JPH11306860A - Paste composition for internal electrode of multilayer ceramic capacitor - Google Patents
Paste composition for internal electrode of multilayer ceramic capacitorInfo
- Publication number
- JPH11306860A JPH11306860A JP12177398A JP12177398A JPH11306860A JP H11306860 A JPH11306860 A JP H11306860A JP 12177398 A JP12177398 A JP 12177398A JP 12177398 A JP12177398 A JP 12177398A JP H11306860 A JPH11306860 A JP H11306860A
- Authority
- JP
- Japan
- Prior art keywords
- internal electrode
- weight
- multilayer ceramic
- organic solvent
- ceramic capacitor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、積層セラミックコ
ンデンサの製造に適用される積層セラミックコンデンサ
内部電極用ペースト（以後、内部電極用ペーストと略称
する）組成物に係り、特に、その乾燥性が改善されて積
層セラミックコンデンサにおける生産性の向上が図れる
内部電極用ペースト組成物の改良に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a paste for internal electrodes of a multilayer ceramic capacitor (hereinafter referred to as "paste for internal electrodes") applied to the production of a multilayer ceramic capacitor, and more particularly to an improvement in the drying property. The present invention relates to an improvement of a paste composition for an internal electrode which can improve productivity of a multilayer ceramic capacitor.
【０００２】[0002]
【従来の技術】この種の積層セラミックコンデンサ（Ｍ
ＬＣＣと称される）として、例えば、図１（Ａ）〜
（Ｂ）に示すような構造のものが知られている。すなわ
ち、このＭＬＣＣ（積層セラミックコンデンサ）ａは、
誘電体層ｂと内部電極が交互に複数積層されたコンデン
サ本体ｄと、このコンデンサ本体ｄの外側に設けられそ
の一方が奇数番目の内部電極c1群に接続され他方が偶数
番目の内部電極c2群に接続された一対の外部電極e1、e2
とでその主要部が構成されるものである。2. Description of the Related Art Multilayer ceramic capacitors of this type (M
LCC), for example, as shown in FIG.
A structure as shown in (B) is known. That is, this MLCC (multilayer ceramic capacitor) a
A capacitor body d in which a plurality of dielectric layers b and internal electrodes are alternately stacked; and a capacitor body d provided outside the capacitor body d, one of which is connected to the odd-numbered internal electrodes c1 group and the other is the even-numbered internal electrodes c2 group. A pair of external electrodes e1, e2 connected to
And constitute the main part.
【０００３】そして、このＭＬＣＣは、従来、以下のよ
うにして製造されている。まず、ポリビニルブチラール
等の有機バインダーが溶解された有機溶剤と、チタン酸
バリウム（ＢａＴｉＯ3 ）、鉛を含むペロブスカイト型
酸化物等の誘電体粉末とを混合し、この混合液をドクタ
ーブレード法により適宜支持体上に塗布してシート状成
型体（このシートは誘電体グリーンシートと称されてい
る）を形成する。[0003] The MLCC is conventionally manufactured as follows. First, an organic solvent in which an organic binder such as polyvinyl butyral is dissolved, and a dielectric powder such as barium titanate (BaTiO 3 ) or a perovskite oxide containing lead are mixed, and the mixed solution is appropriately mixed by a doctor blade method. It is applied on a support to form a sheet-like molded body (this sheet is called a dielectric green sheet).
【０００４】次に、この誘電体グリーンシート上に、Ｎ
ｉ、Ｃｕ等の卑金属粉末、有機バインダーおよび有機溶
剤を主成分とする内部電極用ペーストをスクリーン印刷
法により印刷して電極層を形成し、かつ、乾燥させる。Next, on this dielectric green sheet, N
An internal electrode paste mainly composed of a base metal powder such as i or Cu, an organic binder and an organic solvent is printed by a screen printing method to form an electrode layer, and then dried.
【０００５】次に、内部電極用ペーストから成る電極層
が形成された誘電体グリーンシートを所定枚数重ね合わ
せると共に、これ等を熱圧着させて電極層と誘電体グリ
ーンシートから成る積層体を形成する。[0005] Next, a predetermined number of dielectric green sheets on which an electrode layer made of an internal electrode paste is formed are laminated, and these are thermally pressed to form a laminate composed of the electrode layers and the dielectric green sheets. .
【０００６】次に、この積層体を所定寸法に切断すると
共に、電気炉内に搬入し酸化性雰囲気中において脱バイ
ンダー処理を行い、引き続き還元性雰囲気中において焼
結を行う。Next, the laminate is cut into a predetermined size, carried into an electric furnace, subjected to a binder removal treatment in an oxidizing atmosphere, and subsequently sintered in a reducing atmosphere.
