JPH10259592A - Roll antifouling agent and coating liquid composition containing the same - Google Patents
Roll antifouling agent and coating liquid composition containing the sameInfo
- Publication number
- JPH10259592A JPH10259592A JP6813797A JP6813797A JPH10259592A JP H10259592 A JPH10259592 A JP H10259592A JP 6813797 A JP6813797 A JP 6813797A JP 6813797 A JP6813797 A JP 6813797A JP H10259592 A JPH10259592 A JP H10259592A
- Authority
- JP
- Japan
- Prior art keywords
- weight
- parts
- pts
- paper
- roll
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、すぐれた性質を有
するロール汚れ防止剤、それを含有する塗工液組成物、
および、該塗工液組成物が塗布された塗工紙又は塗工板
紙（以下、塗工（板）紙と略記する）に関するものであ
る。本発明は、塗工層が形成された塗工（板）紙の仕上
げる工程で使用されるスーパーカレンダーやグロスカレ
ンダーなどのロール汚れ防止に優れた効果を発揮するば
かりか、塗工工程時に、塗工層が形成された塗工（板）
紙が接触する第２バツキングロール汚れの防止に対して
も極めて有効である。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a roll antifouling agent having excellent properties, a coating liquid composition containing the same,
The present invention also relates to a coated paper or a coated paperboard (hereinafter, abbreviated as coated (board) paper) to which the coating liquid composition has been applied. INDUSTRIAL APPLICABILITY The present invention not only exerts an excellent effect of preventing roll stains such as a super calender and a gloss calender used in a step of finishing a coated (board) paper having a coated layer formed thereon, but also exerts a coating effect during the coating step. Coating (plate) with a working layer
It is also very effective in preventing the second backing roll from coming into contact with the paper.
【０００２】[0002]
【従来の技術】近年、多色印刷された雑誌類、パンフレ
ット、広告類および包装材類の急速な需要拡大に伴っ
て、塗工紙あるいは塗工板紙の生産が著しく増大してい
る。そのため、塗工速度および仕上げ速度のアップが日
々計られている。また塗工（板）紙の薄物化傾向に伴
い、腰を維持し、白紙光沢および平滑度を出すために、
スーパーカレンダーロールおよびグロスカレンダーロー
ル条件が低圧化と高温化に移行している。これらの傾向
に伴い、各仕上げ用ロールでの汚れが、従来に増して発
生し易くなっており、解決策が切望されている。2. Description of the Related Art In recent years, the production of coated paper or coated paperboard has increased significantly with the rapid increase in demand for magazines, brochures, advertisements, and packaging materials printed in multicolor. Therefore, an increase in the coating speed and the finishing speed is measured every day. In addition, with the tendency of coated (board) paper to become thinner, to maintain stiffness and to achieve white paper gloss and smoothness,
The conditions of the super calender roll and gloss calender roll are shifting to lower pressure and higher temperature. With these tendencies, stains on each finishing roll are more likely to occur than ever before, and there is an eager need for a solution.
【０００３】各仕上げ用ロール汚れの最大の原因は、塗
工液組成物に使用されている合成共重合体ラテックスで
あり、それらの改良手段として、例えば、ステアリン酸
カルシウムやポリエチレンエマルジョン等の各種潤滑剤
の使用量を増やすことや、合成共重合体ラテックスのべ
た付きの改良などが精力的に行われている。また塗工工
程で発生する第２バッキングロール汚れ対策としては、
例えば、塗工液組成物に使用されている天然バインダー
と合成共重合体ラテックス比率の最適化や、合成共重合
体ラテックスのべた付きの改良等が積極的に行われてい
る。[0003] The biggest cause of each finishing roll stain is the synthetic copolymer latex used in the coating liquid composition. As a means for improving these, various lubricants such as calcium stearate and polyethylene emulsion are used. Vigorous efforts have been made to increase the amount of used and to improve the stickiness of the synthetic copolymer latex. Also, as a countermeasure against the second backing roll stain generated in the coating process,
For example, optimization of the ratio of the natural binder and the synthetic copolymer latex used in the coating liquid composition, improvement of the stickiness of the synthetic copolymer latex, and the like have been actively performed.
【０００４】また、仕上げ用ロールの汚れ防止の目的で
はないが、塗工層形成前である湿潤状態の塗工面を有す
る塗工紙の塗工工程や乾燥工程で使用されるコーターや
ドライヤーに、クリアコーティング剤であるポリビニル
アルコール（ＰＶＡ）が付着するのを防ぐ目的で、剥離
剤として高級脂肪族アミンのポリエチレングリコール誘
導体あるいはソルビタンの高級脂肪酸エステルを使用す
ることが知られている（特開昭６３−１１２７９５号公
報）。[0004] Further, although not for the purpose of preventing the finishing roll from being stained, a coater or a dryer used in a coating process or a drying process of a coated paper having a wet coated surface before a coating layer is formed, It is known that a polyethylene glycol derivative of a higher aliphatic amine or a higher fatty acid ester of sorbitan is used as a release agent for the purpose of preventing polyvinyl alcohol (PVA) as a clear coating agent from adhering (Japanese Patent Application Laid-Open No. Sho 63). -112975).
