JPH11184137A - Light-transmitting recording material for electrophotography - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide an electrophotographic light-transmitting recording material for making an OHP manuscript or the like which does not entangle on a fixing roller and which shows excellent paper discharging property, toner transfer property and color reproducibility of a projected image. SOLUTION: This light-transmitting recording material consists of a light- transmitting base body 1 and a toner accepting layer 2 containing a thermoplastic resin on the base body 1. Further a surface treated layer 3 containing a modified silicone oil is formed on the toner accepting layer 2. The surface treated layer 3 preferably contains an antistatic agent, and the content of the modified silicone oil is controlled to 15 to 50 wt.% of the whole material which constitutes the surface treated layer. The obtd. light-transmitting recording material shows excellent paper discharging property and toner transfer property without entangling on a fluoroplastics fixing roller under high speed image output conditions such as for a color copy.

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【０００１】[0001]

【発明の属する技術分野】本発明は、トナー画像を形成
するための電子写真用光透過性被記録材に関し、特にフ
ルカラーコピーに適した電子写真用光透過性被記録材に
関する。The present invention relates to a light-transmitting recording material for electrophotography for forming a toner image, and more particularly to a light-transmitting recording material for electrophotography suitable for full-color copying.

【０００２】[0002]

【従来の技術】一般にＯＨＰ（オーバーヘッドプロジェ
クタ）等の原稿を作成するための電子写真用光透過性被
記録材として、透明な基材上にトナー受容層を設けたも
のが用いられている。このような被記録材にカラートナ
ー画像或いはフルカラートナー画像を形成し、ＯＨＰ装
置を用いてこれらの画像を投影した場合、被記録材上の
カラー画像は十分な発色性を示しているにもかかわら
ず、投影画像が全体的にグレーがかった色調を示し、色
再現性が非常に狭いものになる現象が生じている。この
現象は、被記録材上に形成されたトナー画像（トナー粒
子）により、被記録材上に凹凸が生じ、この凹凸部分に
おいてＯＨＰ投影光が散乱し、スクリーン上に陰影を形
成する結果生じる。特に、中間調部分において再現され
るべき色調が再現できず、グレー化する現象が生じる。
このような現象を低減するために、トナー受容層の樹脂
としてガラス転移温度の低い熱可塑性樹脂を用いること
が試みられている。2. Description of the Related Art In general, as a light-transmissive recording material for electrophotography for preparing an original such as an OHP (overhead projector), a material having a toner receiving layer provided on a transparent base material is used. When a color toner image or a full-color toner image is formed on such a recording material, and these images are projected using an OHP device, the color image on the recording material shows sufficient color development. Instead, the projected image has a grayish color tone as a whole, and the color reproducibility is extremely narrow. This phenomenon occurs as a result of the toner image (toner particles) formed on the recording material causing irregularities on the recording material, and the OHP projection light being scattered in the irregularities to form a shadow on the screen. In particular, a color tone to be reproduced in a halftone portion cannot be reproduced, and a phenomenon of graying occurs.
In order to reduce such a phenomenon, attempts have been made to use a thermoplastic resin having a low glass transition temperature as the resin of the toner receiving layer.

【０００３】トナー受容層の樹脂として、このような柔
らかい樹脂を用いた場合には、トナー粒子をトナー受容
層中に埋没させ平滑性を与えるため、色再現性は改善さ
れるが、電子写真によるトナー画像形成時にトナー受容
層が電子写真装置の定着ローラに巻き付くという問題を
生じた。特に定着ローラとしてフッ素樹脂系の材料を用
いて、被記録材との間にシリコーンオイル等を供給する
ことなく定着を行うプロセス（以下、オイルレスプロセ
スという）では、問題があった。When such a soft resin is used as the resin of the toner receiving layer, the toner particles are buried in the toner receiving layer to give smoothness, so that the color reproducibility is improved. There has been a problem that the toner receiving layer is wound around the fixing roller of the electrophotographic apparatus during toner image formation. In particular, there is a problem in a process of fixing using a fluororesin-based material as a fixing roller without supplying silicone oil or the like to a recording material (hereinafter referred to as an oilless process).

【０００４】この問題を解決するものとして、トナー受
容層にシリコーンオイルやフッ素系オイル等の離型剤を
含有せしめることが提案されている（特開平9-160278
号）。また滑り性向上のためにトナー受容層中にフィラ
ーを添加するとともにフィラーとしてトナー受容層の厚
みよりも平均粒子径の小さいものを使用することによ
り、フィラーが定着ローラによってこすりとられること
を防止することも提案されている（特開平8-305069
号）。In order to solve this problem, it has been proposed to incorporate a release agent such as silicone oil or fluorine-based oil in the toner receiving layer (Japanese Patent Laid-Open No. 9-160278).
issue). Also, by adding a filler to the toner receiving layer to improve the slipperiness and using a filler having an average particle diameter smaller than the thickness of the toner receiving layer, the filler is prevented from being scraped by the fixing roller. It has also been proposed (JP-A-8-305069)
issue).

【０００５】[0005]

【発明が解決しようとする課題】ところで、フルカラー
コピーの場合には、複数の色のトナーを用いて繰り返し
印字しなければならないため、高速化を図るために高い
定着ローラの温度で給紙速度を上げて印字する機種が開
発されている。このように定着ローラの温度が高い機種
の場合、トナー受容層として熱可塑性樹脂を用いた従来
の被記録材では、定着ローラへ巻き付きを確実に防止す
ることができない。また定着ローラへの巻き付きを確実
に防止するためにトナー受容層に多量の離型剤を含有せ
しめた場合には、離型剤により投影光が散乱し、カラー
トナー画像の中間色調において色再現性が低下するとい
う問題がある。In the case of full-color copying, printing must be repeated using toners of a plurality of colors. Therefore, in order to increase the speed, the paper feeding speed must be increased at a high fixing roller temperature. A model that raises and prints has been developed. As described above, in the case of a model in which the temperature of the fixing roller is high, the conventional recording material using a thermoplastic resin as the toner receiving layer cannot reliably prevent winding around the fixing roller. Also, if a large amount of release agent is included in the toner receiving layer to reliably prevent winding around the fixing roller, projection light is scattered by the release agent and color reproducibility in the intermediate color tone of the color toner image Is reduced.

