JPH0978777A - Waterproof cladding material and waterproof cladding structure by using this material - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a sufficient waterproof by blending the aggregate, the cement group inorganic bonding agent for bonding this aggregate to each other and the organic bonding agent made of the high molecular material of resin and rubber so as to form cladding material. SOLUTION: A cladding material 1 is formed of the aggregate 8 made of quartz sand, which is mainly composed of silicon dioxide, stone powder, which is composed mainly of calcium carbonate, slag and light aggregate and the bonding agent 3 for bonding this aggregate 8 to each other. At least one kind, which is selected among the aggregate 8, is blended at 50% by weight or more in relation to the weight of the cladding material 1, and the organic bonding agent such as the aqueous high molecular material of resin and rubber is blended at 10% by weight or more in relation to the weight of the cladding material 1. Hard grains 3 at 0.5μm-5μm is blended as the adhesion reinforcement at 3-15% by weight, and when the compressing force F is applied to the cladding material 1, the bonding agent 3 is deformed so that the aggregate 8 come close to each other. The compressing force is thereby supported by the aggregate 8 so as to improve the load supporting ability.

Description

【発明の詳細な説明】Detailed Description of the Invention

【０００１】[0001]

【発明の属する技術分野】本願発明は、防水被覆材及び
防水被覆の構造に関し、特に、陸屋根等の屋上に形成さ
れる防水被覆等、建築物外面の防水被覆に適したものに
関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a waterproof coating material and a structure of the waterproof coating, and more particularly to a waterproof coating formed on a roof such as a flat roof, which is suitable for a waterproof coating on the outer surface of a building.

【０００２】[0002]

【従来の技術】たとえば、コンクリート製の建物に多く
採用される陸屋根は、内側部に形成される床部と、これ
を取り囲むように形成される立ち上がり部とを備える。
上記床部外表面及び立ち上がり部内側面には、雨水等が
建物内部へ浸入するのを防止するため、防水被覆が形成
されている。2. Description of the Related Art For example, a flat roof, which is often used in concrete buildings, includes a floor portion formed on the inner side and a rising portion formed so as to surround the floor portion.
A waterproof coating is formed on the outer surface of the floor and the inner surface of the rising portion to prevent rainwater and the like from entering the inside of the building.

【０００３】上記防水被覆は、長期にわたって防水機能
を発揮する必要がある。上記防水被覆は、通常、現場施
工によって種々の材料を張り、塗り、あるいは取り付け
る等することにより形成されることが多い。The above waterproof coating needs to exhibit a waterproof function for a long period of time. The waterproof coating is usually formed by applying, painting, or attaching various materials by on-site construction.

【０００４】従来から施工されている防水被覆の構造と
して、アスファルト防水構造、シート防水構造、塗膜防
水構造等、種々の防水被覆の構造がある。Conventional waterproof coating structures include various waterproof coating structures such as an asphalt waterproof structure, a sheet waterproof structure and a coating film waterproof structure.

【０００５】アスファルト防水構造は、溶融したアスフ
ァルトをルーフィング材とともに積層して形成されるも
のであり、アスファルトの溌水性を利用したものであ
る。シート防水構造は、合成ゴム等の可撓性シートを下
地面に接着剤等を用いて隙間なく張りつけ、防水層を形
成するものである。塗膜防水構造は、ウレタンゴム等の
樹脂材料をローラや吹き付け器によって被覆対象物表面
に塗着して防水層を形成するものであり、ガラス繊維等
を積層して強度を増加させることが多い。The asphalt waterproof structure is formed by laminating molten asphalt together with a roofing material, and utilizes the water repellent property of the asphalt. The waterproof sheet structure is a structure in which a flexible sheet of synthetic rubber or the like is adhered to a base surface with an adhesive or the like without any gaps to form a waterproof layer. The waterproof structure is a structure in which a resin material such as urethane rubber is applied to the surface of an object to be coated with a roller or a sprayer to form a waterproof layer, and glass fibers are often laminated to increase the strength. .

【０００６】[0006]

【発明が解決しようとする課題】上記従来の防水被覆構
造は、施工の段階においてあるいは防水被覆の構造自体
に種々の問題がある。The above-mentioned conventional waterproof coating structure has various problems at the stage of construction or in the structure of the waterproof coating itself.

【０００７】すなわち、上記アスファルト防水構造を形
成するには、アスファルトを溶融しなければならないた
め、火災、火傷等の危険がある。また、臭いが発生して
近隣に公害問題を引き起こす場合も多い。また、防水層
を表面に露出させたままの露出防水構造とする場合に
は、防水層の強度が低いため、草木の根に侵されやす
い。さらに、歩行等を行えるようにするには、表面にコ
ンクリートやシート等を敷設する必要がある。That is, since the asphalt must be melted in order to form the asphalt waterproof structure, there is a risk of fire, burns and the like. In addition, odors often cause pollution problems in the neighborhood. Further, in the case of an exposed waterproof structure in which the waterproof layer is exposed on the surface, since the waterproof layer has a low strength, it is easily attacked by the roots of plants. Furthermore, in order to be able to walk or the like, it is necessary to lay concrete or a sheet on the surface.

【０００８】シート防水構造を形成するには、有機溶剤
を含む接着剤を使用することが多いため、換気が悪い場
所等では火災及び中毒の危険性がある。また、シートを
重ね合わせるようにして防水層を形成するが、シートの
収縮によって接合部分がはがれたり、しわが発生しやす
い。また、上記接合部のはがれ等を確認することが困難
である。さらに、通常、シートは製造の最終段階で円筒
状に巻き取られるが、この巻き取り工程においてシート
に応力が作用したまま巻き取られることが多い。ところ
が、この応力が施工後の大きな収縮の原因になることが
多い。また、出入り隅部、出入り隅角部におけるシート
の張り付けが面倒であり、多大な手間を要し、工期も長
くなる。Since an adhesive containing an organic solvent is often used to form a waterproof structure for a sheet, there is a risk of fire and poisoning in a place where ventilation is poor. Further, although the waterproof layer is formed by stacking the sheets, the contraction of the sheets tends to cause peeling of the joint portion and wrinkles. Further, it is difficult to confirm the peeling of the joint portion. Further, the sheet is usually wound into a cylindrical shape at the final stage of manufacturing, but in the winding step, the sheet is often wound with stress applied. However, this stress often causes a large shrinkage after construction. In addition, the entrance and exit corners, and the sticking of the sheet at the entrance and exit corners are troublesome, which requires a great deal of time and labor, and the construction period becomes long.

【０００９】塗膜防水構造は、現場で防水材料を被覆対
象物の表面に塗着して形成されるため、塗膜の厚さを一
定するするのが困難である。また、現場施工であるため
塗膜にピンホール等の欠陥が生じやすく、収縮等が生じ
た場合に防水層の破断につながる。特に、防水性能や作
業性が塗膜を形成する下地の精度に大きく影響される。
しかも、熱劣化、熱収縮等の問題も生じやすい。Since the waterproof structure of the coating film is formed by coating the surface of the object to be coated with a waterproof material on site, it is difficult to make the thickness of the coating film constant. Further, since the coating is carried out on site, defects such as pinholes are likely to occur in the coating film, which leads to breakage of the waterproof layer when contraction occurs. In particular, waterproof performance and workability are greatly affected by the accuracy of the base material that forms the coating film.
Moreover, problems such as heat deterioration and heat shrinkage are likely to occur.

【００１０】さらに、上述した従来の防水被覆構造に共
通する大きな課題は、防水被覆を露出させたままで、歩
行に供したり屋上駐車場に供することが困難なことであ
る。Further, a major problem common to the above-described conventional waterproof coating structures is that it is difficult to walk or to provide a rooftop parking lot with the waterproof coating exposed.

【００１１】すなわち、歩行あるいは運動ができる程度
の床面の強度を得るには、防水被覆の上にウレタン樹脂
等を塗着して厚い保護層を設けたり、表面に硅砂入りの
塗料等でコーティング層を形成しなければならない。さ
らに、駐車場に供するには、床の強度のみならず高い耐
磨耗性を要求されるため、防水被覆の上にコンクリート
等を打設する場合も多い。That is, in order to obtain a floor strength that allows walking or exercise, a urethane resin or the like is applied on a waterproof coating to form a thick protective layer, or the surface is coated with silica sand paint or the like. The layers must be formed. Further, in order to be provided in a parking lot, not only the strength of the floor but also high abrasion resistance is required, so that concrete or the like is often placed on the waterproof coating.

【００１２】また、屋上空間を駐車場や遊び場等に供し
て有効利用を図るには、上述した防水被覆の強度ととも
に、防火性能を検討しなければならない。In addition, in order to effectively utilize the rooftop space by providing it for a parking lot, a playground or the like, it is necessary to consider the fireproof performance as well as the strength of the waterproof coating.

