JPH10281648A - Molten metal holding furnace - Google Patents
Molten metal holding furnaceInfo
- Publication number
- JPH10281648A JPH10281648A JP9963397A JP9963397A JPH10281648A JP H10281648 A JPH10281648 A JP H10281648A JP 9963397 A JP9963397 A JP 9963397A JP 9963397 A JP9963397 A JP 9963397A JP H10281648 A JPH10281648 A JP H10281648A
- Authority
- JP
- Japan
- Prior art keywords
- molten metal
- filter
- holding
- holding chamber
- inclusion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【技術分野】本発明は，金属を溶湯状態に保持する金属
溶湯保持炉に関する。TECHNICAL FIELD The present invention relates to a molten metal holding furnace for holding a metal in a molten state.
【０００２】[0002]
【従来技術】例えば，ダイカスト等において用いる金属
溶湯を保持するため，金属溶湯保持炉が用いられる。金
属溶湯保持炉は，細部の構造には様々な種類があるが，
少なくとも，投入した金属材料を溶解すると共にその溶
湯を保持する第１保持室と，溶湯を汲み出すための汲み
出し口を設けた第２保持室を有している。そして，溶湯
は，上記第１保持室から第２保持室へ送られ，該第２保
持室の汲み出し口から汲み出されてダイカスト等の鋳造
に用いられる。2. Description of the Related Art For example, in order to hold a molten metal used in die casting or the like, a molten metal holding furnace is used. There are various types of details of the metal melt holding furnace,
At least a first holding chamber for dissolving the charged metal material and holding the molten metal, and a second holding chamber provided with a discharge port for drawing the molten metal are provided. Then, the molten metal is sent from the first holding chamber to the second holding chamber, is drawn out from a pumping port of the second holding chamber, and is used for casting such as die casting.
【０００３】このような従来の金属溶湯保持炉において
は，溶湯品質を向上すべく該溶湯中に含有されている介
在物を除去するための方法が種々提案されている。例え
ば，特開平１−２７１０５９号公報においては，上記第
１保持室に溶湯浄化用ガス気泡発生機能及び溶湯撹拌機
能を有する介在物浮上分離装置を設けた金属溶湯保持炉
が示されている。この介在物浮上分離装置を用いれば，
撹拌された溶湯が溶湯浄化用ガスと十分に接触する。そ
のため，溶湯中の介在物を浄化用ガスと共に溶湯表面に
浮上させることができ，これにより，溶湯の清浄度を向
上させることができる。In such a conventional molten metal holding furnace, various methods have been proposed for removing inclusions contained in the molten metal in order to improve the quality of the molten metal. For example, Japanese Patent Application Laid-Open No. 1-271059 discloses a molten metal holding furnace in which the first holding chamber is provided with an inclusion flotation device having a function of generating gas bubbles for purifying the molten metal and a function of stirring the molten metal. With this inclusion flotation device,
The stirred molten metal comes into sufficient contact with the molten metal purifying gas. Therefore, inclusions in the molten metal can be floated on the surface of the molten metal together with the purifying gas, thereby improving the cleanliness of the molten metal.
【０００４】また，特開平７−７１８８０号公報には，
上記と同様の介在物浮上分離装置を配設すると共に，さ
らにその下流側に介在物を捕獲ためのフィルタを設けた
金属溶湯保持炉が示されている。即ち，図６に示すごと
く，この従来の金属溶湯保持炉９は，材料を投入する槽
９１１と溶湯８を加熱する槽９１２とからなる第１保持
室９１と，溶湯８の汲み出し口９２１を有する第２保持
室９２とよりなる。[0004] Japanese Patent Application Laid-Open No. 7-71880 discloses that
A molten metal holding furnace in which the same inclusion flotation apparatus is provided and further provided with a filter for capturing inclusions downstream thereof is shown. That is, as shown in FIG. 6, the conventional molten metal holding furnace 9 has a first holding chamber 91 including a tank 911 for charging a material and a tank 912 for heating the molten metal 8, and a discharge port 921 for discharging the molten metal 8. The second holding chamber 92 is provided.
