JPH1140345A - Organic electroluminescent device - Google Patents
Organic electroluminescent deviceInfo
- Publication number
- JPH1140345A JPH1140345A JP9190830A JP19083097A JPH1140345A JP H1140345 A JPH1140345 A JP H1140345A JP 9190830 A JP9190830 A JP 9190830A JP 19083097 A JP19083097 A JP 19083097A JP H1140345 A JPH1140345 A JP H1140345A
- Authority
- JP
- Japan
- Prior art keywords
- organic electroluminescence
- organic
- sealing resin
- organic electroluminescent
- electroluminescence device
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】この発明は、ホール注入電極
と電子注入電極との間に少なくとも有機材料を用いた発
光層を有する有機エレクトロルミネッセンス素子が基板
上に形成された有機エレクトロルミネッセンス装置に係
り、上記の有機エレクトロルミネッセンス素子が劣化す
るのを抑制するようにした有機エレクトロルミネッセン
ス装置に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an organic electroluminescence device in which an organic electroluminescence element having a light emitting layer using at least an organic material between a hole injection electrode and an electron injection electrode is formed on a substrate. The present invention relates to an organic electroluminescence device that suppresses the deterioration of the organic electroluminescence element.
【０００２】[0002]
【従来の技術】近年、情報機器の多様化等にともなっ
て、従来より一般に使用されているＣＲＴに比べて消費
電力が少なく容積の小さい平面表示素子のニーズが高ま
り、このような平面表示素子の一つとしてエレクトロル
ミネッセンス素子が注目されている。2. Description of the Related Art In recent years, with the diversification of information equipment and the like, the need for a flat display element which consumes less power and has a smaller volume than conventional CRTs has been increased. As one of them, an electroluminescence element has been attracting attention.
【０００３】そして、このようなエレクトロルミネッセ
ンス素子は、使用する材料によって無機エレクトロルミ
ネッセンス素子と有機エレクトロルミネッセンス素子と
に大別される。[0003] Such an electroluminescent element is roughly classified into an inorganic electroluminescent element and an organic electroluminescent element depending on the material used.
【０００４】ここで、無機エレクトロルミネッセンス素
子は、一般に発光部に高電界を作用させ、電子をこの高
電界中で加速して発光中心に衝突させ、これにより発光
中心を励起させて発光させるようになっている。これに
対し、有機エレクトロルミネッセンス素子は、電子注入
電極とホール注入電極とからそれぞれ電子とホールとを
発光部内に注入し、このように注入された電子とホール
とを発光中心で再結合させて、有機分子を励起状態に
し、この有機分子が励起状態から基底状態に戻るときに
蛍光を発光するようになっている。Here, in the inorganic electroluminescence element, a high electric field is generally applied to a light emitting portion, and electrons are accelerated in the high electric field to collide with a light emitting center, thereby exciting the light emitting center to emit light. Has become. In contrast, the organic electroluminescence element injects electrons and holes into the light emitting portion from the electron injection electrode and the hole injection electrode, respectively, and recombines the thus injected electrons and holes at the emission center. The organic molecule is set to an excited state, and emits fluorescence when the organic molecule returns from the excited state to the ground state.
【０００５】そして、無機エレクトロルミネッセンス素
子の場合には、上記のように高電界を作用させるため
に、その駆動電圧として１００〜２００Ｖと高い電圧を
必要とするのに対して、有機エレクトロルミネッセンス
素子の場合には、５〜２０Ｖ程度の低い電圧で駆動でき
るという利点があった。In the case of an inorganic electroluminescent element, a high driving voltage of 100 to 200 V is required to apply a high electric field as described above. In this case, there is an advantage that the device can be driven at a low voltage of about 5 to 20 V.
【０００６】また、上記の有機エレクトロルミネッセン
ス素子の場合には、発光材料である螢光物質を選択する
ことによって適当な色彩に発光する発光素子を得ること
ができ、マルチカラーやフルカラーの表示装置等として
も利用できるという期待があり、さらに低電圧で面発光
できるために、液晶表示素子等のバックライトとして利
用することも考えられた。In the case of the above-mentioned organic electroluminescence element, a light-emitting element which emits light of an appropriate color can be obtained by selecting a fluorescent substance which is a light-emitting material. It is also expected to be able to be used as a backlight, and furthermore, because it is possible to emit surface light at a low voltage, it has been considered to use it as a backlight for a liquid crystal display device or the like.
【０００７】そして、近年においては、このような有機
エレクトロルミネッセンス素子について様々な研究が行
なわれ、ホール注入電極と電子注入電極との間にホール
輸送層と発光層と電子輸送層とを積層させたＤＨ構造と
称される三層構造のものや、ホール注入電極と電子注入
電極との間にホール輸送層と電子輸送性に富む発光層と
が積層されたＳＨ−Ａ構造と称される二層構造のもの
や、ホール注入電極と電子注入電極との間にホール輸送
性に富む発光層と電子輸送層とが積層されたＳＨ−Ｂ構
造と称される二層構造のものが開発されている。In recent years, various studies have been conducted on such an organic electroluminescence device, and a hole transport layer, a light emitting layer and an electron transport layer are laminated between a hole injection electrode and an electron injection electrode. A three-layer structure called a DH structure, or a two-layer structure called an SH-A structure in which a hole transporting layer and a light emitting layer rich in electron transporting property are stacked between a hole injection electrode and an electron injection electrode. A structure having a structure, or a two-layer structure called an SH-B structure in which a light emitting layer having a high hole transporting property and an electron transporting layer are stacked between a hole injecting electrode and an electron injecting electrode has been developed. .
