JPH0959909A - Pavement material - Google Patents

Abstract

PROBLEM TO BE SOLVED: To bring out excellent optical characteristics and strength characteristics. SOLUTION: A paving material for a surface course composed principally of aggregate grains and a binder, contains 1-50 pts.wt. of glass cullet and 0.2-3.0 pts.wt. of mica. The binder is chosen from asphalt, a substitute compound of asphalt, cement, and concrete. It is preferable to use mica coated with titanium oxide and/or iron oxide. It is preferable to use glass cullet having 5mm or finer size. Glass cullet of which surface is made coarse by rubbing or grinding and has 55% or more achievement ratio, can be used.

Description

【発明の詳細な説明】Detailed Description of the Invention

【０００１】[0001]

【発明の属する技術分野】本発明は、例えばアスファル
ト舗装の表層に使用される舗装材料であって、優れた光
学特性や強度特性等を発揮することができる表層用の舗
装材料に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a pavement material used for the surface layer of asphalt pavement, for example, which is capable of exhibiting excellent optical characteristics and strength characteristics.

【０００２】[0002]

【従来の技術】例えば、アスファルト舗装やコンクリー
ト舗装の表層に使用される舗装材料としては骨材粒子と
結合剤を主成分としたものが広く知られているが、最近
では着色効果や反射効果等の光学的特性の付与を目的と
して原料中にガラスカレットの粉末を含有させることも
試みられている（例えば、特開平６−１２８９０２号公
報参照）。2. Description of the Related Art For example, as a pavement material used for the surface layer of asphalt pavement or concrete pavement, aggregate particles and binders are widely known, but recently, coloring effect, reflection effect, etc. It has also been attempted to incorporate glass cullet powder in the raw material for the purpose of imparting the optical characteristics (see JP-A-6-128902).

【０００３】ところが、単に骨材としてガラスカレット
の粉末を加えた場合には全体的にソフトな反射が得られ
ず局部的に反射してしまうという問題点があり、特に歩
行者にとっては車のライトや太陽光が鏡面のように反射
し眩しくて危険であるという問題点があった。また、十
分なマーシャル安定度を得ることが難しく、更にはガラ
スカレットが剥離し易いという問題点もあった。However, when glass cullet powder is simply added as an aggregate, there is a problem that a soft reflection is not obtained as a whole and the light is locally reflected. Especially, for a pedestrian, a light of a car. There was a problem that the sunlight was reflected like a mirror surface and was dazzling and dangerous. Further, it is difficult to obtain sufficient Marshall stability, and further, the glass cullet is easily peeled off.

【０００４】[0004]

【発明が解決しようとする課題】本発明は上記のような
従来の問題点を解決して、全体的にソフトに反射し眩し
さを感じさせることなく優れた光学特性を発揮すること
ができるとともに、十分なマーシャル安定度を発揮する
ことができ、更にはガラスカレットの剥離もなく長期間
にわたって安定した舗装面を維持することができる舗装
材料を提供することを目的として完成されたものであ
る。DISCLOSURE OF THE INVENTION The present invention solves the above-mentioned problems of the prior art and is capable of exhibiting excellent optical characteristics without causing a soft reflection as a whole and causing no glare. The present invention has been completed for the purpose of providing a paving material capable of exhibiting sufficient Marshall stability and maintaining a stable paving surface for a long period of time without peeling of the glass cullet.

【０００５】[0005]

【課題を解決するための手段】上記の課題を解決するた
めになされた本発明の舗装材料は、骨材粒子と結合剤を
主成分とする表層用の舗装材料において、重量％で１〜
５０％のガラスカレットと０．２〜３．０％の雲母を含
有させたことを特徴とするものである。The pavement material of the present invention made to solve the above problems is a pavement material for a surface layer containing aggregate particles and a binder as main components, and the pavement material has a content of 1% by weight.
It is characterized by containing 50% of glass cullet and 0.2 to 3.0% of mica.

