JPH10138438A - Manufacture of decorative plate made of woody plate as base material by laminator - Google Patents
Manufacture of decorative plate made of woody plate as base material by laminatorInfo
- Publication number
- JPH10138438A JPH10138438A JP8300463A JP30046396A JPH10138438A JP H10138438 A JPH10138438 A JP H10138438A JP 8300463 A JP8300463 A JP 8300463A JP 30046396 A JP30046396 A JP 30046396A JP H10138438 A JPH10138438 A JP H10138438A
- Authority
- JP
- Japan
- Prior art keywords
- adhesive
- base material
- board
- decorative
- laminator
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明はラミネータによる化
粧板の製造方法に関し、特に、木質板を基材とする化粧
板のラミネータによる製造方法に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method of manufacturing a decorative board using a laminator, and more particularly to a method of manufacturing a decorative board based on a wooden board using a laminator.
【０００２】[0002]
【従来の技術】合板や木質板を基材として用いて化粧板
を製造するのに、従来からラミネータが用いられてい
る。図２は、従来用いられているラミネータの主要構成
要素を説明するものであり、基材合板あるいは基材木質
板１０が、必要に応じて図示されない除塵装置によって
表面に付着しているごみや木屑が除かれた後、スプレッ
ダー１に送り込まれ、スプレッダー１内の第１の塗布ロ
ール２によって塩化アンモニウム水溶液のような硬化剤
が塗布され、赤外線ヒータ３によって該硬化剤中の水分
がとばされ後、第２の塗布ロール４により尿素樹脂のよ
うな接着主剤が塗布される。塗布された接着剤が同様な
赤外線ヒータ５によって半乾燥状態とされた後、接着剤
が塗布された基材は、一対又は複数対の熱ロールプレス
６間に送られ、そこでシート巻ロール７からの化粧シー
トが貼り合わされる。2. Description of the Related Art Laminators have been conventionally used to manufacture decorative boards using plywood or wood board as a base material. FIG. 2 is a view for explaining main components of a conventionally used laminator. The plywood or the wood substrate 10 is attached to the surface by a dust remover (not shown) as necessary. Is removed, and is fed into a spreader 1, a curing agent such as an ammonium chloride aqueous solution is applied by a first application roll 2 in the spreader 1, and moisture in the curing agent is blown by an infrared heater 3. The second coating roll 4 applies an adhesive agent such as a urea resin. After the applied adhesive is put into a semi-dry state by the similar infrared heater 5, the substrate on which the adhesive is applied is sent between one or more pairs of hot roll presses 6, where the sheet winding roll 7 Are laminated.
【０００３】両面化粧板を製造する場合には、基材の両
面に接着剤が塗布されかつ両面に化粧シートが貼り付け
られる。複数対の熱ロールプレス６のいずれかにエンボ
スを設けることにより、表面にエンボス加工された化粧
板を得ることもできる。When a double-sided decorative board is manufactured, an adhesive is applied to both sides of a base material, and decorative sheets are attached to both sides. By providing an emboss on any one of the plurality of pairs of hot roll presses 6, a decorative board having an embossed surface can be obtained.
【０００４】[0004]
【発明が解決しようとする課題】本発明者らは、上記の
ようなラミネータによる化粧板の製造に長く携わってい
るが、その過程において、基材としてパーティクルボー
ドや中質繊維板のような木質板を用いて化粧板を製造す
るに際し、基材表面に塗布する接着剤の多寡が化粧板の
品質に大きな影響を与えることを経験した。例えば、基
材としてパーティクルボードを用い、その表面に４．５
±０．５ｇ／尺2 で接着剤（例えば、硬化剤：塩化アン
モニウム水溶液、主剤：尿素樹脂）を塗布した場合、塗
布した接着剤の一部がパーティクルボード中に吸い込ま
れていき、表面に凹凸状の接着剤層が形成された。ま
た、接着剤中の水分絶対量が多いと基材表面にチップダ
クが起きやすかった。そこに３０ｇ／ｍ2 のプレコート
化粧薄葉紙を貼り付けたところ、接着不良は生じなかっ
たが、化粧板の一部に貼りしわが生じ、表面性が悪化し
た。The present inventors have long been involved in the production of decorative boards using the above-described laminator. In the process, the present invention uses wood substrates such as particle boards and medium fiber boards as base materials. When manufacturing a decorative board using a board, we experienced that the amount of adhesive applied to the surface of the base material had a great effect on the quality of the decorative board. For example, a particle board is used as a base material, and 4.5
When an adhesive (eg, curing agent: ammonium chloride aqueous solution, main agent: urea resin) is applied at ± 0.5 g / scale 2 , part of the applied adhesive is sucked into the particle board, and the surface has irregularities. An adhesive layer was formed. When the absolute amount of water in the adhesive was large, chipping was likely to occur on the substrate surface. When a precoated decorative tissue paper of 30 g / m 2 was stuck thereon, poor adhesion did not occur, but a part of the decorative plate was wrinkled and the surface property was deteriorated.
