JPH10138879A - Wiper blade - Google Patents

Abstract

PROBLEM TO BE SOLVED: To further smoothen reciprocating motion on a window glass surface and to improve a wiping property by covering a blade consisting of silicone rubber with a membrane of fluorine contained resin. SOLUTION: A sharp and linear edge 4 is provided on a lip part 3 of a blade making contact with a window glass surface. The blade is made of silicone rubber hardness after vulcanization of which is 50-90 deg. in hardness by and A type durometer of JIS K6253. A membrane of fluorine contained resin blended with a resin component the number of valuation of which comes to be at least more than six points in case when an adhesive property with silicone rubber is evaluated by a method in conformity to a cross cut tape method of JIS K5400 is formed on a surface of a blade molded body. As fluorine contained resin of the membrane is excellent in durability and weatherability, it constantly displays stable wiping capacity.

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【０００１】[0001]

【発明の属する技術分野】本発明は、自動車、電車、船
舶、航空機等の各種交通手段のウインドガラスや各種反
応装置、炉、貯槽等のスパイグラス等に装着されるワイ
パー（以下、車両用ワイパーを例にして説明する）にお
いて、これらのガラス面を払拭し清浄化する部材である
ワイパーブレード（以下、単にブレードとする）に関す
るものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a wiper (hereinafter referred to as a vehicle wiper) mounted on a window glass of various transportation means such as an automobile, a train, a ship, and an aircraft, and a spy glass of a reactor, a furnace, a storage tank, and the like. The present invention relates to a wiper blade (hereinafter simply referred to as a blade) which is a member for wiping and cleaning these glass surfaces.

【０００２】[0002]

【従来の技術】車両用ワイパーは、車両のウインドガラ
ス面に装着して、反復運動させることで、そのブレード
部分によりウインドガラス面に付着した雨水、泥水、
雪、みぞれ、ほこり等を払拭して取り除き、運転者等の
視界を確保している。ブレードは一般に、図１に示すよ
うな断面構造をしており、図２に示した状態でウインド
ガラス面に接触使用される。図中、１は保持部、２はネ
ック部、３はリップ部、４はエッジ部、５はウインドガ
ラス、Ｐは加圧方向、Ｍは払拭方向、αはリップ部のウ
インドガラス面に対する倒れ角である。ブレードの機能
において重要なことは、反復運動が円滑に進められて払
拭性能を発揮することであり、特には湾曲したウインド
ガラス５面に対する圧力分布ができるだけ均一で、リッ
プ部３のウインドガラス５面に対する倒れ角αが一定に
なることである。したがって、ブレードの形状、特にウ
インドガラス面に接触するリップ部３の先端部の寸法精
度が重要になる。また、ブレードは常時、ウインドガラ
ス面に加圧、変形された状態でセットされるほか、太陽
からの熱、紫外線やオゾン、風圧、排気ガス等の影響を
まともに受けるという、過酷な条件で使用される。その
ため、ブレードに対する要求特性としては、払拭性、耐
久性、耐候性が必要であり、その他には反復運動時の静
粛性および高速性等が挙げられる。2. Description of the Related Art A wiper for a vehicle is mounted on a window glass surface of a vehicle and repeatedly moved, so that rainwater, muddy water and the like adhered to the window glass surface by a blade portion thereof.
Wipes away snow, sleet, dust, etc., to ensure the driver's view. The blade generally has a cross-sectional structure as shown in FIG. 1, and is used in contact with the window glass surface in the state shown in FIG. In the figure, 1 is a holding portion, 2 is a neck portion, 3 is a lip portion, 4 is an edge portion, 5 is a window glass, P is a pressing direction, M is a wiping direction, and α is a falling angle of the lip portion with respect to the window glass surface. It is. What is important in the function of the blade is that the repetitive motion is smoothly advanced to exhibit the wiping performance. In particular, the pressure distribution on the curved window glass 5 is as uniform as possible, and the lip portion 3 has the same surface as the window 5. Is constant. Therefore, the shape of the blade, particularly the dimensional accuracy of the tip of the lip portion 3 that comes into contact with the window glass surface, is important. In addition, the blade is always set under pressure and deformation on the window glass surface, and it is used under severe conditions where it is directly affected by heat from the sun, ultraviolet rays, ozone, wind pressure, exhaust gas, etc. Is done. Therefore, the characteristics required for the blade include wiping properties, durability, and weather resistance, and other characteristics include quietness during repetitive motion and high speed.

