JPH1177872A - Easily cuttable laminate film packaging material - Google Patents
Easily cuttable laminate film packaging materialInfo
- Publication number
- JPH1177872A JPH1177872A JP25178397A JP25178397A JPH1177872A JP H1177872 A JPH1177872 A JP H1177872A JP 25178397 A JP25178397 A JP 25178397A JP 25178397 A JP25178397 A JP 25178397A JP H1177872 A JPH1177872 A JP H1177872A
- Authority
- JP
- Japan
- Prior art keywords
- layer
- packaging material
- film
- laminated film
- line
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、多層に積層ラミー
トされた積層フィルム包材の切り離しすべき個所に容易
にカッティング可能な切り離し線を設け、該切り離し線
を介して容易にカッティング可能な易カット性積層フィ
ルム包材に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a multi-layer laminated laminating film packaging material which is provided with a cutting line which can be easily cut at a place to be cut, and which can be easily cut through the cutting line. The present invention relates to a functional laminated film packaging material.
【０００２】[0002]
【従来の技術】従来より多層に積層ラミネートされた積
層フィルム包材としては各種のフィルム包材があるが、
このような積層フィルム包材には、このフィルム包材を
容易に引き裂きカッティングするために、積層されるフ
ィルムのいずれかのフィルムを一軸延伸フィルムとし
て、その延伸方向に直線状に引き裂き可能にした易カッ
ト性積層フィルム包材がある。2. Description of the Related Art Conventionally, various film packaging materials have been used as a laminated film packaging material in which a multilayer is laminated.
In such a laminated film packaging material, in order to easily tear and cut the film packaging material, any one of the films to be laminated is made to be a uniaxially stretched film, and the film is easily torn linearly in the stretching direction. There is a cut laminate film packaging material.
【０００３】また、易カット性積層フィルム包材として
は、積層フィルム包材の所定個所にミシン目加工により
直線状のミシン目を貫設して、そのミシン目を切り離し
線として引き裂き易くしたものがある。[0003] In addition, as an easy-cut laminated film packaging material, there is a laminated film packaging material in which a linear perforation is formed through a perforation at a predetermined position of the laminated film packaging material, and the perforation is easily cut off as a separation line. is there.
【０００４】[0004]
【発明が解決しようとする課題】ところで、上記積層フ
ィルム包材などにおけるレトルト食品を包装する密封性
が要求されるようなレトルトパウチ用の易カット性積層
フィルム包材の場合は、フィルムを多層に積層ラミート
した後にミシン目を貫設すると、そのミシン目によって
密封性が損なわれるものである。By the way, in the case of an easy-cut laminated film packaging material for a retort pouch in which the hermeticity for packaging the retort food in the laminated film packaging material or the like is required, the film is formed into a multilayer. If a perforation is pierced after lamination, the sealing property is impaired by the perforation.
【０００５】そのため従来は、図５に示すように、例え
ば多層にラミネートすべき複数のフィルム２１（例えば
延伸ナイロン）、フィルム２２（例えば無延伸ナイロ
ン）、フィルム２３（例えばアルミニウム箔）、フィル
ム２４（例えばポリエチレンテレフタレート）のうち、
例えば１枚のフィルム２１に対して、予めミシン目２１
ａを貫設して易カット性を付与しておき、その後に、そ
のフィルム２１の表裏両面に他のフィルム２２、２３を
接着剤層２５、２６を介して積層ラミネートし、更に必
要に応じてフィルム２４を接着剤層２７を介してフィル
ム２３に積層ラミネートして密封性を確保した切り離し
線を備えた易カット性積層フィルムＡがある。Conventionally, as shown in FIG. 5, for example, a plurality of films 21 (for example, stretched nylon), a film 22 (for example, non-stretched nylon), a film 23 (for example, aluminum foil), and a film 24 (for example, aluminum foil) to be laminated in multiple layers. For example, polyethylene terephthalate)
For example, for one film 21,
a to penetrate the film 21 to provide easy-cutting properties. Thereafter, other films 22 and 23 are laminated and laminated on the front and back surfaces of the film 21 via the adhesive layers 25 and 26, and if necessary. There is an easy-cut laminating film A provided with a separating line which secures the sealing property by laminating the film 24 on the film 23 via the adhesive layer 27.
【０００６】上記レトルトパウチ用包装袋に食品を密封
包装したレトルトパウチ食品は、一般的に湯温により加
熱した後に、切り離し線に沿って引き裂き開封するもの
で、開封時に異常に引裂抵抗が高かったり、あるいはミ
シン目による不連続な引裂抵抗の高低差による反動によ
って高温に加熱された内容物が不用意に人体に付着して
不快な熱さを感じさせたり、また火傷の原因となる場合
もある。[0006] The retort pouch food in which the food is hermetically sealed and packed in the retort pouch packaging bag is generally heated by hot water temperature, and then tears open along the separation line. Alternatively, the contents heated to a high temperature may be inadvertently adhered to the human body due to the recoil due to the discontinuous tearing resistance difference due to the perforations, causing unpleasant heat or causing a burn.
【０００７】そのため、レトルトパウチにおいては、近
年、特に開封時における引裂抵抗の低減化や不連続な引
裂抵抗における高低差の低減化が望まれている。[0007] For this reason, in retort pouches, in recent years, it has been desired to reduce the tear resistance particularly at the time of opening, and to reduce the difference in elevation in discontinuous tear resistance.
