Abstract

PROBLEM TO BE SOLVED: To obtain a low bleeding stress dispersion get material having both characteristics of lightened sol and gel, capable of alleviating bleeding of an oil in the interior of a gel to the surface of an outer coat material, being extremely flexible, following any stress applied, relaxing and dispersing impact and vibration. SOLUTION: This stress dispersion gel material is obtained by cross-linking a liquid polymer containing a functional group selected from an OH group, a COOH group, an epoxy group and an amino group on the end or a side chain with a cross-linking agent containing two or more functional groups selected from an isocyanate group, an epoxy group and an amino group in the presence of at least a catalyst and has both characteristics of sol and gel. The liquid polymer in an amount of 100 pts.wt. is cross-linked with 0.4-0.8 equivalent of the cross-linking agent and 50-300 pts.wt. of at least one oil selected from diisodecyl phthalate and diundecyl phthalate to give the objective gel material.

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【０００１】[0001]

【発明の属する技術分野】本発明は低ブリード性応力分
散ゲル材に係り、詳しくは液状ゴムを多官能の架橋剤に
より架橋反応させて架橋密度を抑えた分子網目を形成
し、これらの分子間にオイルを含有させたオルガノゲル
であり、オイルの低ブリード性に優れ、極めて柔軟であ
ってどのような応力にも追従でき、かつ衝撃や振動を緩
和、分散することができるもので、ベッド、マット、座
布団、サドル、床ずれ防止マット、人体各部にあてて保
護するパッド、椅子の敷物、果物等の傷つきやすい物の
緩衝材等に使用できる低ブリード性応力分散ゲル材に関
する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a low-bleed stress-dispersing gel material, and more particularly, to a crosslinking reaction of a liquid rubber with a polyfunctional crosslinking agent to form a molecular network having a reduced crosslinking density. An oil-containing organogel that has excellent low bleeding properties, is extremely flexible, can follow any stress, and can reduce or disperse shocks and vibrations. The present invention relates to a low bleed stress-dispersing gel material which can be used as a cushion, a saddle, a bedsore prevention mat, a pad to be applied to each part of the human body for protection, a chair rug, a cushioning material for easily damaged items such as fruits, and the like.

【０００２】[0002]

【従来の技術】従来、局部的応力を緩和させる材料とし
ては、主にスポンジが用いられていたが、スポンジは適
度に柔軟性があり、経済的にも有利であっても、応力に
対する追従が劣り、また永久変形が大きい欠点があっ
た。これに代わり超軟質のゲルとしては、水を可塑剤と
するポリアクリル酸、ポリビニルアルコール、ポリウレ
タン、ポリアクリルアミド等のハイドロゲルがよく知ら
れている。しかし、ハイドロゲルも、使用時に吸水率が
変化する欠点があった。2. Description of the Related Art Conventionally, sponges have been mainly used as a material for relieving local stress. However, sponges are moderately flexible and economically advantageous. It was inferior and had the disadvantage of large permanent deformation. Instead of such a soft gel, hydrogels such as polyacrylic acid, polyvinyl alcohol, polyurethane and polyacrylamide using water as a plasticizer are well known. However, hydrogels also have the disadvantage that the water absorption changes when used.

【０００３】一方、非水液体を可塑剤とするゲルは、ポ
リノルボルネン、ポリ塩化ビニル、スチレンブタジエン
系共重合高分子などの高吸油性高分子にオイルなどの可
塑剤を吸収させ、熱加工して所定の形状を得ており、柔
軟性は良好であるが、加工法が限定されるため、表面に
フィルムを接着するような複雑な加工ができず、クリー
プ変形が大きく、また局部的な応力分散に欠ける問題が
指摘されていた。On the other hand, a gel using a non-aqueous liquid as a plasticizer is prepared by absorbing a plasticizer such as oil into a highly oil-absorbing polymer such as polynorbornene, polyvinyl chloride, and styrene-butadiene copolymer, and subjecting the gel to heat processing. Although it has a predetermined shape and has good flexibility, the processing method is limited, so complicated processing such as bonding a film to the surface cannot be performed, large creep deformation, and local stress The problem of lack of dispersion was pointed out.

