JPH11273932A - Colored magnetic powder and method of judging genuine product - Google Patents
Colored magnetic powder and method of judging genuine productInfo
- Publication number
- JPH11273932A JPH11273932A JP9271598A JP9271598A JPH11273932A JP H11273932 A JPH11273932 A JP H11273932A JP 9271598 A JP9271598 A JP 9271598A JP 9271598 A JP9271598 A JP 9271598A JP H11273932 A JPH11273932 A JP H11273932A
- Authority
- JP
- Japan
- Prior art keywords
- magnetic powder
- colored
- powder
- mica
- color
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は有色磁性粉体及び真
性品判定方法、特にその色調及び磁性の改良に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a colored magnetic powder and a method for judging a genuine product, and more particularly to an improvement in color tone and magnetism.
【０００２】[0002]
【従来の技術】近年、顔料或いは磁性粉体などにも単に
色調、或いは磁性といった単純な機能に加え、各種機能
が要求されている。例えば金券類、証明書などには、カ
ラーコピーなどによる複写・偽造が困難な顔料が要求さ
れ、またクレジットカード、キャッシュカード或いは自
動改札用乗車券には情報記録用或いは磁気シールド用磁
性粉体が用いられるが、これらは通常黒色ないし茶色で
意匠性に欠けるため、各種色調の磁性粉体が要求されて
いる。2. Description of the Related Art In recent years, pigments or magnetic powders have been required to have various functions in addition to simple functions such as color tone or magnetism. For example, cash vouchers, certificates, etc., require pigments that are difficult to copy / counterfeit by color copying, and credit cards, cash cards, or tickets for automatic ticket gates use magnetic powder for information recording or magnetic shielding. Although they are used, they are usually black or brown and lack designability, so that magnetic powders of various colors are required.
【０００３】これらの要求に答えるものとして、前者の
複写・偽造を困難にするため、ホログラムの形成、或い
は顔料の塗布パターンに改良を加える（特開平９−２０
０６３）などの手段がとられ、また後者の磁性粉体に意
匠性を付与するために、金属酸化物表面に透明な金属酸
化物皮膜を形成する（特開平２−１２２４１９）などの
手段がとられていた。In order to meet these demands, in order to make copying and counterfeiting of the former difficult, improvements have been made in the formation of holograms or in the application patterns of pigments (JP-A-9-20).
063), and a method of forming a transparent metal oxide film on the metal oxide surface in order to impart design properties to the latter magnetic powder (Japanese Patent Application Laid-Open No. 2-122419). Had been.
【０００４】[0004]
【発明が解決しようとする課題】しかしながら、これら
のいずれの手段も、それぞれの要求を充分に満たすもの
ではなかった。すなわち、複写・偽造を困難にするため
のホログラムの形成にはその製造、準備に多額の費用が
かかり、また塗布パターンなどはコピー機の進歩との相
関を考慮する必要があり、さらにコンピュータグラフィ
ックス処理などを施せば複製は可能であり、偽造の防止
には充分な効果を発揮し得ない。However, none of these means has sufficiently satisfied the respective requirements. In other words, the production and preparation of holograms that make copying and counterfeiting difficult is very costly, and the application pattern must take into account the correlation with the progress of copiers. Copying is possible if processing is performed, and it cannot exert a sufficient effect for preventing forgery.
【０００５】一方、前記磁性粉体に意匠性を付与するた
めの金属酸化物皮膜形成などの手段によっては充分に鮮
明な色調を調整することが困難であり、しかも磁性体の
上に非磁性物を被覆するため、磁性体の存在量に比較し
て磁性が充分に発揮され難いという課題があった。本発
明は前記従来技術の課題に鑑みなされたものであり、そ
の目的は優れた色調及び磁性を有する有色磁性粉体、及
び真性品と複製品の判定が容易な真性品判定方法を提供
することにある。On the other hand, it is difficult to adjust a sufficiently clear color tone by means such as forming a metal oxide film for imparting a design property to the magnetic powder. There is a problem that it is difficult to sufficiently exhibit magnetism as compared with the amount of the magnetic substance. SUMMARY OF THE INVENTION The present invention has been made in view of the problems of the related art, and an object of the present invention is to provide a colored magnetic powder having excellent color tone and magnetism, and a method for determining an authentic product and an authentic product that can easily determine a duplicate product. It is in.
【０００６】[0006]
【課題を解決するための手段】前記目的を達成するため
に本発明者らが鋭意検討を行ったところ、フェライト被
覆雲母チタンに優れた色調及び磁性が認められることを
見いだし、本発明を完成するに至った。すなわち、本発
明にかかる有色磁性粉体は、雲母基板上に二酸化チタン
層が形成され、さらにその上に二価金属種が鉄以外のフ
ェライト層が形成され、前記二酸化チタン層及びフェラ
イト層により生成する干渉色を強調して外観色として看
取し得ることを特徴とする。Means for Solving the Problems The inventors of the present invention have conducted intensive studies to achieve the above object, and have found that ferrite-coated titanium mica has excellent color tone and magnetism, thereby completing the present invention. Reached. That is, in the colored magnetic powder according to the present invention, a titanium dioxide layer is formed on a mica substrate, and a ferrite layer other than iron is formed on the mica substrate, and the divalent metal species is formed by the titanium dioxide layer and the ferrite layer. It is characterized in that the interference color is emphasized and can be viewed as an appearance color.
【０００７】また、本発明の粉体の、二価金属種はコバ
ルト及び／又はマンガンであることが好適である。ま
た、本発明の粉体において、フェライトの被覆量が、雲
母に対し５〜２８０重量％であることが好適である。ま
た、本発明にかかる真性品判定方法は、干渉色が強調さ
れて所定の色調を呈する有色磁性粉体を被塗装体に塗布
し、その拡散反射及び正反射で測色した場合の測色値の
比が所定範囲となり、かつ該塗布域に磁性があるか否か
により塗装体が真性品であるか否かを判定することを特
徴とする。[0007] The divalent metal species of the powder of the present invention is preferably cobalt and / or manganese. Further, in the powder of the present invention, the coating amount of ferrite is preferably 5 to 280% by weight based on mica. In addition, the intrinsic product determination method according to the present invention is a method of measuring a colorimetric value obtained by applying a colored magnetic powder exhibiting a predetermined color tone by emphasizing an interference color to an object to be coated and measuring the color by diffuse reflection and specular reflection. Is determined in a predetermined range, and whether or not the coated body is a genuine product is determined based on whether or not the coating area has magnetism.
【０００８】また、本発明にかかる他の真性品判定方法
は、干渉色が強調されて所定の色調を呈する有色磁性粉
体を被塗装体に所定の意匠形状に塗布し、且つその塗布
域に磁気情報を付加し、意匠形状及び磁気情報の両者に
より塗装体が真性品であるか否かを判定することを特徴
とする。また、本発明にかかる方法において、干渉色に
由来する略同色の色調を呈する有色磁性粉体と有色非磁
性粉体をもちいて意匠形状を形成し、かつ前記有色磁性
粉体は有色非磁性粉体を用いて描かれた意匠形状とは異
なる磁気透かし形状で前記意匠形状内に塗布されること
が好適である。[0008] Further, another method of judging genuine products according to the present invention is to apply a colored magnetic powder exhibiting a predetermined color tone by emphasizing an interference color to an object to be coated in a predetermined design shape, and to apply it to the coating area. It is characterized in that magnetic information is added, and it is determined whether or not the painted body is a genuine product based on both the design shape and the magnetic information. Further, in the method according to the present invention, a design shape is formed using a colored magnetic powder and a colored non-magnetic powder exhibiting substantially the same color tone derived from the interference color, and the colored magnetic powder is a colored non-magnetic powder. It is preferable that a magnetic watermark shape different from the design shape drawn using the body is applied in the design shape.
【０００９】また、本発明にかかる方法において、干渉
色に由来する色調を呈する有色磁性粉体と、有色非磁性
粉体とをもちいて意匠形状を形成し、かつ前記有色磁性
粉体は前記有色非磁性粉体で描かれる意匠形状の一部を
構成することが好適である。また、本発明にかかる方法
において、有色磁性粉体は前記二価金属種が鉄以外のフ
ェライト層を有する粉体であることが好適である。Further, in the method according to the present invention, a design shape is formed using a colored magnetic powder exhibiting a color tone derived from an interference color and a colored non-magnetic powder, and the colored magnetic powder is formed of the colored magnetic powder. It is preferable to constitute a part of the design shape drawn by the nonmagnetic powder. In the method according to the present invention, it is preferable that the colored magnetic powder is a powder in which the divalent metal species has a ferrite layer other than iron.
【００１０】また、本発明にかかる方法において、意匠
形状の形成域は明度７０以下の被塗装体上にあることが
好適である。なお、ここでいう塗布或いは塗装とは、例
えばフィルム上などに塗布を行い、それを被塗装体に貼
着する、或いは転写するなどの手段も含む概念である。Further, in the method according to the present invention, it is preferable that the formation area of the design shape is on an object to be coated having a brightness of 70 or less. The term “coating or painting” as used herein is a concept that includes, for example, means for applying on a film or the like and sticking or transferring it on a body to be coated.
