JPH111837A - Interlaced cohesive bulky yarn - Google Patents
Interlaced cohesive bulky yarnInfo
- Publication number
- JPH111837A JPH111837A JP15380197A JP15380197A JPH111837A JP H111837 A JPH111837 A JP H111837A JP 15380197 A JP15380197 A JP 15380197A JP 15380197 A JP15380197 A JP 15380197A JP H111837 A JPH111837 A JP H111837A
- Authority
- JP
- Japan
- Prior art keywords
- yarn
- interlaced
- bulky yarn
- mixed
- nozzle
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は新規な集合体構造を
有するインターレース抱合嵩高糸に関し、更に詳しく
は、特にタイルカーペット施工継ぎ目の目地の審美性を
改良し得る新規な集合体構造を有するインターレース抱
合嵩高糸に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an interlace-conjugated bulky yarn having a novel aggregate structure, and more particularly to an interlace-conjugate yarn having a novel aggregate structure capable of improving the aesthetics of a joint at a tile carpet construction seam. It relates to a bulky yarn.
【０００２】[0002]
【従来の技術】合成繊維マルチフィラメント嵩高糸のイ
ンターレース抱合糸は、タフテッドカーペットのパイル
糸として汎用されている。また、そのマルチフィラメン
ト嵩高糸に２種以上の糸条を用いて多色とした霜降調の
ミックス外観糸も多用されている。2. Description of the Related Art Synthetic multifilament bulky yarn interlace conjugate yarn is widely used as pile yarn for tufted carpet. In addition, a multicolored mixed appearance yarn of a frosted tone using two or more kinds of yarns for the multifilament bulky yarn is often used.
【０００３】一方、カーペットの使用形態は、施工の便
利さの面で、広幅長尺のカーペットからタイルカーペッ
トへと移行してきて、特に、オフィスビルの室内床用、
廊下用に多く用いられている。[0003] On the other hand, the use of carpets has shifted from wide and long carpets to tile carpets in terms of ease of construction, and especially for indoor floors of office buildings.
It is often used for hallways.
【０００４】ところが、タイルカーペットの場合、カー
ペットの製造工程で裁断されたものを、施行現場で元の
つながりに戻して敷詰めるのではなく、元々かけ離れた
部位にあったもの同士をつないでいくので、そのつなが
り部の目地の不自然さが目立つようになり、特に、多色
パイルカーペットでは大きな問題となっている。[0004] However, in the case of tile carpets, those cut in the carpet manufacturing process are not laid back to the original connection at the enforcement site, but those that were originally located far apart are connected to each other. However, unnatural joints at the joints become conspicuous, and this is a serious problem particularly in a multicolor pile carpet.
【０００５】従来、この問題の解決の為に、多色の構成
や撚糸による撚構造の追加、タフティング組織等で工夫
が加えられてきたが、未だ消費者の満足は得られていな
い。Conventionally, in order to solve this problem, a contrivance has been made with a multi-color structure, addition of a twisted structure with a twisted yarn, tufting structure, etc., but the satisfaction of consumers has not yet been obtained.
【０００６】また、インターレース抱合の糸形態につい
ても、撚糸の上撚と下撚りによるミックス外観の多様化
と同様な考え方で、インターレース抱合糸とインターレ
ース抱合してない糸とのインターレース抱合、或はイン
ターレース抱合した糸同士のインターレース抱合も行な
われてきたが、ミックス感を多様化する程度にとどまっ
ていた。The interlaced yarn form can be interlaced between interlaced yarns and non-interlaced yarns, or interlaced yarns, based on the same concept as diversifying the appearance of the mix by twisting and plying twisted yarns. Interlaced tying of the conjugated yarns has also been performed, but only to the extent that the mix feeling was diversified.
【０００７】即ち、この問題の根本的な原因であるイン
ターレース抱合糸の集合体構造にまで遡及して、タイル
カーペットのつながり部の目地の審美性を改良しようと
する試みはなかった。That is, no attempt has been made to improve the aesthetics of the joint of the tile carpet by going back to the aggregate structure of interlaced conjugate yarns, which is the root cause of this problem.
【０００８】[0008]
【発明が解決しようとする課題】本発明の課題は、特
に、多色パイルのタイルカーペット外観を粒杢調外観と
し、かつ、その施工継ぎ目に自然な目地の繋り観を付与
して審美性を高め得るインターレース抱合嵩高糸を創出
し、併せてその製造方法を提供することにある。SUMMARY OF THE INVENTION An object of the present invention is to provide a multicolored tile carpet having a grained appearance and a natural joint of the joints at the joints. It is an object of the present invention to create an interlaced conjugated bulky yarn capable of increasing the yarn density and to provide a production method thereof.
【０００９】[0009]
【課題を解決するための手段】本発明は、嵩高マルチフ
ィラメント糸の異色糸をインターレースミックスした抱
合糸において、従来のインターレース抱合糸の構造であ
る混繊・交絡部と混繊・非交絡部とに加えて、新たに非
混繊・非交絡部を混在させるとき、カーペットのパイル
において、それぞれの要素構造が外観効果に及ぼす作用
・効果が従来のそれとは全く異質なものに変化すること
を究明し、これにより、本発明の課題を解決できること
を見出し、本発明に到達した。SUMMARY OF THE INVENTION The present invention relates to a conjugated yarn obtained by interlacing different colored yarns of a bulky multifilament yarn in a mixed fiber / entangled portion and a mixed fiber / non-entangled portion which are structures of a conventional interlaced conjugate yarn. In addition to this, when mixing new non-mixed and non-entangled parts, the effect and effect of each element structure on the appearance effect in the carpet pile is completely different from the conventional one. However, the present inventors have found that the object of the present invention can be solved, and have reached the present invention.
【００１０】本発明の課題を解決するための手段は、以
下の通りである。 （１） マルチフィラメント嵩高糸であって、その長さ
方向に沿って、下記（ａ）、（ｂ）および（ｃ）のマル
チフィラメント集合体構造を含むことを特徴とするイン
ターレース抱合嵩高糸。 （ａ）構成フィラメント同士が混繊され、かつ、交絡集
束されている混繊・交絡部［Ａ］、（ｂ）構成フィラメ
ント同士が混繊されているが、交絡集束されていない混
繊・非交絡部［Ｂ］、（ｃ）構成フィラメント同士が混
繊されず、かつ、交絡集束もされていない非混繊・非交
絡部［Ｃ］、（２） ２本以上の糸条を合糸してインタ
ーレース抱合するに際し、間歇的に圧空を噴射する回転
式インターレースノズルを用いて、該間歇的に噴射する
ノズルの口径Ｄ（ｍｍ）を直径３〜６ｍｍの範囲とし、
かつ、該回転ノズルの周速度Ｎ（ｍ／分）と糸条の走行
速度Ｙ（ｍ／分）との関係を０．５≦Ｎ／Ｙ≦２．０の
範囲に保持して、インターレース抱合を行うことを特徴
とするインターレース抱合嵩高糸の製造方法、（３）
上記（１）項に記載のインターレース抱合嵩高糸を基布
に、ループパイル状にタフティングしてなることを特徴
とするタフテットカーペット、および（４） 上記
（３）項記載のタフテッドカーペットを、縦方向および
緯方向に長さ４０〜１５０ｃｍの範囲の大きさに裁断し
て形成されていることを特徴とするタイルカーペット。The means for solving the problems of the present invention are as follows. (1) A multifilament bulky yarn comprising a multifilament aggregate structure of the following (a), (b) and (c) along its length. (A) Mixed fiber / entangled portion [A] in which constituent filaments are mixed and entangled and bundled; (b) Mixed fiber / non-entangled but not entangled bundle of constituent filaments. Unentangled part [B], (c) Non-mixed / unentangled part [C], in which constituent filaments are not mixed and not entangled and bundled, (2) Twist two or more yarns At the time of interlace conjugation, using a rotary interlace nozzle that intermittently ejects compressed air, the diameter D (mm) of the intermittently ejecting nozzle is set to a range of 3 to 6 mm in diameter,
In addition, the relation between the peripheral speed N (m / min) of the rotary nozzle and the running speed Y (m / min) of the yarn is maintained in the range of 0.5 ≦ N / Y ≦ 2.0, and (3) A method for producing an interlaced conjugated bulky yarn,
The tufted carpet, characterized by being tufted in a loop pile shape on the basis of the interlaced bulky yarn according to the above (1), and (4) the tufted carpet according to the above (3). A tile carpet, which is formed by cutting into a size having a length in a range of 40 to 150 cm in a vertical direction and a weft direction.
