JPH11285705A - Manufacture of preliminarily treated stainless steel strip for cold rolling - Google Patents
Manufacture of preliminarily treated stainless steel strip for cold rollingInfo
- Publication number
- JPH11285705A JPH11285705A JP8843898A JP8843898A JPH11285705A JP H11285705 A JPH11285705 A JP H11285705A JP 8843898 A JP8843898 A JP 8843898A JP 8843898 A JP8843898 A JP 8843898A JP H11285705 A JPH11285705 A JP H11285705A
- Authority
- JP
- Japan
- Prior art keywords
- rolling
- steel strip
- roll
- stainless steel
- cold
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、表面光沢が良好な
ステンレス冷延鋼帯を有利に生産するための冷間圧延用
ステンレス予備処理鋼帯の製造方法に関するものであ
る。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for producing a cold-rolled stainless steel pretreated steel strip for advantageously producing a stainless cold rolled steel strip having a good surface gloss.
【０００２】[0002]
【従来の技術】ＳＵＳ４３０に代表されるフェライト系
ステンレス冷延鋼板は、建築内装材、厨房器具、各種装
飾品などの用途に用いられており、これらの用途では優
れた表面光沢が必要である。また、ＳＵＳ３０４に代表
されるオーステナイト系ステンレス冷延鋼板も、厨房器
具などの用途に用いられ、同様に優れた表面光沢が求め
られる。これらの表面光沢が必要なステンレス冷延鋼板
は、従来から、熱間圧延後、焼鈍、酸洗を行い、引き続
いて、この焼鈍酸洗した熱延鋼帯を、ロール直径１００
ｍｍφ以下の小径ロールを具えたクラスター圧延機によ
り、ニート油潤滑下で冷間圧延し、仕上げ焼鈍・酸洗ま
たは光輝焼鈍を行った後、調質圧延あるいはさらにオー
ステナイト系の場合にはバフ研磨を施す一連の工程によ
って製造されてきた。これに対して、最近、上記小径ロ
ールのクラスター圧延機に代わり、より大径のロールを
具えた冷間タンデム圧延機を用いることにより、高能率
に圧延する方法が試みられるようになってきた。2. Description of the Related Art Ferritic stainless steel cold-rolled steel sheets represented by SUS430 are used for applications such as building interior materials, kitchen appliances, and various decorative articles, and these applications require excellent surface gloss. Further, austenitic stainless steel cold-rolled steel sheets represented by SUS304 are also used for kitchen appliances and the like, and similarly excellent surface gloss is required. Conventionally, stainless steel cold rolled steel sheets requiring surface gloss have been subjected to annealing and pickling after hot rolling, and subsequently, the annealed and pickled hot rolled steel strip is rolled to a roll diameter of 100.
Cold rolling under neat oil lubrication by a cluster rolling machine equipped with a small diameter roll of not more than mmφ, finish annealing, pickling or bright annealing, then temper rolling or further buff polishing in case of austenitic system It has been manufactured by a series of steps of applying. On the other hand, recently, a method of performing high-efficiency rolling by using a cold tandem rolling mill provided with a larger-diameter roll instead of the cluster rolling mill of the small-diameter roll has been attempted.
【０００３】しかし、上記冷間タンデム圧延機によって
圧延すれば、ステンレス冷延鋼帯の生産性を高めること
はできるものの、その表面光沢が著しく低下するという
問題があった。表面光沢が低下する理由は、圧延時にロ
ールバイトに大量の圧延油が引き込まれ、鋼帯とロール
とが十分に接触しなくなり、圧延後の鋼帯の表面粗さが
大きくなるからである。また、ＳＵＳ３０４などのオー
ステナイト系ステンレス鋼帯の製造に際しては、冷間圧
延の前に行われる熱延鋼帯の焼鈍で、粒界浸食溝と呼ば
れる深さ１０数μｍ〜数１０μｍの網目状の微小欠陥が
鋼帯表面に生じる。この粒界浸食溝は、通常の冷間圧延
工程で多少傾斜して浅くはなるが、冷延後の焼鈍で発生
するものより深いため、消滅させるためにはバフ研磨で
多くのパス回数を必要としていた。かかるオーステナイ
ト系ステンレス鋼にみられる粒界浸食溝のほかに、ま
た、ステンレス鋼の酸洗前のショット処理で発生するシ
ョット目も、冷延鋼帯の光沢を低下させる要因となって
いた。[0003] However, although the productivity of a cold-rolled stainless steel strip can be increased by rolling with the above-mentioned cold tandem rolling mill, there has been a problem that its surface gloss is remarkably reduced. The reason why the surface gloss is reduced is that a large amount of rolling oil is drawn into the roll bite during rolling, the steel strip and the roll do not come into sufficient contact, and the surface roughness of the rolled steel strip increases. In the production of an austenitic stainless steel strip such as SUS304, a network of microscopic fine grains having a depth called grain boundary erosion grooves having a depth of ten to several tens μm to several tens of μm by annealing of a hot-rolled steel strip performed before cold rolling. Defects occur on the steel strip surface. This grain boundary erosion groove is slightly inclined and shallow in the normal cold rolling process, but it is deeper than that generated by annealing after cold rolling, so many passes are required by buffing to eliminate it And had In addition to the grain boundary erosion grooves found in such austenitic stainless steel, shots generated in the shot treatment before pickling of the stainless steel have also been a factor in reducing the gloss of the cold-rolled steel strip.