【０００３】これらの要求特性に対応するため、従来は
ブレードの材料として主に天然ゴム、イソプレンゴムが
使用され、その他には、クロロプレンゴム、ＥＰＤＭ、
ＳＢＲ又はこれらの材料を適宜混合したゴム混合物等が
使用されていた。しかし、これらのゴム材料からなるブ
レードは摩擦係数μ＝１〜３であるためブレードの円滑
な作動は妨げられ、ワイパーの駆動機構には過度の負荷
がかけられていた。その結果、ウインドガラス面に払拭
の濃淡が生じたり、払拭中に擦過音を生じたりする、い
わゆるビビリ現象等が発生した。そこで、ウインドガラ
スとの摩擦抵抗を低減させるために、上記ゴム材料を用
いたブレードの表面に、ハロゲン化処理、特には塩素ガ
スや次亜塩素酸ソーダと塩酸の混合水溶液等でゴム表面
に塩素を付加する塩素化処理を行って表面の摩擦係数μ
を１未満にし、ウインドガラスとの滑り性を改善してい
た。また、場合によっては、ハロゲン化処理を施した表
面に、更にグラファイトや二硫化モリブデン等の粉体を
塗布して滑り性を改善することもあった。In order to meet these required characteristics, natural rubber and isoprene rubber have been mainly used as blade materials, and chloroprene rubber, EPDM,
SBR or a rubber mixture obtained by appropriately mixing these materials has been used. However, blades made of these rubber materials have a coefficient of friction μ = 1 to 3 so that smooth operation of the blades is hindered, and an excessive load is applied to the drive mechanism of the wiper. As a result, a so-called chattering phenomenon, such as shading of the wiping on the surface of the window glass or a rubbing sound during the wiping, occurred. Therefore, in order to reduce the frictional resistance with the wind glass, the surface of the blade using the above rubber material is subjected to a halogenation treatment, in particular, chlorine gas or a mixed aqueous solution of sodium hypochlorite and hydrochloric acid. Chlorination treatment to add the friction coefficient of the surface μ
Was set to less than 1, and the sliding property with the window glass was improved. In some cases, a powder such as graphite or molybdenum disulfide may be further applied to the halogenated surface to improve the slipperiness.

【０００４】[0004]

【発明が解決しようとする課題】上記の塩素化処理によ
り、ブレードとウインドガラスとの摩擦抵抗を低減させ
るには、ブレード表面の付加塩素量を増やせばよいこと
から、処理時間や処理溶液の塩素濃度を上げていく方法
が採用されている。しかし、この方法では、塩素化処理
が進む（付加塩素量が増える）につれてブレードの摩擦
係数が減少する反面、払拭性能が低下して拭き残し量が
増加する傾向がある。そのため、塩素化処理の程度には
適正領域が存在し、常に、この適正領域内で処理するよ
うに塩素濃度と処理時間の管理をしなければならなかっ
た。しかも、この適正領域は狭いので処理溶液等の管理
が非常に難しく、その結果、市販のワイパーの中には、
ウインドガラスとの摩擦抵抗が大きく、使用初期の段階
で作動時にビビリを生じて、円滑に作動しなかったり、
作動に支障はないが、拭き残しを生じるものがあった。In order to reduce the frictional resistance between the blade and the window glass by the above chlorination treatment, the amount of added chlorine on the blade surface may be increased. A method of increasing the concentration is employed. However, in this method, as the chlorination treatment proceeds (the amount of added chlorine increases), the coefficient of friction of the blade decreases, but the wiping performance tends to decrease and the unwiped amount tends to increase. Therefore, there is an appropriate region for the degree of the chlorination treatment, and it is necessary to control the chlorine concentration and the treatment time so that the treatment is always performed within this appropriate region. Moreover, since the appropriate area is narrow, it is very difficult to control the processing solution and the like, and as a result, some commercially available wipers have
The frictional resistance with the window glass is large, causing chatter during operation in the early stage of use, and it does not work smoothly,
Although there was no problem with the operation, there were some that left unwiped parts.

【０００５】また、ブレードは、前述したように太陽か
らの紫外線や熱、排気ガス、雨、泥水、雪、みぞれ、埃
等との接触や付着等、非常に過酷な条件下で使用される
が、従来の材料を用いたブレードでは使用している間
に、へたり、摩耗、オゾンによる亀裂等が生じて払拭性
能が著しく低下した。具体的には、１年程度で雨水等の
拭き残しが目立つようになり運転者等の十分な視界確保
が困難になるため、ブレードの交換を必要とした。耐久
性能を満足させるには、熱や荷重下での永久歪みが小さ
い材料であること、オゾン等による致命的な亀裂発生を
防止できること、リップ部の耐摩耗性がよいこと、低温
時でもゴム弾性が保持できること等が必要とされる。こ
れらの内、耐摩耗性については、前述したブレード表面
の塩素化処理による低摩擦化で向上できたが、その他の
項目については改善する方法がなかった。そこで、本出
願人は、先にγ−トリフロロプロピルメチルシロキサン
単位を含有するシリコーンゴムからなるブレードを提案
した（特願平８−３７８５９）。このブレードはウイン
ドガラス面で円滑に作動し、払拭性、耐久性、耐候性に
優れたものであったが、材料自体が高価であった。その
ため、より低価格の材料で製造でき、また、より円滑に
作動するブレードが市場より求められていた。そこで、
本発明の目的は、材料価格が安価で、ウインドガラス面
での反復運動が一層円滑で払拭性が良好であり、熱や荷
重下での永久歪みが小さく、紫外線、オゾン、排気ガ
ス、雨水等との接触や低温等の環境への耐久性、耐候性
に優れたブレードを提供することにある。[0005] Further, as described above, the blade is used under extremely severe conditions such as contact with or adhesion to ultraviolet rays and heat from the sun, exhaust gas, rain, muddy water, snow, sleet, dust and the like. In the case of using a blade made of a conventional material, during use, set, abrasion, cracks due to ozone, and the like occurred, and the wiping performance was significantly reduced. Specifically, in about one year, unwiped residue such as rainwater becomes conspicuous, and it becomes difficult to secure a sufficient visibility for a driver or the like. Therefore, the blade needs to be replaced. In order to satisfy the durability performance, the material must have a small permanent set under heat and load, prevent fatal cracking due to ozone, etc., have good abrasion resistance of the lip, and have rubber elasticity even at low temperatures. Is required to be able to be held. Among these, the wear resistance could be improved by lowering the friction by the chlorination treatment of the blade surface described above, but there was no method for improving other items. Therefore, the present applicant has previously proposed a blade made of silicone rubber containing γ-trifluoropropylmethylsiloxane unit (Japanese Patent Application No. 8-37859). This blade operated smoothly on the surface of the window glass and was excellent in wiping properties, durability and weather resistance, but the material itself was expensive. Therefore, there has been a demand in the market for blades that can be manufactured with lower cost materials and that operate more smoothly. Therefore,
The object of the present invention is that the material price is low, the repetitive motion on the window glass surface is smoother and the wiping property is good, the permanent distortion under heat and load is small, ultraviolet rays, ozone, exhaust gas, rain water, etc. An object of the present invention is to provide a blade excellent in durability against environment such as contact with a low temperature or the like and weather resistance.