【０００５】そこで、同じ条件で接着剤塗布量を約１．
０〜３．０ｇ／尺2 としたところ、接着剤のほとんどが
基材表面から吸い込まれてしまい、同様にして３０ｇ／
ｍ2のプレコート化粧薄葉紙を貼り付けたところ、表面
性は向上するものの接着不良箇所が多く発生し、薄葉紙
の剥離がみられた。[0005] Under the same conditions, the amount of adhesive applied is about 1.
When the amount was set to 0 to 3.0 g / scale 2 , most of the adhesive was sucked from the surface of the base material, and similarly, 30 g /
was pasted precoat makeup tissue paper m 2, the surface resistance is much generated bonding defective portion of those improved, peeling of the thin paper was observed.
【０００６】接着剤として酢酸ビニルエマルジョンを使
用し、同じようにして化粧板を製造したが、接着剤塗布
量が多すぎる場合にはやはり張りしわ等の凹凸発生等に
よる表面性の悪化が生じ、少なすぎる場合には接着不良
箇所が多く発生した。それで、通常は、化粧シートの剥
離による商品欠陥が生じるのを回避するために、４．５
ｇ／尺2 程度以上の接着剤を塗布して化粧板を製造する
ようにしており、場合によっては表面に凹凸が発生して
表面性が低下したものが製造されると共に、接着剤を多
く使用することからコスト高の一因ともなっている。[0006] A decorative board was manufactured in the same manner using a vinyl acetate emulsion as an adhesive. However, if the amount of the adhesive applied was too large, the surface property was also deteriorated due to the occurrence of irregularities such as wrinkles. If the amount is too small, many adhesion failure portions occur. Therefore, usually, in order to avoid the occurrence of a product defect due to peeling of the decorative sheet, 4.5 is used.
g / scale 2 or more adhesive is applied to manufacture decorative panels. In some cases, irregularities are generated on the surface and surface properties are reduced, and more adhesive is used. This also contributes to high costs.
【０００７】本発明の目的は、従来の木質板を基材とす
る化粧板のラミネータによる製造方法に生じている上記
のような不都合を解消した化粧板の製造方法を提供する
ことにあり、より具体的には、少ない接着剤の塗布量で
もって表面平滑性が高くかつ接着不良箇所も生じること
のない、木質板を基材とする化粧板のラミネータによる
製造方法を提供することにある。An object of the present invention is to provide a method of manufacturing a decorative board which eliminates the above-mentioned inconvenience which has occurred in a conventional method of manufacturing a decorative board based on a wooden board using a laminator. Specifically, it is an object of the present invention to provide a method for producing a decorative board using a wooden board as a base material by using a laminator, which has a high surface smoothness with a small amount of an applied adhesive and does not cause defective bonding.
