JPH1129344A - 極細ガラス繊維 - Google Patents
極細ガラス繊維Info
- Publication number
- JPH1129344A JPH1129344A JP20217397A JP20217397A JPH1129344A JP H1129344 A JPH1129344 A JP H1129344A JP 20217397 A JP20217397 A JP 20217397A JP 20217397 A JP20217397 A JP 20217397A JP H1129344 A JPH1129344 A JP H1129344A
- Authority
- JP
- Japan
- Prior art keywords
- glass
- weight
- glass fiber
- zno
- fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
フィルタ用として用いても、ボロンガス状物質を発生し
ない濾紙として使用でき、また、Eガラス並みの耐久性
を備え、しかも実用的価格で製造可能な極細ガラス繊維
を提供することを目的とする。 【解決手段】 SiO2 55〜70重量%、(R1)2
O(R1=Na,K) 8〜12重量%、(R2)2O3
(R2=Al,Fe) 1〜15重量%、(R3)O
(R3=Ca,Mg,Ba) 10〜14重量%、Zn
O 0〜15重量%、B2 O3 0.01重量%以下の
組成であり且つ(R2)2O3+ZnOは9〜20重量%
であることを特徴とする。
Description
少ない極細ガラス繊維の改良に関する。
は、ボロンシリケートガラス繊維や耐酸性特殊グレード
の高シリカ分ガラス繊維が知られている。ここで高シリ
カ分とは一般に石英ガラス繊維と総称されるもので、溶
融石英ガラス繊維や高珪酸ガラス繊維、或いは、ゾルゲ
ル法ガラス繊維等が知られ、SiO2 が99.8〜9
9.99重量%のものである。また、極細ガラス繊維は
CガラスだけでなくEガラスでも製造されている。前記
Cガラスの極細ガラス繊維はHEPA、ULPA、超U
LPA等の高性能フィルタ用濾紙、電池用セパレータ、
断熱材等、各種分野で使用されている。また、Eガラス
の極細ガラス繊維は電気絶縁用としてエンプラ用充填
材、特殊紙等に使用されている。
記Cガラスからなる極細ガラス繊維を使用した高性能フ
ィルタ用濾紙で構成されたHEPAフィルタを半導体ク
リーンルームで使用した場合、酸性ガス、或いは、空気
中の水分により化学反応を起こし、ガラス中のB2O3が
ガス状物質としてクリーンルーム内に飛散し、シリコン
ウエハの表面に付着し、特性劣化を引き起こすことが問
題視されている。
HEPAフィルタとして、例えば、特開平5−2022
17号公報、特開平7−292144号公報、特表平9
−504737号公報等に開示されるようなPTFE膜
濾材からなるフィルタ、特開平6−55019号公報、
特開平6−285318号公報等に開示されるような高
珪酸ガラス繊維の濾紙からなるフィルタ、或いは、特開
平7−194911号公報、特開平5−285324号
公報等に開示されるようなガラス繊維の表面を被覆した
濾紙からなるフィルタが提案されている。
るフィルタは低圧力損失で優れた特性を備えるものの、
膜が非常に薄いため均一性能のものが得にくい問題や製
品コストが高いといった問題がある。また、高珪酸ガラ
ス繊維の濾紙からなるフィルタは、材料が高価で実用性
に乏しいといった問題がある。また、ガラス繊維の表面
を薬剤で被覆した濾紙からなるフィルタは、ガラス繊維
1本、1本を均一に被覆することが困難なため、被覆さ
れない部分からボロンガス状物質が発生する危険が高い
といった問題がある。そこで、本発明は、HEPA、U
LPA、超ULPA等の高性能フィルタ用として用いて
も、ボロンガス状物質を発生しない濾紙として使用で
き、また、Eガラス並みの耐久性を備え、しかも実用的
価格で製造可能な極細ガラス繊維を提供することを目的
とする。
は前記目的を達成するべく、SiO2 55〜70重量