【００１３】すなわち、性能の良い防水被覆は樹脂材料
から形成されることが多いため、一般に熱に弱い。この
ため、煙草の火気等が防水被覆に作用すると防水被覆が
簡単に破壊される。したがって、防火性能を向上させる
ために、防水被覆の上にコンクリート、モルタル等の耐
熱層を設けなければならず、非常にコストの高いものと
なる。That is, since a waterproof coating having good performance is often made of a resin material, it is generally weak against heat. Therefore, if the fire or the like of the cigarette acts on the waterproof coating, the waterproof coating is easily destroyed. Therefore, in order to improve the fireproof performance, it is necessary to provide a heat-resistant layer of concrete, mortar or the like on the waterproof coating, which is very expensive.

【００１４】さらに、被覆対象物の表面が伸縮したり、
移動したりすると、これにともなって、防水被覆が変形
する。Further, the surface of the object to be coated expands or contracts,
When it is moved, the waterproof coating is deformed accordingly.

【００１５】特に、コンクリート建物等の屋根防水にお
いては、コンクリートの打設が複数回に分けて行われる
ことが多く、打継部の伸縮によって防水被覆の下地が動
く。In particular, in waterproofing a roof of a concrete building or the like, concrete is often cast in several steps, and the base of the waterproof coating moves due to expansion and contraction of the joint.

【００１６】また、ＰＣ板あるいはＡＬＣ板の目地部
や、コンクリートスラブとＡＬＣ板スラブのジョイント
部等に動きが生じやすい。Further, the joint portion of the PC plate or the ALC plate, the joint portion of the concrete slab and the ALC plate slab, and the like are likely to move.

【００１７】したがって、これらの部位に形成される防
水被覆が、被覆対象物の伸縮等の変形に追随できないと
防水被覆が破壊してしまい、漏水の原因となる。Therefore, if the waterproof coating formed on these portions cannot follow the deformation such as expansion and contraction of the object to be coated, the waterproof coating will be destroyed and cause water leakage.

【００１８】本願発明は、上記従来の問題を解決し、十
分な防水性能、高い強度及び防火性能を備え、しかも被
覆対象物の変形に十分追随することができ、さらに屋上
空間を有効に利用することのできる防水被覆材及びこれ
を用いた防水被覆の構造を提供することをその課題とす
る。The present invention solves the above-mentioned conventional problems, has sufficient waterproof performance, high strength, and fire protection performance, can sufficiently follow the deformation of the object to be coated, and effectively utilizes the rooftop space. It is an object of the present invention to provide a waterproof coating material that can be used and a structure of a waterproof coating that uses the waterproof coating material.

【００１９】[0019]

【課題を解決するための手段】上記課題を解決するた
め、本願発明では、次の技術的手段を講じている。Means for Solving the Problems To solve the above problems, the present invention takes the following technical means.

【００２０】本願の請求項１に記載した発明は、骨材と
この骨材を相互に接合する接合剤とを配合して構成され
る被覆材であって、上記接合剤は、セメント系無機質接
合剤と、樹脂及び／又はゴムの高分子物質からなる有機
質接合剤とを含み、上記骨材の配合割合を５０重量％以
上に設定する一方、上記有機質接合剤の配合割合を１０
重量％以上に設定したことを特徴とする。The invention according to claim 1 of the present application is a coating material formed by mixing an aggregate and a bonding agent for bonding the aggregates to each other, wherein the bonding agent is a cement-based inorganic bonding agent. Agent and an organic binder made of a polymeric substance of resin and / or rubber, and the compounding ratio of the aggregate is set to 50% by weight or more, while the compounding ratio of the organic binder is 10
It is characterized in that it is set to be more than weight%.

【００２１】本願の請求項２に記載した発明は、０．５
μｍ〜５μｍの硬質微粒子を、３重量％〜１５重量％配
合したことを特徴とする。The invention described in claim 2 of the present application is 0.5
It is characterized in that the hard fine particles of μm to 5 μm are mixed in an amount of 3% by weight to 15% by weight.

【００２２】本願の請求項３に記載した発明は、２種以
上の粒径の骨材を配合したことを特徴とする。The invention described in claim 3 of the present application is characterized in that an aggregate having two or more kinds of particle diameters is mixed.

【００２３】本願の請求項４に記載した発明は、上記請
求項１ないし請求項３のいずれかに記載した防水被覆材
によって被覆対象物表面側に形成される防水補強層と、
防火性を備える被覆材によって上記防水補強層の外面に
積層形成される防火層とを備えて構成される防水被覆の
構造に関するものである。The invention described in claim 4 of the present application is a waterproof reinforcing layer formed on the surface side of an object to be coated by the waterproof coating material according to any one of claims 1 to 3,
The present invention relates to a structure of a waterproof coating including a fireproof layer laminated on the outer surface of the waterproof reinforcing layer by a coating material having fireproof property.

【００２４】本願の請求項５に記載し発明は、防水被覆
の最外側に形成される防火層と、被覆対象物表面に形成
される防水下地層と、上記防火層と防水下地層との間に
形成される防水補強層とを備えて構成される防水被覆の
構造において、上記防火層は、防火性を有する被覆材か
ら形成される一方、上記防水補強層は、請求項１ないし
請求項３のいずれかに記載した防水被覆材から形成され
ており、上記防水下地層は、弾性変形可能な樹脂又は／
及びゴムの高分子材料を含んで形成されるとともに、引
張破断にいたる変形量を上記防火層及び防水補強層より
も大きく設定したことを特徴とする。According to a fifth aspect of the present invention, there is provided a fireproof layer formed on the outermost side of the waterproof coating, a waterproof underlayer formed on the surface of the object to be coated, and the fireproof layer and the waterproof underlayer. In the structure of the waterproof coating including the waterproof reinforcing layer formed in the above, the fireproof layer is formed of a coating material having fireproofness, and the waterproof reinforcing layer is formed in the waterproof reinforcing layer. The waterproof underlayer is formed of an elastically deformable resin or /
And a polymeric material such as rubber, and the deformation amount up to tensile rupture is set to be larger than that of the fireproof layer and the waterproof reinforcing layer.

【００２５】本願の請求項６に記載した発明は、上記防
火層、防水補強層、防水下地層のうち少なくとも一層に
おいて、骨材及び／又は接合剤の配合割合を厚さ方向に
連続的に変化させた防水被覆の構造に関する。According to a sixth aspect of the present invention, in at least one of the fireproof layer, the waterproof reinforcing layer and the waterproof underlayer, the blending ratio of the aggregate and / or the bonding agent is continuously changed in the thickness direction. It relates to the structure of a waterproof coating.

【００２６】本願の請求項７に記載した発明は、防火
層、防水補強層及び防水下地層を、骨材及び／又は接合
剤の配合割合を連続的に変化させることにより、これら
各層を一体的に形成したことを特徴とする。In the invention according to claim 7 of the present application, the fireproof layer, the waterproof reinforcing layer, and the waterproof underlayer are integrated by continuously changing the mixing ratio of the aggregate and / or the bonding agent. It is characterized in that it is formed.

【発明の実施の形態】以下、本願発明に係る防水被覆材
について詳細に説明する。BEST MODE FOR CARRYING OUT THE INVENTION The waterproof coating material according to the present invention will be described in detail below.

【００２７】本願発明に係る防水被覆材は、防水性能、
接着強度が高く、しかも骨材及び無機質接合剤を含みな
がら高い柔軟性を備えたものである。The waterproof coating material according to the present invention has a waterproof performance,
It has a high adhesive strength and is highly flexible while containing an aggregate and an inorganic bonding agent.

【００２８】すなわち、本願発明に係る防水被覆材は、
骨材とこの骨材を相互に接合する接合剤とを配合して構
成される被覆材である。That is, the waterproof coating material according to the present invention is
It is a coating material formed by mixing an aggregate and a bonding agent that bonds the aggregates to each other.

【００２９】本願発明においては、上記骨材を相互に接
合する接合剤として、セメント系無機質接合剤と、樹脂
及び／又はゴムの高分子物質からなる有機質接合剤とを
含む。In the present invention, as the bonding agent for bonding the above aggregates to each other, a cement-based inorganic bonding agent and an organic bonding agent made of a polymeric substance of resin and / or rubber are included.

【００３０】上記セメント系接合剤と有機質接合剤とを
含む被覆材料は、一般にポリマーセメントモルタルと称
されるものであり、ポリマーとセメントという２つの活
性成分を含むことに特徴がある。The coating material containing the cement-based binder and the organic binder is generally called polymer cement mortar, and is characterized by containing two active components of polymer and cement.

【００３１】これらポリマーとセメントは、相互にその
性質を補いあって、従来のセメントモルタルの欠点を改
善している。These polymers and cement complement each other in their properties to improve the drawbacks of conventional cement mortar.

【００３２】すなわち、セメントは水と反応してセメン
ト水和物を形成する一方、ポリマーは自着性と接着性を
有するポリマーフィルムを形成して、セメント水和物と
骨材とを強固に接合するのである。That is, the cement reacts with water to form a cement hydrate, while the polymer forms a polymer film having self-adhesiveness and adhesiveness to firmly bond the cement hydrate and the aggregate. To do.