【０００４】以上述べたようなステンレス冷延鋼帯にお
ける表面光沢の低下に対して、これまでにもその改善方
法がいくつか提案されてきた。例えば、特開平２−1691
08号公報には、熱延後のステンレス鋼帯に、焼鈍、酸洗
を施した後、ロールの周面に編み目（クロス目）状の溝
を設けたロールで、冷延前の予備処理圧延を施すことが
開示されている。また、特開平８−229603号公報には、
熱延後のステンレス鋼帯に、焼鈍、酸洗を施した後、予
備処理圧延を施すに際し，ＷＣ合金からなるロールで冷
延前の予備処理圧延を施すことが開示されている。[0004] Several methods for improving the surface gloss of the cold-rolled stainless steel strip described above have been proposed. For example, JP-A-2-1691
In Japanese Patent Publication No. 08, the stainless steel strip after hot rolling is subjected to annealing and pickling, and the roll is provided with a knitted (crossed) groove on the peripheral surface of the roll. Is disclosed. Also, JP-A-8-229603 discloses that
It is disclosed that, after the stainless steel strip after hot rolling is subjected to annealing and pickling and then subjected to pretreatment rolling, pretreatment rolling before cold rolling is performed by a roll made of a WC alloy.
【０００５】[0005]
【発明が解決しようとする課題】しかしながら、上記従
来技術における、予備処理圧延で用いているＷＣ合金ロ
ールは、ロール表面に、周方向の研磨目が存在するのが
一般的であり、このような研磨目を持つワークロールで
圧延すると、鋼帯表面に、スクラッチと呼ばれる、ワー
クロール研磨目の転写に起因する欠陥が新たに生じてし
まう。こうした状態の予備処理鋼帯を、タンデム圧延機
などの冷間圧延機に供給すると、圧延油がスクラッチに
封入されて圧延され、圧延した後にこの欠陥が残存す
る。このため、最終的な冷延鋼帯の表面光沢は十分に改
善されないという問題があった。However, the WC alloy roll used in the pre-treatment rolling in the prior art described above generally has a circumferential polished line on the roll surface. When rolling is performed with a work roll having a polished edge, a new defect called a scratch due to the transfer of the polished eye of the work roll is generated on the surface of the steel strip. When the pre-processed steel strip in such a state is supplied to a cold rolling mill such as a tandem rolling mill, the rolling oil is sealed in a scratch and rolled, and this defect remains after rolling. For this reason, there was a problem that the surface gloss of the final cold rolled steel strip was not sufficiently improved.
【０００６】一方、鋼系ロールの周面に編み目状の溝を
設けたロールで予備処理圧延する方法では、研磨目が傾
斜していることにより、鋼帯表面が圧延方向にせん断変
形を受けるので、スクラッナの転写が軽微ですみ、鋼帯
表面が平滑化され、表面光沢は向上する。しかし、この
方法では、鋼系（通常５wt％程度のCrを含む鍛鋼）ロー
ルを用いているため、傾斜した研磨目が著しく早く磨耗
してしまい、光沢改善の効果が長く持続しないという問
題があった。また、鋼系ロールの場合には、圧延中のロ
ール偏平が大きいため、ロールバイトに引き込まれる圧
延油量が多くなり、圧延油が微小な凹み欠陥に封入され
て光沢向上代が小さくなるという問題もあった。[0006] On the other hand, in the method of performing pretreatment rolling using a roll provided with a stitch-like groove on the peripheral surface of a steel roll, the surface of the steel strip undergoes shear deformation in the rolling direction due to the slanted polishing streaks. In addition, the transfer of the scranna is slight, the surface of the steel strip is smoothed, and the surface gloss is improved. However, in this method, since a steel-based (normally forged steel containing about 5 wt% of Cr) roll is used, the inclined polished line is worn away very quickly, and there is a problem that the effect of improving the gloss is not maintained for a long time. Was. In the case of steel rolls, since the flatness of the roll during rolling is large, the amount of rolling oil drawn into the roll bite increases, and the rolling oil is encapsulated in minute dent defects to reduce the gloss improvement margin. There was also.
【０００７】そこで本発明の目的は、従来技術が抱えて
いる上記問題点を解消することにあり、冷間圧延に供す
るための、スクラッチのない、あるいはまた粒界浸食溝
の少ない、平滑なステンレス予備処理鋼帯を効果的に製
造することにある。そして、この予備処理鋼帯を用い
て、冷間タンデム圧延を含む一連の工程で製造される最
終製品の表面光沢を一層改善することにある。また、本
発明の目的は、このような改善効果が長期にわたり安定
して持続できる、冷間圧延用ステンレス予備処理鋼帯の
製造方法提供することにある。SUMMARY OF THE INVENTION An object of the present invention is to solve the above-mentioned problems of the prior art, and to provide a smooth stainless steel for cold rolling without scratches or with less grain boundary erosion grooves. It is to produce a pre-treatment steel strip effectively. It is another object of the present invention to further improve the surface gloss of a final product manufactured in a series of steps including cold tandem rolling using the pre-treated steel strip. Another object of the present invention is to provide a method for producing a stainless steel pretreated steel strip for cold rolling, in which such improvement effect can be stably maintained for a long time.