【０００８】[0008]
【課題を解決するための手段】上記課題を解決するため
の本発明は、基材である木質板の一面又は両面にスプレ
ッダーにより接着剤を塗布した後、該接着剤塗布面に化
粧シートを連続的に貼り付けていくようにした木質板を
基材とする化粧板のラミネータによる製造方法であっ
て、該スプレッダーによる接着剤の塗布工程の前工程と
して、基材である木質板の一面又は両面を加熱された表
面平滑なロールによって加圧しながら加熱する工程を有
することを特徴とする。In order to solve the above-mentioned problems, the present invention is to apply an adhesive to one or both surfaces of a wooden board as a base material with a spreader, and then to apply a decorative sheet to the adhesive-applied surface. A method for manufacturing a decorative board using a wooden board as a base material, which is to be stuck on the surface, as a pre-process of applying an adhesive by the spreader, one or both surfaces of the wood board as a base material Is heated while pressurizing with a heated surface smooth roll.
【０００９】本発明の方法を実施するのに用いるラミネ
ータは、図１に示すように、スプレッダー１の上流側
に、加熱された表面が平滑なロール２０が位置すること
を除き、従来使用されているラミネータと同様のもので
あってよい。基材である常温の木質板１０は、加熱ロー
ル２０の間を通過することにより加圧と加熱とを受け表
面が平滑化される。その状態の基板木質板の表面に対し
て、以下、従来法と同様にスプレッダー１による接着剤
塗布と乾燥を行い、熱ロールプレスによる化粧シートの
貼り付けを行う。The laminator used to carry out the method of the present invention is conventionally used except that a heated flat roll 20 is located upstream of the spreader 1, as shown in FIG. May be the same as the laminator. The room temperature wooden board 10 as a base material is subjected to pressure and heat by passing between the heating rolls 20, and the surface is smoothed. Thereafter, the spreader 1 applies an adhesive to the surface of the wooden board of the substrate in this state, and then performs drying, and a decorative sheet is attached by a hot roll press.
【００１０】この方法によれば、接着剤の木質板内部へ
の吸い込みがなくかつ表面が平滑化されていることか
ら、接着剤の塗布量が１〜３ｇ／尺2 程度の少量であっ
ても、化粧シートは接着不良部分がなく全面接着され、
表面平滑でかつ表面チップダクもない表面性の良好な化
粧板が得られる。基材としての木質板は、パーティクル
ボード、配向性パーティクルボード、中質繊維板、硬質
繊維板のような木質加工材料を用いる。According to this method, since the adhesive is not sucked into the wood board and the surface is smoothed, even if the applied amount of the adhesive is as small as about 1 to 3 g / scale 2. , The decorative sheet is fully bonded without any defective bonding
A decorative plate having a smooth surface and good surface properties without surface chipping is obtained. As the wood board as the base material, a wood processing material such as a particle board, an oriented particle board, a medium fiber board, and a hard fiber board is used.
【００１１】スプレッダーで塗布する接着剤は、従来法
により木質板表面に化粧シートを貼り付けて化粧板を製
造するのに用いられてる接着剤をそのまま用いることが
できる。例えば、尿素樹脂単独あるいは尿素樹脂２〜５
重量部に対して酢酸ビニルを８〜５重量部の割合で混合
したもの、さらには、熱硬化型酢酸ビニルエマルジョン
のような水性接着剤を用いてもよく、その他、エチレン
酢酸ビニル系エマルジョンのような接着剤であってもよ
い。図示のように、硬化剤と接着主剤とを別個に塗布す
ることも必須でなく、硬化剤と接着主剤とを予め混合し
たものを一基のスプレッダーにより塗布するようにして
もよい。As the adhesive applied by the spreader, the adhesive used for manufacturing a decorative board by attaching a decorative sheet to the surface of a wooden board by a conventional method can be used as it is. For example, urea resin alone or urea resin 2-5
A mixture of 8 to 5 parts by weight of vinyl acetate with respect to parts by weight, or an aqueous adhesive such as a thermosetting vinyl acetate emulsion may be used. A suitable adhesive may be used. As shown in the figure, it is not essential to separately apply the curing agent and the main adhesive, and a mixture of the curing agent and the main adhesive in advance may be applied by a single spreader.