【０００６】[0006]

【課題を解決するための手段】本発明者は、上記の目的
を達成するために、鋭意研究を重ねた結果、シリコーン
ゴムからなるブレードをフッ素樹脂の皮膜で被覆するこ
とに着目し、本発明を完成させた。すなわち、本発明
は、少なくともガラス面を払拭する部分が、シリコーン
ゴムとの接着性がＪＩＳ Ｋ ５４００の碁盤目テープ
法に準拠した方法で評価した場合、評価点数が少なくと
も６点以上となるようにする樹脂成分を配合したフッ素
樹脂の皮膜で被覆され、加硫後の硬度がＪＩＳ Ｋ ６
２５３のＡタイプ・デュロメーターによる硬度で５０〜
９０°であるシリコーンゴムからなることを特徴とする
ワイパーブレードである。Means for Solving the Problems The inventors of the present invention have conducted intensive studies in order to achieve the above-mentioned object, and as a result, have focused on covering a blade made of silicone rubber with a fluororesin film. Was completed. That is, in the present invention, at least the portion for wiping the glass surface has an evaluation score of at least 6 or more when the adhesion to the silicone rubber is evaluated by a method based on the grid tape method of JIS K 5400. Coated with a fluororesin film containing a resin component to be cured, and having a hardness after vulcanization of JIS K6
253 A-type durometer hardness 50 ~
A wiper blade characterized by being made of silicone rubber having an angle of 90 °.

【０００７】[0007]

【発明の実施の形態】以下、本発明のブレードについて
具体的に説明する。ウインドガラス面に接触するブレー
ドのリップ部は、シャープで直線的なエッジを持つこ
と、エッジ部は凹凸のないことが重要である。そうでな
い場合は、拭き残しが生じ、また、円滑に反復運動する
ことが困難となる。ブレードは加硫後の硬度がＪＩＳ
Ｋ ６２５３のＡタイプ・デュロメーターによる硬度で
５０〜９０°、より好ましくは６０〜８０°であるシリ
コーンゴムからなるものであれば、特に限定されない。
例えば、ジメチルシロキサン単位、メチルビニルシロキ
サン単位、メチルフェニルシロキサン単位を、ブレード
が必要とするゴム弾性、圧縮永久歪、耐熱・耐寒性等の
物性に合わせて、任意に配合したシリコーンゴムを使用
することができる。硬度が５０°より低い場合及び９０
°より高い場合は、ブレードのリップ部がウインドガラ
ス面に対して適当な倒れ角を形成できず、払拭能力が悪
化する。したがって、硬度が５０〜９０°の範囲にない
シリコーンゴムを使用するのは好ましくない。また、上
記シリコーンゴムには、顔料やシリカ、炭酸カルシウ
ム、タルク、マイカ、グラファイト等の充填剤を任意に
配合してもよい。BEST MODE FOR CARRYING OUT THE INVENTION Hereinafter, a blade of the present invention will be specifically described. It is important that the lip portion of the blade that comes into contact with the window glass surface has a sharp and straight edge, and that the edge portion has no irregularities. Otherwise, wiping is left behind, and it is difficult to smoothly perform repetitive movements. The hardness of the blade after vulcanization is JIS
The material is not particularly limited as long as it is made of silicone rubber having a hardness of 50 to 90 °, more preferably 60 to 80 °, as measured by an A-type durometer of K6253.
For example, use a silicone rubber in which dimethylsiloxane units, methylvinylsiloxane units, and methylphenylsiloxane units are arbitrarily mixed according to the physical properties such as rubber elasticity, compression set, heat resistance, and cold resistance required by the blade. Can be. Hardness less than 50 ° and 90
If the angle is higher than 0 °, the lip portion of the blade cannot form an appropriate inclination angle with respect to the window glass surface, and the wiping ability deteriorates. Therefore, it is not preferable to use a silicone rubber whose hardness is not in the range of 50 to 90 °. Further, the silicone rubber may optionally contain a filler such as a pigment, silica, calcium carbonate, talc, mica, and graphite.