【０００８】[0008]
【課題を解決するための手段】発明者らは、上記課題の
解決に向けて、予備処理圧延に用いるロールの材質、ロ
ールの周面に形成する研磨目のプロフィールについて詳
細に検討し、本発明を完成するに到った。すなわち、本
発明の要旨構成は以下のとおりである。 (1) 熱間圧延したステンレス鋼帯に、焼鈍、酸洗を施
し、その後、バレル部の少なくとも周面の材料をＷＣ系
超硬合金とし、かつ前記バレル部の周面に、円周方向を
挟んで両側にそれぞれ0.5 〜90°未満のほぼ等しい角度
で傾斜した研摩目を設けた、ワークロールを用いて圧延
することを特徴とする冷間圧延用ステンレス予備処理鋼
帯の製造方法。 (2) 熱間圧延したステンレス鋼帯に、焼鈍、酸洗を施
し、その後、バレル部の少なくとも周面の材料をＷＣ系
超硬合金とし、かつ前記バレル部の周面に、円周方向を
挟んで両側にそれぞれ５〜85°のほぼ等しい角度で傾斜
した研摩目を設けた、ワークロールを用いて圧延するこ
とを特徴とする冷間圧延用ステンレス予備処理鋼帯の製
造方法。 (3) 上記 (1)または (2)において、バレル部が、外層
の材料をＷＣ系超硬合金とし、内層の材料を鋼系合金と
する複合層で形成された、ワークロールを用いて圧延す
ることを特徴とする冷間圧延用ステンレス予備処理鋼帯
の製造方法。 (4) バレル部の周面において、研摩目の表面粗さがＲ
ａ＝0.05〜3.0 μｍである、ワークロールを用いて圧延
することを特徴とする上記 (1)〜 (3)のいずれか１つに
記載の冷間圧延用ステンレス予備処理鋼帯の製造方法。 (5) バレル部の周面において、研摩目の表面粗さがＲm
ax ＝0.2 〜30μｍである、ワークロールを用いて圧延
することを特徴とする上記 (1)〜 (3)のいずれか１つに
記載の冷間圧延用ステンレス予備処理鋼帯の製造方法。
なお、上記各発明において、予備処理圧延は、圧下率５
〜30％の範囲で行うことが望ましい。Means for Solving the Problems In order to solve the above-mentioned problems, the present inventors have studied in detail the material of a roll used for pre-treatment rolling and the profile of a polishing line formed on the peripheral surface of the roll. Was completed. That is, the gist configuration of the present invention is as follows. (1) Annealing and pickling are performed on the hot-rolled stainless steel strip, and thereafter, the material of at least the peripheral surface of the barrel portion is made of WC cemented carbide, and the circumferential direction of the barrel portion is A method for producing a stainless steel pretreated steel strip for cold rolling, characterized in that it is rolled using a work roll provided with polishing lines inclined at substantially equal angles of 0.5 to less than 90 ° on both sides thereof. (2) The hot-rolled stainless steel strip is annealed and pickled, and thereafter, the material of at least the peripheral surface of the barrel portion is made of WC cemented carbide, and the circumferential surface of the barrel portion is oriented in the circumferential direction. A method for producing a stainless steel pre-treated steel strip for cold rolling, characterized in that it is rolled using a work roll, with polishing lines inclined at substantially equal angles of 5 to 85 ° on both sides of the steel strip. (3) In the above (1) or (2), the barrel portion is rolled using a work roll formed of a composite layer in which the material of the outer layer is a WC-based cemented carbide and the material of the inner layer is a steel-based alloy. A method for producing a stainless steel pretreated steel strip for cold rolling, comprising: (4) On the peripheral surface of the barrel, the surface roughness
The method for producing a cold-rolled stainless steel pretreated steel strip according to any one of the above (1) to (3), wherein rolling is performed using a work roll, wherein a = 0.05 to 3.0 μm. (5) On the peripheral surface of the barrel part, the surface roughness
The method for producing a cold-rolled stainless steel pretreated steel strip according to any one of the above (1) to (3), wherein rolling is performed using a work roll, wherein ax = 0.2 to 30 μm.
In each of the above inventions, the pretreatment rolling is performed with a reduction rate of 5%.
It is desirable to carry out in the range of up to 30%.
【０００９】[0009]
【発明の実施の形態】発明者らは、生産性が高い一方
で、表面光沢の点では不利となる、冷間タンデム圧延に
より、ステンレス冷延鋼帯を製造する場合に、冷延鋼帯
の表面光沢を長期にわたり向上させるための方法につい
て検討を行った。その結果、上記目的を達成するために
は、冷間タンデム圧延に供給する素材の表面を、所定の
材質と表面プロフィールを具えた圧延ロールを用いて予
備処理圧延し、そののち冷間タンデム圧延することが有
効であることを知見した。BEST MODE FOR CARRYING OUT THE INVENTION The present inventors have found that while producing a stainless steel cold-rolled steel strip by cold tandem rolling, which has a high productivity but is disadvantageous in terms of surface gloss, A method for improving the surface gloss over a long period was examined. As a result, in order to achieve the above object, the surface of the material to be supplied to the cold tandem rolling is pre-processed and rolled using a rolling roll having a predetermined material and a surface profile, and then cold tandem rolling is performed. Was found to be effective.