【００１１】[0011]
【発明の実施の形態】以下、本発明の構成をさらに詳細
に説明する。本発明において粉体の基板として用いられ
る雲母はどのようなものではよく、一般には市販の白雲
母系雲母（muscovite mica）を用いるが、場合によって
は黒雲母などを用いることも可能である。粒径は特に制
限されないが、干渉色を良好に生成するためには一般市
販の雲母（粒径１〜５０μ程度）の中でも粒径が小さく
粒子形状ができるだけ扁平なものが美しい色調と真珠光
沢が発揮されやすいため、好ましい。BEST MODE FOR CARRYING OUT THE INVENTION Hereinafter, the structure of the present invention will be described in more detail. The mica used as the substrate for the powder in the present invention may be of any type. Generally, commercially available muscovite mica is used, but in some cases biotite may be used. Although the particle size is not particularly limited, in order to produce interference colors favorably, among the commercially available mica (particle size of about 1 to 50 μm), those having a small particle size and as flat as possible the particle shape have a beautiful color tone and pearl luster. It is preferable because it is easily exhibited.
【００１２】そして、本発明においては、例えばチタン
の無機酸塩水溶液を雲母の存在下で加水分解し、雲母粒
子表面に二酸化チタンを析出させ、さらに５００℃〜１
０００℃で焼成することにより、二酸化チタン被覆雲母
を形成することができる。本発明において、これら二酸
化チタンの雲母に対する被覆量は、雲母１００重量部に
対して、好ましくは３５〜２２０重量部、さらに好まし
くは１００〜１９０重量部である。被覆量が３５重量部
よりも少ない場合には十分な彩度を得ることができない
場合があり、また２２０重量部よりも多い場合には二酸
化チタンそのものの色に近くなる傾向にある。以上のよ
うにして二酸化チタン被覆雲母を形成した後、フェライ
ト層を形成する。In the present invention, for example, an aqueous solution of an inorganic acid salt of titanium is hydrolyzed in the presence of mica to precipitate titanium dioxide on the surface of the mica particles.
By firing at 000 ° C., a mica coated with titanium dioxide can be formed. In the present invention, the coating amount of mica with these titanium dioxides is preferably 35 to 220 parts by weight, more preferably 100 to 190 parts by weight, based on 100 parts by weight of mica. When the coating amount is less than 35 parts by weight, sufficient saturation may not be obtained, and when it is more than 220 parts by weight, the color tends to be close to the color of titanium dioxide itself. After forming the titanium dioxide-coated mica as described above, a ferrite layer is formed.
【００１３】このフェライト層の形成方法としては、二
酸化チタン被覆雲母の分散液に鉄の無機酸塩および二価
金属種が鉄以外の金属、例えばコバルトの無機酸塩を加
え、アルカリ水溶液により中和することで水酸化鉄及び
水酸化コバルトなどを二酸化チタン被覆雲母表面へ析出
させ、その後７０〜１１０℃程度で加熱し、常法により
中和、洗浄、乾燥、必要により焼成させる方法などが好
適である。この最外層に被覆されるフェライト層は、雲
母に対して、５〜２８０重量％であることが好ましく、
さらに好ましくは９０〜２４０重量％である。この範囲
のフェライト層を形成することにより干渉色を強調する
ことができ、且つ優れた磁性を得ることができる。The ferrite layer is formed by adding an inorganic acid salt of iron and a metal other than iron, for example, an inorganic acid salt of cobalt to a dispersion of mica coated with titanium dioxide and neutralizing with an aqueous alkali solution. It is preferable that iron hydroxide, cobalt hydroxide, etc. be precipitated on the surface of the titanium dioxide-coated mica by heating, then heated at about 70 to 110 ° C., neutralized, washed, dried, and if necessary, calcined by a conventional method. is there. The ferrite layer coated on the outermost layer is preferably 5 to 280% by weight based on mica.
More preferably, it is 90 to 240% by weight. By forming the ferrite layer in this range, the interference color can be emphasized and excellent magnetism can be obtained.
【００１４】図１には本発明にかかる有色磁性粉体が模
式化されて示されており、同図に示すように、粉体１０
は、中心に雲母１２が存在し、その外周に二酸化チタン
層１４が形成され、さらにその外周にフェライト層１６
が形成されている。前記フェライト層１６は通常、黒色
ないし濃茶色を有している。ここに白色光１８が入射す
ると、フェライト層１６の表面及び雲母１２表面では屈
折率の大きな変化により反射光を生じ、フェライト層１
６での反射光２０と雲母１２表面での反射光２２の干渉
により、特定の色調の反射干渉光２４が生じる。FIG. 1 schematically shows a colored magnetic powder according to the present invention. As shown in FIG.
Has a mica 12 at the center, a titanium dioxide layer 14 formed on the outer periphery thereof, and a ferrite layer 16
Are formed. The ferrite layer 16 usually has a black to dark brown color. When the white light 18 enters here, reflected light is generated due to a large change in the refractive index on the surface of the ferrite layer 16 and the surface of the mica 12, and the ferrite layer 1
The interference between the reflected light 20 at 6 and the reflected light 22 at the surface of the mica 12 produces reflected interference light 24 having a specific color tone.
【００１５】ここで、フェライト層１６が存在しない
と、粉体１０を通過する透過光２６の割合が著しく大き
いため、塗装基板２８からの反射光３０が反射干渉光２
４に比較し著しく強くなり、粉体１０の外観色は実質的
に白色となってしまう。しかし、本発明においてはフェ
ライト層１６が光の透過量を制限しており、この結果粉
体１０の外観色は干渉光２４の色が強調されて看取され
るのである。なお、粉体１０の透過光２６が外方へ帰還
すると、該透過光は前記反射干渉光２４とは補色の関係
にある透過干渉光成分を有するため、反射干渉光２４の
色調を打ち消す作用を生じる。このため、外観色をより
明瞭に得るためには、前記透過干渉光２６を低減するこ
とが好ましい。Here, if the ferrite layer 16 does not exist, the ratio of the transmitted light 26 passing through the powder 10 is extremely large, so that the reflected light 30 from the coating substrate 28
4, and the appearance color of the powder 10 becomes substantially white. However, in the present invention, the ferrite layer 16 limits the amount of light transmission. As a result, the appearance color of the powder 10 is perceived with the color of the interference light 24 emphasized. When the transmitted light 26 of the powder 10 returns to the outside, the transmitted light has a transmission interference light component having a complementary color relationship with the reflection interference light 24, and therefore has an effect of canceling the color tone of the reflection interference light 24. Occurs. For this reason, it is preferable to reduce the transmitted interference light 26 in order to obtain a clearer appearance color.
【００１６】従って、本発明にかかる粉体が塗布される
基材は、黒色あるいは緑色、青色などの明度の低い、Ｌ
値が７０以下の色調のものが好ましい。また、本発明の
有色磁性粉体を塗布する際の組成物において、粉体の配
合量は特に限定されないが、組成物全量に対して通常５
〜３５重量％が好適である。粉体の配合量が少ないと、
隠蔽力が低下し、配合量が過剰になると組成物中で粉体
の分散が不均一になったり、組成物塗装体の外観がまだ
らになったり、組成物の粘度が上昇して作業性や印刷適
正等に好ましくない影響を及ぼすことがある。なお、本
発明において塗装される基材としては、紙、板紙、布、
皮革、金属、プラスティック等、特に限定されず、その
形状も様々なものが適用可能である。もちろん、予め塗
装、印刷、コーティング処理された基材でもよい。Therefore, the base material on which the powder according to the present invention is applied is a black, green, or blue light-
Those having a color tone of 70 or less are preferred. In addition, in the composition when the colored magnetic powder of the present invention is applied, the compounding amount of the powder is not particularly limited.
~ 35% by weight is preferred. If the amount of powder is small,
When the hiding power is reduced and the amount of the compound is excessive, the dispersion of the powder in the composition becomes uneven, or the appearance of the composition coated body becomes mottled, the viscosity of the composition increases, and the workability and This may have an undesirable effect on printability and the like. In addition, as a substrate to be coated in the present invention, paper, paperboard, cloth,
There is no particular limitation on leather, metal, plastic, and the like, and various shapes are applicable. Of course, a substrate that has been previously painted, printed, or coated may be used.
【００１７】本発明にかかる有色磁性粉体と共に配合さ
れるバインダー樹脂とは、粉体を基材上に安定に密着さ
せうる樹脂であり、粉体組成物を基材上に塗装後は該組
成物中の溶剤が揮散して粉体を包埋した状態で基材上に
被膜を形成するものである。バインダー樹脂は基材との
相性や、形成被膜被膜強度、膜厚等によって選択される
ので特に限定されないが、通常塗料や印刷インキのバイ
ンダーとして用いられているものを使用することができ
る。例えば、ギルソナイト、マレイン酸樹脂、環化ゴ
ム、硬化ロジン、石油樹脂、ニトロセルロース、アクリ
ル樹脂、ポリウレタン樹脂、塩素化ポリプロピレン、塩
化ビニル−酢酸ビニル共重合樹脂、エチレン−酢酸ビニ
ル共重合樹脂、塩化ビニル、ポリエステル樹脂、アルキ
ド樹脂、アマニ油、変性フェノール樹脂、フマル酸樹
脂、エポキシエステル樹脂、エポキシアミノ樹脂、エポ
キシフェノール樹脂、ポリエステル樹脂、ビニル樹脂、
ポリアミド樹脂、鉱油ワニス、ケトン樹脂、塩化ゴム、
エチルセルロース、尿素樹脂、メラミン樹脂等が挙げら
れる。The binder resin blended with the colored magnetic powder according to the present invention is a resin capable of stably adhering the powder to the substrate, and after the powder composition is coated on the substrate, the composition is A film is formed on a substrate in a state in which the solvent in the material is volatilized and the powder is embedded. The binder resin is not particularly limited because it is selected according to the compatibility with the base material, the strength of the formed coating film, the film thickness, and the like, but those usually used as binders for paints and printing inks can be used. For example, Gilsonite, maleic acid resin, cyclized rubber, cured rosin, petroleum resin, nitrocellulose, acrylic resin, polyurethane resin, chlorinated polypropylene, vinyl chloride-vinyl acetate copolymer resin, ethylene-vinyl acetate copolymer resin, vinyl chloride , Polyester resin, alkyd resin, linseed oil, modified phenol resin, fumaric acid resin, epoxy ester resin, epoxy amino resin, epoxy phenol resin, polyester resin, vinyl resin,
Polyamide resin, mineral oil varnish, ketone resin, chlorinated rubber,
Ethyl cellulose, urea resin, melamine resin and the like can be mentioned.