【０００６】一方、電子写真によるトナー画像形成時に
おいては、被記録材の表面抵抗率が高いと静電パターン
と呼ばれる画像欠陥が生じることが知られており、この
ためにトナー受容層中に帯電防止剤を入れる等により被
記録材の表面抵抗率をトナーの転写に適した範囲（１０
⁷〜１０¹⁴Ω／□）に調整することが提案されている。On the other hand, when forming a toner image by electrophotography, it is known that an image defect called an electrostatic pattern occurs when the surface resistivity of a recording material is high, and therefore, the toner is charged in a toner receiving layer. The surface resistivity of the recording material is adjusted to a range suitable for toner transfer (10
Adjustment to ⁷ to 10 ¹⁴ Ω / □) has been proposed.

【０００７】しかしトナー受容層中に帯電防止剤を混入
した場合には、色再現性が低下する場合があった。However, when an antistatic agent is mixed in the toner receiving layer, the color reproducibility may decrease.

【０００８】そこで本発明は、定着ローラへの巻き付き
がなく、これにより円滑な給紙、排紙を行うことがで
き、しかもトナー画像がトナー受容層に埋没し、平滑性
もあり、色再現性に優れた被記録材を提供することを目
的とする。また本発明は静電パターンを生じず高品質の
トナー画像を得ることができる被記録材を提供すること
を目的とする。Accordingly, the present invention does not wrap around the fixing roller, thereby enabling smooth paper feeding and discharging, and furthermore, the toner image is buried in the toner receiving layer, has smoothness, and has color reproducibility. It is an object of the present invention to provide a recording material excellent in quality. Another object of the present invention is to provide a recording material capable of obtaining a high quality toner image without generating an electrostatic pattern.

【０００９】[0009]

【課題を解決するための手段】上記目的を達成する本発
明の電子写真用光透過性被記録材は、光透過性の基材
と、該基材上に形成され、熱可塑性樹脂を含むトナー受
容層と、該トナー受容層上に形成され、変性シリコーン
オイルを含む表面処理層とを備えたものである。According to the present invention, there is provided a light-transmitting recording material for electrophotography according to the present invention, which comprises a light-transmitting base material and a toner formed on the base material and containing a thermoplastic resin. And a surface treatment layer formed on the toner receiving layer and containing a modified silicone oil.

【００１０】この電子写真用光透過性被記録材は、トナ
ー受容層上に変性シリコーンオイルを含む表面処理層を
設けたことにより、電子写真のオイルレスプロセスにお
いてトナー受容層が定着ローラに巻き付くことを防止す
るとともに、出図時のトナー受容層の傷や白化の生成を
防止し、高品質の光透過性画像を得ることができる。In this electrophotographic light-transmissive recording material, a surface treatment layer containing a modified silicone oil is provided on the toner receiving layer, so that the toner receiving layer wraps around the fixing roller in an oilless process of electrophotography. This prevents the toner receiving layer from being scratched or whitened at the time of drawing, so that a high quality light transmissive image can be obtained.

【００１１】また表面処理層は、帯電防止剤を含むこと
が好ましい。帯電防止剤を含有せしめることにより、被
記録材の表面抵抗率をトナーの転写に適した範囲（１０
⁷〜１０¹⁴Ω／□）に調整することができる。定着ロー
ラへの巻き付きを防止する効果（離型性）を得る離型剤
として変性シリコーンオイルを用いることにより、かか
る帯電防止剤との併用を可能にし、これにより１層で帯
電防止層と離型層とを兼ねた表面処理層を得ることがで
きる。The surface treatment layer preferably contains an antistatic agent. By incorporating an antistatic agent, the surface resistivity of the recording material is adjusted to a range suitable for toner transfer (10
⁷ to 10 ¹⁴ Ω / □). By using a modified silicone oil as a release agent having an effect of preventing wrapping around the fixing roller (release property), it can be used in combination with such an antistatic agent, whereby a single layer can release the antistatic layer from the antistatic layer. A surface treatment layer also serving as a layer can be obtained.

【００１２】また表面処理層中の変性シリコーンオイル
の量を適量とすることにより、上述した効果を維持した
まま、透過像の色再現性を向上することができる。具体
的には変性シリコーンオイルの含有量は、表面処理層を
形成する全材料中７５重量％以下、好適には１５〜５０
重量％とする。By adjusting the amount of the modified silicone oil in the surface treatment layer to an appropriate amount, the color reproducibility of a transmitted image can be improved while maintaining the above-mentioned effects. Specifically, the content of the modified silicone oil is 75% by weight or less, preferably 15 to 50% of the total material forming the surface treatment layer.
% By weight.

【００１３】以下、図面を参照して本発明の電子写真用
光透過性被記録材を更に詳述する。Hereinafter, the light transmitting recording material for electrophotography of the present invention will be described in more detail with reference to the drawings.

【００１４】図１は、本発明の電子写真用光透過性被記
録材の一実施例を示す図で、この被記録材は光透過性の
基材１、トナー受容層２及び表面処理層３からなり、全
体として光透過性を有する。光透過性は、全光線透過率
で80％以上あることが好ましい。FIG. 1 is a view showing an embodiment of a light-transmitting recording material for electrophotography according to the present invention. The recording material comprises a light-transmitting substrate 1, a toner receiving layer 2, and a surface treatment layer 3. And has optical transparency as a whole. The light transmittance is preferably 80% or more in total light transmittance.

