JP3029558B2 - Manufacturing method of high gloss finish decorative board - Google Patents
Manufacturing method of high gloss finish decorative boardInfo
- Publication number
- JP3029558B2 JP3029558B2 JP7224400A JP22440095A JP3029558B2 JP 3029558 B2 JP3029558 B2 JP 3029558B2 JP 7224400 A JP7224400 A JP 7224400A JP 22440095 A JP22440095 A JP 22440095A JP 3029558 B2 JP3029558 B2 JP 3029558B2
- Authority
- JP
- Japan
- Prior art keywords
- board
- decorative board
- decorative
- resin
- adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【発明の属する技術分野】本発明はキッチン家具の扉や
ショーケースの棚板など垂直面の扉に用いられる高光沢
の化粧ボードの製造方法に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for manufacturing a high-gloss decorative board used for a door on a vertical surface such as a door of kitchen furniture or a shelf of a showcase.
【０００２】[0002]
【従来の技術】キッチン家具の扉やショーケースの棚板
は近年光沢のあるものが好まれる傾向にある。従来の化
粧板は、プレス成形する際に、メラミン樹脂層に接触す
る中間板の光沢を研磨等により上げ、その光沢を化粧板
表面の転写することにより生産していたが、ステンレス
の研磨を十分に実施しても化粧板の加熱成形中に、表面
が“梨地模様”となってしまう。また、最近、塩化ビニ
ルシートのメンブレムプレスによる高光沢化粧板が提案
されているが、表面にキズがつきやすいなどの欠点があ
る。2. Description of the Related Art In recent years, glossy furniture doors and showcase shelves have tended to be preferred. The conventional decorative plate was produced by polishing the intermediate plate in contact with the melamine resin layer by polishing or the like during press molding and transferring the gloss to the surface of the decorative plate. However, the surface of the veneer has a "pattern" during the hot forming of the decorative plate. Recently, a high-gloss decorative board made of a vinyl chloride sheet using a membrane press has been proposed, but has a drawback that the surface is easily scratched.
【０００３】化粧板は主に、合板、ＭＤＦ、パーチクル
ボードなどの木質系ボードに貼り、化粧ボードとしてキ
ッチン家具の扉やショーケースの棚板に使用され、その
加工方法は一般には木質系ボードに酢酸ビニル系接着
剤、エチレン酢酸ビニル系接着剤又はゴム系接着剤を化
粧板並びに木質系ボード双方に塗布し貼り合わせる。こ
の方法では接着剤に含有される水分が木質系ボードに吸
収され、微細な凹凸ができ、あるいは、接着剤の塗りム
ラによって化粧板に部分な微細凹凸が発生することが多
い。[0003] Decorative boards are mainly attached to wood-based boards such as plywood, MDF and particle board, and are used as decorative boards for doors of kitchen furniture and shelf boards of showcases. A vinyl-based adhesive, an ethylene-vinyl acetate-based adhesive or a rubber-based adhesive is applied to both the decorative board and the wood-based board and bonded. In this method, moisture contained in the adhesive is absorbed by the wooden board, and fine unevenness is often formed, or uneven fineness of the adhesive often causes partial fine unevenness on the decorative board.
【０００４】従来の化粧板では、このような方法でも、
化粧板自体が持つ凹凸のため化粧板の外観を損なうこと
なく化粧ボードを加工することが可能であったが、本発
明に用いる熱変形温度が８０〜１２０℃の熱可塑性フィ
ルムを使用し、その上に熱硬化性樹脂を含浸した紙基
材、更に表面にメラミン樹脂含浸紙基材を重ね、加熱加
圧成形してなる高光沢メラミン化粧板のように、表面の
微細な凹凸がない化粧板を木質ボードに貼り合わせる場
合には接着剤の微細な凹凸の有無が化粧ボード表面に著
しく影響し、十分な高光沢調表面が得られないことが多
い。[0004] In the conventional decorative board, even in such a method,
Although it was possible to process the decorative board without impairing the appearance of the decorative board due to the unevenness of the decorative board itself, the heat deformation temperature used in the present invention was 80 to 120 ° C using a thermoplastic film. A decorative board with no fine irregularities on the surface, such as a high-gloss melamine decorative board made by laminating a paper base material impregnated with a thermosetting resin on top of it and further laminating a melamine resin-impregnated paper base material on the surface and heating and pressing. In the case where is bonded to a wooden board, the presence or absence of fine irregularities of the adhesive significantly affects the surface of the decorative board, and a sufficiently high glossy surface cannot be obtained in many cases.