【００１８】また、本発明に係る有色磁性粉体と共に配
合される溶剤としては、一般に塗料やインキに用いられ
る溶剤を用いることが可能であり、通常バインダー樹脂
を良好に溶解して作業性を向上させ、且つこの樹脂溶液
中に有色粉体が良好に分散配合できるものであれば特に
限定されない。例えば、トルエン、キシレン、ｎ−ヘキ
サン、シクロヘキサン、酢酸メチル、酢酸エチル、酢酸
イソプロピル、酢酸ｎ−プロピル、酢酸ｎ−ブチル、酢
酸イソブチル、メタノール、エタノール、ｎ−プロピル
アルコール、イソプロピルアルコール、ｎ−ブチルアル
コール、イゾブチルアルコール、アセトン、メチルエチ
ルケトン、メチルイソブチルケトン、プロピレングリコ
ールモノメチルエーテル、エチレングリコールモノメチ
ルアセテート、エチレングリコールモノエチルエーテ
ル、エチレングリコールモノエチルエーテルアセテート
等が挙げられる。As the solvent to be mixed with the colored magnetic powder according to the present invention, a solvent generally used for paints and inks can be used, and usually, a binder resin is dissolved well to improve workability. There is no particular limitation as long as the colored powder can be dispersed and blended well in the resin solution. For example, toluene, xylene, n-hexane, cyclohexane, methyl acetate, ethyl acetate, isopropyl acetate, n-propyl acetate, n-butyl acetate, isobutyl acetate, methanol, ethanol, n-propyl alcohol, isopropyl alcohol, n-butyl alcohol Isopropyl alcohol, acetone, methyl ethyl ketone, methyl isobutyl ketone, propylene glycol monomethyl ether, ethylene glycol monomethyl acetate, ethylene glycol monoethyl ether, ethylene glycol monoethyl ether acetate, and the like.
【００１９】溶剤としては揮発性の有機溶剤が多く用い
られるが、場合によっては水等を配合しても良い。本発
明の有色磁性粉体を用いる際には、本発明の効果を損な
わない範囲であれば組成物の特性を調節するために前記
必須成分の他に通常塗料やインキに配合されている各種
添加剤を配合してもよい。例えば、可塑剤、ワックス、
湿潤剤、安定剤、染顔料、静電防止剤、消泡剤、酸化防
止剤、レベリング剤、重合禁止剤、フィラー剤等が挙げ
られる。As the solvent, a volatile organic solvent is often used, but in some cases, water or the like may be blended. When the colored magnetic powder of the present invention is used, in addition to the above essential components, various additives that are usually added to paints and inks in order to adjust the properties of the composition as long as the effects of the present invention are not impaired. You may mix | blend an agent. For example, plasticizer, wax,
Examples include wetting agents, stabilizers, dyes and pigments, antistatic agents, antifoaming agents, antioxidants, leveling agents, polymerization inhibitors, filler agents, and the like.
【００２０】本発明において、有色の高い光輝感と、優
れた色調を得るためには塗料組成物中の有色粉体とバイ
ンダー樹脂の重量比は１：２０〜３．５：１０であるこ
とが好適である。このような塗料組成物を基材上に塗装
すると、乾燥により組成物中の溶剤が揮散し、基板上に
バインダー樹脂被膜が形成され、有色粉体はこの被膜中
に保持されて、塗膜が形成される。従って、基板上の塗
膜中、有色粉体とバインダー樹脂の重量比は１：２０〜
３．５：１０の範囲に存する。このような組成比を有す
る塗膜は基板に有色の外観色及び高い光輝感を与え、且
つ良好な色調を発現する。In the present invention, the weight ratio of the colored powder to the binder resin in the coating composition is preferably from 1:20 to 3.5: 10 in order to obtain a high color brilliant feeling and an excellent color tone. It is suitable. When such a coating composition is applied on a substrate, the solvent in the composition volatilizes by drying, a binder resin film is formed on the substrate, and the colored powder is retained in the film, and the coating film is formed. It is formed. Therefore, in the coating film on the substrate, the weight ratio between the colored powder and the binder resin is 1:20 to
It is in the range of 3.5: 10. A coating film having such a composition ratio gives a colored appearance color and a high glitter to the substrate, and develops a good color tone.
【００２１】また、本発明にかかる粉体が用いられる塗
料組成物が基板上に塗装された塗装体において、乾燥後
の塗膜の幾何学的膜厚は０．０１〜０．０７ｍｍである
ことが好適である。塗膜膜厚が小さい場合には粉体によ
る外観色が希薄で隠蔽力が低く、十分な色調や光沢度が
得られない。一方、塗布膜厚が大きすぎると塗膜がうま
くのらずにまだらになることがあり、外観が不均一とな
りやすく、光沢度も低下する傾向にある。Further, in a coated body in which the coating composition using the powder according to the present invention is applied on a substrate, the geometric thickness of the dried coating film is 0.01 to 0.07 mm. Is preferred. When the thickness of the coating film is small, the appearance color of the powder is sparse, the hiding power is low, and sufficient color tone and gloss cannot be obtained. On the other hand, if the coating film thickness is too large, the coating film may be unsatisfactory and may become mottled, the appearance tends to be uneven, and the glossiness tends to decrease.
【００２２】本発明で用いられる塗装方法としては、従
来より行われている塗装方法、印刷方法、コーティング
技術を利用することができ、例えば印刷方法としては凸
板印刷、凹板印刷、グラビア印刷、スクリーン印刷、フ
レキソ印刷、オフセット印刷、インキジェット印刷、静
電印刷等が利用できる。また、はけ塗り、スプレー塗
り、転がし塗り、ステンシル塗り、静電塗り、流し塗
り、浸し塗り、ローラー塗り、吹き付け塗り等の塗装方
法も用いることができる。As the coating method used in the present invention, a conventional coating method, printing method, and coating technique can be used. Examples of the printing method include convex plate printing, concave plate printing, gravure printing, and the like. Screen printing, flexographic printing, offset printing, ink jet printing, electrostatic printing and the like can be used. Further, coating methods such as brush coating, spray coating, rolling coating, stencil coating, electrostatic coating, flow coating, dip coating, roller coating, and spray coating can also be used.
【００２３】また、本発明にかかる真性品判定方法にお
いては、例えば前記有色磁性粉体と、前記フェライト層
の代わりに低次酸化チタン層を形成した略同外観色の有
色非磁性粉体を用いることができる。そして、有色非磁
性粉体で形成した所定形状の模様中に有色磁性粉体で他
の情報を付加した形状（例えばバーコード）を描き、通
常の目視では一の模様しかみえない意匠中に磁気透かし
を設けることができる。In the method for judging genuine products according to the present invention, for example, the colored magnetic powder and the colored non-magnetic powder having substantially the same appearance and having a lower titanium oxide layer formed thereon are used in place of the ferrite layer. be able to. Then, a shape (for example, a bar code) in which other information is added with the colored magnetic powder is drawn in a pattern of a predetermined shape formed of the colored non-magnetic powder, and a magnetic pattern is formed in a design in which only one pattern can be seen by ordinary eyes. A watermark can be provided.
【００２４】さらに、有色非磁性粉体で描いた意匠の一
部に、他の色調の有色磁性粉体で模様を付加すれば、磁
気検出により一部の模様のみを浮き立たせることができ
る。もともと干渉色を強調して外観色を出した粉体で特
定の模様を形成した場合、該粉体は見る角度によって微
妙に色調の異なる、いわゆるフリップフロップ性を有し
ており、カラーコピーなどで複写をとることがきわめて
困難であり、しかもその模様の一部に磁性のみが異なる
部分が存在していた場合、その磁性情報まで複写を行う
ことは事実上不可能である。従って、これらの磁性と干
渉色に基づく色調の両者により、真性品と複写品の判別
はきわめて容易である。Further, by adding a pattern with a colored magnetic powder of another color to a part of the design drawn with the colored nonmagnetic powder, only a part of the pattern can be raised by magnetic detection. Originally, when a specific pattern was formed with a powder that gave an appearance color by emphasizing the interference color, the powder had a so-called flip-flop property in which the color tone was slightly different depending on the viewing angle, such as color copying. It is extremely difficult to make a copy, and if there is a part of the pattern that differs only in magnetism, it is practically impossible to copy the magnetic information. Therefore, it is extremely easy to discriminate a genuine product and a copied product from both the magnetism and the color tone based on the interference color.
【００２５】[0025]
【実施例】以下、本発明の好適な実施例を説明する。フェライトと磁性 本発明者らは、二酸化チタン被覆雲母上に形成するフェ
ライト層を構成する金属種と磁性の相関について検討を
行った。DESCRIPTION OF THE PREFERRED EMBODIMENTS Preferred embodiments of the present invention will be described below. Ferrite and magnetism The present inventors have examined the correlation between the metal species constituting the ferrite layer formed on the titanium dioxide-coated mica and the magnetism.