【０００８】本発明は、上記不都合を解消して、レトル
トパウチとしての密封性を確保するとともに、引裂抵抗
及び不連続な引裂抵抗における高低差の低減化のために
改良したレトルトパウチ食品などの包装に使用する積層
フィルム包材を提供することにある。[0008] The present invention solves the above-mentioned inconveniences, secures the hermeticity of a retort pouch, and improves the packaging of retort pouch foods and the like in order to reduce the height difference in tear resistance and discontinuous tear resistance. It is to provide a laminated film packaging material used for (1).
【０００９】[0009]
【課題を解決するための手段】本発明は、基材フィルム
層の片面に総厚の１／２以上の厚さを有するシーラント
層を備えた積層フィルムの前記シーラント層側から波長
８００〜８０００ｎｍの範囲のレーザー光線を照射して
加熱することにより前記シーラント層を薄化して得られ
た連続ハーフカット線形状若しくはミシン目形状など断
続ハーフカット線形状の薄膜層による切り離し線が設け
られていることを特徴とする易カット性積層フィルム包
材である。According to the present invention, there is provided a laminated film having a sealant layer having a thickness of 1/2 or more of the total thickness on one surface of a base film layer, the laminated film having a wavelength of 800 to 8000 nm from the sealant layer side. A cutting line is provided by a thin film layer having an intermittent half-cut line shape such as a continuous half-cut line shape or a perforated shape obtained by irradiating a laser beam in a range and heating to thin the sealant layer. It is an easy-cut laminated film packaging material.
【００１０】また本発明は、上記発明の易カット性積層
フィルム包材において、前記レーザー光線が波長８００
〜８０００ｎｍの範囲のレーザー光線である易カット性
積層フィルム包材である。[0010] The present invention also provides the easy-cut laminate film packaging material of the above invention, wherein the laser beam has a wavelength of 800.
This is an easily cuttable laminated film packaging material that emits a laser beam in the range of 8000 nm.
【００１１】また本発明は、上記発明の易カット性積層
フィルム包材において、前記薄膜層による切り離し線が
レーザー光線を照射して加熱すると共に押し罫型を用い
て押し罫加工することにより設けられている易カット性
積層フィルム包材である。Further, the present invention provides the easily cuttable laminated film packaging material according to the above invention, wherein the cut line by the thin film layer is provided by irradiating a laser beam and heating and performing a pressing process using a pressing rule. Easy-cut laminated film packaging material.
【００１２】また本発明は、上記発明の易カット性積層
フィルム包材において、前記薄膜層の層厚がシーラント
層の層厚１００％に対して１０〜６０％、好ましくは３
０〜５０％である易カット性積層フィルム包材である。The present invention also provides the easy-cut laminated film packaging material of the present invention, wherein the thickness of the thin film layer is 10 to 60%, preferably 3 to 100% of the thickness of the sealant layer.
It is an easy-cutting laminated film packaging material having 0 to 50%.
【００１３】また本発明は、上記発明の易カット性積層
フィルム包材において、前記基材フィルム層がポリエチ
レンテレフタレートフィルム若しくはポリエチレンテレ
フタレートフィルムとアルミニウム箔若しくはポリエチ
レンテレフタレートフィルムと延伸ナイロンフィルム若
しくはポリエチレンテレフタレートフィルムとアルミニ
ウム箔と延伸ナイロンフィルムとの複合フィルム層であ
り、前記シーラント層が無延伸ポリプロピレン、ポリエ
チレン、エチレン−酢酸ビニル共重合体のいずれかであ
る易カット性積層フィルム包材である。[0013] The present invention also provides the easy-cut laminated film packaging material according to the above invention, wherein the base film layer is a polyethylene terephthalate film or a polyethylene terephthalate film and an aluminum foil, or a polyethylene terephthalate film and a stretched nylon film or a polyethylene terephthalate film and aluminum. An easy-cut laminated film packaging material, which is a composite film layer of a foil and a stretched nylon film, wherein the sealant layer is any of unstretched polypropylene, polyethylene, and ethylene-vinyl acetate copolymer.
【００１４】また本発明は、上記発明の易カット性積層
フィルム包材において、前記レーザー光線がＹＡＧレー
ザー、Ａｒレーザー、半導体レーザー又は炭酸ガスレー
ザーのいずれかである易カット性積層フィルム包材であ
る。[0014] The present invention also provides an easy-cut laminated film packaging material according to the above invention, wherein the laser beam is any one of a YAG laser, an Ar laser, a semiconductor laser and a carbon dioxide laser.
【００１５】[0015]
【作用】本発明の易カット性積層フィルム包材は、積層
フィルムの総厚の１／２以上の厚さのシーラント層側か
ら切り離し線の形状に波長８００〜８０００ｎｍの範囲
のレーザー光線を照射して、このシーラント層を加熱溶
融若しくは軟化により薄化させて、レーザー光線の照射
されない部分のシーラント層の層厚１００％に対して１
０〜６０％、好ましくは３０〜５０％の層厚の薄膜層が
形成され、この薄膜層を切り離し線としたものであり、
この積層フィルムに形成された薄膜層の層厚は、積層フ
ィルムの全層厚に対してもかなり薄くなっているため、
ハーフカット状の切り離し線として、この薄膜層に沿っ
て低い引裂抵抗によって容易にカッティングすることが
できるものである。The easily cuttable laminated film packaging material of the present invention is obtained by irradiating a laser beam having a wavelength in the range of 800 to 8000 nm to the shape of a separation line from the sealant layer having a thickness of 1/2 or more of the total thickness of the laminated film. This sealant layer is thinned by heat melting or softening, and the thickness of the sealant layer is 100% of the thickness of the sealant layer not irradiated with the laser beam.
