JPH11248552A - Member and method for control of temperature - Google Patents
Member and method for control of temperatureInfo
- Publication number
- JPH11248552A JPH11248552A JP4567798A JP4567798A JPH11248552A JP H11248552 A JPH11248552 A JP H11248552A JP 4567798 A JP4567798 A JP 4567798A JP 4567798 A JP4567798 A JP 4567798A JP H11248552 A JPH11248552 A JP H11248552A
- Authority
- JP
- Japan
- Prior art keywords
- temperature
- code
- management
- printed
- machine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、青果物や生鮮食料
品等を保存する際の温度管理に用いるために温度により
色変化する示温部材を用いて形成した温度管理部材に係
り、特に、温度の暴露状況が機械読み取り可能であるよ
うにした温度管理部材及び温度管理方法に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a temperature control member formed by using a temperature indicating member which changes its color depending on temperature for use in temperature control when preserving fruits and vegetables, fresh food products, etc. The present invention relates to a temperature management member and a temperature management method in which an exposure state is machine-readable.
【０００２】[0002]
【従来の技術】従来、温度に反応して色が変化する示温
部材を必要なインク形態（例えば、樹脂等とともに分散
させる）としてラベル等に塗布しておくか、熱転写イン
クリボン等に含有させてラベル等に印刷して温度管理用
のラベルとして用いているものあるが、一般的には、あ
るパターンがあらかじめ印刷または塗布されており、い
ろの変化を目視してその情報を知るというものである。2. Description of the Related Art Conventionally, a temperature indicating member whose color changes in response to temperature is applied to a label or the like in a required ink form (for example, dispersed with a resin or the like), or contained in a thermal transfer ink ribbon or the like. Some are printed on labels or the like and used as labels for temperature control, but in general, a certain pattern is printed or applied in advance, and the information is known by visually observing changes in colors. .
【０００３】また、温度に反応して色が変化する示温部
材としては、下記のような材料があり、１種類または複
数の示温部材をインクに含有させて用いる方法が知られ
ている。Further, as the temperature indicating member which changes its color in response to temperature, the following materials are available, and a method of using one or more kinds of temperature indicating members in an ink is known.
【０００４】．サーモクロミック有機色素 スピロピラン類、ビアントロンやジキサンチレン等の縮
合芳香環の置換したエチレン誘導体など ．金属錯塩結晶 CoCl2・2(CH2)6N4・10H2O、PbCrO4、Cu2HgI4、Ag2HgI4な
ど ．液晶 コレステリック液晶（マイクロカプセルに封入して用い
る） ．電子供与性呈色性化合物と電子受容性化合物と有極
性有機化合物の組み合せ ・電子供与性呈色性化合物 フェニルメタン系化合物（各種フルオラン、フェニルフ
タリド類等）、各種インドリルフタリド、スピロピラ
ン、ロイコオーラミン類、アシルまたはアリールオーラ
ミン類など ・電子受容性化合物 フェノール性水酸基を有する化合物、フェノール性水酸
基を有する化合物の金属塩、各種トリアゾール類、カル
ボン酸類、カルボン酸の金属塩など ・有極性有機物 アルコール類（オレイルアルコール等）、アミド類（ア
セトアセチルアニリド等）、エステル類（ジフェニルフ
タレート等）、水難溶性のカルボン酸の第一級アミン
塩、ケトンまたはエーテル類、少なくても１個の芳香族
残基を結合基とするアゾメチン類など やの方式では、気中懸濁法、噴霧造粒法、パンコー
ティング法、静電合体法、真空蒸着法とうによりマイク
ロカプセル化されて使用される。[0004] Thermochromic organic dyes Spiropyrans, ethylene derivatives substituted with condensed aromatic rings such as Bianthrone and dixanthiylene. Metal complex salt crystals CoCl2.2 (CH2) 6N4 / 10H2O, PbCrO4, Cu2HgI4, Ag2HgI4, etc. Liquid crystal Cholesteric liquid crystal (encapsulated in microcapsules). Combination of electron-donating color-forming compound, electron-accepting compound and polar organic compound ・ Electron-donating color-forming compound Phenylmethane compounds (various fluorans, phenylphthalides, etc.), various indolylphthalides, spiropyrans, Leuco auramines, acyl or aryl auramines, etc.Electron-accepting compounds, compounds having phenolic hydroxyl groups, metal salts of compounds having phenolic hydroxyl groups, various triazoles, carboxylic acids, metal salts of carboxylic acids, etc. Organics Alcohols (eg, oleyl alcohol), Amides (eg, acetoacetylanilide), Esters (eg, diphenylphthalate), primary amine salts of poorly water soluble carboxylic acids, ketones or ethers, at least one fragrance Azomethines, etc., which use group residues as bonding groups, It is used by being microencapsulated by a medium suspension method, a spray granulation method, a pan coating method, an electrostatic coalescence method, or a vacuum evaporation method.
【０００５】これら示温部材を用いた温度管理用ラベル
等は温度により色が変化する様子を視覚で判断してい
る。[0005] The temperature control labels and the like using these temperature indicating members visually judge how the color changes depending on the temperature.
【０００６】また、示温部材は大別すると可逆式と不可
逆式があり、可逆式は温度が上下するとそれに応じて何
回でも色が変化するタイプで、不可逆式はある温度で色
が変化すると元に戻らないタイプである。[0006] The temperature indicating member is roughly classified into a reversible type and an irreversible type. The reversible type is a type in which the color changes as many times as the temperature rises and falls. The irreversible type changes the color at a certain temperature. It is a type that does not return to.
【０００７】可逆式の場合、飲み物のビール等の飲み頃
サイン等に使用されたり、視覚的に注意を促す場合等に
使用されている。また、青果物や生鮮食料品等の温度管
理には温度履歴が残る特公昭５８−１０７０９公報等に
示されているように、浸透材中を温度により粘性が変化
するインク（例えばオレイルアルコールに染料が溶けて
いるインク）が浸透するようになっており、その浸透長
さにより、設定温度以上の温度にどのくらいの時間曝さ
れたかを確認できるようになっている。[0007] In the case of the reversible type, it is used as a sign or the like when drinking beer or the like, or when it is necessary to visually call attention. In addition, as shown in Japanese Patent Publication No. 58-10709, etc., temperature management of fruits and vegetables, fresh foods, and the like has a temperature history. The melted ink is allowed to permeate, and the length of the permeation makes it possible to check how long it has been exposed to a temperature higher than the set temperature.
【０００８】[0008]
【発明が解決しようとする課題】従来の温度管理ラベル
は、温度により色が変化する様子を視覚的に判断するし
かなく、機械により正確に読み取れるような温度管理ラ
ベルは存在しなかった。そのため、人の判断によりその
色を判断することから、誤差が大きかった。可逆式の場
合には温度判断の誤差が生じ、不可逆式の場合には暴露
時間の読取誤差が生じていた。特に、青果物の温度管理
には、温度履歴の不可逆式が使用されていたが、正確に
高温暴露時間を読み取ることができないことから問題に
なっていた。また、この場合、温度管理部材に複数の温
度反応性のインク（融点等の違うインク）を用いて、複
数の浸透性部材に浸透させることにより正確に高温暴露
時間を読み取ることができるものを実現可能であるが、
これでは大型になり、かつ、コスト高になってしまうと
云う問題があった。The conventional temperature control label has no choice but to visually judge how the color changes depending on the temperature, and there is no temperature control label which can be accurately read by a machine. For this reason, since the color is determined by human judgment, the error is large. In the case of the reversible method, an error in temperature judgment occurred, and in the case of the irreversible method, an error in reading the exposure time occurred. In particular, an irreversible temperature history was used for temperature control of fruits and vegetables, but this was a problem because it was not possible to accurately read the high-temperature exposure time. Also, in this case, by using a plurality of temperature-responsive inks (inks having different melting points, etc.) for the temperature control member and penetrating the plurality of permeable members, a high-temperature exposure time can be accurately read. It is possible,
In this case, there is a problem that the size is increased and the cost is increased.