【０００７】次いで、この様な処理が施された積層体
（コンデンサ本体）の両端を研磨し、その一端側では奇
数番目の内部電極群の端面をまた他端側では偶数番目の
内部電極群の端面をそれぞれ露出させた後、その研磨さ
れた両端面に外部電極用ペーストを塗布しかつ乾燥させ
る。そして、電気炉内に搬入させて外部電極の焼結を行
い、かつ、外部電極表面に半田付け性を向上させるため
のニッケルメッキ、錫メッキを施して上記積層セラミッ
クコンデンサ（ＭＬＣＣ）が完成される。Next, both ends of the laminated body (capacitor body) thus treated are polished, and the end face of the odd-numbered internal electrode group is formed on one end and the even-numbered internal electrode group is formed on the other end. After exposing the end faces, the external electrode paste is applied to the polished end faces and dried. Then, the multi-layer ceramic capacitor (MLCC) is completed by carrying it into an electric furnace and sintering the external electrodes, and performing nickel plating and tin plating on the surface of the external electrodes to improve solderability. .
【０００８】ところで、上記誘電体グリーンシート上に
塗布される内部電極用ペーストは、有機溶剤に有機バイ
ンダーを溶解させて調製した有機ビヒクル中にＮｉ、Ｃ
ｕ等の卑金属粉末を配合し、３本ロールミル等により混
練すると共に混合分散し、かつ、粘度調整用に希釈剤と
称される有機溶剤が必要に応じ配合されて成るものであ
る。上記有機ビヒクル中の有機溶剤には、テルピネオー
ル、メチルエチルケトン、ブチルカルビトールアセテー
ト等が用いられ、また、有機バインダーには、エチルセ
ルロース、ニトロセルロース等のセルロース系樹脂や、
メチルメタクレート等のアクリル樹脂が使用される。ま
た、粘度調整用に配合される上記希釈剤としては芳香族
炭化水素や脂肪族炭化水素等が使用される。The paste for internal electrodes applied on the dielectric green sheet is prepared by dissolving Ni, C in an organic vehicle prepared by dissolving an organic binder in an organic solvent.
A base metal powder such as u is kneaded and kneaded by a three-roll mill or the like, mixed and dispersed, and an organic solvent called a diluent is added as needed for viscosity adjustment. As the organic solvent in the organic vehicle, terpineol, methyl ethyl ketone, butyl carbitol acetate and the like are used, and, as the organic binder, ethyl cellulose, cellulose resins such as nitrocellulose,
An acrylic resin such as methyl methacrylate is used. In addition, as the diluent to be blended for adjusting the viscosity, an aromatic hydrocarbon, an aliphatic hydrocarbon, or the like is used.
【０００９】そして、代表的な内部電極用ペーストとし
て、エチルセルロースをテルピネオールに溶解した有機
ビヒクル中にＮｉ粉末を混合分散させたものに、回転粘
度計において１００ｒｐｍでの粘度が５〜６０パスカル
・秒（Ｐａ・ｓ）となるようにトリエチルベンゼン等の
希釈剤を加えて粘度調整したペーストが広く利用されて
いる。A typical internal electrode paste is prepared by mixing and dispersing Ni powder in an organic vehicle in which ethyl cellulose is dissolved in terpineol, and having a viscosity at 100 rpm of 5 to 60 Pascal · s (rotational viscometer). Pastes whose viscosity is adjusted by adding a diluent such as triethylbenzene so as to obtain Pa · s) are widely used.
【００１０】[0010]
【発明が解決しようとする課題】ところで、従来、広く
利用されているＮｉ粉末、エチルセルロースおよびテル
ピネオールを主成分とした上述の内部電極用ペーストは
その乾燥性に劣る欠点を有しており、誘電体グリーンシ
ート上に印刷形成された電極層の乾燥工程に長時間を要
してしまい、積層セラミックコンデンサにおける生産性
の向上を図る上において障害となる問題点を有してい
た。However, the above-mentioned pastes for internal electrodes, which are mainly composed of Ni powder, ethylcellulose and terpineol, which have been widely used in the past, have the disadvantage that their drying properties are inferior. The drying process of the electrode layer printed and formed on the green sheet requires a long time, which has been a problem in improving productivity of the multilayer ceramic capacitor.
