JPH11334292A - Lapping transfer method - Google Patents

Abstract

PROBLEM TO BE SOLVED: To mold sharp and deep pattern in obtaining decoration material or the like by a lapping transfer method. SOLUTION: The transfer method is to transfer a transfer layer to pillar base material B by the use of a transfer sheet S comprising a support body sheet 1 and a transfer layer 2. In this case, a transfer sheet S with a transfer layer formed of a transfer layer comprising at least a peeling layer is prepared in a support body sheet 1 adhered to the base material sheet in the form irregular pattern 4 where resin is cured through irradiation of ionizing radiation in a state of liquid ionizing radiation curable type resin (uncured composition) filled in the recessed part of a roll-recessed plate and resin held between the base material sheet 3 and the roll-recessed plate by allowing a base material sheet 3 to be in contact with resin. Then, the transfer sheet S is compressed and laminated in turn by a roll to a plural lateral surfaces of the pillar base material, and thereafter the support body is peeled, and subsequently a transfer layer having a peeling layer is transferred to the outermost layer after transfer, thus molding irregular pattern 4A in the transfer layer.

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【０００１】[0001]

【発明の属する技術分野】本発明は、扉、窓枠、敷居等
の建具、壁等の内装材、或いは家具等の建材に使用し、
木目導管溝等の凹凸模様を有する柱状化粧材等の転写製
品を製造するラッピング転写法に関する。TECHNICAL FIELD The present invention is used for doors, window frames, sills and other fittings, walls and other interior materials, or furniture and other building materials.
The present invention relates to a lapping transfer method for manufacturing a transfer product such as a column-shaped decorative material having an uneven pattern such as a wood grain conduit groove.

【０００２】[0002]

【従来の技術】従来、柱状基材を用いた化粧材が、複数
の押圧ローラを用いて各側面に順次段階的にシートを積
層していく所謂ラッピング法による装飾で製造され、各
種用途で使用されている。例えば下記及び等に開示
の如き方法があった。2. Description of the Related Art Conventionally, a decorative material using a columnar base material has been manufactured by a so-called wrapping method in which sheets are sequentially and sequentially laminated on each side surface by using a plurality of pressing rollers, and used in various applications. Have been. For example, there is a method disclosed below and the like.

【０００３】特公昭６１−５８９５号公報等に開示の
如く、基材シートが装飾層等の印刷により装飾処理され
てなる化粧シートを、柱状基材にラミネートする形態で
のラッピング法。 特開平５−３３００１３号公報、特開平７−２５１５
７４号公報等に開示の如く、支持体シートと転写層とか
らなる転写シートを用いて、柱状基材に転写層を転写す
る形態での所謂ラッピング転写法。[0003] As disclosed in JP-B-61-5895, etc., a lapping method in which a decorative sheet obtained by decorating a substrate sheet by printing a decorative layer or the like is laminated on a columnar substrate. JP-A-5-330013, JP-A-7-2515
No. 74, etc., a so-called lapping transfer method in which a transfer layer is transferred to a columnar substrate using a transfer sheet comprising a support sheet and a transfer layer.

【０００４】しかし、上記各号公報に開示される様な方
法では、木目導管溝等の凹凸模様を賦形できない。とこ
ろで、この様な凹凸模様を賦形する方法としては、基材
が板材で賦形面が単一平面の場合では、例えば次の様な
(A) 〜(C) の方法があった。However, the method disclosed in each of the above publications cannot form an uneven pattern such as a wood channel groove. By the way, as a method of shaping such an uneven pattern, when the base material is a plate material and the shaping surface is a single plane, for example, the following method is used.
There were methods (A) to (C).

【０００５】(A) 特公昭５８−１４３１２号公報等で
は、ラミネ−トタイプの化粧シートに予め凹凸模様を賦
形した後、基材に積層する事で、凹凸模様を賦形する。 (B) 特許第２５６４２３１号では、ＭＤＦ（中密度繊維
板）からなる木質基材自体にエンボスで凹凸模様を賦形
後、転写シートから転写層を転写し、転写層表面に基材
の凹凸模様を現出させて、基材の凹凸模様を活かす。 (C) 特開平８−３９９２０号公報では、装飾層を有する
転写シートから転写層を転写後、別の着色用転写シート
を間に介してエンボスローラでエンボス後、着色用転写
シートの支持体シートを剥離して、着色用転写シートに
よる被転写着色層を凹部内部に有する凹凸模様を賦形す
る。(A) In Japanese Patent Publication No. 58-14312, etc., an embossed pattern is formed on a laminate type decorative sheet in advance and then laminated on a substrate to form the embossed pattern. (B) In Japanese Patent No. 2564231, after embossing an embossed pattern on a wood substrate itself made of MDF (medium density fiberboard), the transfer layer is transferred from a transfer sheet, and the uneven pattern of the base material is transferred onto the surface of the transfer layer. And make use of the uneven pattern of the base material. (C) In JP-A-8-39920, after transferring a transfer layer from a transfer sheet having a decorative layer, embossing it with an emboss roller via another coloring transfer sheet, and then supporting the transfer sheet for the coloring transfer sheet Is peeled off to form a concavo-convex pattern having the transferred colored layer formed by the coloring transfer sheet inside the concave portion.

【０００６】[0006]

【発明が解決しようとする課題】しかしながら、上記従
来方法では次の様な問題があった。先ず、及びで開
示するラミネ−ト又は転写形態でのラッピング法では、
凹凸模様は賦形できず、得られる化粧材等は意匠性に劣
る。また、ラミネ−ト形態でのラッピング法は、化粧シ
ート全体がそのまま柱状基材に積層される。この為、本
質的には装飾に寄与しない基材シートが化粧材等の最終
製品に添付され省資源的ではない。However, the above conventional method has the following problems. First, in the wrapping method in the form of a laminate or transfer disclosed in and
Uneven patterns cannot be formed, and the resulting decorative material is inferior in design. In the wrapping method in the form of a laminate, the entire decorative sheet is directly laminated on a columnar substrate. For this reason, a base sheet that does not essentially contribute to decoration is attached to a final product such as a decorative material, and is not resource saving.

【０００７】一方、上記(A) 〜(C) による凹凸模様の賦
形方法を、上記したやのラッピング法に適用したと
しても、次の様な問題があった。先ず、(A) の化粧シー
トをラミネ−トする方法の適用では、基材シートとして
熱可塑性樹脂シートに凹凸模様を賦形した化粧シート
を、柱状基材に貼着する事になる為、ラッピングして積
層する時の熱や圧力によって、凹凸模様が浅くなった
り、一部消失する現象が起き易いと言う問題がある。転
写形態となる(B) の方法の適用では、転写層を通してそ
の下の凹凸模様を表現する為に、シャープな凹凸模様は
難しい。しかも、通常のエンボス加工では、柱状基材の
側にまで賦形することが困難であり、その上、柱状基材
断面形状に応じた複数のエンボスローラを転写ローラ同
様に設備する必要があり、柱状基材の場合では平易に製
造できない。更に、ＭＤＦ基材はエンボス自体が入り難
い。また凹凸模様上に転写する為、深い凹凸模様では、
転写層が凹部内部まで入り難く、ローラ圧によるラッピ
ング転写法では難しい。また同じく転写形態となる(C)
の方法の適用では、転写層転写後のエンボスローラによ
る凹凸模様賦形は、柱状基材断面形状に応じた複数のエ
ンボスローラを転写ローラ同様に設備する必要があり、
柱状基材の場合では平易に製造できない。それに加え
て、この方法では間に転写シートを介してエンボスし、
その後転写シートの支持体シートを剥離する為に、深い
凹凸模様は難しく、またシャープな凹凸模様も難しい。
しかも、厚さ数μｍの薄膜の転写層（印刷インキ層）に
対してエンボスする為、凹凸模様として十分目視判別で
きる数１０μｍ〜数１００μｍの凹凸模様を賦形する事
は、原理的にも無理があった。この為、一応の凹凸模様
により凹凸模様無しよりは意匠性は向上するが、リアル
な導管溝表現等は不可能である。On the other hand, even if the method for forming a concavo-convex pattern according to the above (A) to (C) is applied to the above-mentioned wrapping method, the following problems arise. First, in the case of applying the method of laminating a decorative sheet of (A), a decorative sheet in which an irregular pattern is formed on a thermoplastic resin sheet as a base sheet is attached to a columnar base material. There is a problem that the unevenness pattern is likely to be shallow or partially disappear due to heat or pressure when the layers are stacked. In the application of the method (B), which is a transfer mode, it is difficult to form a sharp uneven pattern because the uneven pattern under the transfer layer is expressed through the transfer layer. In addition, it is difficult to form up to the columnar base material side by ordinary embossing, and furthermore, it is necessary to equip a plurality of emboss rollers according to the columnar base material cross-sectional shape in the same manner as the transfer roller, In the case of a columnar substrate, it cannot be manufactured easily. Further, the MDF base material is difficult for the emboss itself to enter. In addition, in order to transfer on the uneven pattern, in the deep uneven pattern,
It is difficult for the transfer layer to enter the inside of the recess, and it is difficult for the lapping transfer method using roller pressure. Also in the transfer form (C)
In the application of the method, the embossing roller shaping after the transfer layer transfer, it is necessary to equip a plurality of embossing rollers according to the columnar substrate cross-sectional shape in the same manner as the transfer roller,
In the case of a columnar substrate, it cannot be manufactured easily. In addition, this method embosses through the transfer sheet in between,
Then, since the support sheet of the transfer sheet is peeled off, it is difficult to form a deep uneven pattern, and it is also difficult to form a sharp uneven pattern.
Moreover, in order to emboss the transfer layer (printing ink layer) of a thin film having a thickness of several μm, it is impossible in principle to form an irregular pattern of several tens μm to several hundred μm which can be visually discriminated as an irregular pattern. was there. For this reason, although the design property is improved by the temporary uneven pattern as compared with the absence of the uneven pattern, it is impossible to realize a realistic conduit groove expression or the like.

【０００８】そこで、本発明の課題は、ラッピング転写
法によって柱状基材を転写装飾して化粧材等とする場合
に、シャープで深い凹凸模様を賦形でき、リアルな木目
導管溝等が表現できる様にする事である。Accordingly, an object of the present invention is to form a sharp and deep uneven pattern when a columnar substrate is transferred and decorated by a lapping transfer method to make a decorative material or the like, and a realistic wood grain conduit groove or the like can be expressed. It is to do.

【０００９】[0009]

【課題を解決するための手段】そこで、上記課題を解決
すべく、本発明のラッピング転写法では、支持体シート
と転写層とからなる転写シートを用いて、柱状基材に転
写層を転写するラッピング転写法において、液状の電離
放射線硬化性樹脂をロール凹版の少なくとも凹部に充填
させると共に該樹脂に基材シートを接触させ該樹脂が基
材シートとロール凹版との間に保持されている状態で電
離放射線を照射して該樹脂を硬化させて凹凸模様とした
該凹凸模様と該基材シートとからなる支持体シートの、
該凹凸模様を有する面に、少なくとも剥離層からなる転
写層を形成した転写シートを用意し、次いで、上記転写
シートを柱状基材の複数の側面に順次ローラで加圧して
積層後、支持体シートを剥離する事で、転写後の最外層
として剥離層を有する転写層を転写し、転写層に前記凹
凸模様を賦形する様にした。その結果、シャープな形状
の凹凸模様を賦形できる。しかも柱状基材が硬質で凹凸
模様をエンボスで賦形出来ない物であっても賦形でき
る。また、この様な場合でも、転写層の厚みを厚くして
おけば、深い凹凸模様も賦形できる。従って、化粧材等
の転写製品は高意匠に出来る事になる。また、凹凸模様
は、化粧シートをラミネ−トする事で付与するので無
く、転写によって付与するので、使用した転写シートの
支持体シートは剥離した後、回収再利用も出来、省資源
的でもある。Therefore, in order to solve the above problems, in the lapping transfer method of the present invention, a transfer layer is transferred to a columnar substrate using a transfer sheet comprising a support sheet and a transfer layer. In the lapping transfer method, a liquid ionizing radiation-curable resin is filled into at least the concave portion of the roll intaglio, and a base sheet is brought into contact with the resin while the resin is held between the base sheet and the roll intaglio. Irradiation of ionizing radiation to cure the resin to form a concavo-convex pattern of the support sheet comprising the base sheet and the concavo-convex pattern,
A transfer sheet having at least a transfer layer formed of a release layer is prepared on the surface having the uneven pattern, and then the transfer sheet is successively pressed with a roller on a plurality of side surfaces of the columnar base material and laminated, and then a support sheet is formed. By peeling off, a transfer layer having a release layer as the outermost layer after the transfer was transferred, and the above-mentioned uneven pattern was formed on the transfer layer. As a result, a sharp uneven pattern can be formed. Moreover, even if the columnar base material is hard and the embossed pattern cannot be formed by embossing, it can be formed. Further, even in such a case, if the thickness of the transfer layer is increased, a deep uneven pattern can be formed. Therefore, a transfer product such as a cosmetic material can be designed with a high design. In addition, since the uneven pattern is provided not by laminating the decorative sheet but by transferring, the support sheet of the used transfer sheet can be recovered and reused after peeling off the used transfer sheet, which is also resource saving. .