【０００９】[0009]
【課題を解決するための手段】請求項１の発明は、温度
に反応し色が変化する示温部材で情報が印刷または塗布
された温度管理部材において、前記情報が機械読み取り
可能な符号であることを特徴とするものである。例え
ば、機械読み取り可能な示温部材として、商品に一般的
に使用しているバーコードと同じような機械読取可能な
符号、すなわち、コードを印刷する。示温部材として
は、ある設定温度（例えば２５℃）以下では無色または
白色であり、その設定温度以上では、青または黒のよう
に、バーコードの読取装置で読み取れるような色に変色
するようになっているか、逆に、設定温度以下で有色で
設定温度以上では無色または白色のインクを用いる。こ
のような示温性を実現する示温部材としては、可逆性イ
ンクを用いた場合、例えば、下記のような電子供与性呈
色性化合物と電子受容性化合物と有極性有機化合物の組
み合せを用いる。 ・電子供与性呈色性化合物（発色剤） フェニルメタン系化合物（各種フルオラン、フェニルフ
タリド類等）、各種インドリルフタリド、スピロピラ
ン、ロイコオーラミン類、アシルまたはアリールオーラ
ミン類など ・電子受容性化合物（顕色剤） フェノール性水酸基を有する化合物、フェノール性水酸
基を有する化合物の金属塩、各種トリアゾール類、カル
ボン酸類、カルボン酸の金属塩など ・有極性有機物 アルコール類（オレイルアルコール等）、アミド類（ア
セトアセチルアニリド等）、エステル類（ジフェニルフ
タレート等）、水難溶性のカルボン酸の第一級アミン
塩、ケトンまたはエーテル類、少なくても１個の芳香族
残基を結合基とするアゾメチン類など この方法では、例えば、マイクロカプセル化して使用
し、発色時に従来の黒白バーコードが読取可能な色、す
なわち、青色または黒色になる電子供与性呈色性化合物
を使用する。設定温度は、オレイルアルコールの融点に
依存することになる。このマイクロカプセルを熱転写イ
ンクリボンに用いる場合、ベースフィルム上に直接また
は剥離層上に少なくても上述のマイクロカプセルが含有
したインク層を形成する。その熱転写インクリボンを用
い、サーマルヘッドにより温度管理ラベルに機械コード
読み取り可能な例えば、バーコードを印刷する。つぎ
に、不可逆性示温系を用いる場合、下記のように、非結
晶−結晶又は相分離−非相分離によるリライタブル系を
利用する。 ・電子供与性呈色性化合物 フェニルメタン系化合物（各種フルオラン、フェニルフ
タリド類等）、各種インドリルフタリド、スピロピラ
ン、ロイコオーラミン類、アシルまたはアリールオーラ
ミン類など ・電子受容性化合物 フェノール性水酸基を有する化合物、フェノール性水酸
基を有する化合物の金属塩、各種トリアゾール類、カル
ボン酸類、カルボン酸の金属塩など ・可逆材 ステロイド系等 この系は、サーマルヘッドにより融点以上に加熱され急
冷された時に無色に固定され、そのインク系のガラス転
移点以上で徐々に発色する。発色したときの色が、従来
の黒白バーコードが読取可能な色、すなわち、青色また
は黒色になる電子供与性呈色性化合物を使用する。この
系を熱転写インクリボンにする場合、ベースフィルム上
に直接または剥離層上に少なくても上述した電子供与性
呈色性化合物、電子受容性化合物、可逆材を含有し、そ
の他としてワックス、樹脂等からなっているインク層を
形成する。その熱転写インクリボンを用い、サーマルヘ
ッドにより温度管理ラベルに機械コード読み取り可能な
例えば、バーコードを印刷する。According to a first aspect of the present invention, in a temperature management member on which information is printed or applied by a temperature indicating member whose color changes in response to temperature, the information is a machine-readable code. It is characterized by the following. For example, as a machine-readable temperature indicating member, a machine-readable code, that is, a code similar to a barcode generally used for a product is printed. The temperature indicating member is colorless or white at a temperature lower than a certain set temperature (for example, 25 ° C.), and changes to a color such as blue or black that can be read by a barcode reading device at a temperature higher than the set temperature. Or, conversely, colorless or white ink is used below the set temperature and above the set temperature. When a reversible ink is used as a temperature indicating member for realizing such a temperature indicating property, for example, a combination of an electron-donating color-forming compound, an electron-accepting compound, and a polar organic compound as described below is used.・ Electron-donating color-forming compounds (color formers) Phenylmethane compounds (various fluorans, phenylphthalides, etc.), various indolyl phthalides, spiropyrans, leuco auramines, acyl or aryl auramines, etc. Compounds having a phenolic hydroxyl group, metal salts of compounds having a phenolic hydroxyl group, various triazoles, carboxylic acids, metal salts of carboxylic acids, etc. Polar organic compounds alcohols (oleyl alcohol, etc.), amides (Eg, acetoacetylanilide), esters (eg, diphenylphthalate), poorly water-soluble primary amine salts of carboxylic acids, ketones or ethers, and azomethines having at least one aromatic residue as a bonding group In this method, for example, microencapsulation and use Black and white barcode readable color, i.e., using an electron-donating coloring compound to be blue or black. The set temperature will depend on the melting point of oleyl alcohol. When the microcapsules are used for a thermal transfer ink ribbon, an ink layer containing at least the above microcapsules is formed directly on the base film or on the release layer. Using the thermal transfer ink ribbon, a bar code, for example, which is readable by a machine code, is printed on a temperature management label by a thermal head. Next, when an irreversible thermodynamic system is used, a rewritable system based on non-crystal-crystal or phase separation-non-phase separation is used as described below.・ Electron-donating color-forming compounds Phenylmethane compounds (various fluorans, phenylphthalides, etc.), various indolylphthalides, spiropyrans, leuco-oramines, acyl or aryl auramines, etc. ・ Electron-accepting compounds, phenolic Compounds with hydroxyl groups, metal salts of compounds with phenolic hydroxyl groups, various triazoles, carboxylic acids, metal salts of carboxylic acids, etc.Reversible materials Steroids, etc.This system is heated to above its melting point by a thermal head and quenched. It is fixed to colorless and gradually develops color above the glass transition point of the ink system. An electron-donating color-forming compound whose color when developed becomes a color readable by a conventional black-and-white bar code, that is, blue or black is used. When this system is used as a thermal transfer ink ribbon, it contains at least the above-mentioned electron-donating color-forming compound, the electron-accepting compound, and a reversible material directly on the base film or on the release layer. An ink layer consisting of Using the thermal transfer ink ribbon, a bar code, for example, which is readable by a machine code, is printed on a temperature management label by a thermal head.
【００１０】請求項２記載の発明は、温度に反応し色が
変化する示温部材で印刷された温度管理部材において、
前記示温部材で印刷または塗布された部分の上または下
部に有色インクで機械読み取り可能な商品管理コードが
印刷または塗布され、前記示温部材の変色前または変色
後の色が前記有色インクの機械読み取り可能な商品管理
コードを読み取る読取装置の光源の波長を吸収すること
を特徴とする。従って、有色インクが従来のバーコード
の場合には青または黒であるため、示温部材の色も同等
の色で発色し、読取装置である赤色の光を吸収するよう
になっている。According to a second aspect of the present invention, there is provided a temperature control member printed with a temperature indicating member that changes color in response to temperature,
A machine management code that is machine-readable with colored ink is printed or applied on the upper or lower part printed or applied with the temperature indicating member, and the color of the temperature indicating member before or after discoloration is machine-readable of the colored ink. It is characterized in that it absorbs the wavelength of the light source of the reading device that reads a simple product management code. Therefore, when the color ink is a conventional bar code, the color is blue or black, so that the temperature indicating member also emits the same color and absorbs the red light which is a reading device.
【００１１】請求項３の発明は、示温部材は使用環境下
で不可逆性であることを特徴とする。この系では、前述
した非結晶−結晶または相分離−非相分離を可逆的に行
えるリライタブル材料系を使用する。A third aspect of the present invention is characterized in that the temperature indicating member is irreversible in a use environment. In this system, a rewritable material system capable of reversibly performing the above-mentioned non-crystal-crystal or phase separation-non-phase separation is used.
【００１２】請求項４の発明は、機械読み取り可能な符
号が複数の示温部材を印刷または塗布することにより形
成されていることを特徴とする。The invention according to a fourth aspect is characterized in that the machine-readable code is formed by printing or applying a plurality of temperature indicating members.
【００１３】請求項５記載の発明は、温度特性が異なる
複数の示温部材を用いることを特徴とする。例えば、可
逆性の示温部材が２種類で、反応する温度が異なる場
合、下記のような電子供与性呈色性化合物と電子受容性
化合物と有極性有機化合物の組み合せを用いる。 ・電子供与性呈色性化合物 ＣＶＬ（クリスタルバイオレットラクトン） ・電子受容性化合物 ビスフェノールＡ ・有極性有機物 示温部材１がオレイルアルコール：設定温度５〜７℃用 示温部材２がラウリルアルコール：設定温度２０℃用 そして、前述したように、上記材料をマイクロカプセル
化して、熱転写リボンにしたものを用いる。また、不可
逆性の示温部材が２種類で、反応する温度が異なる場
合、下記のように、非結晶−結晶または相分離−非相分
離によるリライタブル系を利用する。According to a fifth aspect of the present invention, a plurality of temperature indicating members having different temperature characteristics are used. For example, when there are two types of reversible temperature indicating members and the reaction temperatures are different, the following combinations of an electron-donating color-forming compound, an electron-accepting compound, and a polar organic compound are used. -Electron-donating color-forming compound CVL (Crystal Violet Lactone)-Electron-accepting compound Bisphenol A-Polar organic substance Temperature indicating member 1 is oleyl alcohol: for setting temperature 5-7 ° C Temperature indicating member 2 is lauryl alcohol: setting temperature 20 ° C Then, as described above, a material obtained by microencapsulating the above material to form a thermal transfer ribbon is used. When two types of irreversible temperature indicating members are used and the reaction temperatures are different, a rewritable system based on non-crystal-crystal or phase separation-non-phase separation is used as described below.
【００１４】・電子供与性呈色性化合物 ＣＶＬ ・電子受容性化合物 没食子酸プロピル ・可逆材 示温部材１：コレステロール ：設定温度２８℃ 示温部材２：プレグネノロン ：設定温度４４℃ ・樹脂 スチレンメタクリル酸共重合体 ・ワックス（パラフィンワックス） これにより、熱転写インクリボンを複数作製して、温度
管理部材に機械読み取り可能なコードを印刷する。-Electron-donating color-forming compound CVL-Electron-accepting compound propyl gallate-Reversible material Temperature indicating member 1: Cholesterol: Set temperature 28 ° C Temperature indicating member 2: Pregnenolone: Set temperature 44 ° C Resin Styrene methacrylic acid Coalescing / Wax (paraffin wax) In this way, a plurality of thermal transfer ink ribbons are produced, and a machine-readable code is printed on the temperature management member.
【００１５】請求項６記載の発明は、機械読み取り可能
な商品管理コードを複数の示温部材で印刷し、設定温度
に応じ機械読み取り商品管理コードが変化することを特
徴とするものである。The invention according to claim 6 is characterized in that a machine-readable commodity management code is printed by a plurality of temperature indicating members, and the machine-readable commodity management code changes according to a set temperature.
【００１６】請求項７記載の発明は、複数の示温部材が
使用環境下で不可逆性材料で構成されていることを特徴
とする。The invention according to claim 7 is characterized in that the plurality of temperature indicating members are made of an irreversible material under the use environment.