【０００５】第１保持室９１には，介在物浮上分離装置
５を設けてある。また，第１保持室９１と第２保持室９
２との間には，加熱用のバーナ９６１とヒータ９６２を
備えていると共に，フィルタ保持部９４５を介してフィ
ルタ９４を配設してある。そして，この金属溶湯保持炉
９においては，介在物浮上分離装置５とフィルタ９４と
いう溶湯浄化手段を二重に備えることにより，一層の溶
湯品質向上を狙っている。[0005] The first holding chamber 91 is provided with an inclusion floating separation device 5. Further, the first holding chamber 91 and the second holding chamber 9
2, a heating burner 961 and a heater 962 are provided, and a filter 94 is disposed via a filter holding unit 945. In the molten metal holding furnace 9, the quality of the molten metal is further improved by providing the molten metal purifying means of the inclusion levitation separation device 5 and the filter 94 in duplicate.
【０００６】なお，図６における符号５９は介在物浮上
分離装置５のモータ，符号５２はシャフト，符号５１は
ロータである。また，符号９２９は溶湯汲み出し口９２
１の開閉蓋，符号９２８は溶湯８の酸化防止のための不
活性ガス吹付け装置である。また，符号９１８は，材料
投入口９１９に材料８８を供給するためのコンベア，符
号９１７は材料投入口９１９の開閉扉である。In FIG. 6, reference numeral 59 denotes a motor of the inclusion levitation device 5, reference numeral 52 denotes a shaft, and reference numeral 51 denotes a rotor. Further, reference numeral 929 denotes a melt discharge port 92.
Reference numeral 928 denotes an opening / closing lid and an inert gas spraying device for preventing oxidation of the molten metal 8. Reference numeral 918 denotes a conveyor for supplying the material 88 to the material input port 919, and reference numeral 917 denotes an opening / closing door of the material input port 919.
【０００７】[0007]
【解決しようとする課題】しかしながら，上記従来の金
属溶湯保持炉においては次の問題がある。即ち，近年の
ダイカスト品等の鋳造品における高品質化要求に伴い，
上記介在物浮上分離装置だけを備えた金属溶湯保持炉で
は，要求品質を満足するための溶湯清浄化効果が十分に
は得られない。また，溶湯中の介在物を捕獲するフィル
タだけを備えた金属溶湯保持炉においても同様である。However, the above-mentioned conventional molten metal holding furnace has the following problems. In other words, with the recent demand for higher quality cast products such as die-cast products,
In a molten metal holding furnace having only the above-mentioned inclusion flotation device, the molten metal cleaning effect for satisfying required quality cannot be sufficiently obtained. Further, the same applies to a molten metal holding furnace having only a filter for capturing inclusions in the molten metal.
【０００８】また，上記介在物浮上分離装置５とフィル
タ９４とを備えた金属溶湯保持炉９（図６）において
は，これらを併設したことによる次の不具合が発生す
る。即ち，上記介在物浮上分離装置は，その撹拌力を強
くして十分に溶湯を撹拌するほど溶湯清浄化効果を向上
させることができるという特徴を有している。さらに，
撹拌力を上げて浄化ガスを細かくすることにより，浄化
効果を上げることができるという特徴も有している。一
方，上記フィルタは，これを通過する溶湯の流速が遅い
ほど介在物の捕獲能力が高くなるという特徴を有してい
る。Further, in the molten metal holding furnace 9 (FIG. 6) provided with the above-mentioned inclusion flotation device 5 and the filter 94, the following problems occur due to the simultaneous installation thereof. That is, the inclusion flotation device has a feature that the more the stirring power is increased and the more the molten metal is sufficiently stirred, the more the molten metal cleaning effect can be improved. further,
There is also a feature that the purifying effect can be improved by increasing the stirring power to make the purifying gas finer. On the other hand, the filter has a feature that the lower the flow rate of the molten metal passing therethrough, the higher the ability to capture inclusions.
【０００９】しかしながら，介在物浮上分離装置の浄化
能力を向上すべく撹拌力を強くした場合には，溶湯のフ
ィルタ通過速度を速くし，フィルタの浄化能力の低下及
びフィルタの短寿命化を来してしまう。また，この不具
合を解消すべく介在物浮上分離装置の撹拌力を低くした
場合には，フィルタの浄化能力は高まるが，介在物浮上
分離装置による浄化効果が低くなってしまう。即ち，従
来の介在物浮上分離装置とフィルタの両者を配設した金
属溶湯保持炉においては，上記両者の浄化能力を最大限
に発揮させることができなかった。However, if the stirring power is increased to improve the purification ability of the inclusion flotation device, the speed at which the molten metal passes through the filter is increased, and the purification ability of the filter is reduced and the life of the filter is shortened. Would. When the stirring force of the inclusion flotation device is reduced to solve this problem, the purification ability of the filter is increased, but the purification effect of the inclusion flotation device is reduced. That is, in the conventional molten metal holding furnace in which both the inclusion flotation device and the filter are disposed, the purifying ability of the both cannot be maximized.