【０００４】このため、従来から高分子材料からなる中
空状の外皮内に水、オイル、ゾル状物などの液状体を封
入したもの、あるいは少なくとも末端か側鎖にＯＨ基、
ＣＯＯＨ基、エポキシ基、アミノ基から選ばれた官能基
を有する液状ゴムを、触媒の存在下にイソシアネート
基、エポシキ基、アミノ基から選ばれた官能基を両末端
を含めて２個以上有する化合物あるいは酸無水物からな
る架橋剤により架橋反応させて得られたゲル状物を高分
子材料からなる外皮で被覆したものが多く使用されてい
た。For this reason, conventionally, a liquid material such as water, oil, or sol is sealed in a hollow outer shell made of a polymer material, or an OH group is added at least at the terminal or side chain.
A compound having a liquid rubber having a functional group selected from a COOH group, an epoxy group and an amino group in the presence of a catalyst and having two or more functional groups selected from an isocyanate group, an epoxy group and an amino group at both ends. Alternatively, a gel-like substance obtained by a crosslinking reaction with a crosslinking agent composed of an acid anhydride and coated with a shell made of a polymer material has been used in many cases.

【０００５】[0005]

【発明が解決しようとする課題】しかし、高分子材料の
外皮内に水、オイル、ゾル状物などの液状体を封入した
ものでは、外皮材が破れた場合、内部の液体が外部へ流
れ出して機能を果たさなくなるという問題があり、また
ゲル状物を高分子材料からなる外皮で被覆したもので
は、僅かな応力がかかる場合では、ゲル状物の弾性のた
めに変形が伴わず、十分に応力を分散できない場合があ
った。また、使用時にゲル内部のオイルが外皮材の表面
にしみ出すブリードが生じ接触物を汚したり、ゲル材の
固体部とオイルの分離が生じるという、問題があった。However, in the case where a liquid material such as water, oil, sol or the like is sealed in the outer shell of a polymer material, when the outer shell material is broken, the internal liquid flows out to the outside. There is a problem that the function is not fulfilled.In addition, when a gel-like material is covered with a shell made of a polymer material, when a slight stress is applied, the gel-like material is not deformed due to the elasticity of the gel-like material. Could not be dispersed. In addition, there is a problem in that oil inside the gel bleeds out to the surface of the outer skin material during use, and contaminants are stained, and the solid portion of the gel material is separated from the oil.

【０００６】本発明は、このような問題点を改善するも
のであり、ゲル内部のオイルが外皮材の表面にしみ出す
のを軽減し、極めて柔軟であってどのような応力を与え
てもこれに追従でき、衝撃や振動を緩和、分散すること
ができる軽量化したゾルとゲルの両特性をもった低ブリ
ード性応力分散ゲル材を提供することを目的とする。The present invention has been made to solve such a problem, and reduces the oil inside the gel from seeping out to the surface of the shell material. It is an object of the present invention to provide a low-bleeding stress-dispersing gel material having both characteristics of a sol and a gel, which can reduce and disperse shock and vibration, and have both characteristics.

【０００７】[0007]