【０００８】また、このような有機エレクトロルミネッ
センス素子においては、一般に上記のホール注入電極に
ＩＴＯ（インジウム−スズ酸化物）等の仕事関数が大き
くて透明な電極材料を用い、このホール注入電極をガラ
ス基板等の透明な基板上に形成する一方、電子注入電極
においては、電子が効率よく注入されるようにするた
め、マグネシウム等の仕事関数が小さい電極材料を用い
るようにしていた。In such an organic electroluminescence device, a transparent electrode material having a large work function such as ITO (indium-tin oxide) is generally used for the hole injection electrode, and the hole injection electrode is made of glass. On the other hand, an electrode material having a small work function such as magnesium is used for an electron injection electrode in order to efficiently inject electrons while being formed on a transparent substrate such as a substrate.
【０００９】ここで、このような有機エレクトロルミネ
ッセンス素子を空気中に放置しておくと、空気中におけ
る水分や酸素により仕事関数の低い金属で構成された電
子注入電極が酸化されたり、発光層等に使用した有機材
料が次第に結晶化してショート等が生じ、安定した発光
が行なえなくなるという問題があった。Here, if such an organic electroluminescence element is left in the air, the electron injection electrode made of a metal having a low work function is oxidized by moisture or oxygen in the air, or a light-emitting layer or the like is formed. However, there is a problem in that the organic material used in the method gradually crystallizes to cause a short circuit or the like, so that stable light emission cannot be performed.
【００１０】このため、従来においては、上記のように
基板上に設けた有機エレクトロルミネッセンス素子を封
止樹脂によって被覆し、またこの封止樹脂上にシールド
ガラス等のシールド材を取り付けて、空気中の水分や酸
素により電子注入電極が酸化されたり、発光層等に使用
した有機材料が結晶化したりするのを抑制するようにし
た有機エレクトロルミネッセンス装置が用いられるよう
になった。For this reason, conventionally, the organic electroluminescence element provided on the substrate as described above is covered with a sealing resin, and a shielding material such as a shield glass is attached on the sealing resin to form the organic electroluminescent element in the air. An organic electroluminescence device that suppresses oxidation of the electron injection electrode due to moisture or oxygen and crystallization of the organic material used for the light emitting layer and the like has come to be used.
【００１１】ここで、このように有機エレクトロルミネ
ッセンス素子の周囲を封止樹脂によって被覆するにあた
り、この有機エレクトロルミネッセンス素子の全面を封
止樹脂によって被覆させた場合、この封止樹脂を重合さ
せて硬化させる際に、この封止樹脂の体積が変化し、こ
れにより封止樹脂と有機エレクトロルミネッセンス素子
との接着面に応力が生じて、この有機エレクトロルミネ
ッセンス素子の一部に微少な破壊が発生し、通電時にシ
ョートが生じる等の問題があった。Here, when the periphery of the organic electroluminescent element is covered with the sealing resin, if the entire surface of the organic electroluminescent element is covered with the sealing resin, the sealing resin is polymerized and cured. At the time of this, the volume of this sealing resin changes, thereby causing a stress on the bonding surface between the sealing resin and the organic electroluminescence element, and a minute destruction occurs in a part of the organic electroluminescence element, There is a problem that a short circuit occurs when power is supplied.
【００１２】そこで、近年においては、封止樹脂の硬化
によって有機エレクトロルミネッセンス素子との接着面
に応力が生じるのを少なくするため、上記の封止樹脂に
よって有機エレクトロルミネッセンス素子の全面を被覆
させるのではなく、有機エレクトロルミネッセンス素子
の一部を被覆させずに、この有機エレクトロルミネッセ
ンス素子の周辺部だけを封止樹脂によって被覆し、この
封止樹脂上にシールドガラス等のシールド材を取り付け
ると共に、このシールド材と上記の有機エレクトロルミ
ネッセンス素子の露出部分との間の空間部に水分や酸素
が入るのを抑制するように、この空間部に窒素ガス等の
不活性ガスを充填させるようにしたものが考えられた。Therefore, in recent years, in order to reduce the occurrence of stress on the bonding surface with the organic electroluminescence element due to curing of the sealing resin, it is necessary to cover the entire surface of the organic electroluminescence element with the above sealing resin. Without covering a part of the organic electroluminescence element, only the periphery of the organic electroluminescence element is covered with a sealing resin, and a shielding material such as a shield glass is attached on the sealing resin, In order to suppress the entry of moisture and oxygen into the space between the material and the exposed portion of the organic electroluminescence element, it is considered that the space is filled with an inert gas such as nitrogen gas. Was done.
【００１３】しかし、このように有機エレクトロルミネ
ッセンス素子の周辺部だけを封止樹脂によって被覆し、
この封止樹脂上にシールド材を取り付けて、このシール
ド材と有機エレクトロルミネッセンス素子の露出部分と
の間の空間部に不活性ガスを充填させた場合において
も、この不活性ガスが有機エレクトロルミネッセンス素
子と接触することになり、長時間室温で放置したり、６
０℃以上の高温で放置すると、次第に有機エレクトロル
ミネッセンス素子における有機材料に結晶が析出して、
有機エレクトロルミネッセンス素子が破壊され、通電時
にショートが発生する等の問題が依然として存在した。However, only the peripheral portion of the organic electroluminescence element is covered with the sealing resin as described above,
Even when a shield material is mounted on the sealing resin and a space between the shield material and the exposed portion of the organic electroluminescence element is filled with an inert gas, the inert gas is And leave it at room temperature for a long time,
When left at a high temperature of 0 ° C. or higher, crystals are gradually deposited on the organic material in the organic electroluminescence device,
There still existed a problem that the organic electroluminescence element was destroyed, and a short circuit occurred during energization.