【０００８】ブレードは、全体をシリコーンゴムで形成
してもよいが、ブレードの保持部をポリアミド、ポリカ
ーボネート、ポリアセタール、ポリフェニレンオキシ
ド、ポリフェニレンスルフィド、ポリスルホン、ポリエ
ーテルスルホン、ポリエーテルエーテルケトン、ポリエ
ーテルケトン、ポリエーテルイミド、液晶ポリマー等の
熱可塑性樹脂や、フェノール樹脂、不飽和ポリエステ
ル、エポキシ樹脂、ポリイミド等の熱硬化性樹脂等で形
成してもよい。The blade may be formed entirely of silicone rubber, but the holding portion of the blade may be made of polyamide, polycarbonate, polyacetal, polyphenylene oxide, polyphenylene sulfide, polysulfone, polyether sulfone, polyether ether ketone, polyether ketone, or polyether ketone. It may be formed of a thermoplastic resin such as polyetherimide or a liquid crystal polymer, or a thermosetting resin such as a phenol resin, an unsaturated polyester, an epoxy resin, or a polyimide.

【０００９】ブレード成形体表面には、上記シリコーン
ゴムとの接着性をＪＩＳ Ｋ ５４００の碁盤目テープ
法に準拠した方法で評価した場合、評価点数が少なくと
も６点以上となるようにする樹脂成分を配合したフッ素
樹脂の皮膜を形成させる。シリコーンゴムとの付着性が
ＪＩＳ Ｋ ５４００の碁盤目テープ法に準拠した方法
で評価した場合に、評価点が６点より低いと付着力が弱
すぎて耐久性に問題が生じるので好ましくない。この皮
膜は少なくともウインドガラス面を払拭するブレード部
分を被覆することが必要である。ブレード成形体表面全
部を皮膜で被覆しても何ら問題はない。逆に、この皮膜
でシリコーンゴムからなるブレード表面に被覆しない
と、ウインドガラス面上での作動抵抗が大きくなり、ブ
レードが円滑に作動しなくなる。上記皮膜の厚さは、３
〜３０μｍの範囲とすることが望ましい。厚さが３μｍ
より薄いと十分な耐久性を欠き、３０μｍより厚いと払
拭性が悪くなるからである。When the adhesiveness to the silicone rubber is evaluated by a method in accordance with the cross-cut tape method of JIS K 5400, a resin component is applied to the surface of the blade molded body so that the evaluation score is at least 6 points or more. A film of the blended fluororesin is formed. When the adhesion to the silicone rubber is evaluated by a method based on the grid tape method of JIS K 5400, if the evaluation point is lower than 6, the adhesion is too weak and a problem occurs in durability, which is not preferable. This coating must cover at least the blade portion that wipes the window glass surface. There is no problem even if the entire surface of the blade molding is covered with the coating. Conversely, if the coating is not applied to the surface of the silicone rubber blade, the operating resistance on the window glass surface increases, and the blade does not operate smoothly. The thickness of the film is 3
It is desirable to set the range to 30 μm. 3 μm thick
This is because if the thickness is smaller, sufficient durability is not obtained, and if the thickness is larger than 30 μm, the wiping property is deteriorated.

【００１０】本発明で使用する上記フッ素樹脂として
は、テトラフルオロエチレン、ヘキサフルオロプロペ
ン、クロロトリフルオロエチレン、フッ化ビニリデンあ
るいはフッ化ビニルの単独重合体又は共重合体、更に
は、これらのフルオロオレフィンとエチレン、プロピレ
ン等のオレフィンとの共重合体等が挙げられる。この中
でも特に、ポリテトラフルオロエチレン（ＰＴＦＥ）、
テトラフルオロエチレン／ヘキサフルオロプロペン共重
合体（ＴＦＥ／ＨＦＰ）あるいはテトラフルオロエチレ
ン／エチレン共重合体等のテトラフルオロエチレン重合
体が好適である。また、フッ素樹脂は、その粒度が５０
μｍを超えないもの、すなわち通常０．１〜５０μｍの
範囲にあるものを使用する。粒径が０．１μｍ未満の場
合は、上述したシリコーンゴムとの十分な接着性が発現
し難くなり、形成する皮膜の耐久性に問題が生じる。ま
た、５０μｍを超える場合は、形成する皮膜の表面がざ
らつき、ブレードとしての払拭性能が低下する。The fluororesin used in the present invention includes a homopolymer or a copolymer of tetrafluoroethylene, hexafluoropropene, chlorotrifluoroethylene, vinylidene fluoride or vinyl fluoride, and a fluoroolefin thereof. And olefins such as ethylene and propylene. Among them, polytetrafluoroethylene (PTFE),
A tetrafluoroethylene polymer such as a tetrafluoroethylene / hexafluoropropene copolymer (TFE / HFP) or a tetrafluoroethylene / ethylene copolymer is preferred. The particle size of the fluororesin is 50.
Those not exceeding μm, that is, those usually in the range of 0.1 to 50 μm are used. When the particle size is less than 0.1 μm, sufficient adhesion to the silicone rubber described above is difficult to develop, and a problem arises in the durability of the formed film. On the other hand, if it exceeds 50 μm, the surface of the film to be formed becomes rough, and the wiping performance as a blade is reduced.