【００２６】＜被検試料の調整＞製造例１ 図２に示すような工程により粉体を調製した。すなわ
ち、５０ｇの青干渉色を有する二酸化チタン被覆雲母
（Merck社製雲母チタンIriodin221、以下、Iriodinはメ
ルク社の商標である。）を１００mlのイオン交換水に分
散し、該分散溶液に１５．２ｇのＣｏＣｌ2・６Ｈ2Ｏと
３４．６ｇのＦｅＣｌ3・６Ｈ2Ｏを１１３mlのイオン交
換水に溶解した水溶液を加え、撹拌しながら１０％Ｎａ
ＯＨ水溶液でpH１３に調整した。さらにこの溶液に１．
１３ｇのオレイン酸ナトリウムを加え、撹拌しながら１
００℃で２．５時間加熱した後、濾過、水洗を行い、１
００℃で乾燥した。乾燥後の粉末を６００℃で１時間焼
成<Preparation of Test Sample> Production Example 1 A powder was prepared by the steps shown in FIG. That is, 50 g of titanium dioxide-coated mica having a blue interference color (mica titanium Iriodin 221 manufactured by Merck; hereinafter, Iriodin is a trademark of Merck) is dispersed in 100 ml of ion-exchanged water, and 15.2 g is added to the dispersion. Of CoCl 2 .6H 2 O and 34.6 g of FeCl 3 .6H 2 O in 113 ml of ion-exchanged water were added, and 10% Na was stirred.
The pH was adjusted to 13 with an aqueous OH solution. In addition, 1.
Add 13 g of sodium oleate and add 1 g with stirring.
After heating at 00 ° C for 2.5 hours, the mixture was filtered and washed with water.
Dried at 00 ° C. Fired powder after drying at 600 ° C for 1 hour
【００２７】することによりコバルトフェライト被覆雲
母チタンを合成した。同様の製造方法により、マンガ
ン、鉄（マグネタイト）、銅、亜鉛、マグネシウム、ニ
ッケル、バリウムについて、フェライト層をそれぞれ対
二酸化チタン被覆雲母３０重量％となるように調製し、
その磁性について検証を行った。Thus, titanium mica coated with cobalt ferrite was synthesized. By the same production method, for manganese, iron (magnetite), copper, zinc, magnesium, nickel and barium, the ferrite layers were prepared so as to be 30% by weight of titanium dioxide-coated mica, respectively.
The magnetism was verified.
【００２８】＜試験方法＞ 簡易磁力測定 図３に示すような装置３０により測定した。すなわち、
アクリル基板３２上に立設した２本の支柱３４ａ，３４
ｂの一方内側面に希土類磁石（ネオジム系希土類磁石）
３６を設置している。そして、前記支柱３４ａ，３４ｂ
の間に張り渡された梁部材３８に試料片４０を吊架し、
試料片４０が希土類磁石３６に引きつけられる距離Ｌを
測定し、その距離を磁力とした。<Test Method> Simple magnetic force measurement The magnetic force was measured by an apparatus 30 as shown in FIG. That is,
Two columns 34a, 34 standing on the acrylic substrate 32
Rare earth magnet (neodymium rare earth magnet) on one inner surface of b
36 are installed. And the columns 34a, 34b
The sample piece 40 is suspended on the beam member 38 stretched between the
The distance L at which the sample piece 40 was attracted to the rare earth magnet 36 was measured, and the distance was defined as the magnetic force.
【００２９】なお、試料片は、粉末７ｇをニトロセルロ
ースラッカー１５ｇに分散し、０．２０４mmのアプリケ
ータを用いてＯＨＰシート上に塗膜を形成し、乾燥後塗
膜を５×１０cmに切断して磁力測定用の試料片とした。The sample piece was prepared by dispersing 7 g of powder in 15 g of nitrocellulose lacquer, forming a coating film on an OHP sheet using a 0.204 mm applicator, drying the coating film, and cutting the coating film into 5 × 10 cm. This was used as a sample for measuring magnetic force.
【００３０】＜結果＞結果を次の表１に示す。<Results> The results are shown in Table 1 below.
【表１】 ─────────────────────────── フェライト種 簡易磁力測定値（cm） ─────────────────────────── コバルト ６．０９ マンガン ５．６８ 鉄（マグネタイト） ５．０４ 銅 ４．２７ 亜鉛 磁性無し マグネシウム 磁性無し ニッケル 磁性無し バリウム 磁性無し ─────────────────────────── 一般に、マグネタイトとフェライトの磁性はそれぞれ下
記のように示される（磁性体ハンドブック 朝倉書
店）。[Table 1] ─────────────────────────── Ferrite type Simple magnetic force measurement (cm) ──────────コ バ ル ト Cobalt 6.09 Manganese 5.68 Iron (magnetite) 5.04 Copper 4.27 Zinc No magnetism Magnetism No nickel Magnetism Barium No magnetism ── ───────────────────────── In general, magnetite and ferrite have the following magnetic properties (Magnetic Material Handbook, Asakura Shoten).
【００３１】[0031]
【表２】 ──────────────────────────────── 磁性材 飽和磁化（室温）emu/g ──────────────────────────────── ＣｏＦｅ2Ｏ4 ９４ ＭｎＦｅ2Ｏ4 １１２ Ｆｅ3Ｏ4 ９８ ＮｉＦｅ2Ｏ4 ５６ ＣｕＦｅ2Ｏ4 ３０ ＭｇＦｅ2Ｏ4 ３１ ──────────────────────────────── [Table 2] 材 Magnetic material Saturation magnetization (room temperature) emu / g ──── Ｃｏ CoFe 2 O 4 94 MnFe 2 O 4 112 Fe 3 O 4 98 NiFe 2 O 4 56 CuFe 2 O 4 30 MgFe 2 O 4 31
【００３２】上記表１と表２の結果を比較すると、一般
的にいえばマグネタイト（Ｆｅ3Ｏ4）とＭｎ、Ｃｏを有
するフェライトとは同程度の磁性を持っていると言える
が、本発明のごとくフェライト層を二酸化チタン被覆雲
母上に形成すると、むしろコバルトないしマンガンを含
むフェライト層を形成した方が良好な磁性を示すことが
理解される。Comparing the results in Tables 1 and 2, it can be said that, generally speaking, magnetite (Fe 3 O 4 ) and ferrite containing Mn and Co have similar magnetism. It is understood that when the ferrite layer is formed on the titanium dioxide-coated mica as described above, the formation of the ferrite layer containing cobalt or manganese exhibits better magnetism.
【００３３】二酸化チタン被覆雲母の干渉色と外観色 前記同様に、各種干渉色を有する二酸化チタン被覆雲母
にコバルトフェライト層を形成し、その外観色を観察し
た。その結果を次の表３に示す。なお、コバルトフェラ
イトの被覆量はいずれも３０重量％（対二酸化チタン被
覆雲母）である。 Interference color and appearance color of titanium dioxide-coated mica A cobalt ferrite layer was formed on titanium dioxide-coated mica having various interference colors in the same manner as described above, and the appearance color was observed. The results are shown in Table 3 below. The coating amount of cobalt ferrite was 30% by weight (based on mica coated with titanium dioxide).
【００３４】[0034]
【表３】 ──────────────────────────────── 二酸化チタン被覆雲母 Ｌ ａ ｂ 外観色 ──────────────────────────────── 干渉色 黄 (Iriodin201) 30.19 4.01 11.05 黄 干渉色 赤 (Iriodin211) 24.10 14.17 -6.24 赤 干渉色 青 (Iriodin221) 23.28 -0.67 -10.98 青 干渉色 緑 (Iriodin231) 31.06 -5.55 7.44 緑 ──────────────────────────────── 上記表３より明らかなように、最外層に被覆されるコバ
ルトフェライトが同量であっても、二酸化チタン被覆雲
母の干渉色が異なることで、外観色は明らかに異なって
観察される。[Table 3] チ タ ン Titanium dioxide coated mica Lab appearance color ─────干 渉 Interference color Yellow (Iriodin201) 30.19 4.01 11.05 Yellow Interference color Red (Iriodin211) 24.10 14.17 -6.24 Red Interference color Blue (Iriodin221) 23.28 -0.67 -10.98 Blue Interference color Green (Iriodin231) 31.06 -5.55 7.44 Green ─────────────────────────────よ う As is clear from Table 3, even when the amount of cobalt ferrite coated on the outermost layer is the same, the appearance color is clearly different due to the different interference color of the titanium dioxide-coated mica. .
【００３５】フェライト被覆量と色調及び磁性 次に本発明者らは、フェライト被覆量と外観色及び磁性
との相関について検討を行った。The ferrite coating weight and color and magnetic then present inventors have examined the correlation between the ferrite coating amount and the external color and magnetic.
【００３６】＜試験方法＞粉末の色調は、試料粉末１ｇ
をニトロセルロースビヒクル１５ｇに分散し、０．１０
１mmのアプリケーターを用いて白黒紙（隠蔽率試験紙）
に塗布し、乾燥したものを測色用サンプルとした。測色
はミノルタ製測色機ＣＭ−１０００を用いて測色用サン
プルの黒下地部分及び白下地部分のＬａｂを測定した。
隠蔽力（ΔＥ）は黒下地部分及び白下地部分の色差とし
て、以下の式により求める。ΔＥ＝［（黒下地部分と白
下地部分のＬ値の差）2＋（黒下地部分と白下地部分の
ａ値の差）2＋（黒下地部分と白下地部分のｂ値の
差）2］1/2 また、真偽判定に用いる際の角度による色調やＹ値は、
村上色彩技術研究所製変角分光測色機ＧＣＭＳ−３を用
い、入射角を−４５゜、受光角を−２５゜〜６５゜で測
色用サンプルの黒下地部分を測定することにより求め
た。<Test Method> The color of the powder was 1 g of the sample powder.