【００１５】基材１としては、電子写真による熱定着時
の加熱により熱変形を起こさない耐熱性を有する光透過
性材料を用いる。このような材料として、例えば、ポリ
エチレンテレフタレート(PET)、ポリアミドまたはポリ
イミド等のプラスチックフィルムが挙げられる。これら
の中でも、ポリエチレンテレフタレートが耐熱性及び透
明性の点で特に好ましい。As the substrate 1, a light-transmitting material having heat resistance which does not undergo thermal deformation due to heating during heat fixing by electrophotography is used. Examples of such a material include a plastic film such as polyethylene terephthalate (PET), polyamide, or polyimide. Among them, polyethylene terephthalate is particularly preferred in terms of heat resistance and transparency.

【００１６】基材の厚さは特に限定されないが、電子写
真装置での通紙性を考慮し、50〜300μmの範囲が好適で
ある。例えばポリエチレンテレフタレートの場合には、
厚さは、好ましくは50〜300μm、より好ましくは70〜20
0μm、更に好ましくは100〜150μm程度とする。The thickness of the substrate is not particularly limited, but is preferably in the range of 50 to 300 μm in consideration of the paper passing property in an electrophotographic apparatus. For example, in the case of polyethylene terephthalate,
The thickness is preferably 50-300 μm, more preferably 70-20
0 μm, more preferably about 100 to 150 μm.

【００１７】基材は、その上に形成されるトナー受容層
との密着性を改良する目的で、プラズマ処理、コロナ放
電処理等の表面処理を行ってもよく、またトナー受容層
との間に易接着層を形成してもよい。易接着層として
は、例えば、ポリエステル樹脂、アクリル酸エステル樹
脂、メタアクリル酸エステル樹脂、スチレン−アクリル
酸エステル共重合体、スチレン−メタアクリル酸エステ
ル共重合体等の樹脂が挙げられる。The substrate may be subjected to a surface treatment such as a plasma treatment or a corona discharge treatment for the purpose of improving the adhesion to the toner receiving layer formed thereon. An easy adhesion layer may be formed. Examples of the easy-adhesion layer include resins such as polyester resins, acrylate resins, methacrylate resins, styrene-acrylate copolymers, and styrene-methacrylate copolymers.

【００１８】トナー受容層は、主として光透過性の熱可
塑性樹脂からなる。このような熱可塑性樹脂として、例
えば、ポリエステル系、アクリル系、スチレン系、ゴム
系、塩化ビニル系、酢酸ビニル系樹脂等の種々の熱可塑
性樹脂が挙げられる。これら熱可塑性樹脂を用いること
により、上層に表面処理層がありながらトナー粒子をト
ナー受容層中に埋没させ平滑性を与えることができる。
この平滑性の観点から特にポリエステル系樹脂が好まし
い。The toner receiving layer mainly comprises a light-transmitting thermoplastic resin. Examples of such a thermoplastic resin include various thermoplastic resins such as polyester-based, acrylic-based, styrene-based, rubber-based, vinyl chloride-based, and vinyl acetate-based resins. By using these thermoplastic resins, the toner particles can be buried in the toner receiving layer to provide smoothness even though the surface treatment layer is provided as an upper layer.
From the viewpoint of smoothness, a polyester resin is particularly preferable.

【００１９】トナー受容層は、ブロッキング防止のため
に顔料を含むことが好ましい。顔料としては、結晶性シ
リカ、非晶質シリカ、酸化チタン、炭酸カルシウム、Ｐ
ＭＭＡ等の樹脂粒子が挙げられ、特に透明性の点からＰ
ＭＭＡ等の透明樹脂粒子が好ましい。顔料の粒径は2〜1
5μmの範囲が好ましい。2μmより小さいと十分なブロッ
キング効果を得ることができない。また15μmより大き
いと投影したときに異物のように見え、投影画像の画質
が低下する。顔料の含有量は、トナー受容層を構成する
樹脂固形分に対し0.1〜2重量％とする。The toner receiving layer preferably contains a pigment for preventing blocking. Pigments include crystalline silica, amorphous silica, titanium oxide, calcium carbonate, P
Resin particles such as MMA.
Transparent resin particles such as MMA are preferred. Pigment particle size is 2 ~ 1
A range of 5 μm is preferred. If it is smaller than 2 μm, a sufficient blocking effect cannot be obtained. On the other hand, if it is larger than 15 μm, it looks like a foreign substance when projected, and the image quality of the projected image deteriorates. The content of the pigment is 0.1 to 2% by weight based on the solid content of the resin constituting the toner receiving layer.

【００２０】更にトナー受容層は、上述した成分の他、
レベリング剤、高級アルコール等の造膜助剤、ワックス
等を含有してもよい。Further, in addition to the components described above, the toner receiving layer
It may contain a leveling agent, a film-forming auxiliary such as a higher alcohol, a wax and the like.