【００１４】[0014]
【発明が解決しようとする課題】この発明は、ホール注
入電極と電子注入電極との間に少なくとも有機材料を用
いた発光層が設けられた有機エレクトロルミネッセンス
素子を基板上に形成し、この有機エレクトロルミネッセ
ンス素子を封止樹脂によって被覆するようにした有機エ
レクトロルミネッセンス装置における上記のような問題
を解決することを課題とするものである。SUMMARY OF THE INVENTION According to the present invention, an organic electroluminescent element having at least a light emitting layer using an organic material provided between a hole injection electrode and an electron injection electrode is formed on a substrate. It is an object of the present invention to solve the above-described problem in an organic electroluminescence device in which a luminescence element is covered with a sealing resin.
【００１５】すなわち、この発明においては、有機エレ
クトロルミネッセンス素子を封止樹脂によって被覆する
にあたり、この封止樹脂を硬化させた場合に、この封止
樹脂と有機エレクトロルミネッセンス素子との接触面に
応力が作用して有機エレクトロルミネッセンス素子の一
部が破壊されたり、また有機エレクトロルミネッセンス
素子の周辺部だけを封止樹脂によって被覆し、この封止
樹脂上にシールド材を取り付けて、このシールド材と有
機エレクトロルミネッセンス素子の露出部分との間の空
間部に不活性ガスを充填させた場合においても、この不
活性ガスとの接触によって有機エレクトロルミネッセン
ス素子における有機材料に結晶が生じたりするというこ
ともなく、長期にわたって安定した発光が行なえる有機
エレクトロルミネッセンス装置を提供することを課題と
するものである。That is, in the present invention, when the organic electroluminescent element is covered with the sealing resin, when the sealing resin is cured, stress is applied to the contact surface between the sealing resin and the organic electroluminescent element. The organic electroluminescent element is partially destroyed due to the action, or only the periphery of the organic electroluminescent element is covered with a sealing resin, and a shielding material is attached on the sealing resin. Even when the space between the exposed part of the luminescence element and the inert gas is filled, the organic material in the organic electroluminescence element does not produce crystals due to contact with the inert gas, and the Organic electroluminescence that can emit light stably over a wide area It is an object to provide a sensing device.
【００１６】[0016]
【課題を解決するための手段】この発明の請求項１にお
ける有機エレクトロルミネッセンス素子においては、上
記のような課題を解決するため、ホール注入電極と電子
注入電極との間に少なくとも有機材料を用いた発光層を
有する有機エレクトロルミネッセンス素子が基板上に形
成されると共に、この有機エレクトロルミネッセンス素
子が封止樹脂によって被覆されてなる有機エレクトロル
ミネッセンス装置において、上記の有機エレクトロルミ
ネッセンス素子と封止樹脂との間に有機エレクトロルミ
ネッセンス素子を被覆するように無機保護膜を設けたの
である。In order to solve the above-mentioned problems, at least an organic material is used between the hole injection electrode and the electron injection electrode in the organic electroluminescence device according to the first aspect of the present invention. An organic electroluminescence device having a light emitting layer is formed on a substrate, and the organic electroluminescence device is covered with a sealing resin. Is provided with an inorganic protective film so as to cover the organic electroluminescent element.
【００１７】そして、この請求項１における有機エレク
トロルミネッセンス装置のように、有機エレクトロルミ
ネッセンス素子とこれを被覆する封止樹脂との間に無機
保護膜を設けると、この無機保護膜が緩衝材となり、封
止樹脂が硬化して体積変化した場合であっても、この体
積変化による応力が無機保護膜によって緩和されて有機
エレクトロルミネッセンス素子に加わる応力が減少し、
有機エレクトロルミネッセンス素子の一部が破壊される
のが抑制され、長期にわたって安定した発光が行なえる
ようになる。When an inorganic protective film is provided between the organic electroluminescent element and a sealing resin covering the same, as in the organic electroluminescent device according to the first aspect, the inorganic protective film serves as a buffer material, Even when the sealing resin cures and changes its volume, the stress due to this volume change is alleviated by the inorganic protective film and the stress applied to the organic electroluminescent element decreases,
Destruction of a part of the organic electroluminescence element is suppressed, and stable light emission can be performed for a long time.
【００１８】また、この発明の請求項２における有機エ
レクトロルミルッセンス装置においては、上記のような
課題を解決するため、ホール注入電極と電子注入電極と
の間に少なくとも有機材料を用いた発光層を有する有機
エレクトロルミネッセンス素子が基板上に形成されると
共に、この有機エレクトロルミネッセンス素子の一部が
露出するようにして封止樹脂によりこの有機エレクトロ
ルミネッセンス素子が被覆され、上記の露出部分を閉塞
するようにして封止樹脂上にシールド材が取り付けら
れ、このシールド材と露出部分との間に空間部が形成さ
れてなる有機エレクトロルミネッセンス装置において、
上記の有機エレクトロルミネッセンス素子と封止樹脂と
の間及び上記の露出部分における有機エレクトロルミネ
ッセンス素子を被覆するようにして無機保護膜を設け
た。In the organic electroluminescent device according to a second aspect of the present invention, in order to solve the above-mentioned problems, a light emitting layer using at least an organic material between the hole injection electrode and the electron injection electrode. Is formed on a substrate, and the organic electroluminescent element is covered with a sealing resin so that a part of the organic electroluminescent element is exposed, and the above-mentioned exposed portion is closed. In the organic electroluminescent device in which a shielding material is attached on the sealing resin, and a space is formed between the shielding material and the exposed portion,
An inorganic protective film was provided so as to cover the organic electroluminescent element between the organic electroluminescent element and the sealing resin and the exposed portion.
