
る。次に、グリコール成分としては、脂肪族捷たは脂環
族グリコールが挙げられる。具体的なグリコール成分の
例は、エチレングリコール。The sodium salt of sulfoterephthalic acid is preferably used. Next, examples of glycol components include aliphatic glycols and alicyclic glycols. An example of a specific glycol component is ethylene glycol.

１、ロープロパンジオール、１．４−ブタンジオール。1, low propanediol, 1,4-butanediol.

１．４−７クロヘキサンシオール、１．６−ヘキサンジ
オールなどが好ましいが、それらに、ジエチレングリコ
ール、トリエチレングリコールなどのポリエチレングリ
コール： Ｈ÷０−ＣＨ，−ＣＨ，÷ＯＨ （式中ｎ　＝　２〜１４０の整数）を１〜６０重量係重
量係官せたものでもよい。1.4-7 chlorohexanesiol, 1.6-hexanediol, etc. are preferred, but polyethylene glycols such as diethylene glycol and triethylene glycol: H÷0-CH, -CH,÷OH (in the formula n = 2 ~140 integer) with a weight coefficient of 1 to 60.

以上のコポリエステルエーテルのうちで最も親和力の点
で好ましいのは、たとえば酸成分とじてテレフタル酸８
０〜９９　ｍｏｌ　％と５−スルホインフタル酸１〜２
０　ｍｏｌ　％　ｒグリコール成分としてエチレングリ
コール８２〜９８　ｍｏｌ　％　（！：　ジエチレンク
リコール２〜１８　ｍｏｌ　％からなるものである。Among the above copolyester ethers, the most preferred in terms of affinity is, for example, terephthalic acid 8 as the acid component.
0-99 mol % and 5-sulfoinphthalic acid 1-2
0 mol % r The glycol component consists of 82 to 98 mol % of ethylene glycol (!: 2 to 18 mol % of diethylene glycol).

以上のような混合組成からなる連続層の組成物に占める
。フッ素系化合物（Ａ）と高分子固体（Ｂ）の混合重量
比率Ａ　／　Ｂは、０．００５〜５０．好丑しくけ０２
〜２０である。Ａ／Ｂが０．００５未満、好ましくは０
２未渦でＩｄ　、フィルムの連続層側の表面の易滑性が
十分発現せず、一方、Ａ／Ｂが５０好捷しくば２０を越
すと、高分子固体がフッ素系化合物を十分捕捉できない
ため、フィルムの連続層側の耐摩耗性が悪くなり９好ま
しくない。It occupies the composition of the continuous layer consisting of the above mixed composition. The mixing weight ratio A/B of the fluorine compound (A) and the polymer solid (B) is 0.005 to 50. Koushikake 02
~20. A/B is less than 0.005, preferably 0
2.With no vortex Id, the surface of the continuous layer side of the film does not exhibit sufficient slipperiness, and on the other hand, when A/B exceeds 50 or 20, the polymer solid cannot sufficiently capture the fluorine-based compound. Therefore, the abrasion resistance of the continuous layer side of the film deteriorates, which is undesirable.

本発明積層フィルムにおいては、フッ素系化合物を含む
層は、連続層である必要かある。連続層とは、積層フィ
ルムの任意の表面を顕微鏡倍率２５０倍で光学顕微鏡観
察して、その一視野内において積層フィルムのフッ素化
合物を含む層が連続になっているものである。In the laminated film of the present invention, the layer containing the fluorine compound needs to be a continuous layer. A continuous layer is one in which the layer containing the fluorine compound of the laminated film is continuous within one field of view when an arbitrary surface of the laminated film is observed with an optical microscope at a magnification of 250 times.

仮に、連続でなく不連続になった場合、積層フィルムの
平滑性に全く欠けるものになってしまう。If it becomes discontinuous instead of continuous, the laminated film will lack smoothness at all.

本発明積層フィルムにおいては、フッ素系化合物を含む
連続層側の表面粗さくＲａ）は、０．０１５〜０００５
μ、好ましくは、、０．０１０〜０００５μヤあること
が必要である。Ｒａが０００１５μ、好ましくは００１
０μを越えると該連続層側表面の平滑性が不足してしま
う。一方、Ｒａが０．００５μより小さいと易滑性に欠
けてしまう。In the laminated film of the present invention, the surface roughness Ra) of the continuous layer containing the fluorine compound is 0.015 to 0005.
μ, preferably 0.010 to 0005 μ. Ra is 00015μ, preferably 001
If it exceeds 0μ, the surface of the continuous layer will lack smoothness. On the other hand, if Ra is smaller than 0.005μ, slipperiness will be lacking.

本発明積層フィルムにおいては、フッ素系化合物を含む
連続層の厚みが０００１〜０５μ、好ましくは０．０１
〜０．２μの時、平滑性と易滑性を両立するという本発
明効果が顕著となる。連続層の厚みが０．００１μ、好
ましくは０．０１μよシ薄いと、易滑性が不十分となり
やすく、また、易滑性の耐久性も不十分となシやすいの
で良くない。In the laminated film of the present invention, the thickness of the continuous layer containing the fluorine compound is 0001 to 05μ, preferably 0.01μ.
When the thickness is 0.2μ, the effect of the present invention of achieving both smoothness and slipperiness becomes remarkable. If the thickness of the continuous layer is as thin as 0.001 μm, preferably as thin as 0.01 μm, the slipperiness tends to be insufficient, and the durability of the slipperiness tends to be insufficient, which is not good.