【００１０】本発明は，かかる従来の問題に鑑みてなさ
れたもので，介在物浮上分離装置の浄化能力を低下させ
ることなく，フィルタの浄化能力を十分に発揮させるこ
とができる，金属溶湯保持炉を提供しようとするもので
ある。SUMMARY OF THE INVENTION The present invention has been made in view of such a conventional problem, and has a metal molten metal holding furnace capable of sufficiently exhibiting a purifying ability of a filter without reducing a purifying ability of an inclusion flotation device. It is intended to provide.
【００１１】[0011]
【課題の解決手段】請求項１の発明は，金属を溶解する
と共に溶湯を保持する第１保持室と，溶湯を汲み出すた
めの汲み出し口を設けた第２保持室とを有する金属溶湯
保持炉において，上記第１保持室には，溶湯を撹拌する
と共に浄化用ガスをバブリングさせる介在物浮上分離装
置を配設してあり，また，上記第１保持室と上記第２保
持室との間には介在物を捕獲するためのフィルタを設け
てあり，かつ，上記介在物浮上分離装置と上記フィルタ
との間の溶湯通路には，上記介在物浮上分離装置から上
記フィルタへの直接的な溶湯の流れを抑制するための隔
壁を設けてあることを特徴とする金属溶湯保持炉にあ
る。According to a first aspect of the present invention, there is provided a molten metal holding furnace having a first holding chamber for melting a metal and holding a molten metal, and a second holding chamber provided with a pumping port for drawing the molten metal. In the first holding chamber, an inclusion flotation / separation device for stirring the molten metal and bubbling the purifying gas is disposed in the first holding chamber, and between the first holding chamber and the second holding chamber. Is provided with a filter for trapping inclusions, and a molten metal passage between the inclusion flotation device and the filter is provided with the molten metal directly from the inclusion flotation device to the filter. A metal melt holding furnace is provided with a partition wall for suppressing a flow.
【００１２】本発明において最も注目すべきことは，上
記介在物浮上分離装置と上記フィルタとの間の溶湯通路
には，上記隔壁を設けたことである。この隔壁は，介在
物浮上分離装置からフィルタへの直接的な溶湯の流れを
抑制するため，上記溶湯通路における溶湯の流れを遮る
ように設ける。What is most notable in the present invention is that the partition wall is provided in the molten metal passage between the inclusion flotation device and the filter. The partition is provided so as to block the flow of the molten metal in the molten metal passage in order to suppress the flow of the molten metal directly from the inclusion levitation separation device to the filter.
【００１３】次に，本発明の作用効果につき説明する。
本発明の金属溶湯保持炉は，上記介在物浮上分離装置と
フィルタとの間の溶湯通路に上記隔壁を設けてなる。そ
のため，上記介在物浮上分離装置の溶湯浄化効果を最大
限発揮すべく高回転で溶湯を撹拌しても，フィルタの溶
湯浄化能力を高く維持することができる。Next, the function and effect of the present invention will be described.
The molten metal holding furnace of the present invention is provided with the partition wall in the molten metal passage between the inclusion floating device and the filter. For this reason, even if the molten metal is stirred at a high rotation speed so as to maximize the molten metal purification effect of the inclusion flotation device, the molten metal purification ability of the filter can be maintained high.
【００１４】即ち，上記介在物浮上分離装置を高回転で
回転させ，溶湯を強く撹拌させた場合には，広い範囲に
わたって溶湯が渦巻き状に速い速度で流動する。そのた
め，従来ならば，溶湯は，速い速度で直接的にフィルタ
に到達し，速い速度でフィルタ通過する。That is, when the above-mentioned inclusion flotation device is rotated at a high rotation speed and the molten metal is vigorously stirred, the molten metal flows spirally at a high speed over a wide range. Therefore, conventionally, the molten metal directly reaches the filter at a high speed and passes through the filter at a high speed.
【００１５】これに対し，本発明においては，上記隔壁
を上記溶湯通路に設けてある。そのため，上記の速い流
速の溶湯は，まず隔壁に衝突する。そして，隔壁に衝突
した溶湯は，隔壁の周囲から裏側へ回り込んで，ゆっく
りとした速度でフィルタに到達する。そのため，フィル
タを通過する溶湯は，従来よりもゆっくりとした速度で
通過する。On the other hand, in the present invention, the partition is provided in the molten metal passage. Therefore, the molten metal having the high flow velocity first collides with the partition wall. Then, the molten metal that has collided with the partition wall wraps around the partition wall to the back side and reaches the filter at a slow speed. Therefore, the molten metal passing through the filter passes at a slower speed than before.
