JPH11216315A - Cleaning filter manufacture, cleaning filter, and cleaning apparatus - Google Patents
Cleaning filter manufacture, cleaning filter, and cleaning apparatusInfo
- Publication number
- JPH11216315A JPH11216315A JP10019516A JP1951698A JPH11216315A JP H11216315 A JPH11216315 A JP H11216315A JP 10019516 A JP10019516 A JP 10019516A JP 1951698 A JP1951698 A JP 1951698A JP H11216315 A JPH11216315 A JP H11216315A
- Authority
- JP
- Japan
- Prior art keywords
- titanium oxide
- glass
- granular
- filter
- purification
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本願発明は、酸化チタンの光
触媒機能を利用した浄化フィルターの製造方法、浄化フ
ィルターおよび浄化装置に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for manufacturing a purifying filter utilizing a photocatalytic function of titanium oxide, a purifying filter and a purifying apparatus.
【０００２】[0002]
【従来の技術】一般に、半導体にそのバンドギャップ
（禁制帯幅）以上のエネルギーをもつ波長の光を照射す
ると、価電子帯の電子がその光エネルギーを吸収して励
起され伝導帯へ移動し、半導体内部に電子・正孔対が発
生することはよく知られている。2. Description of the Related Art Generally, when a semiconductor is irradiated with light having a wavelength greater than its band gap (forbidden band), electrons in a valence band absorb the light energy and are excited to move to a conduction band. It is well known that electron-hole pairs are generated inside a semiconductor.
【０００３】酸化チタンも上記と同様な性質を有してお
り、特定波長（例えば、３８０ｎｍ以下の波長）の光に
より光励起となる。この電子と正孔が酸化チタン表面に
拡散移動し、表面に吸着している物質と反応する光触媒
反応を起こす。[0003] Titanium oxide also has the same properties as described above, and is photo-excited by light of a specific wavelength (for example, a wavelength of 380 nm or less). The electrons and holes diffuse and move to the surface of the titanium oxide, causing a photocatalytic reaction in which the electrons and holes react with the substance adsorbed on the surface.
【０００４】近年、上記酸化チタンの光触媒機能は、抗
菌・抗カビ作用を利用する抗菌・抗カビ分野、脱臭・空
気清浄作用を利用する脱臭・空気清浄分野、有害物質を
分解する作用を利用する水処理分野、超親水化現象を利
用する防汚・防曇分野において注目されるようになって
きている。[0004] In recent years, the photocatalytic function of titanium oxide has been used in the field of antibacterial and antifungal utilizing antibacterial and antifungal actions, in the field of deodorizing and air cleaning utilizing deodorizing and air cleaning actions, and in the action of decomposing harmful substances. In the field of water treatment and the field of antifouling and antifogging utilizing the superhydrophilization phenomenon, attention has been given.
【０００５】上記した酸化チタンの光触媒機能に着目し
て、酸化チタンを球状に成形したガラスの表面にコーテ
ィングしたものを用いて、水浄化を行う方法が開発され
ている。[0005] Focusing on the photocatalytic function of titanium oxide, a method of purifying water using a glass obtained by coating titanium oxide in a spherical shape has been developed.
【０００６】[0006]
【発明が解決しようとする課題】ところが、上記のよう
な方法の場合、球状ガラスをバラバラで使用すると、水
の流速が早いところでは球状ガラスが流されるおそれが
あり、利用範囲が限定されるという不具合がある。ま
た、球状ガラスを何らかの容器に収納して使用すると、
特別な容器が必要となり、コスト的に不利となる。However, in the case of the above-mentioned method, if the spherical glass is used separately, there is a possibility that the spherical glass may flow at a place where the flow rate of water is high, and the range of use is limited. There is a defect. Also, if you use spherical glass stored in some container,
Special containers are required, which is disadvantageous in terms of cost.
【０００７】本願発明は、上記のような不具合を解消す
るためになされたもので、酸化チタンをコーティングし
た粒状ガラスの集合体を所定形状に成形することによ
り、利用範囲が限定されることもなく、吸水性、保水性
に優れ、しかも高い光触媒機能を保持した浄化フィルタ
ーを得ることを第１の目的とし、このような浄化フィル
ターを用いた高性能の浄化装置を提供することを第２の
目的とするものである。The present invention has been made in order to solve the above-mentioned problems, and the use range is not limited by forming an aggregate of granular glass coated with titanium oxide into a predetermined shape. A first object is to obtain a purification filter which is excellent in water absorption and water retention and retains a high photocatalytic function, and a second object is to provide a high-performance purification apparatus using such a purification filter. It is assumed that.