【００３３】この結果、混練状態で流動性が増大してワ
ーカビリティが向上し、保水性が向上し、ブリージング
や材料分離に対する抵抗性が向上する。また、硬化する
と、曲げ強度、引張強度が大幅に増加し、防水性に優
れ、乾燥収縮性が低減する。しかも、ポリマー成分の働
きによって、コンクリート、タイル、石材、鋼、ガラ
ス、木材、合成樹脂材料等に対する接着力が増加すると
ともに、耐衝撃性及び耐磨耗性が数１０倍に増加し、さ
らに、耐薬品性、耐候性、耐熱性等も大幅に改善され
る。As a result, the fluidity is increased in the kneaded state, the workability is improved, the water retention is improved, and the resistance to breathing and material separation is improved. Further, when cured, the bending strength and the tensile strength are significantly increased, the waterproof property is excellent, and the drying shrinkage property is reduced. Moreover, the action of the polymer component increases the adhesive force to concrete, tiles, stones, steel, glass, wood, synthetic resin materials, etc., and also increases the impact resistance and abrasion resistance several tens of times. Chemical resistance, weather resistance, heat resistance, etc. are also greatly improved.

【００３４】上記構成の被覆材において、有機質接合剤
の割合を所定の値以上に増加させると、従来のポリマー
セメントモルタルとは全く異なる物性を備える材料がで
きあがる。In the coating material having the above structure, when the proportion of the organic binder is increased to a predetermined value or more, a material having physical properties completely different from that of the conventional polymer cement mortar is produced.

【００３５】すなわち、変形しない骨材と柔軟性の高い
樹脂特性が複合され、特異な変形特性をもつとともに、
従来のポリマーセメントモルタルより優れた防水性能を
発揮する。本願発明は、上記特性に着目し、これを防水
被覆材として利用するものである。That is, an aggregate that does not deform and a highly flexible resin characteristic are combined to have a unique deformation characteristic, and
Exhibits superior waterproofing performance to conventional polymer cement mortar. The present invention focuses on the above characteristics and utilizes them as a waterproof coating material.

【００３６】一方、本願発明に係る上記防水被覆材は、
樹脂の配合割合を高めることにより防水性能が向上する
ものの、強度、耐熱性、防火性等の被覆材としての基本
性能が低下しており、単独で防水被覆材として利用する
ことは困難である。On the other hand, the waterproof coating material according to the present invention is
Although the waterproof performance is improved by increasing the blending ratio of the resin, the basic performance as a coating material such as strength, heat resistance, and fire resistance is deteriorated, and it is difficult to use it alone as a waterproof coating material.

【００３７】さらに、本願発明は、上記被覆材を、防火
性能の高い被覆材及び／又はより柔軟な被覆材と組み合
わせることにより、いままでにない防水被覆構造を提供
しようとするものである。Furthermore, the present invention aims to provide a waterproof coating structure which has never existed by combining the above-mentioned coating material with a coating material having a high fireproof property and / or a more flexible coating material.

【００３８】本願発明に係る被覆材においては、骨材の
配合割合を５０％以上に設定する一方、有機質接合剤の
配合割合を１０重量％以上に設定する。In the coating material according to the present invention, the mixing ratio of the aggregate is set to 50% or more, while the mixing ratio of the organic bonding agent is set to 10% by weight or more.

【００３９】樹脂の配合割合を１０重量％以上に設定す
ることにより、従来のポリマーセメントモルタルでは想
像できなかった、ゴムのような弾力を備え、しかも高い
伸び率を備える物質が得られる。By setting the blending ratio of the resin to 10% by weight or more, it is possible to obtain a substance which has elasticity like rubber and which has a high elongation, which cannot be imagined by the conventional polymer cement mortar.

【００４０】さらに、柔軟性を備えることから、大きく
変形させられても防水性能が低下することがなく、防水
被覆の下地層ないし中間層に採用することにより、被覆
対象物表面の変形変位等によく追随する。Further, since it has flexibility, its waterproof performance does not deteriorate even if it is greatly deformed. By adopting it as a base layer or an intermediate layer of a waterproof coating, it is possible to prevent deformation and displacement of the surface of an object to be coated. Follow well.

【００４１】このため、本願発明に係る防水被覆材を防
水被覆の下地層ないし中間層に採用することにより、防
水性能の優れた防水補強層を構成することができる。Therefore, by adopting the waterproof coating material according to the present invention as the underlayer or intermediate layer of the waterproof coating, a waterproof reinforcing layer having excellent waterproof performance can be constructed.

【００４２】しかも、骨材を５０重量％以上配合してい
るため、厚さ方向の荷重をこの骨材で支持することがで
きる。Moreover, since 50% by weight or more of the aggregate is mixed, the load in the thickness direction can be supported by this aggregate.

【００４３】換言すると、被覆対象物の表面方向の伸び
が大きく、かつ、厚さ方向に変形しにくい防水被覆を形
成することができる。したがって、表面層に荷重が作用
する場合の表面層及び防水被覆全体の変形を最小限に抑
え、防水被覆材の変形による防水性能の低下を有効に防
止することができる。In other words, it is possible to form a waterproof coating in which the object to be coated has a large elongation in the surface direction and is hardly deformed in the thickness direction. Therefore, it is possible to minimize the deformation of the entire surface layer and the waterproof coating when a load acts on the surface layer, and effectively prevent the deterioration of the waterproof performance due to the deformation of the waterproof coating material.

【００４４】さらに、樹脂の配合割合が大きいことか
ら、接着性能に優れる。このため、表面に防火性の高い
硬質の被覆材を積層した場合にも層間で剥離することが
少なく、強度の高い防水被覆を構成することができる。Further, since the blending ratio of the resin is large, the adhesive performance is excellent. Therefore, even when a hard coating material having high fire resistance is laminated on the surface, peeling between layers is less likely to occur, and a waterproof coating having high strength can be configured.

【００４５】上記セメント系無機質接合剤として、水硬
性セメント、気硬性セメント、特殊セメント等種々のも
のがある。本願発明では、特定のセメントに限定される
ことはない。取り扱い易さ、耐熱性、耐水性、耐候性が
よく、また安価に入手できる水硬性セメントを採用する
のが好ましい。水硬性セメントとして、普通ポルトラン
ドセメント、白色ポルトランドセメント等を採用するこ
とができる。As the above cement-based inorganic bonding agent, there are various kinds such as hydraulic cement, air-hardening cement and special cement. The present invention is not limited to a particular cement. It is preferable to use a hydraulic cement that is easy to handle, has good heat resistance, water resistance, and weather resistance, and is inexpensive. As the hydraulic cement, ordinary Portland cement, white Portland cement, etc. can be adopted.

【００４６】一方、上記有機質接合剤として、アクリル
酸アルキルエステル−アクリロニトリル−メタクリル酸
共重合体、イソブチレン−無水マレイン酸共重合体、ブ
タジエン−メタクリル酸共重合体、イソプレン−アクリ
ル酸共重合体、アクリル酸ブチル−アクリル酸共重合体
或いはアクリル酸２−エチルヘキシル−メタクリル酸共
重合体などのアクリル酸エステル−アクリル酸共重合
体、アクリル酸ブチル−メタクリル酸共重合体或いはア
クリル酸２−エチルヘキシル−メタクリル酸共重合体な
どのアクリル酸エステル−メタクリル酸共重合体、カル
ボキシルポリイソブチレン、エチレン−アクリル酸共重
合体、エチレン−メタクリル酸共重合体、ブタジエン−
スチレンカルボキシルエラストマー、ブタジエンアクリ
ロニトリルカルボキシルエラストマー、ブタジエン−メ
タクリロニトリルカルボキシルエラストマー、ブタジエ
ン−塩化ビニリデンカルボキシルエラストマー、ポリク
ロロプレンカルボキシルエラストマー、ポリエチレンカ
ルボキシルエラストマー或いはポリイソブチレンカルボ
キシルエラストマーなどのエマルジョン、水溶液又はデ
ィスパージョンが挙げられる。On the other hand, as the above organic binder, an alkyl acrylate-acrylonitrile-methacrylic acid copolymer, isobutylene-maleic anhydride copolymer, butadiene-methacrylic acid copolymer, isoprene-acrylic acid copolymer, acrylic Butyl acrylate-acrylic acid copolymer or acrylic acid 2-ethylhexyl-methacrylic acid copolymer acrylic acid ester-acrylic acid copolymer, butyl acrylate-methacrylic acid copolymer or 2-ethylhexyl acrylate-methacrylic acid Acrylic ester-methacrylic acid copolymer such as copolymer, carboxyl polyisobutylene, ethylene-acrylic acid copolymer, ethylene-methacrylic acid copolymer, butadiene-
Examples thereof include emulsions, aqueous solutions or dispersions of styrene carboxyl elastomer, butadiene acrylonitrile carboxyl elastomer, butadiene-methacrylonitrile carboxyl elastomer, butadiene-vinylidene chloride carboxyl elastomer, polychloroprene carboxyl elastomer, polyethylene carboxyl elastomer or polyisobutylene carboxyl elastomer.