A thin film layer having a thickness of 0 to 60%, preferably 30 to 50% is formed, and this thin film layer is used as a separation line,
Because the layer thickness of the thin film layer formed on this laminated film is considerably smaller than the total layer thickness of the laminated film,
A half-cutting separation line can be easily cut along the thin film layer with a low tear resistance.
【００１６】また、本発明の易カット性積層フィルム包
材は、シーラント層側から切り離し線の形状にレーザー
光線を照射して加熱溶融若しくは軟化させながら、その
溶融若しくは軟化している部分に沿ってライナー状若し
くはローラー状の押し罫型を用いてプレス押圧により押
し罫加工して薄膜層にした切り離し線が設けられてお
り、この積層フィルムに形成された薄膜層の層厚は、積
層フィルムの全層厚に対してもかなり薄くなっているた
め、ハーフカット状の切り離し線である薄膜層に沿って
低い引裂抵抗によって容易にカッティングすることがで
きるものである。Further, the easily cuttable laminated film packaging material of the present invention can be produced by irradiating a laser beam in a shape of a separation line from the sealant layer side to heat and melt or soften the liner, and apply a liner along the melted or softened portion. A cutting line formed by pressing and pressing into a thin film layer using a press shape using a shape of a roller or a roller is provided, and the thickness of the thin film layer formed on the laminated film is equal to the total thickness of the laminated film. Since the thickness is considerably smaller than the thickness, cutting can be easily performed with a low tear resistance along the thin film layer which is a half-cut-shaped separation line.
【００１７】また、本発明の易カット性積層フィルム包
材の切り離し線は、ミシン目状など断続線状に形成され
ていてもよいが、なるべく連続線状とすることによっ
て、引き裂き開封時において引裂抵抗の不連続性による
不容易な断続的な反動が発生せず、レトルト食品包装用
のパウチとして円滑に開封することができる。Further, the separation line of the easily cuttable laminated film packaging material of the present invention may be formed in an intermittent line shape such as a perforated line. An easy intermittent recoil due to discontinuity of resistance does not occur, and the pouch for retort food packaging can be smoothly opened.
【００１８】また、本発明の易カット性積層フィルム包
材の切り離し線は、ミシン目状など断続線状に形成され
ていてもよく、切り離し線の全長に亘って薄膜層であっ
て且つミシン目状など断続線状に形成されていることに
より、引き裂き開封時において発生する不連続な引裂抵
抗の高低差が低減化でき、よってき開封時における不容
易な反動が低減でき、レトルト食品包装用のパウチとし
て円滑に開封することができる。Further, the separation line of the easy-cut laminated film packaging material of the present invention may be formed in an intermittent line shape such as a perforated line, and is formed as a thin film layer over the entire length of the separation line. Is formed in an intermittent line shape, thereby reducing the difference in the level of discontinuous tear resistance generated at the time of tear-opening, and thereby reducing unsatisfactory recoil at the time of opening. Can be opened smoothly as a pouch.
【００１９】[0019]
【発明の実施の形態】本発明の易カット性積層フィルム
包材を、図１に示す実施の形態にしたがって以下に詳細
に説明する。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS An easily cuttable laminated film packaging material of the present invention will be described below in detail according to an embodiment shown in FIG.
【００２０】図１は、本発明の易カット性積層フィルム
包材Ａの側断面図であり、基材フィルム層１側は、１層
のフィルム層２乃至２層に積層ラミネートされたフィル
ム層２、３など２層以上の積層ラミネートされた複合フ
ィルムからなっていて、例えば該基材フィルム層１のフ
ィルム層２はポリエチレンテレフタレートフィルム、フ
ィルム層３はアルミニウム箔又は延伸ナイロンフィル
ム、又はアルミニウム箔と延伸ナイロンフィルムとの複
合フィルムである。FIG. 1 is a side sectional view of an easily cuttable laminated film packaging material A according to the present invention. The base film layer 1 has a film layer 2 laminated on one film layer 2 or two. , The base film layer 1 is made of a polyethylene terephthalate film, the film layer 3 is made of an aluminum foil or stretched nylon film, or stretched with an aluminum foil. It is a composite film with a nylon film.
【００２１】前記基材フィルム層１の片面にはシーラン
ト層１０が積層ラミネートされており、シーラント層１
０は無延伸ポリプロピレン、ポリエチレン、エチレン−
酢酸ビニル共重合体などが使用されている。A sealant layer 10 is laminated and laminated on one surface of the base film layer 1.
0 is unstretched polypropylene, polyethylene, ethylene-
A vinyl acetate copolymer or the like is used.
【００２２】本発明の易カット性積層フィルム包材Ａ
は、シーラント層１０側から切り離し線を形成すべき部
分に対して、波長８００〜８０００ｎｍの範囲にあるレ
ーザー光線を連続線若しくはミシン線など断続線形状に
照射してシーラント層１０を熱溶融することにより薄化
させて、ハーフカット形状の薄膜層Ｂによる切り離し線
２０が設けられている。なお、レーザー光線の照射は、
長巻き状の積層フィルムを巻き出しながら、その巻き出
し方向に沿って行うことができる。The easily cuttable laminated film packaging material A of the present invention
Is irradiated with a laser beam having a wavelength in the range of 800 to 8000 nm in a discontinuous line shape such as a continuous line or a perforated line to a portion where a separation line is to be formed from the sealant layer 10 side, thereby thermally melting the sealant layer 10. Separation lines 20 are provided by thinning the thin film layer B in a half-cut shape. In addition, irradiation of laser beam,
The unwinding can be performed along the unwinding direction while unwinding the long rolled laminated film.