【００１６】つまり，本発明においては，介在物浮上分
離装置の撹拌力を十分に強くした場合においても，その
影響を直接的に受けることなく，フィルタを通過する溶
湯の流速を低い速度に維持することができる。そのた
め，フィルタの浄化能力は高い状態に維持される。That is, in the present invention, even when the stirring force of the inclusion flotation device is sufficiently increased, the flow rate of the molten metal passing through the filter is maintained at a low speed without being directly affected by the influence. be able to. Therefore, the purifying ability of the filter is maintained at a high level.
【００１７】従って，本発明によれば，介在物浮上分離
装置の浄化能力を低下させることなく，フィルタの浄化
能力を十分に発揮させることができる，金属溶湯保持炉
を提供することができる。なお，溶湯のフィルタ通過速
度を低く維持することはフィルタの長寿命化につなが
る。そのため，本発明によれば，フィルタ交換サイクル
の長期化等による操業効率の向上をも図ることができ
る。Therefore, according to the present invention, it is possible to provide a molten metal holding furnace capable of sufficiently exhibiting the purification ability of the filter without reducing the purification ability of the inclusion flotation device. It should be noted that keeping the molten metal passing speed through the filter low leads to prolonging the life of the filter. Therefore, according to the present invention, it is also possible to improve the operation efficiency by extending the filter replacement cycle.
【００１８】次に，請求項２の発明のように，上記隔壁
の面積は，上記介在物浮上分離装置と上記フィルタとの
間における溶湯通路の断面積の５０〜９０％であること
が好ましい。５０％未満の場合には，上記の隔壁設置の
効果が十分に発揮されないという問題がある。一方，９
０％を超える場合には，溶湯の流動性が妨げられ，第１
保持室から第２保持室へのスムーズな溶湯供給が困難と
なるという問題がある。Next, as in the second aspect of the present invention, the area of the partition wall is preferably 50 to 90% of the cross-sectional area of the molten metal passage between the inclusion flotation device and the filter. When it is less than 50%, there is a problem that the effect of the above-mentioned partition wall installation is not sufficiently exhibited. On the other hand, 9
If it exceeds 0%, the fluidity of the molten metal is hindered,
There is a problem that it is difficult to smoothly supply the molten metal from the holding chamber to the second holding chamber.
【００１９】また，請求項３の発明のように，上記隔壁
は，上記フィルタから延設した取付部材によって固定さ
れていることが好ましい。この場合には，上記隔壁を炉
壁から独立した状態で設けることができる。それ故，例
えば，隔壁の周囲における溶湯の通路を均等に確保する
こともできる。なお，上記取付部材としては，例えば黒
鉛ボルト等の耐熱性の高い部材を用いることができる。Preferably, the partition is fixed by a mounting member extending from the filter. In this case, the partition can be provided independently of the furnace wall. Therefore, for example, the passage of the molten metal around the partition can also be secured uniformly. As the mounting member, a member having high heat resistance such as a graphite bolt can be used.
【００２０】また，請求項４の発明のように，上記隔壁
は，炉壁から延設してある構造にすることもできる。こ
の場合には，フィルタと関わりなく隔壁を設置すること
ができ，構造が簡単になると共にフィルタ交換等の作業
を容易にすることができる。Further, as in the invention of the fourth aspect, the partition may have a structure extending from a furnace wall. In this case, the partition can be installed irrespective of the filter, which simplifies the structure and facilitates operations such as filter replacement.
【００２１】また，上記隔壁としては，十分に耐熱性に
優れた材料を用いて作製する必要がある。例えば，請求
項５の発明のように，上記隔壁は，セラミック又は黒鉛
により作製することができる。Further, it is necessary to manufacture the partition walls using a material having sufficiently high heat resistance. For example, as in the invention of claim 5, the partition can be made of ceramic or graphite.