【００１１】[0011]
【発明の実施の形態】図１は、本発明のインターレース
抱合嵩高糸を構成するフィラメント集合体構造の３つの
要素構造を模式的に図示したものである。FIG. 1 schematically illustrates three element structures of a filament aggregate structure constituting an interlaced bulky yarn of the present invention.
【００１２】該図において、［Ａ］は、構成フィラメン
ト同士が混繊され、かつ、交絡集束されている混繊・交
絡部であり、［Ｂ］は、構成フィラメント同士が混繊さ
れているが、交絡集束されていない混繊・非交絡部であ
り、［Ｃ］は、構成フィラメント同士が混繊されず、か
つ、交絡集束もされていない非混繊・非交絡部である。In the figure, [A] is a mixed fiber / entangled portion in which constituent filaments are mixed and entangled and bundled, and [B] is a mixture of constituent filaments. [C] is a non-mixed / non-entangled portion in which the constituent filaments are not mixed and are not entangled and bundled.
【００１３】まず初めに、要素構造［Ａ］、［Ｂ］、
［Ｃ］それぞれの特徴を主に嵩高性と色のミックス状態
の観点から説明し、その後に、それら要素構造が有機的
に繋がったインターレース抱合嵩高糸がタフティングさ
れカーペットパイル集団を形成したときに奏される効果
について説明する。First, element structures [A], [B],
[C] Each characteristic will be described mainly from the viewpoint of the bulkiness and the color mixing state, and then, when the interlace-conjugated bulky yarns whose element structures are organically connected are tufted to form a carpet pile group. The effect to be achieved will be described.
【００１４】嵩高マルチフィラメント糸が、２種の異色
性のマルチフィラメント群から構成されている場合を例
として説明する。嵩高性の観点から３者を比較すると、
最も嵩高性が高いのは［Ｃ］であり、［Ｂ］は混繊して
るためやや嵩高性が低く目であり、［Ａ］は交絡により
強く集束している為嵩高性は低い。The case where the bulky multifilament yarn is composed of two types of heterofilament multifilaments will be described as an example. Comparing the three from the viewpoint of bulkiness,
[C] has the highest bulkiness, [B] has a slightly low bulkiness due to blending, and is an eye, and [A] has a low bulkiness because it is strongly entangled by entanglement.
【００１５】一方、色のミックス状態の観点から３者を
比較すると、［Ｃ］では、２種の異色性のマルチフィラ
メント群が非混繊の為、引揃え状態にあり、粒杢感があ
って２種の異色の色差が明瞭に視える。これに対して、
［Ｂ］では混繊状態にあって２種の異色性のマルチフィ
ラメント群がミックスされている為、霜降調ないしは２
種の中間色に視え、その上に糸条が捲縮で嵩張って膨ら
んでいるため、色調が霞がかかったぼやけた状態に視え
る。そして［Ａ］は［Ｂ］と同様に混繊されてはいる
が、強く集束されている点で違っていて、色調が霞がか
かってぼやけて見えるということはなく２種の色差が明
瞭に見え、従って、混繊が単繊維オーダーで完全に起こ
っている部分では霜降り調に見えるが、混繊が数本オー
ダーで起こっている部分では、細かな粒杢感に視え、殆
んどは後者の状態になっている。On the other hand, comparing the three from the viewpoint of the color mixing state, in [C], the two different-color multifilament groups are in the aligned state because of non-fiber mixing, and have a grainy feeling. The two different color differences are clearly visible. On the contrary,
In [B], since two types of multi-filaments having different colors are mixed in the mixed state, the frosting or 2
Seen to be the neutral color of the seed, and the yarns are crumpled and bulky and swollen on top of it, so that the color tone looks fuzzy and blurred. And although [A] is mixed like [B], it differs in that it is strongly focused, and the color tone does not look hazy and blurry, and the two kinds of color differences are clearly seen. It looks like, therefore, it looks like a marbling in the part where the mixed fiber is completely in the order of single fiber, but in the part where the mixed fiber is in the order of several fibers, it looks like a fine grained feeling, almost It is in the latter condition.
【００１６】図２は、前記要素構造［Ａ］、［Ｂ］、
［Ｃ］の繋りからなる本発明のインターレース抱合嵩高
糸の好ましい繋りを示した模式図である。該図におい
て、要素構造は［Ｃ］、［Ａ］、［Ｂ］、［Ａ］の順で
繋り、その繋りを一単位ｕとして、繰返し繋がって糸条
を構成することを示している。FIG. 2 shows the element structures [A], [B],
It is a schematic diagram showing preferred connection of the interlace conjugated bulky yarn of the present invention which consists of connection of [C]. In the figure, the element structures are connected in the order of [C], [A], [B], and [A], and the connection is defined as one unit u, which indicates that the connection is repeated and forms a yarn. .
【００１７】この糸条をパイル布帛にタフティングしカ
ーペットとして、そのカーペット表面のパイル集団を見
ると、嵩高性は［Ｃ］と［Ｂ］とにより得られ、色のミ
ックス調子は［Ｃ］と［Ａ］とにより粒杢感があって尚
且つ２種の異色の色差が明瞭に見える外観が表現され、
その中へ霜降調のぼやけた色調の［Ｂ］が散在してい
る。しかし［Ｂ］は繰返しの間隔が離れている上に量的
にも少いので目立った存在ではない。［Ｃ］と［Ａ］だ
けでは、粒杢感の色差が明瞭すぎて人工的なきつさがあ
るのを、［Ｂ］がその中に散在して和らげる作用をして
いる。When this yarn is tufted on a pile fabric to form a carpet and the pile group on the carpet surface is viewed, the bulkiness is obtained by [C] and [B], and the color tone is [C]. With [A], the appearance of a grainy appearance and the two kinds of different color differences can be clearly seen,
[B] of a blurred color tone with a marbling tone is scattered therein. However, [B] is not conspicuous because the repetition interval is large and the repetition interval is small. With [C] and [A] alone, the color difference of the graininess is too clear and there is an artificial tightness, but [B] is scattered inside to soften it.