【０００５】しかしながら、各仕上げ用ロール汚れに対
し、各種潤滑剤の増量は、確かに効果はあるものの、各
種潤滑剤の大半は、接着強度を付与していないため、表
面強度、すなわちドライ強度や耐水性、すなわちウエッ
ト強度の低下をもたらす。また合成共重合体ラテックス
の改良方法であるべた付き防止の手段の一つとしてガラ
ス転移温度を上げることが行われている。確かに、ロー
ル汚れは改善されるものの、大幅なドライ強度の低下を
もたらす。[0005] However, although increasing the amount of various lubricants for each finishing roll stain is certainly effective, most of the various lubricants do not impart adhesive strength, so that the surface strength, that is, the dry strength or the dry strength is not improved. Water resistance, that is, a decrease in wet strength is brought about. Also, raising the glass transition temperature has been performed as one of the means for preventing stickiness, which is a method for improving the synthetic copolymer latex. Indeed, while roll fouling is improved, it results in a significant decrease in dry strength.
【０００６】また、塗工工程で発生する第２バッキング
ロール汚れに対する対策の一つである天然バインダーと
合成共重合体ラテックス比率の最適化において、天然バ
インダー比率を上げると確かに改良される方向に行く
が、塗工液粘度が上がること、さらに白紙光沢や平滑性
等の低下を招くなど、欠点が多い。さらに合成共重合体
ラテックスの改良も、仕上げ用ロール汚れと同じ対策を
とるが、やはり大幅なドライ強度が低下するという、同
様な欠点を持っている。Further, in the optimization of the ratio of the natural binder and the synthetic copolymer latex, which is one of the measures against the contamination of the second backing roll generated in the coating process, the ratio is naturally improved by increasing the ratio of the natural binder. However, there are many drawbacks, such as an increase in the viscosity of the coating solution and a decrease in glossiness and smoothness of blank paper. Further, the improvement of the synthetic copolymer latex takes the same measures as that of the finishing roll stain, but has the same disadvantage that the dry strength is also greatly reduced.
【０００７】さらに、上記公報に記載の剥離剤は、塗工
面形成時に際し、水溶性であるＰＶＡが、コーターやド
ライヤーへ付着するのを改善するためのものであって、
本発明が対象とする、塗工層形成後の塗工紙による各仕
上げロールや第２バッキングロールの汚れを防止するも
のではない。Further, the release agent described in the above publication is for improving the adhesion of water-soluble PVA to a coater or a dryer when forming a coated surface,
The present invention does not prevent the finishing rolls and the second backing roll from being stained by the coated paper after the formation of the coating layer.
【０００８】[0008]
【発明が解決しようとする課題】本発明は、仕上げロー
ルや第２バッキングロールの汚れ防止に有用なロール汚
れ防止剤、それを含有する塗工液組成物、および、該塗
工液組成物が塗布された塗工紙又は塗工板紙を提供する
ことを目的とする。DISCLOSURE OF THE INVENTION The present invention provides a roll stain inhibitor useful for preventing stains on a finishing roll and a second backing roll, a coating composition containing the same, and a coating composition containing the same. It is an object to provide a coated paper or coated paperboard which has been coated.
【０００９】[0009]
【課題を解決するための手段】本発明者は、塗工層形成
後の塗工（板）紙の仕上げ工程で使用されるスーパーカ
レンダーロールやグロスカレンダーロール汚れ防止、さ
らに第２バッキングロール汚れの防止につき検討を重ね
た結果、汚れの最大の原因が合成共重合体ラテックスに
あること、さらに特定の水分散体型のロール汚れ防止剤
が有効であること、また、これを含有してなる塗工液組
成物を塗布した塗工（板）紙は、白紙光沢および印刷光
沢が優れていることを見出し、本発明をなすに至った。Means for Solving the Problems The present inventor has proposed a method for preventing stains on a super calender roll and a gloss calender roll used in a finishing process of a coated (board) paper after forming a coating layer, and further, a stain on a second backing roll. As a result of repeated investigations on prevention, it was found that the biggest cause of soiling was the synthetic copolymer latex, and that a specific water dispersion type roll antifouling agent was effective. The coated (board) paper coated with the liquid composition was found to have excellent white paper gloss and printed gloss, and the present invention was achieved.