【００１２】化粧シートにも特に制限はなく、３０ｇ／
ｍ2 程度の薄葉紙、８０ｇ／ｍ2 程度のチタン紙、６０
ｇ／ｍ2 程度のクラフト紙、自己接着性のない程度に樹
脂含浸されたシート（ＦＦシート）、その他、塩化ビニ
ルシート、ポリオレフィン系シート等であってよい。There is no particular limitation on the decorative sheet.
m 2 about tissue paper, 80g / m 2 about titanium paper, 60
It may be a kraft paper of about g / m 2 , a resin-impregnated sheet (FF sheet) having no self-adhesiveness, a vinyl chloride sheet, a polyolefin sheet, or the like.
【００１３】本発明において、基材である木質板はスプ
レッダーに入る前に、加熱された表面平滑なロール、好
ましくは金属製ロールによって加圧と加熱を受ける。加
圧と加熱とにより木質板表面のリグニンは熱軟化をし、
表面にリグニンによるシール層が形成される。表面平滑
なロールによる圧縮によって木質板の表面が平滑化され
ることに加えて、リグニンによるシール層が形成される
ことにより、塗布された接着剤の基板内部への吸い込み
は阻止されて、少ない塗布量でもって十分な接着力が得
られるとともに、表面の平滑化が達成され、また表面チ
ップダク防止が図られる。In the present invention, the wooden board as the base material is subjected to pressure and heat by a heated flat roll, preferably a metal roll, before entering the spreader. The lignin on the surface of the wooden board undergoes heat softening by pressurization and heating,
A seal layer of lignin is formed on the surface. In addition to the smoothing of the surface of the wooden board by the compression with the smooth surface rolls, the formation of the lignin-based sealing layer prevents the applied adhesive from being sucked into the inside of the substrate, thereby reducing the amount of application. A sufficient adhesive strength can be obtained with the amount, the surface can be smoothed, and the surface chipping can be prevented.
【００１４】素材が木質ボード（例えば、パーティクル
ボード）である場合、リグリン成分の熱軟化温度は気乾
乾燥状態で１３４℃〜２３５℃程度であり、加熱ロール
による加熱温度は該リグリン成分の熱軟化温度よりも高
い温度、好ましくは約５０℃〜１５０℃程度高い温度で
あることが望ましい。本発明者らの実験によれば、加熱
ロールによる加熱温度は高い温度であるほど、接着剤の
塗布量を少なくすることができ、パーティクルボードを
基材として用い、ラインスピード３０〜４０ｍ／分で製
造した場合に、従来法による場合（すなわち、常温の木
質板に直接接着剤を塗布する場合）には、良好な接着性
を得るのに４．５ｇ／尺2 程度を必要としたが、加熱温
度１８０℃では３ｇ／尺2 程度で十分であり、さらに、
３５０℃まで加熱した場合には１ｇ／尺2 程度で十分で
あった。なお、加熱された表面平滑なロールによる木質
板への加圧は線圧１０〜１００ｋｇ／ｃｍ程度で十分で
あり、これ以上加圧することはボードの歩減りの理由で
不都合があり、それ以下の加圧では十分に目的が達成で
きない。When the material is a wood board (eg, a particle board), the heat softening temperature of the ligulin component is about 134 ° C. to 235 ° C. in an air-dried state, and the heating temperature by the heating roll is the heat softening of the ligulin component. It is desirable that the temperature is higher than the temperature, preferably about 50 ° C. to 150 ° C. According to the experiments of the present inventors, the higher the heating temperature by the heating roll, the smaller the amount of the adhesive to be applied, and using a particle board as a base material, at a line speed of 30 to 40 m / min. In the case of manufacturing, in the case of the conventional method (that is, in the case where the adhesive is directly applied to the wood board at normal temperature), about 4.5 g / scale 2 was required to obtain good adhesiveness. At a temperature of 180 ° C., about 3 g / scale 2 is sufficient.
When heated to 350 ° C., about 1 g / scale 2 was sufficient. In addition, it is sufficient to press the wooden board with a heated surface smooth roll at a linear pressure of about 10 to 100 kg / cm. Pressing more than this is inconvenient for the reason of reducing the board, and the following pressures are inconvenient. The purpose cannot be sufficiently achieved by pressurization.