【００１０】前述した特開平２−169108号公報に例示さ
れる、鋼系のクロス目研磨ロールを用いて潤滑油を供給
しつつ予備処理圧延すると、材質が鋼系であることに起
因して、圧延時のロール偏平が大きく、油膜が厚くな
る。このために、鋼系のクロス目研磨ロールでは、十分
にショット目を平滑化できない上、圧延油を供給しても
研磨目の磨耗が早く長期の使用には耐えない。そこで、
発明者らは、ロール（ロールのバレル部）の材質をＷＣ
系超硬合金とすることとした。一方、圧延用ロールは、
一般に、圧延に適用される前に、ロールを軸心周りに回
転させ、ロールの表面に砥石を当てて表面研磨される。
このため、一般のロール（ロールのバレル部）の表面プ
ロフィールは、研磨目が円周方向に付与されたものとな
る。従って、ＷＣ系超硬合金を素材とする、このような
ロールを用いて予備処理圧延すると、研磨目と圧延方向
とが同じであるため、研磨目が鋼板表面に転写されるこ
とになる。このときに、無潤滑で予備処理圧延すると、
圧下率が高いほど、ショット目は減少するものの、研磨
目が深く鋼帯表面に転写されてしまう。[0010] When the pre-treatment rolling is performed while supplying lubricating oil using a steel-based cross-meshing polishing roll as exemplified in the above-mentioned Japanese Patent Application Laid-Open No. 2-169108, the material is steel-based. Roll flatness during rolling is large, and the oil film becomes thick. For this reason, with a steel-based cross-grain polishing roll, the shots cannot be sufficiently smoothed, and even if the rolling oil is supplied, the abrasions are worn quickly and cannot withstand long-term use. Therefore,
The inventors set the material of the roll (barrel of the roll) to WC
Based cemented carbide. On the other hand, the roll for rolling is
Generally, before being applied to rolling, a roll is rotated around an axis and a surface of the roll is polished with a grindstone.
For this reason, the surface profile of a general roll (the barrel portion of the roll) is such that a polishing line is provided in the circumferential direction. Therefore, when pre-treatment rolling is performed using such a roll made of a WC cemented carbide, the polished stitch is transferred to the surface of the steel sheet because the polished stitch and the rolling direction are the same. At this time, if pre-treatment rolling without lubrication,
The higher the rolling reduction, the smaller the number of shots but the deeper the polished eyes are transferred to the steel strip surface.
【００１１】そこで、発明者らは、このＷＣ系超硬合金
製のロールの研磨目を、図１に示すような、ロールの円
周方向を挟んでほぼ等しい角度で傾けたクロス目（編み
目）状とした。そして、このロールを用いて圧延したと
ころ、鋼帯表面に研磨目が転写することを防げられるば
かりか、ロールと鋼帯の圧延方向での相対滑りにより、
研磨目が鋼帯表面を平滑化するように作用することがわ
かった。これにより、冷間タンデム圧延した後の最終製
品の光沢は、著しく向上し、しかも長期間安定して持続
することがわかった。Therefore, the inventors of the present invention have proposed a cross stitch (a stitch) in which the polished stitches of the WC cemented carbide roll are inclined at substantially equal angles with respect to the circumferential direction of the roll as shown in FIG. Shape. And when rolled using this roll, not only is it possible to prevent the abrasive grain from being transferred to the surface of the steel strip, but also by the relative sliding of the roll and the steel strip in the rolling direction,
It was found that the polished eyes acted to smooth the steel strip surface. As a result, it was found that the gloss of the final product after cold tandem rolling was remarkably improved, and was stable for a long time.
【００１２】ロール材質をＷＣ系超硬合金とする部位
は、少なくともバレルの外周部とする必要がある。そし
て、このロールを経済的に生産するには、バレル部の構
造が、外層の材料をＷＣ系超硬合金とし、内層の材料を
鋼系合金とした、複合層で形成されたものであることが
望ましい。また、ロ−ルのバレル部が複合層からなる場
合には、外層である超硬合金スリーブの厚みは、ロール
半径の３％以上とすることが望ましい。なお、超硬合金
としては、ＷＣにCo、Ni、Cr、Tiなどを添加したＷＣ系
超硬合金が好適であり、なかでもCoを添加したものがよ
り好ましい。このように、ロールの材質をＷＣ系超硬合
金とすることにより、ロール偏平は鋼系ロールに比べて
小さくなり、油膜が薄くなって、ショット目の平滑化が
十分に図られる。また、ＷＣ系超硬合金は耐磨耗性に優
れるので、ロールの表面粗さを長期間維持でき、オース
テナイト系ステンレス鋼帯の粒界浸食溝も十分に低減で
きる。It is necessary that the portion where the roll material is made of WC cemented carbide is at least the outer peripheral portion of the barrel. To produce this roll economically, the barrel structure must be formed of a composite layer in which the outer layer is made of a WC-based cemented carbide and the inner layer is made of a steel-based alloy. Is desirable. When the barrel portion of the roll is composed of a composite layer, the thickness of the cemented carbide sleeve as the outer layer is desirably 3% or more of the radius of the roll. As the cemented carbide, a WC-based cemented carbide obtained by adding Co, Ni, Cr, Ti and the like to WC is preferable, and among them, an alloy containing Co is more preferable. In this way, by using a WC-based cemented carbide as the material of the roll, the flatness of the roll becomes smaller than that of the steel-based roll, the oil film becomes thinner, and the shots can be smoothed sufficiently. Further, since the WC cemented carbide is excellent in wear resistance, the surface roughness of the roll can be maintained for a long time, and the grain boundary erosion groove of the austenitic stainless steel strip can be sufficiently reduced.