【００１０】即ち、本発明は下記の通りである。 〔１〕（ａ）ソルビタン脂肪酸エステルおよび／または
ポリオキシエチレンソルビタン脂肪酸エステルおよび／
またはテトラオレイン酸ポリオキシエチレンソルビツト
５０〜９５重量部、（ｂ）ポリアミン系化合物５０〜５
重量部、（ａ）と（ｂ）の合計量１００重量部に対し、
（ｃ）界面活性剤３〜２０重量部、（ｄ）水２０〜２５
０重量部を含有する水分散体からなるロール汚れ防止
剤。 〔２〕顔料１００重量部に対し、合成共重合体ラテック
ス５〜２０重量部、天然バインダー１〜１０重量部、上
記１記載のロール汚れ防止剤０. １〜１０重量部および
各種添加剤を含有してなることを特徴とする塗工液組成
物。 〔３〕紙の片面または両面に、上記２記載の塗工液組成
物が２〜４０ｇ／ｍ2 の厚みで塗布されていることを特
徴とする塗工紙。 〔４〕板紙の片面または両面に、上記２記載の塗工液組
成物が２〜４０ｇ／ｍ2の厚みで塗布されていることを
特徴とする塗工板紙。That is, the present invention is as follows. [1] (a) Sorbitan fatty acid ester and / or polyoxyethylene sorbitan fatty acid ester and / or
Or 50 to 95 parts by weight of polyoxyethylene sorbate tetraoleate, (b) polyamine compound 50 to 5
Parts by weight, based on 100 parts by weight of the total amount of (a) and (b),
(C) 3 to 20 parts by weight of a surfactant, (d) water 20 to 25
An anti-roll stain comprising an aqueous dispersion containing 0 parts by weight. [2] Contains 5 to 20 parts by weight of a synthetic copolymer latex, 1 to 10 parts by weight of a natural binder, 0.1 to 10 parts by weight of the roll antifouling agent described in 1 above, and various additives based on 100 parts by weight of the pigment. A coating liquid composition comprising: [3] A coated paper, characterized in that the coating composition according to the above 2 is applied to one or both sides of the paper at a thickness of 2 to 40 g / m 2 . [4] A coated paperboard, characterized in that the coating composition of the above item 2 is applied to one or both sides of the paperboard at a thickness of 2 to 40 g / m 2 .
【００１１】以下、本発明を詳細に説明する。本発明の
ロール汚れ防止剤に使用されるソルビタン脂肪酸エステ
ルは、例えば、モノステアリン酸ソルビタン、ジステア
リン酸ソルビタン、モノオレイン酸ソルビタン、ジオレ
イン酸ソルビタン、セスキオレイン酸ソルビタン、ヤシ
油脂肪酸ソルビタン、モノパルミチン酸ソルビタン、ト
リステアリン酸ソルビタンおよびトリオレイン酸ソルビ
タンなどが挙げられる。Hereinafter, the present invention will be described in detail. The sorbitan fatty acid ester used in the roll antifouling agent of the present invention includes, for example, sorbitan monostearate, sorbitan distearate, sorbitan monooleate, sorbitan dioleate, sorbitan sesquioleate, sorbitan coconut fatty acid, and sorbitan monopalmitate. Sorbitan tristearate and sorbitan trioleate.
【００１２】ポリオキシエチレンソルビタン脂肪酸エス
テルとしては、モノラウリル酸ポリオキシエチレンソル
ビタン、ポリオキシエチレンヤシ油脂肪酸ソルビタン、
モノパルミチン酸ポリオキシエチレンソルビタン、モノ
ステアリン酸ポリオキシエチレンソルビタン、トリステ
アリン酸ポリオキシエチレンソルビタン、モノオレイン
酸ポリオキシエチレンソルビタンおよびトリオレイン酸
ポリオキシエチレンソルビタンなどが挙げられる。The polyoxyethylene sorbitan fatty acid ester includes polyoxyethylene sorbitan monolaurate, polyoxyethylene coconut fatty acid sorbitan,
Examples include polyoxyethylene sorbitan monopalmitate, polyoxyethylene sorbitan monostearate, polyoxyethylene sorbitan tristearate, polyoxyethylene sorbitan monooleate, and polyoxyethylene sorbitan trioleate.
【００１３】テトラオレイン酸ポリオキシエチレンソル
ビットとしては、テトラオレイン酸ポリオキシエチレン
ソルビットのエチレンオキサイドモル数が、３０から６
０のものが挙げられる。これらの内、耐水性を低下させ
ず、かつ、塗工層形成後の塗工（板）紙による各仕上げ
ロールや第２バッキングロール汚れに対し、特に好まし
いものとしては、ジステアリン酸ソルビタン、ジオレイ
ン酸ソルビタン、トリステアリン酸ソルビタンおよびト
リオレイン酸ソルビタンを挙げることが出来る。尚、こ
れらの混合物も当然本発明に有効である。As polyoxyethylene sorbite tetraoleate, the number of moles of ethylene oxide of polyoxyethylene sorbite tetraoleate is from 30 to 6
0. Among these, sorbitan distearate, dioleic acid, and the like, which do not lower the water resistance and which are stained with the finishing roll or the second backing roll by the coated (board) paper after forming the coating layer, are particularly preferable. Sorbitan, sorbitan tristearate and sorbitan trioleate can be mentioned. Incidentally, these mixtures are naturally effective in the present invention.
【００１４】本発明で使用されるポリアミン系化合物
は、エチレンジアミン、ジエチレントリアミン、トリエ
チレンテトラミン、テトラエチレンペンタミン、さらに
エポキシ変性ポリアミンなどを挙げることができる。好
ましくは、エチレンジアミンおよびジエチレントリアミ
ンである。尚、これらの混合物も当然本発明に有効であ
る。Examples of the polyamine compound used in the present invention include ethylenediamine, diethylenetriamine, triethylenetetramine, tetraethylenepentamine, and an epoxy-modified polyamine. Preferably, they are ethylenediamine and diethylenetriamine. Incidentally, these mixtures are naturally effective in the present invention.