【００１１】ブレードの基材であるシリコーンゴムとの
付着性をＪＩＳ Ｋ ５４００の碁盤目テープ法に準拠
した方法で評価した場合、評価点数が少なくとも６点以
上となるようにするため、上記フッ素樹脂に樹脂成分を
配合する。この樹脂成分としては、アクリル樹脂、エポ
キシ樹脂、シリコーン樹脂、ポリアミドイミド樹脂、ポ
リイミド樹脂、ポリフェニレンスルフィド樹脂、ポリカ
ーボネート樹脂等が挙げられる。また、これらの樹脂
は、その粒度が５０μｍを超えない範囲、すなわち通常
１〜５０μｍの範囲にあるものを使用する。粒径が１μ
ｍ未満の場合は、シリコーンゴムとの接着性を高める機
能が発現し難くなり、形成する皮膜の耐久性に問題が生
じる。また、５０μｍを超える場合は、形成する皮膜の
表面がざらつき、ブレードとしての払拭性能が低下す
る。When the adhesion to the silicone rubber, which is the base material of the blade, is evaluated by a method in accordance with the grid tape method of JIS K 5400, the above fluororesin is used so that the evaluation score is at least 6 points or more. Is blended with a resin component. Examples of the resin component include an acrylic resin, an epoxy resin, a silicone resin, a polyamideimide resin, a polyimide resin, a polyphenylene sulfide resin, and a polycarbonate resin. These resins have a particle size not exceeding 50 μm, that is, a resin having a particle size of usually 1 to 50 μm. Particle size 1μ
When it is less than m, the function of enhancing the adhesion to the silicone rubber is difficult to be exhibited, and a problem arises in the durability of the formed film. On the other hand, if it exceeds 50 μm, the surface of the film to be formed becomes rough, and the wiping performance as a blade is reduced.

【００１２】本発明のブレードを成形するには、プレス
成形、押出成形、射出成形等のほか、得られる成形品
（ブレード）が複数の構成材料からなる場合は、多層押
出成形、複合射出成形等の方法を使用する。成形品の取
り方には、単独、共取り等の様々な方法が採用できる
が、単独で成形する場合は、前述したようにシャープで
直線的なエッジとなるように金型又はダイスの設計を行
うのが望ましい。また、二本のブレードを一体で成形す
る場合は、ウインドガラス面に接触するリップ部側を合
わせた共取りとして成形し、後から鋭利な刃物で切断す
る方法を採用するのが好ましい。In order to mold the blade of the present invention, in addition to press molding, extrusion molding, injection molding, and the like, when the obtained molded article (blade) is composed of a plurality of constituent materials, multilayer extrusion molding, composite injection molding, etc. Use the method. Various methods such as single and co-cutting can be adopted for the method of taking the molded product.However, when molding alone, design the mold or die so as to have sharp and straight edges as described above. It is desirable to do. In the case where two blades are integrally formed, it is preferable to adopt a method in which the lip portion contacting the window glass surface is formed as a co-joining shape, and the cutting is performed later with a sharp blade.

【００１３】ブレード成形体表面にフッ素樹脂皮膜を被
覆するには、既に成形したブレードに皮膜を被覆する場
合は、ごく普通の塗装方法、すなわち刷毛塗り法、スプ
レー法、浸浸法、流延法等のいずれも利用することがで
きる。このとき、ブレード成形体の表面を予めＵＶ処
理、ＥＢ処理、カップリング剤、プライマー等で表面処
理しておくと、ブレードとフッ素樹脂の皮膜との接着性
が向上し、皮膜の耐久性が上がる。また、ブレードの成
形と同時にフッ素樹脂の皮膜を形成する場合は、ブレー
ド成形体表面に形成させようとする皮膜形成材料を、例
えばプレス成形用金型のブレード成形部分全体あるいは
少なくともウインドガラスを払拭する部分に刷毛塗り
法、スプレー法等により予め付着させておき、そこにシ
リコーンゴム材料を充填して成形することで、同時成形
させることができる。In order to coat the surface of the blade molded body with the fluororesin film, when coating the already formed blade with the film, a usual coating method, that is, a brush coating method, a spray method, a dipping method, or a casting method is used. Etc. can be used. At this time, if the surface of the blade molded body is previously subjected to a UV treatment, an EB treatment, a coupling agent, a primer, or the like, the adhesion between the blade and the fluororesin film is improved, and the durability of the film is increased. . When the fluororesin film is formed simultaneously with the molding of the blade, the film forming material to be formed on the surface of the blade molded body is wiped, for example, the entire blade molding portion of a press molding die or at least the window glass. By applying the silicone rubber material to the portion in advance by brush coating, spraying, or the like, and filling it with a silicone rubber material, molding can be performed simultaneously.