【００１７】請求項８記載の発明は、商品等の情報を機
械読取可能な商品管理コードと温度で色が変化する１つ
または複数の示温部材で機械読み取り可能な商品管理コ
ードとが印刷または塗布された温度管理部材を用い、前
記商品管理コードにより温度範囲を管理するようにし
た。従って、温度管理部材が１つまたは複数の示温部材
により構成され、（複数の場合、示温部材の反応温度が
異なる。）その前記コードを読み取ることにより、温度
範囲を限定する。例えば、示温部材が１つの場合、前記
コードを読み取ることにより、設定温度以上または以下
を判断する事ができる。また、示温部材が複数の場合、
複数の示温部材で複数のコードを印刷する。例えば、設
定温度が２８℃の示温部材１でコード１を印刷する。設
定温度が４４℃の示温部材２により、コード２を印刷す
る。コード１とコード２を認識できなければ、温度は２
８℃未満で保存され、コード１だけが認識されれば、２
８℃以上４４℃未満、コード１とコード２の両方が認識
できれば、４４℃以上で保存されていたことがわかる。
さらに、別の方法として、例えば、コードをＪＡＮ８を
用い、設定温度２５℃以下で無色、それ以上で発色する
示温部材１と、設定温度３５℃以下で無色、それ以上で
発色する示温部材２とで機械コードを形成する。その機
械コードとしては、例えば、２５℃以下では［バーの認
識不可］、２５℃以上３５℃未満の場合には［４９００
０００９］、３５℃以上では［６７３０３００７］にな
るように印刷されている。According to the present invention, a product management code capable of machine-reading information of a product or the like and a product management code machine-readable by one or more temperature indicating members whose color changes with temperature are printed or applied. The temperature range is managed by the product management code using the temperature management member. Therefore, the temperature management member is constituted by one or a plurality of temperature indicating members (in a plurality of cases, the reaction temperature of the temperature indicating member is different). By reading the code, the temperature range is limited. For example, when there is one temperature indicating member, it is possible to determine whether the temperature is equal to or higher than the set temperature by reading the code. Also, when there are a plurality of temperature indicating members,
Printing a plurality of codes with a plurality of temperature indicating members. For example, the code 1 is printed on the temperature indicating member 1 having the set temperature of 28 ° C. The code 2 is printed by the temperature indicating member 2 having the set temperature of 44 ° C. If code 1 and code 2 cannot be recognized, the temperature is 2
If stored at less than 8 ° C. and only code 1 is recognized, 2
If it is 8 ° C. or more and less than 44 ° C., and if both Code 1 and Code 2 can be recognized, it is understood that the data was stored at 44 ° C. or more.
Further, as another method, for example, using a JAN8 code, a temperature indicating member 1 that is colorless at a set temperature of 25 ° C. or less and develops a color above it, and a temperature indicating member 2 that is colorless at a set temperature of 35 ° C. or less and develops a color above it. Form the machine code. As the machine code, for example, [the bar cannot be recognized] at 25 ° C. or less, and [4900 when the temperature is 25 ° C. or more and less than 35 ° C.]
0009], it is printed so as to become [6730307] at 35 ° C. or higher.
【００１８】[0018]
【発明の実施の形態】本発明の第一の実施の形態を図１
乃至図８に基づいて説明する。まず、図１に示すもの
は、ラベル状に形成された温度管理部材１であり、この
温度管理部材１には、商品名や発送日、製造日、製造元
等の文字や図形により表現された商品情報２とその商品
情報２の内容を機械読み取り可能にした商品管理コード
としての商品管理用バーコード３とが印刷されている。
その温度管理部材１に示温部材印刷エリア４が設けられ
ている。このような温度管理部材１は、商品に添付して
使用されるものであるが、図２に示すものは、設定温度
以下で管理された状態を示し、示温部材印刷エリア４に
は何も表れていない。また、図３に示すように、前記示
温部材印刷エリア４には、温度に反応して色が変化する
性質を持つ示温部材によって形成された符号としての商
品管理コード５が印刷されており、図３に示した状態に
おいては、設定温度以上で管理されて商品管理コード５
の色が変化した状態を示しているものである。FIG. 1 shows a first embodiment of the present invention.
A description will be given based on FIGS. First, what is shown in FIG. 1 is a temperature management member 1 formed in a label shape. The temperature management member 1 includes a product represented by characters or figures such as a product name, a shipping date, a manufacturing date, and a manufacturer. Information 2 and a bar code 3 for product management as a product management code that makes the contents of the product information 2 machine-readable are printed.
The temperature management member 1 is provided with a temperature member printing area 4. Such a temperature management member 1 is used by being attached to a product, but the one shown in FIG. 2 shows a state where the temperature is controlled below a set temperature, and nothing appears in the temperature member printing area 4. Not. As shown in FIG. 3, a product management code 5 is printed on the temperature indicating member printing area 4 as a code formed by a temperature indicating member having a property of changing color in response to temperature. In the state shown in FIG. 3, the product management code 5
Indicates a state in which the color has changed.
【００１９】そこで、温度が上下するとそれに応じて何
回でも色が変化する可逆式の示温部材を用いた場合から
説明する。まず、可逆式の示温部材としては、例えば、
電子供与性呈色性化合物と電子受容性化合物と有極性有
機化合物との組み合せを用いる。Therefore, a description will be given of a case where a reversible temperature indicating member whose color changes as many times as the temperature rises and falls is used. First, as a reversible temperature indicating member, for example,
A combination of an electron-donating color-forming compound, an electron-accepting compound, and a polar organic compound is used.
【００２０】・電子供与性呈色性化合物（発色剤） フェニルメタン系化合物（各種フルオラン、フェニルフ
タリド類等）、各種インドリルフタリド、スピロピラ
ン、ロイコオーラミン類、アシルまたはアリールオーラ
ミン類など ・電子受容性化合物（顕色剤） フェノール性水酸基を有する化合物、フェノール性水酸
基を有する化合物の金属塩、各種トリアゾール類、カル
ボン酸類、カルボン酸の金属塩など ・有極性有機物 アルコール類（ラウリルアルコール等）、アミド類（ア
セトアセチルアニリド等）、エステル類（ジフェニルフ
タレート等）、水難溶性のカルボン酸の第一級アミン
塩、ケトンまたはエーテル類、少なくても１個の芳香族
残基を結合基とするアゾメチン類など ここで、電子供与性呈色性化合物が色を決定、電子受容
性化合物が濃度を決定し、有極性有機化合物が変色温度
を決定するものであり、この方法を用いた可逆性材料と
してはメタモカラー（パイロットインキ社製）が知られ
ている。本発明で用いる示温部材は、発色の色が前記商
品管理用バーコード３と同じ読取装置が使用可能な青、
または黒が良いので、電子供与性呈色性化合物はクリス
タルバイオレット（ＣＶＬ：青色）や３−ジエチルアミ
ノ−６−メチル−７−アニリノフルオラン等が使用可能
である。Electron-donating color-forming compounds (color formers) Phenylmethane-based compounds (various fluorans, phenylphthalides, etc.), various indolylphthalides, spiropyrans, leuco auramines, acyl or aryl auramines, etc.・ Electron-accepting compounds (developers) Compounds having phenolic hydroxyl groups, metal salts of compounds having phenolic hydroxyl groups, various triazoles, carboxylic acids, metal salts of carboxylic acids, etc. ・ Polar organic alcohols (lauryl alcohol, etc.) ), Amides (such as acetoacetylanilide), esters (such as diphenylphthalate), primary amine salts of poorly water-soluble carboxylic acids, ketones or ethers, and at least one aromatic residue as a bonding group. Azomethines, etc., where the electron-donating color-forming compound determines the color, Compound determines the concentration, which polar organic compound to determine the color change temperature, Metamo color (manufactured by Pilot Ink Co., Ltd.) is known as a reversible material using this method. The temperature indicating member used in the present invention has a color of blue, which can be used by the same reading device as the barcode 3 for merchandise management,
Alternatively, since black is preferable, crystal violet (CVL: blue), 3-diethylamino-6-methyl-7-anilinofluoran, or the like can be used as the electron-donating color-forming compound.
【００２１】具体的な例を示す。 ＊電子供与性呈色性化合物：ＣＶＬ １重量部 ＊電子受容性化合物：没食子酸プロピルエステル（ＰＧＥ） １重量部 ＊有極性有機化合物：ｎ−ラウリルアルコール ２５重量部 を加熱溶解して均質化し、周知のコアセルベーション法
によりカプセル化して得られる。 ＊得られたマイクロカプセル １重量部 ＊エチレン酢ビ共重合体（ＥＶＡ−２１０）１重量部 ＊カルナバワックス ３重量部 ＊パラフィンワックス ３重量部 ＊その他（分散剤等） １重量部 を加熱しながら拡散し、背面に耐熱層の付いた６umのＰ
ＥＴ（ポリエチレンテレフタレート）フィルムにインク
塗工機により加熱しながら塗工して熱転写インクリボン
を得たものを用いた。A specific example will be described. * Electron-donating color-forming compound: 1 part by weight of CVL * Electron-accepting compound: 1 part by weight of propyl gallate (PGE) * Polar organic compound: 25 parts by weight of n-lauryl alcohol is dissolved by heating and homogenized. It is obtained by encapsulation by a well-known coacervation method. * 1 part by weight of obtained microcapsules * 1 part by weight of ethylene-vinyl acetate copolymer (EVA-210) * 3 parts by weight of carnauba wax * 3 parts by weight of paraffin wax * 1 part by weight of other (dispersant, etc.) while heating 6um P which diffuses and has a heat resistant layer on the back
An ET (polyethylene terephthalate) film obtained by applying a heat transfer ink ribbon by applying while heating with an ink coater was used.
【００２２】前記熱転写インクリボンをバーコードプリ
ンタ（株式会社テック製Ｂ−６００）により商品管理コ
ード５を印刷し、ラベル状の温度管理部材１を得た。こ
のようにして得られた温度管理部材１は、商品管理コー
ドが図４に示すように設定温度の前後で、若干のヒステ
リシスを有するが目視よりも正確に判断できる。例え
ば、濃度の相対値が０．５以上で機械読み取りが可能で
あるとすれば、温度上昇時には約１６.５℃ で読取可能
であり、温度降下時には１１℃程度で読取可能になる。A product management code 5 was printed on the thermal transfer ink ribbon by a bar code printer (B-600 manufactured by TEC Co., Ltd.) to obtain a label-like temperature control member 1. The temperature management member 1 thus obtained has a slight hysteresis before and after the set temperature of the product management code as shown in FIG. 4, but can be judged more accurately than visually. For example, assuming that machine reading is possible when the relative value of density is 0.5 or more, reading is possible at about 16.5 ° C. when the temperature rises, and about 11 ° C. when the temperature drops.