【０００５】目止めパテなどで微細な凹凸を防止する方
法があるが、この方法は、本来、基材の目ヤセや凹凸を
防止するもので、全面に行なうには大幅なコストアップ
となることや、化粧板を貼り合わせる場合は接着力が十
分に発現せず好ましい方法とはいえない。[0005] There is a method of preventing fine irregularities by using a putty putty or the like, but this method is originally intended to prevent the base material from being damaged or uneven, and the cost is greatly increased when the method is applied to the entire surface. In addition, when a decorative plate is bonded, the adhesive strength is not sufficiently exhibited, which is not a preferable method.
【０００６】[0006]
【発明が解決しようとする課題】このように、本発明
は、従来の化粧ボードの製造方法では難しかった高光沢
仕上げの化粧ボードの生産を可能にするものである。As described above, the present invention enables the production of a decorative board having a high gloss finish, which has been difficult with the conventional method of manufacturing a decorative board.
【０００７】[0007]
【課題を解決するための手段】本発明は、熱硬化性樹脂
を含浸した紙基材の上に、熱変形温度が８０〜１２０℃
である熱可塑性フィルムを配し、熱硬化性樹脂を含浸し
た紙基材を配し、更に表面にメラミン樹脂含浸紙基材を
重ね、加熱加圧成形してなるメラミン樹脂化粧板を木質
系ボードに貼り合わせるに際し、前記木質系ボード表面
をポリイソシアネート樹脂でプライマー処理することを
特徴とする高光沢仕上げ化粧ボードの製造方法、に関す
るものである。According to the present invention, a heat-curing resin is impregnated on a paper substrate impregnated with a thermosetting resin at a heat deformation temperature of 80 to 120 ° C.
A melamine resin decorative board made by placing a thermoplastic film that is a thermosetting resin impregnated paper base A process for producing a high-gloss finish decorative board, wherein the surface of the wooden board is subjected to a primer treatment with a polyisocyanate resin.
【０００８】本発明者等は、木質系ボードの表面をポリ
イソシアネートによりプライマー処理すれば、防湿効果
を発揮すること、及びポリイソシアネート樹脂の−ＮＣ
Ｏ基と酢酸ビニル系接着剤中の−ＣＯＯＨ基とが反応す
ることに着目し、木質系ボード表面にポリイソシアネー
ト樹脂を塗工し、硬化した後、接着剤を化粧板及び木質
系ボードに塗工し、両者を貼り合わせる技術を開発した
ものである。用いる接着剤としてはエポキシ樹脂系、ゴ
ム系、ポリ酢酸ビニル系、エチレン・酢酸ビニル共重合
系など、いずれの接着剤を用いても良いが、作業性、接
着力を考慮し、更に前記の理由により、ポリ酢酸ビニル
系又はエチレン酢酸ビニル共重合系の接着剤が好まし
い。用いる木質系ボードは合板、ＭＤＦ、パーチクルボ
ードのいずれでも良い。The present inventors have found that if the surface of a wooden board is treated with a primer with a polyisocyanate, a moisture-proof effect can be exhibited, and -NC of the polyisocyanate resin can be obtained.
Focusing on the reaction between the O group and the -COOH group in the vinyl acetate-based adhesive, a polyisocyanate resin is applied to the surface of the wooden board and cured, and then the adhesive is applied to the decorative board and the wooden board. And developed a technology to bond them together. As the adhesive to be used, any adhesive such as an epoxy resin-based, rubber-based, polyvinyl acetate-based, ethylene-vinyl acetate-based copolymer-based adhesive may be used. Accordingly, a polyvinyl acetate-based or ethylene-vinyl acetate copolymer-based adhesive is preferred. The wood board used may be any of plywood, MDF and particle board.