【００１４】なお、以上の説明は、車両用ウインドガラ
スのブレードについて行ったが、前述したように、本発
明のブレードは車両用ワイパーのほか、各種船舶、航空
機等の各種交通手段のウインドガラス、各種反応装置、
炉、貯槽等のスパイグラス等に装着するワイパーにも同
様に適用することができる。また、本発明のブレード
は、それが適用されるガラス類について、有機、無機の
材質、単層、積層の構造、着色、無色の外観、平滑、凹
凸の表面形状等を何ら区別することなく適用可能であ
る。Although the above description has been made with respect to the windshield blades for vehicles, as described above, the blades of the present invention can be used not only for windshield wipers for vehicles but also for windshields for various transportation means such as ships and aircraft. Various reactors,
The present invention can be similarly applied to a wiper mounted on a spy glass or the like in a furnace or a storage tank. Further, the blade of the present invention is applied to glass to which it is applied, without any distinction between organic and inorganic materials, single layer, laminated structure, color, colorless appearance, smoothness, uneven surface shape and the like. It is possible.

【００１５】[0015]

【実施例】以下、本発明の具体的態様について実施例お
よび比較例を挙げて説明するが、本発明はこれらの実施
例の記載に限定されるものではない。 （実施例１）ＪＩＳ Ｋ ６５２３のＡタイプ・デュロ
メーターによる硬度が７０°のシリコーンゴム「ＫＥ−
９７１ｕ」（信越化学工業社製、商品名）１００重量部
に、加硫剤「Ｃ−８」（同前、商品名）２重量部を添加
し、２本ロールで混練した後、１７５℃、１０分の条件
でプレス成形によりウインドガラス面に接触するリップ
部側を合わせた共取りで成形品を得た。このものを２０
０℃、２時間で二次加硫した後、フッ素樹脂塗料「ＴＣ
−７４００ＣＲ」（ダイキン工業社製、商品名）を塗布
し、風乾後、８０℃で３０分、その後１８０℃で３０分
の熱処理を行い、ブレード表面を皮膜で被覆した。そし
て、鋭利な刃物で相対するリップ部の先端部を切断し本
発明のブレードを得た。上記ブレードを、ＪＩＳ Ｄ
５７１０に規定されている試験機を用いて、この規格に
準拠の拭き性能試験と耐久性能試験を行うと共に、ウイ
ンドガラス面との作動について視認による良否の評価を
行い、これらの結果から総合判定を行った。さらに、総
合判定の結果が良好であったものに対し、サンシャイン
ウェザーによる促進試験を行い耐用時間の比較を行っ
た。また、形成した皮膜の、シリコーンゴムとの付着性
をＪＩＳ Ｋ ５４００の碁盤目テープ法に準拠した方
法で評価した。EXAMPLES Hereinafter, specific embodiments of the present invention will be described with reference to examples and comparative examples, but the present invention is not limited to the description of these examples. (Example 1) Silicone rubber “KE-” having a hardness of 70 ° by an A type durometer according to JIS K 6523.
971u "(manufactured by Shin-Etsu Chemical Co., Ltd., 100 parts by weight), 2 parts by weight of a vulcanizing agent" C-8 "(the same name, trade name) were added and kneaded with two rolls. Under a condition of 10 minutes, a molded product was obtained by press molding together with the lip portion contacting the window glass surface. 20
After secondary vulcanization at 0 ° C for 2 hours, the fluororesin paint “TC
-7400CR "(trade name, manufactured by Daikin Industries, Ltd.) was applied, air-dried, and then heat-treated at 80 ° C for 30 minutes and then at 180 ° C for 30 minutes to coat the blade surface with a film. Then, the tip of the opposing lip was cut with a sharp blade to obtain the blade of the present invention. JIS D
Using a tester specified in 5710, a wiping performance test and a durability performance test in accordance with this standard are performed, and a pass / fail evaluation of the operation with the window glass surface is visually performed. went. Furthermore, those having good results of the comprehensive judgment were subjected to an accelerated test using sunshine weather to compare the service life. In addition, the adhesion of the formed film to the silicone rubber was evaluated by a method based on the grid tape method of JIS K 5400.

【００１６】（実施例２）実施例１と同様にして共取り
で成形品を得、このものを２００℃、２時間で二次加硫
した後、「ＴＣ−７１０９ＢＫ」（ダイキン工業社製、
商品名）を塗布し、風乾後、８０℃で３０分、その後２
８０℃で３０分の熱処理を行い、ブレード表面を皮膜で
被覆した。そして、鋭利な刃物で相対するリップ部の先
端部を切断し、本発明のブレードを得た。このものに対
して、上記と同様の試験を行った。(Example 2) A molded product was obtained by co-molding in the same manner as in Example 1 and subjected to secondary vulcanization at 200 ° C for 2 hours, followed by “TC-7109BK” (manufactured by Daikin Industries, Ltd.).
Product name), air-dry, 30 minutes at 80 ° C, then 2
Heat treatment was performed at 80 ° C. for 30 minutes, and the blade surface was covered with a film. Then, the tip of the opposing lip was cut with a sharp blade to obtain the blade of the present invention. This was subjected to the same test as described above.

