JPH0999638A - Recording sheet - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a recording sheet high in the adhesiveness of an ink receiving layer and a base material, excellent in absorbability of an ink receiving layer, high in ink drying properties and generating no curl in use environment, that is, excellent in curl resistance. SOLUTION: In a recording sheet 1 wherein an ink receiving layer is provided on at least the single surface of a base material sheet 2, a primer layer composed of a resin with Tg of -100-50 deg.C is provided between the base material sheet 2 and the ink receiving layer 4.

Description

【発明の詳細な説明】Detailed Description of the Invention

【０００１】[0001]

【発明の属する技術分野】本発明は、インク受容層の剥
がれることや、インク吸収時のインク受容層の浮き出し
がなく、耐カール性、画像の鮮明性に優れたインクジェ
ット記録用シートに関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an ink jet recording sheet excellent in curl resistance and image sharpness without peeling of the ink receiving layer or protrusion of the ink receiving layer during ink absorption. .

【０００２】[0002]

【従来の技術】従来、コンピューターやワードプロセッ
サーの出力プリントとして、ワイアードット記録方式、
感熱発色記録方式、感熱溶融転写記録方式、感熱昇華転
写記録方式、電子写真記録方式、インクジェット記録方
式等の種々の方式が開発されている。この中で、インク
ジェット記録方式は、記録シートとして普通紙を使用で
きること、プリントコストが安いこと、装置がコンパク
トで騒音がなく、高速記録が可能である等の特徴があ
る。このため、コンピューター等によって作製した文
字、図形などの画像情報を迅速かつ正確にアウトプット
するプリンターとしての利用が注目されている。また、
カラー化が容易で、絵柄が鮮明であることから、コンピ
ューターで作製した画像情報をインクジェットプリンタ
ーにより透明な記録シートに記録し、これをＯＨＰ等の
原稿として会議、各種学会発表等において利用する要求
も高まっている。2. Description of the Related Art Conventionally, as an output print of a computer or a word processor, a wire dot recording system,
Various systems such as a thermosensitive coloring recording system, a thermosensitive transfer recording system, a thermosensitive sublimation transfer recording system, an electrophotographic recording system, and an ink jet recording system have been developed. Among them, the ink jet recording method is characterized in that plain paper can be used as a recording sheet, the printing cost is low, the apparatus is compact and there is no noise, and high speed recording is possible. For this reason, attention has been paid to the use as a printer for quickly and accurately outputting image information such as characters and figures produced by a computer or the like. Also,
Since it is easy to colorize and the picture is clear, there is also a request to record image information produced by a computer on a transparent recording sheet with an inkjet printer and use it as a manuscript such as OHP at conferences and various academic conference presentations. It is rising.

【０００３】通常、インクジェットプリンターは、記録
用インクを微細な圧電素子（ピエゾ素子）の圧力、ある
いはサーマルヘッドの加熱によって発生するエアーの圧
力（バブルジェット）によってノズルから噴出し、記録
用シートに付着させることにより記録を行う。このた
め、インクジェット記録に使用される記録用インクとし
ては、インクの乾燥による粘度上昇に起因するノズルか
らのインク噴出不良を防止する為に、乾燥しにくいイン
クが用いられている。通常このインク成分は、染料、樹
脂、添加剤等を水およびアルコールに溶解したものが一
般的である。したがって、インクジェットプリンターで
記録を行う記録用シートは、付着したインクの液状分を
吸収し、インクを乾燥固化させることが要求される。こ
のため基材シート上にインク受容層を形成してインク吸
収性を高めた記録用シートが使用されている。In general, an ink jet printer ejects recording ink from a nozzle by pressure of a fine piezoelectric element (piezo element) or air pressure (bubble jet) generated by heating a thermal head, and adheres to a recording sheet. The recording is performed by causing the recording. For this reason, as a recording ink used for ink jet recording, an ink that is difficult to dry is used in order to prevent ink ejection failure from nozzles due to an increase in viscosity due to drying of the ink. Usually, this ink component is a dye, resin, additive, etc. dissolved in water and alcohol. Therefore, a recording sheet on which recording is performed by an inkjet printer is required to absorb the liquid component of the attached ink and dry and solidify the ink. For this reason, a recording sheet in which an ink receiving layer is formed on a base sheet to enhance ink absorption is used.

【０００４】特に、インクジェットプリンター用の記録
シートのインク受容層には次のような特性が要求され
る。 乾燥性：インクの吸収性に優れ、インク乾燥性が速い
こと。 画像鮮明性：適度なドットの広がりが得られ、にじみ
等のない鮮明な画像が得られること。 耐水性：水分が付着しても画像ににじみや流れ出しが
ないこと。 接着性：インク受容層が簡単に剥がれ落ちないこと。 耐カール性：使用環境においてインク受容層を含む記
録シートにカールを起こさないこと。 このような観点から従来の記録用シートは、基材シート
の上にインク受容層を備え、この受容層として、水溶性
樹脂を用いたもの、親水性樹脂を用いたもの等が考案さ
れている。In particular, the ink receiving layer of a recording sheet for an ink jet printer is required to have the following characteristics. Drying property: Excellent ink absorbency and fast ink drying property. Image clarity: An appropriate dot spread is obtained, and a clear image without blur is obtained. Water resistance: The image does not blur or run out even if moisture adheres. Adhesion: The ink receiving layer does not easily peel off. Curling resistance: Curling does not occur in the recording sheet including the ink receiving layer in the use environment. From such a point of view, conventional recording sheets have an ink receiving layer on a base sheet, and as the receiving layer, one using a water-soluble resin, one using a hydrophilic resin, etc. have been devised. .

