JPS59142252A - Resin composition - Google Patents
Resin compositionInfo
- Publication number
- JPS59142252A JPS59142252A JP1644983A JP1644983A JPS59142252A JP S59142252 A JPS59142252 A JP S59142252A JP 1644983 A JP1644983 A JP 1644983A JP 1644983 A JP1644983 A JP 1644983A JP S59142252 A JPS59142252 A JP S59142252A
- Authority
- JP
- Japan
- Prior art keywords
- ferrite powder
- compsn
- resin
- molecular compd
- stabilizer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
産業上の利用分野
本発明はフェライト粉末を含んだ磁性を付与し得る樹脂
組成物に関する。DETAILED DESCRIPTION OF THE INVENTION Field of the Invention The present invention relates to a resin composition containing ferrite powder and capable of imparting magnetism.
従来例の構成とその問題点
フェライト粉等を含んだ磁性を付与し得る樹脂組成物に
おいて磁気特性を向上させる一手段としてフェライト粉
等の磁性体の充填率向上がある。Structure of the conventional example and its problems One means for improving the magnetic properties of a resin composition containing ferrite powder and the like that can impart magnetism is to improve the filling rate of a magnetic material such as ferrite powder.
しかし、従来の樹脂組成物においてフェライト粉等の磁
性体の充填率向上には加工性、生産性から限界があった
。そこで、加工面から磁気特性を向上させるため外部か
らフェライト粉の配向に必要な磁場、あるいは機械的な
力等を加える取組みがなされていた。しかし、その磁気
特性には限界があった。すなわち、樹脂によりフェライ
ト焼結晶等と比べ単位体積当りの磁性体の充填率が少な
いという問題があった。However, in conventional resin compositions, there are limits to improving the filling rate of magnetic materials such as ferrite powder due to processability and productivity. Therefore, efforts have been made to externally apply a magnetic field or mechanical force necessary to orient the ferrite powder in order to improve the magnetic properties from the processed surface. However, there were limits to its magnetic properties. That is, due to the resin, there is a problem that the filling rate of the magnetic material per unit volume is lower than that of ferrite sintered crystals or the like.
発明の目的
本発明はこのような従来の問題を解決するフェライト粉
等を含んだ磁性を付与し得る樹脂ml成物に関するもの
であり、そのポイントはフェライト粉の充填率を向上さ
せるため分子量1万以下の高分子化合物を組成物中に含
み、最終的には組成物から、該高分子化合物を取り出す
ことにより実質的にフェライト粉の充填率向上をはかり
磁気特性を向上することにある。OBJECTS OF THE INVENTION The present invention relates to a resin ml composition containing ferrite powder and the like that can impart magnetism to solve such conventional problems. The purpose is to substantially improve the filling rate of ferrite powder and improve the magnetic properties by including the following polymer compound in the composition and ultimately removing the polymer compound from the composition.
発明の構成
本発明の樹脂組成物は分子量1万以下の高分子化合物を
組成物中に含むことにより加工性を向上させると共にフ
ェライト粉の配向率を向上させて、更にその分子量1万
以下の高分子化合物を最終的には組成物から収り出すこ
とにより実質的にフエライト粉の充填率向上をはかるも
のである。Structure of the Invention The resin composition of the present invention improves processability and improves the orientation rate of ferrite powder by including a high molecular compound with a molecular weight of 10,000 or less in the composition. By ultimately extracting the molecular compound from the composition, the filling rate of the ferrite powder is substantially improved.
実施例の説明
実施例1〜12
6ナイロン(分子量約17000)、加工助剤(Ca
−St ) 、有機チタン系化合物にて表面処理を施し
たフェライト粉末と分子量1万以下の高分子化合物(エ
ポキシ樹脂)をそれぞれ表−1に示す条件に従い、混練
し、その後約1M立方の大きさに粉砕し、L/D=28
.φθ5の押出し機にて成形した。第1ステツプで芯材
に樹脂マグネット組成物を被覆し、第2ステツプ以降で
分子量1万以下の高分子化合物を取り出す高温、圧縮ゾ
ーンを設けてなるダイスを取り付は押出し成形を行ない
直径約17.5mmで芯材の周囲に高充填のフェライト
粉を含む樹脂マグネット組成物を形成したロール体を得
た。このロール体を所定の寸法に加工し、6極の着磁を
行ない表−1に示す磁気特性を有すルマグネティノクロ
ールを得た。Description of Examples Examples 1 to 12 6 Nylon (molecular weight approximately 17,000), processing aid (Ca
-St), ferrite powder surface-treated with an organic titanium compound and a polymer compound (epoxy resin) with a molecular weight of 10,000 or less are kneaded according to the conditions shown in Table 1, and then mixed into a powder with a size of about 1M cubic. Grind to L/D=28
.. It was molded using an extruder with a diameter of φθ5. In the first step, the core material is coated with a resin magnet composition, and in the second and subsequent steps, a die with a high temperature and compression zone for extracting polymer compounds with a molecular weight of 10,000 or less is attached and extrusion molding is performed. A roll body was obtained in which a resin magnet composition containing highly filled ferrite powder was formed around a core material with a thickness of .5 mm. This roll body was processed to a predetermined size and magnetized with six poles to obtain a Lumagnetino roll having the magnetic properties shown in Table 1.
以下余白
表−1
発明の効果
実施例からも明らかなように、本発明では分子量1万以
下の高分子化合物を組成物中に含むことにより加工時の
見掛は粘度の低下による流れ性の向上、組成物の粘度低
下によるフェライト粉の自由度の大きいこと、更には、
ダイスの高温、強圧綿、強制吸収等による分子量1万以
下の高分子化合物の取り出しによるフェライト粉の体積
充填率の向上環の効果によシ磁気特性の向上を果すこと
が出来る効果を奏するものである。Margin Table 1 Below: Effects of the Invention As is clear from the examples, in the present invention, by including a polymer compound with a molecular weight of 10,000 or less in the composition, the apparent viscosity during processing is reduced and flowability is improved. , a greater degree of freedom for the ferrite powder due to the reduced viscosity of the composition;
It has the effect of improving the volumetric filling rate of ferrite powder by extracting a polymer compound with a molecular weight of 10,000 or less by using a high temperature die, high pressure cotton, forced absorption, etc. The magnetic properties can be improved by the ring effect. be.
Claims (1)
・nFe2o3で示されるフェライト粉末及び分子量1
万以下高分子化合物を含んだ樹脂組成物。a binder consisting of a thermoplastic resin and a stabilizer, and a general formula M.O.
・Ferrite powder represented by nFe2o3 and molecular weight 1
A resin composition containing a polymer compound of less than 10,000 yen.