【００１５】本発明において、ソルビタン脂肪酸エステ
ルおよび／またはポリオキシエチレンソルビタン脂肪酸
エステルおよび／またはテトラオレイン酸ポリオキシエ
チレンソルビットは、５０〜９５重量部である。５０重
量部未満では、仕上げ工程で使用されるスーパーカレン
ダーやグロスカレンダー汚れに対し、効果が薄いばかり
か、アミン系化合物の比率が高いため、塗工液粘度が高
くなりすぎて、塗工が難しい。一方、９５重量部を越え
ると、アミン系化合物の効果が発揮しにくく、塗工工程
で発生する第２バッキングロール汚れの効果が薄いばか
りか、耐水性の効果も出にくい。In the present invention, the sorbitan fatty acid ester and / or polyoxyethylene sorbitan fatty acid ester and / or polyoxyethylene sorbite tetraoleate is 50 to 95 parts by weight. If the amount is less than 50 parts by weight, not only is the effect less effective on supercalender and gloss calender stains used in the finishing process, but also the ratio of the amine compound is high, so that the viscosity of the coating liquid becomes too high and coating is difficult. . On the other hand, if it exceeds 95 parts by weight, the effect of the amine compound is hardly exhibited, and the effect of the second backing roll stain generated in the coating step is not only weak, but also the effect of the water resistance is hardly exhibited.
【００１６】本発明で使用される界面活性剤は、ノニオ
ン活性剤、アニオン活性剤、カチオン活性剤、さらに両
性活性剤などを挙げることができる。ノニオン活性剤と
しては、例えば、ポリオキシエチレンアルキルエーテ
ル、ポリオキシエチレンアルキルフェニルエーテル、ポ
リオキシエチレンアルキルエステル、ソルビタンアルキ
ルエステル、ポリオキシエチレンソルビタンアルキルエ
ステルおよびオキシエチレンオキシプロピレンブロック
コポリマーなどが挙げられる。アニオン活性剤として
は、例えば、脂肪酸塩、高級アルコールの硫酸塩、液体
脂肪油の硫酸エステル塩、二塩基性脂肪酸エステルのス
ルホン酸塩、アルキルアリルスルホン酸塩およびホルマ
リン縮合ナフタリンスルホン酸塩などが挙げられる。カ
チオン活性剤としては、例えば、第一アミン塩、第二ア
ミン塩、第三アミン塩、第四級アンモニウム塩およびピ
リジニウム塩などが挙げられる。また、両性活性剤とし
ては、例えば、カルボン酸型（ペタイン型）、硫酸エス
テル型およびスルホン酸型などが挙げられる。尚、これ
らの混合物も当然本発明に有効である。The surfactant used in the present invention includes a nonionic surfactant, an anionic surfactant, a cationic surfactant, and an amphoteric surfactant. Examples of the nonionic activator include polyoxyethylene alkyl ether, polyoxyethylene alkylphenyl ether, polyoxyethylene alkyl ester, sorbitan alkyl ester, polyoxyethylene sorbitan alkyl ester, and oxyethylene oxypropylene block copolymer. Examples of the anionic activator include fatty acid salts, higher alcohol sulfates, liquid fatty oil sulfates, dibasic fatty acid ester sulfonates, alkylallyl sulfonates, and formalin condensed naphthalene sulfonates. Can be Cationic activators include, for example, primary amine salts, secondary amine salts, tertiary amine salts, quaternary ammonium salts, pyridinium salts, and the like. In addition, examples of the amphoteric activator include a carboxylic acid type (petaine type), a sulfate ester type, a sulfonic acid type, and the like. Incidentally, these mixtures are naturally effective in the present invention.
【００１７】界面活性剤の量は、（ａ）ソルビタン脂肪
酸エステルおよび／またはポリオキシエチレンソルビタ
ン脂肪酸エステルおよび／またはテトラオレイン酸ポリ
オキシエチレンソルビット、及び、（ｂ）ポリアミン系
化合物の合計量１００重量部に対し、界面活性剤が３か
ら２０重量部、好ましくは５から１２重量部である。３
重量部未満では、水分散体が出来ない。一方、２０重量
部を越えると、塗工（板）紙の耐水性が大幅に低下する
ばかりか、泡の発生が大きく実用上使用し難い。The amount of the surfactant is 100 parts by weight in total of (a) sorbitan fatty acid ester and / or polyoxyethylene sorbitan fatty acid ester and / or polyoxyethylene sorbite tetraoleate, and (b) polyamine-based compound. The surfactant is 3 to 20 parts by weight, preferably 5 to 12 parts by weight. 3
If the amount is less than parts by weight, an aqueous dispersion cannot be formed. On the other hand, when the amount exceeds 20 parts by weight, not only the water resistance of the coated (board) paper is significantly reduced, but also the generation of bubbles is large and it is difficult to practically use.