【００１８】カーペット表面のパイル集団が、このよう
な嵩高と色調のパイル集団となっているため、タイルカ
ーペットとして裁断し、任意のタイル同士を施工して敷
詰めても、その継目の目地は自然なつながり感をもって
視える。Since the pile group on the surface of the carpet is a pile group having such bulkiness and color tone, even if it is cut as a tile carpet and any tiles are constructed and laid, the joint of the seam is natural. You can see with a great sense of connection.
【００１９】ここで、比較の為に、従来のインターレー
ス抱合嵩高糸の場合について説明する。図３は従来のイ
ンターレース抱合嵩高糸の場合の要素構造の繋りを示し
た模式図である。図３において、［Ｂ′］は混繊・非交
絡部であって、本発明の糸条でいう［Ｂ］と本質的に同
じものである。また、［Ａ′］は混繊・交絡部であっ
て、本発明の糸条でいう［Ａ］と本質的に同じものであ
る。そして、この従来の糸条の場合には［Ｂ′］と
［Ａ′］との繋りを一単位Ｔとして、繰返し繋って糸条
を構成している。そして通常は［Ｂ′］の長さの方が
［Ａ′］の長さよりも長い。Here, for comparison, the case of a conventional interlaced bulky yarn will be described. FIG. 3 is a schematic view showing the connection of the element structures in the case of the conventional interlaced bulky yarn. In FIG. 3, [B '] is a mixed fiber / non-entangled portion, which is essentially the same as [B] in the yarn of the present invention. [A '] is a mixed fiber / entangled portion, which is essentially the same as [A] in the yarn of the present invention. In the case of this conventional yarn, the connection between [B '] and [A'] is defined as one unit T, and the connection is repeated to form a yarn. Usually, the length of [B '] is longer than the length of [A'].
【００２０】それをタフティングしてカーペットとし、
表面のパイル集団を視ると、全体としては嵩高で霜降調
のぼやけた色調の［Ｂ′］が主となってパイル布帛を形
成しており、その中に集束した細かな粒感の明瞭な色調
のパイルが存在する。[0020] It is tufted to make a carpet,
Looking at the pile group on the surface, the pile fabric is mainly composed of [B '], which is bulky and has a blurred color with a frosty tone, and has a clear fine grain feeling converged therein. There is a pile of tones.
【００２１】ここで、従来から問題とされているのが、
［Ａ′］のパイルが隣り合って縦横方向に集団を作った
塊状の部分が発生することである。この塊状部分は色調
が明瞭な為、非常に目立ち易く、かつ、交絡により糸条
が細く締まっているため虫喰い状に見え審美性を低下さ
せている。Here, what has conventionally been a problem is:
That is, a pile-like portion in which piles of [A '] are adjacent to each other to form a group in the vertical and horizontal directions is generated. This massive portion has a clear color tone and is very conspicuous. In addition, since the thread is thin and tight due to entanglement, it looks like an insect bite and reduces aesthetics.
【００２２】その上に、もっと問題なのは、タイルカー
ペットとして施工した場合、その継ぎ目で霜降調の裁断
面と虫喰状塊の裁断面とが合わされる部分ができること
で、継ぎ目が非常に不自然なものとなり審美性の低いも
のとなってしまう。Further, what is more problematic is that when the tile carpet is constructed, a portion where the cut surface of the frost-like tone and the cut surface of the worm-like mass are formed at the seam, and the seam is very unnatural. It becomes a thing and a thing with low aesthetics.
【００２３】本発明のインターレース抱合嵩高糸と従来
のそれとについて説明したが、今ここで、両者対比し
て、糸構造の違いと、その違いがパイル布帛表面の視感
に及ぼす作用・効果について整理して説明する。The interlace-conjugated bulky yarn of the present invention and the conventional one have been described. Now, in comparison with the both, the difference in the yarn structure and the effect and effect of the difference on the visual perception of the pile fabric surface will be summarized. I will explain.
【００２４】まず、糸構造の基本的な違いは、図３と図
１または図２とを対比して解るように、従来糸条の要素
構造［Ａ′］＝Ａ、［Ｂ′］＝［Ｂ］に対して、本発明
の糸条はそれに新しい要素構造［Ｃ］が加わった構造を
している。これは表層的には、唯単に従来の糸条に
［Ｃ］が加わっただけのように見える。First, the basic difference of the yarn structure is that the element structure of the conventional yarn [A '] = A, [B'] = [, as can be understood by comparing FIG. 3 with FIG. 1 or FIG. In contrast to B], the yarn of the present invention has a structure in which a new element structure [C] is added. On the surface, this looks just like adding a [C] to a conventional yarn.
【００２５】しかしながら、これがカーペットのパイル
を形成したとき、新しい構造要素［Ｃ］が加わったこと
により、従来の要素構造［Ａ］、［Ｂ］の視感効果に
［Ｃ］の効果が加算されるのではなく、意外にも
［Ａ］、［Ｂ］の作用・効果が全く異質もなものに一変
する。However, when this forms a pile of carpet, the effect of [C] is added to the visual effect of the conventional element structures [A] and [B] due to the addition of the new structural element [C]. Instead, surprisingly, the actions and effects of [A] and [B] are completely different.
【００２６】即ち、従来の糸条では、パイル布帛表面の
視感表現の主役は［Ｂ′］であり、［Ａ′］は工程取扱
性付与の有利な点はあるものの視感的には欠点にもなっ
ていた。That is, in the conventional yarn, the leading role of visual expression on the pile fabric surface is [B '], and [A'] is an advantage of imparting process handleability, but is a disadvantage in visual sense. It was also.
【００２７】これに対して、本発明の糸条では、パイル
表面の視感表現の主役は［Ｃ］と［Ａ］でありこの場合
［Ａ］はもはや視感表現の欠点ではなく主役の一部とな
っている。［Ａ］をルーペで拡大してよく観察すると集
束しているために従来の糸条の場合と同様に虫喰い欠点
はあっても、カーペットとして肉眼で見た場合、それ以
上に色のミックス状態が［Ｃ］の擬似態として［Ｃ］に
同質化し主役の一部となっている。On the other hand, in the yarn of the present invention, [C] and [A] play a leading role in the visual expression of the pile surface, and in this case, [A] is no longer a defect of the visual expression but is one of the leading roles. Department. When [A] is magnified with a magnifying glass and observed well, it is converged because of the convergence, as in the case of the conventional thread. However, when viewed with the naked eye as a carpet, the color is more mixed. Is homogenized as [C] as a pseudo-mimic of [C] and is part of the leading role.
【００２８】このように主役が［Ｂ′］から［Ｃ］＋
［Ａ］に変わったことから、従来の霜降調に対し、本発
明では粒杢調の高級感のある視感表面となり、その際、
明瞭な粒杢感すなわち人工的な外観は［Ｂ］による散在
する霜降パイルにより和らげられ、一層審美性に優れた
パイル布帛となる。同時にタイルカーペットの継ぎ目の
不自然さも解消され、施工後のカーペット外観の審美性
も格段に向上する。As described above, the leading role is changed from [B '] to [C] +
Since it has been changed to [A], the present invention provides a high-grade sensation surface with a grained appearance in contrast to the conventional marbled tone.
The clear grained feeling, that is, the artificial appearance, is alleviated by the scattered marbled pile according to [B], and the pile fabric is more excellent in aesthetics. At the same time, the unnaturalness of the joint of the tile carpet is eliminated, and the aesthetic appearance of the carpet after construction is significantly improved.