一方、連続層の厚みが０５μ、好ましくは０２μより厚
いと、フッ素系化合物が連続層表層に配列しにくくなる
結果、やはり、易ａ性が不十分になシやすく、−１だ、
連続層の表面が粗くなりやすいので良くない。On the other hand, if the thickness of the continuous layer is thicker than 05 μm, preferably 02 μm, the fluorine-based compound becomes difficult to arrange on the surface layer of the continuous layer, resulting in insufficient a resistance, which is -1.
This is not good because the surface of the continuous layer tends to become rough.

本発明積層フィルムにおいては、フッ素系化合物を含む
連続層側表面の臨界表面張力（γ　）が３５ｄｙｎｅ／
ｃｍ以下、好ましくは２５　ｄｙｎｅ／ａｍ以下のもの
が、易滑性が非常に良い結果となる。該臨界表面張力が
ろ５　ｄｙｎ　ｅＡｍ＊好ましくけ２５ｄ、ｙｎｅ／ｃ
ｍを越えると易滑性が不足する。なお、該臨界表面張力
の下限は特に限定されないが、フッ素系化合物のフッ素
が選択的に連続層表面に配列される状態の時ノ値が６ｄ
ｙｎ６／ｃｍ　　と考えられているので２通常。In the laminated film of the present invention, the critical surface tension (γ) of the surface of the continuous layer containing the fluorine compound is 35 dyne/
cm or less, preferably 25 dyne/am or less, results in very good slipperiness. The critical surface tension is 5 dyn eAm*preferably 25d, yne/c
If it exceeds m, slipperiness will be insufficient. Note that the lower limit of the critical surface tension is not particularly limited, but the value when the fluorine of the fluorine-based compound is selectively arranged on the surface of the continuous layer is 6d.
2 normal because it is considered to be yn6/cm.

下限は６　ｄ、ｙｎｅ／ｃｍ　である。The lower limit is 6 d, yne/cm.

本発明積層フィルムにおいては、フッ素系化合物を含む
連続層の表層部は、ＥＳＣＡ法による測定値として、フ
ッ素原子（Ｆ）と炭素原子（Ｃ）の個数比率（Ｆ／Ｃ）
が、０５〜２０．打型しくは０７〜１．５であることが
望ましい。ｌｊ’　／　Ｃが２０好ましくは１５より太
きいと、易滑性の耐久性や耐摩耗性および平滑性が打型
しくなくなることがあ９１寸だ、Ｆ／Ｃが０５．好まし
くは０７より小さいと、易滑性が発現しなくなることが
あり、注意を要する。In the laminated film of the present invention, the surface layer portion of the continuous layer containing the fluorine-based compound has a number ratio of fluorine atoms (F) to carbon atoms (C) (F/C) as measured by the ESCA method.
But from 05 to 20. It is desirable that the mold is 07 to 1.5. If lj'/C is thicker than 20, preferably 15, the durability of easy sliding, abrasion resistance and smoothness may become poor in the mold. Preferably, if it is smaller than 07, slipperiness may not develop, so care must be taken.

なお９本発明積層フィルムにおいては、連続層表面に、
直径０．０５〜５μの範囲の半円球状粒予成されている
ことが、平滑性と易滑性の両立に有ないと易滑性に不足
がちとなシ、一方、１０　　個／＋ｍ　’　ｒ好ましく
は１０　個／ｃｍｌよシ多いと、粗面すぎて平滑性が損
われやすい。9 In the laminated film of the present invention, on the surface of the continuous layer,
If smoothness and ease of slipping are not achieved by preforming hemispherical particles with a diameter in the range of 0.05 to 5μ, slipping properties tend to be insufficient. Preferably, if the number is more than 10 pieces/cml, the surface becomes too rough and smoothness is likely to be impaired.

本発明の積層フィルムの少なくとも片面に磁性層を設け
、磁気記録媒体とするのが打型しい。It is preferable to form a magnetic recording medium by providing a magnetic layer on at least one side of the laminated film of the present invention.

この磁性層とは９周知の磁性層でγ−Ｆｅ、Ｏ，。This magnetic layer is a well-known magnetic layer of γ-Fe, O,.

ｃ（、をドープしたγ−Ｆｅ、０．　ＣｒＯ２あるいは
強磁性合金といつだ粉末状磁性材料を有機バインダー中
に分散させ塗布する方法によって形成される磁性層、ま
たけ、Ｆｅ、ｃｏ、　ｌ”ｌｉ　　その他作磁性金属あ
るいはそれらを含む磁性合金を、たとえば、真空蒸着、
スパッタリング、イオンブレーティング。A magnetic layer formed by dispersing and coating a powdered magnetic material in an organic binder with γ-Fe, 0.CrO2 or a ferromagnetic alloy doped with c(, Fe, co, l" li Other magnetic metals or magnetic alloys containing them, for example, by vacuum deposition,
Sputtering, ion blating.

容気メッキ等の方法によって形成される磁性層のいずれ
であってもよいが９本発明の効果を有利に発揮せしめて
磁気記録媒体の精度向上を図る点では、後者の磁性層を
設けるのが打型しい。Any magnetic layer formed by a method such as volume plating may be used; however, in order to advantageously exhibit the effects of the present invention and improve the precision of the magnetic recording medium, it is preferable to provide the latter magnetic layer. It looks like a type.