Was dispersed in 15 g of a nitrocellulose vehicle and 0.10
Black and white paper using a 1mm applicator (concealment rate test paper)
And dried to obtain a colorimetric sample. For colorimetry, Lab was measured on a black base portion and a white base portion of a colorimetric sample using a colorimeter CM-1000 manufactured by Minolta.
The hiding power (ΔE) is obtained by the following equation as a color difference between a black base portion and a white base portion. Delta] E = [(the difference between the b value of the black background portion and the white background portion) (black background portion and the difference between the L value of the white background portion) (the difference between a value of the black background portion and the white background portion) 2 + 2 + 2 ] 1/2 Also, the color tone and Y value depending on the angle used for authenticity determination are
Using a variable angle spectrophotometer GCMS-3 manufactured by Murakami Color Research Laboratory, the angle of incidence was −45 °, and the angle of acceptance was −25 ° to 65 °. .
【００３７】＜結果＞まず、前記同様にして青色干渉色
を有する二酸化チタン被覆雲母に対し、各種フェライト
被覆を行い、その外観色を観察した。結果を図４ないし
７に示す。図４にはそれぞれフェライト被覆量を調整し
た粉体を白下地上及び黒下地上に塗布した場合の測色値
が示されている。なお、同時に二酸化チタン被覆雲母と
フェライト単体を同被覆量に対応させて混合して得た組
成物の測色値も点線で示している。<Results> First, various ferrite coatings were applied to titanium dioxide-coated mica having a blue interference color in the same manner as described above, and the appearance color was observed. The results are shown in FIGS. FIG. 4 shows the colorimetric values obtained when the powders, each having an adjusted ferrite coating amount, were applied on a white base and a black base. At the same time, the colorimetric values of the composition obtained by mixing the titanium dioxide-coated mica and the ferrite alone in correspondence with the same coating amount are also indicated by dotted lines.
【００３８】同図より明らかなように、白下地及び黒下
地上に塗布した場合ともに、混合物より被覆粉体の方が
色調が明瞭であり、特にフェライト量が５重量％を越え
ると被覆粉体は色調の変化が明瞭になるのに対し、混合
物では変化がさほど認められず、しかも目視観察の結果
でも灰色に近く明瞭な色調を観察することはできなかっ
た。また、同様に図５にはフェライト被覆量とＬ値（明
度）が示されている。フェライト被覆による明度の低下
は被覆粉体の方が大きい。混合物の場合には、表層に二
酸化チタン被覆雲母もその存在割合に応じて表出する
が、被覆粉体の場合には粉体の表面がすべて暗色フェラ
イトの被覆されるためと考えられる。As is clear from the drawing, the color tone of the coated powder is clearer than that of the mixture when coated on a white base and a black base, especially when the amount of ferrite exceeds 5% by weight. Although the change in color tone became clear, the change was not so noticeable in the mixture, and the color tone was almost gray and a clear color tone could not be observed by visual observation. Similarly, FIG. 5 shows the ferrite coating amount and the L value (brightness). The decrease in brightness due to the ferrite coating is greater for the coated powder. In the case of the mixture, titanium dioxide-coated mica appears on the surface layer in accordance with the abundance ratio, but in the case of the coated powder, it is considered that the surface of the powder is entirely covered with dark ferrite.
【００３９】さらに、図６には被覆粉体と混合物のそれ
ぞれの隠蔽力が示されている。同図より、被覆粉体の方
が優れた隠蔽力を示すことが理解される。これは、混合
物では白色の雲母チタンの影響で明度が上昇し、被覆粉
末では白色の雲母チタンが存在しないため、フェライト
層による光吸収及び干渉色の強調により明度が低くなる
と考えられる。また、隠蔽力も同様に、混合品では隠蔽
力の低い雲母チタンの影響を受け、被覆粉末ではそのよ
うな影響がないため隠蔽力が高いものと考えられる。つ
まり、隠蔽力差はフェライト層に起因するもので、隠蔽
力が高いほど強く発色していることを意味する。FIG. 6 shows the hiding power of each of the coating powder and the mixture. From the figure, it is understood that the coated powder shows more excellent hiding power. This is thought to be due to the fact that the brightness increases due to the effect of white mica titanium in the mixture and the white mica titanium does not exist in the coating powder, and the lightness decreases due to the light absorption and interference color enhancement by the ferrite layer. Similarly, it is considered that the hiding power is similarly affected by the mica titanium having a low hiding power in the mixed product, and the hiding power is high because the coating powder does not have such an effect. That is, the hiding power difference is caused by the ferrite layer, and the higher the hiding power, the stronger the color.
【００４０】一方、図７にはフェライト被覆量と磁性の
関係が示されている。同図より明らかなように、被覆粉
体の磁性はコバルトフェライトの被覆量に応じて向上す
るが、特に５重量％（対二酸化チタン被覆雲母）程度で
安定する。また、二酸化チタン被覆雲母とコバルトフェ
ライト単体の混合物と比較すると、略同程度の磁性を示
し、雲母チタンへのコバルトフェライトの被覆操作によ
り磁性の低下は認められないことが理解される。On the other hand, FIG. 7 shows the relationship between the ferrite coating amount and the magnetism. As is clear from the figure, the magnetism of the coated powder is improved in accordance with the amount of the cobalt ferrite coated, but is particularly stabilized at about 5% by weight (based on mica coated with titanium dioxide). Also, when compared with a mixture of titanium dioxide-coated mica and cobalt ferrite alone, it shows that the magnetism is substantially the same, and it is understood that the decrease in magnetism is not recognized by the operation of coating titanium mica with cobalt ferrite.
【００４１】次に、コバルトフェライトの各種被覆量の
有色磁性粉体について、具体的な磁力測定結果を示す。Next, specific magnetic force measurement results are shown for colored magnetic powders having various coating amounts of cobalt ferrite.
【表４】 ───────────────────────────────── フェライト被覆量 簡易磁力測定値(cm) 飽和磁化(emu/g) ───────────────────────────────── ３５％ ６．１５ １４．６９ ６０％ ６．７３ ２６．５９ ９０％ ７．０３ ３６．２０ ───────────────────────────────── [Table 4] フ ェ ラ イ ト Ferrite coverage Simple magnetic force measurement (cm) Saturation magnetization ( emu / g) ───────────────────────────────── 35% 6.15 14.69 60% 6.73 26.59 90% 7.03 36.20
【００４２】なお、合成コバルトフェライトと雲母チタ
ンを１：１で混合した場合、磁力が単純に半分になると
仮定すると混合粉末の飽和磁化は２３．４emu/gと算出
できる。この１：１混合品よりもフェライトの量が少な
い、雲母チタンに９０％コバルトフェライトを被覆した
粉末の磁力は３６．２０emu/gであることから、被覆品
は混合品よりも高い磁力を示すことが示唆される。これ
は、雲母チタンにフェライトを被覆すると、フェライト
が雲母チタン上に均一に配向するため磁力が高くなるこ
とによると考えられる。When synthetic cobalt ferrite and titanium mica are mixed at a ratio of 1: 1, the saturation magnetization of the mixed powder can be calculated to be 23.4 emu / g, assuming that the magnetic force is simply halved. Since the magnetic force of powder obtained by coating 90% cobalt ferrite on titanium mica with a smaller amount of ferrite than that of the 1: 1 mixture is 36.20 emu / g, the coating shows a higher magnetic force than the mixture. Is suggested. This is considered to be because when ferrite is coated on titanium mica, the ferrite is uniformly oriented on the titanium mica, so that the magnetic force increases.
【００４３】＜精密磁力測定方法＞磁気天秤により試料
の飽和磁化を測定した。 測定機器：島津製作所株式会社製Magnetic Balance 標準試料：ニッケル粉末（室温での飽和磁化５４．４em
u/g）<Precise Magnetic Force Measurement Method> The saturation magnetization of the sample was measured using a magnetic balance. Measurement device: Magnetic Balance manufactured by Shimadzu Corporation Standard sample: Nickel powder (54.4 em saturation magnetization at room temperature)
u / g)
【００４４】製造例２ ５０ｇの青干渉色を有する二酸化チタン被覆雲母（Merc
k社製雲母チタンIriodin221）を１００mlのイオン交換
水に分散し、該分散溶液に１２．９ｇのＭｎｏＣｌ2・
４Ｈ2Ｏと３５．１ｇのＦｅＣｌ3・６Ｈ2Ｏを１１３ml
のイオン交換水に溶解した水溶液を加え、撹拌しながら
１０％ＮａＯＨ水溶液でpH１３に調整した。さらにこの
溶液に１．１３ｇのオレイン酸ナトリウムを加え、撹拌
しながら１００℃で２．５時間加熱した後、濾過、水洗
を行い、１００℃で乾燥した。乾燥後の粉末を６００℃
で１時間焼成することによりマンガンフェライト被覆雲
母チタンを合成した。 Production Example 2 50 g of titanium dioxide-coated mica having a blue interference color (Merc
(Company K) (Iriodin 221) was dispersed in 100 ml of ion-exchanged water, and 12.9 g of MnoCl 2.
113 ml of 4H 2 O and 35.1 g of FeCl 3 .6H 2 O
Of an ion-exchanged water, and adjusted to pH 13 with a 10% NaOH aqueous solution while stirring. Further, 1.13 g of sodium oleate was added to this solution, heated at 100 ° C. for 2.5 hours with stirring, filtered, washed with water, and dried at 100 ° C. 600 ° C after drying the powder
For 1 hour to synthesize mica ferrite coated with manganese ferrite.
