JPH10102436A - Optical guidance sheet by inorganic ceramic light emitter - Google Patents
Optical guidance sheet by inorganic ceramic light emitterInfo
- Publication number
- JPH10102436A JPH10102436A JP8281767A JP28176796A JPH10102436A JP H10102436 A JPH10102436 A JP H10102436A JP 8281767 A JP8281767 A JP 8281767A JP 28176796 A JP28176796 A JP 28176796A JP H10102436 A JPH10102436 A JP H10102436A
- Authority
- JP
- Japan
- Prior art keywords
- aggregate
- sheet
- light emitting
- luminescent
- inorganic ceramic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【0001】[0001]
【発明の属する技術分野】本発明は、道路、床や階段等
の人が歩行し、或いは車が走行する場所において、夜間
或いは停電時の暗い状態で発光することで安全に歩行又
は走行誘導できる視線誘導シートに関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a line of sight in which a person walking on a road, a floor, a stair, or the like, or a vehicle running, emits light in a dark state at night or at the time of a power outage so that walking or traveling can be guided safely. It relates to a guide sheet.
【0002】[0002]
【従来の技術】従来、床や階段等の人の歩行する通路等
に使用されているシートは、滑り止めの役割を確保した
ものであるが、近年、災害等の停電時の安全確保のため
発光性材料を使用して、避難誘導するものが研究されて
いる。2. Description of the Related Art Conventionally, seats used for walking paths such as floors and stairs have a role of preventing slippage, but in recent years, light is emitted to ensure safety during a power failure such as a disaster. Evacuation guidance has been studied using conductive materials.
【0003】しかしながら、発光性材料はそのままでは
加水分解すると共に、耐候性が不良なため一般に塗料に
して使用され、発光性材料を樹脂中に混入して板状壁面
材として誘導効果の必要な部位に使用され始めている。
しかし、樹脂系の発光材料では、耐候性、耐磨耗性に弱
く耐久性に劣ることから床等の歩行面の使用に困難であ
る問題点があった。However, since the luminescent material is hydrolyzed as it is and has poor weather resistance, it is generally used as a paint, and the luminescent material is mixed into a resin and a portion requiring an induction effect as a plate-like wall material is required. It has begun to be used.
However, the resin-based luminescent material has a problem that it is difficult to use a walking surface such as a floor due to poor weather resistance and abrasion resistance and poor durability.
【0004】[0004]
【発明が解決しようとする課題】そこで本発明は、耐磨
耗性、耐候性に優れて発光性材料の耐久性を向上させる
ことで、人の歩行や車の通行部位に使用でき、発光性骨
材による誘導で夜間或いは停電時の安全歩行走行及び避
難誘導できるシートを提供するものである。SUMMARY OF THE INVENTION Accordingly, the present invention can be used for human walking and car traffic by improving the durability of a luminescent material having excellent wear resistance and weather resistance. An object of the present invention is to provide a seat capable of guiding safe walking and evacuation at night or during a power failure by guidance using aggregates.
【0005】[0005]
【課題を解決するための手段】このため本発明は、道
路、床、階段等の通路等に配置するものであり、光の照
射を受けて発光特性を発揮する発光物質を含有させて成
る無機質セラミック発光体を発光性骨材として、プラス
チックシートや布等のシート材の表面に固着させて成
り、該発光性骨材の配置によって示される誘導路或いは
標示を視認できる構成の無機質セラミックス発光体によ
る視線誘導シートである。なお、発光性骨材を硬質セラ
ミックスや石材等のスリップ防止用骨材に混合してシー
ト材の表面に固着してもよい。SUMMARY OF THE INVENTION Accordingly, the present invention provides an inorganic material which is disposed on a passage such as a road, a floor, a stair, or the like, and which contains a luminescent material which exhibits luminescent characteristics when irradiated with light. A ceramic luminous body is used as a luminous aggregate, which is fixed to the surface of a sheet material such as a plastic sheet or cloth, and an inorganic ceramic luminous body having a configuration in which a guide path or a sign indicated by the arrangement of the luminous aggregate can be visually recognized. It is a gaze guidance sheet. The luminescent aggregate may be mixed with a non-slip aggregate such as hard ceramics or stone, and fixed to the surface of the sheet material.