次に９本発明の積層フィルムおよび磁気記録媒体の製造
方法の大要を述へる。たたし、これに限定されるもので
ない。Next, a summary of the method for manufacturing the laminated film and magnetic recording medium of the present invention will be described. However, it is not limited to this.

（１）　　積層フィルムの製造方法： 先ず９本発明の基体フィルムは、たとえは、前述した熱
可塑性樹脂を押出機１てよって口金から溶融押出し、シ
ート状にキャストし、必要に応して周知の方法で延伸し
て得る。延伸方法は特に限定されるものではないが、た
とえば、同時２軸タテ−ヨー１．Ｉｆ−ヨコ−タテ、ヨ
コータｆ、２段タテ−ヨコ、２段タテ→ヨコ→タテ、２
段タテ→ヨコー同時２軸などの延伸によシ２軸延伸され
るのが望ましい。(1) Method for manufacturing a laminated film: First, the base film of the present invention is produced by melt-extruding the above-mentioned thermoplastic resin from a die using an extruder 1, casting it into a sheet, and, if necessary, using a well-known method. obtained by stretching by a method. The stretching method is not particularly limited, but for example, simultaneous two-axis vertical stretching method 1. If - horizontal - vertical, horizontal f, 2 steps vertical - horizontal, 2 steps vertical → horizontal → vertical, 2
It is preferable to carry out biaxial stretching such as vertical and horizontal simultaneous biaxial stretching.

次いで、基体フィルムの少なくとも片面に、フッ素系化
合物を含む組成物からなる連続層を設ける。Next, a continuous layer made of a composition containing a fluorine-based compound is provided on at least one side of the base film.

連続層を設ける側は１片面のみの場合と両面ともの場合
とがあるが２片面のみの場合には、用途によってはその
反対面も何らかの易滑処理を施さなければならないとい
う必要が生じるので、好ましくは９両面ともに連続層を
設けると９本発明の効果が一層発揮できる。連続層を設
ける方法としては。The continuous layer may be provided on only one side or on both sides, but in the case of only two sides, depending on the application, it may be necessary to apply some kind of smoothing treatment to the opposite side. Preferably, the effects of the present invention can be further exhibited by providing continuous layers on both sides. As a method of providing continuous layers.

■　基体となる無延伸フィルムに、所定量に調製した前
記組成物の溶液を塗布し１次いで逐次もしくは同時に２
軸延伸し、乾燥せしめる方法。■ A solution of the composition prepared in a predetermined amount is applied to a non-stretched film that serves as a base, and then 2 coats are applied sequentially or simultaneously.
A method of axial stretching and drying.

■　基体となる無延伸フィルムを、あらかじめ一方向に
延伸して後、所定量に調製した前記組成物の（容液を塗
布し１次いで、最初の延伸方向と直交の方向に延伸し、
乾燥せしめる方法・ ■　基体となるフィルムをあらかじめ２軸延伸しておき
９次いで所定量に調製した溶液を塗布し、しかる後乾燥
する方法。(1) After pre-stretching the unstretched film as a base in one direction, applying a solution of the composition prepared in a predetermined amount, then stretching in a direction perpendicular to the initial stretching direction,
Drying method: (1) A method of biaxially stretching the base film in advance, applying a solution prepared in a predetermined amount, and then drying.

などが打型しく適用できるが、安定性と生産性の点で■
が最も打型しい。これらの方法は一般に基体フィルムの
製膜工程の終了まで（すなわち巻き取シまで）行われる
が、一旦９基体フィルム単膜として巻き取った後に、伍
布−乾燥の工程を設ける方法でもよい。丑だ、」ニム己
■９■、■の操作は基本操作であり、■、■、■の後に
、たとえば再延伸などのプロセスが加わってもか捷わな
い。塗布に処する前記組成物の溶液は、水溶液あるいは
水性ティスパージョン、水性エマルジョン、アルいは有
機溶媒浴液の形で使用できるか、有機溶媒溶液の形は作
業環境の安全−も避けるに越したことはない。etc. can be applied appropriately, but in terms of stability and productivity...
is the most typical. These methods are generally carried out until the end of the film forming process of the base film (that is, up to the point of winding), but a method may also be used in which a step of drying is provided after the base film is once wound up as a single film. The operations of ■9■ and ■ are basic operations, and it does not matter if a process such as re-stretching is added after ■, ■, ■. The solution of the composition to be applied can be used in the form of an aqueous solution, an aqueous dispersion, an aqueous emulsion, an alkaline or an organic solvent bath, or the form of an organic solvent solution is better to avoid safety in the working environment. There isn't.