【００２３】また、本発明の易カット性積層フィルム包
材Ａは、シーラント層１０側から切り離し線を形成すべ
き部分に対して、波長８００〜８０００ｎｍの範囲にあ
るレーザー光線を照射して熱溶融し、熱溶融されている
部分を、ライナー状若しくはローラー状の押し罫型を用
いてプレスして押し罫加工することにより、連続線若し
くはミシン線など断続線によるハーフカット形状の薄膜
層Ｂによる切り離し線２０が設けられている。なお、レ
ーザー光線の照射及び押し罫型によるプレス加工は、長
巻き状の積層フィルムを巻き出しながら、その巻き出し
方向に沿ってレーザー光線の照射を行いながら、その照
射ラインに整合させたローラー状の押し罫型を押圧回転
させながら行うことができる。The easy-cut laminated film packaging material A of the present invention is heated and melted by irradiating a laser beam having a wavelength in the range of 800 to 8000 nm to a portion where a separation line is to be formed from the sealant layer 10 side. By pressing the hot-melted portion using a liner-shaped or roller-shaped pressing rule and pressing the line, a cutting line is formed by a half-cut thin film layer B by a discontinuous line such as a continuous line or a sewing line. 20 are provided. The laser beam irradiation and pressing by the press-type mold are performed by unrolling a long-winding laminated film, irradiating the laser beam along the unwinding direction, and applying a roller-shaped pressing aligned with the irradiation line. This can be performed while pressing and rotating the ruler.
【００２４】前記薄膜層Ｂは、レーザー光線を照射又は
レーザー光線を照射しながら押し罫加工することによ
り、レーザー光線の照射された前記シーラント層１０の
表面は熱溶融されて、照射されない部分に比較して薄膜
状に形成されている部分であって、レーザー光線の照射
により形成された前記シーラント層１０の薄膜層Ｂの層
厚Ｔ1 は、照射されない部分の層厚Ｔ0 に対して、
Ｔ1 ：Ｔ0 ＝１０〜６０：１００、好ましくはＴ1 ：Ｔ
0 ＝３０〜５０：１００となる比率にて設定されてい
る。The thin film layer B is subjected to creasing while irradiating a laser beam or irradiating a laser beam so that the surface of the sealant layer 10 irradiated with the laser beam is melted by heat, and the thin film layer B is thinner than a portion not irradiated. a portion formed in Jo, thickness T 1 of the film layer B of the sealant layer 10 formed by irradiation of laser beam, the layer thickness T 0 of the portion not irradiated,
T 1 : T 0 = 10 to 60: 100, preferably T 1 : T
0 = 30 to 50: 100.
【００２５】図２は、本発明の一実施の形態による積層
フィルム包材Ａのシーラント層１０側から見た該フィル
ムＡに形成された切り離し線２０の平面図であり、切り
離し線２０となる薄膜層Ｂはその全長に亘ってほぼ同じ
層厚Ｔ1 に薄膜状となっている。FIG. 2 is a plan view of a separation line 20 formed on the laminated film packaging material A according to one embodiment of the present invention as viewed from the sealant layer 10 side of the film A. layer B has a thin film substantially in the same thickness T 1 along its entire length.
【００２６】図３（ａ）は、本発明の他の実施の形態に
よる積層フィルム包材Ａのシーラント層１０側から見た
該フィルムＡに形成された切り離し線２０の平面図であ
り、切り離し線２０となる薄膜層Ｂは、その全長に亘っ
てほぼ同じ層厚Ｔ1 のミシン目状など断続線形状の薄膜
層Ｂ1 を形成したものである。FIG. 3A is a plan view of a separation line 20 formed on the film A of the laminated film packaging material A according to another embodiment of the present invention, as viewed from the sealant layer 10 side. The thin film layer B having a thickness of 20 is formed by forming a thin film layer B 1 having an intermittent line shape such as a perforated shape having substantially the same layer thickness T 1 over its entire length.
【００２７】図３（ｂ）は、本発明のその他の実施の形
態による積層フィルム包材Ａのシーラント層１０側から
見た該フィルムＡに形成された切り離し線２０の平面図
であり、切り離し線２０となる薄膜層Ｂは、その全長に
亘ってほぼ同じ層厚Ｔ1 に薄膜状となっているととも
に、その層厚Ｔ1 の薄膜層Ｂの領域内の全長に亘って、
さらに薄膜状に層厚Ｔ2 （Ｔ1 ＞Ｔ2 ）の断続線形状の
薄膜層Ｂ1 を形成したものである。FIG. 3B is a plan view of a separating line 20 formed on the film A as viewed from the sealant layer 10 side of the laminated film packaging material A according to another embodiment of the present invention. The thin film layer B having a thickness of 20 has a thin film shape with substantially the same layer thickness T 1 over the entire length thereof, and has a thin film layer B over the entire length in the region of the thin film layer B having the layer thickness T 1 .
In which further to form a thin film layer B 1 intermittent line shape of the layer thickness T 2 (T 1> T 2 ) in a thin film shape.