【0006】[0006]
【発明の実施の形態】以下、本発明の形態例を説明す
る。図1において、1はシート材、2は接着剤層、3は
発光性骨材、4はスリップ防止用骨材である。シート材
1は、プラスチック、布、不織布、布と紙の混合材等で
ある。また、接着剤2はフェノール樹脂系或いは各種合
成樹脂接着剤でもよい。DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, embodiments of the present invention will be described. In FIG. 1, 1 is a sheet material, 2 is an adhesive layer, 3 is a luminescent aggregate, and 4 is an anti-slip aggregate. The sheet material 1 is a plastic, cloth, nonwoven fabric, a mixed material of cloth and paper, or the like. Further, the adhesive 2 may be a phenol resin-based adhesive or various synthetic resin adhesives.
【0007】さらに発光性骨材3は、セラミック母材に
発光物質を含有させて成る無機質セラミック発光体であ
り、発光物質としては無機質蛍光体や蓄光性蛍光体の粉
砕体であればよく、硫化物、リン酸塩系、珪酸塩系、ア
ルミン酸塩系等が使用できるのである。また、セラミッ
ク母材としてはシリカやアルミナを含んだ低融点セラミ
ックスの粉砕体がよい。The luminous aggregate 3 is an inorganic ceramic luminous body comprising a ceramic base material containing a luminous substance. The luminous substance may be a pulverized inorganic phosphor or phosphorescent phosphor. Substances, phosphates, silicates, aluminates and the like can be used. Further, as the ceramic base material, a pulverized body of low melting point ceramic containing silica or alumina is preferable.
【0008】そして、セラミック母材に対して発光物質
を5〜50重量%混合して焼成し、これを粉砕して粒状
とした無機質セラミック発光体を発光性骨材3とするも
のであり、発光物質がセラミック母材に包まれた状態で
ある。発光性骨材3の大きさは直径約0.5〜3.3mm
である。この無機質セラミック発光体の発光性骨材
は、前の出願に開示してある。Then, a luminescent substance is mixed with the ceramic base material in an amount of 5 to 50% by weight and fired, and the resulting mixture is pulverized into a granular inorganic ceramic luminescent material to form a luminescent aggregate 3. The substance is wrapped in a ceramic matrix. The size of the luminescent aggregate 3 is about 0.5 to 3.3 mm in diameter.
It is. The luminescent aggregate of this inorganic ceramic luminous body has been disclosed in a previous application.
【0009】なお、スリップ防止用骨材4は、アルミ
ナ、炭化珪素やエミリー等通常使用されている磁器質粒
子やセラミックス粒子が用いられ、その大きさは直径約
0.5〜3.3mm である。そして、シート材の表面に
接着剤2を散布し、発光性骨材3とスリップ防止用骨材
4の混合物を接着剤層の上に散布して発光性骨材3とス
リップ防止用骨材4とを表面に露呈させて固着するので
ある。The slip preventing aggregate 4 is made of generally used porcelain particles or ceramic particles such as alumina, silicon carbide or Emily, and has a diameter of about 0.5 to 3.3 mm. . Then, the adhesive 2 is sprayed on the surface of the sheet material, and the mixture of the luminescent aggregate 3 and the slip preventing aggregate 4 is sprayed on the adhesive layer to form the luminescent aggregate 3 and the slip preventing aggregate 4. Is exposed to the surface and fixed.