【００１８】また、上記（ａ）と（ｂ）の合計量１００
重量部に対し、水は２０から２５０重量部、好ましくは
４０から１８０重量部である。水が２０重量部未満で
は、水分散体型ロール汚れ防止剤自体の粘度が高くなり
すぎて、実用上取り扱いが難しい。一方、２５０重量部
を越えると、水分散体物が、相分離を起こす。本発明の
ロール汚れ防止剤の製造には、通常使用されるホモミキ
サーを用いることが出来る。一般的な製造方法の例とし
ては、あらかじめ、ホモミキサー槽に、所定量のソルビ
タン脂肪酸エステル類とアミン系化合物、さらに界面活
性剤を入れ、約４０００ｒｐｍの回転数で攪拌しなが
ら、所定量の水を加え、約２０分そのままの状態を維持
することによって目的のものが得られる。The total amount of the above (a) and (b) is 100
Water is from 20 to 250 parts by weight, preferably from 40 to 180 parts by weight, based on parts by weight. If the amount of water is less than 20 parts by weight, the viscosity of the aqueous dispersion type roll antifouling agent itself becomes too high, and it is practically difficult to handle. On the other hand, if it exceeds 250 parts by weight, the aqueous dispersion causes phase separation. For the production of the antifouling agent for rolls of the present invention, a commonly used homomixer can be used. As an example of a general manufacturing method, a predetermined amount of sorbitan fatty acid ester, an amine compound, and a surfactant are put in a homomixer tank in advance, and a predetermined amount of water is stirred while being rotated at about 4000 rpm. And maintaining the condition for about 20 minutes to obtain the desired product.
【００１９】本発明の塗工液組成物は、顔料１００重量
部に対し、合成共重合体ラテックス５〜２０重量部、好
ましくは６〜１４重量部である。合成共重合体ラテック
スが５重量部未満では、ドライ強度およびウエット強度
が大幅に低下する。一方、２０重量部を越えると、イン
キ着肉性や白紙光沢が大幅に低下する。また、天然バイ
ンダーは１〜１０重量部、好ましくは２〜６重量部であ
る。天然バインダーが１重量部未満では、保水性が低下
し、塗工面の平滑性が低下する。一方、１０重量部を越
えると、塗工液粘度が高くなりすぎて、塗工が困難にな
る。The coating composition of the present invention is used in an amount of 5 to 20 parts by weight, preferably 6 to 14 parts by weight, based on 100 parts by weight of the pigment. When the amount of the synthetic copolymer latex is less than 5 parts by weight, the dry strength and wet strength are significantly reduced. On the other hand, if it exceeds 20 parts by weight, the ink deposition property and the glossiness of white paper are significantly reduced. The natural binder is used in an amount of 1 to 10 parts by weight, preferably 2 to 6 parts by weight. If the amount of the natural binder is less than 1 part by weight, the water retention is reduced, and the smoothness of the coated surface is reduced. On the other hand, if it exceeds 10 parts by weight, the viscosity of the coating liquid becomes too high, and coating becomes difficult.
【００２０】また、ロール汚れ防止剤は０. １〜１０重
量部、好ましくは０. ２〜５重量部である。ロール汚れ
防止剤が０. １未満では、汚れ防止効果が出ない。一
方、１０重量部を越えると、塗工液の泡が立ちすぎて、
塗工面を荒らすばかりか、塗工（板）紙の耐水性が落ち
る。本発明のロール汚れ防止剤は、あらかじめ合成共重
合体ラテックス中に配合しても、充分効果は発揮され
る。The amount of the roll stain inhibitor is 0.1 to 10 parts by weight, preferably 0.2 to 5 parts by weight. If the roll stain inhibitor is less than 0.1, the stain prevention effect is not obtained. On the other hand, if the amount exceeds 10 parts by weight, the foam of the coating liquid is too high,
Not only does the coated surface become rough, but the water resistance of the coated (board) paper decreases. Even if the roll antifouling agent of the present invention is previously incorporated into a synthetic copolymer latex, the effect is sufficiently exhibited.
【００２１】本発明の塗工液組成物に使用される合成共
重合体ラテックスは、例えば、ＳＢ系ラテックス、アク
リル系ラテックスおよび酢酸ビニル系ラテックスなどが
挙げられる。また、天然バインダーとしては、例えば、
スターチやカゼインなどが挙げられる。さらに、本発明
の塗工液組成物に使用される顔料は、例えば、カオリン
・クレー、炭酸カルシウム、酸化チタンおよびサチン白
などが挙げられる。The synthetic copolymer latex used in the coating composition of the present invention includes, for example, SB latex, acrylic latex and vinyl acetate latex. Also, as a natural binder, for example,
Examples include starch and casein. Further, examples of the pigment used in the coating composition of the present invention include kaolin clay, calcium carbonate, titanium oxide, and satin white.