【００２８】この場合Ｔ2 は、積層フィルム包材Ａの全
層厚Ｔ0 及び薄膜層Ｂの層厚Ｔ1 に対して、Ｔ2 ：Ｔ0
＝１０〜６０：１００、好ましくはＴ2 ：Ｔ0 ＝３０〜
５０：１００、及びＴ1 ＞Ｔ2 の関係が成立するように
設定される。なお、０＜Ｔ1−Ｔ2 ＜３〜１０が適当で
ある。The relative thickness T 1 of the this case T 2 are the total thickness T 0 and the thin film layer B of the laminated film packaging material A, T 2: T 0
= 10 to 60: 100, preferably T 2 : T 0 = 30 to
50: 100 and the relationship of T 1 > T 2 is established. Note that 0 <T 1 −T 2 <3 to 10 is appropriate.
【００２９】本発明の易カット性積層フィルム包材Ａ
は、シーラント層１０側を内面として二枚重ねにして、
図４に示すように、食品を包装するとともにその周囲１
４を加熱シールすることにより、レトルト用食品や電子
レンジ加熱調理用食品類を密封包装するためのパウチ容
器Ｃとすることができる。Easy-cut laminated film packaging material A of the present invention
Is made into two sheets with the sealant layer 10 side as the inner surface,
As shown in FIG.
By heat-sealing 4, a pouch container C for hermetically packaging food for retort and food for microwave cooking can be obtained.
【００３０】該パウチ容器Ｃの一端部から他端部に亘っ
て薄膜層Ｂによる切り離し線２０を設け、必要に応じて
形成した切込部１５を開封の開始点として、この切り離
し線２０に沿ってカット性積層フィルム包材Ａを容易に
引き裂き開封できるレトルトパウチ容器とすることがで
きる。A cut line 20 made of the thin film layer B is provided from one end to the other end of the pouch container C, and the cut portion 15 formed as necessary is used as a starting point of opening along the cut line 20. Thus, it is possible to obtain a retort pouch container that can easily tear open the cut laminated film packaging material A.
【００３１】[0031]
【実施例】以下に本発明の易カット性積層フィルム包材
Ａの具体的実施例を説明する。EXAMPLES Specific examples of the easily cuttable laminated film packaging material A of the present invention will be described below.
【００３２】＜実施例１＞図１に示すようにフィルム層
２にポリエチレンテレフタレートフィルム（厚さ１２μ
ｍ）を用いて、その表面にドライラミネート用接着剤
（例えばウレタン系二液硬化型接着剤）を固形分含有率
が４．０ｇ／ｍ2 若しくはそれ以上となるように塗布乾
燥させて形成したドライラミネート用接着剤層４を介し
てアルミニウム箔をフィルム層３（厚さ７μｍ）として
重ね合わせドライラミネートして基材フィルム層１を形
成した。次に、このアルミニウム箔によるフィルム層３
の表面に、ドライラミネート用接着剤（例えばウレタン
系二液硬化型接着剤）を固形分含有率が２．０ｇ／ｍ2
となるように塗布乾燥させて形成したドライラミネート
用接着剤層５を介して無延伸ポリプロピレンフィルム
（厚さ７０μｍ）をシーラント層１０として重ね合わせ
ドライラミネートして積層フィルム包材を作製した。続
いて、この積層フィルム包材を１００ｃｍ／分の速度に
て移動させながらシーラント層１０の表面に切り離し線
状にＹＡＧレーザー（波長；８００ｎｍ、照射スポット
径；４ｍｍ、出力；５０ＭＷ／ｃｍ2 、パルス幅；７０
ｎｓ、製造メーカー；ホヤコンテニュアム、機種名；カ
スタム）を照射してシーラント層１０を加熱軟化させて
連続線状に薄化させ、薄化深さ３０μｍ、幅０．２ｍｍ
の薄膜層Ｂが得られた。なお、薄膜層Ｂと相対する基材
フィルム層１側の表面には薄膜層Ｂに沿って高さ１５〜
２０μｍの連続線状の盛り上がり線が得られた。これに
よって、積層フィルム包材に薄膜層Ｂによる切り離し線
２０の形成された本発明の易カット性積層フィルム包材
Ａを得た。（図２参照） このようにして得られた本発明の易カット性積層フィル
ム包材Ａをシーラント層１０を内面にしてその切り離し
線２０が表裏で一致するように整合して二枚重ねにした
後、三方周囲を加熱シールしてレトルト食品包装用パウ
チを製袋し、このパウチを切り離し線２０に沿って切り
裂いた結果、引裂抵抗２００ｇｆ若しくはそれ以下の低
い抵抗値にて良好な直線カット性（切り離し線２０以外
の部分での直線カット性に対してずれ量１／２）で開封
できることが判明した。Example 1 As shown in FIG. 1, a polyethylene terephthalate film (thickness: 12 μm)
m) to form a dry laminating adhesive (for example, a urethane-based two-component curable adhesive) on its surface by applying and drying such that the solid content is 4.0 g / m 2 or more. Aluminum foil was laminated as a film layer 3 (thickness: 7 μm) via an adhesive layer 4 for dry lamination, followed by dry lamination to form a base film layer 1. Next, the film layer 3 of this aluminum foil
An adhesive for dry lamination (for example, a urethane-based two-component curable adhesive) having a solid content of 2.0 g / m 2 on the surface of
A non-stretched polypropylene film (thickness: 70 μm) was overlaid as a sealant layer 10 via a dry laminating adhesive layer 5 formed by applying and drying so as to obtain a laminate film packaging material. Subsequently, the laminated film packaging material is cut at the surface of the sealant layer 10 while moving at a speed of 100 cm / min, and linearly cut with a YAG laser (wavelength: 800 nm, irradiation spot diameter: 4 mm, output: 50 MW / cm 2 , pulse) Width; 70
ns, manufacturer: squirt continuum, model name: custom) to irradiate the sealant layer 10 by heating and softening to make it thinner in a continuous line shape, thinning depth 30 μm, width 0.2 mm
Was obtained. The surface on the side of the base film layer 1 opposite to the thin film layer B has a height of 15 to 15 along the thin film layer B.