【０００６】[0006]

【発明の実施の形態】本発明において使用される骨材粒
子としては砕石、砂利、砂などの舗装用骨材を用いるこ
とができ、また結合剤としてはアスファルト、アスファ
ルト代替組成物、セメント、コンクリートから選ばれた
ものを用いることができる。ここで、アスファルト代替
組成物とは、石油系溶剤抽出油からなる樹脂や石油系、
石炭系または／および天然系樹脂や、熱可塑性ゴムおよ
びナフテン酸を配合した樹脂等の、いわゆる「明色舗装
材」と称されるもので、性状をストレートアスファルト
６０−８０または８０−１００のＪＩＳ規格に適合させ
た樹脂をいう。BEST MODE FOR CARRYING OUT THE INVENTION Pavement aggregates such as crushed stone, gravel, and sand can be used as the aggregate particles used in the present invention, and as a binder, asphalt, an asphalt substitute composition, cement, concrete. One selected from the above can be used. Here, the asphalt substitute composition is a resin or petroleum-based solvent comprising petroleum-based solvent-extracted oil,
It is a so-called "light-colored pavement material" such as a coal-based and / or natural-based resin, a resin in which a thermoplastic rubber and naphthenic acid are mixed, and has a property of straight asphalt 60-80 or 80-100 JIS. A resin that conforms to the standard.

【０００７】そして、本発明は前記骨材粒子と結合剤を
主成分とする舗装材料において、重量％で１〜５０％の
ガラスカレットと０．２〜３．０％の雲母を含有させる
点に特徴を有する。ガラスカレットとしては、各種の色
のガラス粉末やリサイクルしたガラス屑等を用いること
ができ、その粒度は均一な分散を確保する点から５mm以
下としておくことが好ましい。また、その含有量は１重
量％より少ないと十分な反射効果や着色効果を得ること
が難しく、一方、５０重量％より多いと十分な機械的強
度を確保することが難しくなるので１〜５０重量％の範
囲が好ましい。And, in the present invention, the pavement material containing the aggregate particles and the binder as the main components contains 1 to 50% by weight of glass cullet and 0.2 to 3.0% of mica. It has characteristics. As the glass cullet, glass powder of various colors, recycled glass scraps, and the like can be used, and the particle size thereof is preferably 5 mm or less from the viewpoint of ensuring uniform dispersion. Further, if the content is less than 1% by weight, it is difficult to obtain sufficient reflection effect and coloring effect, while if it is more than 50% by weight, it becomes difficult to secure sufficient mechanical strength, so 1 to 50% by weight. % Range is preferred.

【０００８】また雲母は、白雲母、金雲母、黒雲母等の
いずれでもよく、重量％で０．２〜３．０％含有させ
る。０．２％未満の場合には、雲母によるパール調の光
沢を十分に発揮することができず、３．０％より多い場
合には結合剤が多量に必要となる。したがって、０．２
〜３．０重量％の範囲で含有させるのが好ましく、雲母
の形状は粒子径が１０〜６５０μm の鱗片状のものを用
いることが強度等の確保の点から好ましい。更に、前記
の雲母は酸化チタンまたは／および酸化鉄でコーティン
グされたものとすることもでき、この場合、酸化チタン
でコーティングされた雲母の被覆率は１０〜７０％、酸
化鉄でコーティングされた雲母の被覆率は４〜６０％で
あることが好ましい。また、雲母が被覆率が１０〜７０
％の酸化チタンでコーティングされ、更にその上に被覆
率が４〜６０％の酸化鉄でコーティングされたものとす
ることもできる。なお前記の被覆率とは、雲母の重量に
対するコーティング膜の重量割合を示すものであり、例
えば酸化チタンのコーティング膜の場合、被覆率が小さ
いと銀色を呈し、厚みを増すに従ってパール調の緑色へ
と変化して種々の色調にコントロールすることができ
る。The mica may be any of muscovite, phlogopite, biotite, etc., and is contained at 0.2 to 3.0% by weight. If it is less than 0.2%, the pearly luster due to mica cannot be sufficiently exhibited, and if it is more than 3.0%, a large amount of binder is required. Therefore, 0.2
The content of mica is preferably from 3.0 to 3.0% by weight, and the shape of the mica is preferably scale-like with a particle size of 10 to 650 μm from the viewpoint of securing strength and the like. Further, the mica may be coated with titanium oxide and / or iron oxide, in which case the mica coated with titanium oxide has a coverage of 10 to 70% and the mica coated with iron oxide. The coverage is preferably 4 to 60%. Also, mica has a coverage of 10 to 70.
% Titanium oxide and further coated with iron oxide having a coverage of 4 to 60%. The above-mentioned coverage indicates the weight ratio of the coating film to the weight of mica.For example, in the case of a titanium oxide coating film, a small coverage results in silver color, and as the thickness increases, it becomes a pearl-like green color. Can be controlled to various color tones.