【００２２】[0022]
実施形態例１ 本発明の実施形態例にかかる金属溶湯保持炉につき，図
１〜図４を用いて説明する。本例の金属溶湯保持炉１
は，ダイカスト用のアルミニウム合金の溶湯を保持する
ための炉である。この金属溶湯保持炉１は，図１に示す
ごとく，金属を溶解すると共に溶湯を保持する第１保持
室１１と，溶湯を汲み出すための汲み出し口１２１を設
けた第２保持室１２とを有する。First Embodiment A molten metal holding furnace according to an embodiment of the present invention will be described with reference to FIGS. Molten metal holding furnace 1 of this example
Is a furnace for holding molten aluminum alloy for die casting. As shown in FIG. 1, the molten metal holding furnace 1 has a first holding chamber 11 for melting a metal and holding the molten metal, and a second holding chamber 12 provided with a pumping port 121 for drawing the molten metal. .
【００２３】第１保持室１１には，溶湯８を撹拌すると
共に浄化用ガスをバブリングさせる介在物浮上分離装置
５を配設してある。また，第１保持室１１と第２保持室
１２との間には介在物を捕獲するためのフィルタ４を設
けてある。かつ，介在物浮上分離装置５とフィルタ４と
の間の溶湯通路１３には，介在物浮上分離装置５からフ
ィルタ４への直接的な溶湯の流れを抑制するための隔壁
２を設けてある。The first holding chamber 11 is provided with an inclusion flotation device 5 for stirring the molten metal 8 and bubbling a purifying gas. Further, a filter 4 for capturing inclusions is provided between the first holding chamber 11 and the second holding chamber 12. In addition, a partition wall 2 for suppressing the flow of the molten metal from the inclusion levitation device 5 to the filter 4 is provided in the molten metal passage 13 between the inclusion levitation device 5 and the filter 4.
【００２４】以下，これを詳説する。図１に示すごと
く，上記第１保持室１１は，炉体１０に設けた材料投入
口１９を開口させた材料投入槽１１１を有していると共
に，加熱バーナ６及び介在物浮上分離装置５を備えてい
る。加熱バーナ６は，炉体１０の上方から第１保持室１
１に向けて火炎６６を発するように設けられ，その火炎
発生部分をセラミックチューブ６１により囲んで溶湯８
内に浸漬されるよう配置してある。Hereinafter, this will be described in detail. As shown in FIG. 1, the first holding chamber 11 has a material charging tank 111 in which a material charging port 19 provided in the furnace body 10 is opened, and includes a heating burner 6 and an inclusion floating separation device 5. Have. The heating burner 6 is provided from above the furnace body 10 to the first holding chamber 1.
1 is provided so as to emit a flame 66 toward the fuel cell 1.
It is arranged to be immersed inside.
【００２５】介在物浮上分離装置５は，炉体１０の外部
に設けた駆動用のモータ５９から下方に向けて延ばした
シャフト５２と，その先端に設けたロータ５１とよりな
る。ロータ５１は，図２に示すごとく，その先端が略円
錐形状をなしており，そのテーパ状の側面に溝５１１を
多数設けてある。また，溝５１１には，不活性ガス吹き
出し孔（図示略）を設けてある。そして，介在物浮上分
離装置５は，図２に示すごとく，ロータ５１を回転させ
ながら，シャフト５２内を通って供給される不活性ガス
７を炉内に吹き出すよう構成されている。なお，本例に
おける不活性ガス７は窒素ガスである。The inclusion flotation device 5 comprises a shaft 52 extending downward from a driving motor 59 provided outside the furnace body 10 and a rotor 51 provided at the tip thereof. As shown in FIG. 2, the tip of the rotor 51 has a substantially conical shape, and a large number of grooves 511 are provided on its tapered side surface. In addition, an inert gas blowing hole (not shown) is provided in the groove 511. As shown in FIG. 2, the inclusion flotation device 5 is configured to blow the inert gas 7 supplied through the shaft 52 into the furnace while rotating the rotor 51. Note that the inert gas 7 in this example is a nitrogen gas.
【００２６】フィルタ４は，図１，図３に示すごとく，
第１保持室１１と第２保持室１２との間の境界部に設け
てある。フィルタ４は，セラミック製のフィルタであっ
て，これを通過する溶湯中の介在物を捕獲するものであ
る。また，フィルタ４に通ずる溶湯通路１３には，図
１，図３，図４に示すごとく，セラミック製の隔壁２を
配設してある。The filter 4 is, as shown in FIGS.
It is provided at a boundary between the first holding chamber 11 and the second holding chamber 12. The filter 4 is a ceramic filter that captures inclusions in the molten metal passing through the filter. Further, as shown in FIGS. 1, 3, and 4, a partition wall 2 made of ceramic is provided in the molten metal passage 13 leading to the filter 4.