塗布方法として（は、メータリングバ一方式、リバース
方式、エアナイフ方式などの公知の方法を用いることが
できる。なお、該溶液中に少量の界面活計剤（たとえは
、ステアリルアルコールなどの高級脂肪族アルコール、
ステアリル酸ブチルエステ／ｌ／　ナトの高級脂肪酸エ
ステル、ラウリン酸などの高級脂肪酸、ステアリルアミ
ドのような高級脂肪族アミド、オクチルアミンのような
高級脂肪族アミン、ドテシルベンセンスルホン酸ソーダ
）や架橋モノマ（たとえば、シランカップリング剤）や
公知の接着促進剤を加えることによって、基体フィルム
や後加工で形成せしめる層との濡れ性・接着性が増す利
点がある。なお、該溶液中には公知の添加剤たとえば帯
電防止剤、熱安定剤、紫外線吸収剤なとか本発明の効果
を損わない量で添加されていてもよいことば勿論である
。As a coating method, known methods such as a metering bar type, a reverse type, and an air knife type can be used. alcohol,
butyl stearyl ester/l/nato higher fatty acid esters, higher fatty acids such as lauric acid, higher aliphatic amides such as stearylamide, higher aliphatic amines such as octylamine, sodium dodecylbenzene sulfonate) and crosslinking monomers. By adding a known adhesion promoter (for example, a silane coupling agent) or a known adhesion promoter, there is an advantage that the wettability and adhesion with the base film and the layer formed in post-processing are increased. It goes without saying that known additives such as antistatic agents, heat stabilizers, and ultraviolet absorbers may be added to the solution in amounts that do not impair the effects of the present invention.

こうして塗布−乾燥をもってしてできる連続層の厚みは
、溶液中の固型分濃度、塗布方法、製膜工程中のどこで
塗布するかなどによシコントロールすることが可能であ
る。′−１だ、塗布する前に基体フィルムの塗布すべき
面にあらかじめコロナ放電処理などの公知の表面処理を
施しておくことは基体フィルムと該連続層との界面の接
着強度を高めるのに有用である。The thickness of the continuous layer formed by coating and drying can be controlled by controlling the concentration of solids in the solution, the coating method, and where in the film forming process the coating is applied. '-1. Before coating, it is useful to perform a known surface treatment such as corona discharge treatment on the surface of the base film to be coated in order to increase the adhesive strength at the interface between the base film and the continuous layer. It is.

次いで、得られた積層フィルムは、必要に応じで少なく
とも片面をコロナ放電処理などの公知の表面処理を施し
て９後加工時の易接着性付加をしておき２巻き取る。Next, the obtained laminated film is subjected to a known surface treatment such as corona discharge treatment on at least one side as required to add easy adhesion during post-processing, and then wound into two rolls.

（２）磁気記録媒体の製造方法： 上記積層フィルムの少なくとも片面、たとえば磁気テー
プにするためには片基、磁気ディスクにするには好まし
くは両面に、既述した磁性層を形成ぜしめて磁気記録媒
体とする。片］」１にのみ磁性層を形成させる場合、積
層フィルムがその片面のみが連続層となっているケース
で（ｒｉ、連続層側あるいはその反対側のどちらに磁性
層を形成せしめてもよいが、記録媒体としての滑り性や
電磁変換特性を総合すれは連続層側に磁性層を形成せし
めるのがより好ましい。最も好ましい組み合せは。(2) Method for manufacturing a magnetic recording medium: The above-described magnetic layer is formed on at least one side of the laminated film, for example, on one side for making a magnetic tape, and preferably on both sides for making a magnetic disk, thereby recording magnetic recording. Use as a medium. When forming a magnetic layer only on one side of the laminated film, if only one side of the laminated film is a continuous layer (ri, the magnetic layer may be formed on either the continuous layer side or the opposite side). In view of the slipperiness and electromagnetic conversion characteristics of the recording medium, it is more preferable to form the magnetic layer on the continuous layer side.The most preferable combination is.

両面ともが連続層である両面積層フィルムの少なくとも
片面に磁性層が設けられる構成のものである。すなわち
、磁性層は連続層を介して設けられるのが最も打型しい
。It has a structure in which a magnetic layer is provided on at least one side of a double-layered film having continuous layers on both sides. In other words, it is most convenient to provide the magnetic layer via a continuous layer.

〔発明の効果９作用、用途〕 本発明の積層フィルム（は、上記したように、フッ素化
合物を含む連続層が積層され、該連続層側表面の表面粗
さが特定以下という特徴ゆえ、先ず平滑性と易滑性が両
立するという効果がある。さらに９本発明積層フィルム
は、易滑性の耐久性に優れ、また耐摩耗性に優れるとい
う効果がある。[Effects of the Invention 9 Effects and Applications] As described above, the laminated film of the present invention is characterized in that continuous layers containing a fluorine compound are laminated, and the surface roughness of the surface of the continuous layer side is below a certain level. Furthermore, the laminated film of the present invention has excellent durability in terms of slipperiness and has excellent abrasion resistance.

さらに２表面粗さか小さいので、フィルムの透明性がよ
い、という効果もある。さらにロールに巻き上げた時９
巻き乱れ・スリ塩・突起の転写がないという効果がある
。Furthermore, since the surface roughness is small, the transparency of the film is also good. When further rolled up into a roll 9
The effect is that there is no irregular winding, no pickpockets, and no transfer of protrusions.

上記の効果ゆえに１本発明積層フィルムは９磁気テープ
やフロッピーディスクなどの磁気記録媒体のベースフィ
ルム、光学用ベースフィルム、コンデンサー用ベースフ
ィルム、グラフインク用ベースフィルム、包装用ベース
フィルム用ニ適シテおり、特に、最近小型軽量化が要請
されているビデオテープレコーター、磁気記録ディスク
等の磁気記録媒体ベースや、蒸着タイプ箔巻コンデンサ
ーベース用としての用途に好適である。さらに。Because of the above effects, the laminated film of the present invention is suitable for use in base films for magnetic recording media such as magnetic tapes and floppy disks, optical base films, capacitor base films, graph ink base films, and packaging base films. In particular, it is suitable for use as magnetic recording media bases such as video tape recorders and magnetic recording disks, which have recently been required to be smaller and lighter, and as bases for vapor-deposited foil-wound capacitors. moreover.