【００１３】また、研磨目を構成する溝は、バレル部の
周面に、円周方向を挟んで両側にそれぞれ0.5 〜90°未
満のほぼ等しい角度で傾斜した溝をクロス目（編み目）
状に形成したものがよい。このように傾斜角度は、円周
方向（圧延方向）から僅かな角度で傾斜していれば効果
が現れる。ただし、前記範囲の傾斜角度の中でも、より
優れた効果を発揮させるためには、５〜85°の範囲に加
工するのが望ましい。というのは、円周方向に傾斜した
研磨目を付与する方法として、例えば、特開平５−2536
04号公報に記載のラッピング研磨による方法、あるいは
ロールの回転速度と砥石の送り速度の関係から研磨目を
斜めに付与する方法などがあるが、いずれの方法によっ
ても、円周方向に対してほぼ対称でかつ編み目（クロス
目) 状をなす研磨目を付与するには、少なくとも周方向
に対して５°以上傾斜させると良いことを把握した。５
°未満の角度では、研磨条件の設定が微妙となり、周方
向研磨と同じとなってしまったり、クロス目を形成でき
ないなど、研磨が困難になるからである。軸方向におい
ても同様なことが言え、85°以上の角度ではクロス目を
形成するのが困難になる。The grooves forming the polished stitches are formed by forming grooves inclined at substantially equal angles of less than 0.5 to 90 ° on both sides with respect to the circumferential direction on the peripheral surface of the barrel portion.
What is formed in the shape is good. As described above, if the inclination angle is inclined at a small angle from the circumferential direction (rolling direction), the effect is exhibited. However, in order to exhibit more excellent effects even in the range of the inclination angle in the above range, it is desirable to process in the range of 5 to 85 °. This is because, as a method of giving a polishing grain inclined in the circumferential direction, for example, Japanese Patent Laid-Open No. 5-2536
There is a method by lapping polishing described in Japanese Patent Publication No. 04, or a method of obliquely giving a polishing eye from the relationship between the rotation speed of the roll and the feed speed of the grinding wheel, but by any method, almost in the circumferential direction It has been found that it is preferable to incline at least 5 ° or more with respect to the circumferential direction in order to provide a symmetric and stitch (cross stitch) polishing stitch. 5
If the angle is less than °, the setting of the polishing conditions becomes delicate, and the polishing becomes difficult, for example, the same as in the circumferential direction polishing, or the cross stitch cannot be formed. The same can be said for the axial direction. At an angle of 85 ° or more, it becomes difficult to form cross eyes.
【００１４】ここに、円周方向に対して所定範囲の角度
をなして傾斜した片側の研磨目は、全てが平行である必
要はないが、鋼帯の蛇行を防ぐ上から、その平均的な傾
斜角度が、円周方向を挟んで反対側に傾斜した研磨目と
ほぼ等しいこと、すなわち、円周方向に対して対称的で
あることが必要がある。なお、研磨目は必ずしも連続的
である必要はなく、製造性の上では、むしろ断続的であ
るほうが好ましい。ロール表面の研磨目は、例えば、回
転砥石や遊離砥粒などによる研磨、研削バイトによる研
削、あるいはエッチングなどいかなる加工方法で付与さ
れたものでもよい。Here, it is not necessary that all of the polished stitches on one side inclined at an angle within a predetermined range with respect to the circumferential direction are parallel to each other. It is necessary that the angle of inclination is substantially equal to the polishing angle inclined to the opposite side with respect to the circumferential direction, that is, it is necessary to be symmetric with respect to the circumferential direction. It should be noted that the polishing lines need not always be continuous, and it is preferable that the polishing lines be intermittent in terms of manufacturability. The polishing surface of the roll surface may be provided by any processing method such as polishing with a rotary grindstone or loose abrasive, grinding with a grinding tool, or etching.
【００１５】発明者等は、さらにロール周面の表面粗さ
を適正範囲に調整することも重要であることを突き止め
た。すなわち、バレル部の周面において、ロールの軸方
向または円周方向に測定した表面粗さがＲａ＝0.05〜3.
0 μｍ、好ましくは0.5 〜2.0 μｍであるか、Ｒmax ＝
0.2 〜30μｍ、好ましくは 0.3〜2.0 μｍであればよ
い。この場合、研磨目が円周方向に対して45°以下なら
ロール軸方向に、45°以上ならロール周方向に測定すれ
ばよい。このようにして測定した表面粗さがＲａ＝0.05
未満、またはＲmax ＝0.2 μｍ未満の場合には、ロール
粗度が低くて十分な平滑化効果が得られなくなり、Ｒａ
＝3.0 μｍ超え、またはＲmax ＝30μｍ超えの場合に
は、上記のいかなる方法によっても安定した研磨目の付
与が難しい上、ロール表面が欠け落ちることがある。な
お、研磨目の粗さ範囲の下で、研磨目の山または溝のピ
ッチは数10〜300 μｍとするのが望ましい。The inventors have further found that it is also important to adjust the surface roughness of the roll peripheral surface to an appropriate range. That is, on the peripheral surface of the barrel portion, the surface roughness measured in the axial direction or circumferential direction of the roll is Ra = 0.05 to 3.
0 μm, preferably 0.5-2.0 μm, or Rmax =
The thickness may be 0.2 to 30 μm, preferably 0.3 to 2.0 μm. In this case, the measurement may be performed in the roll axis direction when the polishing depth is 45 ° or less with respect to the circumferential direction, and in the roll circumferential direction when the polishing depth is 45 ° or more with respect to the circumferential direction. The surface roughness thus measured is Ra = 0.05.