【０００５】[0005]

【発明が解決しようとする課題】しかしながら、ポリビ
ニルアルコールやポリビニルピロリドンのような水溶性
樹脂を塗布して形成したインク受容層は、親水性が高く
画像の鮮明性は良好なものの、樹脂の親水性が高いた
め、基材として用いられるプラスチックフィルムとの接
着性が悪く、簡単に剥がれてしまうという問題点があっ
た。また、インク受容層が吸湿及び脱湿性を有するため
に、低湿環境下では筒状に丸まり、カールを引き起こす
という問題点があった。また、ポリビニルアセタールの
ような適度に疎水化された親水性樹脂を塗布して形成し
たインク受容層においても、基材として用いられるプラ
スチックフィルムとの接着性が悪く、親水性とはいえ水
溶性ではなく、逆に疎水性も備わっているために、イン
クとの馴染みが悪く、画像鮮明性が悪いという問題点を
有していた。However, although the ink receiving layer formed by coating a water-soluble resin such as polyvinyl alcohol or polyvinylpyrrolidone has high hydrophilicity and good image sharpness, the hydrophilicity of the resin is high. Therefore, there is a problem in that the adhesiveness to the plastic film used as the substrate is poor and the film is easily peeled off. Further, since the ink receiving layer has moisture absorption and dehumidification properties, there is a problem that it curls into a cylinder and curls in a low humidity environment. Further, even in the ink receiving layer formed by applying a hydrophilic resin which is appropriately hydrophobized such as polyvinyl acetal, the adhesiveness with the plastic film used as the base material is poor, and it is hydrophilic but water-soluble. On the contrary, since it also has hydrophobicity, it has a problem that it is not well compatible with ink and image sharpness is poor.

【０００６】本発明は、このような事情に鑑みて創案さ
れたものであり、インク受容層と基材シートとの接着性
が強く、使用する環境においてカールが発生しない、す
なわち、耐カール性の優れた記録用シートを提供するこ
とを目的とする。The present invention was devised in view of such circumstances, and the adhesiveness between the ink receiving layer and the base sheet is strong so that curling does not occur in the environment in which it is used, that is, curling resistance is high. It is intended to provide an excellent recording sheet.

【０００７】[0007]

【課題を解決するための手段】上記目的を達成するため
に、本発明は、基材シートの少なくとも片面に、インク
受容層を設けた記録用シートにおいて、基材シートとイ
ンク受容層の間に、Ｔｇが−１００℃〜５０℃の樹脂か
らなるプライマー層が設けられていることを特徴とす
る。また、基材シートが、熱可塑性プラスチックである
ことを特徴とする。In order to achieve the above object, the present invention provides a recording sheet in which an ink receiving layer is provided on at least one side of a base sheet, and the recording sheet is provided between the base sheet and the ink receiving layer. , Tg is −100 ° C. to 50 ° C., and a primer layer made of a resin is provided. Further, the substrate sheet is characterized by being a thermoplastic.

【０００８】本発明の作用は、以下の通りである。基材
シートの少なくとも片面に、インク受容層を設けた記録
用シートにおいて、基材シートとインク受容層の間に、
Ｔｇが−１００℃〜５０℃の樹脂からなるプライマー層
を設けているため、プラスチック基材とインク受容層の
両方への接着性が強くなる。また、プライマー層はＴｇ
が−１００℃〜５０℃の樹脂からなり、柔軟性を有する
ために、使用環境下でカールが起こらないものである。The operation of the present invention is as follows. In a recording sheet provided with an ink receiving layer on at least one side of the base sheet, between the base sheet and the ink receiving layer,
Since the primer layer made of a resin having Tg of −100 ° C. to 50 ° C. is provided, the adhesiveness to both the plastic substrate and the ink receiving layer becomes strong. The primer layer is Tg
Is made of a resin having a temperature of -100 ° C to 50 ° C and has flexibility, so that curling does not occur in the use environment.

【０００９】[0009]

【発明の実施の形態】以下に、本発明の実施の形態につ
いて、図面を参照しながら説明を行う。図１は、本発明
の記録用シートの一つの実施の形態を示す断面図であ
る。図１において、記録用シート１は、基材シート２
と、基材シート２の一方の面に形成されたプライマー層
３、及びその上にインク受容層４を備える。Embodiments of the present invention will be described below with reference to the drawings. FIG. 1 is a sectional view showing one embodiment of the recording sheet of the present invention. In FIG. 1, a recording sheet 1 is a base sheet 2
And a primer layer 3 formed on one surface of the base sheet 2 and an ink receiving layer 4 thereon.