A continuous linear swelling line of 20 μm was obtained. As a result, an easy-cut laminated film packaging material A of the present invention in which the separation line 20 formed by the thin film layer B was formed on the laminated film packaging material was obtained. (See FIG. 2) After the thus-obtained easy-cut laminated film packaging material A of the present invention is aligned with the sealant layer 10 on the inner surface so that the separation lines 20 are aligned on the front and back, and then two sheets are laminated. Heat sealing around the three sides to make a pouch for retort food packaging, and cutting the pouch along the cutting line 20, as a result, a good straight-line cut property with a tear resistance of 200 gf or lower and a low resistance value (separation line) It has been found that the seal can be opened with a deviation amount of 1/2) with respect to the straight-line cutability in a portion other than 20.
【００３３】＜実施例２＞図１に示すようにフィルム層
２にポリエチレンテレフタレートフィルム（厚さ１２μ
ｍ）を用いて、その表面にドライラミネート用接着剤
（例えばウレタン系二液硬化型接着剤）を固形分含有率
が４．０ｇ／ｍ2 若しくはそれ以上となるように塗布乾
燥させて形成したドライラミネート用接着剤層４を介し
てアルミニウム箔をフィルム層３（厚さ７μｍ）として
重ね合わせドライラミネートして基材フィルム層１を形
成した。次に、このアルミニウム箔によるフィルム層３
の表面に、ドライラミネート用接着剤（例えばウレタン
系二液硬化型接着剤）を固形分含有率が２．０ｇ／ｍ2
となるように塗布乾燥させて形成したドライラミネート
用接着剤層５を介して無延伸ポリプロピレンフィルム
（厚さ７０μｍ）をシーラント層１０として重ね合わせ
ドライラミネートして積層フィルム包材を作製した。続
いて、この積層フィルム包材を１００ｃｍ／分の速度に
て移動させながらシーラント層１０の表面に切り離し線
状にＹＡＧレーザー（波長；８００ｎｍ、照射スポット
径；４ｍｍ、出力；５０ＭＷ／ｃｍ2 、パルス幅；７０
ｎｓ、製造メーカー；ホヤコンテニュアム、機種名；カ
スタム）を照射して加熱軟化させた後に、直ちにそのシ
ーラント層１０の切り離し線状に軟化している部分に、
ローラー状の罫押し先端面が同一高さの押し罫型を押圧
回転させながら押し罫加工することにより、薄化深さ３
０μｍ、幅０．２ｍｍの薄膜層が得られた。なお、薄膜
層Ｂと相対する基材フィルム層１側の表面には薄膜層Ｂ
に沿って高さ２０〜２５μｍの連続線状の盛り上がり線
が得られた。これによって、積層フィルム包材に薄膜層
Ｂによる切り離し線２０の形成された本発明の易カット
性積層フィルム包材Ａを得た。（図２参照） このようにして得られた本発明の易カット性積層フィル
ム包材Ａをシーラント層１０を内面にしてその切り離し
線２０が表裏で一致するように整合して二枚重ねにした
後、三方周囲を加熱シールしてレトルト食品包装用パウ
チを製袋し、このパウチを切り離し線２０に沿って切り
裂いた結果、引裂抵抗２００ｇｆ若しくはそれ以下の低
い抵抗値にて良好な直線カット性（切り離し線２０以外
の部分での直線カット性に対してずれ量１／２）で開封
できることが判明した。Example 2 As shown in FIG. 1, a polyethylene terephthalate film (thickness: 12 μm) was formed on the film layer 2.
m) to form a dry laminating adhesive (for example, a urethane-based two-component curable adhesive) on its surface by applying and drying such that the solid content is 4.0 g / m 2 or more. Aluminum foil was laminated as a film layer 3 (thickness: 7 μm) via an adhesive layer 4 for dry lamination, followed by dry lamination to form a base film layer 1. Next, the film layer 3 of this aluminum foil
An adhesive for dry lamination (for example, a urethane-based two-component curable adhesive) having a solid content of 2.0 g / m 2 on the surface of
A non-stretched polypropylene film (thickness: 70 μm) was overlaid as a sealant layer 10 via a dry laminating adhesive layer 5 formed by applying and drying so as to obtain a laminate film packaging material. Subsequently, the laminated film packaging material is cut at the surface of the sealant layer 10 while moving at a speed of 100 cm / min, and linearly cut with a YAG laser (wavelength: 800 nm, irradiation spot diameter: 4 mm, output: 50 MW / cm 2 , pulse) Width; 70
ns, manufacturer: squirt continuum, model name: custom), and after irradiating the material with heat, the portion of the sealant layer 10 that has been softened in a cut-off line immediately,
The pressing depth of the roller-shaped ruled pressing surface is the same as that of the pressing ruled while pressing and rotating, so that the thinning depth is 3
A thin film layer having a thickness of 0 μm and a width of 0.2 mm was obtained. The thin film layer B is provided on the surface on the side of the base film layer 1 opposite to the thin film layer B.