【０００９】熱可塑性フィルムは熱変形温度が８０〜１
２０℃である。この範囲の熱変形温度であれば、成形時
の接着性と得られた化粧板の光沢及び耐熱性とが両立
し、木質系ボードに貼り合わせた化粧ボードは優れた光
沢を有し、他の特性も優れている。この熱可塑性フィル
ムは、厚さ１００〜２５０μｍのＡＢＳフィルムが接着
力及び光沢の維持のために好ましい。The thermoplastic film has a heat distortion temperature of 80 to 1
20 ° C. With a heat deformation temperature in this range, the adhesiveness at the time of molding and the gloss and heat resistance of the obtained decorative board are compatible, and the decorative board bonded to the wooden board has excellent gloss, The characteristics are also excellent. As the thermoplastic film, an ABS film having a thickness of 100 to 250 μm is preferable for maintaining adhesion and gloss.
【００１０】[0010]
【発明の実施の形態】図１は本発明の高光沢化粧板の概
略断面図であり、熱硬化性樹脂含浸基材からなる芯材層
（３）と（５）との間に、熱可塑性フィルム（４）を重
ね合わせ、次に、メラミン樹脂含浸基材からなる化粧層
（２）と、薄いメラミン樹脂含浸基材からなる表面層
（１）を順次重ね、必要により芯材層（３）と化粧層
（２）との間に遮蔽層を挿入し全体を加熱加圧すること
により一体化されている。DESCRIPTION OF THE PREFERRED EMBODIMENTS FIG. 1 is a schematic sectional view of a high-gloss decorative board according to the present invention, in which a thermoplastic material is inserted between core layers (3) and (5) made of a thermosetting resin-impregnated base material. The film (4) is overlaid, and then the decorative layer (2) made of a melamine resin-impregnated base material and the surface layer (1) made of a thin melamine resin-impregnated base material are sequentially stacked, and if necessary, a core material layer (3) The shielding layer is inserted between the and the decorative layer (2), and the whole is heated and pressed to be integrated.
【００１１】次に、図２はこの化粧板（６）を木質系ボ
ード（１０）に貼り合わせた化粧ボードの一例の概略断
面図であり、木質系ボードの表面をロールコーター又は
刷毛塗り等でポリイソシアネート樹脂（９）を１．５〜
２ｇ／３００×３００ｍｍ2塗工し、４時間以上風乾し
た後、化粧板と木質系ボードにそれぞれに酢酸ビニル系
接着剤（７、８）を４〜５ｇ／３００×３００ｍｍ2 塗
工し、化粧板と木質系ボードを貼り合わせる。なお、接
着剤塗工方法としては塗工量の調節の容易さからロール
コーターによる方法が好ましい。Next, FIG. 2 is a schematic sectional view of an example of a decorative board in which the decorative board (6) is bonded to a wooden board (10). The surface of the wooden board is coated with a roll coater or a brush. 1.5 to 1.5 polyisocyanate resin (9)
After applying 2 g / 300 × 300 mm 2 and air-drying for 4 hours or more, apply a 4-5 g / 300 × 300 mm 2 of vinyl acetate adhesive (7, 8) to the decorative board and the wooden board, respectively, Attach the board and the wooden board. In addition, as a method of applying the adhesive, a method using a roll coater is preferable because of easy adjustment of the amount of application.
【００１２】本発明において、木質系ボードを防湿する
ために用いられるポリイソシアネート樹脂としては、Ｔ
ＤＩ系、ＨＤＩ系、ＩＰＤＩ系のいずれでも良い。ま
た、ポリイソシアネート樹脂を塗工後４時間以上風乾す
ることが好ましい。塗工後すぐに接着剤を塗工した場合
は塗膜の形成が十分でなく防水効果が小さく、接着剤中
の水分がボードへ浸透するのを防止する効果が十分に発
揮できないため、化粧板を貼り合わせた後の微細な凹凸
を完全になくすることはできない。In the present invention, as a polyisocyanate resin used for moisture-proofing a wood board, T is used.
Any of DI system, HDI system, and IPDI system may be used. In addition, it is preferable to air dry the polyisocyanate resin for 4 hours or more after coating. If the adhesive is applied immediately after coating, the coating is not sufficiently formed and the waterproof effect is small, and the effect of preventing the moisture in the adhesive from permeating the board cannot be sufficiently exhibited. However, it is not possible to completely eliminate the fine irregularities after bonding.