【００１１】この場合、内部電極用ペーストの溶剤成分
として乾燥速度の速い、例えばブチルセロソルブ等の有
機溶剤を適用する方法が考えられる。しかし、この様な
速乾性の有機溶剤が適用された場合、有機ビヒクル中に
金属粉末を配合して内部電極用ペーストを調製する際、
溶剤成分の速乾性に起因して調製途中において調製組成
物の粘度が増大してしまい、目的の内部電極用ペースト
が得られなくなる別の弊害を生ずる問題点を有してい
る。In this case, a method of applying an organic solvent having a high drying rate, for example, butyl cellosolve, as a solvent component of the internal electrode paste is considered. However, when such a quick-drying organic solvent is applied, when preparing a paste for an internal electrode by mixing a metal powder in an organic vehicle,
There is a problem in that the viscosity of the prepared composition increases during the preparation due to the quick drying property of the solvent component, so that a desired internal electrode paste cannot be obtained.
【００１２】本発明はこの様な問題点に着目してなされ
たもので、その課題とするところは、乾燥性が改善され
て積層セラミックコンデンサにおける生産性の向上が図
れる内部電極用ペースト組成物を提供することにある。The present invention has been made in view of such problems, and an object of the present invention is to provide a paste composition for an internal electrode capable of improving the drying property and improving the productivity of a multilayer ceramic capacitor. To provide.
【００１３】[0013]
【課題を解決するための手段】すなわち、請求項１に係
る発明は、誘電体層と内部電極とが交互に複数積層され
たコンデンサ本体と、このコンデンサ本体の外側に設け
られ上記内部電極群に接続される一対の外部電極とを備
える積層セラミックコンデンサの製造に適用されると共
に、金属粉末、有機バインダーおよび有機溶剤を主成分
とする積層セラミックコンデンサ内部電極用ペースト組
成物を前提とし、上記有機溶剤がジプロピレングリコー
ルモノメチルエーテルを含有し、かつ、上記金属粉末、
有機バインダーおよび有機溶剤の総量に対するジプロピ
レングリコールモノメチルエーテルの配合割合が５〜６
５重量％の範囲に設定されていることを特徴とし、ま
た、請求項２に係る発明は、請求項１記載の発明に係る
積層セラミックコンデンサ内部電極用ペースト組成物を
前提とし、上記金属粉末、有機バインダーおよび有機溶
剤の総量に対する金属粉末の配合割合が２７重量％〜８
５重量％、また、上記総量に対する有機バインダーの配
合割合が１重量％〜８重量％の範囲にそれぞれ設定され
ていることを特徴とするものである。That is, the present invention according to claim 1 is directed to a capacitor body in which a plurality of dielectric layers and internal electrodes are alternately laminated, and the internal electrode group provided outside the capacitor body. Along with being applied to the production of a multilayer ceramic capacitor having a pair of external electrodes connected thereto, a paste composition for a multilayer ceramic capacitor internal electrode containing metal powder, an organic binder and an organic solvent as main components is premised, Contains dipropylene glycol monomethyl ether, and the metal powder,
The mixing ratio of dipropylene glycol monomethyl ether to the total amount of the organic binder and the organic solvent is 5 to 6
It is characterized in that it is set in the range of 5% by weight, and the invention according to claim 2 is based on the paste composition for an internal electrode of a multilayer ceramic capacitor according to the invention according to claim 1; The mixing ratio of the metal powder to the total amount of the organic binder and the organic solvent is 27% by weight to 8%.
5% by weight, and the mixing ratio of the organic binder to the total amount is set in the range of 1% by weight to 8% by weight, respectively.
【００１４】そして、請求項１および２記載の発明に係
る積層セラミックコンデンサ内部電極用ペースト組成物
によれば、金属粉末、有機バインダーおよび有機溶剤の
総量に対し５〜６５重量％の範囲で上記有機溶剤中にジ
プロピレングリコールモノメチルエーテルが含まれてい
るため、ペーストの調製途中において調製組成物の粘度
増大に伴う弊害を引起こすことなくその乾燥性の改善を
図ることが可能となる。According to the paste composition for an internal electrode of a multilayer ceramic capacitor according to the first and second aspects of the present invention, the organic compound is contained in the range of 5 to 65% by weight based on the total amount of metal powder, organic binder and organic solvent. Since dipropylene glycol monomethyl ether is contained in the solvent, it is possible to improve the drying property of the paste without causing any adverse effect due to an increase in the viscosity of the composition during the preparation of the paste.
【００１５】[0015]
【発明の実施の形態】以下、本発明の実施の形態につい
て説明する。Embodiments of the present invention will be described below.
【００１６】この実施の形態に係る内部電極用ペースト
組成物は、Ｎｉ、Ｃｕ等の金属粉末、エチルセルロース
等の有機バインダーおよび有機溶剤としてのジプロピレ
ングリコールモノメチルエーテルでその主成分が構成さ
れ、必要に応じてエチレングリコールモノブチルエーテ
ル等が配合されて成るものである。The paste composition for an internal electrode according to this embodiment is composed of a metal powder such as Ni and Cu, an organic binder such as ethyl cellulose, and dipropylene glycol monomethyl ether as an organic solvent. Accordingly, ethylene glycol monobutyl ether or the like is blended accordingly.