【００４７】エマルジョン、水溶液、ディスパーション
等の形態の高分子物質は、セメント系無機質接合剤との
親和性がよく、容易に混練することができる。The polymeric substance in the form of emulsion, aqueous solution, dispersion or the like has a good affinity with the cement-based inorganic binder and can be easily kneaded.

【００４８】また、樹脂又は／ゴムの水性高分子物質と
して、上述したエマルジョン等の液体状のものを採用で
きるのみならず、たとえば、パウダー状の水性高分子物
質を採用することができる。Further, as the aqueous polymer substance of resin or / rubber, not only the liquid substance such as the above-mentioned emulsion can be adopted, but also the aqueous polymer substance in powder form can be adopted.

【００４９】たとえば、水を加えることによって、容易
にエマルジョン化する酢酸ビニル・ベオバ共重合樹脂等
を採用することによって、補強層を形成する際の作業性
が格段に向上する。For example, by adopting a vinyl acetate / veova copolymer resin or the like which is easily emulsified by adding water, the workability in forming the reinforcing layer is remarkably improved.

【００５０】また、樹脂及び／又はゴムの水性高分子物
質に官能基を含有させることができる。Further, a functional group can be contained in the aqueous polymer material of resin and / or rubber.

【００５１】官能基としては、石灰ケイ酸質接合剤やそ
の水硬反応によって生成した陽イオンや陰イオンとイオ
ン結合したり、配位結合し易い基、更に水素結合を生じ
たり、水酸基のように酸素の不対電子に起因して陽イオ
ンを引き付けて結合するような基が考えられる。As the functional group, a group which forms an ionic bond with a lime siliceous bonding agent or a cation or anion produced by the hydraulic reaction thereof, a group which easily forms a coordinate bond, a hydrogen bond, or a hydroxyl group. It is considered that there is a group that attracts and bonds a cation due to the unpaired electron of oxygen.

【００５２】たとえば、カルボキシル基、水酸基、メチ
ロール基、酸アミド基、ヒドロキシエチル基、ヒドロキ
シプロキル基又はエポキシ基から選ばれた少なくとも１
種を採用することができる。For example, at least one selected from a carboxyl group, a hydroxyl group, a methylol group, an acid amide group, a hydroxyethyl group, a hydroxypropyl group or an epoxy group.
Seeds can be adopted.

【００５３】具体的には、例えば官能基がカルボキシル
基（−ＣＯＯＨ）である場合、この（−ＣＯＯＨ）は水
中で電離しており、２つの（−ＣＯＯＨ）から発生した
２つの水素イオンが１個のカルシウムイオンと置換して
化学的に架橋するので、耐熱性や水密性が格段に向上す
るのである。Specifically, for example, when the functional group is a carboxyl group (-COOH), this (-COOH) is ionized in water, and two hydrogen ions generated from two (-COOH) are 1 Since it replaces individual calcium ions and chemically crosslinks, heat resistance and watertightness are remarkably improved.

【００５４】樹脂及び／又はゴムの水性高分子物質に官
能基を含有させることにより、石灰ケイ酸質接合剤中の
金属イオンや石灰ケイ酸質接合剤が水と反応して生成し
たカルシウムシリケート水和物に起因するカルシウムイ
オン更に水酸化カルシウムからのカルシウムイオンと架
橋反応を起こすことによって、水性高分子物質と石灰ケ
イ酸質接合剤とが互いに結合する。この結果、この架橋
物が骨材間の緩和剤としての機能を発揮し、従来のもの
に比較して、ひび割れを防止し、接着性のみならず水密
性等の被覆材としての性能を格段に向上させるのであ
る。By adding a functional group to an aqueous polymer substance of resin and / or rubber, calcium silicate water produced by reacting metal ions in the lime siliceous binder and the lime siliceous binder with water. The aqueous polymeric substance and the lime siliceous binder are bound to each other by causing a cross-linking reaction with the calcium ion derived from the union and the calcium ion from the calcium hydroxide. As a result, this crosslinked product exerts a function as a relaxing agent between aggregates, prevents cracking, and significantly improves the performance as a covering material such as adhesiveness as well as watertightness as compared with conventional ones. To improve.

【００５５】また、セメントの硬化に際しては、水和反
応及び水の蒸発が原因で体積収縮が起こる。この体積収
縮は約８％程度と言われているが、官能基を含有する樹
脂及び／又はゴムが、石灰ケイ酸質接合剤中の金属イオ
ンや石灰ケイ酸質接合剤が水と硬化反応して生成したカ
ルシウムシリケート水和物に起因するカルシウムイオン
更に水酸化カルシウムからのカルシウムイオンと架橋反
応を起こすことによって硬化物に弾力性が生じる。ま
た、骨材を覆うようにして、高分子物質の膜が形成され
る。この結果、水硬反応に起因する収縮の応力を緩和
し、補強層形成の際、あるいは温度が上昇した際のひび
割れの発生が防止される。When the cement is hardened, volume contraction occurs due to the hydration reaction and the evaporation of water. It is said that this volume shrinkage is about 8%, but the resin and / or rubber containing a functional group causes the metal ions in the lime siliceous bonding agent and the lime siliceous bonding agent to undergo a hardening reaction with water. The cured product has elasticity by causing a cross-linking reaction with the calcium ion derived from the calcium silicate hydrate thus produced and further with the calcium ion from the calcium hydroxide. Further, a film of a polymer substance is formed so as to cover the aggregate. As a result, the stress of shrinkage caused by the hydraulic reaction is relaxed, and cracks are prevented from being formed when the reinforcing layer is formed or when the temperature rises.

【００５６】この結果、弾力性を備えながら、防水性、
耐候性等に優れた被覆層を形成することができる。As a result, while having elasticity, waterproofness,
It is possible to form a coating layer having excellent weather resistance and the like.

【００５７】たとえば、石灰ケイ酸質接合剤を必須成分
とするセメント系無機質接合剤（Ａ）及び樹脂及び／又
はゴムの水性高分子物質等の有機質接合剤（Ｂ）とを必
須成分とする接合剤を採用する場合においては、被覆材
の重量に対して、接合剤（Ａ＋Ｂ）の配合割合を２０〜
４０重量％、好ましくは、２５〜３５重量％とするのが
望ましい。接合剤成分が２０重量％未満であると、被覆
層の機械的強度が低下するとともに、防水性等が低下す
る。一方、４０重量％を超えると、補強層形成時にひび
割れ等が生じやすく。また柔軟性が低下する。For example, a cement inorganic bonding agent (A) containing a lime siliceous bonding agent as an essential component and an organic bonding agent (B) such as an aqueous polymer substance of resin and / or rubber as an essential component are bonded. When the agent is used, the mixing ratio of the bonding agent (A + B) is 20 to the weight of the coating material.
It is desirable that the amount is 40% by weight, preferably 25 to 35% by weight. When the content of the bonding agent component is less than 20% by weight, the mechanical strength of the coating layer is reduced and the waterproof property is reduced. On the other hand, if it exceeds 40% by weight, cracks and the like are likely to occur during formation of the reinforcing layer. In addition, flexibility decreases.

【００５８】一方、樹脂及び／又はゴムの水性高分子物
質等の有機質接合剤（Ｂ）の配合割合は、樹脂及び／又
はゴムの水性高分子物質の種類によっても異なるが、被
覆材の重量に対して、１０重量％〜３０重量％とするの
が好ましい。On the other hand, the blending ratio of the organic binder (B) such as the aqueous polymer substance of resin and / or rubber varies depending on the kind of the aqueous polymer substance of resin and / or rubber, but it depends on the weight of the coating material. On the other hand, it is preferably 10 to 30% by weight.

【００５９】（Ｂ）が１０重量％未満では、骨材間の樹
脂成分が少なくなり、柔軟性の高い被覆層を形成するこ
とができない。また、変形能が少ないため被覆対象物の
変形等に追随することができず、十分な防水性能を発揮
できない。When the content of (B) is less than 10% by weight, the resin component between the aggregates is small, and it is not possible to form a highly flexible coating layer. Further, since the deformability is small, it is impossible to follow the deformation of the object to be coated and the like, so that sufficient waterproof performance cannot be exhibited.

【００６０】一方、（Ｂ）が、３０重量％を越えると骨
材の配合割合が低下して、荷重支持能力が低下する。On the other hand, if the content of (B) exceeds 30% by weight, the proportion of the aggregate is reduced, and the load supporting ability is reduced.

【００６１】骨材として種々のものを採用することがで
きるが、たとえば、二酸化ケイ素を主成分とするケイ
砂、炭酸カルシウムを主成分とする石粉、鉱滓、軽量骨
材から選ばれた少なくとも１種を配合することができ
る。Various materials can be used as the aggregate. For example, at least one selected from silica sand containing silicon dioxide as a main component, stone powder containing calcium carbonate as a main component, slag, and lightweight aggregate. Can be blended.