【００２１】このようなトナー受容層は、層を構成する
材料を適当な溶剤に溶解或いは分散させた塗工液を、バ
ーコート法、ディップ法、スプレー法、及びスピンコー
ト法等の塗工方法で基材１の表面に塗布し、常温或いは
加熱して乾燥することにより形成する。溶剤としては、
通常酢酸エチル、酢酸ブチル、キシレン、ブチルセロソ
ルブ、メチルエチルケトン、トルオール、シクロヘキサ
ノン等の有機溶媒やこれらの混合溶媒が用いられる。ト
ナー受容層の厚さは特に限定されないが、通常2〜30μm
程度、好ましくは3〜15μmとする。Such a toner receiving layer is formed by applying a coating solution obtained by dissolving or dispersing the material constituting the layer in an appropriate solvent, such as a bar coating method, a dipping method, a spraying method, or a spin coating method. Is applied to the surface of the base material 1 and dried at normal temperature or by heating. As the solvent,
Usually, organic solvents such as ethyl acetate, butyl acetate, xylene, butyl cellosolve, methyl ethyl ketone, toluene, cyclohexanone and the like, and a mixed solvent thereof are used. The thickness of the toner receiving layer is not particularly limited, but usually 2 to 30 μm
Degree, preferably 3 to 15 μm.

【００２２】表面処理層３は、主として帯電防止剤と変
性シリコーンオイルからなる。変性シリコーンオイル
は、下記式で表される直鎖状オルガノポリシロキサンの
両末端或いは側鎖が変性されたもので、分子量数十〜数
千のもの（それらの混合物を含む）が用いられる。この
ような離型剤としては市販のものを使用することがで
き、例えばダウ・コーニング社のペインタッド29やペイ
ンタッドDKQ8-8598などが挙げられる。離型剤としては
シリコーンオイルの他、シリコーン系樹脂やシリコーン
系樹脂とアクリル系樹脂とのグラフト或いはブロック共
重合体が知られているが、アクリル系樹脂との共重合体
は帯電防止剤と併用した場合、白濁する場合がある。ま
たシリコーン系樹脂は、高温（例えば200〜250℃）で長
時間（１〜２時間）焼き付け乾燥を行わないと最良の塗
膜が得られないという製法上の問題がある。従って本発
明では変性シリコーンオイルを用いる。これにより、光
透過性、出図時の排紙性及び色再現性を全て満たすこと
ができる。The surface treatment layer 3 mainly comprises an antistatic agent and a modified silicone oil. The modified silicone oil is obtained by modifying both ends or side chains of a linear organopolysiloxane represented by the following formula, and has a molecular weight of several tens to several thousands (including a mixture thereof). Commercially available products can be used as such a release agent, and examples thereof include Paintad 29 and Dow Corning DKQ8-8598. As a release agent, in addition to silicone oil, a silicone resin or a graft or block copolymer of a silicone resin and an acrylic resin is known, but a copolymer with an acrylic resin is used in combination with an antistatic agent. Otherwise, it may become cloudy. Further, the silicone resin has a problem in the production method that the best coating film cannot be obtained unless baking and drying is performed at a high temperature (for example, 200 to 250 ° C.) for a long time (1 to 2 hours). Therefore, the modified silicone oil is used in the present invention. Thereby, it is possible to satisfy all of the light transmittance, the paper discharge property at the time of drawing, and the color reproducibility.

【００２３】[0023]

【化１】 このような変性シリコーンオイルをトナー受容層の表面
に表面処理層３として設けることにより、被記録材の定
着ローラへの巻き付きを防止し、トナー受容層が耐熱性
の低い材料であっても熱定着時に白化したり傷がつくこ
とを低減できる。但し、変性シリコーンオイルの量が多
すぎると投影画像、特に中間調部分の色再現性が悪くな
る。Embedded image By providing such a modified silicone oil as a surface treatment layer 3 on the surface of the toner receiving layer, the recording material is prevented from winding around the fixing roller, and even if the toner receiving layer is made of a material having low heat resistance, heat fixing is performed. Sometimes whitening and scratching can be reduced. However, if the amount of the modified silicone oil is too large, the color reproducibility of a projected image, particularly, a halftone portion is deteriorated.

【００２４】具体的には変性シリコーンオイルの含有量
は、表面処理層を構成する材料全体の７５重量％以下、
好適には１５〜５０重量％とする。表面処理層が帯電防
止剤を含有する場合、帯電防止剤の固形分に対し300重
量％以下、好適には20〜100重量％とする。変性シリコ
ーンオイルの量をこのような範囲とすることにより、離
型性、白化等の防止効果、色再現性の全てを満たすこと
ができる。Specifically, the content of the modified silicone oil is 75% by weight or less based on the whole material constituting the surface treatment layer.
It is preferably 15 to 50% by weight. When the surface treatment layer contains an antistatic agent, the content is 300% by weight or less, preferably 20 to 100% by weight, based on the solid content of the antistatic agent. By setting the amount of the modified silicone oil in such a range, all of the releasability, the effect of preventing whitening and the like, and the color reproducibility can be satisfied.

【００２５】帯電防止剤は、被記録材の表面抵抗率をト
ナーの転写に適した範囲（１０⁷〜１０¹³Ω／□）に調
整するために用いられる。本発明において帯電防止剤
は、トナー受容層に添加することも可能であるが、この
場合、添加量が多すぎると投影画像の色再現性を損う場
合がある。従ってトナー受容層とは別の層として設ける
ことが好ましい。帯電防止層をトナー受容層とは別の層
として設ける場合、表面処理層とも別の層とすることも
可能であるが、本発明の表面処理層に用いる変性シリコ
ーンオイルは、帯電防止剤と併用しても層の透明性及び
色再現性を損うことがないので、製造上の観点からも同
一の層として設けることが最も好適である。The antistatic agent is used to adjust the surface resistivity of the recording material to a range (10 ⁷ to 10 ¹³ Ω / □) suitable for transferring the toner. In the present invention, the antistatic agent can be added to the toner receiving layer, but in this case, if the amount is too large, the color reproducibility of the projected image may be impaired. Therefore, it is preferable to provide it as a layer different from the toner receiving layer. When the antistatic layer is provided as a layer different from the toner receiving layer, the surface treatment layer may be formed as a separate layer.However, the modified silicone oil used in the surface treatment layer of the present invention is used in combination with an antistatic agent. However, since the transparency and color reproducibility of the layers are not impaired, it is most preferable to provide the same layer from the viewpoint of manufacturing.