【００１７】また、この内部電極用ペースト組成物にお
いては、金属粉末、有機バインダーおよび有機溶剤の総
量に対する上記ジプロピレングリコールモノメチルエー
テルの配合割合が５〜６５重量％の範囲に設定されてい
る。この理由は、ジプロピレングリコールモノメチルエ
ーテルの配合割合が５重量％未満であると、他の有機溶
剤が併用された内部電極用ペーストの乾燥性が低下する
ことがあり、また、上記配合割合が６５重量％を越える
と内部電極用ペーストの粘度が低くなり誘電体グリーン
シート上への印刷が困難になる場合があるからである。In the paste composition for an internal electrode, the mixing ratio of the above-mentioned dipropylene glycol monomethyl ether to the total amount of the metal powder, the organic binder and the organic solvent is set in the range of 5 to 65% by weight. The reason for this is that if the blending ratio of dipropylene glycol monomethyl ether is less than 5% by weight, the drying properties of the internal electrode paste in which another organic solvent is used in combination may be reduced. If the content is more than 10% by weight, the viscosity of the internal electrode paste becomes low, and it may be difficult to print on the dielectric green sheet.
【００１８】また、ジプロピレングリコールモノメチル
エーテル等有機溶剤以外の残りの成分、つまり上記金属
粉末と有機バインダーの配合割合については以下の範囲
に設定することが望ましい。すなわち、金属粉末、有機
バインダーおよび有機溶剤の総量に対する金属粉末の配
合割合は２７重量％〜８５重量％、上記総量に対する有
機バインダーの配合割合は１重量％〜８重量％の範囲に
それぞれ設定されることが望ましい。The remaining components other than the organic solvent such as dipropylene glycol monomethyl ether, that is, the mixing ratio of the metal powder and the organic binder are desirably set in the following ranges. That is, the mixing ratio of the metal powder to the total amount of the metal powder, the organic binder, and the organic solvent is set to 27% by weight to 85% by weight, and the mixing ratio of the organic binder to the total amount is set to 1% by weight to 8% by weight. It is desirable.
【００１９】また、この内部電極用ペースト組成物にお
いて金属粉末、有機バインダー等については、一例とし
て挙げた上述のＮｉ、エチルセルロース等の材料以外
に、従来、適用されているその他の材料を適用すること
も可能である。更に、金属粉末、有機バインダーおよび
有機溶剤の総量に対し５〜６５重量％の範囲でジプロピ
レングリコールモノメチルエーテルが配合されているこ
とを条件に、従来、使用されているその他の有機溶剤を
併用して配合することも可能である。In the internal electrode paste composition, as for the metal powder, the organic binder and the like, in addition to the above-mentioned materials such as Ni and ethylcellulose, other materials which have been conventionally applied may be used. Is also possible. Further, provided that dipropylene glycol monomethyl ether is blended in a range of 5 to 65% by weight based on the total amount of the metal powder, the organic binder and the organic solvent, other conventionally used organic solvents are used in combination. It is also possible to mix them.
【００２０】[0020]
【実施例】以下、本発明の実施例について具体的に説明
する。Embodiments of the present invention will be specifically described below.
【００２１】［ビヒクルの調製］ ビヒクルａ：ビヒクル全体に対し８７重量％に相当する
量のジプロピレングリコールモノメチルエーテルをホッ
トプレート上にて６０℃まで加熱する。次に、この中
に、同じく１３重量％に相当する量のエチルセルロース
樹脂を撹拌羽で撹拌しながら添加してビヒクルａを調製
した。[Preparation of Vehicle] Vehicle a: An amount of dipropylene glycol monomethyl ether corresponding to 87% by weight based on the whole vehicle is heated to 60 ° C. on a hot plate. Next, an amount of ethylcellulose resin equivalent to 13% by weight was added thereto while stirring with a stirring blade to prepare a vehicle a.
【００２２】ビヒクルｂ：ビヒクル全体に対し９０重量
％に相当する量のエチレングリコールモノブチルエーテ
ルをホットプレート上にて６０℃まで加熱する。次に、
この中に、同じく１０重量％に相当する量のエチルセル
ロース樹脂を撹拌羽で撹拌しながら添加してビヒクルｂ
を調製した。Vehicle b: An amount of ethylene glycol monobutyl ether corresponding to 90% by weight based on the whole vehicle is heated to 60 ° C. on a hot plate. next,
Ethyl cellulose resin in an amount equivalent to 10% by weight was added thereto while stirring with stirring blades, and vehicle b
Was prepared.