【００２２】本発明の塗工液組成物は、通常使用されて
いる各種添加剤、例えば、分散剤、中和剤、増粘剤、殺
菌剤、印刷向上剤（耐水化剤等を含む）および消泡剤な
ども使用可能である。本発明のロール汚れ防止剤を含有
する塗工液組成物を、基材である紙、板紙などに塗布す
ることにより、アート紙、コート紙、軽量コート紙およ
び微塗工紙などの塗工紙、さらに高級板紙やコート白ボ
ールなどの塗工板紙が得られる。The coating composition of the present invention may contain various commonly used additives such as a dispersant, a neutralizer, a thickener, a bactericide, a print improver (including a waterproofing agent) and the like. Defoamers and the like can also be used. By applying the coating liquid composition containing the roll antifouling agent of the present invention to a base paper, paperboard or the like, coated paper such as art paper, coated paper, lightweight coated paper and lightly coated paper And coated paperboard such as high-grade paperboard and coated white balls.
【００２３】塗布方法は限定されるものではないが、従
来より公知の方法、例えば、ブレードコーター、エアー
ナイフコーター、ロールコーター、サイズプレスコータ
ー、キャストコーターなど通常用いられている方法で
紙、板紙などに塗布し、通常の方法で必要な乾燥を行
い、さらに必要に応じてスーパーカレンダー処理を施す
ことにより、塗工（板）紙を製造することができる。The coating method is not limited, but may be a conventionally known method, for example, a paper, paperboard or the like, which is usually used such as a blade coater, an air knife coater, a roll coater, a size press coater, a cast coater or the like. The coated (board) paper can be manufactured by performing necessary drying by a usual method and further performing a super calender treatment as needed.
【００２４】塗布量は、片面または両面に対し、２から
４０ｇ／ｍ2 である。塗布量は、用途に応じて適宜調整
することができる。The coating amount is 2 to 40 g / m 2 on one side or both sides. The application amount can be appropriately adjusted depending on the application.
【００２５】[0025]
【発明の実施の形態】以下に、実施例および比較例を挙
げ本発明をさらに詳細に説明するが、本発明は、これら
の例によってなんら限定されるものではない。尚、各物
性は次の測定方法に従って求めた。 （１）塗工液粘度 ＢＬ型粘度計（６０ｒｐｍ．ＮＯ．３スピンドル）によ
って２５℃で測定した。 （２）ドライピック ＲＩ印刷試験機（明製作所製）を用いて、印刷インク強
度（ＳＤスーパーデラックス５０紅Ｂ；タック値１５、
東華色素社製）０．４ｃｃ３回重ね刷りを行い、ゴムロ
ールに現れたピッキング状態を別の台紙に裏取りし、そ
の程度を観察する。評価は５点相対評価法で行い、ピッ
キング現象の少ないものほど高得点とした。 （３）ウエットピック強度 ＲＩ印刷試験機を用いて、塗工（板）紙表面を吸水ロー
ルで湿してから、印刷インク（ＳＤスーパーデラックス
５０紅Ｂ；タック値１０、東華色素社製）０.４ｃｃ１
回刷りを行い、ゴムロールに現れたピッキング状態を別
の台紙に裏取りし、その程度を観察する。評価は５点相
対評価法で行い、ピッキング現象の少ないものほど高得
点とした。 （４）インキセット性 ＲＩ印刷試験機を用いて、塗工（板）紙を印刷インキ
（ＳＤスーパーデラックス５０藍、東華色素社製）０.
４ｃｃでベタ刷りし、別の台紙に裏取りし、その乾燥性
を観察する。評価は、５点相対評価法で行い、裏取り台
紙が薄い程高得点とした。 （５）耐ロール汚れ適性 ＳＢ系ラテックスとロール汚れ防止剤の比率で、ＳＢ系
ラテックス１００重量部に換算したロール汚れ防止剤を
所定量入れ、６０℃程度の雰囲気中に約２０分入れなが
ら、攪拌する。次に、この試料をゼロックス紙にマイヤ
ーバーＮｏ. １２で塗布し、１５０℃、３０秒乾燥させ
たものに、ラシャ紙を合わせ、ミニスーパーにて圧力と
温度を変えて評価する。評価は、５点相対評価法で行
い、ラシャ紙の繊維が取られない程、高得点とした。 （６）初期耐水性 仕上げ工程前の塗工（板）紙をＲＩ印刷機を用いて、塗
工（板）紙表面を吸水ロールで湿しながら、印刷インク
（ＳＤスーパーデラックス５０紅Ｂ；タック値１０、東
華色素社製）０. ４ｃｃ１回刷りを行い、ゴムロールに
現れたピッキング状態を別の台紙に裏取りし、その程度
を観察する。評価は５点相対評価法で行い、ピッキング
現象の少ないものほど高得点とした。 （７）白紙光沢 塗工（板）紙表面を、村上式ＧＭ−２６Ｄ型光沢度計に
より、７５度−７５度で測定した。評価は、数字が高い
程良好である。Hereinafter, the present invention will be described in more detail with reference to examples and comparative examples, but the present invention is not limited to these examples. In addition, each physical property was calculated | required according to the following measuring method. (1) Coating liquid viscosity Measured at 25 ° C. with a BL type viscometer (60 rpm, NO.3 spindle). (2) Using a dry pick RI printing tester (manufactured by Mei Seisakusho), the printing ink strength (SD Super Deluxe 50 red B; tack value 15,
0.4cc 3 times overprinting is performed, and the picking state that appears on the rubber roll is backed on another backing paper, and the degree is observed. The evaluation was performed by a 5-point relative evaluation method, and the smaller the picking phenomenon, the higher the score. (3) Wet topic strength Using a RI printing tester, wet the surface of the coated (board) paper with a water-absorbing roll, and then print ink (SD Super Deluxe 50 red B; tack value 10, manufactured by Toka Pigment Co., Ltd.) 0 .4cc1
Repeat printing is performed, and the picking state that appears on the rubber roll is backed up on another backing paper, and the degree is observed. The evaluation was performed by a 5-point relative evaluation method, and the smaller the picking phenomenon, the higher the score. (4) Ink setting properties Using a RI printing tester, the coated (plate) paper was printed with printing ink (SD Super Deluxe 50 indigo, manufactured by Toka Pigment Co., Ltd.).