【００１０】（基材シート）本発明の記録用シートで用
いられる基材シート２としては、従来の記録用シートに
使用されているものと同じ基材シートをそのまま用いる
ことが出来ると共に、その他のものも使用することが出
来、特に制限されない。ポリスチレン系等の合成紙、上
質紙、アート紙、コート紙、キャストコート紙、壁紙、
裏打用紙、合成樹脂含浸紙、エマルジョン樹脂含浸紙、
合成ゴムラテックス含浸紙、合成樹脂内添紙、板紙など
の着色または白色の各種紙やラベル用基材やプラスチッ
クフィルムなどが、あげられる。また、これらの材料を
２種以上貼り合わせた複合基材も使用される。これらの
基材シートの厚みは、用途に応じて、強度などを考慮し
て適宜選択され、特に制限されないが、例えば、通常５
０〜２００μｍ程度である。(Base Sheet) As the base sheet 2 used in the recording sheet of the present invention, the same base sheet as used in conventional recording sheets can be used as it is, and other base sheets can be used. Those can also be used and are not particularly limited. Synthetic paper such as polystyrene, fine paper, art paper, coated paper, cast coated paper, wallpaper,
Backing paper, synthetic resin impregnated paper, emulsion resin impregnated paper,
Examples include various colored or white papers such as synthetic rubber latex-impregnated papers, synthetic resin internal papers, paperboards, base materials for labels and plastic films. Further, a composite base material in which two or more of these materials are bonded together is also used. The thickness of these base material sheets is appropriately selected in consideration of strength and the like according to the application and is not particularly limited, but, for example, usually 5
It is about 0 to 200 μm.

【００１１】プラスチックフィルムでは、耐熱性、寸法
安定性、剛性を備えた熱可塑性プラスチックにより形成
されたものが好ましい。例えば、ポリエチレンテレフタ
レート樹脂、ポリカーボネート樹脂、アクリル樹脂、ポ
リ塩化ビニル樹脂、ポリプロピレン樹脂、ポリスチレン
樹脂、ポリビニルアルコール樹脂、ポリエチレン樹脂、
ジアセテート樹脂、トリアセテート樹脂、ポリイミド樹
脂等の厚さ５〜２５０μｍ程度、好ましくは５０〜１８
０μｍ程度のフィルム状あるいは板状のものがあげられ
る。特に、オーバーヘッドプロジェクター（ＯＨＰ）用
途で用いる場合は、これらのプラスチックフィルムでも
透明性のある基材シートが使用される。ＯＨＰ用途以外
の透明性を必要としない用途には、不透明なプラスチッ
クフィルムや紙などが用いられる。また、基材シートの
一方または両方の面に、必要に応じて、コロナ放電処理
や易接着処理を施してもよい。さらに、インク受容層を
形成していない基材シートの面にカール防止層を設けて
もよい。The plastic film is preferably made of thermoplastic resin having heat resistance, dimensional stability and rigidity. For example, polyethylene terephthalate resin, polycarbonate resin, acrylic resin, polyvinyl chloride resin, polypropylene resin, polystyrene resin, polyvinyl alcohol resin, polyethylene resin,
The thickness of diacetate resin, triacetate resin, polyimide resin, etc. is about 5 to 250 μm, preferably 50 to 18 μm.
A film or plate having a thickness of about 0 μm may be used. In particular, when used for an overhead projector (OHP), a transparent substrate sheet is used even for these plastic films. Opaque plastic films and papers are used for applications that do not require transparency other than OHP applications. Further, one or both surfaces of the base sheet may be subjected to a corona discharge treatment or an easy adhesion treatment as necessary. Further, an anti-curl layer may be provided on the surface of the base sheet on which the ink receiving layer is not formed.