【００１０】[0010]

【発明の実施の形態】以下、本発明のラッピング転写法
について、図面を参照しながら実施の形態を説明する。
なお、図１は本発明のラッピング転写法による凹凸模様
の賦形方法を、その一形態で概念的に説明する説明図で
あり、図２は本発明で用いる転写シートにて、支持体シ
ートが有する凹凸模様を説明する断面図であり、図３は
本発明のラッピング転写法を、より具体的にその一形態
で概念的に説明する概念図（斜視図）であり、図４は転
写シートの支持体シートに凹凸模様を賦形する方法を説
明する概念図である。DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, embodiments of the lapping transfer method of the present invention will be described with reference to the drawings.
FIG. 1 is an explanatory view conceptually illustrating a method of forming a concavo-convex pattern by the lapping transfer method of the present invention in one form, and FIG. 2 is a transfer sheet used in the present invention. 3 is a conceptual diagram (perspective view) conceptually illustrating the lapping transfer method of the present invention more specifically in one form, and FIG. It is a conceptual diagram explaining the method of shaping an uneven | corrugated pattern on a support body sheet.

【００１１】〔概要〕先ず、本発明のラッピング転写法
では、図１（Ａ）に例示する如く、用いる転写シートＳ
には、その支持体シート１に、上記特定の方法で賦形し
た凹凸模様４を有するシートを使用する。該特定方法に
よって凹凸模様を支持体シートに賦形しておく事で、シ
ャープな形状で、また深い凹凸模様も忠実に柱状基材に
賦形する事が可能となる。そして、転写層２としては、
少なくとも剥離層５を有する。転写層２は、転写後の転
写層面に凹凸模様が賦形される為の層として、少なくと
も剥離層５を有する。もちろん、図１（Ａ）の如く、本
発明で使用し得る転写シートＳとしては、剥離層５以外
に、必要に応じ従来公知の装飾層６、接着剤層７等が有
っても良い。[Outline] First, in the lapping transfer method of the present invention, as shown in FIG.
For the support sheet 1, a sheet having a concavo-convex pattern 4 formed by the above-described specific method is used as the support sheet 1. By shaping the uneven pattern on the support sheet by the specific method, it is possible to shape the sharp uneven shape and the deep uneven pattern faithfully on the columnar substrate. And as the transfer layer 2,
It has at least a release layer 5. The transfer layer 2 has at least a release layer 5 as a layer for forming a concavo-convex pattern on the transfer layer surface after transfer. Needless to say, as shown in FIG. 1A, the transfer sheet S that can be used in the present invention may include a conventionally known decorative layer 6, an adhesive layer 7, and the like, if necessary, in addition to the release layer 5.

【００１２】そして、図１（Ｂ）に例示する如く、図１
（Ａ）の如き転写シートＳを柱状基材Ｂにラッピング転
写法によって転写する事で、柱状基材に支持体シート１
の凹凸模様４に基づく凹凸模様４Ａを賦形出来、凹凸模
様４Ａを有する化粧材等の転写製品Ｐが得られる。凹凸
模様４Ａは、転写シートＳの支持体シート１が有する凹
凸模様４と逆凹凸形状の凹凸である。しかも、本発明で
は硬化して三次元高分子架橋体となった凹凸模様４を用
いて賦形する為、転写製品Ｐに転写賦形された凹凸模様
４Ａは、支持体シート１の凹凸模様４が変形する事無く
忠実に逆凹凸となった形状が可能となる。なお、同図の
転写製品Ｐでは、柱状基材Ｂに、接着剤層７、装飾層６
及び剥離層５からなる転写層２がこの順に転写により積
層され、剥離層５に凹凸模様４Ａが賦形された構成であ
る。この様に、剥離層の他に、装飾層等も転写形成すれ
ば、凹凸模様の賦形の他に、絵柄等による装飾も同時に
できる。なお、転写シートを柱状基材に転写する為のラ
ッピング転写法としては、従来公知の方法で良い（図３
参照）。ところで、図１では、剥離層５の厚みは凹凸模
様４の深さよりも厚いが、装飾層６や接着剤層７等の他
の層を転写層２が有する場合には、転写層全体の厚さが
凹凸模様の深さを十分に表現できる厚さであれば良い。
つまり、凹凸模様は装飾層や接着剤層内部にまで入り込
んでも良い。また、支持体シート１に於ける凹凸模様４
は、図２（Ａ）、或いは図１（Ａ）及び（Ｂ）の如く、
凸部４ａと凹部底面となる樹脂層４ｂとから構成しても
良いし、図２（Ｂ）の如く凸部４ａのみから構成しても
良い。As shown in FIG. 1B, FIG.
By transferring the transfer sheet S as shown in (A) to the columnar substrate B by a lapping transfer method, the support sheet 1 is transferred to the columnar substrate.
The uneven pattern 4A based on the uneven pattern 4 can be formed, and a transfer product P such as a cosmetic material having the uneven pattern 4A can be obtained. The concavo-convex pattern 4A is a concavo-convex pattern that is the reverse of the concavo-convex pattern 4 of the support sheet 1 of the transfer sheet S. In addition, in the present invention, since the shaping is performed using the uneven pattern 4 which has been cured to form a three-dimensional polymer crosslinked body, the uneven pattern 4A transferred and shaped on the transfer product P is the uneven pattern 4A of the support sheet 1. Can be faithfully formed into a reverse uneven shape without being deformed. In addition, in the transfer product P of the same figure, the adhesive layer 7 and the decorative layer 6
The transfer layer 2 including the release layer 5 and the transfer layer 2 is laminated by transfer in this order, and the release layer 5 is formed with the uneven pattern 4A. In this manner, if a decorative layer or the like is formed by transfer in addition to the release layer, decoration with a picture or the like can be simultaneously performed in addition to shaping of the uneven pattern. As a lapping transfer method for transferring the transfer sheet to the columnar substrate, a conventionally known method may be used (see FIG. 3).
reference). In FIG. 1, the thickness of the release layer 5 is larger than the depth of the concavo-convex pattern 4. However, when the transfer layer 2 has other layers such as the decoration layer 6 and the adhesive layer 7, the thickness of the entire transfer layer is It is sufficient if the thickness is sufficient to express the depth of the uneven pattern.
That is, the uneven pattern may penetrate into the decoration layer and the adhesive layer. The uneven pattern 4 on the support sheet 1
Is, as shown in FIG. 2 (A) or FIGS. 1 (A) and (B),
It may be composed of the convex portion 4a and the resin layer 4b which is the bottom surface of the concave portion, or may be composed only of the convex portion 4a as shown in FIG.

【００１３】以上の結果、本発明では、シャープで深い
凹凸模様も賦形でき、しかも、ラミネ−ト法に比べて、
剥離した支持体シートは回収再利用も出来、省資源的な
ラッピング法による凹凸模様の賦形方法となる。また、
凹凸模様は転写により賦形されるので、柱状基材に転写
層転写前、或いは転写層転写後にエンボス等で賦形する
場合に比べて、安定的形状の凹凸模様を付与できる。そ
の上、エンボス版をラッピングローラの如き配列をした
複雑な機構をラッピング機に追加する必要も無い。As a result of the above, in the present invention, a sharp and deep uneven pattern can be formed, and moreover, compared with the laminating method,
The peeled support sheet can be recovered and reused, and it becomes a method of shaping an uneven pattern by a resource-saving lapping method. Also,
Since the concavo-convex pattern is formed by transfer, a more stable concavo-convex pattern can be imparted to the columnar base material than in the case where the concavo-convex pattern is formed by embossing before or after the transfer layer transfer. In addition, there is no need to add a complicated mechanism in which the embossing plate is arranged like a wrapping roller to the wrapping machine.

【００１４】以下、更に、本発明のラッピング転写法に
ついて、更に詳述する。Hereinafter, the lapping transfer method of the present invention will be described in more detail.

【００１５】〔柱状基材〕柱状基材Ｂとしては、その外
表面にラッピング法によって転写シートを積層し得る断
面形状であれば、いかなる形状、材料からなる基材でも
良く、特に限定はない。柱状基材の断面形状は、例え
ば、凸多角形状、凹多角形状、円形状、長円形状、方形
形状等である。なお、断面形状が長方形の一形態が板材
である。ラッピング転写法に於ける板材では、その主平
面（一番広い面積の面のこと。これも一つの側面）以外
に少なくとも一つの他の側面も被転写面となる。また、
柱状基材の材料は、木質の場合であればその木材種は、
例えば、杉、松、檜、樫、ラワン、チーク、メラピー等
であり、その形態は、単板、合板、木質中密度繊維板
（ＭＤＦ）、パーティクルボード、集成材等である。こ
の他、柱状基材の材料としては、ケイ酸カルシウム、押
し出しセメント、スラグセメント、ＡＬＣ（軽量気泡コ
ンクリート）、ＧＲＣ（硝子繊維強化コンクリート）、
パルプセメント等の非陶磁器窯業系材料、或いは、鉄、
アルミニウム、銅等の金属材料、陶磁器やガラス等のセ
ラミックス等の無機質材料、ポリプロピレン、ＡＢＳ樹
脂、フェノール樹脂等の樹脂材料等が挙げられる。な
お、柱状基材には、必要に応じ、転写シートの積層に先
立って、必要に応じ、公知の目止め処理、着色塗装処理
等を施しても良い。[Pillar-shaped Substrate] The pillar-shaped substrate B may be a substrate made of any shape and material as long as the transfer sheet can be laminated on its outer surface by a lapping method, and is not particularly limited. The cross-sectional shape of the columnar substrate is, for example, a convex polygonal shape, a concave polygonal shape, a circular shape, an oval shape, a square shape, or the like. One form of a rectangular cross section is a plate material. In the plate material in the lapping transfer method, at least one other side surface is also a transfer surface in addition to the main plane (the surface having the largest area; this is also one side surface). Also,
If the material of the columnar base material is wood,
For example, there are cedar, pine, cypress, oak, lauan, teak, melapy and the like, and the form is veneer, plywood, medium density fiberboard (MDF), particle board, laminated wood, and the like. In addition, as materials for the columnar base material, calcium silicate, extruded cement, slag cement, ALC (lightweight cellular concrete), GRC (glass fiber reinforced concrete),
Non-ceramic ceramic materials such as pulp cement, or iron,
Examples include metal materials such as aluminum and copper, inorganic materials such as ceramics such as ceramics and glass, and resin materials such as polypropylene, ABS resin, and phenol resin. Prior to lamination of the transfer sheet, the columnar base material may be subjected to known sealing treatment, coloring coating treatment, or the like, if necessary, before the lamination.

【００１６】〔支持体シート〕転写シートＳの支持体シ
ート１には、前述図１（Ａ）の如く、基材シート３に特
定の方法によって凹凸模様４が賦形された構成の支持体
シート１を使用する。本発明では、図４に示す如く基材
シートに凹凸模様を賦形するには、液状の電離放射線硬
化性樹脂（の未硬化物）をロール凹版の少なくとも凹部
に充填させると共に該樹脂に基材シートを接触させ、該
樹脂が基材シートとロール凹版との間に保持されている
状態で電離放射線を照射して該樹脂を硬化させて凹凸模
様とする事で、基材シートに凹凸模様を賦形する。な
お、この凹凸模様の賦形方法は、特開昭５７−８７３１
８号公報、特公昭５７−２２７５５号公報、特公昭６３
−５００６６号公報、特開平７−３２４７６号公報等に
開示されるものであって、賦形型（ロール凹版）の凹凸
形状を忠実に電離放射性硬化性樹脂の硬化物（凹凸模
様）として基材シートに賦形する方法である。この方法
は基本的には、以下の工程からなる（図４参照）。[Support Sheet] The support sheet 1 of the transfer sheet S has a concavo-convex pattern 4 formed on a base sheet 3 by a specific method as shown in FIG. Use 1. In the present invention, in order to form a concavo-convex pattern on the substrate sheet as shown in FIG. 4, a liquid ionizing radiation-curable resin (uncured material) is filled into at least the concave portion of the roll intaglio, and the resin is coated with the substrate. The sheet is brought into contact with the substrate, and the resin is cured by irradiation with ionizing radiation in a state where the resin is held between the base sheet and the roll intaglio to form a concavo-convex pattern. Shape. In addition, the method of forming the concavo-convex pattern is described in JP-A-57-8731.
No. 8, JP-B-57-22755, JP-B-63
-50066, JP-A-7-32476, etc., wherein the irregularities of a shaping mold (roll intaglio) are faithfully reproduced as a cured product (irregular pattern) of an ionizing radiation curable resin. This is a method of shaping a sheet. This method basically includes the following steps (see FIG. 4).