【００２３】［実施例１］上記ビヒクルａに金属粉末と
してＮｉ粉末を加え、３本ロールミルにより十分混練し
た後、希釈剤としてジプロピレングリコールモノメチル
エーテルを加えて更に混練し、実施例１に係る内部電極
用ペーストを調製した。[Example 1] Ni powder as a metal powder was added to the above-mentioned vehicle a, kneaded sufficiently by a three-roll mill, and then dipropylene glycol monomethyl ether was added as a diluent and further kneaded. An electrode paste was prepared.
【００２４】尚、この内部電極用ペーストの組成は、Ｎ
ｉ粉末が６０重量％、有機バインダーとしてのエチルセ
ルロース樹脂が４重量％、有機溶剤としてのジプロピレ
ングリコールモノメチルエーテルが３６重量％である。The composition of the internal electrode paste is N
i powder is 60% by weight, ethyl cellulose resin as an organic binder is 4% by weight, and dipropylene glycol monomethyl ether as an organic solvent is 36% by weight.
【００２５】◎乾燥性及び粘度評価 次に、この実施例に係る内部電極用ペーストの乾燥性と
粘度について以下のような評価試験を行った。Evaluation of Drying Property and Viscosity Next, the following evaluation tests were performed on the drying property and viscosity of the internal electrode paste according to this example.
【００２６】まず、内部電極用ペーストの乾燥速度につ
いてセイコー電子（株）社製のＴＧ−ＤＴＡ分析装置を
用いて測定した。すなわち、この内部電極用ペースト２
６ｍｇをアルミナホルダーに入れ、空気中、常温〜８０
℃まで０．５℃／ｍｉｎで昇温した。流量は２００ｍｌ
／ｍｉｎである。First, the drying speed of the internal electrode paste was measured using a TG-DTA analyzer manufactured by Seiko Denshi Co., Ltd. That is, this paste for internal electrodes 2
6 mg was placed in an alumina holder, and in air, at room temperature to 80
The temperature was raised to 0.5 ° C. at a rate of 0.5 ° C./min. Flow rate is 200ml
/ Min.
【００２７】ここで、Ｎｉ粉末、エチルセルロースおよ
びテルピネオールを主成分とした従来の内部電極用ペー
ストにおけるＴＧ値は７０℃で−７％の重量減だった。The TG value of the conventional internal electrode paste containing Ni powder, ethylcellulose and terpineol as main components was -7% at 70 ° C.
【００２８】そこで、７０℃のＴＧ値が−７％より低い
場合を乾燥性が速いとみなした。表１にこの結果を示
す。表１中、「×」が従来の内部電極用ペーストより乾
燥性が遅いペーストで、「○」が従来のペーストより乾
燥性が速いペーストであることを示している。Therefore, when the TG value at 70 ° C. was lower than -7%, the drying property was regarded as fast. Table 1 shows the results. In Table 1, "x" indicates that the paste has a lower drying property than the conventional paste for internal electrodes, and "o" indicates that the paste has a higher drying property than the conventional paste.
【００２９】次に、内部電極用ペーストの粘度測定につ
いてはブルックフィールド（株）社製のＨＢＴ回転粘度
計を用い、２５℃、１００ｒｐｍの条件で行った。Next, the viscosity of the internal electrode paste was measured at 25 ° C. and 100 rpm using an HBT rotational viscometer manufactured by Brookfield Corporation.
【００３０】誘電体グリーンシートに対する印刷性の観
点から粘度が５〜６０パスカル・秒（Ｐａ・ｓ）の範囲
を印刷可能と評価した。表１中、「○」が印刷可能、
「×」が印刷不可能とした。From the viewpoint of printability with respect to the dielectric green sheet, the printability was evaluated in the range of viscosity of 5 to 60 Pascal · sec (Pa · s). In Table 1, "○" is printable,
"X" indicates that printing was impossible.
【００３１】そして、これ等評価を行ったところ、実施
例１に係る内部電極用ペーストは表１に示すように乾燥
性が速く、かつ、印刷可能な粘度であった。As a result of these evaluations, the paste for an internal electrode according to Example 1 had a high drying property and a printable viscosity as shown in Table 1.
【００３２】また、この内部電極用ペーストについて
は、乾燥性が良好であるにも拘らず、ペースト調製途中
における粘度増大の問題は存在しなかった。Further, with respect to the internal electrode paste, despite the good drying property, there was no problem of viscosity increase during the paste preparation.