【００４５】雲母に対する二酸化チタンの被覆量 次に本発明者らは雲母に対する二酸化チタンの被覆量に
ついて検討を行った。なお、雲母チタンに対する二酸化
チタンの被覆量は、雲母の粒径によって大きく異なるた
め、各粒径における二酸化チタンの被覆量と干渉色の関
係を以下の表に示す。これより、干渉を有する雲母チタ
ンの雲母１００重量部に対する二酸化チタンの被覆量
は、３５〜２２０重量部であることが好適である。The coating amount then the inventors of titanium dioxide with respect to mica was examined coverage of titanium dioxide with respect to mica. Since the amount of titanium dioxide coated on mica titanium varies greatly depending on the particle size of mica, the following table shows the relationship between the amount of titanium dioxide coated on each particle size and the interference color. Accordingly, it is preferable that the coating amount of titanium dioxide with respect to 100 parts by weight of the mica titanium having interference is 35 to 220 parts by weight.
【００４６】[0046]
【表５】 微粒子タイプ（主な粒度；５〜２５μm） ────────────────────────────────── 雲母チタンの組成 雲母チタン 干渉色 雲母 二酸化チタン 割合 ────────────────────────────────── Iriodin 201 黄 ４３ ５７ １３３ Iriodin 211 赤 ４２ ５８ １３８ Iriodin 221 青 ３８ ６２ １６３ Iriodin 231 緑 ３２ ６８ ２１３ ────────────────────────────────── なお、割合は、雲母１００重量部に対する二酸化チタン
の被覆量（重量部）で示した。[Table 5] Fine particle type (main particle size: 5 to 25 μm) ────────────────────────────────── Mica Titanium composition mica titanium interference color mica titanium dioxide proportion チ タ ン Iriodin 201 yellow 43 57 133 Iriodin 211 Red 42 58 138 Iriodin 221 Blue 38 62 163 Iriodin 231 Green 32 68 213 ───────────────────────────────割 合 In addition, the ratio was shown by the coating amount (part by weight) of titanium dioxide with respect to 100 parts by weight of mica.
【００４７】[0047]
【表６】 中粒径タイプ（主な粒度；１０〜６０μm） ────────────────────────────────── 雲母チタンの組成 雲母チタン 干渉色 雲母 二酸化チタン 割合 ────────────────────────────────── Iriodin 205 黄 ５７ ４３ ７５ Iriodin 215 赤 ５４ ４６ ８５ Iriodin 217 赤銅 ５３ ４７ ８９ Iriodin 219 紫 ５２ ４８ ９２ Iriodin 225 青 ４８ ５２ １０８ Iriodin 235 緑 ４３ ５７ １３３ ────────────────────────────────── [Table 6] Medium particle size type (main particle size; 10-60 μm) ─────────────────────────────────チ タ ン Composition of titanium mica Titanium mica Interference color Mica Titanium dioxide Proportion ────────────────────────────────── Iriodin 205 yellow 57 43 75 Iriodin 215 Red 54 46 85 Iriodin 217 Bronze 53 47 89 Iriodin 219 Purple 52 48 92 Iriodin 225 Blue 48 52 108 Iriodin 235 Green 43 57 133 ───────────────── ─────────────────
【００４８】[0048]
【表７】 大粒径タイプ（主な粒度；１０〜１２５μm） ────────────────────────────────── 雲母チタンの組成 雲母チタン 干渉色 雲母 二酸化チタン 割合 ────────────────────────────────── Iriodin 249 黄 ７４ ２６ ３５ Iriodin 259 赤 ７１ ２９ ４１ Iriodin 289 青 ６６ ３４ ５２ Iriodin 299 緑 ６４ ３６ ５６ ────────────────────────────────── [Table 7] Large particle size type (main particle size; 10 to 125 μm) ─────────────────────────────────チ タ ン Composition of titanium mica Titanium mica Interference color Mica Titanium dioxide Proportion ────────────────────────────────── Iriodin 249 yellow 74 26 35 Iriodin 259 Red 71 29 41 Iriodin 289 Blue 66 34 52 Iriodin 299 Green 64 36 56 ───────────────────────────── ─────
【００４９】フェライト被覆量 次に、本発明において好適なフェライト被覆量の検討を
行った。The ferrite coating amount was then investigated preferred ferrite coating weight in the present invention.
【表８】 ────────────────────────────────── フェライト被覆雲母チタンの組成 対雲母被覆量 対雲母チタン 二酸化 コハ゛ルト 二酸化 コハ゛ルト 簡易 飽和フェライト 被覆量 雲母 チタン フェライト チタン フェライト 磁力 磁化 ────────────────────────────────── ３５％ ２８ ４６ ２６ １６３ ９２ 6.15 14.69 ６０％ ２４ ３９ ３７ １６３ １５８ 6.73 26.59 ９０％ ２０ ３３ ４７ １６３ ２３７ 7.03 36.20 ────────────────────────────────── Table 8: Composition of ferrite-coated mica titanium vs. mica coverage vs. mica Titanium dioxide Cobalt Dioxide Cobalt Simple saturated ferrite Coverage Mica Titanium ferrite Titanium ferrite Magnetic force ───────────────────────────────── 35% 28 46 26 163 92 6.15 14.69 60% 24 39 37 163 158 6.73 26.59 90% 20 33 47 163 237 7.03 36.20 ────────────
【００５０】上記表８及び同様にして行った試験結果よ
り、本発明において好適なフェライト被覆雲母チタン
は、雲母１００重量部に対し、二酸化チタンを３５〜２
２０重量部被覆し、さらにフェライトを５〜２８０重量
部被覆させ、飽和磁化が５〜４７emu/gの範囲のもので
あることが明確となった。From the results of the above Table 8 and the test conducted in the same manner, the ferrite-coated titanium mica suitable in the present invention is obtained by adding 35 to 2 parts of titanium dioxide to 100 parts by weight of mica.
20 parts by weight and then 5 to 280 parts by weight of ferrite, it became clear that the saturation magnetization was in the range of 5 to 47 emu / g.
【００５１】以上のようにして得られた有色磁性粉体
は、現行パール材とは異なるフェライト被覆雲母チタン
の光学特性と、磁性との組み合わせによりきわめて高い
偽造防止性を有した塗装体を得ることができる。従っ
て、 紙幣や有価証券、商品券などの偽造防止用顔料 磁気印刷（色調と磁力を利用） 化粧品（新規光輝性顔料や磁気による血行促進を促す
ボディ用化粧料） 記録材（意匠性の高いプリペイドカード） 立体印刷（立体的な印刷物による点字や模様の作成） 等に好適に用いることができる。The colored magnetic powder obtained as described above is used to obtain a coated body having an extremely high anti-counterfeiting property by combining the optical properties of ferrite-coated mica titanium different from the current pearl material with the magnetism. Can be. Therefore, anti-counterfeit pigments for banknotes, securities, gift certificates, etc. Magnetic printing (using color and magnetic force) Cosmetics (new brilliant pigments and body cosmetics that promote blood circulation by magnetism) Recording materials (highly designed prepaid Card) It can be suitably used for three-dimensional printing (creation of braille and patterns by three-dimensional printed matter) and the like.
【００５２】例えば、本発明にかかる有色磁性粉体を用
いて印刷用塗料を作成し、種々の偽造防止用模様を印刷
した場合、次のように用いることができる。コピーに
よる複製が困難な印刷パターン、パール色調による正
反射と拡散反射での色調変化（フリップフロップ効果）
を例えば変角分光測色機や積分球などを用いて−４５゜
で光を入射した場合、拡散反射及び正反射で測色したＹ
値より得られるＹ（正反射）／Ｙ（拡散反射）の値が特
定の範囲になるか否かの判別、磁気天秤や磁石への付
着などの方法での磁性の有無の判別。For example, when a printing paint is prepared using the colored magnetic powder according to the present invention and various anti-counterfeiting patterns are printed, it can be used as follows. Printing patterns that are difficult to duplicate by copying, color change due to regular reflection and diffuse reflection due to pearl color tone (flip-flop effect)
When light is incident at −45 ° using, for example, a goniospectrocolorimeter or an integrating sphere, Y is measured by diffuse reflection and specular reflection.
Determination of whether the value of Y (specular reflection) / Y (diffuse reflection) obtained from the value falls within a specific range, determination of the presence or absence of magnetism by a method such as attachment to a magnetic balance or a magnet.
【００５３】これらの３種の判別を行うことにより、偽
造がきわめて困難で且つその真偽の判定を容易に行うこ
とができる。すなわち、本発明にかかる有色磁性粉体
は、下記のようなフリップフロップ性を有する。By performing these three types of discrimination, forgery is extremely difficult and the authenticity can be easily determined. That is, the colored magnetic powder according to the present invention has the following flip-flop properties.