【００２７】隔壁２は，図３，図４に示すごとく，フィ
ルタ４から延設した取付部材２２によって固定してあ
る。取付部材２２としては，黒鉛ボルトを用いてある。
また，隔壁２は，図３，図４に示すごとく，炉体１０か
ら独立した状態で配設してあり，隔壁２と炉体１０の内
壁との間に溶湯が通過する通路１３５を確保してある。As shown in FIGS. 3 and 4, the partition 2 is fixed by a mounting member 22 extending from the filter 4. As the attachment member 22, a graphite bolt is used.
As shown in FIGS. 3 and 4, the partition wall 2 is disposed independently of the furnace body 10, and a passage 135 through which the molten metal passes between the partition wall 2 and the inner wall of the furnace body 10 is secured. It is.
【００２８】また，本例における隔壁２は，図４に示す
ごとく，炉体１０に囲まれた溶湯通路１３の断面積の７
０％を占める面積に設けてある。なお，金属溶湯保持炉
１におけるその他の周辺構造は，従来例（図６）と同様
である。Further, as shown in FIG. 4, the partition wall 2 in this embodiment has a sectional area of 7 mm of the molten metal passage 13 surrounded by the furnace body 10.
It is provided in an area occupying 0%. The other peripheral structures in the molten metal holding furnace 1 are the same as in the conventional example (FIG. 6).
【００２９】次に，本例における作用効果につき説明す
る。本例の金属溶湯保持炉１においては，溶湯８を清浄
化するに当たっては，まず第１保持室１１内において介
在物浮上分離装置５により介在物を浮上させる。具体的
には，介在物浮上分離装置５を駆動させることにより，
ロータ５１が不活性ガス７を吹き出しながら回転する。
これにより，ロータ５１の溝５１１の作用によって溶湯
８が撹拌されて不活性ガス７と十分に接触する。これに
より，図１に示すごとく，溶湯中の介在物８９は，不活
性ガス７と共に溶湯表面に浮上する。Next, the operation and effect of this embodiment will be described. In the molten metal holding furnace 1 of the present embodiment, to clean the molten metal 8, first, the inclusions are floated by the inclusion floating separation device 5 in the first holding chamber 11. Specifically, by driving the inclusion levitation separation device 5,
The rotor 51 rotates while blowing out the inert gas 7.
As a result, the molten metal 8 is stirred by the action of the groove 511 of the rotor 51 and sufficiently contacts the inert gas 7. Thereby, as shown in FIG. 1, the inclusions 89 in the molten metal float on the surface of the molten metal together with the inert gas 7.
【００３０】このとき，上記撹拌による溶湯８の強い流
れは，第２保持室１２側へも向かう。しかしながら，本
例においては，第１保持室１１から第２保持室１２への
溶湯通路１３に上記隔壁２を設けてある。そのため，溶
湯８の強い流れは，溶湯８のの隔壁２への衝突により十
分に弱められる。At this time, the strong flow of the molten metal 8 due to the stirring also goes to the second holding chamber 12 side. However, in the present embodiment, the partition wall 2 is provided in the molten metal passage 13 from the first holding chamber 11 to the second holding chamber 12. Therefore, the strong flow of the molten metal 8 is sufficiently weakened by the collision of the molten metal 8 with the partition wall 2.
【００３１】そして，第１保持室１１から第２保持室１
２への溶湯８の移動は，まず，溶湯８が隔壁２と炉体１
０の壁面との間の間隙１３５から隔壁２の裏側に回り込
む。次いで，溶湯８はゆっくりとした速度でフィルタ４
を通過する。フィルタ４をゆっくりと通過する溶湯８
は，フィルタ４の濾過作用によりさらに十分に介在物を
除去され，清浄度を増して第２保持室１２に送られる。Then, from the first holding chamber 11 to the second holding chamber 1
First, the molten metal 8 is moved to the partition 2 and the furnace body 1.
It goes around to the back side of the partition wall 2 from the gap 135 between it and the 0 wall. Next, the molten metal 8 is filtered at a slow speed by the filter 4.
Pass through. Melt 8 slowly passing through filter 4
Is further sufficiently removed by the filtering action of the filter 4 and is sent to the second holding chamber 12 with increased cleanliness.