【００１２】（プライマー層）基材シートの一方の面に
形成されたプライマー層３は、Ｔｇが−１００℃〜５０
℃の樹脂からなるものである。プライマー層３に用いる
Ｔｇが−１００℃〜５０℃の樹脂としては、例えば、ア
ルキッド樹脂、ポリエステル樹脂、ポリ酢酸ビニル樹
脂、塩ビ酢ビ共重合樹脂、ＮＢＲ樹脂、ＳＢＲ樹脂、ポ
リウレタン樹脂、アクリル系樹脂、ポリアミド等が単独
もしくは混合物、変性物として用いられる。変性物と
は、例えば、水酸基やカルボン酸、４級アンモニウム塩
含有モノマーを共重合もしくはグラフトさせて接着性、
親水性を上げたものなどである。Ｔｇが５０℃を越える
と、基材シート及びインク受容層との接着性が低下して
しまうため、好ましくない。また、耐カール性（クッシ
ョン性）も低下してしまう。また、Ｔｇが−１００℃よ
り低くなると、記録シートを重ねたり、ロール状で保存
したりすると、粘着性を帯び、ブロッキングが発生す
る。また、プライマー層の接着性、塗膜強度を向上させ
るために、上記の樹脂を各種硬化剤、例えばエポキシ樹
脂、メラミン樹脂、イソシアネート等により架橋させて
もよい。上述したプライマー層の形成方法は、従来公知
の種々の方法でよく、例えば、グラビアコート、グラビ
アリバースコート、ロールコート、ワイヤーバーコー
ト、ブレードコート、ナイフコート、エアーナイフコー
ト、コンマコート、スロットダイコート、ディップコー
ト等いずれの方法でもよい。プライマー層の構成する樹
脂に必要に応じて添加剤を加え、適当な溶剤に溶解ある
いは分散させた液を、基材シートにコーティングし、乾
燥して、プライマー層を設ける。プライマー層の厚み
は、乾燥時で、０．０１〜５０μｍ、好ましくは０．１
〜１０μｍとするのが良い。この厚みが、０．１μｍ未
満になると、接着性で十分な性能が発揮せず、一方で、
１０μｍを越えると、記録用シートを裁断時に端面がベ
タついてくる為、製造コストが高くつくと併せて、好ま
しくない。(Primer layer) The primer layer 3 formed on one surface of the base sheet has a Tg of -100 ° C to 50 ° C.
It is made of a resin of ℃. Examples of the resin having Tg of −100 ° C. to 50 ° C. used for the primer layer 3 include alkyd resin, polyester resin, polyvinyl acetate resin, vinyl chloride vinyl acetate copolymer resin, NBR resin, SBR resin, polyurethane resin, acrylic resin. , Polyamide, etc. are used alone or as a mixture or modified product. The modified product is, for example, an adhesive property obtained by copolymerizing or grafting a hydroxyl group, a carboxylic acid, or a quaternary ammonium salt-containing monomer,
For example, those with increased hydrophilicity. If the Tg exceeds 50 ° C., the adhesiveness between the base sheet and the ink receiving layer will deteriorate, which is not preferable. Moreover, curl resistance (cushioning property) is also reduced. When Tg is lower than -100 ° C, when recording sheets are stacked or stored as a roll, the recording sheet becomes tacky and blocking occurs. Further, in order to improve the adhesiveness of the primer layer and the coating film strength, the above resins may be crosslinked with various curing agents such as epoxy resins, melamine resins, isocyanates and the like. The method for forming the above-mentioned primer layer may be various conventionally known methods, for example, gravure coat, gravure reverse coat, roll coat, wire bar coat, blade coat, knife coat, air knife coat, comma coat, slot die coat, Any method such as dip coating may be used. If necessary, an additive is added to the resin constituting the primer layer, and a solution prepared by dissolving or dispersing it in a suitable solvent is coated on the substrate sheet and dried to form the primer layer. The thickness of the primer layer, when dried, is 0.01 to 50 μm, preferably 0.1.
It is good to set it to 10 μm. If this thickness is less than 0.1 μm, adhesiveness will not exhibit sufficient performance, while
If it exceeds 10 μm, the end face becomes sticky when the recording sheet is cut, which is not preferable in addition to high manufacturing cost.

【００１３】（インク受容層）基材シートの一方の面
に、プライマー層を設け、その上にインク受容層４を設
ける。本発明で用いるインク受容層４としては、水溶性
樹脂系、顔料／結着剤系、多孔質層系等の各種受容層が
用いられる。水溶性樹脂系受容層は、水やアルコール等
の水性溶媒に可溶な水溶性樹脂を主体としたものであ
り、従来公知の種々のものが用いられる。例えば、ポリ
ビニルアルコールやポリビニルピロリドン、ポリ（メ
タ）アクリル酸、セルロース系樹脂（ＣＭＣ、ＨＥＣ、
ＨＰＣ等）、ポリアクリルアミド、ポリエチレンオキサ
イド、ポリエチレングリコール、ポリビニルアセタール
系樹脂、ポリビニルメチルエーテル、ポリアミン、ポリ
エチレンイミン、カゼイン、ゼラチン、でんぷん等の水
溶性樹脂及び／またはこれらの共重合体、カチオン／ア
ニオン変性物等の少なくとも１種以上が用いられる。(Ink Receiving Layer) A primer layer is provided on one surface of the substrate sheet, and the ink receiving layer 4 is provided thereon. As the ink receiving layer 4 used in the present invention, various receiving layers such as water-soluble resin type, pigment / binder type and porous layer type are used. The water-soluble resin-based receiving layer is mainly composed of a water-soluble resin soluble in an aqueous solvent such as water or alcohol, and various conventionally known materials are used. For example, polyvinyl alcohol, polyvinylpyrrolidone, poly (meth) acrylic acid, cellulosic resins (CMC, HEC,
HPC, etc.), polyacrylamide, polyethylene oxide, polyethylene glycol, polyvinyl acetal resin, polyvinyl methyl ether, polyamine, polyethyleneimine, casein, gelatin, starch and other water-soluble resins and / or their copolymers, cation / anion modified At least one kind of thing or the like is used.