【００２９】次に、本発明のインターレース抱合嵩高糸
の好ましい態様について、更に詳しく説明する。要素構
造［Ａ］、［Ｂ］および［Ｃ］の長さの関係は、嵩高性
を高く保持するために、［Ａ］の長さは［Ｂ］や［Ｃ］
の長さよりも短い方が好ましい。そして、カーペットの
カラーミックス外観を霜降調でなく、粒杢調とする為
に、［Ａ］、［Ｂ］、［Ｃ］の長さの比率の関係を（２
・［Ａ］＋［Ｃ］）／［Ｂ］を１．５〜３．７の範囲と
して、粒杢因子の［Ｃ］と［Ａ］を多くし、その人工的
できつい外観になりがちである状態を［Ｂ］を散在させ
ることによって和らげることが好ましい。その際［Ｃ］
と［Ｂ］の長さの比率は［Ｃ］／［Ｂ］を０．５〜２．
０とするのがよい。Next, a preferred embodiment of the interlace-conjugated bulky yarn of the present invention will be described in more detail. The relationship between the lengths of the element structures [A], [B] and [C] is such that the length of [A] is [B] or [C] in order to maintain high bulkiness.
It is preferable that the length is shorter than the length. Then, in order to make the appearance of the carpet color mix look grainy rather than marbled, the relationship between the length ratios of [A], [B], and [C] is (2).
・ [A] + [C]) / [B] is in the range of 1.5 to 3.7, and the grain size factors [C] and [A] are increased to tend to give an artificially tight appearance. It is preferable to alleviate a certain state by scattering [B]. At that time [C]
The ratio of the length of [C] / [B] is 0.5 to 2.
It is better to set to 0.
【００３０】そして、上記の様な関係を［Ａ］、［Ｂ］
および［Ｃ］に持たせるには、その繋りを［Ｃ］、
［Ａ］、［Ｂ］、［Ａ］の繋りを繰返し単位とする構造
とするのが最も好ましく、勿論一部にそれとは違った配
列を含んでいても差支えない。Then, the above relations are defined as [A] and [B]
And [C], the connection is [C],
It is most preferable to use a structure in which the connection of [A], [B], and [A] is a repeating unit. Of course, a part of the structure may have a different arrangement.
【００３１】具体的な長さとしては、例えば２５００デ
ニールのインターレース抱合嵩高糸の場合、［Ａ］は９
〜１４ｍｍの範囲、［Ｂ］は１８〜２４ｍｍの範囲、
［Ｃ］は１７〜３３ｍｍの範囲で、繰返しの一単位
［Ｃ］、［Ａ］、［Ｂ］、［Ａ］は６３〜７９ｍｍの範
囲が好ましく、このｍ当りの繰返し単位の数は１２．７
〜１５．９回／ｍの範囲が好ましい範囲である。As a specific length, for example, in the case of 2500 denier interlaced bulky yarn, [A] is 9
１４14 mm range, [B] is 18-24 mm range,
[C] is in the range of 17 to 33 mm, and one unit of repetition [C], [A], [B], and [A] is preferably in the range of 63 to 79 mm, and the number of repeating units per m is 12. 7
A range of 15.9 times / m is a preferable range.
【００３２】本発明の糸条の繊度はパイルカーペット用
途としては、１８００〜３０００デニールの範囲、単繊
維デニールは８〜２５デニールの範囲が好ましい。The fineness of the yarn of the present invention is preferably in the range of 1800 to 3000 denier for use as a pile carpet, and the single fiber denier is preferably in the range of 8 to 25 denier.
【００３３】また、色差のない無地のカーペットでも形
態的な面で同様の効果は得られるが、審美性に優れたカ
ーペットを製造するためには色のミックスした糸条を用
いるのが好ましい。Although the same effect can be obtained in terms of morphology even with a solid carpet having no color difference, it is preferable to use a yarn in which colors are mixed in order to produce a carpet having excellent aesthetics.
【００３４】色をミックスした糸条は、顔料による原着
糸、染色された糸、染色により互いに異染又は濃淡に染
まる糸等を組合せてインターレース抱合することによっ
て製造される。また互いに光沢の異なる糸条を用いても
類似の効果が得られる。A yarn having a mixed color is produced by interlacing a combination of a dyed yarn, a dyed yarn, a yarn which is dyed differently or shaded by dyeing, or the like. Similar effects can be obtained by using yarns having different gloss from each other.
【００３５】インターレースの交絡部［Ａ］の数は３０
〜５０個／ｍの範囲が好ましく、特に２４〜３５個／ｍ
が好ましい。The number of interlaced parts [A] of the interlace is 30.
-50 / m, preferably 24-35 / m
Is preferred.
【００３６】糸条を構成する合成繊維マルチフィラメン
ト糸としては、同種又は異種のポリマーの組合せでもよ
く、例えばポリエステル、ナイロン６、ナイロン６６が
適している。As the synthetic fiber multifilament yarn constituting the yarn, a combination of the same or different polymers may be used. For example, polyester, nylon 6, and nylon 66 are suitable.
【００３７】尚、フィラメント断面は、丸断面の他三角
断面で異形度が２．５〜４．５の範囲のものであっても
よく、異型中空断面で異形度が１．０〜２．５の範囲の
ものであってもよい。The filament cross section may be a round cross section or a triangular cross section having a degree of irregularity in the range of 2.5 to 4.5, and a irregular hollow section having a degree of irregularity of 1.0 to 2.5. May be in the range.
【００３８】嵩高糸の捲縮形態は、エアースタッファ
ー、機械押込、エアー吹付衝突、タスラン解舒等の捲縮
賦形等公知の所謂ＢＣＦ賦形による３次元ランダムクリ
ンプが適している。As the crimped form of the bulky yarn, three-dimensional random crimping by known so-called BCF shaping, such as crimping such as air stuffer, mechanical indentation, air spray collision, and unwinding of Taslan, is suitable.
【００３９】次に、本発明のインターレース抱合嵩高糸
の製造方法について説明する。図４は、本発明の糸条の
製造方法を説明する為の工程模式図である。また図５は
エアーノズルの作用を説明するためのノズル断面図であ
る。Next, the method for producing the interlace-conjugated bulky yarn of the present invention will be described. FIG. 4 is a process schematic diagram for explaining the yarn manufacturing method of the present invention. FIG. 5 is a cross-sectional view of the nozzle for explaining the operation of the air nozzle.
【００４０】本発明のインターレース抱合嵩高糸の製造
方法は、衣料用の細繊度の抱合嵩高糸からカーペット等
インテリア用太繊度の抱合嵩高糸まで広く適用可能であ
るが、特にカーペット用抱合嵩高糸の製造に適してい
る。また、用いる糸条もフィラメントの捲縮糸・非捲縮
糸や紡績糸など広く用いることができる。The method for producing the interlaced conjugated bulky yarn of the present invention can be widely applied from fine conjugated bulky yarns for clothing to conjugated bulky yarns for carpets and other interiors. Suitable for manufacturing. Also, the yarn used can be widely used, such as a crimped yarn of a filament, a non-crimped yarn, and a spun yarn.