【００３２】このように，本例の金属溶湯保持炉１にお
いては，上記隔壁２の存在によって，介在物浮上分離装
置５とフィルタ４のそれぞれの溶湯清浄化能力を，互い
に悪影響を及ぼすことなく，最大限に発揮させることが
できる。それ故，従来のように，介在物浮上分離装置５
の効果を高めればフィルタ４の効果が低下するというよ
うなこともない。As described above, in the molten metal holding furnace 1 of the present embodiment, the presence of the partition wall 2 does not adversely affect each of the inclusion flotation devices 5 and the filter 4 in the molten metal cleaning ability without adversely affecting each other. You can make the most of it. Therefore, the inclusion flotation device 5
If the effect of the filter 4 is enhanced, the effect of the filter 4 does not decrease.
【００３３】したがって，本例の金属溶湯保持炉１によ
れば，従来よりも介在物の少ない優れた品質の溶湯８を
得ることができる。また，フィルタ４は，溶湯通過速度
が遅いほど寿命が長くなるという特性を有している。そ
のため，本例の金属溶湯保持炉１によれば，フィルタ４
の交換サイクルを長くすることができ，金属溶湯保持炉
１の連続操業時間の延長及びフィルタ交換回数の減少に
よる操業効率の向上をも図ることができる。Therefore, according to the molten metal holding furnace 1 of the present embodiment, it is possible to obtain the molten metal 8 of excellent quality with fewer inclusions than in the prior art. Further, the filter 4 has a characteristic that the longer the molten metal passage speed, the longer the life. Therefore, according to the molten metal holding furnace 1 of the present embodiment, the filter 4
Can be lengthened, the continuous operation time of the molten metal holding furnace 1 can be extended, and the operation efficiency can be improved by reducing the number of filter replacements.
【００３４】実施形態例２ 本例においては，実施形態例１の金属溶湯保持炉１にお
ける，溶湯の清浄化効果を実験により評価した。実験
は，金属溶湯保持炉１によって得られた溶湯８を用いて
実際にダイカスト品を作製し，そのダイカスト品に含有
されている介在物量を評価することにより行った。ま
た，比較のために，金属溶湯保持炉１の隔壁２を取り除
いた状態において得られた溶湯を用いてダイカスト品を
作製し，同様に評価した。Embodiment 2 In this embodiment, the cleaning effect of the molten metal in the molten metal holding furnace 1 of Embodiment 1 was evaluated by experiments. The experiment was performed by actually producing a die-cast product using the molten metal 8 obtained by the molten metal holding furnace 1 and evaluating the amount of inclusions contained in the die-cast product. For comparison, a die-cast product was prepared using the molten metal obtained in a state where the partition walls 2 of the molten metal holding furnace 1 were removed, and evaluated in the same manner.
【００３５】ダイカスト品中の介在物量の評価は，介在
物がダイカスト品の切削加工において切削工具の刃具欠
け不良につながることに着目し，その刃具欠け不良率に
より評価した。評価の結果，隔壁２を取り外した状態に
おいては，従来と同様に刃欠け不良が２．５％発生し
た。これに対し，隔壁２を配設した状態においては，刃
欠け不良が０．０２％に減少した。この結果から，隔壁
２の設置により溶湯品質が格段に向上することが分か
る。In the evaluation of the amount of inclusions in the die-cast product, attention was paid to the fact that the inclusions would lead to defective cutting of the cutting tool in the cutting of the die-cast product, and the evaluation was made based on the defective ratio of the defective tool. As a result of the evaluation, in a state where the partition wall 2 was removed, 2.5% of chipping defects occurred as in the conventional case. On the other hand, in the state where the partition wall 2 was provided, the blade chipping defect was reduced to 0.02%. From this result, it is understood that the quality of the molten metal is remarkably improved by installing the partition wall 2.
【００３６】実施形態例３ 本例は，図５に示すごとく，隔壁２０２を炉体１０の底
部から延設した例である。即ち，本例の隔壁２０２は，
フィルタ４と関わることなく，炉体１０に直接設けてあ
る。なお，隔壁２０２の材質は，炉体１０と同じ耐火用
レンガである。その他は，実施形態例１と同様である。
この場合には，フィルタ４の交換の際においても隔壁２
０２をそのままの状態に保持させることができ，フィル
タ４の交換作業を容易に行うことができる。その他，実
施形態例１と同様の効果が得られる，Embodiment 3 In this embodiment, as shown in FIG. 5, a partition wall 202 is extended from the bottom of the furnace body 10. That is, the partition 202 of the present example
It is provided directly on the furnace body 10 without involving the filter 4. The material of the partition wall 202 is the same refractory brick as the furnace body 10. Other configurations are the same as those of the first embodiment.