【００６２】この場合、上記骨材から選ばれた少なくと
も１種（Ｃ）の配合割合は、被覆材の重量に対して、４
５〜８０重量％、好ましくは、５０〜７０重量％に設定
するのが望ましい。In this case, the compounding ratio of at least one kind (C) selected from the above aggregates is 4 with respect to the weight of the covering material.
It is desirable to set 5 to 80% by weight, preferably 50 to 70% by weight.

【００６３】（Ｃ）が４５重量％未満では、接合剤成分
が多くなるため、被覆層形成の際等に被覆層が大きく収
縮する恐れがある。一方、（Ｃ）が８０重量％を超える
と、骨材間の接合強度が低下して、被覆層の強度、荷重
支持能力が低下する。When the content of (C) is less than 45% by weight, the amount of the bonding agent component is large, so that the coating layer may be largely shrunk when the coating layer is formed. On the other hand, when (C) is more than 80% by weight, the joint strength between the aggregates is lowered, and the strength of the coating layer and the load supporting ability are lowered.

【００６４】このように、骨材としてケイ砂や石粉を加
えると、石灰ケイ酸質接合剤の水硬反応によって生成し
たカルシウムイオンが、ケイ砂等を構成するシリカ等に
吸着されて、カルシウムジシリケートが生成し、このカ
ルシウムジシリケート層と樹脂及び／又はゴムの水性高
分子物質が、ケイ砂、石粉、鉱滓或いはセメントゲルか
ら選ばれた少なくとも１種と、強固に接合するととも
に、緻密で、しかも体積収縮が少なくなって、補強層形
成の際のひび割れ等も少なくなる。As described above, when silica sand or stone powder is added as an aggregate, calcium ions generated by the hydraulic reaction of the lime siliceous binder are adsorbed by silica or the like which constitutes silica sand, etc. Silicate is formed, and the calcium disilicate layer and the aqueous polymer material of resin and / or rubber firmly bond with at least one selected from silica sand, stone powder, slag or cement gel, and are dense and Moreover, volume shrinkage is reduced, and cracks and the like when forming the reinforcing layer are reduced.

【００６５】本願の請求項２に記載した発明は、０．５
μｍ〜５μｍの硬質微粒子を、３重量％〜１５重量％配
合したことを特徴とするものである。The invention described in claim 2 of the present application is 0.5
It is characterized in that 3 to 15% by weight of hard fine particles of 5 to 5 μm are mixed.

【００６６】上記硬質微粒子物質は、接着強化剤として
配合されるものであり、骨材間の接合力を高めるのみな
らず、表面に形成される防火層、あるいは内面に形成さ
れる防水下地層に対する接着力が高まる。The above-mentioned hard fine particle substance is blended as an adhesion strengthening agent, and not only enhances the bonding force between the aggregates, but also to the fireproof layer formed on the surface or the waterproof underlayer formed on the inner surface. Adhesive strength increases.

【００６７】硬質微粒子物質を配合することにより、接
着性能が高まる機構は明らかでないが、セメント等の無
機質接合剤及び／又は樹脂等の水性高分子物質の平均自
由半径とオーダー的に近似した大きさの硬質微粒子が存
在することにより、無機質接合剤及び／又は水性高分子
物質の主鎖の一部の自由度が拘束される結果、主鎖全体
の運動が抑制され、隣接分子との間の作用力が低分子間
の作用と同様の関係になり、分子間結合をさらに促進さ
せるためと考えることができる。Although the mechanism of enhancing the adhesive performance by incorporating the hard fine particle substance is not clear, the size is orderly approximated to the average free radius of the inorganic binder such as cement and / or the aqueous polymer substance such as resin. The presence of such hard fine particles restrains a part of the degree of freedom of the main chain of the inorganic binder and / or the aqueous polymer substance, and as a result, the movement of the whole main chain is suppressed and the action between adjacent molecules is exerted. It can be considered that the force has the same relationship as the action between the small molecules and further promotes the intermolecular bond.

【００６８】特に、粒径０．５μｍ〜５μｍ程度の硬質
微粒子を添加することにより、接着強度を格段に高める
ことができる。このことは、たとえば、アクリル樹脂等
の合成樹脂エマルジョン中の樹脂粒子の径が０．０１μ
ｍ〜１μｍであり、硬質微粒子物質の粒径に近いオーダ
ーであることから推測することができる。したがって、
できれば１μｍ〜２μｍ程度の粒径の硬質微粒子を配合
するのが好ましい。In particular, the addition of hard fine particles having a particle size of about 0.5 μm to 5 μm can significantly increase the adhesive strength. This means that, for example, the diameter of resin particles in a synthetic resin emulsion such as an acrylic resin is 0.01 μm.
It can be estimated from m to 1 μm, which is on the order of the particle size of the hard particulate material. Therefore,
If possible, it is preferable to add hard fine particles having a particle diameter of about 1 μm to 2 μm.

【００６９】硬質微粒子物質の粒径が５μｍ以上になる
と、骨材の粒径に近づき、接着力の増加を期待できな
い。一方、０．５μｍ以下の粒径になると、混練の際に
飛散しやすくなり、取り扱いにくい。When the particle size of the hard particulate material is 5 μm or more, the particle size approaches that of the aggregate, and an increase in adhesive strength cannot be expected. On the other hand, when the particle size is 0.5 μm or less, the particles tend to be scattered during kneading and are difficult to handle.

【００７０】なお、接着強化剤の全部が５μｍ以下であ
る必要はなく、５μｍ以下の粒径の硬質微粒子を所定量
含むものであれば、十分な効果を期待することができ
る。また、１μｍ以下の粒子を含むものであればより望
ましい。It is not necessary that all the adhesion strengthening agents have a size of 5 μm or less, and a sufficient effect can be expected as long as they contain a predetermined amount of hard fine particles having a particle size of 5 μm or less. Further, it is more preferable that the particles include particles of 1 μm or less.

【００７１】また、硬質微粒子物質の配合割合は、被覆
層の硬さ、厚さ等に応じて変更することができる。接合
剤、骨材の配合割合から、接着力等を向上させるに最も
好ましい割合を選定すればよく、一般に、３重量％〜１
５重量％の間で選択することができる。The mixing ratio of the hard particulate material can be changed according to the hardness and thickness of the coating layer. The most preferable ratio for improving the adhesive strength and the like may be selected from the mixing ratios of the bonding agent and the aggregate, and generally 3% by weight to 1%.
It can be selected between 5% by weight.

【００７２】硬質微粒子物質として、たとえば、微粉末
鉱滓、フライアッシュ、シリカフューム、ポゾラン、又
はゼオライトが挙げられる。Examples of the hard particulate material include fine powder slag, fly ash, silica fume, pozzolan, or zeolite.

【００７３】本願の請求項３に記載した発明は、骨材と
して、２種以上の粒径のものを配合したものである。In the invention described in claim 3 of the present application, aggregates having two or more kinds of particle diameters are mixed.

【００７４】粒径の異なる２種以上の骨材を配合するこ
とによって、被覆材の耐ひび割れ性、接着性、変形能を
大幅に向上させることができる。By mixing two or more kinds of aggregates having different particle sizes, the crack resistance, adhesiveness and deformability of the covering material can be greatly improved.

【００７５】粒径の異なる２種以上の骨材を配合するこ
とによって、上記効果が得られるのは、被覆層内での骨
材の分布が平均化され、変形した際に、骨材間に分布す
る接合剤全体に応力が作用して変形能が発揮され、一部
に変形や応力が集中することがなくなるためであると考
えられる。この結果、ひび割れ性が高まるとともに、全
体としての弾力性、変形能が高まるものと考えられる。The above effect can be obtained by mixing two or more kinds of aggregates having different particle diameters because the distribution of the aggregates in the coating layer is averaged and the aggregates are deformed. It is considered that this is because the stress acts on the entire distributed bonding agent to exert the deformability, and the deformation and the stress are not concentrated on a part. As a result, it is considered that the crackability is enhanced and the elasticity and deformability as a whole are enhanced.

【００７６】また、骨材間の隙間の大きさが小さくなる
結果、接合剤が硬化する際の各隙間の収縮量が平均化さ
れ、硬化時に被覆層の一部に応力が集中することがなく
なる。このため、接着力が高まるものと考えられる。Further, as a result of the size of the gap between the aggregates being reduced, the shrinkage amount of each gap when the cement is cured is averaged, and stress is not concentrated on a part of the coating layer during curing. . Therefore, it is considered that the adhesive strength is increased.

【００７７】一方、骨材間の隙間が小さくなることから
圧縮方向の変形抵抗が大きくなり、荷重支持能力が高ま
る。On the other hand, since the gap between the aggregates is reduced, the deformation resistance in the compression direction is increased, and the load supporting ability is increased.