If Rmax is less than 0.2 μm, the roll roughness is so low that a sufficient smoothing effect cannot be obtained.
If it exceeds 3.0 .mu.m or if Rmax exceeds 30 .mu.m, it is difficult to provide a stable polishing grain by any of the above methods, and the roll surface may be chipped off. It is desirable that the pitch of the peaks or grooves be within a range of several tens to 300 μm within the range of the roughness of the polishing line.
【００１６】以上説明した材質と表面プロフィールを満
たすバレルからなるロールを用いて予備処理圧延するの
であるが、このときの予備処理圧延圧下率は５〜30％の
範囲で行うことが望ましい。Pre-treatment rolling is performed using a roll made of a barrel that satisfies the above-described material and surface profile. The pre-treatment rolling reduction at this time is preferably in the range of 5 to 30%.
【００１７】本発明によって上述した効果がもたらされ
る理由は次のように考えられる。すなわち、ロールによ
る鋼帯の予備処理圧延で、ロールバイト内において、ロ
ール表面が圧延方向に一定の速度で移動するのに対し
て、鋼帯の移動速度は入側ではロール表面より遅く、出
側ではロール表面より早くなる。このため、ロールバイ
ト内ではロール表面と鋼帯表面は圧延方向に相対的に滑
ることになる。このとき、研磨目が圧延方向に対して傾
いていると、研磨目の凸部が鋼帯表面に接触したまま鋼
帯表面を相対的に移動するので、移動した部分の鋼帯表
面はせん断変形により平滑になり、ショット目や粒界浸
食溝を低減できるのである。特に、予備処理圧延の圧下
率が10％程度以上になると、鋼帯とロールとの圧延方向
相対滑り量が数ｍｍとなり、研磨目のピッチが数10μｍ
〜300 μｍ程度であれば、ほぼ鋼帯全面を平滑にするこ
とができる。The reason why the above-described effects are brought about by the present invention is considered as follows. That is, in the pre-treatment rolling of the steel strip by the roll, the roll surface moves at a constant speed in the rolling direction in the roll bite, whereas the moving speed of the steel strip is slower on the input side than on the roll surface, and on the output side. Then it is faster than the roll surface. Therefore, the roll surface and the steel strip surface slide relatively in the rolling direction in the roll bite. At this time, if the polishing line is inclined with respect to the rolling direction, the convex portion of the polishing line relatively moves on the steel band surface while being in contact with the steel band surface. Thus, shots and grain boundary erosion grooves can be reduced. In particular, when the rolling reduction of the pretreatment rolling is about 10% or more, the relative sliding amount between the steel strip and the roll in the rolling direction becomes several mm, and the pitch of the polished mesh is several tens μm.
If the thickness is about 300 μm, almost the entire surface of the steel strip can be smoothed.
【００１８】また、この平滑化作用は、鋼帯表面を主と
してせん断変形させることによるものであるから、本発
明によって予備処理圧延を施すと、鋼帯表面のみが加工
硬化して、予備処理工程後の冷間圧延工程におけるオイ
ルピットの生成やスクラッチの転写を、極く少なくかつ
浅いものにする効果があることもわかった。Further, since this smoothing action is mainly caused by shear deformation of the surface of the steel strip, when pre-treatment rolling is performed according to the present invention, only the surface of the steel strip is work-hardened, and after the pre-treatment step, It was also found that the formation of oil pits and the transfer of scratches in the cold rolling step were extremely small and shallow.
【００１９】[0019]
【実施例】以下、実施例に基づいて説明する。熱間圧延
後、焼鈍、ショットブラストによるデスケーリング（機
械的な表面酸化膜の破砕）および酸洗を行った、板厚4.
0 ｍｍのＳＵＳ４３０，ＳＵＳ３０４ステンレス熱延鋼
帯を、酸洗設備の直後に設置した図２に示す１スタンド
の圧延機にて圧下率10％の予備処理圧延を行った。この
ステンレス予備処理鋼帯を、ロール径 600ｍｍで、４段
ミル５スタンドのタンデム圧延機にて１００コイルづつ
冷間圧延（圧下率は予備処理圧延との合計圧下率で50
％）し、次いで仕上げ焼鈍と酸洗を行った後、調質圧
延、ＳＵＳ３０４についてはさらに１パスのバフ研磨を
行った。Embodiments will be described below with reference to embodiments. After hot rolling, annealing, descaling by shot blasting (mechanical crushing of surface oxide film) and pickling were performed.
The 0 mm SUS430 and SUS304 stainless hot rolled steel strips were subjected to pretreatment rolling at a rolling reduction of 10% by a one-stand rolling mill shown in FIG. 2 installed immediately after the pickling equipment. The stainless pre-treated steel strip was cold-rolled by 100 coils at a roll diameter of 600 mm in a tandem rolling mill of four-stage mill and five stands (reduction rate was 50% in total reduction rate with pre-treatment rolling).
%), Followed by finish annealing and pickling, followed by temper rolling, and SUS304 was further buffed by one pass.