【課題を解決するための手段】本願の請求項１の発明
は、末端か側鎖にＯＨ基、ＣＯＯＨ基、エポキシ基、ア
ミノ基から選ばれた官能基を有する液状高分子を、少な
くとも触媒の存在下にイソシアネート基、エポキシ基、
アミノ基から選ばれた官能基を両末端を含めて２個以上
有する架橋剤により架橋反応させて得られたゾルとゲル
の両特性をもった応力分散ゲル材において、上記液状高
分子１００重量部に対して、架橋剤０．４〜０．８当
量、更にフタル酸ジイソデシルあるいはフタル酸ジウン
デシルから選ばれた少なくとも１種のオイルを５０〜３
００重量部を添加し、架橋反応させて得られた低ブリー
ド性応力分散ゲル材にあり、オイルとしてフタル酸ジイ
ソデシルあるいはフタル酸ジウンデシルから選ばれた少
なくとも１種を使用することにより低ブリード性を改善
することができる。According to the first aspect of the present invention, a liquid polymer having a functional group selected from an OH group, a COOH group, an epoxy group, and an amino group at a terminal or a side chain is used as a catalyst. In the presence of isocyanate groups, epoxy groups,
100 parts by weight of the liquid polymer in a stress-dispersing gel material having both properties of a sol and a gel obtained by performing a cross-linking reaction with a cross-linking agent having two or more functional groups selected from amino groups including both ends. To 0.4 to 0.8 equivalents of a crosslinking agent, and 50 to 3 oils selected from diisodecyl phthalate or diundecyl phthalate.
The low bleed property is obtained by adding 00 parts by weight and performing a crosslinking reaction. The low bleed property is obtained by using at least one kind selected from diisodecyl phthalate or diundecyl phthalate as an oil. can do.

【０００８】本願の請求項２の発明は、高分子中空体が
添加され低ブリード性応力分散ゲル材である。即ち、本
発明では、液状高分子を多官能の架橋剤により程度に架
橋反応させて分子網目を形成し、これらの分子間に多量
の可塑剤を含有させることで、ゾルとゲルの両特性を付
与し、極めて柔軟であってどのような応力を与えてもこ
れに追従でき、応力を与えた時には、充分に応力分散が
できる応力分散性材にある。しかも、高分子中空体ある
いは高分子発泡体を充填させることにより、軽量なゲル
材に仕上げることができる。The invention of claim 2 of the present application is a low bleed stress-dispersing gel material to which a hollow polymer body is added. That is, in the present invention, the liquid polymer is cross-linked to a certain extent by a polyfunctional cross-linking agent to form a molecular network, and by containing a large amount of a plasticizer between these molecules, both properties of the sol and the gel can be obtained. It is a stress dispersing material that is extremely flexible and can follow any stress applied, and can sufficiently disperse stress when stress is applied. Moreover, by filling the polymer hollow body or the polymer foam, a lightweight gel material can be finished.

【０００９】本願の請求項３の発明は、少なくとも応力
負荷面をポリエステル系ポリウレタンフィルムからなる
外皮材で被覆した低ブリード性応力分散ゲル材であり、
より一層低ブリード性を改善することができる。The invention according to claim 3 of the present application is a low bleed stress-dispersing gel material in which at least a stress-loaded surface is covered with a shell material made of a polyester-based polyurethane film,
The bleeding property can be further improved.

【００１０】[0010]

【発明の実施の形態】本発明で使用する液状高分子は、
少なくとも末端か側鎖にＯＨ基、ＣＯＯＨ基、エポキシ
基、アミノ基から選ばれた官能基を有し、主鎖にポリブ
タジエン、ポリイソプレン、ポリエーテルポリオール、
ポリエステルポリオールを有している。具体的には、
１，４ポリブタジエン（出光石油化学社製Ｒ−４５Ｈ
Ｔ、Ｒ−１５ＨＴ等）、液状ポリイソプレンゴム（クラ
レ社製ＬＩＲ−４０３、４１０）等が挙げられる。BEST MODE FOR CARRYING OUT THE INVENTION The liquid polymer used in the present invention is:
OH group at least at the terminal or side chain, COOH group, epoxy group, having a functional group selected from amino group, the main chain polybutadiene, polyisoprene, polyether polyol,
Has polyester polyol. In particular,
1,4 polybutadiene (R-45H manufactured by Idemitsu Petrochemical Co., Ltd.)
T, R-15HT, etc.), and liquid polyisoprene rubber (LIR-403, 410, manufactured by Kuraray Co., Ltd.).