【００７８】上記２種以上の粒径として、平均粒度の比
が８ないし１２である２種以上の骨材を配合するのが好
ましい。平均粒度の比が５以下であると、オーダの近接
した粒子が増加して、骨材の分布にばらつきが生じる恐
れが出る。一方、平均粒度の比が１２以上になると、大
粒子の分布にばらつきが出て、骨材間の力の伝達を均一
に行うことができなくなり、荷重支持能力にばらつきが
生じ、ひび割れ等の発生につながる。As the above-mentioned two or more kinds of particle size, it is preferable to mix two or more kinds of aggregates having an average particle size ratio of 8 to 12. When the ratio of the average particle size is 5 or less, the number of particles close to the order increases, and the aggregate distribution may vary. On the other hand, when the ratio of the average particle size is 12 or more, the distribution of large particles becomes uneven, and it becomes impossible to uniformly transmit the force between the aggregates, resulting in the uneven load supporting ability and the occurrence of cracks. Leads to.

【００７９】粒度の異なる骨材としては、たとえば、粒
度の異なるケイ砂と炭酸カルシウムのように、粒度の異
なる異種の骨材を採用することもできるし、同種の骨材
で粒度のみ異なるものを採用することもできる。As aggregates having different grain sizes, different types of aggregates having different grain sizes such as silica sand and calcium carbonate having different grain sizes can be adopted, or aggregates of the same type but different in grain size can be used. It can also be adopted.

【００８０】通常、天然の骨材は粒度分布をもってお
り、平均粒度を尺度として採用することができる。Usually, natural aggregate has a particle size distribution, and the average particle size can be used as a scale.

【００８１】骨材の粒径は形成しようとする補強層の厚
さ、表面性状、樹脂構造物の種類等によって決定される
が、最大粒度が５００μｍ以下のものを採用することに
よって、滑らかな表面を備える薄い被覆層を形成するこ
とが可能となる。特に、好ましくは、最大粒度を３００
μｍ以下に設定するのが好ましい。The particle size of the aggregate is determined by the thickness of the reinforcing layer to be formed, the surface texture, the type of the resin structure, etc., but the maximum particle size of 500 μm or less is used to obtain a smooth surface. It is possible to form a thin coating layer comprising Particularly preferably, the maximum particle size is 300
It is preferably set to be less than or equal to μm.

【００８２】被覆層の厚さは、樹脂構造物の種類、補強
の目的等によって異なるが、骨材の粒径等を選択するこ
とによって、０．２ｍｍ程度から数ｃｍまで形成するこ
とができる。The thickness of the coating layer varies depending on the type of resin structure, the purpose of reinforcement, etc., but can be formed from about 0.2 mm to several cm by selecting the particle size of the aggregate.

【００８３】本願発明に係る補強層は、エアガン等を用
いたり、刷毛等を用いて樹脂構造物の外面等に容易に形
成することができる。The reinforcing layer according to the present invention can be easily formed on the outer surface or the like of the resin structure by using an air gun or a brush.

【００８４】本願の請求項４に記載した発明は、上述し
た柔軟な防水被覆材を用いて、従来にない防水被覆構造
を形成しようとするものである。The invention described in claim 4 of the present application is intended to form a waterproof coating structure which has not been hitherto used, by using the above-mentioned flexible waterproof coating material.

【００８５】本願発明に係る防水被覆の構造は、本願の
請求項１ないし請求項３のいずれかに記載した防水被覆
材によって形成された防水補強層と、防火性を備える被
覆材によって、上記防水補強層の外面に積層形成される
防火層とを備える。The structure of the waterproof coating according to the present invention comprises the waterproof reinforcing layer formed by the waterproof coating material according to any one of claims 1 to 3 of the present application and the fireproof coating material. A fireproof layer laminated on the outer surface of the reinforcing layer.

【００８６】上記防水補強層は、上述したように、高い
防水性能を備えるとともに、柔軟であり変形能が大きい
とともに、接着性能が高い。As described above, the waterproof reinforcing layer has high waterproof performance, is flexible and has a large deformability, and has high adhesive performance.

【００８７】したがって、この防水補強層を被覆対象物
の表面に形成することにより、被覆対象物表面の変形、
動き等によく追随する。このため、被覆対象物の変形に
起因する、防水性能の破壊を防止することができる。Therefore, by forming this waterproof reinforcing layer on the surface of the coated object, the deformation of the surface of the coated object,
Follows movements well. Therefore, it is possible to prevent the waterproof performance from being destroyed due to the deformation of the covering object.

【００８８】たとえば、コンクリートの下地にひび割れ
が生じても、その部分の防水補強層が伸縮してこれに対
応し、防水性が低下することはない。For example, even if a crack is generated in the base of concrete, the waterproof reinforcing layer at that portion expands and contracts, and the waterproof property does not deteriorate.

【００８９】また、防水補強層は骨材を含むため、荷重
支持能力が高く、防火層に圧縮力が作用しても、防水被
覆自体が大きく変形することはない。このため、歩行や
駐車場に供する防水床を構成することも可能となる。Further, since the waterproof reinforcing layer contains aggregates, it has a high load-bearing capacity, and the waterproof coating itself is not largely deformed even when a compressive force acts on the fireproof layer. Therefore, it is possible to configure a waterproof floor for walking and parking.

【００９０】さらに、一般に防火層は変形能が低く、防
水補強層の変形が大きくなると、ひび割れ等が生じる。
一方、防水性能は上記防水補強層で維持することができ
る。このため、被覆対象物のひび割れ等の異常を、防水
被覆の表面から目視により早期に発見することが可能と
なる。この結果、防水被覆の性能を長期にわたって維持
管理することが可能となり、信頼性の高い防水被覆の構
造を形成することができる。Further, the fireproof layer generally has a low deformability, and when the deformation of the waterproof reinforcing layer becomes large, cracks or the like occur.
On the other hand, the waterproof performance can be maintained by the waterproof reinforcing layer. For this reason, it becomes possible to detect an abnormality such as a crack of the object to be covered by visual inspection from the surface of the waterproof covering at an early stage. As a result, the performance of the waterproof coating can be maintained for a long period of time, and a highly reliable waterproof coating structure can be formed.

【００９１】上記防火性を備える被覆材として、種々の
ものを用いることができる。たとえば、防水補強層を形
成する防水被覆材の有機質接合剤の配合割合を低下させ
る一方、セメント性無機質接合剤及び骨材の配合割合を
増加させることによって形成される防火被覆材を採用す
ることができる。Various materials can be used as the coating material having the fireproof property. For example, it is possible to adopt a fireproof coating material formed by increasing the mixing ratio of the cementitious inorganic bonding agent and the aggregate while decreasing the mixing ratio of the organic bonding agent of the waterproof coating material forming the waterproof reinforcing layer. it can.

【００９２】上記防火被覆材は、有機質接合剤の配合割
合を１．５重量％〜８重量％まで低下させることによっ
て得られるものであり、その分セメント系無機質接合剤
及び骨材の配合割合を増加させたものである。The above-mentioned fireproof coating material is obtained by reducing the compounding ratio of the organic binder to 1.5% to 8% by weight, and the mixing ratio of the cement-based inorganic binder and the aggregate is increased accordingly. It is an increase.

【００９３】有機質接合剤の配合割合を低下させること
により、被覆層の機械的強度が高まり、また、耐候性、
耐磨耗性、耐熱性が高まる。By reducing the blending ratio of the organic binder, the mechanical strength of the coating layer is increased, and the weather resistance,
Increased wear resistance and heat resistance.

【００９４】さらに、有機質接合剤の配合割合を１．５
〜５重量パーセントにまで低下させると、上記防火被覆
材は火炎によって表面からしだいに変質させられて、骨
材間に空隙が形成され、多孔質状に変化するという特性
を発現する。Furthermore, the blending ratio of the organic binder is 1.5.
When the content is reduced to -5% by weight, the fireproof coating material is gradually modified from the surface by a flame to form voids between the aggregates and exhibits a property of being changed into a porous state.

【００９５】すなわち、骨材間の空隙を埋めるようにし
て存在する接合剤が、骨材の移動を伴うことなく変質し
て、骨材間に空隙を形成するのである。したがって、防
火層自体が大きく変形することもなく、また、防水補強
層に対する接着力が火炎によって大きく低下することな
く断熱性が高まる。この結果、防火性のみならず、高い
耐火性能を発揮するようになる。That is, the bonding agent existing so as to fill the voids between the aggregates is altered without moving the aggregates to form voids between the aggregates. Therefore, the fireproof layer itself is not significantly deformed, and the adhesive strength to the waterproof reinforcing layer is not significantly reduced by the flame, and the heat insulating property is enhanced. As a result, not only fire resistance but also high fire resistance performance is exhibited.

【００９６】上記接合剤の変質は解明されていないが、
樹脂成分等の炭化、酸化、昇華、収縮や、セメント系無
機質接合剤に含まれる結合水の放出等によって達成され
るものと考えられる。Although the alteration of the above-mentioned bonding agent has not been clarified,
It is considered to be achieved by carbonization, oxidation, sublimation, shrinkage of the resin component or the like, or release of bound water contained in the cement-based inorganic bonding agent.

【００９７】一方、上記防火層は、通常多孔質ではな
く、通常の被覆層として機能する。しかも、有機質成分
が配合されているため、防水性能も優れている。On the other hand, the above-mentioned fireproof layer is not usually porous, but functions as an ordinary coating layer. Moreover, since it contains organic components, it has excellent waterproof performance.