【０００８】[0008]
【課題を解決するための手段】請求項１の発明では、上
記課題を解決するために、表面に酸化チタン液を塗布し
た粒状ガラスを、所定形状の型内に収納して所定温度で
加熱処理することにより、前記粒状ガラス同士を溶着さ
せて所定形状に一体化すると同時に粒状ガラスの表面に
塗布された酸化チタンを定着させることにより、所定形
状の浄化フィルターを製造するようにしている。According to the first aspect of the present invention, in order to solve the above-mentioned problem, a granular glass having a surface coated with a titanium oxide liquid is housed in a mold having a predetermined shape and heated at a predetermined temperature. By doing so, the granular glass is welded together and integrated into a predetermined shape, and at the same time, the titanium oxide applied on the surface of the granular glass is fixed, thereby producing a purification filter of a predetermined shape.
【０００９】上記のようにしたことにより、粒状ガラス
の溶着一体化と同時に酸化チタンの定着が得られること
となり、製造工程の簡略化が図れる。また、得られる浄
化フィルターは、高い光触媒機能を保持し、しかも設置
個所が限定されることもなく、また、定形性を有してい
るので各種の浄化装置にも適用可能となる。さらに、吸
水性、保水性に優れているため、浄化能力の相乗化をも
図ることができる。さらにまた、光触媒機能の一つであ
る汚れを落ちやすくする効果により、汚れが着いても何
度でも水洗いすることができるため、再利用が可能とな
る。[0009] By the above-mentioned method, the fixing of titanium oxide can be obtained simultaneously with the fusion and integration of the granular glass, and the manufacturing process can be simplified. Further, the obtained purification filter has a high photocatalytic function, is not limited in its installation location, and has a fixed form, so that it can be applied to various purification devices. Furthermore, since it is excellent in water absorption and water retention, synergistic purifying ability can be achieved. Still further, the effect of easily removing dirt, which is one of the photocatalytic functions, can be washed as many times as possible even when dirt arrives, so that it can be reused.
【００１０】請求項３の発明では、上記課題を解決する
ために、表面に酸化チタンのコーティング層を有する粒
状ガラス同士が所定形状に溶着一体化している。According to the third aspect of the present invention, in order to solve the above-mentioned problems, granular glasses having a coating layer of titanium oxide on their surfaces are welded and integrated in a predetermined shape.
【００１１】上記のように構成したことにより、高い光
触媒機能を保持し、しかも設置個所が限定されることも
なく、また、定形性を有しているので各種の浄化装置に
も適用可能となる。さらに、吸水性、保水性に優れてい
るため、浄化能力の相乗化をも図ることができる。さら
にまた、光触媒機能の一つである汚れを落ちやすくする
効果により、汚れが着いても何度でも水洗いすることが
できるため、再利用が可能となる。[0011] With the above-mentioned structure, the photocatalyst function is maintained, the installation location is not limited, and since it has a fixed shape, it can be applied to various purification devices. . Furthermore, since it is excellent in water absorption and water retention, synergistic purifying ability can be achieved. Still further, the effect of easily removing dirt, which is one of the photocatalytic functions, can be washed as many times as possible even when dirt arrives, so that it can be reused.
【００１２】請求項５の発明では、上記課題を解決する
ために、表面に酸化チタンのコーティング層を有する粒
状ガラス同士が所定形状に溶着一体化されている浄化フ
ィルターを用いて浄化装置を構成している。According to a fifth aspect of the present invention, in order to solve the above-mentioned problems, a purifying apparatus is constituted by using a purifying filter in which granular glasses each having a titanium oxide coating layer on the surface are welded and integrated in a predetermined shape. ing.
【００１３】このようにしたことにより、高性能の浄化
装置が低コストで得られる。By doing so, a high-performance purifying device can be obtained at low cost.
【００１４】請求項２、４および６の発明におけるよう
に、前記粒状ガラスとして、ガラス瓶等のリサイクル時
に生成されるガラスカレットを用いた場合、廃品の有効
利用が可能となり、より一層のコストダウンを図ること
ができる。When the glass cullet generated at the time of recycling a glass bottle or the like is used as the granular glass as in the inventions of claims 2, 4 and 6, it is possible to effectively use waste and further reduce costs. Can be planned.