【００１３】[0013]
《実施例１》坪量１９５ｇ／ｍ2 のクラフト紙に水溶性
フェノール樹脂を含浸乾燥して得た樹脂分３５％の含浸
紙１枚の上に、厚さ１５０μｍ、熱変形温度１００℃で
あるＡＢＳフィルムを重ね、次に、前記と同じ含浸紙１
枚、及び坪量１２０ｇ／ｍ2の化粧紙にメラミン樹脂を
含浸乾燥して得た樹脂分５０％の化粧層を順次重ね合わ
せ、その化粧層にステンレス板として光沢度計での測定
値が３００以上である鏡面仕上げのステンレス鋼板を重
ね、１６０℃、１００ｋｇ／ｃｍ2 の条件で加熱加圧成
形し、厚さ０．７ｍｍの高光沢のメラミン樹脂化粧板を
得た。この化粧板の裏面をサンドペーパーによりサンデ
ィング処理をし、酢酸ビニル系接着剤（積水化学製 エ
スダイン ５４０１Ｗ）を４〜５ｇ／３００×３００ｍ
ｍ2 ロールコーターにより塗工した。一方、木質系ボー
ドとしてＭＤＦを使用し、その表面に、ＴＤＩ系ポリイ
ソシアネート樹脂（住友バイエル製 Ｌ−７５）を１ｇ
／３００×３００ｍｍ2 ロールコーターにより塗工し、
４時間風乾した後、酢酸ビニル系接着剤（積水化学製
エスダイン ５４０１Ｗ）を４〜５ｇ／３００×３００
ｍｍ2 ロールコーターにより塗工し、化粧板とＭＤＦを
貼り合わせ高光沢の化粧ボードを得た。Example 1 A kraft paper having a basis weight of 195 g / m 2 was impregnated with a water-soluble phenol resin and dried on a piece of impregnated paper having a resin content of 35%, which had a thickness of 150 μm and a heat deformation temperature of 100 ° C. Overlay the ABS film, then impregnated paper 1 as above
A decorative layer having a resin content of 50% obtained by impregnating and drying a melamine resin on a piece of paper and a decorative paper having a basis weight of 120 g / m 2 is sequentially superimposed on each other. The mirror-finished stainless steel plates as described above were stacked, and heated and pressed under the conditions of 160 ° C. and 100 kg / cm 2 to obtain a 0.7-mm thick high-gloss melamine resin decorative plate. The back surface of this decorative board is sanded with sandpaper, and 4-5 g of vinyl acetate-based adhesive (ESDUINE 5401W manufactured by Sekisui Chemical) / 300 × 300 m
It was coated by m 2 roll coater. On the other hand, MDF was used as a wood-based board, and 1 g of TDI-based polyisocyanate resin (L-75 manufactured by Sumitomo Bayer) was applied to the surface of the board.
/ 300 × 300mm Coating with 2 roll coater,
After air drying for 4 hours, use a vinyl acetate adhesive (Sekisui Chemical
Esdine 5401W) 4-5g / 300x300
Coating was performed with a mm 2 roll coater, and a decorative board and MDF were bonded to obtain a high-gloss decorative board.
【００１４】《実施例２》実施例１において、ＭＤＦに
塗工するポリイソシアネート樹脂としてＨＤＩ系ポリイ
ソシアネート樹脂（住友バイエル製 Ｎ−７５）を使用
する以外は実施例１と全く同様にして高光沢の化粧ボー
ドを得た。Example 2 High gloss was obtained in the same manner as in Example 1 except that an HDI-based polyisocyanate resin (N-75 manufactured by Sumitomo Bayer) was used as the polyisocyanate resin applied to the MDF. I got a makeup board.
【００１５】《比較例１》化粧板を得るまでは実施例と
全く同様にし、酢酸ビニル系接着剤を７〜８ｇ／３００
×３００ｍｍ2 ロールコーターにより塗工した。ＭＤＦ
に対してはポリイソシアネート樹脂によるプライマー処
理をせず、酢酸ビニル系接着剤を７〜８ｇ／３００×３
００ｍｍ2 ロールコーターにより塗工し、両者を貼り合
わせ化粧ボードを得た。<< Comparative Example 1 >> Until a decorative plate was obtained, the same procedure as in the Example was carried out.