【００２６】帯電防止剤としては、公知のものを使用す
ることができ、例えば、四級アンモニウム塩系化合物、
ピリジニウム塩系化合物、ホスホニウム塩系化合物、ア
ルキルベタイン系化合物、アルキルイミダゾリン系化合
物、アルキルアラニン系化合物、ポリオキシエチレン型
非イオン系化合物、多価アルコール型非イオン系化合
物、ポリビニルベンジル型カチオンやポリアクリル酸型
カチオン等の導電性樹脂、Sn0₂やSn0₂-Sb等の金属酸化
物超微粒子をバインダー樹脂中に分散したもの等が挙げ
られる。特に四級アンモニウム塩系化合物、ポリアクリ
ル酸型カチオンが好適である。このような導電性樹脂
は、トナー受容層との密着性が良好で、且つ変性シリコ
ーンオイルと共存した場合に層の透明性を損わないとい
う利点がある。As the antistatic agent, known ones can be used. For example, quaternary ammonium salt compounds,
Pyridinium salt compounds, phosphonium salt compounds, alkyl betaine compounds, alkyl imidazoline compounds, alkyl alanine compounds, polyoxyethylene type nonionic compounds, polyhydric alcohol type nonionic compounds, polyvinylbenzyl type cations and polyacryls acid type conductive resin cation such, and the like that the metal oxide ultrafine particles such as Sn0 ₂ or Sn0 ₂ -Sb dispersed in a binder resin. Particularly, quaternary ammonium salt compounds and polyacrylic acid type cations are preferred. Such a conductive resin has an advantage that it has good adhesion to the toner receiving layer and does not impair the transparency of the layer when coexisting with a modified silicone oil.

【００２７】表面処理層には、上述した成分の他、界面
活性剤、ワックス等の添加剤を添加することができる。Additives such as surfactants and waxes can be added to the surface treatment layer in addition to the above-mentioned components.

【００２８】表面処理層は、上述した材料を適当な溶剤
に溶解或いは分散した塗工液を、バーコート法、ディッ
プ法、スプレー法、及びスピンコート法等の塗工方法で
トナー受容層上に積層し、常温或いは加熱して乾燥する
ことにより形成する。溶剤としては、通常イソプロパノ
ール、メタノール、ブチルセロソルブ、水、メタ変性ア
ルコール等の溶媒が用いられる。The surface treatment layer is formed by dissolving or dispersing the above-mentioned materials in an appropriate solvent, and applying a coating solution such as a bar coating method, a dipping method, a spraying method and a spin coating method on the toner receiving layer. It is formed by stacking and drying at room temperature or by heating. As the solvent, a solvent such as isopropanol, methanol, butyl cellosolve, water, or a meta-modified alcohol is usually used.

【００２９】表面処理層の厚さは、厚すぎると結果的に
被記録材におけるシリコーンオイルの添加量が多くなり
投影画像の色再現性が低下するので、シリコーンオイル
の塗布量を塗布・乾燥後10〜200mg/m²程度とすることが
好ましい。If the thickness of the surface treatment layer is too large, the amount of silicone oil added to the recording material will eventually increase, and the color reproducibility of the projected image will decrease. It is preferable to be about 10 to ²⁰⁰ mg / m ² .

【００３０】上述した本発明の電子写真用光透過性被記
録材は、OHPシートとして用いる場合、光透過性が全光
線透過率（JIS K-7105）で少なくとも80％以上、好ま
しくは95％以上とする。またヘイズ（JIS K-7105）が
少なくとも10％以下、好ましくは7％以下であることが
好ましい。When the above-mentioned light-transmitting recording material for electrophotography of the present invention is used as an OHP sheet, its light transmittance is at least 80% or more, preferably 95% or more in total light transmittance (JIS K-7105). And Further, the haze (JIS K-7105) is at least 10% or less, preferably 7% or less.

【００３１】本発明の光透過性被記録材は、特にオイル
レスの高速出図プロセス好適に適用されるが、この様な
電子写真方式のみに限られるものではなく、従来のすべ
ての電子写真方式にも適用することが可能である。The light-transmissive recording material of the present invention is suitably applied particularly to an oil-less high-speed drawing process. However, the present invention is not limited to such an electrophotographic system, and all conventional electrophotographic systems can be used. It is also possible to apply to.

【００３２】[0032]

【実施例】以下、本発明の実施例を説明する。尚、実施
例において特に断らない限り「部」は重量部を表す。 実施例１ 厚さ100μmのポリエチレンテレフタレートフィルムの上
に下記処方のトナー受容層用塗工液を塗布後、乾燥し厚
さ８μmのトナー受容層を形成した。Embodiments of the present invention will be described below. In the examples, “parts” means “parts by weight” unless otherwise specified. Example 1 A coating liquid for a toner receiving layer having the following formulation was applied onto a 100 μm thick polyethylene terephthalate film, and then dried to form a 8 μm thick toner receiving layer.

【００３３】 ポリエステル樹脂（ハ゛イロン＃200） ４６．４９部 PMMA顔料（粒径10μｍ） ０．０９部 レベリング剤 ０．３０部 メチルエチルケトン １８．５８部 トルオール １８．５４部 シクロヘキサノン １６．００部Polyester resin (Pylon # 200) 46.49 parts PMMA pigment (particle size 10 μm) 0.09 parts Leveling agent 0.30 parts Methyl ethyl ketone 18.58 parts Toluol 18.54 parts Cyclohexanone 16.00 parts

【００３４】次いでトナー受容層上に、下記処方の表面
処理層用塗工液を塗布量8.75g/m²となるように塗布し
た。その後乾燥して表面処理層を形成した。Next, a coating liquid for a surface treatment layer having the following formulation was applied on the toner receiving layer so as to have a coating amount of 8.75 g / m ² . Thereafter, drying was performed to form a surface treatment layer.