【０００９】このように構成されたものにおいては、所
定量のガラスカレットと雲母を含有させてあるので、ガ
ラスカレットの反射効果に加えて雲母の反射効果により
全体がパール調のマイルドな光沢であり、ソフトに反射
して非常に目に優しく、かつ容易に認知ができることと
なり、また雲母のバインダー的効果によりマーシャル安
定度が向上して割れや欠け等の発生を確実に防止できる
こととなるとともに、ガラスカレットの剥離を防止して
長期間にわたって安定した舗装面を確保できることとな
る。また、ガラスカレットの剥離防止と安定性を確保す
るために、ガラスカレットの相互の摩擦によるもみ磨り
・磨り潰し作用によりガラスカレットの表面を粗面にす
ることにより、他の骨材等の接着性と充填密度の向上も
可能となる。Since the glass cullet and the mica of a predetermined amount are contained in the one constructed in this way, the whole has a pearl-like mild luster due to the reflection effect of the mica in addition to the reflection effect of the glass cullet. , It is soft to the eye and very easy to recognize, and the binder effect of mica improves the Marshall stability to prevent cracks and chips from occurring. The peeling of the cullet can be prevented and a stable pavement surface can be secured for a long period of time. Also, in order to prevent the peeling and stability of the glass cullet, the surface of the glass cullet is roughened by the rubbing / grinding action due to the mutual friction of the glass cullet, and the adhesion of other aggregates etc. Also, the packing density can be improved.

【００１０】[0010]

【実施例】以下に本発明を実施例により更に詳細に説明
する。 〔第１の実施例〕表１に示す組成からなる舗装材料を１
４５℃で混合した後、常法に従いアスファルト舗装の表
層として施工した。施工後の表層の安定度とフロー値を
マーシャル試験により測定した。なお、結合材としては
ストレートアスファルト８０−１００を使用し、骨材と
してはＪＩＳ Ａ５００１規格に基づく各種粒度の砕石
を使用した。また、ガラスカレットとしては粒径が１〜
５mmのもの（Ａ）と粒径が１mm以下のもの（Ｂ）の茶色
のガラスカレットを使用し、雲母としては厚みが１μm
、粒径が４０〜２００μm の鱗片状で色調がパール
調、被覆率が３０％の酸化チタンをコーティングしたも
のを使用した。一方、比較例として表２に示すような組
成からなる、ガラスカレットおよび雲母を含有させない
もの（各比較例の左欄）と、ガラスカレットのみを含有
させ、雲母を含有させないもの（各比較例の右欄）の舗
装材料を作成して同様の試験を行ったが、比較例に比べ
てガラスカレットおよび雲母の両方を含有している本発
明の舗装材料が優れた安定度を発揮できることが確認で
きた。また、本発明のものは雲母の含有によりソフトな
パール調の拡散反射を呈することも確認できた。なお、
本発明のフロー値も細粒度アスファルト混合物の基準値
である２０〜８０(1/100cm)の範囲を十分満足するもの
であった。The present invention will be described in more detail with reference to the following examples. [First Example] A paving material having the composition shown in Table 1 was used.
After mixing at 45 ° C, it was applied as a surface layer of asphalt pavement according to a conventional method. The stability and flow value of the surface layer after the construction were measured by the Marshall test. As the binder, straight asphalt 80-100 was used, and as the aggregate, crushed stones having various particle sizes based on JIS A5001 standard were used. Further, the glass cullet has a particle size of 1 to
A brown glass cullet with a diameter of 5 mm (A) and a grain diameter of 1 mm or less (B) is used, and the thickness of the mica is 1 μm.
A scaly particle having a particle size of 40 to 200 μm, a color tone of pearl, and a titanium oxide coating having a coverage of 30% were used. On the other hand, as comparative examples, those having a composition as shown in Table 2 and not containing glass cullet and mica (left column of each comparative example) and those containing only glass cullet and not containing mica (for each comparative example) The same test was conducted by making the paving material (right column), but it was confirmed that the paving material of the present invention containing both glass cullet and mica can exhibit excellent stability as compared with the comparative example. It was It was also confirmed that the present invention exhibits soft pearl-like diffuse reflection due to the inclusion of mica. In addition,
The flow value of the present invention also sufficiently satisfies the standard value of the fine particle size asphalt mixture of 20 to 80 (1/100 cm).