Coating was performed with a × 300 mm 2 roll coater. MDF
No primer treatment with a polyisocyanate resin, and 7-8 g of vinyl acetate adhesive / 300 × 3
Coating was performed with a 00 mm two- roll coater, and both were laminated to obtain a decorative board.
【００１６】《比較例２》坪量１９５ｇ／ｍ2 のクラフ
ト紙に水溶性フェノール樹脂を含浸乾燥して得た樹脂分
３５％の含浸紙を３枚重ね、更に、坪量１２０ｇ／ｍ2
の化粧紙にメラミン樹脂を含浸乾燥して得た樹脂分５０
％の化粧層を重ね合わせ、その化粧層にステンレス板と
して光沢度計による測定値が３００以上である鏡面仕上
げのステンレス鋼板を重ね、１６０℃、１００ｋｇ／ｃ
ｍ2 の条件で加熱加圧成形し、厚さ０．８ｍｍの化粧板
を得、裏面をサンドペーパーによりサンディング処理を
し、酢酸ビニル系接着剤を７〜８ｇ／３００×３００ｍ
ｍ2 ロールコーターにより塗工する。また、ＭＤＦに対
してはポリイソシアネート樹脂によるプライマー処理を
せず、酢酸ビニル系接着剤を７〜８ｇ／３００×３００
ｍｍ2 ロールコーターにより塗工し、両者を貼り合わせ
化粧ボードを得た。[0016] "Comparative Example 2" basis weight 195 g / m 2 kraft paper three sheets of water-soluble phenolic resin impregnated dry resin content of 35% of the impregnated paper obtained, further, a basis weight of 120 g / m 2
Resin obtained by impregnating and drying melamine resin on decorative paper
% Of a decorative layer, and a mirror-finished stainless steel plate having a value measured by a gloss meter of 300 or more as a stainless steel plate is superimposed on the decorative layer at 160 ° C. and 100 kg / c.
heated pressure molding under the conditions of m 2, to obtain a veneer having a thickness of 0.8 mm, and the sanding process by sand paper backside, 7~8g / 300 × 300m vinyl acetate-based adhesive
The m 2 roll coater to a coating. Further, MDF is not subjected to a primer treatment with a polyisocyanate resin, and a vinyl acetate-based adhesive is used in an amount of 7 to 8 g / 300 × 300.
Coating was performed using a mm 2 roll coater, and both were laminated to obtain a decorative board.
【００１７】得られた各化粧ボードについて、加工後の
外観、化粧板の平面引張り強度について、ＪＡＳの試験
方法に準じて評価し、表１に示す結果を得た。なお、表
面化粧層はグラビア印刷紙を使用した。The appearance of each decorative board after processing and the planar tensile strength of the decorative board were evaluated according to the JAS test method, and the results shown in Table 1 were obtained. The surface decorative layer used was gravure printing paper.
【００１８】 表 １ ───────────────────────────── 加工後の外観 平面引張り強度（kg/cm2) ───────────────────────────── 実施例１ 高光沢で表面平滑 ４以上 実施例２ 高光沢で表面平滑 ４以上 比較例１ 梨地模様の傾向あり ４以上 比較例２ 表面にうねり発生 ４以上 ─────────────────────────────Table 1 外 観 Appearance after processing Plane tensile strength (kg / cm 2 ) ─── ────────────────────────── Example 1 High gloss and smooth surface 4 or more Example 2 High gloss and smooth surface 4 or more Comparative Example 1 Nashiji There is a tendency of pattern 4 or more Comparative Example 2 Swelling on the surface 4 or more ─────────────────────────────
【００１９】実施例では、接着剤による微細な凹凸を防
止することによって、高光沢で、表面が平滑な化粧ボー
ドを得ることができた。また、平面引っ張り強度もＪＡ
Ｓ規格の４ｋｇ／ｃｍ2 以上をクリアしている。In the example, a decorative board having a high gloss and a smooth surface could be obtained by preventing fine irregularities due to the adhesive. Also, the plane tensile strength is JA
Clears S standard of 4 kg / cm 2 or more.