【００２３】つぎに、不可逆性の示温部材としては、非
結晶−結晶または相分離−非相分離によるリライタブル
系の下記のような材料を利用した。 ・電子供与性呈色性化合物 フェニルメタン系化合物（各種フルオラン、フェニルフ
タリド類等）、各種インドリルフタリド、スピロピラ
ン、ロイコオーラミン類、アシルまたはアリールオーラ
ミン類など ・電子受容性化合物 フェノール性水酸基を有する化合物、フェノール性水酸
基を有する化合物の金属塩、各種トリアゾール類、カル
ボン酸類、カルボン酸の金属塩など・可逆材 ステロイド系等 ＊電子供与性呈色性化合物 ：ＣＶＬ １重量部 ＊電子受容性化合物 ：没食子酸プロピル １重量部 ＊可逆材 ：コレステロール ５重量部 ＊樹脂 ：スチレンメタクリル酸共重合体（Ａ−１４Ｐ 大日本インキ化学社製） ５重量部 をトルエンとシクロヘキサノンの１：１溶媒で完全に溶
解する。Next, as the irreversible temperature indicating member, the following rewritable materials based on non-crystal-crystal or phase separation-non-phase separation were used.・ Electron-donating color-forming compounds Phenylmethane compounds (various fluorans, phenylphthalides, etc.), various indolylphthalides, spiropyrans, leuco-oramines, acyl or aryl auramines, etc. ・ Electron-accepting compounds, phenolic Compounds having a hydroxyl group, metal salts of compounds having a phenolic hydroxyl group, various triazoles, carboxylic acids, metal salts of carboxylic acids, etc., reversible materials, steroids, etc. * Electron donating color former: CVL 1 part by weight * Electron acceptor Compound: 1 part by weight of propyl gallate * Reversible material: 5 parts by weight of cholesterol * Resin: 5 parts by weight of styrene methacrylic acid copolymer (A-14P, manufactured by Dainippon Ink and Chemicals, Inc.) in a 1: 1 solvent of toluene and cyclohexanone Dissolve completely.
【００２４】 ＊パラフィンワックス ５重量部 の混合物をボールミルで加熱しながら溶解したものを加
え（固形分２０％）、自然冷却しながら分散をする。背
面に耐熱層の付いた６umのＰＥＴ（ポリエチレンテレフ
タレート）フィルムにインク塗工機により塗工して熱転
写インクリボンを得たものを用いた。* A mixture obtained by dissolving a mixture of 5 parts by weight of paraffin wax while heating with a ball mill is added (solid content: 20%), and dispersed while cooling naturally. A 6 μm PET (polyethylene terephthalate) film having a heat-resistant layer on the back surface was coated with an ink coating machine to obtain a thermal transfer ink ribbon.
【００２５】不可逆式においては図５に示すように、設
定温度以上になると徐々に発色し、最終的に飽和濃度に
達する。この設定温度は、このインク系のガラス転移点
に相当し、非結晶で無色化している系がＴｇ点以上で徐
々に結晶化して発色するようになっている。その系を図
６に示す。サーマルヘッド等で加熱−急冷して、商品管
理コード５を印刷すると無色で固定される。この商品管
理コード５はガラス転移点Ｔｇ以上に暖まると徐々に発
色し、図５に示すように時間により濃度が異なる。その
ため、相対値で０．５に達した時に機械読取ができると
すると、転移点Ｔｇ以上の温度の環境下に３８時間以上
曝されていたことがわかる。前記インクはこのＴｇが約
２８℃程度である。目視であるとその管理時間があいま
いになることは言うまでもない。ここで、Ａは呈色性材
料（ロイコ染料）、Ｂは顕色剤（フェノール系化合
物）、Ｃは可逆剤である。そのため、無色状態は、Ａと
Ｂとが切り離され、ＢとＣとが結合している状態であ
り、有色状態はＡとＢとが結合され、Ｃが切り離された
状態であり、流動状態は、Ａ，Ｂ，Ｃのそれぞれが切り
離された状態である。In the irreversible method, as shown in FIG. 5, when the temperature exceeds a set temperature, the color gradually develops, and finally reaches a saturation density. This set temperature corresponds to the glass transition point of the ink system, and the non-crystalline and colorless system gradually crystallizes and develops color above the Tg point. The system is shown in FIG. When the product management code 5 is printed after heating and quenching with a thermal head or the like, it is fixed in a colorless state. The product management code 5 gradually develops its color when it warms above the glass transition point Tg, and its density varies with time as shown in FIG. Therefore, if machine reading can be performed when the relative value reaches 0.5, it can be understood that the device has been exposed to an environment having a temperature equal to or higher than the transition point Tg for 38 hours or more. The Tg of the ink is about 28 ° C. Needless to say, the visual management time becomes ambiguous. Here, A is a coloring material (leuco dye), B is a developer (phenolic compound), and C is a reversible agent. Therefore, the colorless state is a state in which A and B are separated and B and C are combined, the colored state is a state in which A and B are combined and C is separated, and the flow state is , A, B, and C are separated.
【００２６】図７に示すものは、設定温度以下で管理さ
れた温度管理部材１であり、示温部材の商品管理コード
５が無色または白色で、バーコードスキャナー６では認
識できない。これに対して、設定温度以上であると図８
に示すように、商品管理コード５が発色し、バーコード
スキャナー６での認識が可能になる。可能になった時点
でどのような温度環境にあるのかが正確にわかる。FIG. 7 shows a temperature management member 1 managed at a temperature lower than a set temperature. The product management code 5 of the temperature indicating member is colorless or white and cannot be recognized by the barcode scanner 6. On the other hand, if the temperature is higher than the set temperature,
As shown in (1), the product management code 5 is colored, and can be recognized by the barcode scanner 6. When it becomes possible, it is possible to know exactly what temperature environment it is in.
【００２７】本発明の第二の実施の形態を図９乃至図１
３に基づいて説明する。本実施の形態においては、第一
の実施の形態の場合と異なり、示温部材印刷エリア４が
商品管理用バーコード３と同じエリアに位置している。
その際、示温部材は前述の実施の形態と同じインクが使
用可能で、べたパターン７で良い。べたパターン７は商
品管理用バーコード３の上面・下面のどちらに印刷して
もよい。このようにして印刷された示温インクは可逆性
示温部材で印刷された場合、設定温度以下で管理された
場合は図１０のようになり、図１２に示すようにバーコ
ードリーダ６により商品管理用バーコード３が読取可能
であるが、設定温度以上で管理された場合、図１１に示
すようにべたパターン７が発色し、図１３に示すよう
に、商品管理用バーコード３が読み取れなくなる（商品
管理用バーコード３とべたパターン７が発色した場合の
光吸収波長帯がほぼ同じになるような電子供与性呈色性
化合物を使用しているため）。同様に、不可逆性部材で
印刷された場合、第一の実施の形態の図５で示したよう
に、不可逆性示温部材はＴｇ以上で徐々に発色する特性
であり、ある時間経過後は図１１に示すようになり、バ
ーコードリーダ７で読めなくなる（商品管理バーコード
３のバーの部分とスペース部分とのコントラストが取れ
ないため）。FIGS. 9 to 1 show a second embodiment of the present invention.
3 will be described. In the present embodiment, unlike the case of the first embodiment, the temperature indicating member printing area 4 is located in the same area as the barcode 3 for product management.
At this time, the same ink as in the above-described embodiment can be used for the temperature indicating member, and the solid pattern 7 may be used. The solid pattern 7 may be printed on either the upper surface or the lower surface of the barcode 3 for product management. When the temperature indicating ink printed in this manner is printed with a reversible temperature indicating member, and when the temperature is controlled at a set temperature or lower, the state becomes as shown in FIG. 10, and as shown in FIG. Although the barcode 3 is readable, if the temperature is controlled at a set temperature or higher, the solid pattern 7 is colored as shown in FIG. 11 and the barcode 3 for product management cannot be read as shown in FIG. (Because an electron-donating color-forming compound is used such that the light absorption wavelength bands when the management barcode 3 and the solid pattern 7 are colored are substantially the same.) Similarly, when printed with an irreversible member, as shown in FIG. 5 of the first embodiment, the irreversible temperature indicating member has a characteristic of gradually developing color at Tg or higher, and after a certain time elapses, FIG. , And cannot be read by the barcode reader 7 (because the contrast between the bar portion and the space portion of the product management barcode 3 cannot be obtained).
【００２８】このようにして得られた温度管理部材１は
図１２のようにして機械読み取りが可能になる。すなわ
ち、図１２に示したものは、設定温度以下で管理された
場合であり、べたパターン７は無色であるので、商品管
理用バーコード３が読取可能であり、設定温度以上で管
理された場合、図１３に示すように、べたパターン７が
発色し、商品管理用バーコード３がバーコードスキャナ
ー６で認識できなくなるので、環境温度や高温暴露時間
を知ることができる。従って、本実施の形態において
は、機械読み取り可能な符号としての情報は、商品管理
用バーコード３となり、べたパターン７はその商品管理
用バーコード３を読取可能或いは不可とする媒体とな
る。The temperature control member 1 thus obtained can be read by a machine as shown in FIG. That is, what is shown in FIG. 12 is a case where the bar code is managed at a temperature lower than the set temperature, and since the solid pattern 7 is colorless, the barcode 3 for merchandise management is readable and the bar code 3 is managed at a temperature higher than the set temperature. As shown in FIG. 13, the solid pattern 7 is colored and the barcode 3 for merchandise management cannot be recognized by the barcode scanner 6, so that the environmental temperature and the high-temperature exposure time can be known. Therefore, in the present embodiment, the information as a machine-readable code is the barcode 3 for managing products, and the solid pattern 7 is a medium that makes the barcode 3 for managing products readable or unreadable.
【００２９】以上のようにして得られた温度管理部材１
は電子供与性呈色性化合物と電子受容性化合物等を用い
る方式だけに限定するものでなく、他の方式でもよい。
設定温度や設定発色時間等は別にこれに限定されるもの
でない。また、変色する色等も読取装置がその変色する
色により吸収する光源を有してればよい。また、印刷方
式も熱転写インクリボンに限定されるものでなく、スク
リン印刷やホットスタンプ等の方式によってもよいこと
は云うまでもない。The temperature control member 1 obtained as described above
Is not limited to a system using an electron-donating color-forming compound and an electron-accepting compound, but may be another system.
The set temperature, the set color development time, and the like are not limited to these. Further, it is sufficient that the reading device has a light source that absorbs the discolored color and the like by the discolored color. Further, the printing method is not limited to the thermal transfer ink ribbon, and it goes without saying that a method such as screen printing or hot stamping may be used.
【００３０】また、前述の各実施の形態では、ある設定
温度以下で無色、設定温度以上で発色の場合を示した
が、これに限られるものでなく逆でもよいことは云うま
でもない。Further, in each of the above-described embodiments, the case of colorlessness at a temperature lower than a certain set temperature and color development at a temperature higher than the set temperature has been described. However, it is needless to say that the present invention is not limited to this and may be reversed.