【００４１】特に、カーペット用抱合嵩高糸を製造する
場合には、マルチフィラメント嵩高糸が適しており、こ
の場合について以下に更に詳しく説明する。カーペット
用嵩高抱合糸に用いる糸条は、図４の糸条１、２でいえ
ば、それぞれ嵩高糸を用い、エアースタッファー加工、
機械押込加工、タスランループの解舒加工、仮撚加工、
偏芯型或はサイドバイサイド型コンジュゲート糸の捲縮
発現等による捲縮嵩高糸が用いられるが、その中でも特
にエアースタッファ加工した捲縮嵩高糸が適している。Particularly when producing conjugated bulky yarn for carpet, multifilament bulky yarn is suitable, and this case will be described in more detail below. The yarns used for the bulky conjugate yarn for carpets are, for example, yarns 1 and 2 in FIG.
Mechanical indentation, unwinding of Taslan loop, false twisting,
A crimped bulky yarn resulting from the development of crimping of an eccentric type or side-by-side type conjugate yarn is used. Among them, a crimped bulky yarn processed by air stuffing is particularly suitable.
【００４２】カーペットに異色ミックス外観を付与する
ためには、異染性のポリマーからなる糸条の組合せまた
は同種ポリマーでも顔料で異色に着色した糸条の組合せ
を用いるとよい。例えば、ナイロン、ポリエステル或は
ポリプロピレンからなる糸条の組合せや、ナイロン１０
０％の場合には、酸性染料に染まるＮＨ2 末端基の多い
ナイロン糸条と塩基性染料に染まるＳＯ3 末端基の多い
ナイロン糸条との組合せ等である。In order to give the carpet a different mixed appearance, it is preferable to use a combination of yarns composed of heterochromatic polymers or a combination of yarns of the same polymer and colored in different colors with a pigment. For example, a combination of yarns made of nylon, polyester or polypropylene, or nylon 10
In the case of 0%, a combination of a nylon yarn having many NH 2 end groups dyeing an acid dye and a nylon yarn having many SO 3 terminal groups dyeing a basic dye is used.
【００４３】また、用いる糸条の繊度はカーペット用の
場合、図４の糸条１、２で言えば、それぞれ８００〜１
５００デニールの範囲、単繊維繊度は８〜２５デニール
の範囲が好ましい。また供給する糸条は２本でなく３本
であってもよい。In the case of carpets, the fineness of the yarn used is 800 to 1 in the case of yarns 1 and 2 in FIG.
The range of 500 denier and single fiber fineness are preferably in the range of 8 to 25 denier. Also, the number of supplied yarns may be three instead of two.
【００４４】図４において、糸条１、２は、それぞれ供
給ローラ３、４により供給され、ヤーンガイド５で合糸
して、インターレースノズル６へ供給され、間歇抱合処
理されて、引取ローラ７によって引取られ巻取ローラ８
でインターレース抱合嵩高糸として巻取られる。In FIG. 4, the yarns 1 and 2 are supplied by supply rollers 3 and 4 respectively, are combined by a yarn guide 5, are supplied to an interlace nozzle 6, are intermittently conjugated, and are taken by a take-up roller 7. Take-up winding roller 8
Is wound as an interlaced bulky yarn.
【００４５】ガイド５で糸条１、２を合糸する際、等糸
長の引揃えが、カーペットのタフティング性と目面の点
で好ましいが、インターレース抱合糸の嵩高性を向上さ
せる目的で５％までの範囲でフィード差を持たせてもよ
く、供給ローラ３、４の速度関係で設定される。When the yarns 1 and 2 are combined by the guide 5, it is preferable that the equal yarn lengths be aligned in terms of the tufting property and the eye surface of the carpet, but for the purpose of improving the bulkiness of the interlaced conjugate yarn. The feed difference may be provided within a range of up to 5%, and is set according to the speed relationship of the supply rollers 3 and 4.
【００４６】また、インターレースノズルへのオーバー
フィード率即ち供給ローラ３、４と引取ローラ８との間
のオーバーフィード率は２〜１０％として、インターレ
ース抱合し易くするとよい。The overfeed ratio to the interlace nozzle, that is, the overfeed ratio between the supply rollers 3 and 4 and the take-up roller 8 is preferably set to 2 to 10% to facilitate interlacing.
【００４７】インターレースノズル６は図５に示すよう
な間歇的に圧空を噴射する回転式インターレースノズル
である。ノズル６において、回転体９に設けられた圧空
噴射孔１０（該図では６個）が回転移動して、圧空配管
１１より出た枝管１２（固定）の位置に来て連通したと
き圧空が噴射され、次の圧空噴射孔１０が回転して来る
までは圧空は噴射されず、間歇的に圧空が噴射される。The interlace nozzle 6 is a rotary interlace nozzle which injects compressed air intermittently as shown in FIG. In the nozzle 6, when the compressed air injection holes 10 (six in the figure) provided in the rotating body 9 rotate and come to the position of the branch pipe 12 (fixed) coming out of the compressed air pipe 11, the compressed air is released. No compressed air is injected until the next compressed air injection hole 10 is rotated, and the compressed air is injected intermittently.
【００４８】ノズル６の圧空噴射孔１０より噴射された
圧空は圧空受部１３により受けられる。該圧空受部１３
には糸条１、２が通過する溝１４が設けられている。The compressed air injected from the compressed air injection hole 10 of the nozzle 6 is received by the compressed air receiving portion 13. The compressed air receiving portion 13
Is provided with a groove 14 through which the yarns 1 and 2 pass.
【００４９】インターレース抱合の条件では、まず、間
歇的に圧空を噴射するノズルの口径Ｄ（ｍｍ）を直径３
〜６ｍｍの範囲とすることが必要である。直径が３ｍｍ
未満の場合、圧空流量が少なく、図２に示した混繊・交
絡部［Ａ］の絡みが弱くまた短くなりすぎて糸条の取扱
性が問題となる。また逆に６ｍｍを越えると流量が多す
ぎて、混繊・交絡部［Ａ］が長くなりすぎ、かつ図２に
示した非混繊・非交絡部［Ｃ］が短くなり、糸条の嵩高
性が低くなり、カラーミックスの杢調子も低級なものと
なってしまう。In the interlace conjugation condition, first, the diameter D (mm) of the nozzle for intermittently injecting compressed air is set to a diameter of 3 mm.
It is necessary to be within a range of ６6 mm. 3mm in diameter
If it is less than 1, the compressed air flow rate is small, and the entanglement of the mixed fiber / entangled portion [A] shown in FIG. 2 is weak and too short, and the handling of the yarn becomes a problem. Conversely, if it exceeds 6 mm, the flow rate is too large, and the mixed / entangled portion [A] becomes too long, and the non-mixed / non-entangled portion [C] shown in FIG. The quality is low, and the heather tone of the color mix is low.