【００９８】さらに、防水補強層と共通の有機接合剤を
採用することにより、防水補強層に対する接着強度を高
めることができる。このため、層間剥離が生じることも
なく、強靱な防水被覆を形成することができる。Further, by adopting the same organic bonding agent as the waterproof reinforcing layer, the adhesive strength to the waterproof reinforcing layer can be increased. Therefore, a strong waterproof coating can be formed without delamination.

【００９９】本願の請求項５に記載した発明は、請求項
４に記載した防水被覆を構成する防火層及び防水補強層
に加えて防水下地層を形成したものである。According to the invention described in claim 5 of the present application, a waterproof underlayer is formed in addition to the fireproof layer and the waterproof reinforcing layer constituting the waterproof coating described in claim 4.

【０１００】上記防水下地層は、弾性変形可能な樹脂又
は／及びゴムの高分子物質を含んで形成され、引張破断
にいたる変形量を上記防火層及び防水補強層よりも大き
く設定している。The waterproof underlayer is formed by containing a polymeric substance of elastically deformable resin or / and rubber, and the deformation amount up to tensile rupture is set to be larger than that of the fireproof layer and the waterproof reinforcing layer.

【０１０１】すなわち、変形能の大きい層を下地層とし
て形成し、その上に防水補強層、防火層を形成するので
ある。That is, a layer having a large deformability is formed as an underlayer, and a waterproof reinforcing layer and a fireproof layer are formed thereon.

【０１０２】上記構成によって、防水被覆層内部の変形
能がさらに大きくなり、被覆対象物表面の割れ、変形、
移動等に十分追随して変形することができるこのため、
防水性能を長期に渡って維持することができる。With the above structure, the deformability inside the waterproof coating layer is further increased, and the surface of the coating object is cracked, deformed, or deformed.
Because it can be deformed sufficiently following movement
The waterproof performance can be maintained for a long time.

【０１０３】しかも、上記防水下地層の引張破断にいた
る変形量を上記防火層及び防水補強層よりも大きく設定
しているため、上記上記防火層あるいは防水補強層にひ
び割れ等が生じても、防水性能を維持することができ
る。Moreover, since the deformation amount of the waterproof underlayer leading to the tensile rupture is set to be larger than that of the fireproof layer and the waterproof reinforcing layer, even if the fireproof layer or the waterproof reinforcing layer is cracked, the waterproof layer is waterproof. The performance can be maintained.

【０１０４】また、ひび割れが、最外側に形成される防
火層から生じるため、防水被覆の異常を目視によって早
期に発見して補修することができる。このため、防水性
能の維持管理を容易に行うことが可能となり、信頼性の
高い防水被覆の構造を提供することができる。Further, since the cracks are generated from the fireproof layer formed on the outermost side, the abnormality of the waterproof coating can be visually detected and repaired at an early stage. Therefore, it becomes possible to easily maintain and manage the waterproof performance, and it is possible to provide a highly reliable waterproof coating structure.

【０１０５】上記防水下地層を形成する防水被覆材とし
て、上記防水補強層及び防火層に、接合剤として採用し
た樹脂成分を含むものを採用するのが好ましい。各層の
層間における接着力が高まるからである。As the waterproof covering material for forming the waterproof underlayer, it is preferable to adopt a waterproof coating material containing the resin component adopted as the bonding agent in the waterproof reinforcing layer and the fireproof layer. This is because the adhesion between the layers is increased.

【０１０６】たとえば、アクリル酸アルキルエステル・
アクリルニトリル・メタクリル酸共重合体水性エマルジ
ョン等を被覆対象物の表面に塗布して防水下地層を形成
することができる。For example, acrylic acid alkyl ester
A waterproof underlayer can be formed by applying an acrylonitrile / methacrylic acid copolymer aqueous emulsion or the like to the surface of the object to be coated.

【０１０７】上記各層の厚さは、要求される防火性能、
防水性能、あるいは、被覆対象物の特性、表面性状、各
被覆材の特性等によって決定することができる。The thickness of each of the above layers depends on the required fire protection performance,
It can be determined by the waterproof performance, the characteristics of the object to be coated, the surface properties, the characteristics of each coating material, or the like.

【０１０８】たとえば、防水下地層を０．５〜１ｍｍ、
防水補強層を２〜３ｍｍ、防火層を２〜３ｍｍで形成す
ることができる。For example, the waterproof underlayer is 0.5 to 1 mm,
The waterproof reinforcing layer can be formed with a thickness of 2 to 3 mm and the fireproof layer can be formed with a thickness of 2 to 3 mm.

【０１０９】もちろん、防火性能を高めるには、防火層
の厚さを大きくとればよく、一方、被覆対象物の変形が
大きい場合には、防水下地層及び防水補強層の厚さを大
きくとればよい。Of course, in order to enhance the fireproof performance, the thickness of the fireproof layer may be increased, while if the deformation of the covered object is large, the thickness of the waterproof underlayer and the waterproof reinforcement layer may be increased. Good.

【０１１０】本願の請求項６に記載した発明は、上記防
火層、防水補強層、防水下地層のうち少なくとも一層に
おいて、骨材及び／又は接合剤の配合割合を厚さ方向に
連続的に変化させたものである。According to a sixth aspect of the present invention, in at least one of the fireproof layer, the waterproof reinforcing layer and the waterproof underlayer, the blending ratio of the aggregate and / or the bonding agent is continuously changed in the thickness direction. It was made.

【０１１１】上述したように、本願発明に係る防火層、
防水補強層及び防水下地層は、基本的に、骨材、有機質
接合剤、無機質接合剤を含んで構成されるとともに、各
層の上記配合成分の割合を変化させることにより構成す
ることができる。As described above, the fireproof layer according to the present invention,
The waterproof reinforcing layer and the waterproof underlayer are basically composed of an aggregate, an organic bonding agent, and an inorganic bonding agent, and can be structured by changing the ratio of the above-mentioned compounding components of each layer.

【０１１２】したがって、上記配合割合を連続的に変化
させることにより、より少ない厚さで、防火性能、防水
性能の高い防水被覆を構成することができる。Therefore, by continuously changing the above-mentioned mixing ratio, a waterproof coating having a high fireproof performance and a high waterproof performance can be constructed with a smaller thickness.

【０１１３】上記配合割合を連続的に変化させる手段と
して、各層を複数の工程に分けて塗着形成するととも
に、各工程の配合成分を変化させることが考えられる。As a means for continuously changing the blending ratio, it is conceivable that each layer is divided into a plurality of steps for coating and formed, and the blending component in each step is changed.

【０１１４】また、本願発明に係る防水被覆の構造は、
建築された建物に限定されることはなく、工場において
板状の材料に適用することもできる。したがって、配合
成分をコントロールしながら吹き付け器から噴射しつ
つ、防水被覆を形成することも可能である。Further, the structure of the waterproof coating according to the present invention is
It is not limited to built buildings, but can also be applied to plate-shaped materials in factories. Therefore, it is possible to form a waterproof coating while controlling the blending components and spraying from a spraying device.

【０１１５】なお、配合成分を連続的に変化させるの
は、請求項７に記載した発明のように、全層にわたって
変化させてもよく、また、防火層、防水補強層あるいは
防水下地層のうちから選択された１層であってもよい。The composition components may be continuously changed, as in the invention described in claim 7, over all the layers, and among the fireproof layer, waterproof reinforcing layer or waterproof underlayer. It may be one layer selected from.

【０１１６】[0116]

【作用】図１及び図２に基づいて本願発明に係る防水被
覆材の作用を説明する。なお、これらの図は、本願発明
に係る被覆材の内部構造を模式的に表している。The operation of the waterproof coating material according to the present invention will be described with reference to FIGS. 1 and 2. Note that these drawings schematically show the internal structure of the covering material according to the present invention.

【０１１７】図１に示すように、被覆材１の内部には、
骨材８を取り囲むようにして接合剤３が存在する。As shown in FIG. 1, inside the covering material 1,
The bonding agent 3 is present so as to surround the aggregate 8.

【０１１８】上記骨材８は変形不可能である一方、上記
接合剤は変形可能である。したがって、図２に示すよう
に、上記構成の被覆材１に圧縮力Ｆが作用すると、上記
接合剤３が変形して、骨材８が互いに近接させられる。The aggregate 8 is not deformable, while the cement is deformable. Therefore, as shown in FIG. 2, when the compressive force F acts on the covering material 1 having the above structure, the bonding agent 3 is deformed and the aggregates 8 are brought close to each other.

【０１１９】このため、被覆材１に一定以上の変形が生
じると圧縮抵抗が急激に増加し、圧縮力が上記骨材８に
よって支持されることになる。したがって、樹脂接合剤
のみで形成される被覆層に比べて変形が極めて小さくな
り、荷重支持能力が向上する。Therefore, when the covering material 1 is deformed to a certain extent or more, the compression resistance rapidly increases and the compressive force is supported by the aggregate 8. Therefore, the deformation is extremely small as compared with the coating layer formed only of the resin bonding agent, and the load supporting ability is improved.