【００５４】[0054]
【表９】 雲母チタン（Iriodin 221） ──────────────────────────────────── 正反射 Y(20) Y(25) Y(30) Y(35) Y(40) Y(45) Y(50) Y(55) Y(60) Y(65) ──────────────────────────────────── 拡散反射 Y(-25) 4 5 9 18 72 184 112 26 11 8 Y(-20) 3 5 9 17 70 181 110 26 11 8 Y(-15) 3 5 8 17 68 175 106 25 11 7 Y(-10) 3 5 8 16 65 166 101 24 10 7 Y(-5) 3 5 8 15 61 156 95 22 10 7 Y(0) 3 4 7 13 55 140 85 20 9 6 Y(5) 2 3 6 12 47 120 73 17 7 5 Y(10) 2 3 5 9 38 97 59 14 6 4 Y(15) 1 2 4 7 29 74 45 11 5 3 ────────────────────────────────────[Table 9] Titanium mica (Iriodin 221) ──────────────────────────────────── Specular reflection Y ( 20) Y (25) Y (30) Y (35) Y (40) Y (45) Y (50) Y (55) Y (60) Y (65) ──────────── ──────────────────────── Diffuse reflection Y (-25) 4 5 9 18 72 184 112 26 11 8 Y (-20) 3 5 9 17 70 181 110 26 11 8 Y (-15) 3 5 8 17 68 175 106 25 11 7 Y (-10) 3 5 8 16 65 166 101 24 10 7 Y (-5) 3 5 8 15 61 156 95 22 10 7 Y (0) 3 4 7 13 55 140 85 20 9 6 Y (5) 2 3 6 12 47 120 73 17 7 5 Y (10) 2 3 5 9 38 97 59 14 6 4 Y (15) 1 2 4 7 29 74 45 11 5 3 ────────────────────────────────────
【００５５】[0055]
【表１０】 ３５％コバルトフェライト被覆雲母チタン ──────────────────────────────────── 正反射 Y(20) Y(25) Y(30) Y(35) Y(40) Y(45) Y(50) Y(55) Y(60) Y(65) ──────────────────────────────────── 拡散反射 Y(-25) 7 11 22 62 248 580 384 108 37 20 Y(-20) 6 11 21 59 236 554 367 103 36 19 Y(-15) 6 10 19 53 211 494 328 92 32 17 Y(-10) 5 9 17 48 193 452 300 84 29 15 Y(-5) 5 8 15 42 168 394 261 73 25 13 Y(0) 4 6 12 35 139 324 215 60 21 11 Y(5) 3 5 10 27 110 257 171 48 17 9 Y(10) 2 4 7 20 82 191 127 36 12 7 Y(15) 2 3 5 14 57 134 89 25 9 5 ────────────────────────────────────[Table 10] 35% cobalt ferrite coated mica titanium ──────────────────────────────────── Regular reflection Y (20) Y (25) Y (30) Y (35) Y (40) Y (45) Y (50) Y (55) Y (60) Y (65) ─────────── ───────────────────────── Diffuse reflection Y (-25) 7 11 22 62 248 580 384 108 37 20 Y (-20) 6 11 21 59 236 554 367 103 36 19 Y (-15) 6 10 19 53 211 494 328 92 32 17 Y (-10) 5 9 17 48 193 452 300 84 29 15 Y (-5) 5 8 15 42 168 394 261 73 25 13 Y (0) 4 6 12 35 139 324 215 60 21 11 Y (5) 3 5 10 27 110 257 171 48 17 9 Y (10) 2 4 7 20 82 191 127 36 12 7 Y (15) 2 3 5 14 57 134 89 25 9 5 ────────────────────────────────────
【００５６】[0056]
【表１１】 ６０％コバルトフェライト被覆雲母チタン ──────────────────────────────────── 正反射 Y(20) Y(25) Y(30) Y(35) Y(40) Y(45) Y(50) Y(55) Y(60) Y(65) ──────────────────────────────────── 拡散反射 Y(-25) 9 16 33 83 211 394 309 142 69 41 Y(-20) 8 15 31 77 197 367 288 132 65 38 Y(-15) 7 13 27 68 173 323 253 116 57 33 Y(-10) 6 11 24 61 154 288 226 103 51 30 Y(-5) 5 9 20 50 127 237 186 85 42 24 Y(0) 4 8 16 40 102 191 150 69 34 20 Y(5) 3 6 13 32 82 152 119 55 27 16 Y(10) 2 4 9 23 58 109 85 39 19 11 Y(15) 2 3 6 16 40 74 58 27 13 8 ────────────────────────────────────[Table 11] Titanium mica coated with 60% cobalt ferrite ──────────────────────────────────── Regular reflection Y (20) Y (25) Y (30) Y (35) Y (40) Y (45) Y (50) Y (55) Y (60) Y (65) ───────────拡 散 Diffuse reflection Y (-25) 9 16 33 83 211 394 309 142 69 41 Y (-20) 8 15 31 77 197 367 288 132 65 38 Y (-15) 7 13 27 68 173 323 253 116 57 33 Y (-10) 6 11 24 61 154 288 226 103 51 30 Y (-5) 5 9 20 50 127 237 186 85 42 24 Y (0) 4 8 16 40 102 191 150 69 34 20 Y (5) 3 6 13 32 82 152 119 55 27 16 Y (10) 2 4 9 23 58 109 85 39 19 11 Y (15) 2 3 6 16 40 74 58 27 13 8 ────────────────────────────────────
【００５７】上記表９〜１１の結果より明らかなよう
に、通常の雲母チタンに比較し、本発明にかかるフェラ
イト被覆雲母チタンはフリップフロップ性が著しく強く
なっていることが理解される。以上の点を参酌すると、
拡散反射は−２５〜１５゜、正反射は２０〜６５゜の範
囲であって、さらに好ましくは拡散反射−２５゜〜１５
゜、正反射４０゜〜５０゜の範囲であることが好適であ
る。As is clear from the results of Tables 9 to 11, it is understood that the ferrite-coated mica titanium according to the present invention has a significantly higher flip-flop property than the ordinary mica titanium. Considering the above points,
Diffuse reflection is in the range of −25 ° to 15 °, specular reflection is in the range of 20 ° to 65 °, and more preferably, diffuse reflection is −25 ° to 15 °.
And the regular reflection is preferably in the range of 40 ° to 50 °.
【００５８】また、本発明にかかる有色磁性粉体を用い
て特定の意匠性の高い模様などを描いた場合、該模様は
それぞれ干渉色が強調された色調を有するため、美し
く、且つ例えば変角測色機などを用いると角度によって
看取される色調が微妙に異なり、カラーコピーなどが困
難であると共に、該模様に特定の磁気情報を付加させる
ことも可能で、両者による偽造防止印刷に対しては、全
く同一の顔料などを用いない限り、複製がきわめて困難
である。When a pattern having a high design property is drawn using the colored magnetic powder according to the present invention, the pattern has a color tone in which the interference color is emphasized, so that the pattern is beautiful and, for example, has a variable angle. When using a colorimeter or the like, the color tone perceived by the angle is slightly different, making it difficult to make color copies and the like, and it is also possible to add specific magnetic information to the pattern. In other words, it is extremely difficult to duplicate unless exactly the same pigment is used.
【００５９】さらに、図８（Ａ）に示すように、被塗装
体５０上に、有色非磁性粉体の塗布部分５２と、該有色
非磁性粉体と略同一の色調を有する有色磁性粉体塗布部
分５４を形成した場合、両者の色調はほぼ同一なのであ
るから、外観上有色磁性粉体塗布部分５４は看取でき
ず、またコピーもできない。しかしながら、同図（Ｂ）
に示すように、磁性検出を詳細に行えば、有色磁性粉体
５４を塗布した部分を判別でき、その塗布形状等まで検
出を行えば、例えばバーコードを形成するなど、塗布状
態に情報を付加することが可能となる。Further, as shown in FIG. 8 (A), a coated portion 52 of a colored non-magnetic powder is coated on a body 50 to be coated, and a colored magnetic powder having substantially the same color tone as the colored non-magnetic powder. When the coated portion 54 is formed, the color tone of the two is almost the same, so that the colored magnetic powder coated portion 54 cannot be seen or copied in appearance. However, FIG.
As shown in (2), if the magnetic detection is performed in detail, the portion where the colored magnetic powder 54 is applied can be determined, and if the applied shape and the like are detected, information is added to the applied state such as forming a bar code. It is possible to do.
【００６０】むろん、例えばチューリップの花の部分の
みを赤系の有色磁性粉体で塗布し、葉の部分を緑色系の
有色非磁性粉体で塗布するなど、目視観察と磁性観察の
両者で異なる情報を付加することも可能である。以下、
さらに本発明の粉体を塗料として用いる場合の配合例を
挙げるが、本発明はこれらによって限定されるものでは
ない。なお、特に限定のない限り、配合量は重量％で表
す。Needless to say, both the visual observation and the magnetic observation are different, for example, only the tulip flowers are coated with a red colored magnetic powder and the leaves are coated with a green colored non-magnetic powder. It is also possible to add information. Less than,
Further examples of the case where the powder of the present invention is used as a coating material will be described, but the present invention is not limited thereto. Unless otherwise specified, the amount is expressed in% by weight.