【００１５】[0015]
【実施例】以下、実施例により本発明を説明する。 〔実施例１〕図１に示すように、従来公知のラミネータ
のスプレッダー上流に表面が平滑な鉄製のロールを一対
配置し、電熱ヒーターにより加熱可能とした。基材とし
ての１５ｍｍ×９０９ｍｍ×１８１８ｍｍのパーティク
ルボードを、該鉄製ロールを線圧５０ｋｇ／ｃｍで対向
させた状態で１８０℃に加熱し、その間を３０ｍ／分の
速度で通過させた後、スプレッダーに送り込んだ。The present invention will be described below with reference to examples. [Embodiment 1] As shown in Fig. 1, a pair of iron rolls having a smooth surface were arranged upstream of a spreader of a conventionally known laminator, and heating was possible by an electric heater. A particle board of 15 mm × 909 mm × 1818 mm as a base material was heated to 180 ° C. with the iron rolls facing each other at a linear pressure of 50 kg / cm, and passed at a speed of 30 m / min. Sent.
【００１６】スプレッダー内で、一方の表面に、最初に
塩化アンモニウム水溶液を硬化剤として０．５ｇ／尺2
塗布し、赤外線ヒータで硬化剤の水分をとばしたあと、
尿素樹脂系接着剤を２ｇ／尺2 で塗布した。接着剤を半
乾燥状態とし、次いで、化粧シートとして４５ｇ／ｍ2
の薄葉紙であるプレコート紙を接着剤を塗布した表面側
に熱ロールプレス間で貼り付けた。In the spreader, on one surface, first, an aqueous solution of ammonium chloride was used as a curing agent in an amount of 0.5 g / m 2.
After applying and blowing out the moisture of the curing agent with an infrared heater,
The urea resin-based adhesive was applied at 2 g / scale 2 . The adhesive was put into a semi-dry state, and then 45 g / m 2 as a decorative sheet
Was applied between the hot roll presses on the surface side on which the adhesive was applied.
【００１７】〔実施例２〕実施例１と同様であるが、接
着剤の塗布と化粧シートの貼り付けをパーティクルボー
ドの両面について行った。 〔実施例３〕基材として、２．７ｍｍ×９０９ｍｍ×１
８１８ｍｍの中質繊維板を用い、化粧シートとして３０
ｇ／ｍ2 のプレコート紙を用い、接着剤塗布量を主剤
１．０ｇ／尺2 、硬化剤０．２ｇ／尺2 とした以外は、
実施例１と同様にして化粧板を製造した。Example 2 As in Example 1, the application of an adhesive and the attachment of a decorative sheet were performed on both sides of the particle board. [Example 3] As a substrate, 2.7 mm x 909 mm x 1
Using 818 mm high quality fiberboard, 30
using precoated paper g / m 2, except that the adhesive application weight base resin 1.0 g / scale 2, and the curing agent 0.2 g / scale 2,
A decorative board was manufactured in the same manner as in Example 1.
【００１８】〔実施例４〕接着剤として尿素樹脂３：酢
酸ビニルエマルジョン７である尿素酢酸ビニルエマルジ
ョンを２ｇ／尺2 で塗布し、塗布後に、赤外線ヒーター
で乾燥させた以外は、実施例１と同様にして化粧板を製
造した。Example 4 Example 1 was repeated except that urea resin 3: vinyl acetate emulsion 7, a urea vinyl acetate emulsion 7 was applied as an adhesive at a rate of 2 g / scale 2 and dried with an infrared heater after the application. Similarly, a decorative board was manufactured.
【００１９】〔実施例５〕基材として１８ｍｍ×９０９
ｍｍ×１８１８ｍｍのパーティクルボードを用いたこ
と、接着剤としてエチレン酢酸ビニルエマルジョンを３
ｇ／尺2 で塗布したこと、化粧シートとして０．１５ｍ
ｍ厚の塩化ビニルシートを用いたこと以外は、実施例１
と同様にして化粧板を製造した。Example 5 18 mm × 909 as a base material
mm × 1818 mm particle board was used.
g / size 2 and 0.15m as decorative sheet
Example 1 except that a m-thick vinyl chloride sheet was used.
A decorative board was produced in the same manner as described above.