【００１７】表面に目的とする凹凸模様の凹凸形状と
同形状且つ逆凹凸の凹凸形状（凹凸模様）４０を形成し
た円筒形状の版胴（ロール凹版）５０を用意し、これを
軸芯６０の回りに回転させる。 連続帯状の基材シート３を、該ロール凹版の周速度と
同速度で供給する。 該基材シート３と該ロール凹版５０とを、その間に電
離放射線硬化性樹脂の未硬化液状組成物７０を介して重
ね合わせて密着させ、該液状組成物が該ロール凹版の少
なくとも凹部を完全に充填する様にする。 その状態のままで電離放射線照射装置８０から電離放
射線Ｒを照射して、該液状組成物を架橋、硬化させる。 而る後に、基材シート３を、それに接着し且つロール
凹版上の凹凸形状４０が賦形された電離放射線硬化性樹
脂の硬化物からなる凹凸模様４と共に、ロール凹版から
剥離除去する。この結果、凹凸模様４が基材シート３に
接着した構成で支持体シート１が得られる。A cylindrical plate cylinder (roll intaglio) 50 having a concave and convex shape (concavo-convex pattern) 40 having the same shape as the target concavo-convex pattern and a reverse concavo-convex pattern on the surface is prepared. Rotate around. The continuous belt-shaped substrate sheet 3 is supplied at the same speed as the peripheral speed of the roll intaglio. The base sheet 3 and the roll intaglio 50 are overlapped and adhered to each other with an uncured liquid composition 70 of ionizing radiation-curable resin therebetween, and the liquid composition completely covers at least the concave portion of the roll intaglio. Fill. In that state, the liquid composition is irradiated with ionizing radiation R from the ionizing radiation irradiation device 80 to crosslink and cure the liquid composition. Thereafter, the base sheet 3 is peeled off from the roll intaglio together with the concave / convex pattern 4 made of a cured product of the ionizing radiation-curable resin on which the concave / convex shape 40 on the roll intaglio is adhered and formed. As a result, the support sheet 1 is obtained in a configuration in which the uneven pattern 4 is adhered to the base sheet 3.

【００１８】以上の方法に於いて、ロール凹版５０（賦
形型）としては、公知の凹版、グラビア版、エンボス版
と基本的には、同様の材料、同様の構造、同様の製法に
よるものを用いれば良い。ロール凹版の材料としては、
通常は鉄、銅等の金属が用いられる。但し、ロール凹版
内部から紫外線或いは可視光線を照射する場合には、硝
子、石英等の透明な材料を用いる。ロール凹版の軸芯の
回りの回転駆動は、通常の輸転式グラビア印刷機、輪転
式エンボス機等と同様な機構、方法を用いれば良い。基
材シートのロール凹版への密着の為には、ゴム、金属等
のローラ（圧着ローラ）９０で圧着する。又基材シート
のロール凹版からの剥離にもゴム、金属等のローラ（剥
離ローラ）１００で押さえて剥離する。基材シートは連
続帯状のものを用いる。此の様な基材シートは巻出ロー
ル（供給ロール）から巻き出して、凹凸模様の賦形後は
巻取りロール（排紙ロール）で巻き取る。In the above method, the roll intaglio 50 (shaping mold) is basically a known intaglio, gravure, or embossing plate, and is basically made of the same material, the same structure, and the same manufacturing method. You can use it. As a material for roll intaglio,
Usually, metals such as iron and copper are used. However, when irradiating ultraviolet light or visible light from inside the roll intaglio, a transparent material such as glass or quartz is used. The rotary drive about the axis of the intaglio roll may be performed by using the same mechanism and method as those of a normal transfer type gravure printing machine, rotary embossing machine, or the like. In order to adhere the base sheet to the roll intaglio, the base sheet is pressed by a roller (pressure roller) 90 made of rubber, metal, or the like. Also, when the base sheet is peeled from the roll intaglio, the base sheet is peeled by pressing with a roller (peeling roller) 100 made of rubber, metal or the like. The base sheet is a continuous strip. Such a base material sheet is unwound from an unwinding roll (supply roll), and is wound up by a take-up roll (paper discharge roll) after shaping of the uneven pattern.

【００１９】基材シートとロール凹版とを、その間に電
離放射線硬化性樹脂の未硬化液状組成物を介して重ね合
わせて密着させる態様としては、次の(1) 〜(3) があ
る。(1) 先ず基材シート上に液状組成物を塗布し、次い
で該塗布面がロール凹版表面に向くようにして、該基材
シートを該ロール凹版に重ね合わせる。(2) 図４の如く
先ずロール凹版５０上に液状組成物７０をＴダイ等の塗
液供給装置２００を用いて塗布し、次いで該ロール凹版
上の塗布面に基材シート３を重ね合わせる。(3)先ずロ
ール凹版上と基材シート上との各々に液状組成物を塗布
し、次いで該基材シートと該ロール凹版とを各々の塗布
面が対向する様にして重ね合わせる。There are the following (1) to (3) as modes in which the base sheet and the roll intaglio are overlapped and adhered to each other with an uncured liquid composition of an ionizing radiation-curable resin therebetween. (1) First, a liquid composition is applied on a base sheet, and then the base sheet is superimposed on the roll intaglio such that the applied surface faces the surface of the roll intaglio. (2) As shown in FIG. 4, first, the liquid composition 70 is applied onto the roll intaglio 50 using a coating liquid supply device 200 such as a T-die, and then the base sheet 3 is superimposed on the application surface on the roll intaglio. (3) First, the liquid composition is applied to each of the roll intaglio and the base sheet, and then the base sheet and the roll intaglio are overlapped so that the respective application surfaces face each other.

【００２０】ロール凹版と基材シート間にある未硬化液
状組成物への電離放射線の照射の態様としては、次の
とがある。図４の如く電離放射線に対して透明な基
材シートを選び（例えば、紫外線に対してはポリプロピ
レンシート、電子線に対しては薄葉紙を選択）、基材シ
ート側から照射する。電離放射線に対して透明なロー
ル凹版を選び（例えば、紫外線に対して石英のロール凹
版を選択）、ロール凹版の内部から照射する。The mode of irradiation of the uncured liquid composition between the intaglio roll and the substrate sheet with ionizing radiation is as follows. As shown in FIG. 4, a base sheet transparent to ionizing radiation is selected (for example, a polypropylene sheet is selected for ultraviolet rays, and a thin paper sheet is selected for electron beams), and irradiation is performed from the base sheet side. A roll intaglio that is transparent to ionizing radiation is selected (for example, a quartz roll intaglio is selected for ultraviolet rays) and irradiated from inside the roll intaglio.

【００２１】基材シート３の材料は、電離放射線の照射
が上記の態様が可能である樹脂シートが代表的であ
る。すなわち、基材シートの材料としては、ポリエチ
レンテレフタレート、ポリブチレンテレフタレート、ポ
リエチレンナフタレート等の熱可塑性樹脂ポリエステル
樹脂、ポリエチレン、ポリプロピレン、ポリメチルペン
テン、オレフィン系熱可塑性樹脂エラストマー等のポリ
オレフィン樹脂、ポリ塩化ビニル、ポリカーボネート、
ポリスチレン、ＡＢＳ樹脂、アクリル樹脂等の樹脂シー
ト、薄葉紙、上質紙、クラフト紙、和紙等の紙、硝
子、ビニロン、ポリエステル、セルロース等の繊維から
なる不織布、或いは織布、アルミニウム、鉄、銅等の
金属箔等がある。なお、上記〜は、透明ロール凹版
内からの紫外線照射射、又は電子線等の高透過性放射線
の場合のみ可能である。また、基材シートの厚さは通常
２０〜２００μｍ程度のものを用いる。A typical example of the material of the base sheet 3 is a resin sheet which can be irradiated with ionizing radiation in the above-described manner. That is, as the material of the base sheet, thermoplastic resin polyester resin such as polyethylene terephthalate, polybutylene terephthalate, polyethylene naphthalate, polyethylene, polypropylene, polymethylpentene, polyolefin resin such as olefin-based thermoplastic resin elastomer, polyvinyl chloride , Polycarbonate,
Resin sheets such as polystyrene, ABS resin, acrylic resin, etc., paper such as thin paper, woodfree paper, kraft paper, Japanese paper, non-woven fabric consisting of fibers such as glass, vinylon, polyester, cellulose, or woven fabric, aluminum, iron, copper, etc. There are metal foils and the like. The above conditions (1) to (4) are possible only in the case of ultraviolet irradiation from inside the transparent roll intaglio, or in the case of highly transparent radiation such as an electron beam. The thickness of the base sheet is usually about 20 to 200 μm.

【００２２】電離放射線硬化性樹脂としては、分子中に
（メタ）アクリロイル基、（メタ）アクリロイルオキシ
基等の重合性不飽和結合、又は、エポキシ基等のカチオ
ン重合性官能基を有するプレポリマー、モノマー、又は
ポリマー、或いはポリチオ一ル化合物からなり、これら
を１種のみ又は２種以上適宜混合した組成物を用いる。
組成物は、未硬化時に液状のものを用いる。Examples of the ionizing radiation-curable resin include a prepolymer having a polymerizable unsaturated bond such as a (meth) acryloyl group or a (meth) acryloyloxy group, or a cationic polymerizable functional group such as an epoxy group in a molecule. A composition comprising a monomer, a polymer, or a polythiol compound, and a mixture of one or two or more of these compounds is used.
The composition used is a liquid when uncured.

【００２３】前記分子中に重合性不飽和結合を有するプ
レポリマーの例としては、不飽和ジカルボン酸と多価ア
ルコールの縮合物等の不飽和ポリエステル類、ポリエス
テル（メタ）アクリレート、ウレタン（メタ）アクリレ
ート、エポキシ（メタ）アクリレート、メラミン（メ
タ）アクリレート等の（メタ）アクリレート類がある
〔尚、本明細書では（メタ）アクリレートとは、アクリ
レート又はメタクリレートの意味で用いる。以下同
様〕。前記分子中に重合性不飽和結合を有するモノマー
の例としては、スチレン、α−メチルスチレン等のスチ
レン系モノマー、（メタ）アクリル酸メチル、（メタ）
アクリル酸−２−エチルヘキシル、（メタ）アクリル酸
メトキシエチル、（メタ）アクリル酸ブトキシエチル等
の単官能（メタ）アクリル酸エステル類、エチレングリ
コールジ（メタ）アクリレート、プロピレングリコール
ジ（メタ）アクリレート、１，６−ヘキサンジオールジ
（メタ）アクリレート、ジエチレングリコールジ（メ
タ）アクリレート、トリエチレングリコールジ（メタ）
アクリート、トリメチロールプロパントリ（メタ）アク
リレート、ペンタエリスリトールテトラ（メタ）アクリ
レート、ジペンタエリスリトールヘキサ（メタ）アクリ
レート等の多官能（メタ）アクリル酸エステル類、（メ
タ）アクリル酸−２−（Ｎ，Ｎ−ジエチルアミノ）エチ
ル、（メタ）アクリル酸−２−（Ｎ，Ｎ−ジメチルアミ
ノ）エチル、（メタ）アクリル酸−２−（Ｎ，Ｎ−ジベ
ンジルアミノ）エチル等の不飽和酸の置換アミノアルコ
ールエステル類、（メタ）アクリルアミド等の不飽和カ
ルボン酸アミド、分子中に２個以上のメルカプト基を有
するポリチオール化合物、例えば、トリメチロールプロ
パントリチオグリコレート、トリメチロールプロパント
リチオプロピレート、ペンタエリスリトールテトラチオ
グリコール等がある。Examples of the prepolymer having a polymerizable unsaturated bond in the molecule include unsaturated polyesters such as a condensate of an unsaturated dicarboxylic acid and a polyhydric alcohol, polyester (meth) acrylate, and urethane (meth) acrylate. And (meth) acrylates such as epoxy (meth) acrylate and melamine (meth) acrylate [In the present specification, (meth) acrylate is used to mean acrylate or methacrylate. The same applies hereinafter. Examples of the monomer having a polymerizable unsaturated bond in the molecule include styrene-based monomers such as styrene and α-methylstyrene, methyl (meth) acrylate, (meth)
Monofunctional (meth) acrylates such as 2-ethylhexyl acrylate, methoxyethyl (meth) acrylate, butoxyethyl (meth) acrylate, ethylene glycol di (meth) acrylate, propylene glycol di (meth) acrylate, 1,6-hexanediol di (meth) acrylate, diethylene glycol di (meth) acrylate, triethylene glycol di (meth)
Polyfunctional (meth) acrylates such as acrylate, trimethylolpropane tri (meth) acrylate, pentaerythritol tetra (meth) acrylate, dipentaerythritol hexa (meth) acrylate, and (meth) acrylic acid-2- (N, Substituted aminos of unsaturated acids such as N-diethylamino) ethyl, 2- (N, N-dimethylamino) ethyl (meth) acrylate, 2- (N, N-dibenzylamino) ethyl (meth) acrylate Alcohol esters, unsaturated carboxylic acid amides such as (meth) acrylamide, polythiol compounds having two or more mercapto groups in the molecule, for example, trimethylolpropanetrithioglycolate, trimethylolpropanetrithiopropylate, pentaerythritol Such as tetrathioglycol .