【００１５】[0015]
【発明の実施の形態】以下、添付の図面を参照して、本
願発明の好適な実施の形態について詳述する。Preferred embodiments of the present invention will be described below in detail with reference to the accompanying drawings.
【００１６】まず、図１を参照して本実施の形態にかか
る浄化フィルターの製造方法を説明する。First, a method for manufacturing a purification filter according to this embodiment will be described with reference to FIG.
【００１７】ガラス瓶等のリサイクル時に生成されるガ
ラスカレット１の表面に、酸化チタンを塗布して酸化チ
タン層２を形成する〔図１（イ）参照〕。このガラスカ
レット１の粒径は、平均５ｍｍ程度が望ましい。また、
酸化チタン層２の膜厚は、０．５〜５μｍが望ましい。
なお、酸化チタン層２の膜厚が０．５μｍ未満の場合、
酸化チタンの量が不足して十分な光触媒機能が得られな
いし、酸化チタン層２の膜厚が５μｍを超えると、後述
する熱処理後に酸化チタン層２が不透明となり、光の到
達を阻害するおそれがある。Titanium oxide is applied to the surface of a glass cullet 1 generated during recycling of a glass bottle or the like to form a titanium oxide layer 2 (see FIG. 1A). The average particle size of the glass cullet 1 is preferably about 5 mm. Also,
The thickness of the titanium oxide layer 2 is preferably 0.5 to 5 μm.
When the thickness of the titanium oxide layer 2 is less than 0.5 μm,
If the amount of titanium oxide is insufficient, a sufficient photocatalytic function cannot be obtained, and if the thickness of the titanium oxide layer 2 exceeds 5 μm, the titanium oxide layer 2 becomes opaque after a heat treatment described later, which may hinder the arrival of light. is there.
【００１８】上記工程を経たガラスカレット１，１・・
を、図１（ロ）に示すように、所定形状の型３内に収納
し、該型３を、炉内に入れてガラスカレット１，１・・
相互間に隙間ができるように（即ち、ガラスカレット
１，１・・同士が部分的に溶着するように）、加熱処理
して所定形状に一体化し、その後炉内にて自然冷却し
て、図１（ハ）に示すような直方体形状の浄化フィルタ
ー４を製造する。この加熱処理の際には、酸化チタン層
２がガラスカレット１の表面に定着される（換言すれ
ば、コーティングされる）。上記加熱処理における加熱
条件は、７００〜８００℃で２〜３時間とされるが、本
実施の形態の場合、７４０℃で２．５時間、昇温速度
２．３℃／ｍｉｎとされる。The glass cullet 1, 1...
Is housed in a mold 3 having a predetermined shape, as shown in FIG. 1 (b), and the mold 3 is placed in a furnace and the glass cullets 1, 1,.
Heat treatment is performed to integrate them into a predetermined shape so that a gap is formed between them (that is, so that the glass cullets 1, 1... Are partially welded to each other), and then naturally cooled in a furnace. A purifying filter 4 having a rectangular parallelepiped shape as shown in FIG. During this heat treatment, the titanium oxide layer 2 is fixed on the surface of the glass cullet 1 (in other words, it is coated). The heating conditions in the heat treatment are 700 to 800 ° C. for 2 to 3 hours. In the case of the present embodiment, the heating is performed at 740 ° C. for 2.5 hours and at a heating rate of 2.3 ° C./min.
【００１９】上記浄化フィルター４の厚さｔは、その中
心部への光の到達を確保する必要があるところから、３
０ｍｍ以下とされる。厚さｔが３０ｍｍを超えると、中
心部への光の到達量が減少し、ガラスカレット１におけ
る酸化チタン層２の光触媒機能が不十分となる。The thickness t of the purifying filter 4 is set at 3 because it is necessary to ensure that light reaches the center of the filter.
0 mm or less. When the thickness t exceeds 30 mm, the amount of light reaching the center decreases, and the photocatalytic function of the titanium oxide layer 2 in the glass cullet 1 becomes insufficient.