【００１１】また、架橋剤としては、イソシアネート
基、エポキシ基、アミノ基から選ばれた官能基を両末端
を含めて２個以上有するものである。イソシアネート基
を有するものは、４，４’−ジフェニルメタンジイソシ
アネート、トルエン２，４’−ジイソシアネート、ヘキ
サメチレンジジイソシアネート、トリフェニルメタント
リイソシアネート、ポリアリールポリイソシアネートな
どがある。また、エポキシ基を有するものは、１，４ブ
タンジオールジグリシジルエーテル、ネオペンチルグリ
コールジグリシジルエーテル、トリメチロールエタント
リグリシジルエーテルなどがある。また、アミノ基を有
するものは、メタキシレンジアミン、ジエチレントリア
ミン、トリエチレンテトラミン、ジアミノフェニルメタ
ンなどがある。更に、３，３’−４，４’ベンゾフェノ
ンテトラカルボン酸二無水物、Ｍ−フェビレン−ビスマ
レイミドのような酸無水物がある。The crosslinking agent has two or more functional groups selected from isocyanate groups, epoxy groups and amino groups at both ends. Those having an isocyanate group include 4,4'-diphenylmethane diisocyanate, toluene 2,4'-diisocyanate, hexamethylene didiisocyanate, triphenylmethane triisocyanate, and polyaryl polyisocyanate. Those having an epoxy group include 1,4 butanediol diglycidyl ether, neopentyl glycol diglycidyl ether, and trimethylolethane triglycidyl ether. Those having an amino group include metaxylenediamine, diethylenetriamine, triethylenetetramine, and diaminophenylmethane. Further, there are acid anhydrides such as 3,3'-4,4'benzophenonetetracarboxylic dianhydride and M-fevirene-bismaleimide.

【００１２】上記架橋剤の添加量は、液状高分子１００
重量部に対して０．４〜０．８当量である。０．４当量
未満になると、架橋が不充分であり、架橋した材料が外
皮材の破れによって容易に流出してしまう。また、０．
８当量を越えると、架橋した材料が十分架橋して硬くな
り、低応力下での応力分散性が悪くなる。The amount of the crosslinking agent added is 100
It is 0.4 to 0.8 equivalent to parts by weight. If it is less than 0.4 equivalent, the crosslinking is insufficient, and the crosslinked material easily flows out due to the tear of the outer skin material. Also, 0.
If the amount exceeds 8 equivalents, the crosslinked material is sufficiently crosslinked and hardened, and the stress dispersibility under low stress is deteriorated.

【００１３】オイルとしては、フタル酸ジイソデシル
（分子量：４４７）あるいはフタル酸ジウンデシル（分
子量：４７５）から選ばれた少なくとも１種であり、こ
れらより分子量が小さなフタル酸系可塑剤ではブリード
アウトしやすく、一方これらより分子量が大きなフタル
酸系可塑剤ではゲル材との相溶性が悪くなりゲルと可塑
剤が分離しやすくなる。The oil is at least one selected from diisodecyl phthalate (molecular weight: 447) and diundecyl phthalate (molecular weight: 475). A phthalic acid-based plasticizer having a smaller molecular weight than these tends to bleed out. On the other hand, a phthalic acid-based plasticizer having a higher molecular weight than these has poor compatibility with the gel material, and the gel and the plasticizer are easily separated.

【００１４】上記オイルの添加量としては、液状高分子
１００重量部に対して５０〜３００重量部であり、５０
重量部未満では、ゲル材の硬度が高くなり充分な応力分
散性が得られなくなったり、応力を除いた時の変形回復
が遅いという問題があり、３００重量部を超えると、ゲ
ル材中にオイルが保持しきれなくなってゲルとオイルが
分離しやすくなったり、外皮材よりブリードアウトしや
すくなる。The amount of the oil to be added is 50 to 300 parts by weight based on 100 parts by weight of the liquid polymer.
If the amount is less than parts by weight, there is a problem that the hardness of the gel material becomes high and sufficient stress dispersibility cannot be obtained, and the recovery of deformation when stress is removed is slow. Can no longer be retained and the gel and oil can be easily separated or bleed out more easily than the skin material.