【００２４】分子中にカチオン重合性官能基を有するプ
レポリマーとしては、ビスフェノール型エポキシ樹脂、
ノボラック型エポキシ樹脂、脂肪族型エポキシ樹脂等、
脂肪環型エポキシ樹脂等のエポキシ樹脂、脂肪族系ビニ
ルエーテル、芳香族系ビニルエーテル、ウレタン系ビニ
ルエーテル、エステル系ビニルエーテル等のビニルエー
テル系樹脂、環状エーテル系樹脂、スピロ系化合物等の
プレポリマー等がある。As the prepolymer having a cationically polymerizable functional group in the molecule, bisphenol type epoxy resin,
Novolak epoxy resin, aliphatic epoxy resin, etc.
Examples include epoxy resins such as alicyclic epoxy resins, vinyl ether resins such as aliphatic vinyl ethers, aromatic vinyl ethers, urethane vinyl ethers, and ester vinyl ethers; cyclic ether resins; and prepolymers such as spiro compounds.

【００２５】以上の化合物を必要に応じ１種もしくは２
種以上混合して用いるが、樹脂組成物に通常の塗工適性
を付与するために、前記プレポリマー又はオリゴマーを
５重量％以上、前記モノマー及び／又はポリチオールを
９５重量％以下とすることが好ましい。また、硬化物の
可撓性、表面硬度、剥離性等の物性を調節する為に前記
プレポリマー、オリゴマー、モノマーの少なくとも１種
に対して、以下の様な電離放射線非硬化性樹脂を１〜７
０重量％程度混合して用いることができる。電離放射線
非硬化性樹脂としてはウレタン系樹脂、セルロース系樹
脂、ポリエステル系樹脂、アクリル系樹脂、ブチラール
樹脂、ポリ塩化ビニル、ポリ酢酸ビニル等の熱可塑性樹
脂を用いることができる。If necessary, one or two of the above compounds may be used.
The prepolymer or oligomer is preferably used in an amount of 5% by weight or more, and the monomer and / or polythiol is preferably used in an amount of 95% by weight or less in order to impart ordinary coating suitability to the resin composition. . Further, in order to adjust physical properties such as flexibility, surface hardness, and releasability of the cured product, at least one of the above prepolymers, oligomers, and monomers, the following ionizing radiation non-curable resin is used. 7
About 0% by weight can be mixed and used. As the ionizing radiation non-curable resin, a thermoplastic resin such as a urethane resin, a cellulose resin, a polyester resin, an acrylic resin, a butyral resin, polyvinyl chloride, and polyvinyl acetate can be used.

【００２６】また、剥離性を向上させる為は、電離放射
線非硬化性樹脂としてシリコーン樹脂、ポリオレフィン
樹脂等の樹脂の他に、ワックス等を用いても良い。これ
らは１種又は２種以上を用いて剥離性を調整する。In order to improve the releasability, a wax or the like may be used as the non-ionizing radiation curable resin in addition to a resin such as a silicone resin and a polyolefin resin. These may be used alone or in combination of two or more to adjust the releasability.

【００２７】なお、紫外線で硬化させる場合には前記電
離放射線硬化性樹脂組成物に光重合開始剤を添加する。
分子中にラジカル重合性不飽和結合を有する化合物に対
しては、アセトフェノン類、ベンゾフェノン類、ミヒラ
ーベンゾイルベンゾエート、α−アミロキシムエステ
ル、テトラメチルメウラムモノサルファイド、チオキサ
ントン類等がある。分子中にカチオン重合性官能基を有
する化合物に対しては、芳香族ジアゾニウム塩、芳香族
スルホニウム塩、芳香族ヨードニウム塩、メタロセン化
合物、ベンゾインスルホン酸エステル、ジアリルヨード
シル塩等がある。又、必要に応じて更に、光増感剤とし
てｎ−ブチルアミン、トリエチルアミン、トリ−ｎ−ブ
チルホスフィン等を混合して用いることもできる。In the case of curing with ultraviolet rays, a photopolymerization initiator is added to the ionizing radiation-curable resin composition.
Examples of the compound having a radical polymerizable unsaturated bond in the molecule include acetophenones, benzophenones, Michler benzoyl benzoate, α-amyloxime ester, tetramethylmeuram monosulfide, thioxanthones, and the like. Compounds having a cationically polymerizable functional group in the molecule include aromatic diazonium salts, aromatic sulfonium salts, aromatic iodonium salts, metallocene compounds, benzoinsulfonic acid esters, diallyliodosyl salts, and the like. Further, if necessary, n-butylamine, triethylamine, tri-n-butylphosphine, or the like can be further mixed and used as a photosensitizer.

【００２８】以上の電離放射線硬化性樹脂組成物の未硬
化液状組成物をロール凹版、或いは基材シートに塗工す
るには公知の各種方法、例えば、ロールコート、カーテ
ンフローコート、Ｔダイコート（図４）等の方法を用
る。特にロール凹版塗工の場合はインキパン中の液状組
成物に、回転するロール凹版を浸漬させる（所謂ドブ浸
け）も可能である。The uncured liquid composition of the above ionizing radiation-curable resin composition is applied to a roll intaglio or a substrate sheet by various known methods, for example, roll coating, curtain flow coating, T-die coating (see FIG. Use a method such as 4). In particular, in the case of roll intaglio coating, it is possible to immerse the rotating roll intaglio in the liquid composition in the ink pan (so-called dip dipping).

【００２９】尚、ここで電離放射線としては、電磁波又
は荷電粒子線のうち分子を重合、架橋し得るエネルギー
を有するものを意味し、紫外線、可視光線、Ｘ線、電子
線、α線等があるが、通常紫外線、又は電子線が用いら
れる。紫外線源としては、超高圧水銀灯、高圧水銀灯、
低圧水銀灯、カーボンアーク灯、ブラックライトラン
プ、メタルハライドランプ等の光源が使用される。電子
線源としては、コッククロフトワルトン型、バンデグラ
フト型、共振変圧器型、絶縁コア変圧器型、或いは、直
線型、ダイナミトロン型、高周波型等の各種電子線加速
器を用い、１００〜１０００ｋｅＶ、好ましくは、１０
０〜３００ｋｅＶのエネルギーをもつ電子を照射するも
のが使用される。Here, the ionizing radiation means an electromagnetic wave or a charged particle beam having energy capable of polymerizing and cross-linking molecules, and includes ultraviolet rays, visible rays, X-rays, electron rays, α rays and the like. However, ultraviolet rays or electron beams are usually used. Ultra-high pressure mercury lamps, high pressure mercury lamps,
Light sources such as low-pressure mercury lamps, carbon arc lamps, black light lamps, and metal halide lamps are used. As the electron beam source, various types of electron beam accelerators such as Cockcroft-Walton type, Van degraft type, resonance transformer type, insulating core transformer type, or linear type, dynamitron type, high frequency type, etc. are used, preferably 100 to 1000 keV, preferably. Is 10
A device that irradiates electrons having an energy of 0 to 300 keV is used.

【００３０】〔凹凸模様〕支持体シート１に於ける凹凸
模様４としては、特に限定は無い。凹凸模様は、例え
ば、砂目、梨地、ヘアライン、万線状溝、花崗岩の劈開
面の凹凸模様、木目導管溝、木目年輪模様、布目の表面
テクスチュア、皮絞、文字、幾何学模様等である。特に
本発明では、シャープな凹凸模様や深い凹凸模様を転写
製品に賦形できるので、化粧材にて高意匠な凹凸模様が
可能である。支持体シートに於ける凹凸模様の高さ及び
形状は、ほぼそのまま転写製品に於ける凹凸模様の深さ
及び形状となる。また、本発明の転写法ではシャープで
且つ深い凹凸模様を転写製品に賦形出来るので、ロール
凹版として、原形状（原稿）に忠実な凹凸模様、或いは
原形状とは異なっていても視覚的に原形状の凹凸を忠実
に再現出来る凹凸模様を有するものを用いることが効果
的である。前者の例としては原稿から型採りした母型上
にメッキして製造する電鋳エンボス版等である。また、
後者の例としては特開平４−３０８７９９号公報等で開
示される様に、多段階エッチング等によって、ロール凹
版の凹凸形状の凹部深さを変化させて得られる、高さが
変化する凹凸模様等が好適である。凹凸模様４の高さ
は、凹凸模様を賦形する転写製品の用途等にもよるが、
例えば３０〜１００μｍ程度である。この範囲とすれ
ば、化粧材等の転写製品に十分に高意匠性の凹凸模様を
賦形できる。[Concavo-convex pattern] The concavo-convex pattern 4 on the support sheet 1 is not particularly limited. The uneven pattern is, for example, a grain, a satin finish, a hairline, a linear groove, a concave and convex pattern of a cleavage face of granite, a grain conduit groove, a grain annual ring pattern, a texture of a cloth grain, a leather squeezing, a character, a geometric pattern, and the like. . In particular, in the present invention, a sharp uneven pattern or a deep uneven pattern can be formed on a transfer product, so that a highly-designed uneven pattern can be formed with a decorative material. The height and shape of the concavo-convex pattern in the support sheet are almost the same as the depth and shape of the concavo-convex pattern in the transfer product. Further, in the transfer method of the present invention, a sharp and deep concave-convex pattern can be formed on a transfer product. Therefore, as a roll intaglio, even if the concave-convex pattern faithful to the original shape (original document) or the original shape is different, it is visually recognized. It is effective to use a material having an uneven pattern that can faithfully reproduce the unevenness of the original shape. An example of the former is an electroformed embossing plate or the like manufactured by plating a mother die taken from a manuscript. Also,
As an example of the latter, as disclosed in Japanese Patent Application Laid-Open No. 4-308799, etc., a concave-convex pattern having a variable height obtained by changing the concave depth of the concave-convex shape of the roll intaglio by multi-step etching or the like. Is preferred. The height of the uneven pattern 4 depends on the use of the transfer product for forming the uneven pattern,
For example, it is about 30 to 100 μm. Within this range, a transferable product such as a cosmetic material can be provided with a sufficiently high-design irregularity pattern.

【００３１】〔支持体シートの他の構成要素〕以上の様
にして得られる支持体シートには、更に必要に応じ、転
写層側に転写層（剥離層）との剥離性を向上させる為、
支持体シートの構成要素として離型層を設けても良い。
もちろん、離型層は凹凸模様による凹凸形状が消失しな
い程度の厚さとする。また、離型層は本来薄くても機能
する。離型層の厚さは例えば０．１〜５μｍ程度であ
る。離型層としては、例えば、シリコーン樹脂、メラミ
ン樹脂、ポリアミド樹脂、ウレタン樹脂、ポリオレフィ
ン樹脂、ワックス等の単体又はこれらを含む混合物が用
いられる。また、剥離性の調整の為に、支持体の転写層
側の面にコロナ放電処理、オゾン処理等を行っても良
い。[Other components of the support sheet] The support sheet obtained as described above may be further provided on the transfer layer side, if necessary, in order to improve the releasability from the transfer layer (release layer).
A release layer may be provided as a component of the support sheet.
Of course, the thickness of the release layer is set to such an extent that the uneven shape due to the uneven pattern does not disappear. Further, the release layer functions even if it is originally thin. The thickness of the release layer is, for example, about 0.1 to 5 μm. As the release layer, for example, a simple substance such as a silicone resin, a melamine resin, a polyamide resin, a urethane resin, a polyolefin resin, a wax, or a mixture containing these is used. In order to adjust the releasability, the surface of the support on the transfer layer side may be subjected to corona discharge treatment, ozone treatment, or the like.