特に、磁気記録媒体のうちでも、高密度化が要請されて
いる。メタルテープ用や、蒸着またはスパッタリングに
よるテープ用やディスク用に適しておｐ、さらに最も適
しているのは、磁性層が薄くて走行性が重視される蒸着
テープ用途である。In particular, there is a demand for higher density among magnetic recording media. It is suitable for metal tapes, tapes formed by vapor deposition or sputtering, and disks, and most suitable for use in vapor-deposited tapes where the magnetic layer is thin and runnability is important.

なお、磁気記録媒体とした場合は９本発明フィルムが平
滑性と易滑性が両立しているので、従来公知の磁気記録
媒体に比べて、電磁変換特性と走付性が共に優れている
という効果を得ることができる。とりわけ、磁気テープ
とした場合、近年問題となりつつあるｒ高湿度下におけ
る舟行性の悪化」がみられないという効果がある。In addition, when used as a magnetic recording medium, the film of the present invention has both smoothness and slipperiness, so it is said to be superior in both electromagnetic conversion characteristics and running properties compared to conventionally known magnetic recording media. effect can be obtained. In particular, when magnetic tape is used, it has the effect of not causing "deterioration of navigation under high humidity," which has become a problem in recent years.

ま／こ９本発明積層フィルムの両面ともが連続層の場合
、磁気テープで走行性のために従来必要とされているバ
ックコートが不要だなるという効果もある。また蒸着テ
ィスフで磁性面保護のため。9. When both sides of the laminated film of the present invention are continuous layers, there is an advantage that a back coat, which is conventionally required for magnetic tape running properties, is not required. It is also used to protect magnetic surfaces with vapor-deposited tape.

従来必要とされているトップコートが不要になるという
効果も期待できる。It can also be expected to eliminate the need for a top coat, which is conventionally required.

上り己の効果を有するので磁気記録媒体は、磁気テープ
、磁気カード、磁気ティスフとして＋　？ＩＬ算機、オ
ーテイオ、ビテビデ計測用の各用途に用いることができ
、特にビデオ用として用いるのが打型しい。Magnetic recording media, such as magnetic tapes, magnetic cards, and magnetic disks, have their own effects. It can be used for various purposes such as IL calculator, audio, and video video measurement, and it is particularly suitable for use in video.

〔測定・評価法〕[Measurement/evaluation method]

本発明の各特性値の測定法と効果の評価基糸を次に捷と
めて示す。The methods for measuring each characteristic value and the basis for evaluating the effects of the present invention are summarized below.

（１）　　連続層の厚みｃＬ（μ）： 連続層にセロハンテープを貼り、セロテープ端部の連続
層をジメチルホルムアミド等の溶剤で溶解除去する。次
いでセロテープははがし、セロテープで保護された面と
、溶解除去した面との境界を小坂研究所製ＥＴ−１０高
精度段差測定器により測定し、埋みを求める。(1) Thickness cL (μ) of continuous layer: Cellophane tape is applied to the continuous layer, and the continuous layer at the end of the cellophane tape is dissolved and removed using a solvent such as dimethylformamide. Next, the cellophane tape is removed, and the boundary between the surface protected by the cellophane tape and the surface that has been dissolved and removed is measured using an ET-10 high-precision level difference measuring device manufactured by Kosaka Institute to determine the filling.

上記方法で困難な場合は９日立製作所製透過型電子顕微
鏡ＨＵ　−１２型を用い９型層フィルムの超薄断面切片
を観斯し、厚みを求める。If the above method is difficult, use a transmission electron microscope model HU-12 manufactured by Hitachi, Ltd. to observe an ultra-thin section of the type 9 layer film to determine the thickness.

（２）　　表面粗さ、　　Ｒａ（μ）：触針式表面伍さ
計による測定（直を示す（カットオフ０．２５　ｒｒ＝
ｒｒ＋、測定値４闘での値。但し、ＪＩＳ−Ｂ−０６０
１による）。(2) Surface roughness, Ra (μ): Measurement using a stylus type surface roughness meter (indicates directness (cutoff 0.25 rr=
rr+, measured value after 4 fights. However, JIS-B-060
1).

（３）　　臨界表面張力＋　　γＣ（ｄｙｎｅ／ｃｍ　
）　：Ａ　Ｓ　Ｔ　Ｉｖｌ　−Ｄ　−２５７８−６７Ｔ
法によって。(3) Critical surface tension + γC (dyne/cm
):AST Ivl-D-2578-67T
By law.

２Ｄ’Ｃ，６５％雰囲気下にて測定した。Measured under 2D'C, 65% atmosphere.

（４）　ＩＣ３ＣＡ法によるｙ　／　ＣＨ国際電気株式
会社製のＥＳＣＡスペクＩ・ロメータＰＩ！Ｓ−２００
型を用い、フッ素ｌ５（Ｆ１８）軌道スペクトルを測定
し、各スペクトルの積分強度比を求め９個数比率Ｆ　／
　Ｃに換算した。(4) y by IC3CA method / ESCA Spec I Rometer PI manufactured by CH Kokusai Electric Co., Ltd. S-200
Using a mold, measure the fluorine l5 (F18) orbital spectrum, calculate the integrated intensity ratio of each spectrum, and calculate the number ratio F /
Converted to C.