【００２０】〔比較例１〕実施例１と同様であるが、た
だし、鉄製ロールによる加圧と加熱は行わなかった。 〔比較例２〕接着剤塗布量４．５ｇ／尺2 とし、鉄製ロ
ールによる加圧と加熱は行わなかった以外は、実施例１
と同様にして化粧板を製造した。[Comparative Example 1] As Example 1, except that pressurization and heating with an iron roll were not performed. [Comparative Example 2] Example 1 was repeated except that the amount of adhesive applied was 4.5 g / size 2 and pressure and heating with an iron roll were not performed.
A decorative board was produced in the same manner as described above.
【００２１】〔比較〕各実施例品と比較例品について、
表面平滑性、表面チップダク発生の有無、接着不足等の
比較を行った。実施例品ではいずれも表面のチップダク
（ザラツキ）はなく、また、化粧シートの接着不良の発
生も皆無であった。比較例品では表面平滑性の悪化、表
面チップダク発生、接着不足の発生が多く見られた。[Comparison] For each example product and comparative example product,
The surface smoothness, the occurrence of surface chipping, the lack of adhesion, and the like were compared. In each of the examples, there was no chipping (roughness) on the surface, and no adhesion failure of the decorative sheet occurred. In the comparative example, surface smoothness was deteriorated, surface chipping occurred, and adhesion was insufficient.
【００２２】[0022]
【発明の効果】本発明の方法によれば、少ない接着剤塗
布量で接着不良のないかつ表面性の高い化粧板を得るこ
とができ、製造コストの低減に寄与することができる。
また、ホルマリン系接着剤を用いた場合、塗布量が少な
い分、ホルマリン放出量が低減できるという付随的効果
も奏される。According to the method of the present invention, it is possible to obtain a decorative plate having no adhesive failure and high surface properties with a small amount of adhesive applied, which can contribute to a reduction in manufacturing cost.
In addition, when a formalin-based adhesive is used, an additional effect that the amount of formalin released can be reduced by the small amount of application is also exerted.
【図１】本発明の方法の実施に用いるラミネータを説明
する図。FIG. 1 is a diagram illustrating a laminator used for carrying out a method of the present invention.
【図２】従来のラミネータを説明する図。FIG. 2 is a diagram illustrating a conventional laminator.
１０…基材（木質板）、２０…加熱された表面平滑なロ
ール、１…スプレッダー、６…熱ロールプレス、７…化
粧シート。DESCRIPTION OF SYMBOLS 10 ... Base material (wood board), 20 ... Heated surface smooth roll, 1 ... Spreader, 6 ... Hot roll press, 7 ... Decorative sheet.
Claims (3)
レッダーにより接着剤を塗布した後、該接着剤塗布面に
化粧シートを連続的に貼り付けていくようにした木質板
を基材とする化粧板のラミネータによる製造方法であっ
て、該スプレッダーによる接着剤の塗布工程の前工程と
して、基材である木質板の一面又は両面を加熱された表
面平滑なロールによって加圧しながら加熱する工程を有
することを特徴とする化粧板のラミネータによる製造方
法。An adhesive is applied to one or both surfaces of a wooden board as a base material by a spreader, and a decorative board is continuously attached to the adhesive applied surface. A step of heating one side or both sides of a wooden board as a base material under pressure by a heated smooth surface roll as a pre-process of an adhesive application process using the spreader. A method for producing a decorative board using a laminator.
は、基材である木質板の一面又は両面にリグニンによる
シール層が形成される温度以上であることを特徴とする
請求項１記載の化粧板のラミネータによる製造方法。2. The decorative board according to claim 1, wherein a heating temperature of the roll having a smooth surface is equal to or higher than a temperature at which a sealing layer made of lignin is formed on one or both sides of a wooden board as a base material. Manufacturing method using a laminator.
は、基材である木質板素材のリグニンの熱軟化温度より
も約５０℃〜１５０℃高い温度であることを特徴とする
請求項１記載の化粧板のラミネータによる製造方法。3. The heating temperature of the roll having a smooth surface is about 50 ° C. to 150 ° C. higher than the thermal softening temperature of lignin of a wooden board material as a base material. A method of manufacturing a decorative board using a laminator.