【００１４】顔料／結着剤系受容層は、従来公知の各種
顔料及び上記のような水溶性樹脂等からなる。各種顔料
としては、例えば、シリカ、コロイダルシリカ、クレ
ー、炭酸カルシウム、酸化チタン、有機微粒子、アルミ
ナゾルなどの微粒子フィラーがあげられる。顔料／結着
剤の混合比は、１０／１〜１／１０の範囲が好適であ
る。接着性、耐カール性の点からは、４／６〜１／１０
の範囲が好ましく、インク乾燥性、画像鮮明性を重視す
るという点からは、１０／１〜６／４の範囲が好適であ
る。The pigment / binder system receiving layer comprises various conventionally known pigments and the above water-soluble resins. Examples of various pigments include fine particle fillers such as silica, colloidal silica, clay, calcium carbonate, titanium oxide, organic fine particles, and alumina sol. The mixing ratio of pigment / binder is preferably in the range of 10/1 to 1/10. 4/6 to 1/10 in terms of adhesion and curl resistance
Is preferable, and a range of 10/1 to 6/4 is preferable from the viewpoint that importance is attached to ink drying property and image clarity.

【００１５】多孔質層系インク受容層は、従来公知の各
種顔料及び上記の各種水溶性樹脂からなり、各種顔料間
に空隙を有するように設計したものである。顔料／水溶
性樹脂の混合比は、１０／１〜３／１の範囲が好適であ
る。また、塗工適性、塗膜強度、密着性の向上を目的と
して、上記の顔料と水溶性樹脂の組成中に各種のポリマ
ーや添加剤の添加も可能である。例えば、シリカ、コロ
イダルシリカ、クレー、炭酸カルシウム、酸化チタン、
有機微粒子、アルミナゾルなどの微粒子フィラーがあげ
られる。粒径は、０．１〜２０μｍのものが良く、全固
形分に対して０．１〜１０％を加えることが好ましい。
全固形分に対して０．１％未満では、記録シートを重ね
たり、ロール状で保存したりするとき、ブロッキングが
生じやすく、１０％を越えると透明性を落とすことにな
り、好ましくない。この他に、各種界面活性剤、酸化防
止剤、紫外線吸収剤、消泡剤、親水性の高い各種変性オ
イル等を本発明の効果を妨げない範囲で混合して用いる
こともできる。The porous layer type ink receiving layer is composed of various conventionally known pigments and the above various water-soluble resins, and is designed to have voids between various pigments. The mixing ratio of pigment / water-soluble resin is preferably in the range of 10/1 to 3/1. Further, various polymers and additives may be added to the composition of the pigment and the water-soluble resin for the purpose of improving coating suitability, coating film strength and adhesion. For example, silica, colloidal silica, clay, calcium carbonate, titanium oxide,
Examples thereof include fine particle fillers such as organic fine particles and alumina sol. The particle size is preferably 0.1 to 20 μm, and it is preferable to add 0.1 to 10% of the total solid content.
If it is less than 0.1% based on the total solid content, blocking tends to occur when recording sheets are stacked or stored in a roll form, and if it exceeds 10%, the transparency is deteriorated, which is not preferable. In addition, various surfactants, antioxidants, ultraviolet absorbers, antifoaming agents, various types of highly hydrophilic modified oils, and the like can be mixed and used as long as the effects of the present invention are not impaired.

【００１６】上述した各種のインク受容層の形成方法
は、従来公知の種々の方法でよく、例えば、グラビアコ
ート、グラビアリバースコート、ロールコート、ワイヤ
ーバーコート、ブレードコート、ナイフコート、エアー
ナイフコート、コンマコート、スロットダイコート、デ
ィップコート等いずれの方法でもよい。インク受容層の
構成する樹脂に必要に応じて添加剤を加え、適当な溶剤
に溶解あるいは分散させた液を、基材シートにコーティ
ングし、乾燥して、インク受容層を設ける。尚、コーテ
ィング量の確保のため、同一組成の液を複数回重ねて、
コーティングしてもよい。インク受容層の厚みは、乾燥
時で、０．０１〜５０μｍ、好ましくは０．１〜１０μ
ｍとするのが良い。この厚みが、０．１μｍ未満になる
と、接着性、耐カール性で十分な性能が発揮せず、一方
で、１０μｍを越えると、製造コストが高くつくと併せ
て、好ましくない。The various ink receiving layers described above may be formed by various conventionally known methods, for example, gravure coat, gravure reverse coat, roll coat, wire bar coat, blade coat, knife coat, air knife coat, Any method such as comma coating, slot die coating or dip coating may be used. If necessary, an additive is added to the resin constituting the ink receiving layer, and a solution prepared by dissolving or dispersing it in a suitable solvent is coated on the substrate sheet and dried to form the ink receiving layer. In addition, in order to secure the coating amount, the liquid of the same composition is layered several times,
It may be coated. The thickness of the ink receiving layer when dried is 0.01 to 50 μm, preferably 0.1 to 10 μm.
m. If the thickness is less than 0.1 μm, the adhesiveness and curl resistance will not exhibit sufficient performance, while if it exceeds 10 μm, the manufacturing cost will be high and it is not preferable.