【０１２０】一方、引張変形に対しては上記骨材は関与
せず、接合剤が破壊するまで変形することができる。し
たがって、上記接合剤の変形特性、骨材の配合割合等を
調節することによって、種々の特性を備える被覆材を形
成することが可能となる。On the other hand, the above-mentioned aggregate does not participate in the tensile deformation, and it can be deformed until the cement is broken. Therefore, it becomes possible to form a covering material having various characteristics by adjusting the deformation characteristics of the bonding agent, the mixing ratio of the aggregate, and the like.

【０１２１】[0121]

【実施例】以下、本願発明に係る実施例を、図１、表１
及び表２に基づいて説明する。EXAMPLES Examples according to the present invention will be described below with reference to FIG. 1 and Table 1.
And it demonstrates based on Table 2.

【０１２２】図１に、本願発明に係る防水被覆４の断面
構造を示す。FIG. 1 shows a sectional structure of the waterproof coating 4 according to the present invention.

【０１２３】図１に示すように、防水被覆４は、被覆の
最外側に形成される防火層６と、被覆対象物２の表面に
形成される防水下地層５と、上記防火層６と防水下地層
５との間に形成される防水補強層７とを備えて構成され
る。As shown in FIG. 1, the waterproof coating 4 comprises a fireproof layer 6 formed on the outermost side of the coating, a waterproof base layer 5 formed on the surface of the object 2 to be coated, the fireproof layer 6 and the waterproof layer 6. The waterproof reinforcing layer 7 formed between the base layer 5 and the base layer 5 is provided.

【０１２４】表１に、上記防火層６を形成する防火被覆
材の成分構成の例を示す。Table 1 shows an example of the composition of the fireproof coating material forming the fireproof layer 6.

【０１２５】[0125]

【表１】 [Table 1]

【０１２６】表２に、上記防水補強層７を形成する防水
被覆材の成分構成の例を示す。Table 2 shows an example of the component constitution of the waterproof coating material forming the waterproof reinforcing layer 7.

【０１２７】[0127]

【表２】 [Table 2]

【０１２８】本実施例に係る防水下地層５は、上記防火
層６及び防水補強層７に採用した有機質接合剤であるア
クリル系樹脂と同じ樹脂から形成されている。The waterproof underlayer 5 according to this embodiment is formed of the same resin as the acrylic resin which is the organic bonding agent used for the fireproof layer 6 and the waterproof reinforcing layer 7.

【０１２９】具体的には、上記アクリル樹脂エマルジョ
ンを被覆対象物２の表面に塗着して構成され、１００％
以上の伸び率を備える。Concretely, the acrylic resin emulsion is applied to the surface of the object to be coated 2 and is 100%.
It has the above elongation rate.

【０１３０】なお、本実施例において、上記防水下地層
の厚さは１ｍｍ、防水補強層の厚さは２ｍｍ、防火層の
厚さは２ｍｍに設定している。In this embodiment, the waterproof underlayer has a thickness of 1 mm, the waterproof reinforcing layer has a thickness of 2 mm, and the fireproof layer has a thickness of 2 mm.

【０１３１】上記各層は、エアガンによって各被覆材を
吹き付け塗装することにより形成することができる。The above layers can be formed by spraying and coating each coating material with an air gun.

【０１３２】本願発明は、上記実施例に限定されること
はない。実施例において、接合剤としてアクリル系樹脂
を採用したが、酢酸ビニル系樹脂等他の種類の樹脂を採
用することができる。The present invention is not limited to the above embodiments. Although the acrylic resin is used as the bonding agent in the examples, other types of resins such as vinyl acetate resin can be used.

【０１３３】また、骨材等の配合割合も実施例に限定さ
れることはなく、被覆層の厚さ等に応じて変更すること
ができる。Further, the mixing ratio of the aggregate or the like is not limited to the examples, and can be changed according to the thickness of the coating layer and the like.

【図面の簡単な説明】[Brief description of drawings]

【図１】本願発明に係る被覆材の作用を説明する模式図
である。FIG. 1 is a schematic diagram illustrating the operation of a coating material according to the present invention.

【図２】本願発明に係る被覆材の作用を説明する模式図
である。FIG. 2 is a schematic view for explaining the action of the coating material according to the present invention.

【図３】本願発明に係る防水被覆の構造を示す断面図で
ある。FIG. 3 is a sectional view showing a structure of a waterproof coating according to the present invention.

【符号の説明】[Explanation of symbols]

１ 被覆材 ２ 被覆対象物 ３ 接合剤 ４ 防水被覆 ５ 防水下地層 ６ 防火層 ７ 防水補強層 ８ 骨材 DESCRIPTION OF SYMBOLS 1 Coating material 2 Covering object 3 Bonding agent 4 Waterproof coating 5 Waterproof underlayer 6 Fireproof layer 7 Waterproof reinforcement layer 8 Aggregate

Claims (7)

【特許請求の範囲】[Claims] 【請求項１】 骨材とこの骨材を相互に接合する接合剤
とを配合して構成される被覆材であって、 上記接合剤は、セメント系無機質接合剤と、樹脂及び／
又はゴムの高分子物質からなる有機質接合剤とを含み、 上記骨材の配合割合を５０重量％以上に設定する一方、 上記有機質接合剤の配合割合を１０重量％以上に設定し
たことを特徴とする、防水被覆材。1. A coating material formed by mixing an aggregate and a bonding agent for bonding the aggregates to each other, wherein the bonding agent is a cement-based inorganic bonding agent, a resin and / or
Or an organic binder made of a polymer material of rubber, wherein the compounding ratio of the aggregate is set to 50% by weight or more, while the compounding ratio of the organic binder is set to 10% by weight or more. Yes, waterproof covering material. 【請求項２】 ０．５μｍ〜５μｍの硬質微粒子を、３
重量％〜１５重量％配合したことを特徴とする請求項１
に記載の防水被覆材。2. A hard fine particle of 0.5 μm to 5 μm is added to 3
% To 15% by weight, wherein the composition is blended.
The waterproof coating material described in. 【請求項３】 ２種以上の粒径の骨材を配合したことを
特徴とする、請求項１又は請求項２のいずれかに記載の
防水被覆材。3. The waterproof coating material according to claim 1, wherein the aggregate has two or more kinds of particle diameters. 【請求項４】 上記請求項１ないし請求項３のいずれか
に記載した防水被覆材によって、被覆対象物表面側に形
成される防水補強層と、 防火性を備える被覆材によって、上記防水補強層の外面
に積層形成される防火層とを備えて構成される防水被覆
の構造。4. A waterproof reinforcing layer formed on the surface side of an object to be covered by the waterproof covering material according to any one of claims 1 to 3, and a waterproof reinforcing layer comprising a fireproof covering material. A structure of a waterproof coating configured to include a fireproof layer laminated on the outer surface of the. 【請求項５】 防水被覆の最外側に形成される防火層
と、被覆対象物表面に形成される防水下地層と、上記防
火層と防水下地層との間に形成される防水補強層とを備
えて構成される防水被覆の構造において、 上記防火層は、防火性を有する被覆材から形成される一
方、 上記防水補強層は、請求項１ないし請求項３のいずれか
に記載した防水被覆材から形成されており、 上記防水下地層は、弾性変形可能な樹脂又は／及びゴム
の高分子材料を含んで形成されるとともに、引張破断に
いたる変形量を上記防火層及び防水補強層よりも大きく
設定したことを特徴とする、防水被覆の構造。5. A fireproof layer formed on the outermost side of the waterproof coating, a waterproof underlayer formed on the surface of the object to be coated, and a waterproof reinforcing layer formed between the fireproof layer and the waterproof underlayer. In the structure of a waterproof coating provided, the fireproof layer is formed of a fireproof coating material, and the waterproof reinforcing layer is the waterproof coating material according to any one of claims 1 to 3. The waterproof underlayer is formed by including an elastically deformable resin or / and rubber polymer material, and has a deformation amount up to tensile rupture larger than that of the fireproof layer and the waterproof reinforcing layer. A waterproof coating structure characterized by being set. 【請求項６】 上記防火層、防水補強層、防水下地層の
うち少なくとも一層において、骨材及び／又は接合剤の
配合割合を厚さ方向に連続的に変化させている請求項４
に記載の防水被覆の構造。6. The compounding ratio of the aggregate and / or the bonding agent in at least one of the fireproof layer, the waterproof reinforcing layer and the waterproof underlayer is continuously changed in the thickness direction.
Structure of waterproof coating described in. 【請求項７】 上記防火層、防水補強層及び防水下地層
を、骨材及び／又は接合剤の配合割合を連続的に変化さ
せることにより、これら各層を一体的に形成したことを
特徴とする、防水被覆の構造。7. The fireproof layer, the waterproof reinforcing layer, and the waterproof underlayer are formed integrally by continuously changing the compounding ratio of the aggregate and / or the bonding agent. , Waterproof coating structure.