【0010】この形態例によると、無機質セラミック発
光性骨材3と無機硬質材のスリップ防止用骨材4が高強
度な粒子状のため耐磨耗に優れており、且つ歩行に対し
て滑りを防止できるのである。また、夜間及び災害等の
停電時等において、発光性骨材3の発光特性により視線
誘導効果が生じるのである。したがって、通路面にシー
トを連続して接続することで夜間の歩行又は避難通路と
して発光し安全に誘導できるのである。According to this embodiment, the inorganic ceramic luminescent aggregate 3 and the inorganic hard anti-slip aggregate 4 are high-strength particles, so that they are excellent in wear resistance and slip on walking. It can be prevented. Further, at night or at the time of a power outage such as a disaster, a gaze guidance effect is generated by the light emitting characteristics of the light emitting aggregate 3. Therefore, by continuously connecting the seat to the passage surface, it is possible to emit light as a walking or evacuation passage at night and to guide the vehicle safely.
【0011】なお、本発明においては発光性骨材の素材
及び大きさは問わず、光の照射を受けて発光特性を発揮
する発光物質を含有させて成る無機質セラミック発光体
であればよく、その発光物質の含有量も限定されない。
また、発光性骨材とスリップ防止用骨材の混合割合も適
宜である。したがって、スリップ防止用骨材を混合しな
いで発光性骨材だけをシート材に固着してもよく、この
場合は強い発光によって視線誘導に優れるのである。In the present invention, regardless of the material and size of the luminescent aggregate, any inorganic ceramic luminous body containing a luminescent material that exhibits luminous characteristics upon being irradiated with light may be used. The content of the luminescent substance is not limited.
The mixing ratio of the luminescent aggregate and the slip preventing aggregate is also appropriate. Therefore, only the luminescent aggregate may be fixed to the sheet material without mixing the slip preventing aggregate, and in this case, the line of sight is excellent by strong light emission.
【0012】さらに、スリップ防止用骨材の素材及び大
きさも適宜であるが耐磨耗性に優れるものが適切であ
り、また適宜に着色してもよい。なお、シート材の素材
及び大きさも任意であり、薄いセラミックス板でもよ
く、フレキシブルなシート材でもよい。また、シートの
役割としては、床、階段等の通路自体の連続又は断続し
たた誘導路を形成する他、通路面での矢印や標示等の表
示面を形成する誘導シートでもよく、形成しようとする
表示状態に発光性骨材をシート材に露呈固着させればよ
い。さらに、施工し易いようにシートの裏部に接着剤を
塗布して剥離可能な離型紙を貼着してもよい。The material and size of the anti-slip aggregate are also appropriate, but those having excellent abrasion resistance are appropriate, and they may be appropriately colored. The material and size of the sheet material are also arbitrary, and may be a thin ceramic plate or a flexible sheet material. In addition, as the role of the sheet, in addition to forming a continuous or intermittent guideway of the passage itself such as a floor or a stair, a guide sheet forming a display surface such as an arrow or a sign on the passage surface may be used. The luminescent aggregate may be exposed and fixed to the sheet material in the display state to be performed. Furthermore, an adhesive may be applied to the back of the sheet and a release paper that can be peeled off may be adhered to facilitate the construction.
【0013】[0013]
【発明の効果】本発明の請求項1によると、発光性骨材
の発光によって夜間及び停電時の通路歩行或いは車の走
行が安全に誘導され、無機質セラミック発光体のため耐
候性及び耐磨耗性に優れて耐久性が向上するのである。
また請求項2では、滑り止めの路面が得られて安全行で
きるのである。According to the first aspect of the present invention, the light emission of the luminous aggregate safely guides the walking of the passage or the car at night or during a power failure, and the inorganic ceramic luminous body has weather resistance and abrasion resistance. It is excellent in durability and durability is improved.
According to the second aspect, a non-slip road surface is obtained, and the vehicle can be safely driven.