Solid print with 4 cc, backing on another mount, and observing its drying property. The evaluation was performed by a 5-point relative evaluation method, and the higher the backing sheet was, the higher the score was. (5) Roll dirt resistance suitability A predetermined amount of a roll dirt inhibitor converted to 100 parts by weight of the SB latex in the ratio of the SB latex and the roll dirt inhibitor was added, and was placed in an atmosphere at about 60 ° C. for about 20 minutes. Stir. Next, this sample was applied to Xerox paper with a Meyer bar No. 12, dried at 150 ° C. for 30 seconds, combined with rasha paper, and evaluated by changing the pressure and temperature in a mini supermarket. The evaluation was performed by a five-point relative evaluation method, and a high score was set so that the fiber of the rasha paper was not removed. (6) Initial water resistance The printing ink (SD super deluxe 50 crimson B; tack) is applied to the coated (board) paper before the finishing step using an RI printer while the surface of the coated (board) paper is wet with a water absorbing roll. A value of 10 (manufactured by Toka Pigment Co., Ltd.) is printed 0.4 cc once, and the picking state that appears on the rubber roll is backed on another backing paper, and the degree is observed. The evaluation was performed by a 5-point relative evaluation method, and the smaller the picking phenomenon, the higher the score. (7) White Paper Gloss The surface of the coated (board) paper was measured at 75 to 75 degrees using a Murakami GM-26D gloss meter. The higher the number, the better the evaluation.
【００２６】[0026]
【実施例１〜６】表１に示す配合で、ロール汚れ防止剤
として表２に示す各種を用い、塗工液組成物を以下に述
べる方法で調整した。尚、この組成物は、印刷適性評価
用のものである。まず、クレー７０重量部、炭酸カルシ
ウム３０重量部、分散剤０.２重量部および中和剤０.１
重量部を所定の水で分散し、顔料スラリーを調整した。
次に、あらかじめ溶液化しておいたスターチ３重量部と
ＳＢ系ラテックス１０重量部、さらに表２に示した各種
の成分内容を所定の方法で水分散体にしたロール汚れ防
止剤を所定添加量加え、かき混ぜ混合したのち、適量の
水を加えて、最終固形分６５重量％の塗工液組成物を得
た。Examples 1 to 6 Coating liquid compositions were prepared by the methods described below using the formulations shown in Table 1 and the various types shown in Table 2 as roll stain inhibitors. This composition is for evaluation of printability. First, 70 parts by weight of clay, 30 parts by weight of calcium carbonate, 0.2 parts by weight of a dispersant, and 0.1 part of a neutralizing agent.
A part by weight was dispersed in predetermined water to prepare a pigment slurry.
Next, 3 parts by weight of the starch and 10 parts by weight of the SB-based latex, which had been made into a solution in advance, and a predetermined amount of an anti-roll antifouling agent obtained by dispersing the contents of various components shown in Table 2 by a predetermined method were added. After stirring and mixing, an appropriate amount of water was added to obtain a coating liquid composition having a final solid content of 65% by weight.
【００２７】次に、市販の上質紙に、この塗工液組成物
を塗工量１３ｇ／ｍ2 になるようにマイヤーバーで塗工
し、熱風乾燥機（１５０℃、３０秒）にて乾燥した。次
にこの塗工紙をスーパーカレンダー（温度５０℃、線圧
１５ｋｇ／ｃｍ、２回通紙）、温度２３℃、湿度６５％
の恒温恒湿室にて調整したものを試料として、各種測定
を行った。なお、初期耐水性は、スーパーカレンダー掛
け前の塗工紙を所定の評価方法にて評価を行った。結果
を表２に示す。Next, this coating liquid composition was applied to a commercially available high-quality paper with a Meyer bar so as to have a coating amount of 13 g / m 2, and dried with a hot air drier (150 ° C., 30 seconds). did. Next, the coated paper was supercalendered (temperature: 50 ° C., linear pressure: 15 kg / cm, passed twice), temperature: 23 ° C., humidity: 65%
Various measurements were carried out using a sample adjusted in the constant temperature and humidity chamber as a sample. In addition, the initial water resistance evaluated the coating paper before super calendaring by the predetermined evaluation method. Table 2 shows the results.