【００１９】そして、この請求項２における有機エレク
トロルミネッセンス装置のように、有機エレクトロルミ
ネッセンス素子の一部が露出するようにして封止樹脂に
より有機エレクトロルミネッセンス素子を被覆し、この
露出部分を閉塞するようにして上記の封止樹脂上にシー
ルド材を設けるにあたり、上記の有機エレクトロルミネ
ッセンス素子と封止樹脂との間及びこの露出部分におい
て、有機エレクトロルミネッセンス素子を無機保護膜で
被覆すると、封止樹脂の硬化によって有機エレクトロル
ミネッセンス素子の一部が破壊されるのがより一層抑制
されると共に、上記の空間部にどのようなガスが充填さ
れていても、このガスが有機エレクトロルミネッセンス
素子に接触して有機エレクトロルミネッセンス素子にお
ける有機材料が結晶化するのが防止され、長期にわたっ
て安定した発光が行なえるようになる。As in the organic electroluminescence device according to the second aspect, the organic electroluminescence device is covered with a sealing resin so that a part of the organic electroluminescence device is exposed, and the exposed portion is closed. In providing a shielding material on the sealing resin, the organic electroluminescence element is covered with an inorganic protective film between the organic electroluminescence element and the sealing resin and at the exposed portion, thereby forming a sealing resin. The hardening further suppresses the destruction of a part of the organic electroluminescent element, and even if any gas is filled in the space, the gas contacts the organic electroluminescent element and the organic electroluminescent element contacts the organic electroluminescent element. Organic materials in electroluminescent devices Is prevented from reduction, stable emission is so performed over a long period.
【００２０】ここで、上記の請求項１，２の有機エレク
トロルミネッセンス装置のように、有機エレクトロルミ
ネッセンス素子を無機保護膜で被覆させるようにする
と、この無機保護膜を有機エレクトロルミネッセンス素
子の場合と同様に真空蒸着法で形成することができるよ
うになる。Here, when the organic electroluminescent element is covered with an inorganic protective film as in the organic electroluminescent device according to the first and second aspects, the inorganic protective film is formed in the same manner as in the case of the organic electroluminescent element. Can be formed by a vacuum evaporation method.
【００２１】そして、この無機保護膜としては、上記の
ように封止樹脂が硬化して体積変化する場合に、この体
積変化による応力が緩和させて有機エレクトロルミネッ
センス素子に加わる応力を減少させることができるよう
なものであればよく、好ましくは、有機エレクトロルミ
ネッセンス素子との接着力が弱い一酸化ケイ素で構成さ
れた無機保護膜を設けるようにする。As described above, when the sealing resin cures and changes its volume as described above, the inorganic protective film can reduce the stress applied to the organic electroluminescent element by relaxing the stress due to the change in volume. Any material can be used as long as it can be formed, and preferably, an inorganic protective film made of silicon monoxide having a weak adhesive strength to the organic electroluminescence element is provided.
【００２２】また、この無機保護膜の厚みが薄いと、上
記のように封止樹脂が硬化して体積変化した場合に、こ
の体積変化による応力が有機エレクトロルミネッセンス
素子に加わるのを十分に緩和することがてきなくなるた
め、この無機保護膜の膜厚を５００Å以上、好ましくは
５０００Å以上になるようにする。When the thickness of the inorganic protective film is small, when the sealing resin is hardened and changes in volume as described above, the stress due to the change in volume is sufficiently reduced from being applied to the organic electroluminescence element. Therefore, the thickness of the inorganic protective film is set to 500 ° or more, preferably 5000 ° or more.
【００２３】[0023]
【実施例】以下、この発明の実施例に係る有機エレクト
ロルミネッセンス装置を添付図面に基づいて具体的に説
明すると共に、比較例を挙げ、この発明の実施例におけ
る有機エレクトロルミルッセンス装置においては、長期
にわたって安定した発光が行なえるようになることを明
らかにする。DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, an organic electroluminescence device according to an embodiment of the present invention will be specifically described with reference to the accompanying drawings, and a comparative example will be given. Clarify that stable light emission can be performed for a long time.
【００２４】（実施例１）この実施例１における有機エ
レクトロルミネッセンス装置においては、図１に示すよ
うに、ガラス基板１上にＩＴＯで構成されて膜厚が２０
００Åになった透明なホール注入電極１１を形成し、こ
のホール注入電極１１上に、下記の化１に示すトリフェ
ニルアミン誘導体ＭＴＤＡＴＡで構成されて膜厚が５０
０Åになったホール輸送層１２と、下記の化２に示すα
ＮＰＤからなるホスト材料中に下記の化３に示すルブレ
ンが５重量％ドープされて膜厚が２００Åになった発光
層１３と、下記の化４に示すトリス（８−キノリノー
ル）アルミニウム錯体Ａｌｑ3で構成されて膜厚が５０
０Åになった電子輸送層１４とを順々に積層させると共
に、この電子輸送層１４上の一部にマグネシウム・イン
ジウム合金で構成されて膜厚が２０００Åになった電子
注入電極１５を設け、さらにこの電子注入電極１５の上
にアルミニウム膜で構成されて膜厚が１５０００Åにな
った電極保護膜１６を設けて有機エレクトロルミネッセ
ンス素子１０を形成した。(Embodiment 1) As shown in FIG. 1, an organic electroluminescence device according to Embodiment 1 is made of ITO on a glass substrate 1 and has a thickness of 20 mm.