%、(R1)2O(R1=Na,K) 8〜12重量
%、(R2)2O3(R2=Al,Fe) 1〜15重量
%、(R3)O(R3=Ca,Mg,Ba) 10〜1
4重量%、ZnO 0〜15重量%、B2 O3 0.0
1重量%以下の組成であり且つ(R2)2O3+ZnOは
9〜20重量%であることを特徴とするもので、ボロン
ガス状物質を発生しないで且つ実用的価格で製造できる
ものである。また、請求項2記載の極細ガラス繊維は、
前記ZnOを10重量%以上としたことを特徴とするも
ので、製造に際し、ガラスの溶融温度があまり高くなら
ず紡糸性に優れるものである。
るための原料ガラスとしては、基本組成が73SiO2
−15Na2O−12CaOのいわゆるソーダ石灰ガラ
スが用いられる。ところが、このような組成のソーダ石
灰ガラスを平均繊維径2μm以下に紡糸すると比表面積
が大きくなり、板ガラスでは問題とならなかった風化作
用、即ち、空気中の水分や炭酸ガスによってアルカリ成
分が溶出してガラス繊維が破壊されることによって繊維
強度が著しく低下してしまい繊維製品を製造できないと
いったことになる。このため、本発明では、前記ソーダ
石灰ガラスにAl2O3とZnOを添加することにより、
SiO2 55〜70重量%、(R1)2O(R1=N
a,K) 8〜12重量%、(R2)2O3(R2=A
l,Fe) 1〜15重量%、(R3)O(R3=C
a,Mg,Ba) 10〜14重量%、ZnO 0〜1
5重量%、B2 O3 0.01重量%以下の組成であり
且つ(R2)2O3+ZnOは9〜20重量%とするもの
である。
ため、B2O3を10重量%程度配合することで、徐冷点
(1013 P粘度となる温度)ではB3+イオンが非架橋
酸素イオンを引き付けて〔BO4 〕4面体構造をつく
り、ガラス網目構造の切れ目を閉じて組織の破壊を抑制
するようにしていたので、B2O3を0.01重量%以下
にするために、アルカリの溶出を抑制する副成分とし
て、(R2)2O3(R2=Al,Fe)を1〜15重量
%、ZnOを0〜15重量%、且つ(R2)2O3+Zn
Oを9〜20重量%とするものである。前記(R2)2
O3(R2=Al,Fe)が1〜15重量%の範囲にあ
れば、ガラス表面でアルミノシリケート等の錯塩が形成
され、これが保護膜として働き、耐水性と耐酸性等の耐
久性を向上することができる。しかしながら、(R2)
2O3(R2=Al,Fe)が1重量%未満では、アルカ
リ溶出量が大きくなり風化作用に対する効果が見られな
い。また、(R2)2O3(R2=Al,Fe)が15重
量%を超えると、Tf値(繊維紡糸時の102 .5 P粘
度となる温度)が高くなり繊維化が難しくなる。また、
(R2)2O3+ZnOを9〜20重量%とするのは、Z
nOを配合することでアルカリ溶出量を小さくできるた
め、Al2O3の量を少なくすることによってガラスの溶
融温度を低くして紡糸性を良好とするためである。特
に、ZnOを10重量%以上とすることで、紡糸性を極
めて良好にできるものである。
5重量%未満とすると、SiO4の4面体の3次元網目
構造の隙間に副成分の金属原子が入り込むことから、水
分、炭酸ガス等の影響を受けて風化し易くなる。また、
前記SiO2 が70重量%を超えると、紡糸温度(繊維
紡糸時の粘度が103 Pとなる温度)が高くなり繊維化
がし辛くなる。また、前記(R1)2O(R1=Na,
K)を8重量%未満とすると、SiO2と混合加熱さ
れ、ガラスの融点を下げて溶け易くする作用が低くな
る。また、(R1)2 O(R1=Na,K)が12重量
%を超えると、Na2OとK2OのNa+イオンとK+イオ
ンは酸素との結合力が弱いため、製造されたガラス繊維
が水と接触すると簡単に溶け出す水溶現象が生じて風化
作用の影響を受けやすくなる。また、前記(R3)O
(R3=Ca,Mg,Ba)を10重量%未満とする
と、SiO2 と混合加熱され、ガラスの融点を下げて溶
け易くする作用が低くなり、しかも風化作用防止の補助
効果が低下する。また、(R3)O(R3=Ca,M
g,Ba)が14重量%を超えると、失透温度が高くな