【００３２】〔剥離層〕本発明では、転写する転写層２
の必須構成要素はこの剥離層５のみである。支持体シー
トの凹凸模様を柱状基材に賦形する為には、転写層とし
ては最低限、支持体シートの凹凸模様に接する剥離層が
有れば足りるからである。剥離層は転写層の受容層とし
て機能する。転写層が剥離層のみの場合は、柱状基材に
付与されるのは凹凸模様である。印刷等による絵柄の付
与は必要無く、凹凸模様のみの賦形で足りる場合等であ
る。従って、転写層が剥離層のみの場合には、剥離層に
は凹凸模様の深さに対応する十分な厚さとするのが好ま
しい。なお、転写層が剥離層以外に装飾層や接着剤層等
も有する場合には、これら層からなる転写層として凹凸
模様の深さに対応する厚さがあれば良い。従って、剥離
層の厚さは０．１〜１００μｍ程度である。[Release Layer] In the present invention, the transfer layer 2 to be transferred is used.
Is an essential component only of this release layer 5. This is because, in order to form the uneven pattern of the support sheet on the columnar substrate, it is sufficient that the transfer layer has at least a release layer in contact with the uneven pattern of the support sheet. The release layer functions as a receiving layer of the transfer layer. When the transfer layer is only a release layer, the uneven pattern is applied to the columnar substrate. In some cases, it is not necessary to provide a picture pattern by printing or the like, and it is sufficient to form only an uneven pattern. Therefore, when the transfer layer is only the release layer, it is preferable that the release layer has a sufficient thickness corresponding to the depth of the uneven pattern. In the case where the transfer layer also has a decorative layer, an adhesive layer, and the like in addition to the release layer, the transfer layer formed of these layers only needs to have a thickness corresponding to the depth of the uneven pattern. Therefore, the thickness of the release layer is about 0.1 to 100 μm.

【００３３】なお、剥離層は無色透明でも良いが、着色
透明でも良い。着色透明の剥離層は装飾層を兼用する層
とできる。また、剥離層は、その下の層として装飾層等
も同時に転写する場合には、装飾層等の下層を保護する
等の為の機能層としてや、塗装感等の意匠感を付与する
等の為の装飾層の一種として使用する事もある。また、
装飾層が無い場合には、剥離層は不透明（無色又は着
色）でも良い。The release layer may be colorless and transparent, but may be colored and transparent. The colored transparent release layer can be a layer also serving as a decoration layer. Further, when the decorative layer and the like are simultaneously transferred as a layer below the release layer, a functional layer for protecting the lower layer such as the decorative layer and the like, and a design feeling such as a paint feeling are imparted. It is sometimes used as a kind of decorative layer. Also,
If there is no decorative layer, the release layer may be opaque (colorless or colored).

【００３４】上記の様な剥離層としては、用途や物性等
に応じた従来公知の材料で、従来公知の方法で形成すれ
ば良く、特に制限は無い。例えば、剥離層の材料として
は、ポリメチル（メタ）アクリレート、ポリブチル（メ
タ）アクリレート、メチル（メタ）アクリレート−ブチ
ル（メタ）アクリレート共重合体等のアクリル樹脂、ポ
リエチレン、ポリプロピレン、ポリメチルペンテン、オ
レフィン系熱可塑性樹脂エラストマー等のポリオレフィ
ン樹脂、酢酸ビニル樹脂、ブチラール樹脂、塩化ビニル
−酢酸ビニル共重合体、セルロース系樹脂等の熱可塑性
樹脂、ポリウレタン樹脂、エポキシ樹脂、フェノール樹
脂、尿素樹脂、ジアリルフタレート樹脂、メラミン樹
脂、グアナミン樹脂、不飽和ポリエステル系樹脂、アミ
ノアルキッド樹脂、メラミン−尿素共縮合樹脂、珪素樹
脂、ポリシロキサン樹脂等の常温又は熱硬化性樹脂、或
いはアクリレート系、エポキシ系等の電離放射線硬化性
樹脂等を、これら樹脂の単体、又は混合物の形で用い
る。熱硬化性樹脂等の硬化性樹脂は、耐擦傷性等の表面
物性が要求される用途では好適である。また、剥離層の
形成は、例えば、グラビア印刷、シルクスクリーン印
刷、オフセット印刷等の印刷法や、グラビアコート、ロ
ールコート、或いはＴダイ等による溶融押出塗工等の塗
工法等で形成すれば良い。溶融押出塗工は、上記ポリオ
レフィン樹脂等で溶液等で塗工出来ない場合に好まし
く、また５０μｍや１００μｍ等と厚く形成する場合に
も好ましい。The release layer as described above may be formed by a conventionally known method using a conventionally known material according to the application and physical properties, and is not particularly limited. For example, as a material of the release layer, acrylic resin such as polymethyl (meth) acrylate, polybutyl (meth) acrylate, methyl (meth) acrylate-butyl (meth) acrylate copolymer, polyethylene, polypropylene, polymethylpentene, olefin-based Polyolefin resin such as thermoplastic resin elastomer, vinyl acetate resin, butyral resin, vinyl chloride-vinyl acetate copolymer, thermoplastic resin such as cellulose resin, polyurethane resin, epoxy resin, phenol resin, urea resin, diallyl phthalate resin, Room temperature or thermosetting resins such as melamine resin, guanamine resin, unsaturated polyester resin, amino alkyd resin, melamine-urea co-condensation resin, silicon resin, polysiloxane resin, or ionizing radiation of acrylate type, epoxy type, etc. The curable resin or the like, used in the form of a single resin, or a mixture. A curable resin such as a thermosetting resin is suitable for applications requiring surface properties such as scratch resistance. The release layer may be formed by, for example, a printing method such as gravure printing, silk screen printing, or offset printing, or a coating method such as gravure coating, roll coating, or melt extrusion coating using a T-die or the like. . Melt extrusion coating is preferred when the above-mentioned polyolefin resin or the like cannot be applied with a solution or the like, and is also preferred when the coating is formed as thick as 50 μm or 100 μm.

【００３５】また、剥離層中には、必要に応じて更に、
ベンゾトリアゾール系、ベンゾフェノン系等の紫外線吸
収剤、ヒンダードアミン系ラジカル捕捉剤等の光安定
剤、シリカ、球状α−アルミナ等の粒子からなる減摩
剤、下記装飾層で列記する光輝性顔料等の着色顔料、体
質顔料、滑剤等を添加しても良い。In the release layer, if necessary,
Benzotriazole-based, benzophenone-based UV absorbers, light stabilizers such as hindered amine radical scavengers, lubricating agents consisting of particles such as silica and spherical α-alumina, and coloring of glittering pigments listed in the decorative layer below Pigments, extenders, lubricants and the like may be added.

【００３６】〔装飾層〕装飾層６には特に限定は無い。
従来公知の物で良い。例えば、グラビア印刷、シルクス
クリーン印刷、オフセット印刷等の従来公知の方法、材
料で絵柄等を印刷した絵柄層、単なる着色樹脂層、透明
樹脂層、或いはアルミニウム、クロム等の金属を公知の
蒸着法等で部分又は全面に形成した金属薄膜層等であ
る。絵柄は、木目模様、大理石や御影石等の石目模様、
タイル調模様、煉瓦調模様、布目模様、文字、幾何学模
様など任意である。凹凸模様と装飾層との組み合わせの
例としては、例えば凹凸模様は導管溝柄として、装飾層
は木目模様の絵柄層等とする組み合わせ、凹凸模様は花
崗岩劈開面の凹凸で、装飾層は花崗岩の石目模様の絵柄
層とする組み合わせ等は好適である。[Decoration Layer] The decoration layer 6 is not particularly limited.
Conventionally known ones may be used. For example, a conventionally known method such as gravure printing, silk screen printing, offset printing, etc., a picture layer printed with a picture or the like with a material, a simple colored resin layer, a transparent resin layer, or a metal such as aluminum, chromium or the like by a known vapor deposition method And a metal thin film layer or the like formed on a part or the entire surface. The pattern is a wood grain pattern, a stone pattern such as marble or granite,
Tile patterns, brick patterns, cloth patterns, characters, geometric patterns, etc. are optional. As an example of the combination of the uneven pattern and the decorative layer, for example, the uneven pattern is a conduit groove pattern, the decorative layer is a combination of a wood grain pattern layer, etc., the uneven pattern is the unevenness of the granite cleavage surface, the decorative layer is the granite A combination with a stone-patterned pattern layer is suitable.

【００３７】なお、絵柄層用インキは、バインダー等か
らなるビヒクル、顔料や染料等の着色剤、これに適宜加
える各種添加剤からなる。バインダーには、例えば、ア
クリル樹脂、塩素化ポリオレフィン樹脂、塩素化ポリプ
ロピレン、酢酸ビニル樹脂、ブチラール樹脂、塩化ビニ
ル−酢酸ビニル共重合体、セルロース系樹脂等の熱可塑
性樹脂、ポリウレタン樹脂、エポキシ樹脂等の常温又は
熱硬化性樹脂等を、これら樹脂の単体、又は混合物の形
で用いる。着色剤の顔料は、チタン白、カーボンブラッ
ク、弁柄、黄鉛、群青等の無機顔料、アニリンブラッ
ク、キナクリドン、イソインドリノン、フタロシアニン
ブルー等の有機顔料、アルミニウム箔粉等の金属顔料、
二酸化チタン被覆雲母箔粉等の真珠光沢（パール）顔料
等である。The picture layer ink comprises a vehicle such as a binder, a coloring agent such as a pigment or a dye, and various additives appropriately added thereto. For the binder, for example, acrylic resin, chlorinated polyolefin resin, chlorinated polypropylene, vinyl acetate resin, butyral resin, vinyl chloride-vinyl acetate copolymer, thermoplastic resin such as cellulose resin, polyurethane resin, epoxy resin, etc. A room temperature or thermosetting resin or the like is used alone or in the form of a mixture of these resins. Colorant pigments include titanium white, carbon black, red iron oxide, graphite, inorganic pigments such as ultramarine blue, aniline black, quinacridone, isoindolinone, organic pigments such as phthalocyanine blue, metal pigments such as aluminum foil powder,
Pearlescent pigments such as mica foil powder coated with titanium dioxide.

【００３８】〔接着剤層〕転写層に於ける接着剤層７
は、必要に応じで設ける。接着剤層７は、柱状基材側に
接着剤層を設ける場合や、接着剤層無しの転写層で接着
する場合には省略できる。接着剤層７は転写シートに予
め又は転写シート使用時に設ける。使用時に設ける形態
では、未乾燥状態等で接着剤層にタックが有っても良
い。また、柱状基材側に接着剤層を設ける場合でも、接
着剤層は予め又は転写シート使用時に設ける。転写シー
ト使用時の形態では、未乾燥状態等で接着剤層にタック
が有っても良い。[Adhesive layer] Adhesive layer 7 in transfer layer
Is provided as needed. The adhesive layer 7 can be omitted when an adhesive layer is provided on the columnar base material side or when a transfer layer without an adhesive layer is used for bonding. The adhesive layer 7 is provided on the transfer sheet in advance or when the transfer sheet is used. In the form provided at the time of use, the adhesive layer may have a tack in an undried state or the like. Further, even when the adhesive layer is provided on the columnar substrate side, the adhesive layer is provided in advance or when the transfer sheet is used. When the transfer sheet is used, the adhesive layer may have a tack in an undried state or the like.

【００３９】転写シートや柱状基材に設ける接着剤層の
樹脂としては、特に制限は無く、柱状基材、用途等に応
じて従来公知の樹脂を使用すれば良い。例えば、熱可塑
性樹脂や硬化性樹脂（未硬化物）である。硬化性樹脂
は、熱、湿気（水）、紫外線や電子線等の電離放射線等
で硬化する樹脂である。熱の場合は熱硬化性樹脂、湿気
の場合は１液硬化型ウレタン樹脂等、電離放射線の場合
は紫外線硬化性樹脂や電子線硬化性樹脂等の電離放射線
硬化性樹脂等である。また、上記熱可塑性樹脂や硬化性
樹脂は、加熱軟化温度（硬化性樹脂ではその未硬化組成
物に対する温度）を選ぶ事で熱融着型接着剤として使用
でき、また加熱軟化温度が高い樹脂でも、溶剤溶液（含
む分散液）等とすれば、溶剤揮散型接着剤として使用で
きる。なお、転写シートに於ける転写層は、凹凸模様４
を転写層で埋め尽くすに十分な厚みとする事が好ましい
が、この為に、剥離層や装飾層等で十分な厚みとしない
場合には、接着剤層によって転写層を必要な厚みとする
と良い。従って、転写シートに於ける接着剤層の厚み
は、支持体シートに於ける凹凸模様の高さにもよるが、
５〜１００μｍ程度である。また、柱状基材の場合で
も、接着剤層は同様の厚み範囲で良い。The resin of the adhesive layer provided on the transfer sheet or the columnar substrate is not particularly limited, and a conventionally known resin may be used according to the columnar substrate, application, and the like. For example, it is a thermoplastic resin or a curable resin (uncured material). The curable resin is a resin that is cured by heat, moisture (water), ionizing radiation such as ultraviolet rays and electron beams, and the like. In the case of heat, a thermosetting resin is used. In the case of moisture, a one-component curable urethane resin is used. In the case of ionizing radiation, an ionizing radiation curable resin such as an ultraviolet curable resin or an electron beam curable resin is used. Further, the thermoplastic resin and the curable resin can be used as a heat-sealing adhesive by selecting a heat softening temperature (a temperature for the uncured composition in the case of the curable resin), and a resin having a high heat softening temperature can be used. , A solvent solution (including a dispersion) or the like can be used as a solvent-evaporating adhesive. The transfer layer in the transfer sheet has an uneven pattern 4
It is preferable that the thickness is sufficient to fill the transfer layer with the transfer layer. For this reason, if the thickness of the release layer or the decoration layer is not sufficient, the transfer layer may be formed to a necessary thickness by the adhesive layer. . Therefore, although the thickness of the adhesive layer in the transfer sheet depends on the height of the uneven pattern in the support sheet,
It is about 5 to 100 μm. Also, in the case of a columnar substrate, the adhesive layer may have a similar thickness range.