【００１７】また、基材シートのインク受容層が形成さ
れる面とは反対の面に、カール防止層、帯電防止層等を
設けても良い。カール防止層としては、インク受容層と
同様な水溶性樹脂や、アクリル系樹脂、ポリエステル樹
脂等を用いることが可能であるが、特に、アクリル樹脂
または、変性アクリル樹脂、ポリエステル樹脂を用いる
と、耐ブロッキング性、スリップ性の付与といった点か
らも有用である。カール防止層の厚みは、乾燥時で０．
１〜５０μｍ程度が好ましく、前述のインク受容層の形
成方法と同様な方法が選べる。Further, an anti-curl layer, an antistatic layer or the like may be provided on the surface of the substrate sheet opposite to the surface on which the ink receiving layer is formed. As the anti-curl layer, it is possible to use the same water-soluble resin as the ink receiving layer, an acrylic resin, a polyester resin, or the like. In particular, when an acrylic resin, a modified acrylic resin, or a polyester resin is used, It is also useful in terms of imparting blocking property and slip property. The thickness of the anti-curl layer is 0.
The thickness is preferably about 1 to 50 μm, and the same method as the above-mentioned method for forming the ink receiving layer can be selected.

【００１８】また、記録用シートの粉塵による汚染防止
や、プリンターでの搬送の安定性をもたせるため、下記
の帯電防止剤を含む帯電防止層を設けることができる。
帯電防止剤としては、従来公知の陽イオン、陰イオン、
両性イオン、非イオン系のいずれの帯電防止剤を使用で
きる。例えば、第４級アンモニウム塩、ポリアミン誘導
体などのカチオン系帯電防止剤、アルキルホスフェート
などのアニオン系帯電防止剤、脂肪酸エステルなどのノ
ニオン系帯電防止剤が、あげられる。帯電防止層は、上
記の帯電防止剤と有機ないし無機フィラーなどの滑剤を
添加してもよく、それらを溶剤に溶解または分散させた
配合液を、公知の方法、すなわち、グラビアコート、グ
ラビアリバースコート、ロールコート等の方法で塗布、
乾燥して、形成される。その帯電防止層の厚みは、乾燥
時で０．００１〜０．１μｍ程度である。Further, an antistatic layer containing the following antistatic agent can be provided in order to prevent the recording sheet from being contaminated by dust and to stabilize the conveyance in the printer.
As the antistatic agent, conventionally known cations, anions,
Either a zwitterionic or nonionic antistatic agent can be used. Examples thereof include cationic antistatic agents such as quaternary ammonium salts and polyamine derivatives, anionic antistatic agents such as alkyl phosphates, and nonionic antistatic agents such as fatty acid esters. The antistatic layer may be added with the above antistatic agent and a lubricant such as an organic or inorganic filler, and a compounded solution obtained by dissolving or dispersing them in a solvent by a known method, that is, gravure coating, gravure reverse coating. , Roll coating, etc.,
Dry and form. The thickness of the antistatic layer is about 0.001 to 0.1 μm when dried.

【００１９】[0019]

〔プライマー層の組成〕[Composition of primer layer]

ポリエステル樹脂 単独 （東洋紡（株）製 バイロン１０３、Ｔｇ４７℃） （２０％メチルエチルケトン／トルエン〔１／１〕溶
液） 〔インク受容層の組成〕 ポリビニルアルコール樹脂 単独 （クラレ（株）製 ＰＶＡ ２１７） （２０％水／ＩＰＡ〔２／１〕溶液）Polyester resin alone (Vylon 103 manufactured by Toyobo Co., Ltd., Tg 47 ° C.) (20% methyl ethyl ketone / toluene [1/1] solution) [Composition of ink receiving layer] polyvinyl alcohol resin alone (PVA 217 manufactured by Kuraray Co., Ltd.) (20 % Water / IPA [2/1] solution)

【００２０】（実施例２）プライマー層を下記組成に
て、乾燥時塗布量が３．０ｇ／ｍ² となるように、ま
た、インク受容層の組成を下記のとおりとして乾燥時塗
布量が１０ｇ／ｍ² となるようにした以外は、実施例１
と同様にして記録用シートを作成した。 〔プライマー層の組成〕 スチレン−ブタジエン共重合体 単独 （日本ゼオン（株）製 ニポールＳＸ１１０７、Ｔｇ１
７℃） （２０％水／ＩＰＡ〔２／１〕溶液） 〔インク受容層の組成〕 ポリビニルピロリドン樹脂 単独 （ＢＡＳＦ社製 Ｋ−９０） （１０％水／ＩＰＡ〔２／１〕溶液）(Example 2) The primer layer was made to have the following composition so that the dry coating amount was 3.0 g / m ^2, and the composition of the ink receiving layer was as follows so that the dry coating amount was 10 g. Example 1 except that it was set to be / m ^2.
A recording sheet was prepared in the same manner as. [Composition of Primer Layer] Styrene-butadiene copolymer alone (Nipol SX1107, manufactured by Nippon Zeon Co., Ltd., Tg1)
(7 ° C) (20% water / IPA [2/1] solution) [Composition of ink receiving layer] Polyvinylpyrrolidone resin alone (BASF K-90) (10% water / IPA [2/1] solution)