In this case, even when the filter 4 is replaced,
02 can be maintained as it is, and the replacement work of the filter 4 can be easily performed. In addition, the same effects as those of the first embodiment can be obtained.
【図１】実施形態例１の金属溶湯保持炉の構成を示す説
明図。FIG. 1 is an explanatory view showing a configuration of a molten metal holding furnace of a first embodiment.
【図２】実施形態例１における，介在物浮上分離装置の
要部を示す説明図。FIG. 2 is an explanatory diagram showing a main part of the inclusion levitation separation device in the first embodiment.
【図３】実施形態例１における，隔壁の配設状態を示す
説明図。FIG. 3 is an explanatory diagram showing an arrangement state of partition walls in the first embodiment.
【図４】図３のＡ−Ａ線矢視断面図。FIG. 4 is a sectional view taken along line AA of FIG. 3;
【図５】実施形態例３における，隔壁の配設状態を示す
説明図。FIG. 5 is an explanatory view showing an arrangement state of partition walls in a third embodiment.
【図６】従来例の金属溶湯保持炉の構成を示す説明図。FIG. 6 is an explanatory view showing a configuration of a conventional molten metal holding furnace.
【符号の説明】 １．．．金属溶湯保持炉， １０．．．炉体， １１．．．第１保持室， １２．．．第２保持室， １２１．．．汲み出し口， １３．．．溶湯通路， ２．．．隔壁， ２２．．．取付部材， ４．．．フィルタ， ５．．．介在物浮上分離装置， ５１．．．ロータ， ６．．．バーナ， ７．．．不活性ガス， ８．．．溶湯，[Explanation of Codes] . . 9. Molten metal holding furnace, . . Furnace body, 11. . . First holding chamber, 12. . . Second holding chamber, 121. . . 12. Pumping outlet, . . Molten metal passage, 2. . . Partition wall, 22. . . 3. mounting member; . . Filter, 5. . . Inclusion flotation device, 51. . . Rotor, 6. . . Burner, 7. . . 7. inert gas; . . Molten metal,
Claims (5)
１保持室と，溶湯を汲み出すための汲み出し口を設けた
第２保持室とを有する金属溶湯保持炉において，上記第
１保持室には，溶湯を撹拌すると共に浄化用ガスをバブ
リングさせる介在物浮上分離装置を配設してあり，ま
た，上記第１保持室と上記第２保持室との間には介在物
を捕獲するためのフィルタを設けてあり，かつ，上記介
在物浮上分離装置と上記フィルタとの間の溶湯通路に
は，上記介在物浮上分離装置から上記フィルタへの直接
的な溶湯の流れを抑制するための隔壁を設けてあること
を特徴とする金属溶湯保持炉。1. A molten metal holding furnace having a first holding chamber for melting a metal and holding a molten metal and a second holding chamber provided with a pumping port for drawing the molten metal, wherein the first holding chamber has Is provided with an inclusion flotation / separation device for stirring the molten metal and bubbling the purifying gas, and between the first holding chamber and the second holding chamber for trapping inclusions. A filter is provided, and a partition for suppressing the flow of molten metal from the inclusion levitation device to the filter is provided in a molten metal passage between the inclusion levitation device and the filter. A furnace for holding molten metal, which is provided.
上記介在物浮上分離装置と上記フィルタとの間における
溶湯通路の断面積の５０〜９０％であることを特徴とす
る金属溶湯保持炉。2. The method according to claim 1, wherein the area of the partition wall is
A molten metal holding furnace having a cross-sectional area of 50 to 90% of a cross-sectional area of a molten metal passage between the inclusion flotation device and the filter.
上記フィルタから延設した取付部材によって固定されて
いることを特徴とする金属溶湯保持炉。3. The method according to claim 1, wherein the partition wall comprises:
A molten metal holding furnace fixed by a mounting member extending from the filter.
上記隔壁は，炉壁から延設してあることを特徴とする金
属溶湯保持炉。4. The method according to claim 1, wherein:
The above-mentioned partition wall is extended from a furnace wall, and the molten metal holding furnace characterized by the above-mentioned.
上記隔壁は，セラミック又は黒鉛により作製してあるこ
とを特徴とする金属溶湯保持炉。5. The method according to claim 1, wherein:
The above-mentioned partition wall is made of ceramic or graphite, and is a molten metal holding furnace.