【００３３】［実施例２］上記ビヒクルａを用いて内部
電極用ペーストを調製した。この内部電極用ペーストの
組成は、Ｎｉ粉末が３２重量％、エチルセルロース樹脂
が３重量％、ジプロピレングリコールモノメチルエーテ
ルが６５重量％であった。Example 2 An internal electrode paste was prepared using the above-mentioned vehicle a. The composition of the internal electrode paste was such that Ni powder was 32% by weight, ethyl cellulose resin was 3% by weight, and dipropylene glycol monomethyl ether was 65% by weight.
【００３４】そして、実施例１と同様な乾燥性と粘度の
評価試験を行ったところ、実施例１に係る内部電極用ペ
ーストと同様、乾燥性が速く、かつ、印刷可能な粘度で
あった。また、乾燥性が良好であるにも拘らず、ペース
ト調製途中における粘度増大の問題も存在しなかった。An evaluation test of drying property and viscosity was conducted in the same manner as in Example 1. As a result, as in the case of the internal electrode paste according to Example 1, the drying property was fast and the printable viscosity was obtained. In addition, despite the good drying property, there was no problem of viscosity increase during paste preparation.
【００３５】［実施例３］上記ビヒクルｂに金属粉末と
してＮｉ粉末を加え、３本ロールミルにより十分混練し
た後、希釈剤としてジプロピレングリコールモノメチル
エーテルを加えて更に混練し、実施例３に係る内部電極
用ペーストを調製した。Example 3 Ni powder as a metal powder was added to the above-mentioned vehicle b, and the mixture was sufficiently kneaded by a three-roll mill. Then, dipropylene glycol monomethyl ether was added as a diluent and further kneaded. An electrode paste was prepared.
【００３６】尚、この内部電極用ペーストの組成は、Ｎ
ｉ粉末が７５重量％、有機バインダーとしてのエチルセ
ルロース樹脂が２重量％、有機溶剤としてのジプロピレ
ングリコールモノメチルエーテルが５重量％、エチレン
グリコールモノブチルエーテルが１８重量％である。The composition of the internal electrode paste was N
i powder is 75% by weight, ethyl cellulose resin as an organic binder is 2% by weight, dipropylene glycol monomethyl ether as an organic solvent is 5% by weight, and ethylene glycol monobutyl ether is 18% by weight.
【００３７】そして、実施例１と同様な乾燥性と粘度の
評価試験を行ったところ、実施例１に係る内部電極用ペ
ーストと同様、乾燥性が速く、かつ、印刷可能な粘度で
あった。また、乾燥性が良好であるにも拘らず、ペース
ト調製途中における粘度増大の問題も存在しなかった。Then, the same dryness and viscosity evaluation test as in Example 1 was carried out. As a result, the dryability was high and the printable viscosity was as in the case of the internal electrode paste according to Example 1. In addition, despite the good drying property, there was no problem of viscosity increase during paste preparation.
【００３８】［実施例４］上記ビヒクルａを用いて内部
電極用ペーストを調製した。この内部電極用ペーストの
組成は、Ｎｉ粉末が５０重量％、エチルセルロース樹脂
が３重量％、ジプロピレングリコールモノメチルエーテ
ルが４７重量％であった。Example 4 An internal electrode paste was prepared using the vehicle a. The composition of the internal electrode paste was such that Ni powder was 50% by weight, ethyl cellulose resin was 3% by weight, and dipropylene glycol monomethyl ether was 47% by weight.
【００３９】そして、実施例１と同様な乾燥性と粘度の
評価試験を行ったところ、実施例１に係る内部電極用ペ
ーストと同様、乾燥性が速く、かつ、印刷可能な粘度で
あった。また、乾燥性が良好であるにも拘らず、ペース
ト調製途中における粘度増大の問題も存在しなかった。Then, the same dryness and viscosity evaluation test as in Example 1 was performed. As a result, the dryability was fast and the printable viscosity was the same as that of the internal electrode paste according to Example 1. In addition, despite the good drying property, there was no problem of viscosity increase during paste preparation.
【００４０】［実施例５］上記ビヒクルａを用いて内部
電極用ペーストを調製した。この内部電極用ペーストの
組成は、Ｎｉ粉末が７０重量％、エチルセルロース樹脂
が１．５重量％、ジプロピレングリコールモノメチルエ
ーテルが２８．５重量％であった。Example 5 An internal electrode paste was prepared using the above-mentioned vehicle a. The composition of the internal electrode paste was such that Ni powder was 70% by weight, ethyl cellulose resin was 1.5% by weight, and dipropylene glycol monomethyl ether was 28.5% by weight.