【００２１】（実施例３）プライマー層を下記組成に
て、乾燥時塗布量が３．０ｇ／ｍ² となるように、ま
た、インク受容層の組成を下記のとおりとして乾燥時塗
布量が１０ｇ／ｍ² となるようにした以外は、実施例１
と同様にして記録用シートを作成した。 〔プライマー層の組成〕 アクリル酸エステル樹脂 単独 （日本ゼオン（株）製 ニポールＳＸ１７０６、Ｔｇ０℃） （２０％水／ＩＰＡ〔２／１〕溶液） 〔インク受容層の組成〕 ポリビニルアルコール樹脂 １重量部 （クラレ（株）製 ＰＶＡ ２１７） （１０％水／ＩＰＡ〔２／１〕溶液） コロイダルシリカ ４重量部 （日産化学（株）製 ＳＴ−０Ｌ） （２０％水／ＩＰＡ〔２／１〕溶液）(Example 3) A primer layer having the following composition was applied so that the dry coating amount was 3.0 g / m ^2, and the composition of the ink receiving layer was as follows, so that the dry coating amount was 10 g. Example 1 except that it was set to be / m ^2.
A recording sheet was prepared in the same manner as. [Composition of primer layer] Acrylic ester resin alone (Nipol SX1706 manufactured by Nippon Zeon Co., Tg 0 ° C) (20% water / IPA [2/1] solution) [Composition of ink receiving layer] 1 part by weight of polyvinyl alcohol resin (Kuraray Co., Ltd. PVA 217) (10% water / IPA [2/1] solution) Colloidal silica 4 parts by weight (Nissan Chemical Co., Ltd. ST-0L) (20% water / IPA [2/1] solution )

【００２２】（比較例１）基材シートとして、厚み１０
０μｍの透明なポリエチレンテレフタレートフィルム
（東レ（株）製 ルミラーＴ−６０）を用い、その一方
の面にインク受容層を下記組成で乾燥時塗布量が１０ｇ
／ｍ² になるように、バーコート法にて塗布後、８０℃
で５分間乾燥させて、記録用シートを作成した。（プラ
イマー層は設けない。） 〔インク受容層の組成〕 ポリビニルアルコール樹脂 （クラレ（株）製 ＰＶＡ ２１７） （１０％水／ＩＰＡ〔２／１〕溶液）Comparative Example 1 A substrate sheet having a thickness of 10
A transparent polyethylene terephthalate film (Lumirror T-60, manufactured by Toray Industries, Inc.) having a thickness of 0 μm was used, and an ink receiving layer having the following composition on one surface thereof had a dry coating amount of 10 g.
/ M ² after coating by bar coating method at 80 ℃
And dried for 5 minutes to prepare a recording sheet. (No primer layer is provided.) [Composition of ink receiving layer] Polyvinyl alcohol resin (PVA 217 manufactured by Kuraray Co., Ltd.) (10% water / IPA [2/1] solution)

【００２３】（比較例２）プライマー層を下記組成に
て、乾燥時塗布量が０．２ｇ／ｍ² となるように、ま
た、インク受容層の組成を下記のとおりとして乾燥時塗
布量が１０ｇ／ｍ² となるようにした以外は、実施例１
と同様にして記録用シートを作成した。 〔プライマー層の組成〕 ポリエステル樹脂 単独 （東洋紡（株）製 バイロン２９０、Ｔｇ７２℃） （２０％メチルエチルケトン／トルエン〔１／１〕溶
液） 〔インク受容層の組成〕 ポリビニルアルコール樹脂 単独 （クラレ（株）製 ＰＶＡ ２１７） （１０％水／ＩＰＡ〔２／１〕溶液）Comparative Example 2 A primer layer having the following composition was applied so that the dry coating amount was 0.2 g / m ^2, and the composition of the ink receiving layer was as follows, so that the dry coating amount was 10 g. Example 1 except that it was set to be / m ^2.
A recording sheet was prepared in the same manner as. [Composition of primer layer] Polyester resin alone (Vylon 290, Tg 72 ° C manufactured by Toyobo Co., Ltd.) (20% methyl ethyl ketone / toluene [1/1] solution) [Composition of ink receiving layer] polyvinyl alcohol resin alone (Kuraray Co., Ltd.) Manufactured PVA 217) (10% water / IPA [2/1] solution)

【００２４】上記の実施例および比較例の記録用シート
について、インクジェットプリンター（ＣＡＮＯＮ社製
ＢＪＣ−４００Ｊ）を用いて、テストパターンを印刷
し、下記の表１に示す結果を得た。尚、表１に示した各
性能の評価方法は、以下の通りである。A test pattern was printed on the recording sheets of the above Examples and Comparative Examples using an ink jet printer (BJC-400J manufactured by CANON), and the results shown in Table 1 below were obtained. In addition, the evaluation method of each performance shown in Table 1 is as follows.