【００２８】[0028]
【比較例１】ロール汚れ防止剤を用いないこと以外は実
施例１と同様にして、塗工液組成物を調製し、試料を作
成した後、各種測定を行なった。結果を表３に示す。Comparative Example 1 A coating liquid composition was prepared and a sample was prepared in the same manner as in Example 1 except that no roll stain inhibitor was used, and various measurements were made. Table 3 shows the results.
【００２９】[0029]
【比較例２】ロール汚れ防止剤として、ステアリン酸カ
ルシウム（潤滑剤）を０. ８重量部用いた以外は、実施
例１と同様にして、塗工液組成物を調製し、試料を作成
した後、各種測定を行なった。結果を表３に示す。Comparative Example 2 A coating liquid composition was prepared and a sample was prepared in the same manner as in Example 1 except that 0.8 part by weight of calcium stearate (lubricant) was used as a roll stain inhibitor. And various measurements. Table 3 shows the results.
【００３０】[0030]
【比較例３〜１４】ロール汚れ防止剤として、表３、４
に記載されている各種を用いた以外は、実施例１と同様
にして、塗工液組成物を調製し、試料を作成した後、各
種測定を行なった。結果を表３、４に示す。Comparative Examples 3 to 14 Tables 3 and 4
The coating liquid composition was prepared and samples were prepared in the same manner as in Example 1 except for using various kinds described in the above section, and various measurements were performed. The results are shown in Tables 3 and 4.
【００３１】[0031]
【表１】 [Table 1]
【００３２】[0032]
【表２】 [Table 2]
【００３３】[0033]
【表３】 [Table 3]
【００３４】[0034]
【表４】 [Table 4]
【００３５】[0035]
【発明の効果】本発明のロール汚れ防止剤は、塗工液組
成物に用いることにより、塗工（板）紙のインキセット
性を維持しつつ、白紙光沢、ドライ強度およびウエット
ピック強度といった実用物性に優れ、かつ、良好な耐ロ
ール汚れ適性を示すことが出来る。The roll antifouling agent of the present invention, when used in a coating liquid composition, can be used for practical purposes such as white paper gloss, dry strength and wet topic strength while maintaining the ink setting of coated (board) paper. It has excellent physical properties and can exhibit good roll stain resistance.
【００３６】したがって、本発明は、上記の実用物性に
加えて、塗工（板）紙の仕上げ工程である耐スーパーカ
レンダー汚れ適性や、耐グロスカレンダー汚れ適性など
に優れた効果を発揮するばかりか、塗工工程時の第２バ
ッキングロール汚れ適性にも優れた効果を発揮する。Therefore, the present invention, in addition to the above-mentioned practical physical properties, not only exhibits excellent effects such as suitability for super calender stain and suitability for gloss calender stain, which are finishing steps of coated (board) paper. Also, it has an excellent effect on the suitability for dirt on the second backing roll during the coating process.
Claims (4)
／またはポリオキシエチレンソルビタン脂肪酸エステル
および／またはテトラオレイン酸ポリオキシエチレンソ
ルビツト５０〜９５重量部、（ｂ）ポリアミン系化合物
５０〜５重量部、（ａ）と（ｂ）の合計量１００重量部
に対し、（ｃ）界面活性剤３〜２０重量部、（ｄ）水２
０〜２５０重量部を含有する水分散体からなるロール汚
れ防止剤。(1) 50 to 95 parts by weight of a sorbitan fatty acid ester and / or polyoxyethylene sorbitan fatty acid ester and / or polyoxyethylene sorbite tetraoleate; (b) 50 to 5 parts by weight of a polyamine compound; (c) 3 to 20 parts by weight of a surfactant, (d) water 2 based on 100 parts by weight of the total amount of a) and (b)
A roll antifouling agent comprising an aqueous dispersion containing 0 to 250 parts by weight.
ラテックス５〜２０重量部、天然バインダー１〜１０重
量部、請求項１記載のロール汚れ防止剤０.１〜１０重
量部および各種添加剤を含有してなることを特徴とする
塗工液組成物。2. 100 parts by weight of a pigment, 5 to 20 parts by weight of a synthetic copolymer latex, 1 to 10 parts by weight of a natural binder, 0.1 to 10 parts by weight of a roll antifouling agent according to claim 1, and various additives. A coating liquid composition comprising an agent.
塗工液組成物が２〜４０ｇ／ｍ2 の厚みで塗布されてい
ることを特徴とする塗工紙。3. A coated paper characterized in that the coating composition according to claim 2 is applied on one or both sides of the paper at a thickness of 2 to 40 g / m 2 .
の塗工液組成物が２〜４０ｇ／ｍ2 の厚みで塗布されて
いることを特徴とする塗工板紙。4. Coated paperboard, characterized in that the coating liquid composition according to claim 2 is applied to one or both sides of the paperboard at a thickness of 2 to 40 g / m 2 .