【００１７】（実施例３）実施例１と同様にして共取り
で成形品を得、このものを２００℃、２時間で二次加硫
した。その後、成形品に２５４ｎｍの波長のＵＶ光を５
分間照射した。それから、フッ素樹脂塗料「ＴＣ−７１
０９ＢＫ］（ダイキン工業社製、商品名）を塗布し、風
乾後、８０℃で３０分、その後２８０℃で３０分の熱処
理を行い、ブレード表面に皮膜を形成した。その後、鋭
利な刃物で相対するリップ部の先端部を切断し、本発明
のブレードを得た。このものに対して、上記と同様の試
験を行った。Example 3 A molded product was obtained by co-molding in the same manner as in Example 1, and was subjected to secondary vulcanization at 200 ° C. for 2 hours. Thereafter, UV light having a wavelength of 254 nm is applied to the molded product for 5 minutes.
Irradiated for minutes. Then, the fluororesin paint “TC-71
09BK] (trade name, manufactured by Daikin Industries, Ltd.) and air-dried, followed by heat treatment at 80 ° C. for 30 minutes and then at 280 ° C. for 30 minutes to form a film on the blade surface. Thereafter, the tip of the opposing lip was cut with a sharp blade to obtain the blade of the present invention. This was subjected to the same test as described above.

【００１８】（実施例４）実施例１と同様にして共取り
で成形品を得、このものを２００℃、２時間で二次加硫
した。その後、成形品に２５４ｎｍの波長のＵＶ光を５
分間照射した。それから、フッ素樹脂塗料「ＴＣ−７４
００ＣＲ］（ダイキン工業社製、商品名）を塗布し、風
乾後、８０℃で３０分、その後１８０℃で３０分の熱処
理を行い、ブレード表面に皮膜を形成した。その後、鋭
利な刃物で相対するリップ部の先端部を切断し、本発明
のブレードを得た。このものに対して、上記と同様の試
験を行った。Example 4 A molded product was obtained by co-machining in the same manner as in Example 1, and was subjected to secondary vulcanization at 200 ° C. for 2 hours. Thereafter, UV light having a wavelength of 254 nm is applied to the molded product for 5 minutes.
Irradiated for minutes. Then, the fluororesin paint “TC-74
[00CR] (trade name, manufactured by Daikin Industries, Ltd.), air-dried, and then heat-treated at 80 ° C. for 30 minutes and then at 180 ° C. for 30 minutes to form a film on the blade surface. Thereafter, the tip of the opposing lip was cut with a sharp blade to obtain the blade of the present invention. This was subjected to the same test as described above.

【００１９】（比較例１）実施例１〜４で得たブレード
と同じ寸法で天然ゴム製の市販ブレードを用い、ＪＩＳ
Ｋ ５４００の碁盤目テープ法に準拠した付着性評価
試験を除いて、上記と同様の試験を行った。(Comparative Example 1) A commercially available natural rubber blade having the same dimensions as the blades obtained in Examples 1 to 4 was used.
The same test as described above was conducted, except for an adhesion evaluation test based on the K5400 grid tape method.

【００２０】（比較例２）実施例１において、フッ素樹
脂塗料でブレードに皮膜を作らないものを用い、比較例
１と同様の試験を行った。(Comparative Example 2) The same test as in Comparative Example 1 was carried out in Example 1 except that the coating was not formed on the blade with a fluororesin paint.

【００２１】（比較例３）実施例１において、ＪＩＳ
Ｋ ６２５３のＡタイプ・デュロメーターによる硬度が
３０°のシリコーンゴム「ＫＥ−９３１ｕ」（信越化学
工業社製、商品名）を使用した以外は、すべて同様の成
形及び処理を行ったものを用い、比較例１と同様の試験
を行った。(Comparative Example 3)
Except for using silicone rubber "KE-931u" (manufactured by Shin-Etsu Chemical Co., Ltd., trade name) having a hardness of 30 [deg.] With an A-type durometer of K6253, all molded and treated in the same manner and compared. The same test as in Example 1 was performed.

【００２２】（比較例４）実施例１と同様にして共取り
で成形品を得、このものを２００℃、２時間で二次加硫
した。それから付着性を向上させる樹脂成分を配合して
いないフッ素粉体塗料「ＡＣＸ−３１」（ダイキン工業
社製、商品名）をスプレー塗装し、２００℃で３時間の
熱処理を行い、ブレード表面に皮膜を形成した。その
後、鋭利な刃物で相対するリップ部の先端部を切断し、
本発明のブレードを得た。このものに対して、比較例１
と同様の試験を行った。Comparative Example 4 A molded product was obtained by co-molding in the same manner as in Example 1, and was subjected to secondary vulcanization at 200 ° C. for 2 hours. Then, a fluorine powder coating “ACX-31” (trade name, manufactured by Daikin Industries, Ltd.), which does not contain a resin component for improving adhesion, is spray-coated and heat-treated at 200 ° C. for 3 hours to form a film on the blade surface. Was formed. After that, cut the tip of the opposite lip with a sharp blade,
A blade according to the invention was obtained. Comparative Example 1
The same test was performed.