A transparent hole injection electrode 11 having a thickness of 100 ° is formed.
The hole transport layer 12 that has become 0 ° and α represented by the following chemical formula 2
A light emitting layer 13 having a thickness of 200 ° formed by doping 5% by weight of rubrene shown in the following chemical formula 3 into a host material made of NPD and a tris (8-quinolinol) aluminum complex Alq 3 shown in the following chemical formula 4 It is composed and the film thickness is 50
The electron transport layer 14 having a thickness of 0 ° is sequentially laminated, and an electron injection electrode 15 made of a magnesium-indium alloy and having a thickness of 2000 ° is provided on a part of the electron transport layer 14. An organic electroluminescent element 10 was formed by providing an electrode protection film 16 made of an aluminum film and having a thickness of 15000 ° on the electron injection electrode 15.
【００２５】[0025]
【化１】 Embedded image
【００２６】[0026]
【化２】 Embedded image
【００２７】[0027]
【化３】 Embedded image
【００２８】[0028]
【化４】 Embedded image
【００２９】そして、このようにガラス基板１上に形成
された有機エレクトロルミネッセンス素子１０の全面を
覆うようにして膜厚が５０００Åになった一酸化ケイ素
ＳｉＯからなる無機保護膜２０を設けた。なお、上記の
有機エレクトロルミネッセンス素子１０の作製及び無機
保護膜２０の形成は、全て抵抗加熱式真空蒸着法により
行ない、いずれも真空度５×１０-6Ｔｏｒｒで、基板温
度の制御なしの条件で行なった。Then, an inorganic protective film 20 made of silicon monoxide SiO having a film thickness of 5000 ° was provided so as to cover the entire surface of the organic electroluminescence element 10 formed on the glass substrate 1 as described above. The production of the organic electroluminescence element 10 and the formation of the inorganic protective film 20 were all performed by a resistance heating vacuum evaporation method, and all were performed at a degree of vacuum of 5 × 10 −6 Torr and without control of the substrate temperature. Done.
【００３０】また、このように有機エレクトロルミネッ
センス素子１０を無機保護膜２０で被覆した後、この無
機保護膜２０全体を覆うようにして、さらにエポキシ系
の紫外線硬化型の封止樹脂３０を膜厚が１０〜２０μｍ
になるようにベタ付けし、その上にシールドガラスから
なるシールド材３１を載置させ、その後、上記の封止樹
脂３０に紫外線を照射させて、この封止樹脂３０を硬化
させた。なお、上記のような操作は、湿度０．５％以下
で窒素ガスを充填させたドライボックス中において室温
で行なった。After the organic electroluminescent element 10 is covered with the inorganic protective film 20 as described above, the entire surface of the inorganic protective film 20 is covered with an epoxy-based UV-curable sealing resin 30. Is 10 to 20 μm
Then, a shield material 31 made of shield glass was placed thereon, and then the sealing resin 30 was irradiated with ultraviolet light to cure the sealing resin 30. The above operation was performed at room temperature in a dry box filled with nitrogen gas at a humidity of 0.5% or less.
【００３１】（比較例１）この比較例１における有機エ
レクトロルミネッセンス装置においては、上記の実施例
１における有機エレクトロルミネッセンス装置におい
て、上記のＳｉＯからなる無機保護膜２０を設けないよ
うにし、それ以外については、上記の実施例１の場合と
同様にして有機エレクトロルミネッセンス装置を作製し
た。Comparative Example 1 In the organic electroluminescent device of Comparative Example 1, the inorganic protective film 20 made of SiO was not provided in the organic electroluminescent device of Example 1 described above. In the same manner as in Example 1 above, an organic electroluminescence device was manufactured.
【００３２】そして、上記の実施例１及び比較例１の各
有機エレクトロルミネッセンス装置を、温度６０℃、湿
度９０％の恒温恒湿器中に放置させ、その後、上記のホ
ール注入電極１１をプラス、電子注入電極１５をマイナ
スにして電圧を印加させ、各有機エレクトロルミネッセ
ンス装置における発光状態を調べた。Then, the organic electroluminescent devices of Example 1 and Comparative Example 1 were allowed to stand in a thermo-hygrostat at a temperature of 60 ° C. and a humidity of 90%. The voltage was applied with the electron injection electrode 15 being negative, and the light emission state in each organic electroluminescence device was examined.
【００３３】この結果、上記の比較例１の有機エレクト
ロルミネッセンス装置においては、上記の恒温恒湿器中
に２４時間放置した場合に、有機エレクトロルミネッセ
ンス素子１０にショートが生じて発光が得られなかっ
た。As a result, in the organic electroluminescence device of Comparative Example 1 described above, when the organic electroluminescence device 10 was left in the constant temperature and humidity chamber for 24 hours, short-circuit occurred in the organic electroluminescence device 10 and no light emission was obtained. .
【００３４】これに対して、上記の実施例１の有機エレ
クトロルミネッセンス装置においては、上記の恒温恒湿
器中に２４時間放置した後であっても、十分な発光が得
られた。On the other hand, in the organic electroluminescence device of Example 1 described above, sufficient light emission was obtained even after being left in the constant temperature and humidity chamber for 24 hours.