【００４０】なお、上記熱可塑性樹脂としては、例え
ば、特公平７−４３６号公報等に開示されるダイマー酸
とエチレンジアミンとの縮重合により得られる重合物等
のポリアミド樹脂、熱可塑性ウレタン樹脂、塩化ビニル
−酢酸ビニル共重合体、ポリ酢酸ビニル樹脂、アクリル
樹脂等を用いれば良い。前記ダイマー酸とエチレンジア
ミンとの縮合物からなるポリアミドとしては、例えば融
点が１５０〜１７０℃のポリアミドと、融点が１８０〜
２３０℃のポリアミドとの混合物が好ましい一例であ
る。これらのポリアミドの具体例としては、ナイロン
６、ナイロン６６、ナイロン６１０、ナイロン６１２、
ナイロン１１、ナイロン１２、共重合ナイロン、ナイロ
ンＭＸＤ、ナイロン４６等が挙げられ、特にバーサロン
型ポリアミドが好ましい。この他、上記熱可塑性樹脂と
しては、ポリプロピレン、ポリエチレン、ポリメチルペ
ンテン、エチレン−プロピレン−ブテン３元共重合体、
オレフィン系熱可塑性エラストマー等のポリオレフィン
樹脂等も用途に応じて使用できる。Examples of the thermoplastic resin include polyamide resins such as a polymer obtained by polycondensation of dimer acid and ethylenediamine disclosed in Japanese Examined Patent Publication No. 7-436, etc., thermoplastic urethane resins, and chloride resins. A vinyl-vinyl acetate copolymer, a polyvinyl acetate resin, an acrylic resin, or the like may be used. As the polyamide composed of a condensate of the dimer acid and ethylenediamine, for example, a polyamide having a melting point of 150 to 170 ° C. and a melting point of 180 to 170 ° C.
A mixture with a polyamide at 230 ° C. is a preferred example. Specific examples of these polyamides include nylon 6, nylon 66, nylon 610, nylon 612,
Nylon 11, nylon 12, copolymerized nylon, nylon MXD, nylon 46, and the like can be mentioned, and a varsal type polyamide is particularly preferable. In addition, as the thermoplastic resin, polypropylene, polyethylene, polymethylpentene, ethylene-propylene-butene terpolymer,
Polyolefin resins such as olefinic thermoplastic elastomers can also be used depending on the application.

【００４１】また、上記熱硬化性樹脂としては、例え
ば、フェノール樹脂、尿素樹脂、ジアリルフタレート樹
脂、熱硬化型ウレタン樹脂、エポキシ樹脂等を使用でき
る。また、熱硬化型ウレタン樹脂等は、未硬化時に常温
固体の樹脂組成物としても使用でき、予め転写シートに
設けておく構成での接着剤層としても使用できる。この
場合、転写シート積層時に熱融着性とすべくその時点で
完全硬化させない為には、接着剤層形成時の加熱乾燥条
件を調整し、流動性を失う程度に不完全硬化させるか、
或いは、イソシアネートにブロックイソシアネートを用
いても良い。As the thermosetting resin, for example, phenol resin, urea resin, diallyl phthalate resin, thermosetting urethane resin, epoxy resin and the like can be used. Further, the thermosetting urethane resin or the like can be used as a resin composition which is solid at room temperature when it is not cured, and can also be used as an adhesive layer having a structure provided in advance on a transfer sheet. In this case, in order not to completely cure at that time in order to make it heat-fusible at the time of laminating the transfer sheet, adjust the heating and drying conditions at the time of forming the adhesive layer and perform incomplete curing to the extent that fluidity is lost,
Alternatively, a blocked isocyanate may be used as the isocyanate.

【００４２】接着剤層の形成は、上記樹脂を、水や有機
溶剤等の溶媒（又は分散媒）に溶解（又は分散）した溶
液（又は分散液）の形態で、或いは無溶剤液状物やホッ
トメルトの形態で施す。形成法には特に限定は無く、従
来公知の塗工法、例えば、ロールコート、リバースロー
ルコート、ナイフコート、グラビアコート、ロッドコー
ト等で行えば良い。或いは、シルクスクリーン印刷等の
印刷法でも良い。また、柱状基材側に設ける場合には、
スプレーコート等の塗工法でも良い。The adhesive layer may be formed in the form of a solution (or dispersion) in which the above resin is dissolved (or dispersed) in a solvent (or dispersion medium) such as water or an organic solvent, or a solvent-free liquid or hot liquid. Apply in the form of melt. The forming method is not particularly limited, and may be performed by a conventionally known coating method, for example, roll coating, reverse roll coating, knife coating, gravure coating, rod coating, or the like. Alternatively, a printing method such as silk screen printing may be used. Also, when provided on the columnar substrate side,
A coating method such as spray coating may be used.

【００４３】なお、転写シートの転写層を、剥離層以外
に例えば装飾層や接着剤層等も含めた複層から構成する
場合、層間密着力を向上させる為の易接着層等がそれら
層間に有しても良い事は、従来公知の転写シートと同様
である。When the transfer layer of the transfer sheet is composed of multiple layers including, for example, a decorative layer and an adhesive layer in addition to the release layer, an easy-adhesion layer for improving interlayer adhesion is provided between the layers. What may be included is the same as a conventionally known transfer sheet.

【００４４】〔転写〕転写は、もちろん複数の転写ロー
ラにより柱状基材の複数の側面に、順次、段階的に小面
積毎に転写して行く従来公知の所謂ラッピング転写法に
よれば良い（特公昭５９−５１９００号公報、特開平５
−３３００１３号公報、特公平３−２６６６号公報等参
照）。なお、図３の概念図でその一形態を例示するラッ
ピング転写法では、押圧ローラ（ラッピングローラ）１
１ａ〜１１ｄで転写シートを柱状基材Ｂの各側面に順次
加圧積層後、距離を隔てて、剥離ローラ１２ａ〜１２ｃ
で支持体シートを剥離する様に図示したが、例えば特に
熱融着で転写層を接着させる場合等では、支持体シート
の剥離は押圧ローラを剥離ローラとして圧開放直後に剥
離しても良い。また、剥離は手作業で行っても良い。[Transfer] Of course, the transfer may be performed by a conventionally known so-called lapping transfer method in which a plurality of transfer rollers sequentially and stepwisely transfer a plurality of side surfaces to a plurality of side surfaces of the columnar base material for each small area. JP-B-59-51900, JP-A-5-51900
-330013, JP-B-3-2666, etc.). In the lapping transfer method, an example of which is shown in the conceptual diagram of FIG. 3, a pressing roller (lapping roller) 1
In steps 1a to 11d, the transfer sheet is successively pressed and laminated on each side surface of the columnar base material B, and then separated from each other by peeling rollers 12a to 12c.
Although it is illustrated that the support sheet is peeled off, the support sheet may be peeled off immediately after pressure release by using a pressing roller as a peeling roller, particularly in a case where the transfer layer is bonded by, for example, thermal fusion. The peeling may be performed manually.

【００４５】図３に於いては、柱状基材Ｂを、複数の送
りローラ１４上に載置して、長手方向（矢印方向）に搬
送し、柱状基材の搬送速度に同調した速度で、転写シー
トＳを柱状基材に対して供給し、押圧ローラ１１ａ〜１
１ｄによって転写シートの柱状基材への積層を、柱状基
材の長手方向に略直交又は直交する方向に向かって、小
面積毎に段階的に行う。同図では柱状基材の転写すべき
各側面は、断面が折れ線形状となる様な面であり、各側
面は各々単一の平面を成すので、各側面毎にぞれぞれ専
用の円筒状の押圧ローラを用いる。従って、小面積毎の
積層は各側面単位で行われる。なお、押圧ローラ（或い
は剥離ローラも）は、柱状基材に対し図面手前側に設け
た分のみを図示簡略化の為に表示してある。そして、転
写シート積層後、同図では、剥離ローラ１２ａ〜１２ｃ
によって、転写シートＳの支持体シート１のみを剥離す
れば、化粧材等の転写製品Ｐが得られる。In FIG. 3, the columnar base material B is placed on a plurality of feed rollers 14 and transported in the longitudinal direction (the direction of the arrow), at a speed synchronized with the transport speed of the columnar substrate. The transfer sheet S is supplied to the columnar base material, and the pressing rollers 11a to 1
In step 1d, the transfer sheet is laminated on the columnar base material in a stepwise manner for each small area in a direction substantially perpendicular to or perpendicular to the longitudinal direction of the columnar substrate. In the figure, each side surface of the columnar substrate to be transferred is a surface having a polygonal cross section, and each side surface forms a single plane, so that each side surface has a dedicated cylindrical shape. Is used. Therefore, lamination for each small area is performed for each side surface. In addition, for the pressing roller (or the peeling roller), only the portion provided on the front side of the drawing with respect to the columnar base material is shown for simplification of the drawing. Then, after the transfer sheets are laminated, in the same figure, the release rollers 12a to 12c
Thus, if only the support sheet 1 of the transfer sheet S is peeled off, a transfer product P such as a decorative material is obtained.

【００４６】なお、同図では、転写時に転写シートに接
着剤層を形成する場合は、その接着剤層中の溶剤分の乾
燥や接着力の活性化、或いは転写シートの予熱を、熱風
等を使用した乾燥装置或いは加熱装置１３ａで、押圧ロ
ーラに供給直前に出来る様にしてある。また、同様に、
柱状基材Ｂについても転写時に柱状基材に接着剤層を形
成する場合は、その接着剤層中の溶剤分の乾燥や接着力
の活性化、或いは柱状基材の予熱を、上記同様な乾燥装
置或いは加熱装置１３で、押圧ローラに供給直前に出来
る様にしてある。In the same figure, when an adhesive layer is formed on the transfer sheet at the time of transfer, drying of the solvent in the adhesive layer, activation of the adhesive force, or preheating of the transfer sheet is performed by hot air or the like. The drying device or the heating device 13a used can perform the process immediately before the supply to the pressing roller. Similarly,
When an adhesive layer is formed on the columnar base material at the time of transfer also for the columnar base material B, drying of the solvent in the adhesive layer, activation of the adhesive force, or preheating of the columnar base material is performed in the same manner as described above. An apparatus or a heating device 13 is provided so that it can be made immediately before supply to the pressing roller.

【００４７】〔後加工：凹凸模様の凹部への着色インキ
の付与〕転写された転写層の凹凸模様４Ａの凹部には、
更に着色インキを充填して、固化させても良い。その結
果、凹部のみが他と区別されて着色した装飾模様が得ら
れる。特に木目導管等とする凹部に着色インキを充填し
固化させれば、化粧材等の転写製品に対して、より意匠
感に富んだ木目導管等を表現できる。[Post-Processing: Applying Colored Ink to Depressions of Concavo-convex Pattern] In the concave portions of the concavo-convex pattern 4A of the transferred transfer layer,
Further, it may be solidified by filling with a coloring ink. As a result, a decorative pattern in which only the concave portions are distinguished from the others and colored is obtained. In particular, if a colored ink is filled into a concave portion serving as a wood grain conduit or the like and solidified, it is possible to express a wood grain conduit or the like which is more rich in design for a transfer product such as a decorative material.