【００１５】上記高分子中空体としては、ポリアクリロ
ニトリル、塩化ビニリデン、これらの共重合体などを素
材とした中空体であり、具体的にはこれらの素材を隔壁
として低沸点、炭化水素を内包する中空体、あるいは作
業性を向上させるために中空体の表面に炭酸カルシウ
ム、タルク等のゴム用充填材を付着させたものでもよ
い。また、高分子発泡体としては、独立気泡をもったポ
リエチレン、ポリプロピレン、ポリウレタン等の粉体で
ある。これらの高分子中空体や高分子発泡体は、少なく
とも１種類使用することができ、具体的には粒径の相違
するものを２種類以上使用することができる。The hollow polymer body is a hollow body made of polyacrylonitrile, vinylidene chloride, a copolymer thereof, or the like. Specifically, these materials are used as partition walls to contain a low boiling point and hydrocarbons. A hollow body or a body obtained by attaching a rubber filler such as calcium carbonate or talc to the surface of the hollow body to improve workability may be used. The polymer foam is a powder of polyethylene, polypropylene, polyurethane or the like having closed cells. At least one kind of these polymer hollow bodies and polymer foams can be used, and specifically, two or more kinds having different particle diameters can be used.

【００１６】上記高分子中空体や高分子発泡体の粒径は
２ｍｍ以下、好ましくは０．５ｍｍ以下である。粒径が
２ｍｍを超えると、高分子中空体や高分子発泡体が液状
高分子、可塑剤等と分離してしまい、均質なゲル材にな
らず、また柔軟性が失われ十分な応力分散能力や振動、
衝撃緩和性が発揮できない。高分子中空体あるいは高分
子発泡体の添加量の体積分率は１０〜８０％である。も
し体積分率が１０％未満になると、十分な軽量化効果が
得られず、一方８０％を超えると、硬度が高くなりすぎ
るため、またゲル材の伸びが小さくなり、変形に対する
回復性も低下するため、十分な振動、衝撃緩和性、応力
分散性が発揮できない。The particle diameter of the polymer hollow body or the polymer foam is 2 mm or less, preferably 0.5 mm or less. When the particle size exceeds 2 mm, the polymer hollow body or polymer foam is separated from the liquid polymer, plasticizer, etc., and does not become a homogeneous gel material, and also loses flexibility and has sufficient stress dispersion ability. And vibration,
Cannot exhibit impact relaxation. The volume fraction of the added amount of the polymer hollow body or the polymer foam is 10 to 80%. If the volume fraction is less than 10%, a sufficient weight-reducing effect cannot be obtained, while if it exceeds 80%, the hardness becomes too high, the elongation of the gel material becomes small, and the recovery from deformation also decreases. Therefore, sufficient vibration, shock relaxation and stress dispersibility cannot be exhibited.