【００５０】そして、ノズルの口径Ｄを３〜６ｍｍとし
たとき、噴射圧空を糸条に効果的に作用させ、ノズルの
位置噴射で図２に示した糸条構造の一単位ｕ（［Ｃ］、
［Ａ］、［Ｂ］、［Ａ］の繋り］を形成させる為には、
ノズル回転体９の周速度Ｎ（ｍ／分）を糸条ｙの走行速
度Ｙ（ｍ／分）との関係を０．５≦Ｎ／Ｙ≦２．０の範
囲に保持して、インターレース抱合を行うことが必要で
ある。Ｎ／Ｙが０．５未満では、圧空噴射時間が長くな
り混繊・交絡部［Ａ］が長く強固になり嵩高性の低下
と、杢調子の低級化をひきおこしてしまう。When the diameter D of the nozzle is 3 to 6 mm, the jet pressure air effectively acts on the yarn, and one unit u ([C]) of the yarn structure shown in FIG. ,
In order to form [A], [B], and [A],
The relation between the peripheral speed N (m / min) of the nozzle rotator 9 and the running speed Y (m / min) of the yarn y is maintained in the range of 0.5 ≦ N / Y ≦ 2.0, and the interlace conjugation is performed. It is necessary to do. If N / Y is less than 0.5, the compressed air injection time becomes longer, the mixed fiber / entangled portion [A] becomes longer and firmer, which causes a decrease in bulkiness and a lower grade of heather.
【００５１】逆にＮ／Ｙが２．０を越えると、圧空噴射
時間が短くなり、混繊・交絡部［Ａ］の絡みが弱くなり
取扱い性が低下してしまう。On the other hand, if N / Y exceeds 2.0, the compressed air injection time is shortened, the entanglement of the mixed / entangled portion [A] is weakened, and the handleability is reduced.
【００５２】最も好ましい条件では、ノズル口径を４．
５ｍｍとし、Ｎ／Ｙ＝１．０とした場合である。その上
で、抱合嵩高糸の繊度との関係から付加する混繊・交絡
部［Ａ］の数を決め、Ｎ／Ｙとの関係からノズル噴射孔
１０の数を決めるとよい。Under the most preferable conditions, the nozzle diameter is set to 4.
5 mm and N / Y = 1.0. After that, the number of the mixed / entangled portions [A] to be added may be determined from the relationship with the fineness of the conjugated bulky yarn, and the number of the nozzle injection holes 10 may be determined from the relationship with N / Y.
【００５３】例えば、カーペット用の繊度１８００〜３
０００デニールの範囲の糸条の場合、交絡部［Ａ］の数
は３０〜５０個／ｍの範囲が好ましく、ノズル１０の１
噴射で２個の交絡部［Ａ］を形成することから、回転体
９の周長が３０ｃｍの場合ノズル噴射孔１０は４〜８個
の範囲で設けるのが好ましい。For example, fineness 1800-3 for carpet
In the case of a yarn in the range of 000 denier, the number of the entangled portions [A] is preferably in the range of 30 to 50 yarns / m.
Since two entangled portions [A] are formed by injection, it is preferable to provide 4 to 8 nozzle injection holes 10 when the circumference of the rotating body 9 is 30 cm.
【００５４】ノズル噴射孔１０の走行糸ｙに対する圧空
噴射角は垂直に噴射するのが好ましく、角度を設ける場
合でも９０°±５°の範囲がよい。また、回転体９の回
転方向は糸の進行方向でも逆方向でもよい。The compressed air injection angle of the nozzle injection hole 10 with respect to the traveling yarn y is preferably perpendicularly injected, and even when an angle is provided, the angle is preferably in a range of 90 ° ± 5 °. Further, the rotation direction of the rotating body 9 may be the traveling direction of the yarn or the reverse direction.
【００５５】加工速度は５０〜１０００ｍ／ｍｉｎの範
囲で糸条の繊度に合わせて設定すればよいが、カーペッ
ト用の２，５００デニール前後の糸条では３００〜６０
０ｍ／ｍｉｎの範囲が糸構造形成の点で好ましい。The processing speed may be set in the range of 50 to 1000 m / min in accordance with the fineness of the yarn, but 300 to 60 denier yarn for carpet is used.
The range of 0 m / min is preferable from the viewpoint of forming a yarn structure.
【００５６】圧空圧は２〜１０ｋｇ／ｃｍ2 の範囲で、
カーペット用の場合は３〜７ｋｇ／ｃｍ2 が好ましい。The pneumatic pressure is in the range of 2 to 10 kg / cm 2 ,
In the case of a carpet, it is preferably 3 to 7 kg / cm 2 .
【００５７】本発明のインターレース抱合嵩高糸は、タ
フティング機を用いて、この嵩高糸をフェースヤーンと
して、基布にループパイル状にタフティングし、さらに
裏うち樹脂層を形成してタフテッドカーペットとする。The interlace-conjugated bulky yarn of the present invention is tufted using a tufting machine to tuft the bulky yarn into a face yarn in the form of a loop pile on a base fabric, and further forming a resin layer on the back. And
【００５８】次いで、そのカーペットを縦方向および緯
方向に長さ４０〜１５０ｃｍの範囲の大きさに裁断し、
タイルカーペットとする。Next, the carpet is cut into a size having a length of 40 to 150 cm in the longitudinal direction and the weft direction,
Tile carpet.
【００５９】[0059]
［実施例１］繊度１３００デニール／８０フィラメント
のカチオン可染タイプナイロン６のエアースタッファー
加工されたマルチフィラメント嵩高糸と繊度１３００デ
ニール／８０フィラメントのレギュラー染色タイプナイ
ロン６エアースタッファー加工されたマルチフィラメン
ト嵩高糸とを引揃えて、間歇的に圧空を噴射する回転式
インターレースノズルを用いて、ノズル回転体周長３
０．９ｃｍ、ノズル口径４．５ｍｍ、ノズル孔数４個、
ノズル回転体周速度６００ｍ／ｍｉｎ、圧空圧５ｋｇ／
ｃｍ2 、オーバーフィード率５％、糸条速度６００ｍ／
ｍｉｎでインターレース抱合加工した。Example 1 Multi-filament bulky yarn of 1300 denier / 80 filament cationic dyeable nylon 6 air-stuffed and regular dyed type of 1300 denier / 80 filament nylon 6 air-stuffed multi-filament bulky yarn Using a rotary interlace nozzle that intermittently ejects compressed air, the nozzle rotor body circumference 3
0.9 cm, nozzle diameter 4.5 mm, four nozzle holes,
Nozzle rotating body peripheral speed 600m / min, air pressure 5kg /
cm 2 , overfeed rate 5%, yarn speed 600 m /
min interlaced.
【００６０】得られたインターレース抱合嵩高糸をゲー
ジ１／１０、ステッチ１２個／インチ、パイル長３．５
ｍｍのループパイルにタフティングしてループカーペッ
トを得、それを縦横６０ｃｍ長の正方形に裁断してタイ
ルカーペットとした。The obtained interlaced conjugated bulky yarn was gauge 1/10, stitched 12 pieces / inch, pile length 3.5.
A loop carpet was obtained by tufting into a loop pile having a length of 60 mm and cut into a square having a length of 60 cm and a tile carpet.
【００６１】評価は、糸構造およびタフティング時の糸
の取扱性、カーペットパイルの嵩高性、カラーミックス
外観、タイルカーペット継ぎ目の目地の繋りの自然さに
ついて行った。Evaluations were made on the yarn structure, yarn handling during tufting, bulkiness of the carpet pile, color mix appearance, and the naturalness of the connection of the joints of the tile carpet.