【００４８】この為には、後加工として、従来公知のワ
イピング法を利用できる。ワイピング法では、例えばド
クターブレードコート法やナイフコート法等によって、
凹部を含む表面全面に着色インキを塗布した後、凹部以
外の表面から着色インキを除去する事により、凹部内部
のみに着色インキを充填する。充填後は、凹部内の着色
インキを固化する。固化は、溶剤等の揮発成分が有る場
合は乾燥し、揮発成分が無い無溶剤の場合は熱や紫外線
等の電離放射線による硬化反応により硬化し、またこれ
ら乾燥及び硬化の両方により行う。なお、充填は凹部内
の全部でなくても良い。また、着色インキとしては、ビ
ヒクルのバインダーとしてアクリル樹脂、塩化ビニル−
酢酸ビニル共重合体、セルロース系樹脂等の熱可塑性樹
脂、２液硬化型ウレタン樹脂、エポキシ樹脂等の熱硬化
性樹脂、不飽和アクリレート系、エポキシ系等の電離放
射線硬化型樹脂等の従来公知の樹脂を用い、これに着色
剤としてキナクリドン、イソインドリノン等の有機顔
料、カーボンブラック、弁柄等の無機顔料、二酸化チタ
ン被覆雲母箔粉等の光輝性顔料等を配合し、さらに必要
に応じてその他添加剤を配合したインキ、或いはエマル
ション型の水系インキ等を使用する。凹部が木目導管溝
の場合、一般には黒褐色、茶褐色系の色のインキを用い
る。For this purpose, a conventionally known wiping method can be used as the post-processing. In the wiping method, for example, by a doctor blade coating method or a knife coating method,
After the colored ink is applied to the entire surface including the concave portion, the colored ink is removed from the surface other than the concave portion, so that only the inside of the concave portion is filled with the colored ink. After filling, the colored ink in the recess is solidified. The solidification is performed by drying when there is a volatile component such as a solvent, and by using a non-solvent having no volatile component, the resin is cured by a curing reaction using ionizing radiation such as heat or ultraviolet rays, and is performed by both drying and curing. Note that the filling does not have to be performed in the entire recess. In addition, as a coloring ink, acrylic resin, vinyl chloride-
Conventionally known thermoplastic resins such as vinyl acetate copolymers, cellulosic resins and the like, two-component curable urethane resins, thermosetting resins such as epoxy resins, unsaturated acrylate resins, ionizing radiation-curable resins such as epoxy resins, etc. Using a resin, a coloring agent such as quinacridone, an organic pigment such as isoindolinone, carbon black, an inorganic pigment such as a red iron oxide, a glittering pigment such as titanium dioxide-coated mica foil powder, and the like. An ink containing other additives or an emulsion-type water-based ink is used. In the case where the concave portion is a grain conduit groove, generally, a black-brown or brown-colored ink is used.

【００４９】〔後加工：上塗り層の形成〕転写後の転写
層の表面に、耐久性、塗装感等の意匠感等を付与する為
に、更に上塗り層を塗装する等しても良い。この様な上
塗り層としては、ポリ４フッ化エチレン、ポリフッ化ビ
ニリデン等のフッ素樹脂、アクリル樹脂等の熱可塑性樹
脂、アクリル樹脂、シリコーン樹脂、ウレタン樹脂等の
熱、湿気、紫外線等で硬化する硬化性樹脂の１種又は２
種以上の樹脂をバインダーとし、これに必要に応じて、
ベンゾトリアゾール、超微粒子酸化セリウム等の紫外線
吸収剤、ヒンダードアミン系ラジカル捕捉剤等の光安定
剤、着色顔料、シリカ、球状α−アルミナ等の微粒子か
らなる減摩剤、体質顔料、滑剤等を添加した塗料を用い
る。塗工はスプレー塗装、フローコート等の公知の塗工
法で行う。上塗り層の厚さは１〜１００μｍ程度であ
る。通常は転写層表面に賦形された凹凸模様が埋没しな
い程度の厚さ（例えば１０μｍ程度）とするが、凹凸模
様が埋没しても、転写層の最外層としての剥離層が、光
輝性顔料等を含有したり上塗り層とに屈折率差があり、
光反射性であれば、それらによる内部反射を利用して、
凹凸模様を視覚的に浮き立たせる事もできる。[Post-Processing: Formation of Overcoat Layer] In order to impart a design feeling such as durability and a painted feeling to the surface of the transfer layer after the transfer, an overcoat layer may be further applied. As such an overcoating layer, curing such as fluorine resin such as polytetrafluoroethylene and polyvinylidene fluoride, thermoplastic resin such as acrylic resin, acrylic resin, silicone resin, urethane resin and the like, which is cured by heat, moisture, ultraviolet ray, or the like. One or two of the conductive resins
More than one kind of resin as a binder, if necessary,
UV absorbers such as benzotriazole and ultrafine cerium oxide, light stabilizers such as hindered amine radical scavengers, coloring pigments, lubricating agents consisting of fine particles such as silica and spherical α-alumina, extender pigments, lubricants, etc. were added. Use paint. Coating is performed by a known coating method such as spray coating or flow coating. The thickness of the overcoat layer is about 1 to 100 μm. Usually, the thickness is such that the uneven pattern formed on the surface of the transfer layer is not buried (for example, about 10 μm). However, even if the uneven pattern is buried, the release layer as the outermost layer of the transfer layer has a glittering pigment. Etc. or there is a refractive index difference with the overcoat layer,
If it is light reflective, use the internal reflection by them,
The uneven pattern can also be visually raised.

【００５０】〔木質化粧材の用途〕本発明で得られる転
写製品の用途は特に制限は無い。例えば、化粧材とし
て、窓枠、扉枠、扉、手摺、敷居、鴨居等の建具、壁
面、天井、床等の建築物の内装材、サイディング等の外
壁、塀、屋根、門扉、破風板等の外装材、箪笥等の家
具、或いはテレビ受像機等の弱電・ＯＡ機器のキャビネ
ットの表面化粧材、自動車、電車、航空機、船舶等の乗
物内装材、物入れ等の容器等として用いる。[Use of wood decorative material] The use of the transfer product obtained by the present invention is not particularly limited. For example, as decorative materials, window frames, door frames, doors, handrails, thresholds, doors and other fittings, wall materials, ceilings, flooring and other building interior materials, siding and other exterior walls, fences, roofs, gates, gable boards, etc. Exterior materials, furniture such as a chest of drawers, surface decoration materials for cabinets of light electric / OA equipment such as television receivers, interior materials for vehicles such as automobiles, trains, aircraft, and ships, containers for storage, and the like.

【００５１】[0051]

【実施例】以下、本発明を実施例によって、更に具体的
に説明する。EXAMPLES The present invention will be described more specifically with reference to the following examples.

【００５２】〔支持体シート〕先ず、厚さ３８μｍの２
軸延伸ポリエチレンテレフタレートフィルムからなる基
材シートの片面に、木目導管溝形状の突起で、それぞれ
の高さが１０〜７０μｍの範囲で分布する凹凸模様を次
の様にして形成して、支持体シートとした。[Support Sheet] First, a sheet of 38 μm thick 2
A support sheet is formed on one side of a base sheet made of an axially stretched polyethylene terephthalate film, with a wood-grain conduit groove-shaped projection having an uneven pattern in which the respective heights are distributed in a range of 10 to 70 μm as follows. And

【００５３】図４の如き装置を用い、ロール凹版として
は鉄芯の周囲を被覆した銅層に上記凹凸模様とは逆凹凸
形状の凹部をエッチングで形成した版胴を用い、電離放
射線硬化性樹脂には３官能ウレタンアクリレート系のプ
レポリマーとジペンタエリスリトールヘキサアクリレー
トとの混合物からなる紫外線硬化性樹脂の未硬化液状組
成物を用い、基材シート送り速度２０ｍ／分で、電離放
射線照射装置として水銀灯を用いて、出力１６０ｗ／ｃ
ｍの条件で紫外線を照射して電離放射線硬化性樹脂を架
橋、硬化させて、基材シートに凹凸模様を賦形した支持
体シートを得た。Using an apparatus as shown in FIG. 4, a roll cylinder is used as a roll intaglio, a plate cylinder in which a concave portion having a concave and convex shape reverse to the above concave and convex pattern is formed on a copper layer covering the periphery of an iron core by etching. An uncured liquid composition of a UV-curable resin composed of a mixture of a trifunctional urethane acrylate prepolymer and dipentaerythritol hexaacrylate is used at a substrate sheet feed speed of 20 m / min and a mercury lamp as an ionizing radiation irradiation device. And the output is 160 w / c
UV irradiation was performed under the conditions of m to crosslink and cure the ionizing radiation-curable resin, thereby obtaining a support sheet having a substrate sheet with a concavo-convex pattern.

【００５４】〔転写層：剥離層、装飾層、接着剤層〕上
記支持体シートの凹凸模様側の面に、エチレン−プロピ
レン−ブテン共重合体（プロピレン９０重量％）からな
るオレフィン系熱可塑性エラストマーに、エルカ酸アミ
ド（滑剤）を５００ｐｐｍ、ベンゾトリアゾール系紫外
線吸収剤を８，０００ｐｐｍ、ヒンダードアミン系ラジ
カル捕捉剤を４，０００ｐｐｍ添加したものを、Ｔダイ
から溶融押出しして、支持体シートの凹凸模様が完全に
埋められる様な厚さ８０μｍの剥離層を塗工形成した。
更に剥離層の表面にコロナ放電処理を施した上で、バイ
ンダーはアクリルポリオールとヘキサメチレンジイソシ
アネートとからなる２液硬化型ウレタン樹脂で、着色顔
料はカーボンブラック、キナクリドン、イソインドリノ
ン及びフタロシアニンブルーからなる着色インキで、オ
ーク柄の木目模様の装飾層をグラビア印刷で形成した。
更に、装飾層の上に接着剤層として、ダイマー酸とエチ
レンジアミンとの縮合物からなるポリアミド２８重量
部、酸化チタン２１．５重量部、キシレン３２重量部、
イソブタノール１８重量部、マイクロシリカ０．５重量
部からなる塗工液をロールコートで塗布後、１４０℃で
２０秒間乾燥して指触乾燥し、塗布量３０ｇ／ｍ² （固
形分基準）の接着剤層を塗工形成し巻き取って、図１
（Ａ）に示す様な、基材シート３に凹凸模様４を有する
支持体シート１上に、転写層２として剥離層５、装飾層
６及び接着剤層７をこの順に有する転写シートＳを得
た。[Transfer Layer: Release Layer, Decorative Layer, Adhesive Layer] An olefin-based thermoplastic elastomer composed of an ethylene-propylene-butene copolymer (propylene 90% by weight) is formed on the surface of the support sheet on the side of the uneven pattern. Of erucamide (lubricant), 8,000 ppm of a benzotriazole-based UV absorber and 4,000 ppm of a hindered amine radical scavenger were melt-extruded from a T-die to obtain a concave-convex pattern on a support sheet. Was formed by coating to form a release layer having a thickness of 80 μm so as to completely fill the layer.
Further, after performing a corona discharge treatment on the surface of the release layer, the binder is a two-part curable urethane resin composed of acrylic polyol and hexamethylene diisocyanate, and the coloring pigment is composed of carbon black, quinacridone, isoindolinone and phthalocyanine blue. An oak wood grain decorative layer was formed by gravure printing with a colored ink.
Further, as an adhesive layer on the decorative layer, 28 parts by weight of a polyamide made of a condensate of dimer acid and ethylenediamine, 21.5 parts by weight of titanium oxide, 32 parts by weight of xylene,
A coating solution consisting of 18 parts by weight of isobutanol and 0.5 part by weight of microsilica was applied by roll coating, dried at 140 ° C. for 20 seconds, and touch-dried to obtain a coating amount of 30 g / m ² (solid content basis). The adhesive layer is applied and formed and wound up.
As shown in (A), a transfer sheet S having a release layer 5, a decorative layer 6, and an adhesive layer 7 as a transfer layer 2 in this order on a support sheet 1 having an uneven pattern 4 on a base sheet 3 is obtained. Was.

【００５５】次に、図３に示す様な装置で、上記転写シ
ートＳを用いて、ＭＤＦからなる柱状基材Ｂに対して、
送り速度８ｍ／分で、鉄芯の表面をシリコーンゴムで被
覆した表面温度１７０℃の押圧ローラ１１ａ〜１１ｄで
押圧して積層後、剥離ローラ１２ａ〜１２ｃで支持体シ
ートのみを剥離して、転写製品Ｐとして木質系の化粧材
を得た。その結果、化粧材には、装飾層による木目柄の
みならず、木質意匠に特徴的な導管溝の凹凸模様も転写
により賦形されており、リアルで高意匠であった。Next, using the transfer sheet S described above, a columnar base material B made of MDF is applied to an apparatus as shown in FIG.
At a feeding speed of 8 m / min, the surface of the iron core is coated with silicone rubber and pressed by pressing rollers 11a to 11d at a surface temperature of 170 ° C., and after laminating, only the support sheet is peeled off by peeling rollers 12a to 12c and transferred. A wood-based decorative material was obtained as product P. As a result, in the decorative material, not only the grain pattern by the decorative layer but also the irregular pattern of the conduit groove characteristic of the woody design were formed by transfer, and the design was realistic and high in design.