【００３１】次に、本発明の第三の実施の形態を図１４
乃至図１８に基づいて説明する。本実施の形態における
温度管理部材１には、商品名や発送日、製造日、製造元
等の商品情報２とその商品情報２を例えばＪＡＮコード
を用いて機械読み取り可能にした商品管理用バーコード
３とが印刷されている。その温度管理部材１に示温部材
印刷エリア４が複数個（図１４では２個所）設けられて
いる。これらの示温部材印刷エリア４には、設定温度に
より変色する示温部材により温度管理コード５が印刷さ
れている。これらの示温部材印刷エリア４：４−１と示
温部材印刷エリア４：４−２には反応温度または反応時
間の異なる示温部材で機械読取可能な温度管理コード５
が印刷または塗布されている。Next, a third embodiment of the present invention will be described with reference to FIG.
18 through FIG. The temperature management member 1 according to the present embodiment includes a product name 2 such as a product name, a shipping date, a manufacturing date, and a manufacturer, and a product management barcode 3 in which the product information 2 is machine-readable using, for example, a JAN code. And are printed. The temperature management member 1 is provided with a plurality (two in FIG. 14) of temperature member printing areas 4. A temperature management code 5 is printed on these temperature indicating member printing areas 4 by a temperature indicating member that changes color according to a set temperature. In the temperature indicating member printing area 4: 4-1 and the temperature indicating member printing area 4: 4-2, a temperature management code 5 that is machine-readable with a temperature indicating member having a different reaction temperature or reaction time is used.
Is printed or applied.
【００３２】ここで温度管理部材１は、例えばＪＡＮコ
ードのように商品管理コード３と同じ体系にしておく。
可逆式の示温部材を用いた場合（反応温度が異なる２つ
以上の示温部材を用いる）、例えば、下記のような電子
供与性呈色性化合物と電子受容性化合物と有極性有機化
合物の組み合せを用いる。Here, the temperature management member 1 has the same system as the product management code 3, for example, a JAN code.
When a reversible temperature indicator is used (two or more temperature indicators having different reaction temperatures are used), for example, the following combination of an electron-donating color-forming compound, an electron-accepting compound, and a polar organic compound is used. Used.
【００３３】・電子供与性呈色性化合物 フェニルメタン系化合物（各種フルオラン、フェニルフ
タリド類等）、各種インドリルフタリド、スピロピラ
ン、ロイコオーラミン類、アシルまたはアリールオーラ
ミン類など ・電子受容性化合物 フェノール性水酸基を有する化合物、フェノール性水酸
基を有する化合物の金属塩、各種トリアゾール類、カル
ボン酸類、カルボン酸の金属塩など ・有極性有機物 アルコール類（ラウリルアルコール等）、アミド類（ア
セトアセチルアニリド等）、エステル類（ジフェニルフ
タレート等）、水難溶性のカルボン酸の第一級アミン
塩、ケトンまたはエーテル類、少なくても１個の芳香族
残基を結合基とするアゾメチン類など ここで、電子供与性呈色性化合物が色を決定、電子受容
性化合物が濃度を決定し、有極性有機化合物が変色温度
を決定するものであり、この方法を用いた可逆性材料と
してはメタモカラー（パイロットインキ社製）が知られ
ている。本発明の実施の形態で用いる示温部材は、発色
の色が前記商品管理用バーコード３と同じ読取装置が使
用可能な青、または黒が良いので、電子供与性呈色性化
合物はクリスタルバイオレット（ＣＶＬ：青色）や３−
ジエチルアミノ−６−メチル−７−アニリノフルオラン
（黒）等が使用可能である。Electron-donating color-forming compounds Phenylmethane compounds (various fluorans, phenylphthalides, etc.), various indolyl phthalides, spiropyrans, leuco auramines, acyl or aryl auramines, etc. Compounds Compounds having a phenolic hydroxyl group, metal salts of compounds having a phenolic hydroxyl group, various triazoles, carboxylic acids, metal salts of carboxylic acids, etc. ・ Polar organic organic alcohols (lauryl alcohol, etc.), amides (acetoacetylanilide, etc.) ), Esters (such as diphenylphthalate), primary amine salts of water-insoluble carboxylic acids, ketones or ethers, and azomethines having at least one aromatic residue as a bonding group. The color-forming compound determines the color, and the electron-accepting compound determines the concentration. Polar organic compound is intended to determine discoloration temperature, Metamo color as reversible material using this method (manufactured by Pilot Ink Co., Ltd.) is known. The temperature indicating member used in the embodiment of the present invention is preferably blue or black, which can be used by a reading device having the same color as the barcode 3 for merchandise management. Therefore, the electron donating color forming compound is crystal violet ( CVL: blue) or 3-
Diethylamino-6-methyl-7-anilinofluoran (black) and the like can be used.
【００３４】次に、具体的な例を示す。示温部材印刷エ
リア４：４−１に印刷する示温部材は。設定温度を５℃
とする。 ＊電子供与性呈色性化合物：ＣＶＬ １重量部 ＊電子受容性化合物：没食子酸プロピルエステル（ＰＧＥ） １重量部 ＊有極性有機化合物：オレイルアルコール ２５重量部 を加熱溶解して均質化し、周知のコアセルベーション法
によりカプセル化して得られる。 ＊得られたマイクロカプセル １重量部 ＊エチレン酢ビ共重合体（ＥＶＡ−２１０）１重量部 ＊カルナバワックス ３重量部 ＊パラフィンワックス ３重量部 ＊その他（分散剤等） １重量部 を加熱しながら拡散し、背面に耐熱層の付いた４.５μ
ｍ のＰＥＴ（ポリエチレンテレフタレート）フィルム
にインク塗工機により加熱しながら塗工して熱転写イン
クリボンを得た。同様にして、示温部材印刷エリア４：
４−２に印刷する示温部材は、設定温度を１６℃とす
る。 ＊電子供与性呈色性化合物：ＣＶＬ １重量部 ＊電子受容性化合物：没食子酸プロピルエステル（ＰＧＥ） １重量部 ＊有極性有機化合物：ｎ−ラウリルアルコール ２５重量部 を加熱溶解して均質化し、周知のコアセルベーション法
によりカプセル化して得られる。 ＊得られたマイクロカプセル １重量部 ＊エチレン酢ビ共重合体（ＥＶＡ−２１０）１重量部 ＊カルナバワックス ３重量部 ＊パラフィンワックス ３重量部 ＊その他（分散剤等） １重量部 を加熱しながら拡散し、背面に耐熱層の付いた4.5μｍ
ＰＥＴ（ポリエチレンテレフタレート）フィルムにイン
ク塗工機により加熱しながら塗工して熱転写インクリボ
ンを得た。Next, a specific example will be described. The temperature indicating member to be printed in the temperature indicating member printing area 4: 4-1. Set temperature to 5 ℃
And * Electron-donating color-forming compound: 1 part by weight of CVL * Electron-accepting compound: 1 part by weight of propyl gallate (PGE) * Polar organic compound: 25 parts by weight of oleyl alcohol is homogenized by heating and dissolving. It is obtained by encapsulation by the coacervation method. * 1 part by weight of obtained microcapsules * 1 part by weight of ethylene-vinyl acetate copolymer (EVA-210) * 3 parts by weight of carnauba wax * 3 parts by weight of paraffin wax * 1 part by weight of other (dispersant, etc.) while heating Diffuse, 4.5μ with heat-resistant layer on the back
m was applied to a PET (polyethylene terephthalate) film while being heated by an ink coater to obtain a thermal transfer ink ribbon. Similarly, the temperature indicating member printing area 4:
The temperature indicating member to be printed in 4-2 has a set temperature of 16 ° C. * Electron-donating color-forming compound: 1 part by weight of CVL * Electron-accepting compound: 1 part by weight of propyl gallate (PGE) * Polar organic compound: 25 parts by weight of n-lauryl alcohol is dissolved by heating and homogenized. It is obtained by encapsulation by a well-known coacervation method. * 1 part by weight of obtained microcapsules * 1 part by weight of ethylene-vinyl acetate copolymer (EVA-210) * 3 parts by weight of carnauba wax * 3 parts by weight of paraffin wax * 1 part by weight of other (dispersant, etc.) while heating Diffuse, 4.5μm with heat-resistant layer on the back
The PET (polyethylene terephthalate) film was coated while heating with an ink coating machine to obtain a thermal transfer ink ribbon.
【００３５】前記熱転写インクリボンをカラーバーコー
ドプリンタ（株式会社テック製ＣＢ−４１８：４連のカ
ラーバーコードプリンタ）により温度管理コード５を印
刷し、温度管理ラベル１を得た。このようにして得られ
た温度管理ラベル１は、図１３乃至図１７に示すような
特性で、次のように温度が分類できる。 （ａ）Ｔ＜５℃の場合 示温部材印刷エリア４：４−１、４−２に印刷された温
度管理コード５が、図１５に示すように読取不可である
（濃度の相対値で０．５以上で読取可能な読取装置を用
いる）。 （ｂ）５℃≦Ｔ＜１６℃の場合 示温部材印刷エリア４：４−１内の温度管理コード５だ
けが図１６に示すように読取可能になる。 （ｃ）Ｔ≧１６℃の場合 示温部材印刷エリア４：４−１と示温部材印刷エリア
２：４−２内の両方の温度管理コード５が図１７に示す
ように読取可能になる。The thermal transfer ink ribbon was printed with a temperature control code 5 using a color barcode printer (CB-418, manufactured by Tech Co., Ltd .: four color barcode printers) to obtain a temperature control label 1. The temperature management label 1 thus obtained can be classified into the following temperatures with the characteristics shown in FIGS. (A) When T <5 ° C. The temperature management code 5 printed on the temperature indicating member printing areas 4: 4-1 and 4-2 cannot be read as shown in FIG. Use a reading device that can read 5 or more). (B) When 5 ° C. ≦ T <16 ° C. Only the temperature management code 5 in the temperature indicating member printing area 4: 4-1 can be read as shown in FIG. (C) When T ≧ 16 ° C. Both the temperature management codes 5 in the temperature indicating member printing area 4: 4-1 and the temperature indicating member printing area 2: 4-2 become readable as shown in FIG.