, A continuous linear swelling line having a height of 20 to 25 μm was obtained. As a result, an easy-cut laminated film packaging material A of the present invention in which the separation line 20 formed by the thin film layer B was formed on the laminated film packaging material was obtained. (See FIG. 2) After the easily cut laminate film packaging material A of the present invention thus obtained is aligned with the sealant layer 10 on the inner surface so that the separation line 20 is aligned on the front and back, and then two sheets are stacked. Heat sealing around the three sides to make a pouch for retort food packaging, and the pouch was cut along the cutting line 20. As a result, a good straight-line cut property with a tear resistance of 200 gf or lower and a low resistance value (cutting line) It has been found that the seal can be opened with a shift amount of）) with respect to the straight-line cutability at a portion other than 20.
【００３４】＜実施例３＞上記実施例１、実施例２にお
けるフィルム層３に延伸ナイロンフィルム（厚さ１５μ
ｍ）を用いた以外は、実施例１、実施例２と同様にし
て、積層フィルム包材に薄膜層Ｂによる切り離し線２０
の形成された本発明の易カット性積層フィルム包材Ａを
得た。このようにして得られた本発明の易カット性積層
フィルム包材Ａをシーラント層１０を内面にしてその切
り離し線２０が表裏で一致するように整合して二枚重ね
にした後、三方周囲を加熱シールしてレトルト食品包装
用パウチを製袋し、このパウチを切り離し線２０に沿っ
て切り裂いた結果、引裂抵抗２００ｇｆ若しくはそれ以
下の低い抵抗値にて良好な直線カット性（切り離し線２
０以外の部分での直線カット性に対してずれ量１／２）
で開封できることが判明した。<Embodiment 3> A stretched nylon film (15 μm thick) was used as the film layer 3 in the above-mentioned Embodiments 1 and 2.
m), except that the cut line 20 formed by the thin film layer B was applied to the laminated film packaging material in the same manner as in Example 1 and Example 2.
Was obtained, and the easily cuttable laminated film packaging material A of the present invention was formed. The thus-obtained easy-cut laminated film packaging material A of the present invention is aligned with the sealant layer 10 as the inner surface so that the separation lines 20 thereof are aligned on the front and back, and two sheets are stacked. As a result, a pouch for retort food packaging is formed, and the pouch is cut along the cutting line 20. As a result, a good straight-line cut property (cutting line 2) is obtained with a tear resistance of 200 gf or a low resistance value of 200 gf or less.
(The amount of deviation is 1/2 with respect to the straight-line cutability at a part other than 0)
It was found that it could be opened with.
【００３５】＜実施例４＞上記実施例２、実施例３にお
いて使用した罫押し先端面が同一高さの押し罫型に代え
て、その先端面に同一高さ（５〜１０μｍ高さ）の突起
面を断続線状に備えたローラー状押し罫型を用いた以外
は、実施例１又は実施例２と同様にして、積層フィルム
包材に薄膜層Ｂと該薄膜層Ｂ領域内に形成された断続的
薄膜層Ｂ1とによる切り離し線２０の形成された本発明
の易カット性積層フィルム包材Ａを得た。（図３（ｂ）
参照） このようにして得られた本発明の易カット性積層フィル
ム包材Ａをシーラント層１０を内面にしてその切り離し
線２０が表裏で一致するように整合して二枚重ねにした
後、三方周囲を加熱シールしてレトルト食品包装用パウ
チを製袋し、このパウチを切り離し線２０に沿って切り
裂いた結果、最高の引裂抵抗２００ｇｆ若しくはそれ以
下の不連続な引裂抵抗であって、その引裂抵抗の高低差
が５０〜１００ｇｆに低減化され、また良好な直線カッ
ト性（切り離し線２０以外の部分での直線カット性に対
してずれ量１／２）で開封できることが判明した。<Embodiment 4> Instead of the creasing die having the same height as the crimping tip used in the second and third embodiments, the tip having the same height (5 to 10 μm height) is provided on the tip. A thin film layer B and a thin film layer B are formed in a region of the thin film layer B in the same manner as in Example 1 or Example 2, except that a roller-shaped pressing rule having a protruding surface in an intermittent line shape is used. It was to obtain an easy cut laminate film packaging material a of the present invention formed of disconnect line 20 by the intermittent thin layer B 1. (FIG. 3 (b)
(See Reference) The thus-obtained easy-cut laminated film packaging material A of the present invention is aligned with the sealant layer 10 on the inner surface so that the separation lines 20 thereof coincide with each other on the front and back sides to form a two-layer stack. Heat sealing is performed to form a pouch for retort food packaging, and the pouch is cut along the cutting line 20. As a result, the pouch has a maximum tear resistance of 200 gf or less, and a discontinuous tear resistance of less than 200 gf. It was found that the difference was reduced to 50 to 100 gf, and that the package could be opened with good straight-line cutability (a shift amount 量 from the straight-line cutability at a portion other than the separation line 20).
【００３６】[0036]
【発明の効果】本発明の易カット性積層フィルム包材
は、レトルト食品包装用など密封包装用のパウチとして
の良好な密封性を確保できるとともに容易開封性能を備
えたパウチを製袋するための包材として効果的であり、
積層フィルム包材の切り離し線を形成すべき位置に連続
線状の薄膜層による切り離し線を設けたことにより、製
袋されたパウチの良好な密封性を確保しつつ、開封時に
おける引裂抵抗の低減化及び不連続な引裂抵抗における
高低差の低減化のために効果的である。The easily cuttable laminated film packaging material of the present invention can ensure good sealing properties as a pouch for hermetically sealed packaging such as for retort food packaging, and can be used to form a pouch having easy opening performance. Effective as a packaging material,
Reduced tear resistance at the time of opening while ensuring good sealing of bag-made pouches by providing a continuous thin film layer at the position where the separation line of the laminated film packaging material should be formed. This is effective for reducing the difference in elevation in discontinuous and tear resistance.