【００２０】上記のようにして得られた浄化フィルター
４は、酸化チタンへの光の接触面積が大幅に増大すると
ともに、ガラスカレット１，１・・間に形成される隙間
の存在により、高通水性、高通気性、高吸水性、高保水
性を有するものとなる。The purification filter 4 obtained as described above has a large water contact area with the titanium oxide, and has a high water permeability due to the presence of the gap formed between the glass cullets 1, 1... It has high air permeability, high water absorption and high water retention.
【００２１】上記製造方法によれば、ガラスカレット
１，１・・の溶着一体化と同時に酸化チタン層２の定着
が得られることとなり、製造工程の簡略化が図れる。ま
た、得られる浄化フィルター４は、高い光触媒機能を保
持し、しかも設置個所が限定されることもなく、また、
定形性を有しているとともに、高い通水性および通気性
を有しているので各種の浄化装置にも適用可能となる。
さらに、上記したように吸水性、保水性に優れているた
め、浄化能力の相乗化をも図ることができる。さらにま
た、光触媒機能の一つである汚れを落ちやすくする効果
により、汚れが着いても何度でも水洗いすることができ
るため、再利用が可能となる。According to the above manufacturing method, the fixing of the titanium oxide layer 2 can be obtained at the same time as the welding and integration of the glass cullets 1, 1,..., And the manufacturing process can be simplified. Further, the obtained purification filter 4 retains a high photocatalytic function, and is not limited in its installation location.
Since it has a fixed shape and high water permeability and air permeability, it can be applied to various purification devices.
Further, as described above, since it is excellent in water absorption and water retention, synergistic purifying ability can be achieved. Still further, the effect of easily removing dirt, which is one of the photocatalytic functions, can be washed as many times as possible even when dirt arrives, so that it can be reused.
【００２２】図２には、本実施の形態にかかる浄化フィ
ルター４の使用例である水浄化装置が示されている。FIG. 2 shows a water purification apparatus as an example of use of the purification filter 4 according to the present embodiment.
【００２３】この水浄化装置は、薄板形状とされた複数
枚の浄化フィルター４，４・・を傾斜させて水槽５の上
方に棚状に設け、これらの浄化フィルター４，４・・の
上方から前記水槽５内の水を流すように構成されてい
る。符号６は汲み上げポンプ、７は浄化フィルター４を
支持する支持枠である。このように構成された水浄化装
置の場合、各浄化フィルター４を構成するガラスカレッ
ト１，１・・に対する光Ｉの照射が十分に得られること
となり、効率的に光触媒機能を向上させることができ
る。In this water purification apparatus, a plurality of thin-plate-shaped purification filters 4, 4,... Are inclined and provided in a shelf above a water tank 5, and from above these purification filters 4, 4,. The water in the water tank 5 is configured to flow. Reference numeral 6 denotes a pump, and reference numeral 7 denotes a support frame for supporting the purification filter 4. In the case of the water purification device configured as described above, the irradiation of the light I to the glass cullets 1, 1,... Constituting each purification filter 4 can be sufficiently obtained, and the photocatalytic function can be efficiently improved. .
【００２４】図３には、本実施の形態にかかる浄化フィ
ルター４の使用例である水浄化装置が示されている。FIG. 3 shows a water purification apparatus as an example of use of the purification filter 4 according to the present embodiment.
【００２５】この場合、透明な水槽８内の側面に沿うよ
うにして薄板形状とされた複数枚の浄化フィルター４，
４・・を配設している。このように構成された水浄化装
置の場合、各浄化フィルター４を構成するガラスカレッ
ト１，１・・に対する光Ｉの照射が十分に得られること
となり、効率的に光触媒機能を向上させることができ
る。In this case, a plurality of purification filters 4, which are formed in a thin plate along the side surface in the transparent water tank 8,
4 ... is arranged. In the case of the water purification device configured as described above, the irradiation of the light I to the glass cullets 1, 1,... Constituting each purification filter 4 can be sufficiently obtained, and the photocatalytic function can be efficiently improved. .
【００２６】図４には、本実施の形態にかかる浄化フィ
ルター４の使用例である空気浄化装置が示されている。FIG. 4 shows an air purifying apparatus as an example of using the purifying filter 4 according to the present embodiment.