【0014】[0014]
【実施例1】組成が3(BuMg)O-8Al2O3で緑色の発光色の
紫外線蛍光材を30重量%と、セラミック母材を70重
量%配合し、850゜Cで30分焼成し炉内放冷して無
機質セラミック発光体を形成し、これを粒径3.3〜2.0mm
に粉砕して発光性骨材を得た。なお、セラミック母材の
組成は、SiO2が52.0重量%、Al2O3が5.3重量%、B2O3が
25.4重量%、Fe2O3が0.03重量%、TiO2が0.05重量%、C
aOが0.35重量%、K2Oが2.35重量%、Ng2Oが11.0重量
%、他3.52重量%である。And 30 wt% of green-emitting color UV fluorescing material in Example 1 composition 3 (BuMg) O-8Al 2 O 3, mixed with ceramic matrix 70 wt%, and baked 30 minutes at 850 ° C Allowed to cool in the furnace to form an inorganic ceramic luminous body, which has a particle size of 3.3 to 2.0 mm
To obtain a luminescent aggregate. The composition of the ceramic base material is as follows: SiO 2 is 52.0% by weight, Al 2 O 3 is 5.3% by weight, and B 2 O 3 is
25.4 wt%, Fe 2 O 3 0.03 wt%, TiO 2 is 0.05 wt%, C
aO 0.35 wt%, K 2 O is 2.35 wt%, Ng 2 O 11.0 wt%, other 3.52% by weight.
【0015】また、組成がSrAl2O4で緑色の発光色の蓄
光性蛍光材を30重量%と、前記のセラミック母材を7
0重量%配合し、850゜Cで30分焼成し炉内放冷し
て無機質セラミック発光体を形成し、これを粒径3.3〜
2.0mmに粉砕して発光性骨材を得た。Further, 30% by weight of a phosphorescent phosphor having a composition of SrAl 2 O 4 and emitting a green light is used, and the ceramic base material is used in an amount of 7% by weight.
0% by weight, baked at 850 ° C. for 30 minutes, and allowed to cool in a furnace to form an inorganic ceramic luminous body.
It was crushed to 2.0 mm to obtain a luminescent aggregate.
【0016】この二種類の発光性骨材夫々6Kg/m2を、
MMA樹脂をベースコートとして1.8Kg/m2接着した30
cm2のシート材上に散布し、その上にMMA樹脂をトッ
プコートとして0.2Kg/m2施して発光性骨材の上端部を少
し露出させて固着してシートを得る。Each of the two types of luminescent aggregates is 6 kg / m 2 ,
1.8 kg / m 2 bonded with MMA resin as base coat 30
It is spread on a sheet material of cm 2 , and 0.2 kg / m 2 of MMA resin is applied as a top coat on the sheet material so that the upper end portion of the luminescent aggregate is slightly exposed and fixed to obtain a sheet.
【0017】このシートを構内の道路上に停止ラインと
して施し、発光性の試験を行った。その結果、蛍光発光
性及びリン光発光性とも良好であった。なお、蛍光発光
性試験は、夜間10m離れた場所から自動車のヘッドラ
イトを照射してその発光性を目視にて評価したものであ
り、リン光発光性は夜間10m離れた場所から自動車の
ヘッドライトを1分間照射し、消灯3分後にその発光性
を目視にて評価したものである。This sheet was applied as a stop line on a road in the premises, and a light emission test was performed. As a result, both the fluorescence emission property and the phosphorescence emission property were good. The fluorescence emission test was conducted by irradiating a car headlight from a place 10 m away at night and visually evaluating its luminescence. Was irradiated for 1 minute, and the light emission was visually evaluated 3 minutes after the light was turned off.
【0018】他の実験において、紫外線蛍光材だけの発
光性骨材を用いた場合は、蛍光輝度が高く、一般道路用
の視線誘導シートとして有効であるが、消灯後はリン光
輝度は殆ど認められなかったのである。また、蓄光性蛍
光材だけの発光性骨材を用いた場合は、照射時の蛍光輝
度は低いが、消灯後のリン光輝度が高く田舎道のように
周囲に灯火がなく非常に暗い箇所では有効である。本例
では、紫外線蛍光材と蓄光性蛍光材とを併用しているた
め蛍光発光性及びリン光発光性とも優れたのである。In another experiment, when a luminous aggregate consisting only of an ultraviolet fluorescent material was used, the fluorescent luminance was high, and it was effective as a line-of-sight guide sheet for ordinary roads. It was not done. In addition, when a luminescent aggregate composed only of the phosphorescent phosphor is used, the fluorescent luminance at the time of irradiation is low, but the phosphorescent luminance after the light is turned off is high, and in a very dark place such as a country road, where there is no surrounding light such as a country road. It is valid. In this example, since the ultraviolet fluorescent material and the phosphorescent fluorescent material are used in combination, the fluorescent light emitting property and the phosphorescent light emitting property are excellent.