【００１７】触媒としては、トリエチルアミン、Ｎ，
Ｎ，Ｎ’，Ｎ’−テトラメチルエチルジアミン、テトラ
メチルグアニジン、トリエチレンジアミン、ジメチルア
ミノエタノール、ビス（２−ジメチルアミノエチル）エ
ーテル、トリス（ジメチルアミノメチル）フェノール、
ジメチルアミノメチルフェノール等のアミン、あるいは
スタナスオクトエート、ジブチルチンジアセテート、ジ
ブリルチンジラウレート、ジブリルチンマーカブチド、
オクチン酸鉛等の有機錫化合物がある。上記触媒の添加
量は、特に液状高分子をイソシアネート基を有する架橋
剤により架橋反応させる場合には、液状高分子１００重
量部に対して、触媒０．００５〜３重量部であり、また
液状高分子をエポキシ基を有する架橋剤により架橋反応
させる場合には、液状高分子１００重量部に対して、触
媒１０〜３０重量部である。この範囲外においては、架
橋が不充分でゲル材が形成されず、また架橋反応が早く
なり過ぎて、ゲル硬度のバラツキが大きくなる。As a catalyst, triethylamine, N,
N, N ′, N′-tetramethylethyldiamine, tetramethylguanidine, triethylenediamine, dimethylaminoethanol, bis (2-dimethylaminoethyl) ether, tris (dimethylaminomethyl) phenol,
Amines such as dimethylaminomethylphenol, or stannas octoate, dibutyltin diacetate, dibrilltin dilaurate, dibriltin carbubutide,
There are organotin compounds such as lead octoate. The amount of the catalyst to be added is 0.005 to 3 parts by weight of the catalyst per 100 parts by weight of the liquid polymer, particularly when the liquid polymer is subjected to a crosslinking reaction with a crosslinking agent having an isocyanate group. When a molecule is subjected to a crosslinking reaction with a crosslinking agent having an epoxy group, the catalyst is used in an amount of 10 to 30 parts by weight based on 100 parts by weight of the liquid polymer. Outside this range, crosslinking is insufficient and a gel material is not formed, and the crosslinking reaction is too fast, resulting in a large variation in gel hardness.

【００１８】また、本発明では、上記添加剤以外に、例
えばアルキル酸エステルナトリウム等に界面活性剤、Ｂ
ＨＴ、Ｉｒｇａｎｏｘ １０１０、同１０７６、ＢＢ
Ｍ、ＢＨＡ等の酸防止剤、例えばＶｉｏｓｏｒｂ １０
０、同１３０、同１２０、Ｃｙａｓｏｒｂ ＵＶ−２４
等の紫外線吸収剤、あるいは例えばペンタクロロフェノ
ール、銅−８−ヒドロキシキノリン等の防黴剤を添加す
ることができる。In the present invention, in addition to the above additives, for example, a surfactant such as sodium alkyl ester,
HT, Irganox 1010, 1076, BB
Acid inhibitors such as M, BHA, for example, Biosorb 10
0, 130, 120, Cyasorb UV-24
And an antifungal agent such as pentachlorophenol and copper-8-hydroxyquinoline.

【００１９】応力分散性材料の製造方法では、上記液状
高分子に、可塑剤および界面活性剤を添加し、その後架
橋剤、触媒を加えて攪拌機にて均一に混合した後、更に
高分子中空体や高分子発泡体を添加して均一に混合し、
十分に脱水する。これをエラストマー製フィルムからな
る外皮材を敷設した型に流し込み、２０〜８０°Ｃで１
〜１２０分間加熱して架橋した後、室温にて１〜２４時
間熟成する。In the method for producing a stress-dispersing material, a plasticizer and a surfactant are added to the above liquid polymer, and then a crosslinking agent and a catalyst are added and uniformly mixed with a stirrer. And polymer foam and mix them evenly,
Dehydrate well. This is poured into a mold in which a skin material made of an elastomer film is laid, and at 20 to 80 ° C., 1
After heating for ~ 120 minutes for crosslinking, aging is carried out at room temperature for 1 to 24 hours.

【００２０】エラストマー製フィルムからなる外皮材
は、少なくとも応力がかかる負荷面に被覆してより一層
オイルのブリードアウトを防止することにあり、伸縮性
に富んだ厚さ３０〜２００μｍのポリエステルポリウレ
タンフィルムであり、応力分散性材料の粘着性を阻止す
るとともに、適度な応力分散を促進するうえで、好まし
い。ポリエーテルポリウレタンフィルムの場合には、上
記オイルにより膨潤し、外皮材表面に著しくオイルのブ
リードアウトを生じる。The outer shell material made of an elastomeric film is intended to further prevent oil bleed-out by covering at least the load surface to which stress is applied, and is made of a stretchable polyester polyurethane film having a thickness of 30 to 200 μm. Yes, it is preferable because it prevents adhesion of the stress dispersing material and promotes appropriate stress dispersion. In the case of a polyether polyurethane film, it swells due to the above oil, and causes significant bleed out of the oil on the surface of the skin material.