【００６２】その結果、糸構造は、混繊・交絡部
［Ａ］、混繊・非交絡部［Ｂ］および非混繊・非交絡部
［Ｃ］のそれぞれの長さは、９ｍｍ、２４ｍｍおよび３
５ｍｍであって、［Ｃ］、［Ａ］、［Ｂ］、［Ａ］を一
単位とする繋りの繰返し構造で形成されていた。その繰
返し単位ｕの長さは７７ｍｍ、１ｍ長さ当りの繰返し回
数は１３回／ｍ、交絡部の数［Ａ］は２６個／ｍであっ
た。As a result, the yarn structure is such that the lengths of the mixed fiber / entangled part [A], the mixed fiber / non-entangled part [B] and the non-woven / unentangled part [C] are 9 mm, 24 mm and 3
It was 5 mm, and was formed in a continuous repeating structure with [C], [A], [B], and [A] as one unit. The length of the repeating unit u was 77 mm, the number of repetitions per 1 m length was 13 times / m, and the number of interlaced parts [A] was 26 pieces / m.
【００６３】また、長さ比（２［Ａ］＋［Ｃ］）／
［Ｂ］は２．２であり、カーペット外観は粒杢調であ
り、また［Ｃ］／［Ｂ］は１．５で粒杢に［Ｂ］が散在
し、自然な和らぎ感のある粒杢となっていた。また、そ
の結果、タイルカーペットの継ぎ目の目地も一体物のよ
うな感じで撃がっていた。（［Ｃ］＋［Ｂ］）／２
［Ａ］は３．３であり、カーペットの嵩高性も十分にバ
ルキーな感触があった。The length ratio (2 [A] + [C]) /
[B] is 2.2, the appearance of the carpet is grainy, and [C] / [B] is 1.5, and [B] is scattered in the grain, giving a natural relaxation. Had become. Also, as a result, the joints of the tile carpet were shot with a feeling of one piece. ([C] + [B]) / 2
[A] was 3.3, and the bulkiness of the carpet was sufficiently bulky.
【００６４】［実施例２］繊度がそれぞれ８３０デニー
ル／４８フィラメントのレギラー可染タイプ、レギュラ
ー濃染タイプ、カチオン可染タイプの３者のナイロン６
エアースタッファー加工嵩高加工糸を引揃えて、間歇的
に圧空を噴射する回転式インターレースノズルを用いて
インターレース抱合加工した。インターレースノズルは
ノズル回転体周長を３０．９ｃｍ、ノズル孔数４個と
し、ノズル口径を２〜８ｍｍの範囲で変化させ、またノ
ズル回転体の速度を糸速に対してＮ／Ｙ＝０．３〜２．
３の範囲で変化させた。糸速度は６００ｍ／ｍｉｎと
し、圧空圧５ｋｇ／ｃｍ2 、オーバーフィード率５％と
した。[Example 2] Nylon 6 of three types, a regular dyeable type, a regular dark dyeable type and a cationic dyeable type, each having a fineness of 830 denier / 48 filaments
The air stuffer-processed bulky yarn was aligned and interlaced using a rotary interlace nozzle that intermittently ejects compressed air. The interlace nozzle has a nozzle rotating body circumference of 30.9 cm and four nozzle holes, changes the nozzle diameter in the range of 2 to 8 mm, and sets the speed of the nozzle rotating body to N / Y = 0. 3-2.
3 was changed. The yarn speed was 600 m / min, the pneumatic pressure was 5 kg / cm 2 , and the overfeed rate was 5%.
【００６５】得られたインターレース抱合嵩高糸をゲー
ジ１／１０、ステッチ１２個／インチ、パイル長３．５
ｍｍのループパイルにタフティングしてループカーペッ
トを得、それを６０ｃｍ長の正方形に裁断しタイルカー
ペットとした。The obtained interlaced conjugated bulky yarn was gauged 1/10, stitched 12 pieces / inch, pile length 3.5.
The loop carpet was tufted to obtain a loop carpet, which was cut into a square having a length of 60 cm to obtain a tile carpet.
【００６６】評価は、糸構造およびタフティング時の糸
の取扱性、カーペットパイルの嵩高性、カラーミックス
外観、タイルカーペット継ぎ目の目地の繋りの自然さに
ついて行った。Evaluations were made on the yarn structure, the handling properties of the yarn during tufting, the bulkiness of the carpet pile, the appearance of the color mix, and the naturalness of the connection between the joints of the tile carpet.
【００６７】その結果は表１に示したとおりである。実
験Ｎｏ．１はノズル口径Ｄが小さい為、混繊交絡部
［Ａ］の長さが短くカーペットのタフト性が悪く、粒杢
感も低級となり、タイル目地の審美性も低い。逆にＮ
ｏ．８はＤが大きい為［Ａ］が長く、［Ｃ］が短くなる
為、嵩高性が低く、粒杢感も低級となり、タイル目地の
審美性も低い。ノズル口径は３〜６ｍｍが好ましい。The results are as shown in Table 1. Experiment No. In No. 1, since the nozzle diameter D was small, the length of the mixed fiber entangled portion [A] was short, the tuft property of the carpet was poor, the graininess was low, and the aesthetics of the tile joint was low. Conversely N
o. In No. 8, [D] is large, [A] is long, and [C] is short, so that the bulkiness is low, the graininess is low, and the aesthetics of the tile joint is low. The nozzle diameter is preferably 3 to 6 mm.
【００６８】実験Ｎｏ．８はＮ／Ｙが小さく、圧空噴射
時間が長くなる為［Ａ］が長くなり、嵩高性が低く、粒
杢感も低級なものとなりタイル目地の審美性も低い。Experiment No. In No. 8, the N / Y is small and the compressed air injection time is long, so that [A] is long, the bulkiness is low, the graininess is low, and the aesthetics of the tile joint is low.
【００６９】実験Ｎｏ．１３はＮ／Ｙが大きく、圧空噴
射時間が短い為［Ａ］が短くなり、タイル性が悪く、そ
の為、粒杢感も低級で、タイル目地の審美性も低い。Ｎ
／Ｙは０．５〜２．０が好ましい。Experiment No. No. 13 has a large N / Y and a short compressed air injection time, so that [A] is short, and the tile properties are poor. Therefore, the graininess is low and the aesthetics of the tile joint is low. N
/ Y is preferably 0.5 to 2.0.
【００７０】[0070]
【表１】 [Table 1]
【００７１】［実施例３］実施例２と同じ嵩高糸の構成
で、間歇的に圧空を噴射する回転式インターレースノズ
ルを用いて、ノズル回転体周長を３０．９ｃｍ、ノズル
口径４．５ｍｍ、圧空圧５ｋｇ／ｃｍ2 、オーバーフィ
ード率５％に固定し、ノズル孔数を２〜１０個の範囲で
変化させ、糸速度４００ｍ／ｍｉｎまたは６００ｍ／ｍ
ｉｎでＮ／Ｙを１．０として抱合加工した。Example 3 Using the same bulky yarn structure as in Example 2, using a rotary interlace nozzle for intermittently ejecting compressed air, a nozzle rotating body circumference of 30.9 cm, a nozzle diameter of 4.5 mm, The air pressure is fixed at 5 kg / cm 2 , the overfeed rate is 5%, the number of nozzle holes is changed in the range of 2 to 10, and the yarn speed is 400 m / min or 600 m / m.
Conjugation processing was performed in which N / Y was set to 1.0.
【００７２】評価は実施例２と同様に行なった。その結
果を表２、表３に示した。The evaluation was performed in the same manner as in Example 2. The results are shown in Tables 2 and 3.