【００１１】[0011]

【表１】 [Table 1]

【００１２】[0012]

【表２】 [Table 2]

【００１３】〔第２の実施例〕第１の実施例のうち、結
合材をストレートアスファルト８０−１００に替えてス
トレートアスファルト６０−８０を用い、第１の実施例
と同様の測定を行った結果も、マーシャル安定度および
フロー値は第１の実施例と同様に優れたものであること
が確認できた。[Second Embodiment] The result of performing the same measurement as in the first embodiment by using the straight asphalt 60-80 instead of the straight asphalt 80-100 as the binder in the first embodiment. However, it was confirmed that the Marshall stability and the flow value were as excellent as those in the first example.

【００１４】〔第３の実施例〕重量％で結合材としてア
スファルト代替組成物を６．５％、平均粒度２．５mmの
ガラスカレット２０〜３０％、砂利（Ｓ−５相当）６０
〜６５％、残部が石粉（粒度が１mm以下のガラスカレッ
トでもよい）からなるアスファルト代替混合物を作成
し、更に雲母を添加してアスファルト混合物と同様に施
工して表層としたところ、優れたマーシャル安定度を示
し、また明色でソフトなパール調の拡散反射を呈するこ
とが確認できた。また、表３に示されるように酸化チタ
ンまたは／および酸化鉄でコーティングした雲母の形状
や厚み、含有量等を変化させることによってシルバーメ
タリックやゴールドやワイン色調の種々の光沢が得られ
ることも確認できた。[Third Example] 6.5% by weight of an asphalt substitute composition as a binder, 20 to 30% of glass cullet having an average particle size of 2.5 mm, and gravel (equivalent to S-5) 60% by weight
~ 65%, the rest is made of stone powder (may be a glass cullet with a particle size of 1mm or less) asphalt substitute mixture was created, and mica was added, and the same process as the asphalt mixture was performed to make the surface layer, excellent marshall stability. In addition, it was confirmed that the diffuse reflection of light color and soft pearl tone was exhibited. Further, as shown in Table 3, it was confirmed that various glosses such as silver metallic, gold and wine tones can be obtained by changing the shape, thickness and content of the mica coated with titanium oxide and / or iron oxide. It was

【００１５】[0015]

【表３】 [Table 3]

【００１６】〔第４の実施例〕表４に示されるように、
半たわみ舗装における超早強セメント、超速硬セメント
または普通セメント等のセメント中に、粒度が１mm以下
のガラス粉末と粒子径が１０〜２００μm の雲母を含有
させたものを水と混合して施工したところ、シルバーメ
タリックや赤味ゴールドや明るい金属光沢色等の種々の
ソフトな光沢が得られることが確認できた。なお、ガラ
ス粉末を含有させない場合には金属光沢調の発色はほと
んど見られなかった。[Fourth Embodiment] As shown in Table 4,
Construction was performed by mixing cement containing ultra-fast cement, ultra-hard cement or ordinary cement in semi-flexible pavement with glass powder with a particle size of 1 mm or less and mica with a particle size of 10 to 200 μm mixed with water. However, it was confirmed that various soft luster such as silver metallic, red gold, and bright metallic luster color can be obtained. When the glass powder was not contained, almost no metallic luster color was observed.

【００１７】[0017]

【表４】 [Table 4]

【００１８】〔第５の実施例〕第１の実施例において、
ガラスカレットの粉砕にインペラーミルによる従来の粉
砕品（図２参照）を、磨砕方式によるガラスカレット相
互の摩擦によるもみ磨り・磨り潰しを実施したガラスカ
レット（図１参照）に置換して同様の評価をした結果、
従来のガラスカレットに比較して磨砕方式によるガラス
カレットを使用したものは１５％以上のマーシャル安定
度の向上が確認できた。また転圧においても良好な舗装
面が得られ、剥離もし難く、耐衝撃性の向上も確認でき
た。なお、磨砕方式によるガラスカレットにおいて実績
率５５％以下では上記の効果が少なく、５８％〜６５％
であると加工費も含めトータル的にはもっとも効果があ
る。更に実績率が６６％以上であるとより高い効果が確
認できたが、現時点ではガラスカレットの加工費用が増
大するという問題がある。[Fifth Embodiment] In the first embodiment,
For crushing the glass cullet, replace the conventional crushed product by an impeller mill (see Fig. 2) with a glass cullet (see Fig. 1) that has been rubbed and ground by friction between the glass cullets by the grinding method. As a result of the evaluation,
As compared with the conventional glass cullet, it was confirmed that the glass cullet using the grinding method improved the Marshall stability by 15% or more. In addition, a good paved surface was obtained even under rolling pressure, peeling was difficult, and improvement in impact resistance was confirmed. In addition, in the glass cullet by the grinding method, when the actual rate is 55% or less, the above effect is small and 58% to 65%.
Therefore, the total effect including the processing cost is the most effective. Further, a higher effect could be confirmed when the performance rate was 66% or more, but at the present time, there is a problem that the processing cost of the glass cullet increases.