（５）　　表面の半円球状粒子の個数、Ｎ（個／Ｃｍ２
）：連続層側表面につ′ルミニウム蒸着し１日本光学製
微分干渉顕微鋭で写真倍率２００倍で撮影し。(5) Number of semicircular spherical particles on the surface, N (pieces/Cm2
): Aluminium was vapor-deposited on the surface of the continuous layer side, and the photograph was taken with a Nippon Kogaku differential interference microscope at a magnification of 200x.

さらに１０００倍に拡大した後、２０ｃｍ”当シに存在
する半球状粒子の突起の個数を目視で数え１ｃｍ’当り
に換算する。数える対象の大きさは１点で見えるもの（
さらに拡大すると、これが０．０５μに相当）から、直
径５ＩＩＩＩＩ１寸でのものである。After further magnifying 1000 times, visually count the number of protrusions of hemispherical particles present in a 20cm area and convert it to 1cm'.The size of the object to be counted is that which can be seen at one point (
If you enlarge it further, this corresponds to 0.05μ), so it has a diameter of 5III1.

（６）　　易滑性、すなわち、μＳ： Ａ　Ｓ　Ｔ　Ｍ　　Ｄ　−１８９４−６６により、フィ
ルムの連続層側入面同志の静摩擦係数μｓを測った。(6) Sliding property, ie, μS: The coefficient of static friction μs between the entrance surfaces of the continuous layers of the film was measured according to ASTM D-1894-66.

滑り性がよいのは、μＳが１．５以下、好１しくは１０
以下である。Good slipperiness means that μS is 1.5 or less, preferably 10
It is as follows.

（７）　　易滑性の耐久性： テープ状にしたフィルムの連続層側表面を金属（ＳＵＳ
）固定カイト（５画φ）に５００回繰返し接触走行させ
た後、上記＋６１の　μＳを測定した。(7) Durability of slipperiness: The continuous layer side surface of the tape-shaped film is made of metal (SUS
) The fixed kite (5 strokes φ) was repeatedly touched and traveled 500 times, and then the above +61 μS was measured.

走行される折のμＳよりも０１以内の差であれば耐久性
は良く（○）、差が０．１を越えれば耐久性は悪い（Ｘ
）と評価する。If the difference is within 0.1 from the μS when running, the durability is good (○), and if the difference exceeds 0.1, the durability is bad (X
).

（８）　　耐摩耗性： テープ状にしたフィルムの連続層側表面を金属（ＳＵＳ
　）固定ガイド（５ｍ［Ｉｌφ）に５００回繰返し接触
走行させた後、フィルム上に付着したスクラッチ量を観
察し、その数の多少で次のごとく評価した。(8) Abrasion resistance: The continuous layer side surface of the tape-shaped film is made of metal (SUS
) After running in contact with a fixed guide (5 m [Ilφ) 500 times, the amount of scratches adhered to the film was observed, and the number of scratches was evaluated as follows.

（９）　　高湿度下走行性、μに＝ ２５’ｃ、８５％ＲＨの環境下で１／２インチ幅にスリ
ットされたフィルムに１００ｇの荷重をかけ。(9) Runability under high humidity, 100 g of load was applied to a film slit into 1/2 inch width in an environment of μ = 25'c and 85% RH.

引き取シ速度１ｃｍ／ｓｅｃで引張った時の巻取９側テ
ンシヨンＴを求め９次式により　μｋを算出した。The tension T on the winding 9 side when the film was pulled at a take-off speed of 1 cm/sec was determined, and μk was calculated using the 9th equation.

１ μに＝−１ｏｇ− π　　　　　１００ （□１１□カ’　ｌ：’ｍ　ｌ”ｎ、□よういいケイ、
え。］磁気テープ用として、μｋ（は０５以下が好まし
く。1 μ=-1og- π 100 (□11□Ka'l:'ml"n, □Yoiikei,
picture. ] For magnetic tape, μk is preferably 05 or less.

さらには０４以下がより打型しい。Furthermore, 04 or less is more suitable for hitting.

００）　　磁気テープの走行１生ニ ア　０　Ｄ　ＯＨｚ　　の信号を記録させた試料磁気テ
ープをテープレコーダに装填して９走行開始・停止を繰
り返しながら１０ｃｍ／ｓｅｃの走行速度で走行させ。00) Running of Magnetic Tape A sample magnetic tape on which a signal of near 0 D OHz was recorded was loaded into a tape recorder and run at a running speed of 10 cm/sec while repeating 9 running starts and stops.

同時に出力を測定しながら走行時間が１００時間になる
捷で試、験しだ。その間を通じてテープがガイトローラ
に張り付いたしせずにスムーズに走行し、かつ、１００
時間後の出力低下が２．０　ｄ　Ｂ未満のものを「走行
性良好」とし、それ以外は「走行性不良」と判定した。At the same time, I measured the output and tested it on a train with a running time of 100 hours. Throughout this period, the tape runs smoothly without sticking to the guide roller, and
Those whose output decrease after hours was less than 2.0 dB were determined to have "good running performance", and the others were determined to have "poor running performance".