【図１】本発明の易カット性積層フィルム包材の一例を
示す部分側断面図。FIG. 1 is a partial sectional side view showing an example of an easily cut laminated film packaging material of the present invention.
【図２】本発明の易カット性積層フィルム包材の一例を
示す部分平面図。FIG. 2 is a partial plan view showing an example of an easily cut laminated film packaging material of the present invention.
【図３】（ａ）〜（ｂ）は本発明の易カット性積層フィ
ルム包材の他の例を示す部分平面図。3 (a) and 3 (b) are partial plan views showing another example of the easily cuttable laminated film packaging material of the present invention.
【図４】本発明の易カット性積層フィルム包材を用いて
ヒートシール形成したパウチ容器の斜視図。FIG. 4 is a perspective view of a pouch container formed by heat sealing using the easily cut laminated film packaging material of the present invention.
【図５】従来の易カット性積層フィルム包材の側断面
図。FIG. 5 is a side sectional view of a conventional easy-cut laminated film packaging material.
Ａ…易カット性積層フィルム包材 Ｂ…薄膜層 Ｂ1 …
薄膜層 Ｃ…パウチ容器 １…基材フィルム層 ２…フィルム層 ３…フィルム層
４、５…接着剤層 １０…シーラント層 １４…ヒートシール部 １５…切
欠部 ２０…切り離し線A: Easy-cut laminated film packaging material B: Thin film layer B 1 ...
Thin film layer C: Pouch container 1: Base film layer 2: Film layer 3: Film layer 4, 5, Adhesive layer 10: Sealant layer 14: Heat seal portion 15: Notch portion 20: Separation line
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 ＦＩ Ｂ３２Ｂ 27/16 Ｂ３２Ｂ 27/16 27/28 １０１ 27/28 １０１ 27/32 27/32 Ｃ 27/34 27/34 27/36 27/36 Ｂ６５Ｄ 65/28 Ｂ６５Ｄ 65/28 ──────────────────────────────────────────────────続 き Continued on the front page (51) Int.Cl. 6 Identification code FI B32B 27/16 B32B 27/16 27/28 101 27/28 101 27/32 27/32 C 27/34 27/34 27/36 27/36 B65D 65/28 B65D 65/28
Claims (6)
の厚さを有するシーラント層を備えた積層フィルムの前
記シーラント層側からレーザー光線を照射して加熱する
ことにより前記シーラント層を薄化して得られた連続ハ
ーフカット線形状若しくはミシン目形状など断続ハーフ
カット線形状の薄膜層による切り離し線が設けられてい
ることを特徴とする易カット性積層フィルム包材。1. A laminating film having a sealant layer having a thickness of 1/2 or more of the total thickness on one side of a base film layer is irradiated with a laser beam from the sealant layer side to heat the sealant layer. An easily cuttable laminated film packaging material, characterized in that a cut line formed by a thin film layer having an intermittent half cut line shape such as a continuous half cut line shape or a perforated shape obtained by thinning is provided.
ｎｍの範囲のレーザー光線である請求項１記載の易カッ
ト性積層フィルム包材。2. The method according to claim 1, wherein the laser beam has a wavelength of 800 to 8000.
The easily cuttable laminated film packaging material according to claim 1, which is a laser beam in a range of nm.
線を照射して加熱すると共に押し罫型を用いて押し罫加
工することにより設けられている請求項１又は請求項２
記載の易カット性積層フィルム包材。3. A cut line formed by the thin film layer is provided by irradiating a laser beam and heating the sheet, and performing a pressing process using a pressing rule.
The easily cuttable laminated film packaging material described in the above.
００％に対して１０〜６０％、好ましくは３０〜５０％
である請求項１乃至請求項３記載の易カット性積層フィ
ルム包材。4. The method according to claim 1, wherein the thickness of the thin film layer is 1
10% to 60%, preferably 30% to 50% with respect to 00%
The easily cuttable laminated film packaging material according to claim 1, wherein:
タレートフィルム若しくはポリエチレンテレフタレート
フィルムとアルミニウム箔若しくはポリエチレンテレフ
タレートフィルムと延伸ナイロンフィルム若しくはポリ
エチレンテレフタレートフィルムとアルミニウム箔と延
伸ナイロンフィルムとの複合フィルム層であり、前記シ
ーラント層が無延伸ポリプロピレン、ポリエチレン、エ
チレン−酢酸ビニル共重合体のいずれかである請求項１
乃至請求項４記載の易カット性積層フィルム包材。5. The sealant according to claim 1, wherein the base film layer is a polyethylene terephthalate film, a polyethylene terephthalate film and an aluminum foil, a polyethylene terephthalate film and a stretched nylon film, or a composite film layer of a polyethylene terephthalate film, an aluminum foil and a stretched nylon film. 2. The layer according to claim 1, wherein the layer is any of unstretched polypropylene, polyethylene, and ethylene-vinyl acetate copolymer.
The easily cuttable laminated film packaging material according to claim 4.
レーザー、半導体レーザー又は炭酸ガスレーザーのいず
れかである請求項１乃至請求項５記載の易カット性積層
フィルム包材。6. The laser beam is a YAG laser, Ar
6. The easy-cut laminated film packaging material according to claim 1, which is any one of a laser, a semiconductor laser and a carbon dioxide laser.