【００３５】次に、この実施例１の有機エレクトロルミ
ネッセンス装置を上記の恒温恒湿器中に所定時間放置さ
せて、この有機エレクトロルミネッセンス装置における
ダークスポットの成長を調べるようにした。ここで、ダ
ークスポットの成長を調べるにあたっては、その有機エ
レクトロルミネッセンス素子１０の発光面を倍率５０倍
の光学顕微鏡を用いて写真撮影を行ない、各放置時間に
おけるダークスポットの面積を求めて、ダークスポット
の面積率を算出し、その結果を下記の表１に示した。Next, the organic electroluminescent device of Example 1 was allowed to stand in the above-mentioned thermo-hygrostat for a predetermined time to examine the growth of dark spots in the organic electroluminescent device. Here, when examining the growth of the dark spot, a photograph was taken of the light emitting surface of the organic electroluminescence element 10 using an optical microscope with a magnification of 50 times, and the area of the dark spot at each leaving time was determined. Was calculated, and the results are shown in Table 1 below.
【００３６】[0036]
【表１】 [Table 1]
【００３７】この結果から明らかなように、有機エレク
トロルミネッセンス素子１０と封止樹脂３０との間にＳ
ｉＯからなる無機保護膜２０を設けた実施例１の有機エ
レクトロルミネッセンス装置においては、高温高湿度下
で放置させた場合においても、ダークスポットの成長が
非常に少なく、安定した発光が行なえるようになってい
た。As is apparent from the result, the distance between the organic electroluminescence element 10 and the sealing resin 30
In the organic electroluminescence device of Example 1 provided with the inorganic protective film 20 made of iO, even when the device is left under high temperature and high humidity, the growth of dark spots is very small and stable light emission can be performed. Had become.
【００３８】（実施例２）この実施例２における有機エ
レクトロルミネッセンス装置においては、上記の実施例
１における有機エレクトロルミネッセンス装置と同様に
して有機エレクトロルミネッセンス素子１０を作製する
と共に、この有機エレクトロルミネッセンス素子１０の
全面を覆うようにしてＳｉＯからなる無機保護膜２０を
設けた。(Embodiment 2) In the organic electroluminescence device according to the second embodiment, an organic electroluminescence device 10 is manufactured in the same manner as the organic electroluminescence device according to the first embodiment, and the organic electroluminescence device 10 is manufactured. An inorganic protective film 20 made of SiO was provided so as to cover the entire surface of the substrate.
【００３９】そして、この実施例２の有機エレクトロル
ミネッセンス装置においては、上記のように有機エレク
トロルミネッセンス素子１０を被覆した無機保護膜２０
を上記の封止樹脂３０で被覆させるにあたり、この無機
保護膜２０の周辺部分に上記の封止樹脂３０を設け、そ
の中央部においては封止樹脂３０を設けずに、無機保護
膜２０が露出するようにし、この状態で、この封止樹脂
３０上にシールドガラスからなるシールド材３１を載置
させ、その後、上記の封止樹脂３０に紫外線を照射して
硬化させた。なお、このようにして実施例２の有機エレ
クトロルミネッセンス装置を作製すると、上記の無機保
護膜２０とシールド材３１との間の空間部３２にドライ
ボックス中における窒素ガスが充填された状態になっ
た。In the organic electroluminescence device according to the second embodiment, the inorganic protective film 20 covering the organic electroluminescence element 10 as described above is used.
Is covered with the sealing resin 30, the sealing resin 30 is provided around the inorganic protective film 20, and the inorganic protective film 20 is exposed without providing the sealing resin 30 at the center. In this state, a shield material 31 made of shield glass was placed on the sealing resin 30, and then the sealing resin 30 was cured by irradiating it with ultraviolet rays. When the organic electroluminescence device of Example 2 was manufactured in this manner, the space 32 between the inorganic protective film 20 and the shield material 31 was filled with nitrogen gas in the dry box. .
【００４０】（比較例２）この比較例２における有機エ
レクトロルミネッセンス装置においては、上記の実施例
２における有機エレクトロルミネッセンス装置におい
て、上記のＳｉＯからなる無機保護膜２０を設けないよ
うにし、それ以外については、上記の実施例２の場合と
同様にして有機エレクトロルミネッセンス装置を作製し
た。Comparative Example 2 In the organic electroluminescent device of Comparative Example 2, the inorganic protective film 20 made of SiO was not provided in the organic electroluminescent device of Example 2 described above. Produced an organic electroluminescence device in the same manner as in Example 2 described above.
【００４１】そして、上記の実施例２及び比較例２の各
有機エレクトロルミネッセンス装置についても、上記の
実施例１及び比較例１の場合と同様に、温度６０℃、湿
度９０％の恒温恒湿器中に放置させ、その後、上記のホ
ール注入電極１１をプラス、電子注入電極１５をマイナ
スにして電圧を印加させ、各有機エレクトロルミネッセ
ンス装置における発光状態を調べた。As for the organic electroluminescent devices of Example 2 and Comparative Example 2, as in the case of Example 1 and Comparative Example 1, a thermo-hygrostat at a temperature of 60 ° C. and a humidity of 90% was used. After that, the above-mentioned hole injection electrode 11 was made positive and the electron injection electrode 15 was made negative to apply a voltage, and the light emission state in each organic electroluminescence device was examined.
【００４２】この結果、上記の比較例２の有機エレクト
ロルミネッセンス装置においては、上記の恒温恒湿器中
に３０時間放置した場合に、有機エレクトロルミネッセ
ンス素子１０にショートが生じて発光が得られなかっ
た。As a result, in the organic electroluminescence device of Comparative Example 2 described above, when the organic electroluminescence device 10 was left in the constant temperature and humidity chamber for 30 hours, short-circuit occurred in the organic electroluminescence device 10 and no light emission was obtained. .