【００３６】このように可逆式示温部材を用いると、現
在の管理温度が機械的にその範囲を特定できる。ここで
は２種類の示温部材を用いたがこれ以上にするとさらに
管理温度範囲を特定できる。By using the reversible temperature indicating member, the range of the current control temperature can be specified mechanically. Here, two types of temperature indicating members are used. However, if the number of the temperature indicating members is increased, the control temperature range can be further specified.
【００３７】次に、不可逆示温部材を用いる場合（反応
温度の異なる複数の示温部材を用いるか、またはその組
み合せの示温部材を用いる）、結晶−非結晶または相分
離−非相分離によるリライタブル系が利用可能である。Next, when an irreversible temperature indicating member is used (a plurality of temperature indicating members having different reaction temperatures or a combination of temperature indicating members is used), a rewritable system by crystal-amorphous or phase separation-non-phase separation is used. Available.
【００３８】．反応温度が異なる示温部材 ＜示温部材１＞ ・電子供与性呈色性化合物 フェニルメタン系化合物（各種フルオラン、フェニルフ
タリド類等）、各種インドリルフタリド、スピロピラ
ン、ロイコオーラミン類、アシルまたはアリールオーラ
ミン類など ・電子受容性化合物 フェノール性水酸基を有する化合物、フェノール性水酸
基を有する化合物の金属塩、各種トリアゾール類、カル
ボン酸類、カルボン酸の金属塩など ・可逆材 ステロイド系等 ＊電子供与性呈色性化合物：ＣＶＬ １重量部 ＊電子受容性化合物 ：没食子酸プロピル １重量部 ＊可逆材 ：コレステロール ５重量部 ＊樹脂 ：スチレンメタクリル酸共重合体（Ａ−１４Ｐ 大 日本インキ化学社製） ５重量部 をトルエンとシクロヘキサノンの１：１溶媒で完全に溶
解する。[0038] Temperature indicating members having different reaction temperatures <Temperature indicating member 1>-Electron-donating color-forming compound Phenylmethane-based compound (various fluorans, phenylphthalides, etc.), various indolylphthalides, spiropyrans, leuco-olamines, acyl or aryl Auramines, etc. ・ Electron-accepting compounds Compounds having a phenolic hydroxyl group, metal salts of compounds having a phenolic hydroxyl group, various triazoles, carboxylic acids, metal salts of carboxylic acids, etc. ・ Reversible materials Steroids, etc. * Electron donating Coloring compound: CVL 1 part by weight * Electron accepting compound: propyl gallate 1 part by weight * Reversible material: cholesterol 5 parts by weight * Resin: styrene methacrylic acid copolymer (A-14P, manufactured by Dainippon Ink and Chemicals, Inc.) 5 parts by weight Part is completely dissolved with a 1: 1 solvent of toluene and cyclohexanone.
【００３９】 ＊ワックス（３号） ２０重量部 ＊パラフィンワックス ５重量部 の混合物をボールミルで加熱しながら溶解したもを加え
（固形分２０％）、上述の溶解物を加え、自然冷却しな
がら分散をする。背面に耐熱層の付いた4.5μｍのＰＥ
Ｔ（ポリエチレンテレフタレート）フィルムにインク塗
工機により、塗工して熱転写インクリボンを得た。ガラ
ス転移点が２８℃前後であり、２８℃以上では徐々に発
色する。20 parts by weight of wax (No. 3) * A mixture of 5 parts by weight of paraffin wax dissolved while heating with a ball mill is added (solid content: 20%), the above-mentioned dissolved material is added, and the mixture is dispersed while cooling naturally. do. 4.5μm PE with heat-resistant layer on back
A T (polyethylene terephthalate) film was coated with an ink coater to obtain a thermal transfer ink ribbon. The glass transition point is around 28 ° C., and at 28 ° C. or higher, color gradually develops.
【００４０】 ＜示温部材２＞ ＊電子供与性呈色性化合物：ＣＶＬ １重量部 ＊電子受容性化合物 ：没食子酸プロピル １重量部 ＊可逆材 ：プレグネノロン ５重量部 ＊樹脂 ：スチレンメタクリル酸共重合体 １０重量部 をトルエンとシクロヘキサノンの１：１溶媒で完全に溶
解する。<Temperature Display Member 2> * Electron-donating color-forming compound: 1 part by weight of CVL * Electron-accepting compound: 1 part by weight of propyl gallate * Reversible material: 5 parts by weight of pregnenolone * Resin: styrene-methacrylic acid copolymer 10 parts by weight are completely dissolved in a 1: 1 solvent of toluene and cyclohexanone.
【００４１】 ＊ワックス（３号） ２０重量部 ＊パラフィンワックス ５重量部 の混合物をボールミルで加熱しながら溶解したもを加え
（固形分２０％）、上述の溶解物を加え、自然冷却しな
がら分散をする。背面に耐熱層の付いた4.5μｍのＰＥ
Ｔ（ポリエチレンテレフタレート）フィルムにインク塗
工機により、塗工して熱転写インクリボンを得た。示温
部材２のＴｇは４４℃であった。20 parts by weight of wax (No. 3) * A mixture of 5 parts by weight of paraffin wax dissolved while heating with a ball mill is added (solid content: 20%), and the above-mentioned dissolved material is added, followed by natural cooling and dispersion. do. 4.5μm PE with heat-resistant layer on back
A T (polyethylene terephthalate) film was coated with an ink coater to obtain a thermal transfer ink ribbon. Tg of the temperature indicating member 2 was 44 ° C.
【００４２】カラーバーコードプリンタ（株式会社テッ
ク製ＣＢ−４１８：４連のカラーバーコードプリンタ）
により、示温部材印刷エリア４：４−１に＜示温部材１
＞、示温部材印刷エリア４：４−２に＜示温部材２＞で
温度管理コード５を印刷し、温度管理部材１を得た。Color barcode printer (CB-418: 4 color barcode printers manufactured by Tech Co., Ltd.)
As a result, the temperature indicating member printing area 4: 4-1 becomes <temperature indicating member 1>.
> The temperature control code 5 was printed on the temperature indicating member printing area 4: 4-2 using <temperature indicating member 2>, and the temperature controlling member 1 was obtained.
【００４３】図１８からわかるように、＜示温部材１＞
は３０℃で約１時間で読取可能（発色濃度の相対値が
０．５以上）になり、＜示温部材２＞は４６℃約１時間
で読取可能になる。１時間の温度管理状況が前記温度管
理コード５を読取ることにより、可逆式を用いた場合と
同様に把握可能である。As can be seen from FIG. 18, <temperature indicating member 1>.
Becomes readable at 30 ° C. in about 1 hour (relative value of color density is 0.5 or more), and <temperature indicating member 2> becomes readable in about 1 hour at 46 ° C. By reading the temperature management code 5 for the one-hour temperature management status, it can be grasped in the same manner as in the case of using the reversible method.
【００４４】ガラス転移点により発色する時間や発色温
度が決定する系である。ガラス転移点は材料や配合比に
より左右されるので、同じ材料でも配合比によりコント
ロールすることも可能である。This is a system in which the color development time and color development temperature are determined by the glass transition point. Since the glass transition point depends on the material and the mixing ratio, the same material can be controlled by the mixing ratio.
【００４５】不可逆式においては図５に示すように、設
定温度以上（Ｔｇ以上）になると徐々に発色し、最終的
に飽和濃度に達する。この設定温度はこのインク系のガ
ラス転移点に相当し、非結晶で無色化している系がＴｇ
点以上で徐々に結晶化して発色するようになっている。
すなわち、サーマルヘッド等で加熱−急冷して、温度管
理コード５を印刷すると無色で固定される。この温度管
理コード５はガラス転移点（Ｔｇ）以上に暖まると徐々
に発色し、図１８に示すように時間により濃度が異な
る。この濃度が相対値で０．５に達した時に読み取れる
とすると、Ｔｇ＋２℃の温度の環境下に１時間以上曝さ
れたことがわかる。（温度と発色する時間は、可逆材等
の濃度によりコントロールすることが可能で、これに限
るものではない）。In the irreversible method, as shown in FIG. 5, when the temperature becomes higher than the set temperature (Tg or more), the color gradually develops, and finally reaches the saturation density. This set temperature corresponds to the glass transition point of this ink system, and the amorphous and colorless system has a Tg
Above the point, it gradually crystallizes and develops color.
That is, when the temperature management code 5 is printed after heating and quenching with a thermal head or the like, the color is fixed to be colorless. The temperature management code 5 gradually develops color when it is heated to a temperature equal to or higher than the glass transition point (Tg), and the density varies depending on time as shown in FIG. If it can be read when this concentration reaches a relative value of 0.5, it can be understood that it was exposed to the environment of Tg + 2 ° C. for 1 hour or more. (The temperature and the time for color development can be controlled by the concentration of a reversible material or the like, and are not limited thereto.)
【００４６】複数の示温部材により温度管理コード５が
印刷されているので、示温部材２の発色がなければ、１
時間経過後の温度は３０℃以上４６℃未満であることが
わかる。この示温部材の温度設定範囲が狭ければ、測定
環境温度が何度であるかを特定できることになることは
云うまでもない。また、目視であるとその管理時間があ
いまいになることは云うまでもない。ここでは反応温度
が異なり、発色時間がほぼ同じ特性を示す示温部材の例
を示したが、これに限るものでなく、例えば、ある温度
での発色速度が違う複数の示温部材を用いた場合、暴露
時間が特定できる。また、発色速度や発色温度が異なる
示温部材を複数設ければ、測定環境が把握できることは
云うまでもない。Since the temperature management code 5 is printed by a plurality of temperature indicating members, if the temperature indicating member 2 is not colored, 1
It can be seen that the temperature after the lapse of time is 30 ° C. or more and less than 46 ° C. It goes without saying that if the temperature setting range of the temperature indicating member is narrow, it is possible to specify the number of measurement environment temperatures. Needless to say, when viewed visually, the management time becomes ambiguous. Here, the reaction temperature is different, the example of the temperature indicating member showing the substantially same characteristics of the coloring time is shown, but the present invention is not limited to this.For example, when a plurality of temperature indicating members having different coloring speeds at a certain temperature are used, Exposure time can be specified. Further, it is needless to say that the measurement environment can be grasped by providing a plurality of temperature indicating members having different coloring speeds and coloring temperatures.