【００３５】 帯電防止性樹脂 １．００部 （エレコント゛PQ-50B：綜研化学社製 固形分50%） メタ変性アルコール ９８．６８部 変性シリコーンオイル ０．３２部 （ヘ゜インタット゛29：タ゛ウ・コーニンク゛社製 固形分100%）1.00 part of antistatic resin (Elecont PQ-50B: solid content 50%, manufactured by Soken Chemical Co.) 98.68 parts of meta-modified alcohol 0.32 parts of modified silicone oil (Paint 29: solid manufactured by Tow Koningk Co., Ltd.) Min 100%)

【００３６】このように製造した被記録材に、市販のフ
ルカラーコピー機（CLC-500：キャノン製）を使用して
転写スピード100mm/secでイエロー画像を転写させ、外
部定着機で定着させた。定着手段としては表面がフッ素
樹脂の外部定着機を用い、定着温度170℃、定着スピー
ド30mm/secでイエロー画像を定着させた。この際、原稿
として「PS PLAT DOT TABLET DT-1」（三菱化学社製）
を用い、倍率を400％として定着させた。A yellow image was transferred onto the recording material thus produced at a transfer speed of 100 mm / sec using a commercially available full-color copying machine (CLC-500: manufactured by Canon) and fixed by an external fixing machine. A yellow image was fixed at a fixing temperature of 170 ° C. and a fixing speed of 30 mm / sec using an external fixing machine having a fluororesin surface as a fixing means. At this time, "PS PLAT DOT TABLET DT-1" (manufactured by Mitsubishi Chemical Corporation)
And fixed at a magnification of 400%.

【００３７】この場合の排紙の状態、トナー転写の状態
及び出図後の表面の状態（傷及び表層剥がれ）を観察
し、それぞれ良い（○）、悪い（△）、非常に悪い
（×）の三段階で評価した。尚、表層剥がれとはトナー
受容層が侵されている程度を表したものである。また
「PS PLAT DOT TABLET DT-1」の150Lの６階調目の位置
を中間調とし、この中間調部分の光学特性を評価するた
めにJIS K-7105による全光線透過率（％）及びヘイズ
値を測定した。ヘイズ値は、［ヘイズ］＝｛［拡散透過
率(%)］／［全光線透過率(%)］｝×100で求められ、そ
の値が大きいほど投影画像の中間調部分が黒くなる程度
が大きい。更に出図する前の表面抵抗率を測定した。In this case, the state of paper discharge, the state of toner transfer, and the state of the surface after drawing (scratch and peeling of the surface layer) were observed, and they were good (、), bad (△), and very bad (×), respectively. Was evaluated in three stages. The surface layer peeling indicates the degree to which the toner receiving layer is damaged. In addition, the position of the 6th gradation of 150L of "PS PLAT DOT TABLET DT-1" is set as the halftone, and the total light transmittance (%) and haze according to JIS K-7105 are used to evaluate the optical characteristics of this halftone part. The value was measured. The haze value is calculated by [haze] = {[diffuse transmittance (%)] / [total light transmittance (%)]} × 100, and the larger the value, the more the halftone portion of the projected image becomes black. large. Further, the surface resistivity before drawing was measured.

【００３８】結果は表２に示すように、排紙性、転写
性、表面状態はいずれも良好な結果を示し、中間調部分
についても実用上十分な透過性を示した。As shown in Table 2, the paper discharge property, the transfer property and the surface condition were all good, and the halftone part showed practically sufficient transparency.

【００３９】[0039]

【表１】 [Table 1]

【００４０】[0040]

【表２】 実施例２〜５ 表面処理層の変性シリコーンオイルの含有量を、表１に
示すように変化させて、それ以外は実施例１と同様にし
て電子写真用光透過性被記録材を製造した。これら被記
録材についても実施例１と同様に光透過性、ヘイズ値、
排紙性、転写性、表面の傷、表層剥がれ及び表面抵抗率
を評価した。結果を表２に示す。[Table 2] Examples 2 to 5 Light-transmissive recording materials for electrophotography were produced in the same manner as in Example 1 except that the content of the modified silicone oil in the surface treatment layer was changed as shown in Table 1. For these recording materials, the light transmittance, haze value,
The paper discharge property, transfer property, surface damage, surface layer peeling and surface resistivity were evaluated. Table 2 shows the results.

【００４１】実施例６、７ 表面処理層の膜厚をそれぞれ６μｍ（実施例５）、７μ
ｍ（実施例６）と変え、それ以外は実施例１と同様にし
て電子写真用光透過性被記録材を製造した。これら被記
録材についても実施例１と同様に光透過性、ヘイズ値、
排紙性、転写性、表面の傷、表層剥がれ及び表面抵抗率
を評価した。結果を表２に示す。Examples 6 and 7 The thicknesses of the surface treatment layers were 6 μm (Example 5) and 7 μm, respectively.
m (Example 6), and the other conditions were the same as in Example 1 to produce a light-transmissive recording material for electrophotography. For these recording materials, the light transmittance, haze value,
The paper discharge property, transfer property, surface damage, surface layer peeling and surface resistivity were evaluated. Table 2 shows the results.