Ｑｌｌ　　電磁変換特注： 試料磁気記録媒体を再生した時の出力イ二号を一画面分
でみた場合に、出力信号が強く、かつ信号波形がフラッ
トであるものを「良好」、出力信号が弱いか信号波形が
変形しているものを「不良」と判定した。Qll Electromagnetic conversion custom order: When looking at the output No. 2 when reproducing the sample magnetic recording medium on one screen, it is "good" if the output signal is strong and the signal waveform is flat, and if the output signal is weak or not. Those whose signal waveforms were deformed were determined to be "defective."

実施例１ 炭素数が９のペルフルオロアルキル基を含有スる含フッ
累オリゴマエマルション、「アサヒガードｐ、ａ−７１
０Ｊ（旭硝子株式会社製）を、固型分濃度で２重量％て
なるように水溶液として調製した。Example 1 Fluorine-containing oligomer emulsion containing a perfluoroalkyl group having 9 carbon atoms, "Asahi Guard P, a-71"
0J (manufactured by Asahi Glass Co., Ltd.) was prepared as an aqueous solution with a solid content concentration of 2% by weight.

一方、固有粘度０．６５のポリエチレンテレフタレート
を２９０°Ｃで溶融押出し、静電印加しつつ２０゛Ｃの
キャストドラム上にキャストし、無延伸シートとした後
１周速差をもたせた一対のロール間で９０°Ｃで長手方
向に３６倍延伸した。On the other hand, polyethylene terephthalate with an intrinsic viscosity of 0.65 was melt-extruded at 290°C and cast onto a cast drum at 20°C while applying electrostatic charge to form a non-stretched sheet, which was then placed between a pair of rolls with a one-peripheral speed difference. The film was stretched 36 times in the longitudinal direction at 90°C.

この−軸延伸フィルムの片面に１７０Ｖｔｌ・分／、ｌ
のエイ・ルギー量のコロナ放電処処を施し、その面に該
７ツ素エマルジヨンの調製水溶液をメータＩＪ　７グバ
ーを用いて塗布した後、テンタ内で両端をクリップで把
持して９５°Ｃで幅方向に６５倍延伸し。170Vtl・min/,l on one side of this -axially stretched film
After applying a prepared aqueous solution of the 7 element emulsion to the surface using a meter IJ 7 gripper, hold both ends with clips in a tenter and heat at 95°C. Stretched 65 times in the direction.

同じくテンタ内で９幅方向に５％弛緩させつつ２１０’
ｃで５秒間熱処理して、完全に水分を除去した。210' while relaxing 5% in the width direction in the same tenter.
C for 5 seconds to completely remove moisture.

かくして得られた積層フィルムは、光学顕微鏡観察の結
果、塗布した面側の層、すなわち、フッ素系化合物を含
む層が連続層であることを確認した。寸だ、該連続層の
厚みは０口２０μであった。As a result of optical microscopic observation of the thus obtained laminated film, it was confirmed that the layer on the coated side, that is, the layer containing the fluorine compound, was a continuous layer. Indeed, the thickness of the continuous layer was 20 μm.

なお、積層フィルムの全厚み（ｄ１５μであった。Note that the total thickness of the laminated film (d was 15μ).

この積層フィルムの評価結果を第１表に示した。The evaluation results of this laminated film are shown in Table 1.

なお、連続層と反対側の面の表面粗さは０．００５５μ
であった。第１表の結果から９該積層フィルムは、平滑
性と易滑性か両立して優れ、かつ、易滑計の耐久性に優
れ、かつ、耐、輩耗件が優れ、かつ。The surface roughness of the surface opposite to the continuous layer is 0.0055μ.
Met. From the results in Table 1, 9 the laminated film has excellent smoothness and ease of slipping, has excellent durability when measured on slippage, and has excellent resistance to wear and tear.

高湿度下走行性に優れていることがわかった。It was found that it has excellent running performance under high humidity conditions.

実施例２ なる炭素数９のベルフルオロア九・キル基を有するもの
を用い、高分子固体（Ｂ）として１次のコポリエステル
エーテルを用いて混合し、塗布組成物の主成分とした。Example 2 A polymer having a perfluoroa9-kyl group having 9 carbon atoms was used and mixed with a primary copolyester ether as the polymer solid (B) to form the main component of a coating composition.

すなわち、酸成分がテレフタル酸８５モル係と５−スル
ホイノフタル酸１５モル係からなり、グ！Ｊ　−１−ル
成分カ、エチレンクリコール９５モル係とジエチレング
リコール５モル係からなる固有粘度０５７のコポリエス
テルエーテルを用いた。That is, the acid component consists of 85 moles of terephthalic acid and 15 moles of 5-sulfoinophthalic acid, and Gu! A copolyester ether having an intrinsic viscosity of 057 and consisting of 95 moles of ethylene glycol and 5 moles of diethylene glycol was used as a component.

上記ＡとＢを、固型分重量比率Ａ／Ｂ＝１／１　　にし
て８５゛Ｃ熱水に＠解せしめ２合計固型分濃度２重量係
の水溶液を調製した。なお溶解に際し、対水溶液重量で
０４０５重量係重量％ンルベンゼンス）ｖホン酸ソーダ
を添加した。The above A and B were dissolved in 85°C hot water at a solid content weight ratio of A/B = 1/1 to prepare an aqueous solution having a total solid content concentration of 2 parts by weight. During the dissolution, 0.405% by weight of sodium phonate was added based on the weight of the aqueous solution.