【００４３】ここで、この比較例２における有機エレク
トロルミネッセンス装置の状態を調べると、窒素ガスが
充填された空間部３２と接触している部分において、上
記の有機エレクトロルミネッセンス素子１０に結晶が生
じ、これがショートの原因になっていることが分かっ
た。Here, when the state of the organic electroluminescent device in Comparative Example 2 was examined, crystals were formed in the organic electroluminescent element 10 at a portion in contact with the space 32 filled with nitrogen gas. This turned out to be the cause of the short.
【００４４】これに対して、上記の実施例２の有機エレ
クトロルミネッセンス装置においては、上記の恒温恒湿
器中に３０時間放置した後であっても、十分な発光が得
られた。On the other hand, in the organic electroluminescence device of Example 2 described above, sufficient light emission was obtained even after being left in the constant temperature and humidity chamber for 30 hours.
【００４５】また、この実施例２の有機エレクトロルミ
ネッセンス装置についても、上記の実施例１の場合と同
様に、恒温恒湿器中に所定時間放置させて、この有機エ
レクトロルミネッセンス装置におけるダークスポットの
成長を調べ、各放置時間におけるダークスポットの面積
率を算出し、その結果を下記の表２に示した。Further, the organic electroluminescent device of the second embodiment is also left in a thermo-hygrostat for a predetermined period of time to grow dark spots in the organic electroluminescent device, as in the case of the first embodiment. And the area ratio of dark spots at each standing time was calculated. The results are shown in Table 2 below.
【００４６】[0046]
【表２】 [Table 2]
【００４７】この結果、この実施例２における有機エレ
クトロルミネッセンス装置においても、長期にわたって
安定した発光が行なえるようになっていた。As a result, also in the organic electroluminescence device of Example 2, stable light emission can be performed for a long period of time.
【００４８】次に、上記の実施例１における有機エレク
トロルミネッセンス装置において、上記のＳｉＯからな
る無機保護膜２０の膜厚だけを下記の表３に示すように
変更させた各有機エレクトロルミネッセンス装置をそれ
ぞれ１００個作製し、各有機エレクトロルミネッセンス
装置を、それぞれ温度６０℃、湿度９０％の恒温恒湿器
中で１日放置させた後、各有機エレクトロルミネッセン
ス装置におけるショート発生率を調べ、その結果を表３
に合わせて示した。Next, in the organic electroluminescence device in the first embodiment, each of the organic electroluminescence devices in which only the thickness of the inorganic protective film 20 made of SiO was changed as shown in Table 3 below was used. After 100 organic electroluminescent devices were manufactured, each organic electroluminescent device was allowed to stand for 1 day in a thermo-hygrostat at a temperature of 60 ° C. and a humidity of 90%, and the short-circuit occurrence rate in each organic electroluminescent device was examined. 3
Indicated according to
【００４９】[0049]
【表３】 [Table 3]
【００５０】この結果、ＳｉＯからなる無機保護膜２０
を設けた各有機エレクトロルミネッセンス装置は、この
ような無機保護膜２０を設けなかった有機エレクトロル
ミネッセンス装置に比べてショート発生率が著しく低下
しており、特に、このＳｉＯからなる無機保護膜２０の
膜厚を５０００Å以上にした場合には、有機エレクトロ
ルミネッセンス装置におけるショート発生率が非常に少
なくなっていた。As a result, the inorganic protective film 20 made of SiO
The organic electroluminescent device provided with the organic EL device has a significantly reduced short-circuit occurrence rate as compared with the organic electroluminescent device not provided with such an inorganic protective film 20. In particular, the film thickness of the inorganic protective film 20 made of SiO When the thickness was set to 5000 ° or more, the occurrence rate of short circuit in the organic electroluminescence device was extremely low.
【００５１】[0051]
【発明の効果】以上詳述したように、この発明の請求項
１における有機エレクトロルミネッセンス装置において
は、有機エレクトロルミネッセンス素子とこれを被覆す
る封止樹脂との間に無機保護膜を設けるようにしたた
め、この無機保護膜が緩衝材となり、封止樹脂が硬化し
て体積変化した場合であっても、この体積変化による応
力がこの無機保護膜によって緩和されて、有機エレクト
ロルミネッセンス素子に加わる応力が減少し、有機エレ
クトロルミネッセンス素子の一部が破壊するのが防止さ
れて、長期にわたって安定した発光が行なえるようにな
った。As described above in detail, in the organic electroluminescence device according to the first aspect of the present invention, the inorganic protective film is provided between the organic electroluminescence element and the sealing resin covering the same. However, even when the inorganic protective film becomes a buffer material and the sealing resin cures and the volume changes, the stress due to the volume change is relieved by the inorganic protective film, and the stress applied to the organic electroluminescent element decreases. However, it was possible to prevent a part of the organic electroluminescence element from being destroyed, and to stably emit light over a long period of time.