【００２０】[0020]
【発明の効果】本発明の高光沢化粧ボードの製造方法
は、従来の化粧ボードの木質系ボードへの貼りつけ方法
では、接着剤の微細な凹凸によって、活かされなかった
化粧板の高光沢、及び平滑性を十分に発現した化粧ボー
ドを提供することができる。得られた化粧ボードは、高
級感が要求されるシステムキッチン扉、ショーケースの
棚板等として好適であり、また、接着剤の使用量を半分
程度とすることができることから、加工コストを大きく
削減できる。The method for producing a high-gloss decorative board of the present invention is based on the conventional method of attaching a decorative board to a wood-based board. In addition, a decorative board sufficiently exhibiting smoothness can be provided. The obtained decorative board is suitable for system kitchen doors and showcase shelves, etc., which require a sense of luxury, and the amount of adhesive used can be reduced to about half, thereby greatly reducing processing costs. it can.
【図面の簡単な説明】[Brief description of the drawings]
【図１】 本発明の高光沢化粧板の一例の概略断面図FIG. 1 is a schematic cross-sectional view of an example of a high gloss decorative board of the present invention.
【図２】 本発明の高光沢化粧ボードの一例の概略断面
図FIG. 2 is a schematic sectional view of an example of the high gloss decorative board of the present invention.
１ 表面層 ２ 化粧層 ３ 芯材層 ４ 熱可塑性フィルム ５ 芯材層 ６ 化粧板 ７ 酢酸ビニル系接着剤層 ８ 酢酸ビニル系接着剤層 ９ ポリイソシアネート樹脂プライマー層 １０ 木質系ボード DESCRIPTION OF SYMBOLS 1 Surface layer 2 Decorative layer 3 Core material layer 4 Thermoplastic film 5 Core material layer 6 Decorative board 7 Vinyl acetate adhesive layer 8 Vinyl acetate adhesive layer 9 Polyisocyanate resin primer layer 10 Wood board
───────────────────────────────────────────────────── フロントページの続き (56)参考文献 特開 平２−155732（ＪＰ，Ａ) 特開 昭56−19757（ＪＰ，Ａ) 特開 平５−140339（ＪＰ，Ａ) 特開 平８−90508（ＪＰ，Ａ) 特開 平７−178864（ＪＰ，Ａ) 特開 平８−34094（ＪＰ，Ａ) 特開 平９−39191（ＪＰ，Ａ) 特開 平９−29893（ＪＰ，Ａ) 特開 平５−318669（ＪＰ，Ａ) 特開 平７−108647（ＪＰ，Ａ) (58)調査した分野(Int.Cl.7，ＤＢ名) B32B 1/00 - 35/00 ────────────────────────────────────────────────── ─── Continuation of the front page (56) References JP-A-2-155732 (JP, A) JP-A-56-19757 (JP, A) JP-A-5-140339 (JP, A) JP-A 8- 90508 (JP, A) JP-A-7-178864 (JP, A) JP-A-8-34094 (JP, A) JP-A-9-39191 (JP, A) JP-A-9-29893 (JP, A) JP-A-5-318669 (JP, A) JP-A-7-108647 (JP, A) (58) Fields investigated (Int. Cl. 7 , DB name) B32B 1/00-35/00
Claims (2)
熱変形温度が８０〜１２０℃である熱可塑性フィルムを
配し、熱硬化性樹脂を含浸した紙基材を配し、更に表面
にメラミン樹脂含浸紙基材を重ね、加熱加圧成形してな
るメラミン樹脂化粧板を木質系ボードに貼り合わせるに
際し、前記ボード表面をポリイソシアネート樹脂でプラ
イマー処理することを特徴とする高光沢仕上げ化粧ボー
ドの製造方法。1. A paper base material impregnated with a thermosetting resin,
A thermoplastic film having a heat deformation temperature of 80 to 120 ° C. is provided, a paper base material impregnated with a thermosetting resin is provided, and a melamine resin-impregnated paper base material is further laminated on the surface, and heated and pressed. A method for producing a decorative board having a high gloss finish, characterized in that when the decorative melamine resin board is bonded to a wooden board, the board surface is subjected to a primer treatment with a polyisocyanate resin.
ｍのＡＢＳフィルムである請求項１記載の化粧ボードの
製造方法。2. A thermoplastic film having a thickness of 60 to 150 μm.
2. The method for producing a decorative board according to claim 1, wherein the decorative board is an ABS film.