【００４７】次に、本発明の第四の実施の形態を図１９
に基づいて説明する。前記各実施の形態においては、温
度管理部材１をラベル状のものとして形成した状態につ
いて説明したが、本実施の形態は、段ボール紙等による
包装箱８に商品管理用バーコード３及び温度管理コード
５等を直接印刷したものである。従って、包装箱８毎に
冷蔵庫等に保管された状態の履歴を直接的に知ることが
でき、しかも、バーコードリーダ６等により機械読み取
りが可能となるものである。Next, a fourth embodiment of the present invention will be described with reference to FIG.
It will be described based on. In each of the above embodiments, the state in which the temperature management member 1 is formed as a label is described. However, in this embodiment, the product management barcode 3 and the temperature management code are provided on the packaging box 8 made of corrugated cardboard or the like. 5 is directly printed. Therefore, the history of the state stored in the refrigerator or the like for each packaging box 8 can be directly known, and further, machine reading by the bar code reader 6 or the like is possible.
【００４８】本発明の第五の実施の形態を図２０乃至図
２２に基づいて説明する。本実施の形態では、複数の示
温部材で複数の機械読み取り可能な温度管理コード５を
温度管理部材１内に設けたものである。すなわち、１つ
の温度管理コード５内に複数の示温部材で印刷した部分
を設けることにより、温度管理部材１の省資源化を図っ
た。A fifth embodiment of the present invention will be described with reference to FIGS. In the present embodiment, a plurality of machine-readable temperature management codes 5 are provided in the temperature management member 1 with a plurality of temperature indicating members. That is, by providing a portion printed with a plurality of temperature indicating members in one temperature management code 5, the resource saving of the temperature management member 1 is achieved.
【００４９】まず、図２０は機械読取可能なコードとし
て使用するＪＡＮ８を示したものである。すなわち、具
体的には、ＪＡＮ８は次のように、 ０：（０００１１０１） １：（００１１００１） ２：（００１００１１） ３：（０１１１１０１） ４：（０１０００１１） ５：（０１１０００１） ６：（０１０１１１１） ７：（０１１１０１１） ８：（０１１０１１１） ９：（０００１０１１） であり、これが印刷された印刷パターンが図２０に示さ
れている。このＪＡＮ８の印刷パターンを利用して、複
数の示温部材により印刷する。示温部材としては前述の
第三の実施の形態で使用したものをそのまま利用可能で
ある。First, FIG. 20 shows a JAN 8 used as a machine-readable code. That is, specifically, JAN8 is as follows: 0: (0001101) 1: (0011001) 2: (0010011) 3: (0111101) 4: (01000011) 5: (01100001) 6: (01011111) 7 : (0111011) 8: (0110111) 9: (0001011), and the print pattern on which this is printed is shown in FIG. Using the JAN8 print pattern, printing is performed by a plurality of temperature indicating members. The temperature indicating member used in the third embodiment can be used as it is.
【００５０】例えば、図２１(ａ)(ｂ)(ｃ)に示すよう
に、設定温度Ｔ１で反応する示温部材１を黒く塗りつぶ
した所に、ハッチングされた部分を連ねて示温部材２に
よりその領域を印刷する。ただし、Ｔ１＜Ｔ２とする。
このようにして得られた印刷パターンは、環境温度Ｔが
Ｔ２＞Ｔ＞Ｔ１を満足した場合、示温部材１が印刷され
た部分が発色する。すなわち図２１(ａ)は４を意味す
る。図２１(ｂ)は９になり、図２１(ｃ)は０になる。そ
して、環境温度ＴがＴ＞Ｔ２となった場合、図２１(ａ)
は６に変化する。図２１(ｂ)は７に変化し、図２１(ｃ)
は３に変化する。この原理により、詳細な理由は後述す
るが、環境温度ＴがＴ２＞Ｔ＞Ｔ１の時の図２２(ａ)に
示す「４９０００００９」なるバーコードは、環境温度
ＴがＴ＞Ｔ２となった場合のバーコードは「６７３０３
００７」となるように設定することができる。For example, as shown in FIGS. 21 (a), 21 (b) and 21 (c), the temperature indicating member 1 which reacts at the set temperature T1 is blacked out, and the hatched portion is connected by the temperature indicating member 2 to the area. Print. However, it is assumed that T1 <T2.
In the printing pattern thus obtained, when the environmental temperature T satisfies T2>T> T1, a portion where the temperature indicating member 1 is printed develops a color. That is, FIG. 21 (b) is 9 and FIG. 21 (c) is 0. Then, when the environmental temperature T becomes T> T2, FIG.
Changes to 6. FIG. 21 (b) changes to 7 and FIG. 21 (c)
Changes to 3. According to this principle, a detailed reason will be described later. However, when the environmental temperature T is T2>T> T1, the bar code “49000009” shown in FIG. The bar code is “67303
007 ”.
【００５１】これを用いてＪＡＮ８のコードでは下記の
ような組み合せが可能である（×は読取不可）。 環境温度： Ｔ１＞Ｔ Ｔ２＞Ｔ＞Ｔ１ Ｔ＞Ｔ２ × ０ ３ × ０ ６ × １ ３ × １ ７ × ２ ７ × ２ ８ × ４ ６ × ４ ７ × ４ ８ × ５ ７ × ５ ８ × ９ ７ 図２２(ａ)はＪＡＮ８コードが＜４９００００９＞にな
っているが、実際には下記のような印刷がされている。
（なお、左の４から示してある。） 図１１(a)に相当 図１１(b)に相当 環境温度 Ｔ＜Ｔ１ Ｔ２＞Ｔ＞Ｔ１ Ｔ＞Ｔ２ ４： 無色 → ４ → ６ に変化する印刷パターン ９： 無色 → ９ → ７ に変化する印刷パターン ０： 無色 → ０ → ３ に変化する印刷パターン ０： 無色 → ０ → ０ 示温部材１だけで０を印刷 ０： 無色 → ０ → ３ に変化する印刷パターン ０： 無色 → ０ → ０ 示温部材１だけで０を印刷 ０： 無色 → ０ → ０ 示温部材１だけで０を印刷 ９： 無色 → ９ → ７ に変化する印刷パターン 以上のように変化するように示温部材１または２で印刷
することにより１つの温度管理コードで温度範囲を指定
することが可能であることがわかる。すなわち、Ｔ＜Ｔ
１の時は読取り不可、Ｔ２＞Ｔ＞Ｔ１の時＜４９０００
００９＞として認識する。Ｔ＞Ｔ２の時＜６７３０３０
０７＞として認識する。機械コード読取装置がどのコー
ドを認識したかにより、環境状況を把握できる。Using this, the following combinations are possible in the JAN8 code (x is not readable). Environmental temperature: T1> T T2>T> T1 T> T2 × 03 × 06 × 13 × 17 × 27 × 28 × 46 × 47 × 48 × 57 × 58 × 97 × 97 In FIG. 22A, the JAN8 code is <4900009>, but actually, the following printing is performed.
(Incidentally, it is shown from 4 on the left.) Corresponding to FIG. 11 (a) Corresponding to FIG. 11 (b) Environmental temperature T <T1 T2>T> T1 T> T2 4: Printing that changes from colorless to 4 to 6 Pattern 9: Print pattern changing to colorless → 9 → 7 0: Print pattern changing to colorless → 0 → 3 0: Print colorless → 0 → 0 Print 0 only with temperature indicator 1 0: Colorless → Change to 0 → 3 Print pattern 0: colorless → 0 → 0 Print 0 only with temperature indicator 1 0: Colorless → 0 → 0 Print 0 only with temperature indicator 1 9: Colorless → print pattern that changes to 9 → 7 Changes as above Thus, it can be seen that by printing with the temperature indicating member 1 or 2, it is possible to specify the temperature range with one temperature management code. That is, T <T
When it is 1, reading is impossible, and when T2>T> T1, it is <49000.
009>. When T> T2 <673030
07>. The environmental status can be grasped based on which code is recognized by the machine code reader.
【００５２】ここでは、ＪＡＮ８を用いたが、これに限
定されるものでなく、ＪＡＮ、コード３９、ＮＷ７、Ｉ
ＴＦ、コード１２８、コード４９、コード９３、オリジ
ナルのコード等でも良く、１次元だけでなく２次元コー
ドでも良いことは云うまでもない。また、温度を管理す
るだけの意味では商品管理コード３と同じ体系でなくて
もよい。Here, JAN8 is used, but the present invention is not limited to this. JAN, code 39, NW7,
Needless to say, TF, code 128, code 49, code 93, an original code, etc., and not only a one-dimensional code but also a two-dimensional code may be used. Further, the system does not have to be the same system as the product management code 3 only in the sense of managing the temperature.
【００５３】また、発色の色が青または黒の例を示した
が、読取装置が対応する色であれば何でもよい。Although the example in which the color is blue or black has been described, any color may be used as long as the reading device corresponds to the color.
【００５４】さらに、前記各実施の形態では、熱転写イ
ンクリボンの例を示したがこれに限定されることがな
い。また、示温材料として呈色性化合物と顕色剤、可逆
材等の方法を用いたがこれに限定されるものではない。Further, in each of the above embodiments, an example of the thermal transfer ink ribbon has been described, but the present invention is not limited to this. In addition, a method using a color developing compound, a color developer, a reversible material, or the like was used as the temperature indicating material, but is not limited thereto.
【００５５】[0055]
【発明の効果】請求項１記載の発明は、温度に反応し色
が変化する示温部材で情報が印刷または塗布された温度
管理部材において、前記情報が機械読み取り可能な符号
であるので、個人的な視認による判断等による誤差がな
く、機械読取により商品等が保存された環境温度を管理
することができると云う効果を有する。According to the first aspect of the present invention, in a temperature control member on which information is printed or applied by a temperature indicating member whose color changes in response to temperature, since the information is a machine-readable code, it can be used for personal use. There is no error due to a visual recognition, and the environmental temperature at which a product or the like is stored can be managed by machine reading.