【0019】[0019]
【実施例2】実施例1で得られた蓄光性蛍光材を用いた
発光性骨材をさらに粉砕して粒径2.0〜1.0mmとし、高硬
質骨材である粒径2.0〜1.0mmの炭化珪素のスリップ防止
用骨材と夫々50重量%づつ混合し、これをMMA樹脂
をベースコートとして1.5Kg/m2接着したシート材上に4
Kg/m2散布し、さらにその上にMMA樹脂をトップコー
トとして0.2Kg/m2施して発光性骨材及びスリップ防止用
骨材の上端部を少し露出させて固着してシートを得た。Example 2 The luminescent aggregate using the phosphorescent material obtained in Example 1 was further pulverized to a particle size of 2.0 to 1.0 mm, and carbonized with a particle size of 2.0 to 1.0 mm, which is a high-hardness aggregate. Each was mixed with a silicon anti-slip aggregate at a ratio of 50% by weight, and this was mixed on a sheet material adhered to 1.5 kg / m 2 using MMA resin as a base coat.
Kg / m 2 by spraying, to obtain a sheet by fixing further on to slightly expose the upper portion of 0.2 Kg / m 2 applied to luminescent aggregate and slip preventing aggregate the MMA resin as a top coat thereon.
【0020】そして、このシートを6cm巾に裁断し、地
下道階段のステップ部に接着剤にて固着した。階段巾は
3m、段数20段で階段頭上4mに80Wの蛍光灯を2
個設置した。実験によると、4分間照射後消灯し、消灯
後15分間は十分なリン光輝度を示し、8時間後でも視
認可能であった。また、50重量%の一般硬質骨材によ
りステップのスリップ防止効果も十分認められた。Then, this sheet was cut into a width of 6 cm and fixed to the step portion of the underpass stairs with an adhesive. The width of the stairs is 3m, the number of steps is 20, and 2 fluorescent lamps of 80W are placed 4m above the stairs.
We installed individually. According to the experiment, it turned off after irradiation for 4 minutes, showed sufficient phosphorescent brightness for 15 minutes after turning off, and was visible even after 8 hours. In addition, the effect of preventing the step from slipping was sufficiently recognized by 50% by weight of the general hard aggregate.
【図1】本発明の一形態例を示す拡大縦断面図である。FIG. 1 is an enlarged vertical sectional view showing one embodiment of the present invention.
1 シート材 2 接着剤 3 発光性骨材 4 スリップ防止用骨材 DESCRIPTION OF SYMBOLS 1 Sheet material 2 Adhesive 3 Luminescent aggregate 4 Aggregate for slip prevention
Claims (2)
のであり、光の照射を受けて発光特性を発揮する発光物
質を含有させて成る無機質セラミック発光体を発光性骨
材として、プラスチックシートや布等のシート材の表面
に固着させて成り、該発光性骨材の配置によって示され
る誘導路或いは標示を視認できることを特徴とする無機
質セラミックス発光体による視線誘導シート。1. An inorganic ceramic luminous body which is disposed in a passage, such as a road, a floor, a staircase, etc., and which contains a luminous substance which exhibits luminous characteristics when irradiated with light, as a luminous aggregate. A line-of-sight guide sheet made of an inorganic ceramic luminous body, which is fixed to a surface of a sheet material such as a plastic sheet or a cloth, so that a guide path or a sign indicated by the arrangement of the luminescent aggregate can be visually recognized.
のスリップ防止用骨材に混合してシート材の表面に固着
した請求項1の視線誘導シート。2. The line-of-sight guide sheet according to claim 1, wherein the luminescent aggregate is mixed with a slip-preventing aggregate such as hard ceramics or stone and fixed to the surface of the sheet.