【００２１】[0021]

【実施例】次に、本発明を具体的な実施例により更に詳
細に説明する。 実施例１〜２、比較例１〜３ 表１に示す材料の内、高分子中空体を除く配合物を攪拌
機に投入し、均一に混合した後、減圧乾燥機にて１ｔｏ
ｒｒ以下で６０分間脱水した後、攪拌機にて高分子中空
体を混合した。これを外皮材である４００ｍｍ×４００
ｍｍの寸法をもつポリエステルポリウレタン製の袋内に
流し込み、８０°Ｃで６０分間加熱して架橋させた後、
室温にて２４時間熟成してゲル化し、応力分散ゲル材を
得た。Next, the present invention will be described in more detail with reference to specific examples. Examples 1 and 2 and Comparative Examples 1 to 3 Among the materials shown in Table 1, a compound excluding the hollow polymer body was charged into a stirrer, mixed uniformly, and then 1 ton with a reduced pressure dryer.
After dehydration at rr or less for 60 minutes, the polymer hollow body was mixed with a stirrer. This is 400mm x 400
After pouring into a bag made of polyester polyurethane with dimensions of mm and heating at 80 ° C for 60 minutes to crosslink,
It was aged at room temperature for 24 hours to form a gel to obtain a stress-dispersed gel material.

【００２２】得られた応力分散ゲル材にニット製のカバ
ー材を取付け、７０°Ｃのオーブン中に１２０分間加熱
した後、室温下で２４時間放置した後、ニット地カバー
から応力分散ゲル材を取り出し、外皮材表面へのオイル
のブリードアウトの有無とゲル材とオイルの分離の有無
を調べた。その結果を、表１に併記する。A knitted cover material was attached to the obtained stress-dispersing gel material, heated in an oven at 70 ° C. for 120 minutes, left at room temperature for 24 hours, and then the stress-dispersing gel material was removed from the knitted fabric cover. It was taken out and the presence or absence of bleed-out of the oil on the surface of the skin material and the separation of the oil from the gel material were examined. The results are also shown in Table 1.

【００２３】[0023]

【表１】 [Table 1]

【００２４】この結果、オイルとしてフタル酸ジイソデ
シルやフタル酸ジウンデシルを用いて得られた応力分散
ゲル材では、外皮材表面へのオイルのブリードアウトや
ゲル材とオイルの分離がないことが判る。一方、上記以
外のオイルを用いた場合には、オイルの分子量が小さい
ために外皮材表面へのオイルのブリードアウトが発生し
ていることが判る。As a result, it can be seen that the stress-dispersing gel material obtained by using diisodecyl phthalate or diundecyl phthalate as the oil does not bleed out the oil to the surface of the outer skin material or separate the gel material from the oil. On the other hand, when an oil other than those described above was used, it was found that the bleed out of the oil to the surface of the skin material occurred because the molecular weight of the oil was small.

【００２５】[0025]

【発明の効果】以上のように本願の請求項１の発明で
は、液状高分子１００重量部に対して、架橋剤０．４〜
０．８当量、更にフタル酸ジイソデシルあるいはフタル
酸ジウンデシルから選ばれた少なくとも１種のオイルを
５０〜３００重量部を添加し、架橋反応させて得られた
低ブリード性応力分散ゲル材にあり、液状高分子を多官
能の架橋剤により程度に架橋反応させて分子網目を形成
し、これらの分子間に多量の可塑剤を含有させること
で、ゾルとゲルの両特性を付与し、極めて柔軟であって
どのような応力を与えてもこれに追従でき、応力を与え
た時には、充分に応力分散ができ、またオイルとしてフ
タル酸ジイソデシルあるいはフタル酸ジウンデシルから
選ばれた少なくとも１種を使用することにより低ブリー
ド性を有する効果がある。As described above, according to the first aspect of the present invention, the crosslinking agent is added in an amount of from 0.4 to 100 parts by weight of the liquid polymer.
0.8-equivalent, 50-300 parts by weight of at least one oil selected from diisodecyl phthalate or diundecyl phthalate is added to the low-bleed stress-dispersing gel material obtained by a crosslinking reaction. The polymer is cross-linked to a certain degree with a polyfunctional cross-linking agent to form a molecular network, and a large amount of a plasticizer is contained between these molecules, thereby giving both sol and gel properties and being extremely flexible. Any stress can be followed, and when stress is applied, the stress can be sufficiently dispersed and the oil can be reduced by using at least one selected from diisodecyl phthalate or diundecyl phthalate as an oil. There is an effect of having a bleeding property.