【００７３】カーペットのタフト性と品質の評価による
と、実験Ｎｏ．３、４、６、７が好ましく、実施例３の
糸繊度と条件の下ではノズル孔数は４〜６個が好まし
い。実験Ｎｏ．１と５では交絡が少なくタフト性が悪
く、その為、カーペットの審美性も悪くなっている。実
験Ｎｏ．４と８では、［Ａ］が長く［Ｃ］が短いため、
粒杢感不良、タイル目地不良となっている。According to the evaluation of the tufting property and quality of the carpet, the results of Experiment No. 3, 4, 6, and 7 are preferable, and under the yarn fineness and conditions of Example 3, the number of nozzle holes is preferably 4 to 6. Experiment No. In Nos. 1 and 5, there is little confounding and the tufting property is poor, and therefore the aesthetics of the carpet are also poor. Experiment No. In 4 and 8, [A] is long and [C] is short,
Poor grain feeling and poor tile joints.
【００７４】[0074]
【表２】 [Table 2]
【００７５】[0075]
【表３】 [Table 3]
【００７６】[0076]
【発明の効果】本発明によれば、特に、多色パイルのタ
イルカーペットの外観を従来のインターレース抱合嵩高
糸による霜降調外観から杢調外観へと審美性を高め、か
つ、施工継ぎ目に自然な目地の繋り感を付与して審美性
を高め得る新規な糸構造のインターレース抱合嵩高糸を
創出し、併せてその製造方法を提供することができる。According to the present invention, in particular, the appearance of a tile carpet of a multicolor pile is improved from a marbled appearance by a conventional interlaced conjugated bulky yarn to a heathered appearance, and a natural seam is formed at the construction seam. An interlace-conjugated bulky yarn having a novel yarn structure capable of imparting a joint feeling and enhancing aesthetics can be created, and a manufacturing method thereof can be provided.
【図１】本発明のインターレース抱合嵩高糸を構成する
フィラメント集合体構造の３つの要素構造の模式図。FIG. 1 is a schematic view of three element structures of a filament aggregate structure constituting an interlaced bulky yarn of the present invention.
【図２】本発明のインターレース抱合嵩高糸における要
素構造の好ましい繋りを示した模式図。FIG. 2 is a schematic view showing a preferable connection of element structures in the interlaced bulky yarn of the present invention.
【図３】従来のインターレース抱合嵩高糸における要素
構造の繋りを示した模式図。FIG. 3 is a schematic view showing the connection of element structures in a conventional interlaced bulky yarn.
【図４】本発明の糸条の製造方法を説明する為の工程模
式図。FIG. 4 is a schematic process diagram for explaining the method for producing a yarn of the present invention.
【図５】エアーノズルの作用を説明するためのノズル断
面図。FIG. 5 is a cross-sectional view of a nozzle for explaining the operation of the air nozzle.
［Ａ］、［Ａ′］：混繊・交絡部 ［Ｂ］、［Ｂ′］：混繊・非交絡部 ［Ｃ］：非混繊・非交絡部 ｕ ：本発明の抱合嵩高糸構造の繰返し単位 Ｔ ：従来の抱合嵩高糸構造の繰返し単位 １、２：嵩高糸（供給糸） ３、４：供給ローラ ５ ：ヤーンガイド ６ ：間歇噴射インターレースノズル ７ ：引取ローラ ８ ：巻取ローラ ９ ：回転体 １０ ：圧空噴射孔 １１ ：圧空配管 １２ ：圧空配管枝管 １３ ：圧空受部 １４ ：糸条が通過する溝 ｙ ：糸条 [A], [A ']: Mixed fiber / entangled part [B], [B']: Mixed fiber / non-entangled part [C]: Non-mixed / non-entangled part u: The conjugated bulky yarn structure of the present invention Repetition unit T: Repetition unit of conventional conjugated bulky yarn structure 1, 2: Bulky yarn (supply yarn) 3, 4: Supply roller 5: Yarn guide 6: Intermittent jet interlace nozzle 7: Take-up roller 8: Winding roller 9: Rotating body 10: Compressed air injection hole 11: Compressed air piping 12: Compressed air piping branch pipe 13: Compressed air receiving part 14: Groove through which the yarn passes y: Thread
Claims (6)
の長さ方向に沿って、下記（ａ）、（ｂ）および（ｃ）
のマルチフィラメント集合体構造を含むことを特徴とす
るインターレース抱合嵩高糸。 （ａ）構成フィラメント同士が混繊され、かつ、交絡集
束されている混繊・交絡部［Ａ］、（ｂ）構成フィラメ
ント同士が混繊されているが、交絡集束されていない混
繊・非交絡部［Ｂ］、（ｃ）構成フィラメント同士が混
繊されず、かつ、交絡集束もされていない非混繊・非交
絡部［Ｃ］。1. A multifilament bulky yarn having the following (a), (b) and (c) along its length direction:
An interlaced conjugated bulky yarn comprising the multifilament aggregate structure of the above. (A) Mixed fiber / entangled portion [A] in which constituent filaments are mixed and entangled and bundled; (b) Mixed fiber / non-entangled but not entangled bundle of constituent filaments. Unentangled part [B], (c) Non-mixed / unentangled part [C] in which constituent filaments are not mixed together and are not entangled and focused.
［Ｂ］および非混繊・非交絡部［Ｃ］が、［Ｃ］［Ａ］
［Ｂ］［Ａ］の繋りを繰返し単位として繋った請求項１
記載のインターレース抱合嵩高糸。2. The mixed / entangled portion [A], the mixed / non-entangled portion [B], and the non-mixed / non-entangled portion [C] are [C] [A].
Claim 1 wherein the connection of [B] and [A] is connected as a repeating unit.
The interlaced bulky yarn described.
異色性のマルチフィラメント群から構成されている請求
項１または２記載のインターレース抱合嵩高糸。3. The interlace-conjugated bulky yarn according to claim 1, wherein the multifilament bulky yarn is composed of a plurality of heterochromatic multifilament groups.
ス抱合するに際し、間歇的に圧空を噴射する回転式イン
ターレースノズルを用いて、該間歇的に噴射するノズル
の口径Ｄ（ｍｍ）を直径３〜６ｍｍの範囲とし、かつ、
該回転ノズルの周速度Ｎ（ｍ／分）と糸条の走行速度Ｙ
（ｍ／分）との関係を０．５≦Ｎ／Ｙ≦２．０の範囲に
保持して、インターレース抱合を行うことを特徴とする
インターレース抱合嵩高糸の製造方法。4. When interlacing two or more yarns by interlacing them, using a rotary interlace nozzle that intermittently ejects compressed air, the diameter D (mm) of the intermittently ejecting nozzle is determined. Range from 3 to 6 mm in diameter, and
The peripheral speed N (m / min) of the rotary nozzle and the running speed Y of the yarn
(M / min) in a range of 0.5 ≦ N / Y ≦ 2.0, and performing interlaced conjugation.
ース抱合嵩高糸を基布にループパイル状にタフティング
してなることを特徴とするタフテッドカーペット。5. A tufted carpet obtained by tufting the interlaced bulky yarn according to claim 1, 2 or 3 in a loop pile shape on a base fabric.
を、縦方向および緯方向に長さ４０〜１５０ｃｍの範囲
の大きさに裁断して形成されていることを特徴とするタ
イルカーペット。6. A tile carpet, which is formed by cutting the tufted carpet according to claim 5 into a size having a length in a range of 40 to 150 cm in a longitudinal direction and a weft direction.