【００１９】[0019]

【発明の効果】以上の説明からも明らかなように、本発
明は組成中に所定量のガラスカレットと雲母を含有させ
ることにより、全体的にソフトに反射し眩しさを感じさ
せることなく優れた光学特性を発揮することができると
ともに、十分なマーシャル安定度を発揮することがで
き、更にはガラスカレットの剥離もなく長期間にわたっ
て安定した舗装面を維持することができるものである。
また、ガラスカレットのリサイクル品を利用することに
より省資源に貢献するという利点もある。よって本発明
は従来の問題点を一掃した舗装材料として、産業の発展
に寄与するところは極めて大である。As is apparent from the above description, the present invention is excellent in that the composition contains a predetermined amount of glass cullet and mica, and is softly reflected as a whole without feeling glare. In addition to exhibiting optical characteristics, sufficient Marshall stability can be exhibited, and further, stable pavement surface can be maintained for a long period of time without peeling of the glass cullet.
There is also an advantage that it contributes to resource saving by using recycled glass cullet. Therefore, the present invention is extremely large in that it contributes to industrial development as a pavement material that eliminates the conventional problems.

【図面の簡単な説明】[Brief description of drawings]

【図１】従来法により粉砕したガラスカレットを用いた
舗装材料の断面図である。FIG. 1 is a cross-sectional view of a paving material using glass cullet crushed by a conventional method.

【図２】磨砕方式により粉砕したガラスカレットを用い
た舗装材料の断面図である。FIG. 2 is a sectional view of a paving material using glass cullet crushed by a grinding method.

フロントページの続き (72)発明者 竹村 俊昭 愛知県江南市前野町東200番地 (72)発明者 森 直樹 愛知県岩倉市西市町無量寺85 清和寮402Front Page Continuation (72) Inventor Toshiaki Takemura 200 East Higashi Maeno-cho, Konan City, Aichi Prefecture (72) Inventor Naoki Mori 85 Muroji Temple, Nishi-shi Town, Iwakura City, Aichi Prefecture Seiwa Dormitory 402

Claims (5)

【特許請求の範囲】[Claims] 【請求項１】 骨材粒子と結合剤を主成分とする表層用
の舗装材料において、重量％で１〜５０％のガラスカレ
ットと０．２〜３．０％の雲母を含有させたことを特徴
とする舗装材料。1. A pavement material for a surface layer containing aggregate particles and a binder as main components, containing 1 to 50% by weight of glass cullet and 0.2 to 3.0% of mica. Characteristic paving material. 【請求項２】 結合剤がアスファルト、アスファルト代
替組成物、セメント、コンクリートから選ばれたもので
ある請求項１に記載の舗装材料。2. The paving material according to claim 1, wherein the binder is selected from asphalt, an asphalt substitute composition, cement and concrete. 【請求項３】 雲母が酸化チタンまたは／および酸化鉄
でコーティングされたものである請求項１または２に記
載の舗装材料。3. The paving material according to claim 1, wherein the mica is coated with titanium oxide and / or iron oxide. 【請求項４】 ガラスカレットの粒度が５mm以下である
請求項１または２または３に記載の舗装材料。4. The paving material according to claim 1, wherein the particle size of the glass cullet is 5 mm or less. 【請求項５】 ガラスカレットを相互の摩擦によるもみ
磨り・磨り潰し作用によって、表面を粗面にし、且つ実
績率５５％以上としたことを特徴とする請求項１または
２または３または４に記載の舗装材料。5. The surface of the glass cullet is roughened by a rubbing / grinding action by mutual friction, and the actual rate is 55% or more. Paving material.