【００２７】この場合、薄板円盤形状とされた浄化フィ
ルター４を円筒状の透明容器からなる空気通路９内に配
設して構成されている。符号１０は空気循環装置であ
る。このように構成された空気浄化装置の場合、各浄化
フィルター４を構成するガラスカレット１，１・・に対
する光Ｉの照射が十分に得られることとなり、効率的に
光触媒機能を向上させることができる。なお、光Ｉとし
て太陽光を利用できない場合には、空気通路８内に紫外
線ランプを設置すればよい。In this case, the cleaning filter 4 having a thin disk shape is disposed in an air passage 9 formed of a cylindrical transparent container. Reference numeral 10 denotes an air circulation device. In the case of the air purification device configured as described above, the irradiation of the light I to the glass cullets 1, 1,... Constituting each purification filter 4 is sufficiently obtained, and the photocatalytic function can be efficiently improved. . If sunlight cannot be used as the light I, an ultraviolet lamp may be provided in the air passage 8.
【００２８】上記以外にも、本実施の形態にかかる浄化
フィルターは、冷蔵庫内の殺菌、クーラや煙草の集塵装
置としての利用も可能である。In addition to the above, the purification filter according to the present embodiment can be used as a sterilizer in a refrigerator, and a dust collector for coolers and cigarettes.
【００２９】なお、本実施の形態においては、廃ガラス
瓶の破砕により生ずるガラスカレットの表面に酸化チタ
ン層を形成したものを用いたが、これにに代えてガラス
原材料から球状化したものに酸化チタン層を形成したも
のを用いてもよい。In the present embodiment, a glass cullet formed by crushing a waste glass bottle and having a titanium oxide layer formed on the surface is used. What formed the layer may be used.
【００３０】[0030]
【発明の効果】請求項１の発明によれば、表面に酸化チ
タン液を塗布した粒状ガラスを、所定形状の型内に収納
して所定温度で加熱処理することにより、前記粒状ガラ
ス同士を溶着させて所定形状に一体化すると同時に粒状
ガラスの表面に塗布された酸化チタンを定着させること
により、所定形状の浄化フィルターを製造するようにし
たので、粒状ガラスの溶着一体化と同時に酸化チタンの
定着が得られることとなり、製造工程の簡略化が図れる
という優れた効果がある。また、得られる浄化フィルタ
ーは、高い光触媒機能を保持し、しかも設置個所が限定
されることもなく、また、定形性を有しているので各種
の浄化装置にも適用可能となる。さらに、吸水性、保水
性に優れているため、浄化能力の相乗化をも図ることが
できる。さらにまた、光触媒機能の一つである汚れを落
ちやすくする効果により、汚れが着いても何度でも水洗
いすることができるため、再利用が可能となる。According to the first aspect of the present invention, the granular glass having the surface coated with the titanium oxide liquid is housed in a mold having a predetermined shape and heated at a predetermined temperature to weld the granular glass to each other. By purifying the titanium oxide applied to the surface of the granular glass at the same time as integrating the titanium oxide into a predetermined shape, a purification filter of a predetermined shape is manufactured. Is obtained, and there is an excellent effect that the manufacturing process can be simplified. Further, the obtained purification filter has a high photocatalytic function, is not limited in its installation location, and has a fixed form, so that it can be applied to various purification devices. Furthermore, since it is excellent in water absorption and water retention, synergistic purifying ability can be achieved. Still further, the effect of easily removing dirt, which is one of the photocatalytic functions, can be washed as many times as possible even when dirt arrives, so that it can be reused.
【００３１】請求項３の発明によれば、表面に酸化チタ
ンのコーティング層を有する粒状ガラス同士が所定形状
に溶着一体化しているので、高い光触媒機能を保持し、
しかも設置個所が限定されることもなく、また、定形性
を有しているので各種の浄化装置にも適用可能となると
いう優れた効果がある。さらに、吸水性、保水性に優れ
ているため、浄化能力の相乗化をも図ることができる。
さらにまた、光触媒機能の一つである汚れを落ちやすく
する効果により、汚れが着いても何度でも水洗いするこ
とができるため、再利用が可能となる。According to the third aspect of the present invention, the granular glass having a coating layer of titanium oxide on the surface is welded and integrated in a predetermined shape, so that a high photocatalytic function is maintained,
In addition, the installation location is not limited, and since it has a fixed shape, there is an excellent effect that it can be applied to various purification devices. Furthermore, since it is excellent in water absorption and water retention, synergistic purifying ability can be achieved.