【００４１】そして、実施例１と同様な乾燥性と粘度の
評価試験を行ったところ、実施例１に係る内部電極用ペ
ーストと同様、乾燥性が速く、かつ、印刷可能な粘度で
あった。また、乾燥性が良好であるにも拘らず、ペース
ト調製途中における粘度増大の問題も存在しなかった。Then, the same dryness and viscosity evaluation test as in Example 1 was carried out. As a result, the dryability was high and the printable viscosity was as in the case of the internal electrode paste according to Example 1. In addition, despite the good drying property, there was no problem of viscosity increase during paste preparation.
【００４２】［実施例６］上記ビヒクルｂに金属粉末と
してＮｉ粉末を加え、３本ロールミルにより十分混練し
た後、希釈剤としてジプロピレングリコールモノメチル
エーテルを加えて更に混練し、実施例６に係る内部電極
用ペーストを調製した。Example 6 Ni powder as a metal powder was added to the above-mentioned vehicle b, and the mixture was sufficiently kneaded by a three-roll mill. Then, dipropylene glycol monomethyl ether was added as a diluent and further kneaded. An electrode paste was prepared.
【００４３】尚、この内部電極用ペーストの組成は、Ｎ
ｉ粉末が７０重量％、有機バインダーとしてのエチルセ
ルロース樹脂が１．２重量％、有機溶剤としてのジプロ
ピレングリコールモノメチルエーテルが１８重量％、エ
チレングリコールモノブチルエーテルが１０．８重量％
である。The composition of the internal electrode paste was N
i powder 70% by weight, ethyl cellulose resin as an organic binder 1.2% by weight, dipropylene glycol monomethyl ether as an organic solvent 18% by weight, ethylene glycol monobutyl ether 10.8% by weight
It is.
【００４４】そして、実施例１と同様な乾燥性と粘度の
評価試験を行ったところ、実施例１に係る内部電極用ペ
ーストと同様、乾燥性が速く、かつ、印刷可能な粘度で
あった。また、乾燥性が良好であるにも拘らず、ペース
ト調製途中における粘度増大の問題も存在しなかった。Then, the same dryness and viscosity evaluation test as in Example 1 was carried out. As a result, the dryability was high and the printable viscosity was as in the case of the internal electrode paste according to Example 1. In addition, despite the good drying property, there was no problem of viscosity increase during paste preparation.
【００４５】［比較例１］上記ビヒクルａを用いて内部
電極用ペーストを調製した。この内部電極用ペーストの
組成は、Ｎｉ粉末が３２重量％、エチルセルロース樹脂
が２重量％、ジプロピレングリコールモノメチルエーテ
ルが６６重量％であった。Comparative Example 1 An internal electrode paste was prepared using the above-mentioned vehicle a. The composition of the internal electrode paste was such that Ni powder was 32% by weight, ethyl cellulose resin was 2% by weight, and dipropylene glycol monomethyl ether was 66% by weight.
【００４６】そして、実施例１と同様な乾燥性と粘度の
評価試験を行ったところ、実施例１に係る内部電極用ペ
ーストと同様に乾燥性は良好であったが、粘度について
は印刷不可能な粘度であった。これは、金属粉末、有機
バインダーおよび有機溶剤の総量に対するジプロピレン
グリコールモノメチルエーテルの配合割合が６５重量％
を越えたためと思われる。An evaluation test of drying property and viscosity was performed in the same manner as in Example 1. As a result, the drying property was good as in the case of the internal electrode paste according to Example 1, but the viscosity was not printable. Viscosity. This is because the mixing ratio of dipropylene glycol monomethyl ether to the total amount of the metal powder, the organic binder and the organic solvent is 65% by weight.
Probably because it exceeded.
【００４７】［比較例２］上記ビヒクルｂに金属粉末と
してＮｉ粉末を加え、３本ロールミルにより十分混練し
た後、希釈剤としてジプロピレングリコールモノメチル
エーテルを加えて更に混練し、比較例２に係る内部電極
用ペーストを調製した。[Comparative Example 2] Ni powder as a metal powder was added to the above-mentioned vehicle b, kneaded sufficiently with a three-roll mill, and dipropylene glycol monomethyl ether was added as a diluent and further kneaded. An electrode paste was prepared.
【００４８】尚、この内部電極用ペーストの組成は、Ｎ
ｉ粉末が７０重量％、有機バインダーとしてのエチルセ
ルロース樹脂が２．６重量％、有機溶剤としてのジプロ
ピレングリコールモノメチルエーテルが４重量％、エチ
レングリコールモノブチルエーテルが２３．４重量％で
あった。The composition of the internal electrode paste was N
i powder was 70% by weight, ethyl cellulose resin as an organic binder was 2.6% by weight, dipropylene glycol monomethyl ether as an organic solvent was 4% by weight, and ethylene glycol monobutyl ether was 23.4% by weight.