【００４２】実施例８ 表面処理層に含有される変性シリコーンオイルとして、
異なる変性シリコーンオイル（DKQ8-8598：ダウコーニ
ング社製）を０．６４部用い、表面処理層の膜厚を８μ
ｍとした以外は実施例１と同様にして電子写真用光透過
性被記録材を製造した。この被記録材についても実施例
１と同様に光透過性、ヘイズ値、排紙性、転写性、表面
の傷、表層剥がれ及び表面抵抗率を評価した。結果を表
２に示す。Example 8 As the modified silicone oil contained in the surface treatment layer,
Using 0.64 parts of a different modified silicone oil (DKQ8-8598: manufactured by Dow Corning), the thickness of the surface treatment layer was 8 μm.
A light-transmissive recording material for electrophotography was produced in the same manner as in Example 1 except that m was used. This recording material was evaluated for light transmittance, haze value, paper dischargeability, transferability, surface damage, surface layer peeling and surface resistivity in the same manner as in Example 1. Table 2 shows the results.

【００４３】表２に示す結果からも明らかなように、実
施例の被記録材はすべて、外部定着機出図条件において
も良好な排紙性、転写性、表面状態を示し、また中間調
部分の光透過性も優れていた。特にシリコーンオイルの
含有量が比較的少量の場合（実施例２、３、６、７）に
はヘイズ値も低く投影画像の色再現性に優れていた。As is evident from the results shown in Table 2, all the recording materials of the examples exhibited good paper dischargeability, transferability and surface condition even under the conditions of the external fixing machine, and the halftone portion. Was also excellent in light transmittance. In particular, when the silicone oil content was relatively small (Examples 2, 3, 6, and 7), the haze value was low and the color reproducibility of the projected image was excellent.

【００４４】比較例１ 表面処理層に含有される離型剤として、シリコーン・ア
クリル樹脂ブロック共重合体（モテ゛ィハ゜ーFT1718：日本油
脂社製）を用い、それ以外は実施例１と同様にして電子
写真用光透過性被記録材を製造した。この被記録材につ
いて実施例１と同様に光透過性、ヘイズ値、排紙性、転
写性、表面の傷、表層剥がれ及び表面抵抗率を評価し
た。結果を表２に示す。COMPARATIVE EXAMPLE 1 A silicone / acrylic resin block copolymer (Motivation FT1718: manufactured by NOF CORPORATION) was used as a release agent contained in the surface treatment layer. An optically transparent recording material for use was manufactured. In the same manner as in Example 1, the recording material was evaluated for light transmittance, haze value, paper dischargeability, transferability, surface damage, surface layer peeling, and surface resistivity. Table 2 shows the results.

【００４５】比較例２ 表面処理層に含有される離型剤として、シリコーン・ア
クリル樹脂グラフト共重合体（サイマックUE-450：東亜合成
化学社製）を用い、それ以外は実施例１と同様にして電
子写真用光透過性被記録材を製造した。この被記録材に
ついて実施例１と同様に光透過性、ヘイズ値、排紙性、
転写性、表面の傷、表層剥がれ及び表面抵抗率を評価し
た。結果を表２に示す。Comparative Example 2 A silicone-acrylic resin graft copolymer (CYMAC UE-450: manufactured by Toa Gosei Chemical Co., Ltd.) was used as a release agent contained in the surface treatment layer. Thus, a light-transmissive recording material for electrophotography was manufactured. The light transmittance, haze value, paper discharge property,
The transferability, surface scratches, surface layer peeling and surface resistivity were evaluated. Table 2 shows the results.

【００４６】表２の結果からもわかるように、離型剤と
してシリコーンオイルではなくシリコーン／アクリル樹
脂共重合体を用いた場合には、円滑な排紙ができず、ま
たトナーの転写も不完全であった。尚、これら比較例
１，２はトナー転写が不完全であるので光学特性（光透
過性、ヘイズ値）は参考にならない。As can be seen from the results in Table 2, when the silicone / acrylic resin copolymer was used as the release agent instead of silicone oil, smooth paper discharge was not possible, and the transfer of toner was incomplete. Met. Incidentally, in Comparative Examples 1 and 2, since the toner transfer is incomplete, the optical characteristics (light transmittance, haze value) cannot be referred to.

【００４７】比較例３、４ 厚さ100μmのポリエチレンテレフタレートフィルムの上
に下記処方のトナー受容層用塗工液を塗布後、乾燥し厚
さ８μmのトナー受容層を形成した。Comparative Examples 3 and 4 A coating liquid for a toner receiving layer having the following formulation was applied on a 100 μm thick polyethylene terephthalate film, and then dried to form a 8 μm thick toner receiving layer.

【００４８】 ポリエステル樹脂（ハ゛イロン#200） １００部 トルエン ２００部 メチルエチルケトン ２００部 変性シリコーンオイル（ヘ゜インタット゛29） １部Polyester resin (Vylon # 200) 100 parts Toluene 200 parts Methyl ethyl ketone 200 parts Modified silicone oil (Paintat 29) 1 part

【００４９】このトナー受容層表面に帯電防止剤を含む
表面処理液を塗工し、表面抵抗値を10⁸〜10⁹（Ω／□）
に調整し、電子写真用光透過性被記録材を製造した。A surface treatment liquid containing an antistatic agent is applied to the surface of the toner receiving layer, and the surface resistance is adjusted to 10 ⁸ to 10 ⁹ (Ω / □).
To produce a light transmissive recording material for electrophotography.

【００５０】帯電防止処理を施さない被記録材（比較例
３）と施した被記録材（比較例４）についても実施例１
と同様に光透過性、ヘイズ値、排紙性、転写性、表面の
傷、表層剥がれ及び表面抵抗率を評価した。結果を表２
に示す。The recording material without the antistatic treatment (Comparative Example 3) and the recording material with the antistatic treatment (Comparative Example 4) were used in Example 1.
In the same manner as in the above, light transmittance, haze value, paper discharge property, transfer property, surface flaw, surface layer peeling and surface resistivity were evaluated. Table 2 shows the results
Shown in

【００５１】比較例５、６ 変性シリコーンオイルの含有量を０．４部とした以外
は、比較例３、４と同様にして電子写真用光透過性被記
録材を製造した。Comparative Examples 5 and 6 Light-transmissive recording materials for electrophotography were produced in the same manner as in Comparative Examples 3 and 4, except that the content of the modified silicone oil was changed to 0.4 part.