【００２０】上記予備処理圧延機は、図２において、上
下一対のワークロール２、バックアップロール３からな
るものである。予備処理圧延のワークロールは、Co20wt
％を含むＷＣ系超硬合金からなるスリーブ（スリーブ
厚：ロール半径の５％）を、鋼芯材に嵌合した複合ロー
ルである。また、予備処理圧延に用いたワークロールに
は、表１に示すように、バレル部の材質と表面プロフィ
ール（研磨目のロールの周方向からの角度と、ＪＩＳ
Ｂ０６０１にしたがい、研磨目と45°以下なら軸方向
に、45°以上なら周方向に測定したロール周面の表面粗
さ）を種々に組合せたものを用いた。冷間タンデム圧延
に用いた各スタンドのロール径とロールの表面粗さは、
それぞれ、＃１〜＃４が、600 ｍｍでＲa 0.25μｍ、＃
５が、600 ｍｍでＲa 0.1 μｍとした。また、圧延油の
粘度は40 cSt／50℃、濃度は５％とし、圧延速度は400
ｍ／min とした。なお、調質圧延は、ロール径 600ｍ
ｍ、Ｒa ＝0.03μｍの鏡面ロールによるドライ圧延で、
またバフ研磨は、＃400 のバフ砥石による１パス研磨で
行った。The pre-treatment rolling mill shown in FIG. 2 comprises a pair of upper and lower work rolls 2 and a backup roll 3. Work roll for pre-treatment rolling is Co20wt
% Is a composite roll in which a sleeve (sleeve thickness: 5% of the roll radius) made of a WC-based cemented carbide containing 0.1% is fitted to a steel core material. Further, as shown in Table 1, the work roll used for the pre-treatment rolling had the material and surface profile of the barrel portion (the angle from the circumferential direction of the roll of the polished eye, JIS).
According to B0601, various combinations of polishing grain and surface roughness of the roll peripheral surface measured in the axial direction when it is 45 ° or less and in the circumferential direction when it is 45 ° or more) were used. The roll diameter and roll surface roughness of each stand used for cold tandem rolling are as follows:
# 1 to # 4 are Ra 0.25 μm at 600 mm,
5, 600 mm and Ra 0.1 μm. The viscosity of the rolling oil is 40 cSt / 50 ° C, the concentration is 5%, and the rolling speed is 400
m / min. In addition, temper rolling, roll diameter 600m
m, Ra = 0.03 μm by dry rolling with a mirror roll,
The buffing was performed by one-pass polishing using a # 400 buffing wheel.
【００２１】[0021]
【表１】 [Table 1]
【００２２】こうにして得られたステンレス冷延鋼帯に
ついて、それぞれＪＩＳ Ｚ８７４１光沢度測定方法
（Ｇｓ２０°）にしたがい光沢度を測定し、１コイル
目、１０コイル目、５０コイル目及び１００コイル目で
相互に比較した。測定した結果を表１に併せて示す。The stainless steel cold-rolled steel strip thus obtained was measured for glossiness in accordance with JIS Z8741 glossiness measurement method (Gs20 °), and the first coil, the tenth coil, the 50th coil, and the 100th coil were measured. Were compared with each other. Table 1 also shows the measurement results.
【００２３】表１に示した結果からわかるように、本発
明に従って、材質をＷＣ系超硬合金とし、周面に所定の
クロス目を付与したワークロールで予備処理圧延すれ
ば、その後のタンデム冷間圧延を含む一連の工程を経て
製造されたステンレス鋼帯の光沢を著しく高めることが
できる。特に、ＷＣ系超硬合金ロールでは、鋼系ロール
を用いた場合に比較して、潤滑油を供給した場合にも油
膜が薄くなって優れた光沢改善効果が得られ、しかも磨
耗が少ないので、圧延距離に対する効果の低下が少な
く、長期間にわたって持続することがわかる。本発明で
得られた効果は、前述したような、ＷＣ系超硬合金ロー
ルの圧延時における鋼帯表面の平滑化作用、加工硬化作
用によるものであると考えられる。そして、ステンレス
鋼帯の光沢に不利な、大径ロール及び高粘度圧延油を用
いた高速タンデム冷間圧延を施しても、最終鋼帯製品の
光沢を長時間にわたって良好に維持することが可能にな
る。As can be seen from the results shown in Table 1, according to the present invention, if the material is made of WC cemented carbide and pre-processed and rolled by a work roll having a predetermined cross-cut on the peripheral surface, the subsequent tandem cooling The gloss of the stainless steel strip produced through a series of steps including hot rolling can be significantly increased. In particular, in the case of a WC-based cemented carbide roll, compared with the case of using a steel-based roll, even when lubricating oil is supplied, the oil film is thinned, and an excellent gloss improving effect is obtained, and the wear is small. It can be seen that the effect on the rolling distance does not decrease much and lasts for a long time. It is considered that the effects obtained in the present invention are due to the smoothing action and the work hardening action of the steel strip surface during rolling of the WC cemented carbide roll as described above. Even if high-speed tandem cold rolling using a large-diameter roll and high-viscosity rolling oil, which is disadvantageous to the gloss of the stainless steel strip, is performed, the gloss of the final steel strip product can be maintained well for a long time. Become.