り、紡糸性が悪くなる。
較例と共に説明する。まず、カレットガラスを磁製乳鉢
で250μm以下に粉砕し、これに表1のガラス組成と
なるように、亜鉛華(ZnO)及び/又はアルミナ(A
l2O3)を加えてよく混合し、試料1〜16を調合し
た。次に、調合したガラス粉末約20gを磁製るつぼに
入れ、電気炉中で1300℃、4時間加熱溶融し、ガラ
スペレットを作製した。このようにして得られたガラス
ペレットをそれぞれ磁製乳鉢で粉砕し、500μm、4
20μm、250μmの標準網ふるいで順番にふるい分
けを行い、250〜420μmのガラス粉末を約5g分
別した。その後、分別したガラス粉末をエチルアルコー
ル(99.5容量%)でよく洗い微粉を取り除いた後、
乾燥器で約125℃で30分間乾燥させてデシケータ中
に保存した。
験(JIS−R−3502-1995 に準拠)を行った。即
ち、まず、ナス型フラスコ中に40mlの蒸留水を入
れ、10分間以上沸騰水溶中に保持した。次に、各試料
を5g量り取ってフラスコ中に投入し、更に、10ml
の蒸留水で器壁の内面に付着した試料を洗い落とし、ゆ
るく振り動かして試料集積物の上部が一様な平面を保つ
ように安定させた。次に、冷却器を取り付け、沸騰水溶
中で60分間加熱した。次いで、フラスコを水溶中から
取り出して直ちに流水で冷却し、内溶液を硬質ガラス製
ビーカに移した。これにメチルレッド指示薬を3滴加
え、溶出したアルカリ成分を0.005mol/リット
ル硫酸で摘定した。また、別に同様の方法で空試験を行
った。尚、試験結果は空試験結果を差し引いた後、0.
005mol/リットルの硫酸の消費ミリリットル数に
0.31を乗じた後、投入試料量当たりのNa2Oのm
g数に換算した。また、各試料を粉砕し、小形溶融炉に
投入し、ノズル温度を103 ポイズ温度に設定し、0.
35μm程度のフィラメントを紡糸した。前記結果を表
1に示した。
5.8重量%配合する場合は、ZnOを8.0〜10.
0重量%配合することで、アルカリ溶出量を0.06m
g・Na2 O/g以下に抑制できる。特に、試料6はア
ルカリ溶出量も少なく、紡糸性に最も優れていた。ま
た、試料8の通り、Al2O3を1.5重量%配合する場
合は、ZnOを15.0重量%配合することで、アルカ
リ溶出量を0.06mg・Na2 O/g以下に抑制でき
る。また、試料9〜12の通り、Al2O3のみ配合する
場合は、9.1〜16.5重量%配合することで、アル
カリ溶出量を0.06mg・Na2 O/g以下に抑制で
きる。但し、試料12の通り、Al2O3を16.5重量
%配合する場合は、ガラス繊維の紡糸温度が高くなる問
題がある。また、試料13〜15の通り、Al2O3を
7.9〜8.0重量%配合する場合は、ZnOを3.0
〜10.0重量%配合することで、アルカリ溶出量を
0.06mg・Na2 O/g以下に抑制できる。また、
試料16の通り、Al2O3を10.4重量%、ZnOを
10.0重量%配合することで、アルカリ溶出量を0.
04mg・Na2 O/g以下に、最も優れた抑制ができ
る。
ーンルーム用フィルタ等の原材料として使用できるもの
で、半導体クリーンルームで問題視されているボロンガ
ス状物質の汚染源をガラス中に含まない。また、風化作
用による繊維劣化がないため繊維製品としての所望の強
度得られる。更にまた、ホウケイ酸ガラスと同等の融点
であるため、紡糸温度を低く押さえられ繊維化が容易で
且つガラス溶融炉の炉寿命を縮めることがなく、石英ガ
ラス、Eガラス、耐アルカリガラス等よりも安く製造で
きる。
Claims (2)
- 【請求項1】 SiO2 55〜70重量%、(R1)2
O(R1=Na,K) 8〜12重量%、(R2)2O3
(R2=Al,Fe) 1〜15重量%、(R3)O
(R3=Ca,Mg,Ba) 10〜14重量%、Zn
O 0〜15重量%、B2 O3 0.01重量%以下の
組成であり且つ(R2)2O3+ZnOは9〜20重量%
であることを特徴とする極細ガラス繊維。 - 【請求項2】 前記ZnOを10重量%以上としたこと
を特徴とする請求項1記載の極細ガラス繊維。