【００５６】請求項２記載の発明は、温度に反応し色が
変化する示温部材で印刷された温度管理部材において、
前記示温部材で印刷または塗布された部分の上または下
部に有色インクで機械読み取り可能な温度管理コードが
印刷または塗布され、前記示温部材の変色前または変色
後の色が前記有色インクの機械読み取り可能な温度管理
コードを読取る読取装置の光源の波長を吸収するように
したので、小さな領域に温度管理コードを印刷すること
ができると云う効果を有する。According to a second aspect of the present invention, there is provided a temperature control member printed with a temperature indicating member that changes color in response to temperature,
A machine-readable temperature management code is printed or applied with colored ink on the upper or lower part printed or applied with the temperature indicating member, and the color of the temperature indicating member before or after discoloration is machine readable of the colored ink. Since the wavelength of the light source of the reading device that reads the temperature control code is absorbed, the temperature control code can be printed in a small area.
【００５７】請求項３記載の発明は、示温部材は使用環
境下で不可逆性であるようにしたので、温度管理部材が
おかれた環境状態の履歴を確実に得ることができると云
う効果を有する。According to the third aspect of the present invention, since the temperature indicating member is made irreversible under the use environment, there is an effect that the history of the environmental state in which the temperature control member is placed can be reliably obtained. .
【００５８】請求項４記載の発明は、機械読み取り可能
な符号が複数の示温部材を印刷または塗布することによ
り形成されているので、複数の温度領域の管理を容易に
行なうことができると云う効果を有する。According to the fourth aspect of the present invention, since the machine-readable code is formed by printing or applying a plurality of temperature indicating members, a plurality of temperature regions can be easily managed. Having.
【００５９】請求項５記載の発明は、温度特性が異なる
複数の示温部材を用いるので、複数の温度領域の管理を
容易に行なうことができると云う効果を有する。According to the fifth aspect of the invention, since a plurality of temperature indicating members having different temperature characteristics are used, there is an effect that a plurality of temperature regions can be easily managed.
【００６０】請求項６記載の発明は、機械読み取り可能
な温度管理コードを複数の示温部材で印刷し、設定温度
に応じ機械読み取り温度管理コードが変化するので、数
値的に変化する状態で温度管理を行なうことができると
云う効果を有する。According to a sixth aspect of the present invention, since a machine-readable temperature management code is printed by a plurality of temperature indicating members and the machine-readable temperature management code changes in accordance with the set temperature, the temperature management code is changed numerically. Has the effect of being able to perform
【００６１】請求項７記載の発明は、複数の示温部材が
使用環境下で不可逆性材料で構成されているので、複数
の温度領域の環境下における履歴を正確に得ることがで
きると云う効果を有する。According to the seventh aspect of the present invention, since the plurality of temperature indicating members are made of an irreversible material under the use environment, the effect that the history in the environment of the plurality of temperature ranges can be obtained accurately can be obtained. Have.
【００６２】請求項８記載の発明は、商品等の情報を機
械読取可能な商品管理コードと温度で色が変化する１つ
または複数の示温部材で機械読み取り可能な温度管理コ
ードとが印刷または塗布された温度管理部材を用い、前
記温度管理コードにより温度範囲を管理するようにした
ので、個人的な視認による判断等による誤差がなく、機
械読取により温度や暴露時間を管理することができると
云う効果を有する。According to an eighth aspect of the present invention, a product management code capable of machine-readable information on a product or the like and a temperature management code machine-readable by one or more temperature indicating members whose color changes with temperature are printed or applied. Since the temperature range is managed by the temperature management code using the temperature management member set as above, there is no error due to the judgment by the individual visual recognition, and the temperature and the exposure time can be managed by the machine reading. Has an effect.
【図１】本発明の第一の実施の形態を示すもので、温度
管理部材の平面図である。FIG. 1 is a plan view of a temperature management member according to a first embodiment of the present invention.
【図２】設定温度以下で管理された状態を示す温度管理
部材の平面図である。FIG. 2 is a plan view of a temperature management member showing a state where the temperature is controlled below a set temperature.
【図３】設定温度以上で管理された状態を示す温度管理
部材の平面図である。FIG. 3 is a plan view of a temperature management member showing a state where the temperature is controlled at a set temperature or higher.
【図４】可逆性の示温部材の温度と濃度との関係を示す
グラフである。FIG. 4 is a graph showing the relationship between the temperature and the concentration of a reversible temperature indicating member.
【図５】示温部材の所定の温度下における経過時間と濃
度との関係を示すグラフである。FIG. 5 is a graph showing a relationship between elapsed time and concentration at a predetermined temperature of a temperature indicating member.
【図６】示温部材の物理的変態の状態を示す説明図であ
る。FIG. 6 is an explanatory diagram showing a physical transformation state of the temperature indicating member.
【図７】機械読み取りにより商品コードのみが読取可能
である状態を示す平面図である。FIG. 7 is a plan view showing a state where only a product code can be read by machine reading.
【図８】機械読み取りにより商品コードと温度管理コー
ドとの両方が読取可能である状態を示す平面図である。FIG. 8 is a plan view showing a state where both a product code and a temperature management code can be read by machine reading.
【図９】本発明の第二の実施の形態を示すもので、温度
管理部材の平面図である。FIG. 9 shows a second embodiment of the present invention, and is a plan view of a temperature management member.
【図１０】設定温度以下で管理された状態を示す温度管
理部材の平面図である。FIG. 10 is a plan view of the temperature management member showing a state where the temperature is controlled below a set temperature.
【図１１】設定温度以上で管理された状態を示す温度管
理部材の平面図である。FIG. 11 is a plan view of a temperature management member showing a state where the temperature is controlled at a set temperature or higher.
【図１２】機械読み取りにより商品コードのみが読取可
能である状態を示す平面図である。FIG. 12 is a plan view showing a state in which only a product code can be read by machine reading.
【図１３】機械読み取りにより商品コードと温度管理コ
ードとの両方が読取可能である状態を示す平面図であ
る。FIG. 13 is a plan view showing a state where both a product code and a temperature management code can be read by machine reading.
【図１４】本発明の第三の実施の形態を示す温度管理部
材の平面図である。FIG. 14 is a plan view of a temperature management member according to a third embodiment of the present invention.
【図１５】環境温度がＴ１以下の場合の温度管理部材の
平面図である。FIG. 15 is a plan view of the temperature management member when the environmental temperature is equal to or lower than T1.
【図１６】環境温度がＴ１からＴ２の範囲の場合の温度
管理部材の平面図である。FIG. 16 is a plan view of the temperature management member when the environmental temperature is in a range from T1 to T2.
【図１７】環境温度がＴ２以上の場合の温度管理部材の
平面図である。FIG. 17 is a plan view of the temperature management member when the environmental temperature is equal to or higher than T2.
【図１８】示温部材の物理的変態の状態を示す説明図で
ある。FIG. 18 is an explanatory diagram showing a physical transformation state of the temperature indicating member.
【図１９】本発明の第四の実施の形態を示す斜視図であ
る。FIG. 19 is a perspective view showing a fourth embodiment of the present invention.
【図２０】本発明の第五の実施の形態を示すもので、０
から９のＪＡＮコードを示すパターン図である。FIG. 20 shows a fifth embodiment of the present invention, in which 0
9 is a pattern diagram showing JAN codes No. 9 to No. 9. FIG.
【図２１】二種の示温部材によりコードが変化する状態
を示すもので、(ａ)は４から６の変化、(ｂ)は９から７
の変化、(ｃ)は０から３の変化を示すものである。FIGS. 21A and 21B show a state in which a cord is changed by two types of temperature indicating members, wherein FIG. 21A shows a change from 4 to 6, and FIG.
(C) shows a change from 0 to 3.
【図２２】二種の示温部材によりバーコードとして変化
する状態を示すもので、(ａ)は「４９０００００９」を
表示し、(ｂ)は「６７３０３００７」を表示するもので
ある。FIGS. 22A and 22B show a state of changing as a bar code by two kinds of temperature indicating members, where FIG. 22A shows “49000009” and FIG. 22B shows “67303007”.
１ 温度管理部材 ３ 商品管理コード ５ 温度管理コード 1 Temperature management member 3 Product management code 5 Temperature management code
Claims (8)
報が印刷または塗布された温度管理部材において、前記
情報が機械読み取り可能な符号であることを特徴とする
温度管理部材。1. A temperature management member on which information is printed or applied by a temperature indicating member whose color changes in response to temperature, wherein the information is a machine-readable code.
刷された温度管理部材において、前記示温部材で印刷ま
たは塗布された部分の上または下部に有色インクで機械
読み取り可能な商品管理コードが印刷または塗布され、
前記示温部材の変色前または変色後の色が前記有色イン
クの機械読み取り可能な商品管理コードを読取る読取装
置の光源の波長を吸収することを特徴とする温度管理部
材。2. A temperature management member printed with a temperature indicating member whose color changes in response to temperature, wherein a product management code readable by machine with colored ink is provided above or below a portion printed or applied with the temperature indicating member. Printed or coated,
A temperature management member, wherein a color before or after the color change of the temperature indicating member absorbs a wavelength of a light source of a reader for reading a machine-readable commodity management code of the colored ink.
ことを特徴とする請求項１又は２記載の温度管理部材。3. The temperature control member according to claim 1, wherein the temperature indicating member is irreversible in a use environment.
材を印刷または塗布することにより形成されていること
を特徴とする請求項１又は２記載の温度管理部材。4. The temperature management member according to claim 1, wherein the machine-readable code is formed by printing or applying a plurality of temperature indicating members.
ることを特徴とする請求項４記載の温度管理部材。5. The temperature management member according to claim 4, wherein a plurality of temperature indicating members having different temperature characteristics are used.
数の示温部材で印刷し、設定温度に応じ機械読み取り可
能な商品管理コードが変化することを特徴とする請求項
４又は５記載の温度管理部材。6. The temperature management member according to claim 4, wherein a machine readable product management code is printed by a plurality of temperature indicating members, and the machine readable product management code changes according to a set temperature. .
材料で構成されていることを特徴とする請求項４，５又
は６記載の温度管理部材。7. The temperature control member according to claim 4, wherein the plurality of temperature indicating members are made of an irreversible material under a use environment.
コードと温度で色が変化する１つまたは複数の示温部材
で機械読み取り可能な商品管理コードとが印刷または塗
布された温度管理部材を用い、前記商品管理コードによ
り温度範囲を管理するようにしたことを特徴とする温度
管理方法。8. A temperature management member printed or coated with a product management code capable of machine-readable information such as a product and a product management code machine-readable by one or more temperature indicating members whose color changes with temperature. A temperature management method, wherein a temperature range is managed by the product management code.