【００５２】また、この発明の請求項２における有機エ
レクトロルミルッセンス装置においては、有機エレクト
ロルミネッセンス素子の一部が露出するようにして封止
樹脂により有機エレクトロルミネッセンス素子を被覆
し、この露出部分を閉塞するようにして封止樹脂上にシ
ールド材を設けるにあたり、上記の有機エレクトロルミ
ネッセンス素子と封止樹脂との間及びこの露出部分にお
いて、有機エレクトロルミネッセンス素子を無機保護膜
で被覆するようにしたため、封止樹脂の硬化によって有
機エレクトロルミネッセンス素子の一部が破壊されるの
がより一層抑制されると共に、シールド材と無機保護膜
との間の空間部にどのようなガスが充填されていても、
この無機保護膜によってガスが有機エレクトロルミネッ
センス素子に接触するのが抑制され、この有機エレクト
ロルミネッセンス素子における有機材料がガスと接触し
て結晶化するのが防止され、長期にわたって安定した発
光が行なえるようになった。Further, in the organic electroluminescent device according to claim 2 of the present invention, the organic electroluminescent element is covered with a sealing resin so that a part of the organic electroluminescent element is exposed, and the exposed portion is covered with the sealing resin. In providing the shielding material on the sealing resin so as to close, between the organic electroluminescence element and the sealing resin and in the exposed portion, so as to cover the organic electroluminescence element with an inorganic protective film, Even if the part of the organic electroluminescence element is further suppressed from being destroyed by the curing of the sealing resin, even if any space is filled with a gas between the shielding material and the inorganic protective film,
This inorganic protective film suppresses the gas from coming into contact with the organic electroluminescence element, prevents the organic material in the organic electroluminescence element from being brought into contact with the gas and crystallizing, and enables stable light emission for a long period of time. Became.
【図１】この発明の実施例１に係る有機エレクトロルミ
ネッセンス装置の概略説明図である。FIG. 1 is a schematic explanatory view of an organic electroluminescence device according to a first embodiment of the present invention.
【図２】比較例１における有機エレクトロルミネッセン
ス装置の概略説明図である。FIG. 2 is a schematic explanatory view of an organic electroluminescence device in Comparative Example 1.
【図３】この発明の実施例２に係る有機エレクトロルミ
ネッセンス素子の概略説明図である。FIG. 3 is a schematic explanatory view of an organic electroluminescence device according to a second embodiment of the present invention.
【図４】比較例２の有機エレクトロルミネッセンス装置
の概略説明図である。FIG. 4 is a schematic explanatory view of an organic electroluminescence device of Comparative Example 2.
１ 基板（ガラス基板） １０ 有機エレクトロルミネッセンス素子 １１ ホール注入電極 １２ ホール輸送層 １３ 発光層 １４ 電子輸送層 １５ 電子注入電極 ２０ 無機保護膜 ３０ 封止樹脂 ３１ シールド材 ３２ 空間部 Reference Signs List 1 substrate (glass substrate) 10 organic electroluminescence element 11 hole injection electrode 12 hole transport layer 13 light emitting layer 14 electron transport layer 15 electron injection electrode 20 inorganic protective film 30 sealing resin 31 shielding material 32 space
Claims (4)
少なくとも有機材料を用いた発光層を有する有機エレク
トロルミネッセンス素子が基板上に形成されると共に、
この有機エレクトロルミネッセンス素子が封止樹脂によ
って被覆されてなる有機エレクトロルミネッセンス装置
において、上記の有機エレクトロルミネッセンス素子と
封止樹脂との間に有機エレクトロルミネッセンス素子を
被覆するように無機保護膜が設けられてなることを特徴
とする有機エレクトロルミネッセンス装置。An organic electroluminescent element having a light emitting layer using at least an organic material between a hole injection electrode and an electron injection electrode is formed on a substrate,
In an organic electroluminescence device in which the organic electroluminescence element is covered with a sealing resin, an inorganic protective film is provided between the organic electroluminescence element and the sealing resin so as to cover the organic electroluminescence element. An organic electroluminescent device, comprising:
少なくとも有機材料を用いた発光層を有する有機エレク
トロルミネッセンス素子が基板上に形成されると共に、
この有機エレクトロルミネッセンス素子の一部が露出す
るようにして封止樹脂によりこの有機エレクトロルミネ
ッセンス素子が被覆され、上記の露出部分を閉塞するよ
うにして封止樹脂上にシールド材が取り付けられ、この
シールド材と露出部分との間に空間部が形成されてなる
有機エレクトロルミネッセンス装置において、上記の有
機エレクトロルミネッセンス素子と封止樹脂との間及び
上記の露出部分における有機エレクトロルミネッセンス
素子を被覆するようにして無機保護膜が設けられてなる
ことを特徴とする有機エレクトロルミネッセンス装置。2. An organic electroluminescence device having a light emitting layer using at least an organic material between a hole injection electrode and an electron injection electrode is formed on a substrate,
The organic electroluminescent element is covered with a sealing resin so that a part of the organic electroluminescent element is exposed, and a shield material is attached on the sealing resin so as to close the above-mentioned exposed part. In an organic electroluminescence device in which a space is formed between the material and the exposed portion, the organic electroluminescence device is coated between the organic electroluminescence device and the sealing resin and the organic electroluminescence device in the exposed portion. An organic electroluminescence device comprising an inorganic protective film.
ロルミネッセンス装置において、上記の無機保護膜が一
酸化ケイ素で構成されていることを特徴とする有機エレ
クトロルミネッセンス装置。3. The organic electroluminescence device according to claim 1, wherein the inorganic protective film is made of silicon monoxide.
ネッセンス装置において、上記の一酸化ケイ素で形成さ
れた無機保護膜の膜厚が５０００Å以上であることを特
徴とする有機エレクトロルミネッセンス装置。4. The organic electroluminescence device according to claim 3, wherein the inorganic protective film formed of silicon monoxide has a thickness of 5000 ° or more.