実施例１と同じポリエチレンテレフタレートを実施例１
と同様に一軸延伸した。その−軸延伸フィルムに、上記
水溶液を実施例１と同様に塗布し。The same polyethylene terephthalate as in Example 1 was used in Example 1.
It was uniaxially stretched in the same way. The above aqueous solution was applied to the -axially stretched film in the same manner as in Example 1.

続いて、実施例１と同様に横延伸９熱処理して積層フィ
ルムを得た。この積層フィルムを光学顕微鏡観察した結
果、塗布した面側の層、すなわち。Subsequently, in the same manner as in Example 1, the film was subjected to transverse stretching and heat treatment to obtain a laminated film. As a result of observing this laminated film with an optical microscope, the layer on the coated side, ie.

ＡとＢの混合層が連続層であることを確認した。It was confirmed that the mixed layer of A and B was a continuous layer.

また、該連続層の厚みは、０．０１３μであった。Further, the thickness of the continuous layer was 0.013μ.

なお、積層フィルムの全厚みは１５μであった。Note that the total thickness of the laminated film was 15 μm.

この積層フィルムの評価結果を第１表に示した。The evaluation results of this laminated film are shown in Table 1.

第１表の結果から、該積層フィルムは、平滑性と易滑性
が両立して優れ、かつ、易滑性の耐久性に優れ、かつ、
耐摩耗性に優れ、かつ高湿度下走行性に優れていること
がわかった。From the results in Table 1, it can be seen that the laminated film has both excellent smoothness and easy sliding properties, has excellent durability of easy sliding properties, and
It was found that it has excellent abrasion resistance and excellent running performance under high humidity.

実施例ろ、４および比較例１．２ フッ素化合物の固型分濃度をそれぞれＯ０５゜０．５，
４．．１０各重最％とし／ζ以外＋ｄ　、実施例１と同
様にして、積層フィルムを得だ。全ての積層フィルムの
塗布層は連続層になっていた。上記濃度の順にそれぞれ
を、比較例１．実施例３９実施例４．比較例２とし、そ
れら積層フィルムの評価結果を第２表に示しだ。第２表
から、実施例ろ。Example 4 and Comparative Example 1.2 The solid concentration of the fluorine compound was O05°0.5, respectively.
4. ．． A laminated film was obtained in the same manner as in Example 1, with the maximum weight of each weight being 10/+d except for ζ. The coating layers of all laminated films were continuous layers. Comparative Example 1. Example 39 Example 4. As Comparative Example 2, the evaluation results of these laminated films are shown in Table 2. Examples from Table 2.

４が平滑性、易謂性を両立して優らしめることがわかる
。比較例３は易滑性に欠け、比較例４は平滑性に欠ける
ことかわかる。It can be seen that 4 provides both smoothness and ease of error. It can be seen that Comparative Example 3 lacks slipperiness, and Comparative Example 4 lacks smoothness.

実施例５ 実施例１において、塗布を両面に同時に同一条件で行な
った以外は９全ての条件を実施例１と同様にして、全厚
み１５μの両面積層フィルムを得た。該両面積層フィル
ム断面を光学顕微鏡観察した結果１片面（０面）も他の
片面（＠而）の両側層ともが連続層だなっていた。それ
ぞれの連続層の厚みは、０面側が００２１μ、＠面側が
００２３μであった。各面の評価結果を第３表に示した
。Example 5 A double-sided laminated film with a total thickness of 15 μm was obtained under all nine conditions as in Example 1, except that coating was performed on both sides simultaneously under the same conditions. As a result of optical microscopic observation of the cross section of the double layered film, it was found that both the layers on one side (0 side) and the other side (@) were continuous layers. The thickness of each continuous layer was 0021 μm on the 0 side and 0023 μm on the @ side. The evaluation results for each aspect are shown in Table 3.

第３表の結果から、該両面積層フィルムは、平滑性と易
滑性が両立して優れ９かつ、易滑性の耐久性に優れ、か
つ高湿度上走行性に優れていることがわかる。次いで、
０面（テ、磁性層としてＣｏ−Ｎｉ　　合金を９厚さ１
０００Ｈになるように真空蒸着し、１／２インチ幅にス
リンｌ−して所定の蒸着磁気テープとした。この磁気テ
ープを評価した結果。From the results in Table 3, it can be seen that the double layered film has both excellent smoothness and easy sliding properties9, excellent durability of easy sliding properties, and excellent runnability under high humidity conditions. Then,
0 side (Te, Co-Ni alloy as magnetic layer 9 thickness 1
The magnetic tape was vacuum-deposited to a thickness of 000H, and then rinsed to a width of 1/2 inch to obtain a predetermined vapor-deposited magnetic tape. The results of evaluating this magnetic tape.

磁気テープの走行性と電磁変換特性がともに１良好」で
あった。The running properties of the magnetic tape and the electromagnetic conversion characteristics were both rated as 1 good.

Claims (1)

【特許請求の範囲】[Claims] （１）基体フィルム層の少なくとも片面に、フッ素化合
物を含む連続層が積層されてなる積層フィルムであり、
フッ素系化合物か積層された側の表面の表面粗さくＲａ
）が、　０．０１５〜Ｏ，ＯＯ５／４であることを特徴
とする積層フィルム。(1) A laminated film in which a continuous layer containing a fluorine compound is laminated on at least one side of a base film layer,
Surface roughness Ra of the surface on which the fluorine-based compound is laminated
) is 0.015 to O, OO5/4.