【００２３】試験の結果を表１に示す。なお、表中、拭
き性能試験と耐久性能試験では、ＪＩＳ規格内のものを
○、ＪＩＳ規格外のものを×、作動評価ではビビリのな
いものを○、あるものを×で表した。また、付着製の評
価については、ＪＩＳ Ｋ５４００の碁盤目テープ法に
準拠した評価を行った。Table 1 shows the results of the test. In the table, in the wiping performance test and the durability performance test, those within the JIS standard were indicated by ○, those not conforming to the JIS standard were indicated by x, those without chatter in the operation evaluation were indicated by 、, and some were indicated by x. In addition, the evaluation of the adhered product was performed in accordance with the grid tape method of JIS K5400.

【００２４】[0024]

【表１】 [Table 1]

【００２５】表１に示した結果から明らかなように、本
発明のブレードは拭き性能、耐久性能、動作性能のいず
れも良好で耐用時間も大幅に延長した。As is evident from the results shown in Table 1, the blade of the present invention exhibited good wiping performance, durability performance, and operation performance, and the service life was greatly extended.

【００２６】[0026]

【発明の効果】本発明のブレードは、特殊なシリコーン
ゴム材料を用いる必要がなく、ＪＩＳＫ ６２５３のＡ
タイプ・デユロメーターによる硬度が５０〜９０°であ
れば任意のシリコーンゴム材料を用いることができる。
その結果、材料コストが下がり、安価に製品を供給する
ことができる。また、皮膜のフッ素樹脂は耐久性、耐候
性に優れているため、常に安定した払拭能を発揮するも
のとなる。更に、自由な着色もできるため、自動車等の
色に合わせたりする等、デザイン性の自由度が広がる。
また、低温特性、高温特性、耐紫外線性、耐オゾン性等
の環境特性に優れているため、初期性能が長期間持続
し、数年間交換をしなくとも良好な視界を確保すること
ができる。The blade of the present invention does not require the use of a special silicone rubber material, and is JIS K 6253 A
Any silicone rubber material can be used as long as the hardness according to the type durometer is 50 to 90 °.
As a result, material costs are reduced, and products can be supplied at low cost. Further, since the fluororesin of the film is excellent in durability and weather resistance, it always exerts a stable wiping ability. Furthermore, since it can be freely colored, the degree of freedom in design is expanded, for example, in accordance with the color of an automobile or the like.
In addition, since it has excellent environmental characteristics such as low-temperature characteristics, high-temperature characteristics, ultraviolet light resistance, and ozone resistance, the initial performance is maintained for a long time, and a good view can be secured without replacement for several years.

【図面の簡単な説明】[Brief description of the drawings]

【図１】本発明が適用されるブレードの一実施態様を示
す概略断面図である。FIG. 1 is a schematic sectional view showing an embodiment of a blade to which the present invention is applied.

【図２】図１に示したブレードのウインドガラス面との
接触状態を示す概略説明図である。FIG. 2 is a schematic explanatory view showing a contact state of a blade shown in FIG. 1 with a window glass surface.

【符号の説明】[Explanation of symbols]

１…保持部、２…ネック部、３…リップ部、４…エッジ
部、５…ウインドガラス、Ｐ…加圧方向、Ｍ…払拭方
向、α…リップ部のウインドガラス面に対する倒れ角。DESCRIPTION OF SYMBOLS 1 ... holding | maintenance part, 2 ... neck part, 3 ... lip part, 4 ... edge part, 5 ... window glass, P ... pressing direction, M ... wiping direction, (alpha) ... Falling angle of the lip part with respect to the window glass surface.

Claims (1)

【特許請求の範囲】[Claims] 【請求項１】 少なくともガラス面を払拭する部分が、
シリコーンゴムとの接着性がＪＩＳ Ｋ ５４００の碁
盤目テープ法に準拠した方法で評価した場合、評価点数
が少なくとも６点以上となるようにする樹脂成分を配合
したフッ素樹脂の皮膜で被覆され、加硫後の硬度がＪＩ
Ｓ Ｋ ６２５３のＡタイプ・デュロメーターによる硬
度で５０〜９０°であるシリコーンゴムからなることを
特徴とするワイパーブレード。At least a portion for wiping a glass surface,
When the adhesiveness to silicone rubber is evaluated by a method based on the grid tape method of JIS K 5400, it is coated with a fluororesin film containing a resin component so that the evaluation score is at least 6 or more. Hardness after sulfurization is JI
A wiper blade comprising a silicone rubber having a hardness of 50 to 90 [deg.] According to an A type durometer of SK6253.