【００２４】[0024]
【発明の効果】以上説明したように、本発明による予備
処理圧延を行えば、従来、ステンレス冷延鋼帯の光沢に
不利であった冷間タンデム圧延を行っても、優れた光沢
を有する冷延製品を製造することが可能になる。しか
も、本発明によれば、ロールの磨耗が少ないので、上記
効果が長時間安定して維持可能となる。したがって、本
発明によれば、多大な設備投資を必要とすることなく、
光沢が優れたステンレス冷延鋼帯を、効率的に、安価に
提供することが可能になる。As described above, by performing the pretreatment rolling according to the present invention, even if cold tandem rolling, which was conventionally disadvantageous to the gloss of a cold rolled stainless steel strip, is performed, a cold roll having excellent gloss can be obtained. It is possible to manufacture rolled products. In addition, according to the present invention, the above effects can be stably maintained for a long time because the roll is less worn. Therefore, according to the present invention, without requiring a large capital investment,
It is possible to efficiently provide a cold rolled stainless steel strip with excellent gloss at low cost.
【図１】本発明に用いるロールのバレル部表面の研磨目
を示す図である。FIG. 1 is a view showing a polished surface of a barrel portion surface of a roll used in the present invention.
【図２】本発明の予備処理圧延に適用した圧延機を示す
図である。FIG. 2 is a diagram showing a rolling mill applied to pretreatment rolling of the present invention.
１ 被圧延材 ２ ワークロール ３ バックアップロール ４ クーラントノズル ５ クーラント（圧延油） DESCRIPTION OF SYMBOLS 1 Rolled material 2 Work roll 3 Backup roll 4 Coolant nozzle 5 Coolant (rolling oil)
───────────────────────────────────────────────────── フロントページの続き (72)発明者 剣持 一仁 千葉県千葉市中央区川崎町１番地 川崎製 鉄株式会社技術研究所内 (72)発明者 永井 肇 千葉県千葉市中央区川崎町１番地 川崎製 鉄株式会社千葉製鉄所内 (72)発明者 砂盛 泰理 千葉県千葉市中央区川崎町１番地 川崎製 鉄株式会社千葉製鉄所内 ──────────────────────────────────────────────────続 き Continuing from the front page (72) Kazuhito Kenmochi 1 Kawasaki-cho, Chuo-ku, Chiba-city, Chiba Prefecture Inside the Technical Research Institute of Kawasaki Steel Co., Ltd. (72) Hajime Nagai 1-1 Kawasaki-cho, Chuo-ku, Chiba-shi, Chiba Kawasaki Steel Co., Ltd.Chiba Works (72) Inventor Yasushi Yamori 1 Kawasaki-cho, Chuo-ku, Chiba City, Chiba Prefecture Kawasaki Steel Co., Ltd.Chiba Works
Claims (5)
酸洗を施し、その後、バレル部の少なくとも周面の材料
をＷＣ系超硬合金とし、かつ前記バレル部の周面に、円
周方向を挟んで両側にそれぞれ0.5 〜90°未満のほぼ等
しい角度で傾斜した研摩目を設けた、ワークロールを用
いて圧延することを特徴とする冷間圧延用ステンレス予
備処理鋼帯の製造方法。1. A hot rolled stainless steel strip is annealed,
After pickling, the material of at least the peripheral surface of the barrel portion is made of a WC cemented carbide, and the peripheral surface of the barrel portion is substantially equal to each other on both sides with respect to the circumferential direction at an angle of less than 0.5 to 90 °. A method for producing a stainless steel pretreated steel strip for cold rolling, characterized in that it is rolled using a work roll provided with a slanted polishing grain.
酸洗を施し、その後、バレル部の少なくとも周面の材料
をＷＣ系超硬合金とし、かつ前記バレル部の周面に、円
周方向を挟んで両側にそれぞれ５〜85°のほぼ等しい角
度で傾斜した研摩目を設けた、ワークロールを用いて圧
延することを特徴とする冷間圧延用ステンレス予備処理
鋼帯の製造方法。2. A hot rolled stainless steel strip is annealed,
After pickling, the material of at least the peripheral surface of the barrel portion is made of WC cemented carbide, and on the peripheral surface of the barrel portion, on both sides with respect to the circumferential direction, at approximately the same angle of 5 to 85 °. A method for producing a cold-rolled stainless steel pretreated steel strip, characterized by rolling using a work roll provided with inclined polishing lines.
ル部が、外層の材料をＷＣ系超硬合金とし、内層の材料
を鋼系合金とする複合層で形成された、ワークロールを
用いて圧延することを特徴とする冷間圧延用ステンレス
予備処理鋼帯の製造方法。3. The work roll according to claim 1, wherein the barrel portion is formed of a composite layer in which the material of the outer layer is a WC cemented carbide and the material of the inner layer is a steel alloy. A method for producing a stainless steel pretreated steel strip for cold rolling, characterized by rolling.
粗さがＲａ＝0.05〜3.0 μｍである、ワークロールを用
いて圧延することを特徴とする請求項１〜３のいずれか
１項に記載の冷間圧延用ステンレス予備処理鋼帯の製造
方法。4. The rolling method according to claim 1, wherein the surface of the barrel portion is rolled using a work roll having a surface roughness of Ra = 0.05 to 3.0 μm. 3. The method for producing a stainless steel pretreated steel strip for cold rolling according to item 1.
粗さがＲmax ＝0.2〜30μｍである、ワークロールを用
いて圧延することを特徴とする請求項１〜３のいずれか
１項に記載の冷間圧延用ステンレス予備処理鋼帯の製造
方法。5. The rolling method according to claim 1, wherein the peripheral surface of the barrel portion is rolled using a work roll having a surface roughness Rmax of 0.2 to 30 μm. A method for producing the pretreated stainless steel strip for cold rolling according to the above.