【００６１】配合例１ グラビアインキ 有色磁性粉体 ３０．０％ エチレン−酢酸ビニル共重合樹脂 ７．５ 塩素化ポリプロピレン ５．５ トルエン ２８．０ 酢酸エチル ８．５ メチルエチルケトン １７．０ イソプロピルアルコール ２．５ ポリエチレンワックス ０．８ 静電防止剤 ０．２ Formulation Example 1 Gravure ink colored magnetic powder 30.0% Ethylene-vinyl acetate copolymer resin 7.5 Chlorinated polypropylene 5.5 Toluene 28.0 Ethyl acetate 8.5 Methyl ethyl ketone 17.0 Isopropyl alcohol 2.5 Polyethylene wax 0.8 Antistatic agent 0.2
【００６２】配合例２ グラビアインキ 有色磁性粉体 １５．０％ ポリアミド樹脂 １５．０ ロジンエステル ４．０ ニトロセルロース ３．０ イソプロピルアルコール ４６．０ 酢酸エチル ５．０ トルエン １０．０ ポリエチレンワックス ２．０ Formulation Example 2 Gravure ink colored magnetic powder 15.0% Polyamide resin 15.0 Rosin ester 4.0 Nitrocellulose 3.0 Isopropyl alcohol 46.0 Ethyl acetate 5.0 Toluene 10.0 Polyethylene wax 2.0
【００６３】配合例３ グラビアインキ 有色磁性粉体 ２０．０％ 硬化ロジン １５．０ 石油系樹脂 １０．０ トルエン ５５．０ Formulation Example 3 Gravure ink colored magnetic powder 20.0% Cured rosin 15.0 Petroleum resin 10.0 Toluene 55.0
【００６４】配合例４ グラビアインキ 有色磁性粉体 ３０．０％ ニトロセルロース １０．０ ブチルセルソルブ １０．０ ナフサ ２５．０ シクロヘキサン ２５．０ Formulation Example 4 Gravure ink colored magnetic powder 30.0% Nitrocellulose 10.0 Butyl cellosolve 10.0 Naphtha 25.0 Cyclohexane 25.0
【００６５】配合例５ グラビアインキ 有色磁性粉体 １４．０％ エチレン−酢酸ビニル共重合樹脂 ７．２ 塩素化ポリプロピレン ５．８ トルエン ５８．０ 酢酸エチル １１．０ イソプロピルアルコール ３．０ ポリエチレンワックス ０．８ 静電防止剤 ０．２ Formulation Example 5 Gravure ink colored magnetic powder 14.0% Ethylene-vinyl acetate copolymer 7.2 Chlorinated polypropylene 5.8 Toluene 58.0 Ethyl acetate 11.0 Isopropyl alcohol 3.0 Polyethylene wax 0.0 8 Antistatic agent 0.2
【００６６】配合例６ スクリーンインキ 有色磁性粉体 １５．０％ アクリル樹脂 ２０．０ ナフサ ３５．０ ブチルセルソルブ ３０．０ Formulation Example 6 Colored magnetic powder of screen ink 15.0% acrylic resin 20.0 naphtha 35.0 butyl cellosolve 30.0
【００６７】配合例７ スクリーンインキ 有色磁性粉体 １５．０％ ニトロセルロース １５．０ シクロヘキサノン ４０．０ イソホロン １０．０ ナフサ １０．０ ジブチルフタレート １０．０ Formulation Example 7 Colored magnetic powder for screen ink 15.0% Nitrocellulose 15.0 Cyclohexanone 40.0 Isophorone 10.0 Naphtha 10.0 Dibutyl phthalate 10.0
【００６８】配合例８ スクリーンインキ 有色磁性粉体 ２０．０％ ニトロセルロース ２０．０ シクロヘキサノン ４５．０ イソホロン １０．０ ジオクチルフタレート ５．０ Formulation Example 8 Colored magnetic powder for screen ink 20.0% Nitrocellulose 20.0 Cyclohexanone 45.0 Isophorone 10.0 Dioctyl phthalate 5.0
【００６９】[0069]
【発明の効果】以上説明したように本発明にかかる有色
磁性粉体は、二酸化チタン被覆雲母上にさらに二価金属
種が鉄以外のフェライト層を設けたので、優れた色調と
共に良好な磁性を付与することができる。また、本発明
にかかる真性品判定方法によれば、干渉色を強調して特
定の色調を得た有色磁性粉体を用いて模様を形成し、且
つ該模様に磁気情報を付与することで、きわめて複製の
困難な塗装体を得ることができるため、真性品の判定を
容易かできる。。As described above, since the colored magnetic powder according to the present invention has a ferrite layer other than iron in which the divalent metal species is further provided on the titanium dioxide-coated mica, it has excellent color tone and good magnetism. Can be granted. Further, according to the authentic article determination method according to the present invention, by forming a pattern using a colored magnetic powder having a specific color tone by emphasizing the interference color, and by giving magnetic information to the pattern, Since it is possible to obtain a coated body that is extremely difficult to duplicate, it is possible to easily determine the authentic product. .
【図１】本発明にかかる有色磁性粉体の発色機構の説明
図である。FIG. 1 is an explanatory diagram of a coloring mechanism of a colored magnetic powder according to the present invention.
【図２】本発明にかかる有色磁性粉体の製造工程の説明
図である。FIG. 2 is an explanatory diagram of a process for producing a colored magnetic powder according to the present invention.
【図３】本発明かかる有色磁性粉体の磁性評価に用いた
簡易磁性測定装置の説明図である。FIG. 3 is an explanatory view of a simple magnetometer used for evaluating the magnetism of the colored magnetic powder according to the present invention.
【図４】本発明にかかる有色磁性粉体のフェライト被覆
量と色調の相関の説明図である。FIG. 4 is an explanatory diagram of a correlation between a ferrite coating amount of a colored magnetic powder and a color tone according to the present invention.
【図５】本発明にかかる有色磁性粉体のフェライト被覆
量と明度の相関の説明図である。FIG. 5 is an explanatory diagram of a correlation between a ferrite coating amount of a colored magnetic powder according to the present invention and lightness.
【図６】本発明にかかる有色磁性粉体のフェライト被覆
量と隠蔽力の相関の説明図である。FIG. 6 is an explanatory diagram of the correlation between the amount of ferrite coating of the colored magnetic powder according to the present invention and the hiding power.
【図７】本発明にかかる有色磁性粉体のフェライト被覆
量と磁性の相関の説明図である。FIG. 7 is an explanatory diagram of the correlation between the amount of ferrite coating of the colored magnetic powder according to the present invention and magnetism.
【図８】本発明にかかる真性品判定方法の一実施例の説
明図である。FIG. 8 is an explanatory diagram of one embodiment of a method of determining an intrinsic product according to the present invention.
１０ 有色磁性粉体 １２ 雲母 １４ 二酸化チタン層 １６ フェライト層 １８ 白色入射光 ２４ 反射干渉光 DESCRIPTION OF SYMBOLS 10 Colored magnetic powder 12 Mica 14 Titanium dioxide layer 16 Ferrite layer 18 White incident light 24 Reflection interference light
フロントページの続き (51)Int.Cl.6 識別記号 ＦＩ Ｇ１１Ｂ 5/74 Ｇ１１Ｂ 5/74 13/00 13/00 Continued on the front page (51) Int.Cl. 6 Identification code FI G11B 5/74 G11B 5/74 13/00 13/00
Claims (8)
れ、さらにその上に二価金属種が鉄以外のフェライト層
が形成され、前記二酸化チタン層及びフェライト層によ
り生成する干渉色を強調して外観色として看取し得るこ
とを特徴とする有色磁性粉体。1. A titanium dioxide layer is formed on a mica substrate, and a ferrite layer other than iron is formed on the mica substrate. The interference color generated by the titanium dioxide layer and the ferrite layer is emphasized. A colored magnetic powder that can be seen as an external color.
種はコバルト及び／又はマンガンであることを特徴とす
る有色磁性粉体。2. The colored magnetic powder according to claim 1, wherein the divalent metal species is cobalt and / or manganese.
において、フェライトの被覆量が、雲母に対し５〜２８
０重量％であることを特徴とする有色磁性粉体。3. The powder according to claim 1, wherein the coating amount of ferrite is 5 to 28 with respect to mica.
A colored magnetic powder, which is 0% by weight.
有色磁性粉体を被塗装体に塗布し、その拡散反射及び正
反射で測色した場合の測色値の比が所定範囲となり、か
つ該塗布域に磁性があるか否かにより塗装体が真性品で
あるか否かを判定する真性品判定方法。4. A colored magnetic powder exhibiting a predetermined color tone in which an interference color is emphasized is applied to an object to be coated, and a ratio of colorimetric values obtained by colorimetry with diffuse reflection and specular reflection thereof becomes a predetermined range, And a method of determining whether or not the coated body is an intrinsic product based on whether or not the coating area is magnetic.
有色磁性粉体を被塗装体に所定の意匠形状に塗布し、且
つその塗布域に磁気情報を付加し、意匠形状及び磁気情
報の両者により塗装体が真性品であるか否かを判定する
真性品判定方法。5. A method of applying a colored magnetic powder exhibiting a predetermined color tone by emphasizing an interference color to a coating object in a predetermined design shape, and adding magnetic information to the coated area, and applying the design information and the magnetic information. An authentic article determination method for determining whether or not the painted body is an authentic article by both.
由来する略同色の色調を呈する有色磁性粉体と有色非磁
性粉体をもちいて意匠形状を形成し、かつ前記有色磁性
粉体は有色非磁性粉体で描かれる意匠形状とは異なる磁
気透かし形状で前記意匠形状内に塗布されることを特徴
とする真性品判定方法。6. The method according to claim 5, wherein a design shape is formed by using a colored magnetic powder and a colored non-magnetic powder exhibiting substantially the same color tone derived from an interference color, and wherein the colored magnetic powder is A method for judging an intrinsic product, wherein the design is applied in the design shape with a magnetic watermark shape different from the design shape drawn with colored non-magnetic powder.
由来する色調を呈する有色磁性粉体と、有色非磁性粉体
とをもちいて意匠形状を形成し、かつ前記有色磁性粉体
は前記有色非磁性粉体で描かれる意匠形状の一部を構成
することを特徴とする真性品判定方法。 【請求項７】 請求項５ないし６のいずれかに記載の方
法において、有色磁性粉体は請求項１ないし３のいずれ
かに記載の粉体であることを特徴とする真性品判定方
法。7. The method according to claim 5, wherein a colored magnetic powder exhibiting a color tone derived from an interference color and a colored non-magnetic powder are used to form a design shape, and wherein said colored magnetic powder is A method for determining authenticity, comprising forming a part of a design shape drawn with colored non-magnetic powder. 7. The method according to claim 5, wherein the colored magnetic powder is the powder according to any one of claims 1 to 3.
法において、意匠形状の形成域は明度７０以下の被塗装
体上にあることを特徴とする真性品の判定方法。8. The method according to claim 4, wherein the formation area of the design shape is on an object to be coated having a brightness of 70 or less.