【００２６】本願の請求項２の発明は、高分子中空体あ
るいは高分子発泡体を充填させることにより、軽量なゲ
ル材に仕上げることができる効果がある。The invention of claim 2 of the present application has an effect that a lightweight gel material can be finished by filling a polymer hollow body or a polymer foam.

【００２７】本願の請求項３の発明は、少なくとも応力
負荷面をポリエステル系ポリウレタンフィルムからなる
外皮材で被覆した低ブリード性応力分散ゲル材であり、
より一層低ブリード性を改善することができる効果があ
る。The invention according to claim 3 of the present application is a low bleed stress-dispersing gel material in which at least a stress-loaded surface is covered with a shell material made of a polyester-based polyurethane film,
There is an effect that the low bleeding property can be further improved.

───────────────────────────────────────────────────── フロントページの続き (72)発明者 野口 徹 神戸市長田区浜添通４丁目１番21号 三ツ 星ベルト株式会社内 ────────────────────────────────────────────────── ─── Continuing on the front page (72) Inventor Toru Noguchi 4-1-1-21 Hamazoedori, Nagata-ku, Kobe Mitsuhoshi Belt Co., Ltd.

Claims (3)

【特許請求の範囲】[Claims] 【請求項１】 末端か側鎖にＯＨ基、ＣＯＯＨ基、エポ
キシ基、アミノ基から選ばれた官能基を有する液状高分
子を、少なくとも触媒の存在下にイソシアネート基、エ
ポキシ基、アミノ基から選ばれた官能基を両末端を含め
て２個以上有する架橋剤により架橋反応させて得られた
ゾルとゲルの両特性をもった応力分散ゲル材において、
上記液状高分子１００重量部に対して、架橋剤０．４〜
０．８当量、更にフタル酸ジイソデシルあるいはフタル
酸ジウンデシルから選ばれた少なくとも１種のオイルを
５０〜３００重量部を添加し、架橋反応させて得られた
ことを特徴とする低ブリード性応力分散ゲル材。1. A liquid polymer having a functional group selected from an OH group, a COOH group, an epoxy group and an amino group at a terminal or a side chain is selected from an isocyanate group, an epoxy group and an amino group in the presence of at least a catalyst. In a stress-dispersing gel material having both characteristics of a sol and a gel obtained by performing a crosslinking reaction with a crosslinking agent having two or more functional groups including both ends,
The crosslinking agent is 0.4 to 100 parts by weight of the liquid polymer.
A low bleed stress-dispersing gel obtained by adding 0.8 to 50 parts by weight of at least one oil selected from diisodecyl phthalate or diundecyl phthalate, followed by crosslinking reaction. Wood. 【請求項２】 高分子中空体が添加される請求項１記載
の低ブリード性応力分散ゲル材。2. The low bleed stress-dispersing gel material according to claim 1, wherein a polymer hollow body is added. 【請求項３】 少なくとも応力負荷面をポリエステル系
ポリウレタンフィルムからなる外皮材で被覆した請求項
１または２記載の低ブリード性応力分散ゲル材。3. The low bleed stress-dispersing gel material according to claim 1, wherein at least the stress-loaded surface is covered with a skin material made of a polyester-based polyurethane film.