【００４９】そして、実施例１と同様な乾燥性と粘度の
評価試験を行ったところ、実施例１に係る内部電極用ペ
ーストと同様に印刷可能な粘度であったが、乾燥性は遅
くなった。これは、金属粉末、有機バインダーおよび有
機溶剤の総量に対するジプロピレングリコールモノメチ
ルエーテルの配合割合が５重量％未満であったためと思
われる。An evaluation test of the drying property and the viscosity was performed in the same manner as in Example 1. As a result, the printing property was similar to that of the internal electrode paste according to Example 1, but the drying property was slow. . This is probably because the mixing ratio of dipropylene glycol monomethyl ether to the total amount of the metal powder, the organic binder, and the organic solvent was less than 5% by weight.
【００５０】[0050]
【表１】 [Table 1]
【００５１】[0051]
【発明の効果】請求項１および２記載の発明に係る積層
セラミックコンデンサ内部電極用ペースト組成物によれ
ば、金属粉末、有機バインダーおよび有機溶剤の総量に
対し５〜６５重量％の範囲で上記有機溶剤中にジプロピ
レングリコールモノメチルエーテルが含まれているた
め、ペーストの調製途中において調製組成物の粘度増大
に伴う弊害を引起こすことなくその乾燥性の改善を図る
ことが可能となる。According to the paste composition for an internal electrode of a multilayer ceramic capacitor according to the first and second aspects of the present invention, the organic compound is contained in the range of 5 to 65% by weight based on the total amount of the metal powder, the organic binder and the organic solvent. Since dipropylene glycol monomethyl ether is contained in the solvent, it is possible to improve the drying property of the paste without causing any adverse effect due to an increase in the viscosity of the composition during the preparation of the paste.
【００５２】従って、積層セラミックコンデンサにおけ
る生産性の向上を図ることができる効果を有する。Accordingly, there is an effect that the productivity of the multilayer ceramic capacitor can be improved.
【図１】図１（Ａ）は積層セラミックコンデンサの概略
斜視図であり、図１（Ｂ）は図１（Ａ）の一部切欠断面
図である。FIG. 1 (A) is a schematic perspective view of a multilayer ceramic capacitor, and FIG. 1 (B) is a partially cutaway sectional view of FIG. 1 (A).
ａ：積層セラミックコンデンサ ｂ：誘電体層 ｃ：内部電極 ｄ：コンデンサ本体 e1：外部電極 e2：外部電極 a: multilayer ceramic capacitor b: dielectric layer c: internal electrode d: capacitor body e1: external electrode e2: external electrode
Claims (2)
れたコンデンサ本体と、このコンデンサ本体の外側に設
けられ上記内部電極群に接続される一対の外部電極とを
備える積層セラミックコンデンサの製造に適用されると
共に、金属粉末、有機バインダーおよび有機溶剤を主成
分とする積層セラミックコンデンサ内部電極用ペースト
組成物において、 上記有機溶剤がジプロピレングリコールモノメチルエー
テルを含有し、かつ、上記金属粉末、有機バインダーお
よび有機溶剤の総量に対するジプロピレングリコールモ
ノメチルエーテルの配合割合が５〜６５重量％の範囲に
設定されていることを特徴とする積層セラミックコンデ
ンサ内部電極用ペースト組成物。1. A multilayer ceramic capacitor comprising: a capacitor body in which a plurality of dielectric layers and internal electrodes are alternately stacked; and a pair of external electrodes provided outside the capacitor body and connected to the internal electrode group. Along with being applied to the production, a metal powder, a paste composition for a multilayer ceramic capacitor internal electrode containing an organic binder and an organic solvent as main components, wherein the organic solvent contains dipropylene glycol monomethyl ether, and the metal powder, A paste composition for an internal electrode of a multilayer ceramic capacitor, wherein a mixing ratio of dipropylene glycol monomethyl ether to the total amount of an organic binder and an organic solvent is set in a range of 5 to 65% by weight.
溶剤の総量に対する金属粉末の配合割合が２７重量％〜
８５重量％、また、上記総量に対する有機バインダーの
配合割合が１重量％〜８重量％の範囲にそれぞれ設定さ
れていることを特徴とする請求項１記載の積層セラミッ
クコンデンサ内部電極用ペースト組成物。2. The mixing ratio of the metal powder to the total amount of the metal powder, the organic binder and the organic solvent is 27% by weight or more.
2. The paste composition for an internal electrode of a multilayer ceramic capacitor according to claim 1, wherein 85% by weight and a compounding ratio of the organic binder with respect to the total amount are respectively set in a range of 1% by weight to 8% by weight.