【００２５】（１）接着性 基材シートと、プライマー層ないしインク受容層との接
着性を、目視にて確認評価した。 ○：ニチバン（株）製セロテープ、エルパックＬＰ−１
２を記録シートのインク受容層面に、親指で３往復擦り
つけて、そのテープを剥がし取ろうとしても層が落ちな
い。 ×：ニチバン（株）製セロテープ、エルパックＬＰ−１
２を記録シートのインク受容層面に、親指で３往復擦り
つけて、そのテープを剥がし取ろうとすると、簡単に層
が落ちる 。(1) Adhesiveness The adhesiveness between the base sheet and the primer layer or the ink receiving layer was visually confirmed and evaluated. ○: Selling tape manufactured by Nichiban Co., Ltd., L-Pack LP-1
The layer does not drop even if the tape is peeled off by rubbing 2 with the thumb 3 times back and forth on the ink receiving layer surface of the recording sheet. ×: Nichiban Co., Ltd. cellophane tape, L-pack LP-1
When 2 is rubbed 3 times back and forth with the thumb on the ink receiving layer surface of the recording sheet to peel off the tape, the layer easily drops.

【００２６】（２）耐カール性 記録用シートを温度１５℃、相対湿度１０％の環境下
に、３時間放置後、カールの発生度合を目視にて確認評
価した。 ○：ほとんどカールしない。（Ａ４サイズで、四隅の各
隅の高さが１０ｍｍを越えない。） ×：かなりカールする。（Ａ４サイズで、四隅の各隅の
高さが２０ｍｍを越える。）(2) Curling resistance After the recording sheet was left in an environment of a temperature of 15 ° C. and a relative humidity of 10% for 3 hours, the degree of curling was visually confirmed and evaluated. ○: Almost no curl. (A4 size, the height of each of the four corners does not exceed 10 mm.) X: Curls considerably. (In A4 size, the height of each of the four corners exceeds 20 mm.)

【００２７】[0027]

【表１】 [Table 1]

【００２８】[0028]

【発明の効果】本発明の記録用シートは、基材シートの
少なくとも片面に、インク受容層を設け、基材シートと
インク受容層の間に、Ｔｇが−１００℃〜５０℃の樹脂
からなるプライマー層を設けることにより、Ｔｇが−１
００℃〜５０℃の樹脂であるため、プラスチック基材と
インク受容層の両方への接着性が強くなり、さらに、使
用する環境においてカールが発生しない。The recording sheet of the present invention is provided with an ink receiving layer on at least one side of a base sheet, and is made of a resin having a Tg of −100 ° C. to 50 ° C. between the base sheet and the ink receiving layer. By providing the primer layer, Tg is -1.
Since it is a resin of 00 ° C to 50 ° C, the adhesiveness to both the plastic substrate and the ink receiving layer is strong, and further, curling does not occur in the environment in which it is used.

【図面の簡単な説明】[Brief description of drawings]

【図１】本発明の記録用シートの一つの実施の形態を示
す断面図である。FIG. 1 is a cross-sectional view showing one embodiment of a recording sheet of the present invention.

【符号の説明】[Explanation of symbols]

１ 記録用シート ２ 基材シート ３ プライマー層 ４ インク受容層 DESCRIPTION OF SYMBOLS 1 Recording sheet 2 Base sheet 3 Primer layer 4 Ink receiving layer

─────────────────────────────────────────────────────
─────────────────────────────────────────────────── ───

【手続補正書】[Procedure amendment]

【提出日】平成８年１月３０日[Submission date] January 30, 1996

【手続補正１】[Procedure Amendment 1]

【補正対象書類名】明細書[Document name to be amended] Statement

【補正対象項目名】発明の名称[Correction target item name] Name of invention

【補正方法】変更[Correction method] Change

【補正内容】[Correction contents]

【発明の名称】 記録用シートTitle of the invention Recording sheet

Claims (2)

【特許請求の範囲】[Claims] 【請求項１】 基材シートの少なくとも片面に、インク
受容層を設けた記録用シートにおいて、基材シートとイ
ンク受容層の間に、Ｔｇが−１００℃〜５０℃の樹脂か
らなるプライマー層が設けられていることを特徴とする
記録用シート。1. A recording sheet in which an ink receiving layer is provided on at least one side of a base sheet, wherein a primer layer made of a resin having a Tg of −100 ° C. to 50 ° C. is provided between the base sheet and the ink receiving layer. A recording sheet, which is provided. 【請求項２】 基材シートが、熱可塑性プラスチックで
あることを特徴とする上記の請求項１に記載する記録用
シート。2. The recording sheet according to claim 1, wherein the base sheet is a thermoplastic plastic.