【００５６】〔実施例２〕実施例１に於いて、転写シー
トには予め接着剤層は形成していないシートを用いて、
転写シートの転写時に転写シートに塗工形成し、乾燥装
置１３ａで溶剤を必要量乾燥後、残っている溶剤により
接着剤層が粘着性を有している状態で、インラインで転
写した。その結果、実施例１同様に、木目柄及び転写で
賦形された導管溝の凹凸模様により、リアルで高意匠な
木質系の化粧材が得られた。Example 2 In Example 1, a transfer sheet was used in which an adhesive layer was not formed beforehand.
When the transfer sheet was transferred, the transfer sheet was coated and formed, and a required amount of solvent was dried by a drying device 13a. Then, the transfer was performed in-line with the remaining solvent having a tacky adhesive layer. As a result, similarly to Example 1, a woody decorative material having a realistic and high design was obtained by the wood grain pattern and the concave and convex pattern of the conduit groove formed by transfer.

【００５７】〔実施例３〕厚さ５０μｍの２軸延伸ポリ
エチレンテレフタレートフィルムからなる基材シートの
片面に、木目導管溝形状の突起で、それぞれの高さが１
０〜７０μｍの範囲で分布する凹凸模様を実施例１同様
の加工方法で形成して、支持体シートとした。なお、凹
凸模様を形成する為の電離放射線硬化性樹脂には、シリ
コーンアクリレートを主体とする紫外線硬化性樹脂を用
いた。そして、得られた支持体シートの凹凸模様側の面
に、アクリルポリオールとヘキサメチレンジイソシアネ
ートとからなる透明な２液硬化型ウレタン樹脂を、ロー
ルコート法で塗布し指触乾燥させて厚さ８０μｍ（固形
分基準）の剥離層を塗工形成して、シートを一旦巻き取
った。次に、更に剥離層塗工面に、バインダーはアクリ
ル樹脂とウレタン樹脂との７対３重量比の混合樹脂で、
着色顔料はカーボンブラック、キナクリドン、イソイン
ドリノン及びフタロシアニンブルーからなる着色インキ
で、オーク柄の木目模様の絵柄層とベタ柄の隠蔽層とか
らなる装飾層をグラビア印刷で形成して、基材シートに
凹凸模様を有する支持体シート上に、転写層として剥離
層、装飾層（絵柄層と隠蔽層）をこの順に有する転写シ
ートを得た。Example 3 One side of a base sheet made of a biaxially stretched polyethylene terephthalate film having a thickness of 50 μm was provided with wood-grain conduit-shaped protrusions each having a height of 1 mm.
Concavo-convex patterns distributed in the range of 0 to 70 μm were formed by the same processing method as in Example 1 to obtain a support sheet. In addition, as the ionizing radiation curable resin for forming the concavo-convex pattern, an ultraviolet curable resin mainly composed of silicone acrylate was used. Then, a transparent two-component curable urethane resin composed of acrylic polyol and hexamethylene diisocyanate is applied by a roll coating method on the surface of the obtained support sheet on the side of the concavo-convex pattern by a roll coating method and dried by touch to a thickness of 80 μm ( A release layer (solid basis) was formed by coating, and the sheet was once wound up. Next, on the coating surface of the release layer, a binder is a mixed resin of an acrylic resin and a urethane resin in a weight ratio of 7: 3,
The coloring pigment is a coloring ink composed of carbon black, quinacridone, isoindolinone and phthalocyanine blue. A transfer sheet having a release layer and a decorative layer (a pattern layer and a concealing layer) as a transfer layer in this order on a support sheet having an uneven pattern was obtained.

【００５８】そして、上記転写シートを使用し、柱状基
材には棒状に加工したＭＤＦを使用して、図３の如き装
置のラッピング機にて実施例２と同様にしてラッピング
転写を行った。転写シートには、２液硬化型ウレタン樹
脂を転写シートにインラインで塗布して乾燥装置で溶剤
を必要量乾燥後、残っている溶剤により接着剤層が粘着
性を有している状態で、押圧ローラにて転写シートを柱
状基材に圧着させてラミネートした後、剥離ローラで支
持体シートのみを剥離して、転写製品Ｐとして化粧扉枠
材となる木質系の化粧材を得た。その結果、化粧材に
は、装飾層による木目柄のみならず、木質意匠に特徴的
な導管溝の凹凸模様も転写により賦形されており、リア
ルで高意匠であった。Using the above-mentioned transfer sheet, and using MDF processed into a rod as a columnar substrate, lapping transfer was carried out in the same manner as in Example 2 using a wrapping machine of an apparatus as shown in FIG. The transfer sheet is coated with a two-component curable urethane resin in-line and dried with a drying device to dry the required amount of solvent. After the transfer sheet was pressed against the columnar substrate with a roller and laminated, the support sheet was peeled off with a peeling roller to obtain a wood-based decorative material serving as a decorative door frame material as a transfer product P. As a result, in the decorative material, not only the grain pattern by the decorative layer but also the irregular pattern of the conduit groove characteristic of the woody design were formed by transfer, and the design was realistic and high in design.

【００５９】[0059]

【発明の効果】本発明のラッピング転写法によれば、
凹凸模様は、既に転写シート内部で賦形された剥離層等
の転写層を転写する事で賦形する為、シャープな形状の
凹凸模様を賦形できる。凹凸模様賦形済の化粧シートを
ラミネ−トする方法では、その基材シートとなる熱可塑
性樹脂シートがラミネ−ト時の熱圧で変形し、凹凸模様
が浅くなったり、一部消失する現象が起き易かったが、
本発明では転写による為、転写シートに於ける凹凸模様
をそのまま忠実に賦形出来、ラミネ−トでは不可能なシ
ャープな凹凸模様を賦形できる。しかも、転写シートに
て形成しておく凹凸模様は、熱圧による機械的エンボス
では無く、前述特定の方法によって賦形型を用いて電離
放射線硬化性樹脂の硬化物として形成するので、機械的
エンボスでは不可能なシャープな形状の凹凸模様を、転
写製品に賦形できる。 しかも、柱状基材が例えば金属等の硬質材料で凹凸模
様をエンボスで賦形出来ない物であっても、転写する転
写層の厚み次第でシャープで且つまた深い凹凸模様も賦
形できる。従って、化粧材等の転写製品は高意匠にでき
る。例えば、リアルな導管溝表現等が可能である。 また、凹凸模様は、化粧シートのラミネ−トでは無く
転写によって賦形するので、使用した転写シートの支持
体シートは剥離後、回収再利用も出来、省資源的であ
る。According to the wrapping transfer method of the present invention,
Since the concavo-convex pattern is formed by transferring a transfer layer such as a release layer already formed in the transfer sheet, a sharp concavo-convex pattern can be formed. In the method of laminating a decorative sheet on which an embossed pattern has been formed, the thermoplastic resin sheet serving as the base sheet is deformed by the heat pressure at the time of laminating, and the embossed pattern becomes shallow or partially disappears. Was easy to happen,
In the present invention, since the transfer is performed by transfer, the uneven pattern on the transfer sheet can be faithfully formed as it is, and a sharp uneven pattern which cannot be formed by lamination can be formed. In addition, the uneven pattern formed on the transfer sheet is not mechanically embossed by heat and pressure, but is formed as a cured product of the ionizing radiation-curable resin using a shaping mold by the above-described specific method. It is possible to form a sharp pattern on the transfer product, which is impossible with conventional methods. In addition, even if the columnar substrate is a hard material such as a metal and the like, the uneven pattern cannot be formed by embossing, a sharp and deep uneven pattern can be formed depending on the thickness of the transfer layer to be transferred. Therefore, a transfer product such as a cosmetic material can be designed with a high design. For example, a realistic conduit groove expression or the like is possible. In addition, since the uneven pattern is formed not by laminating the decorative sheet but by transfer, the support sheet of the used transfer sheet can be recovered and reused after peeling, thereby saving resources.

【図面の簡単な説明】[Brief description of the drawings]

【図１】本発明のラッピング転写法での凹凸模様の賦形
方法を、その一形態で概念的に説明する説明図。FIG. 1 is an explanatory diagram conceptually illustrating a method of forming a concavo-convex pattern by a lapping transfer method of the present invention in one form thereof.

【図２】本発明で用いる転写シートで、支持体シートが
有する凹凸模様を説明する断面図。FIG. 2 is a cross-sectional view illustrating a concavo-convex pattern of a support sheet in the transfer sheet used in the present invention.

【図３】本発明のラッピング転写法を、その一形態で概
念的に説明する概念図（斜視図）。FIG. 3 is a conceptual diagram (perspective view) conceptually illustrating the lapping transfer method of the present invention in one form.

【図４】転写シートの支持体シートに凹凸模様を賦形す
る方法を説明する概念図。FIG. 4 is a conceptual diagram illustrating a method of forming a concavo-convex pattern on a support sheet of a transfer sheet.

【符号の説明】[Explanation of symbols]

１ 支持体シート ２ 転写層 ３ 基材シート ４ 凹凸模様 ４Ａ 凹凸模様（転写製品側） ４ａ 凹凸模様の凸部 ４ｂ 凹凸模様の凹部底面となる樹脂層 ５ 剥離層 ６ 装飾層 ７ 接着剤層 １１、１１ａ〜１１ｄ 押圧ローラ １２、１２ａ〜１２ｃ 剥離ローラ １３ａ、１３ｂ 加熱装置、乾燥装置 １４ 送りローラ ４０ 凹凸形状 ５０ ロール凹版 ６０ 軸芯 ７０ 液状組成物 ８０ 電離放射線照射装置 ９０ 圧着ローラ １００ 剥離ローラ ２００ 塗液供給装置 Ｂ 柱状基材 Ｐ 転写製品（化粧材等） Ｓ 転写シート DESCRIPTION OF SYMBOLS 1 Support sheet 2 Transfer layer 3 Substrate sheet 4 Concavo-convex pattern 4A Concavo-convex pattern (transfer product side) 4a Convex part of concavo-convex pattern 4b Resin layer used as the bottom of concave part of concavo-convex pattern 5 Release layer 6 Decorative layer 7 Adhesive layer 11, 11a-11d Pressing Roller 12, 12a-12c Peeling Roller 13a, 13b Heating Device, Drying Device 14 Feed Roller 40 Roughness Shape 50 Roll Intaglio 60 Shaft Core 70 Liquid Composition 80 Ionizing Radiation Irradiation Device 90 Pressure Roller 100 Peeling Roller 200 Coating Liquid Supply device B Column-shaped base material P Transfer product (cosmetic material etc.) S Transfer sheet

Claims (1)

【特許請求の範囲】[Claims] 【請求項１】 支持体シートと転写層とからなる転写シ
ートを用いて、柱状基材に転写層を転写するラッピング
転写法において、 液状の電離放射線硬化性樹脂をロール凹版の少なくとも
凹部に充填させると共に該樹脂に基材シートを接触させ
該樹脂が基材シートとロール凹版との間に保持されてい
る状態で電離放射線を照射して該樹脂を硬化させて凹凸
模様とした該凹凸模様と該基材シートとからなる支持体
シートの、該凹凸模様を有する面に、少なくとも剥離層
からなる転写層を形成した転写シートを用意し、 次いで、上記転写シートを柱状基材の複数の側面に順次
ローラで加圧して積層後、支持体シートを剥離する事
で、転写後の最外層として剥離層を有する転写層を転写
し、転写層に前記凹凸模様を賦形する、ラッピング転写
法。In a lapping transfer method for transferring a transfer layer to a columnar substrate using a transfer sheet comprising a support sheet and a transfer layer, a liquid ionizing radiation-curable resin is filled into at least a concave portion of a roll intaglio. The concave-convex pattern and the concave-convex pattern formed by curing the resin by irradiating ionizing radiation while the resin is held between the substrate sheet and the roll intaglio while contacting the substrate sheet with the resin. A transfer sheet having a transfer layer formed of at least a release layer is prepared on the surface having the uneven pattern of the support sheet formed of the base sheet, and then the transfer sheet is sequentially formed on a plurality of side surfaces of the columnar base material. A lapping transfer method in which a transfer layer having a release layer as an outermost layer after transfer is transferred by laminating the support sheet after pressing and laminating with a roller, and the concavo-convex pattern is formed on the transfer layer.