Still further, the effect of easily removing dirt, which is one of the photocatalytic functions, can be washed as many times as possible even when dirt arrives, so that it can be reused.
【００３２】請求項５の発明によれば、表面に酸化チタ
ンのコーティング層を有する粒状ガラス同士が所定形状
に溶着一体化されている浄化フィルターを用いて浄化装
置を構成したので、高性能の浄化装置が低コストで得ら
れるという優れた効果がある。According to the fifth aspect of the present invention, the purifying device is constituted by using the purifying filter in which the granular glasses having the coating layer of titanium oxide on the surface are welded and integrated in a predetermined shape, so that a high-performance purifying device is provided. There is an excellent effect that the device can be obtained at low cost.
【００３３】請求項２、４および６の発明におけるよう
に、前記粒状ガラスとして、ガラス瓶等のリサイクル時
に生成されるガラスカレットを用いた場合、廃品の有効
利用が可能となり、より一層のコストダウンを図ること
ができる。When glass cullet generated at the time of recycling glass bottles or the like is used as the granular glass as in the inventions of claims 2, 4 and 6, it is possible to effectively use waste products and further reduce costs. Can be planned.
【図１】（イ）〜（ハ）は本願発明の実施の形態にかか
る浄化フィルターの製造方法を示す工程図である。FIGS. 1A to 1C are process diagrams showing a method for manufacturing a purification filter according to an embodiment of the present invention.
【図２】本願発明の実施の形態にかかる浄化フィルター
の製造方法により製造された浄化フィルターの使用例で
ある水浄化装置を示す側面図である。FIG. 2 is a side view showing a water purification device which is an example of use of a purification filter manufactured by a method for manufacturing a purification filter according to an embodiment of the present invention.
【図３】本願発明の実施の形態にかかる浄化フィルター
の製造方法により製造された浄化フィルターの使用例で
ある水浄化装置を示す斜視図である。FIG. 3 is a perspective view showing a water purification device which is an example of use of a purification filter manufactured by a method for manufacturing a purification filter according to an embodiment of the present invention.
【図４】本願発明の実施の形態にかかる浄化フィルター
の製造方法により製造された浄化フィルターの使用例で
ある空気浄化装置を示す斜視図である。FIG. 4 is a perspective view showing an air purification device which is an example of use of a purification filter manufactured by a method for manufacturing a purification filter according to an embodiment of the present invention.
１は粒状ガラス（ガラスカレット）、２は酸化チタン
層、３は型、４は浄化フィルター、Ｉは光。1 is a granular glass (glass cullet), 2 is a titanium oxide layer, 3 is a mold, 4 is a purification filter, and I is light.
Claims (6)
スを、所定形状の型内に収納して所定温度で加熱処理す
ることにより、前記粒状ガラス同士を溶着させて所定形
状に一体化すると同時に粒状ガラスの表面に塗布された
酸化チタンを定着させることを特徴とする浄化フィルタ
ーの製造方法。1. A granular glass having a surface coated with a titanium oxide liquid is accommodated in a mold having a predetermined shape, and heated at a predetermined temperature to fuse the granular glasses and integrate them into a predetermined shape. A method for producing a purification filter, comprising fixing titanium oxide applied to the surface of granular glass.
クル時に生成されるガラスカレットとされていることを
特徴とする前記請求項１記載の浄化フィルターの製造方
法。2. The method according to claim 1, wherein the granular glass is a glass cullet generated when recycling a glass bottle or the like.
する粒状ガラス同士が所定形状に溶着一体化されている
ことを特徴とする浄化フィルター。3. A purifying filter characterized in that granular glass having a titanium oxide coating layer on the surface is welded and integrated in a predetermined shape.
クル時に生成されるガラスカレットとされていることを
特徴とする前記請求項３記載の浄化フィルター。4. The purification filter according to claim 3, wherein the granular glass is a glass cullet generated when recycling a glass bottle or the like.
する粒状ガラス同士が所定形状に溶着一体化されている
浄化フィルターを用いたことを特徴とする浄化装置。5. A purifying apparatus using a purifying filter in which granular glasses having a titanium oxide coating layer on their surfaces are welded and integrated in a predetermined shape.
クル時に生成されるガラスカレットとされていることを
特徴とする前記請求項５記載の浄化装置。6. The purification apparatus according to claim 5, wherein the granular glass is a glass cullet generated at the time of recycling a glass bottle or the like.