【００５２】帯電防止処理を施さない被記録材（比較例
５）と施した被記録材（比較例６）についても実施例１
と同様に光透過性、ヘイズ値、排紙性、転写性、表面の
傷、表層剥がれ及び表面抵抗率を評価した。結果を表２
に示す。The recording material without the antistatic treatment (Comparative Example 5) and the recording material with the antistatic treatment (Comparative Example 6) were also used in Example 1.
In the same manner as in the above, light transmittance, haze value, paper discharge property, transfer property, surface flaw, surface layer peeling and surface resistivity were evaluated. Table 2 shows the results
Shown in

【００５３】表２の結果からもわかるように、表面処理
層を設けずにトナー受容層にシリコーンオイルを含有せ
しめた場合には、少量では（比較例５、６）外部定着機
出図条件における定着ローラへの巻き付き（排紙性）が
改善されなかった。多量に含有せしめた場合で、帯電防
止剤を含まない場合には（比較例３）、排紙性は改善し
たが、帯電防止剤を含まないため、トナーの飛散りや静
電パターンの出現などトナーの定着性、転写性に問題が
あった。また多量に含有せしめた場合でも、帯電防止剤
を含む場合には（比較例４）、高速出図条件における定
着ローラへの巻き付きが改善されなかった。As can be seen from the results in Table 2, when the silicone oil was contained in the toner receiving layer without providing the surface treatment layer, a small amount (Comparative Examples 5 and 6) was obtained under the external fixing machine drawing conditions. The winding around the fixing roller (paper discharging property) was not improved. When a large amount was contained and no antistatic agent was contained (Comparative Example 3), the paper discharging property was improved, but since the antistatic agent was not contained, toner scattering such as toner scattering or appearance of an electrostatic pattern was observed. There was a problem in the fixing property and the transfer property. In addition, even when the antistatic agent was contained in a large amount, when the antistatic agent was included (Comparative Example 4), the wrapping around the fixing roller under high-speed drawing conditions was not improved.

【００５４】[0054]

【発明の効果】以上の実施例からも明らかなように、本
発明の電子写真用光透過性被記録材はトナー受容層の上
にシリコーンオイルを含む表面処理層を設けたことによ
り、トナー受容層のトナー定着性を阻害することなく被
記録材の定着ローラへの巻き付きを効果的に防止するこ
とができ、更に出図後の傷や白化を防止することができ
る。また本発明の光透過性被記録材は、シリコーンオイ
ルの含有量を適量とすることにより投影画像の色再現性
を向上させ、特にカラーコピーで問題となる中間調での
投影画像のグレー化を防止することができる。さらに本
発明の光透過性被記録材はシリコーンオイルと帯電防止
剤を同一層に共存させることにより、上述した効果に加
え、トナー受容層の機能を損うことなく帯電防止効果を
得ることができる。As is clear from the above examples, the light-transmitting recording material for electrophotography of the present invention has a toner receiving layer provided with a surface treatment layer containing silicone oil on the toner receiving layer. It is possible to effectively prevent the recording material from being wound around the fixing roller without impairing the toner fixing property of the layer, and it is possible to prevent scratches and whitening after drawing. Further, the light-transmissive recording material of the present invention improves the color reproducibility of the projected image by adjusting the content of the silicone oil to an appropriate amount, and particularly reduces the gray level of the projected image in a half tone which is a problem in color copying. Can be prevented. Furthermore, in the light-transmissive recording material of the present invention, in addition to the above-described effects, the antistatic effect can be obtained without impairing the function of the toner receiving layer by coexisting the silicone oil and the antistatic agent in the same layer. .

【図面の簡単な説明】[Brief description of the drawings]

【図１】本発明の電子写真用光透過性被記録材の一実施
例を示す断面図FIG. 1 is a cross-sectional view showing one embodiment of a light-transmitting recording material for electrophotography according to the present invention.

【符号の説明】[Explanation of symbols]

１・・・・・・基材 ２・・・・・・トナー受容層 ３・・・・・・表面処理層 DESCRIPTION OF SYMBOLS 1 ... Base material 2 ... Toner receiving layer 3 ... Surface treatment layer

Claims (3)

【特許請求の範囲】[Claims] 【請求項１】光透過性の基材と、該基材上に形成され、
熱可塑性樹脂を含むトナー受容層と、該トナー受容層上
に形成され、変性シリコーンオイルを含む表面処理層と
を備えた電子写真用光透過性被記録材。1. A light-transmitting substrate, and formed on the substrate,
A light-transmissive recording material for electrophotography, comprising: a toner receiving layer containing a thermoplastic resin; and a surface treatment layer formed on the toner receiving layer and containing a modified silicone oil. 【請求項２】前記表面処理層は、さらに帯電防止剤を含
むことを特徴とする請求項１記載の電子写真用光透過性
被記録材。2. The light-transmissive recording material for electrophotography according to claim 1, wherein said surface treatment layer further contains an antistatic agent. 【請求項３】前記表面処理層は、変性シリコーンオイル
の含有量が層形成材料全体の１５〜５０重量％の範囲で
あることを特徴とする請求項１又は２記載の電子写真用
光透過性被記録材。3. The light-transmitting material for electrophotography according to claim 1, wherein the content of the modified silicone oil in the surface-treated layer is in a range of 15 to 50% by weight of the whole layer forming material. Recording material.