JPH0948939A - Emulsion ink for stencil printing - Google Patents

Abstract

PROBLEM TO BE SOLVED: To obtain a water-in-oil emulsion ink for stencil printing which does not exhibit set off and has an improved dryability by incorporating a silicone wax into an oil phase comprising a nonvolatile oil, a colorant, an emulsifier, and a resin. SOLUTION: This ink is prepd. by incorporating a silicone wax into an oil phase comprising a non- or hardly volatile oil, a colorant, an emulsifier, and a resin. A machine oil boiling at 200 deg.C or higher is pref. as the non- or hardly volatile oil. A pref. emulsifier is a nonionic surfactant having an HLB of 7 or lower. Rosin and an alkyd resin are used as the resin. A silicone ester wax and an alcohol-modified silicone wax are esp. pref. as the wax and those having an m.p. of 40-120 deg.C exhibit good fixability and set-off prevention effects. The emulsion is formed by mixing and dispersing the oil phase components and emulsifying while adding water. This ink is stably held on a stencil printing press and gives a print free from set off.

Description

【発明の詳細な説明】Detailed Description of the Invention

【０００１】[0001]

【産業上の利用分野】本発明は孔版印刷に用いられる印
刷インキに関し、特にインキの裏移りのしない、乾燥性
の改善された感熱孔版印刷用エマルジョンィンキに関す
るものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a printing ink used for stencil printing, and more particularly to an emulsion ink for heat-sensitive stencil printing which does not cause ink settling and has an improved drying property.

【０００２】[0002]

【従来の技術】近年、孔版印刷はデジタル方式により版
の作成が容易に行えるようになったことから、簡易印刷
として広く利用されるようになった。孔版印刷における
製版は、一般に、熱可塑性樹脂フィルムからなる孔版印
刷用原紙を用いて、サーマルヘッド等により直接熱可塑
性樹脂フィルムを加熱溶融して穿孔印字し製版される。
印刷はこのようにして形成された穿孔画像の穿孔部を介
して行われ、インキ供給側よりインキを穿孔部に通過せ
しめ、紙等の被印刷物表面にインキを付着させるもので
ある。2. Description of the Related Art In recent years, stencil printing has come to be widely used as simple printing since it has become possible to easily create a plate by a digital method. Plate making in stencil printing is generally carried out by using a stencil printing base paper made of a thermoplastic resin film to directly heat and melt the thermoplastic resin film with a thermal head or the like to perform perforation printing for plate making.
Printing is performed through the perforated portion of the perforated image formed in this way, and the ink is allowed to pass through the perforated portion from the ink supply side so that the ink adheres to the surface of the printed material such as paper.

【０００３】現在、広く利用されている孔版印刷は、メ
ンテナンスフリーの簡易印刷を基本とすることから印刷
後の洗浄処理は行わず、インキを長時間版面に放置して
もインキの乾燥による穿孔部目詰まりが起きず、様々な
環境下でも次の印刷直後から良好な印刷物が得られるこ
とが要望されている。Since stencil printing, which is widely used at present, is based on simple maintenance-free printing, washing treatment after printing is not performed, and even if the ink is left on the plate for a long time, the perforated portion is formed by drying the ink. It is desired that a good printed matter can be obtained immediately after the next printing even under various environments without causing clogging.

【０００４】そのため孔版印刷用インキは、一般に着色
剤を分散した高沸点オイル中に多量の水を乳化した構成
からなり、放置によリ硬化しない油中水滴型エマルジョ
ンタイプの印刷インキが用いられ、種々改良が行なわれ
てきた。Therefore, the stencil printing ink is generally composed of a high boiling point oil in which a colorant is dispersed and a large amount of water is emulsified, and a water-in-oil emulsion type printing ink which does not harden upon standing is used. Various improvements have been made.

【０００５】しかしながら、上述したように、インキは
版面での乾燥性が抑えられているにもかかわらず、印刷
後の被印刷面における乾燥は主として被印刷物中へのイ
ンキの浸透によるため、乾燥が遅く、印刷後の未乾燥イ
ンキが次の印刷物の非印刷面に移行する、いわゆる裏移
りの問題や、印刷物のハンドリングの際に汚れる等の問
題が生じていた。However, as described above, although the drying property of the ink on the plate surface is suppressed, the drying on the printing surface after printing is mainly due to the permeation of the ink into the printing object. Slowly, there has been a problem that the undried ink after printing is transferred to the non-printed surface of the next printed matter, so-called set-off problem, and stains are caused when handling the printed matter.

【０００６】そのため、版面にインキを長時間放置した
場合の機上放置安定性と印刷後の裏移り防止双方を両立
させるために、これまで多くの提案がなされてきた。例
えば、特開平２−４１３７６号公報記載の従来例にあっ
ては、紫外線硬化型インキを用いることが開示されてお
り、特開平６−１２８５１６号公報記載の従来例にあっ
ては、印刷後に皮膜形成する物質を加えることが開示さ
れており、特開平６−１１６５２５号公報記載の従来例
にあっては、平均粒子径約８〜３０μｍの固体粒子を含
有せしめることが開示されており、特開平６−２２０３
８２号公報記載の従来例にあっては、造膜形成する０／
Ｗ型エマルジョン樹脂を含有せしめることが開示されて
おり、平６−２２０３８３号公報記載の従来例にあって
は、二種以上の異なるＨＬＢ価を有する界面活性剤を用
いることが開示されており、特開平６−２９３８７３号
公報記載の従来例にあっては、キレート化合物を含有せ
しめることが開示されている。Therefore, many proposals have been made so far in order to achieve both the on-machine stability when ink is left on the plate surface for a long time and the prevention of set-off after printing. For example, in the conventional example described in JP-A-2-41376, it is disclosed to use an ultraviolet curable ink, and in the conventional example described in JP-A-6-128516, a film is printed after printing. It is disclosed that a substance to be formed is added, and in the conventional example described in JP-A-6-116525, it is disclosed that solid particles having an average particle diameter of about 8 to 30 μm are contained. 6-2203
In the conventional example described in Japanese Patent Publication No. 82, 0 /
It is disclosed that a W type emulsion resin is contained, and in the conventional example described in Japanese Patent Laid-Open No. 6-220383, it is disclosed that two or more kinds of surfactants having different HLB values are used. In the conventional example described in JP-A-6-293873, it is disclosed that a chelate compound is contained.

【０００７】[0007]

【発明が解決しようとする課題】しかしながら、孔版簡
易印刷の長所であるメンテナンスフリーの機上放置安定
性を損なうことなく、裏移りしない乾燥性の良いインキ
は、未だ満足なものは得られていない。However, an ink having good dryability that does not set off without impairing the maintenance-free on-machine leaving stability, which is an advantage of simple stencil printing, has not been obtained yet. .

【０００８】本発明は、このような状況に鑑みてなされ
たもので、印刷機版面上においては長時間の放置によっ
ても変化せず安定した状態で保持され、しかも、印刷後
は未乾燥のインキが次の非印刷面に移行しない、いわゆ
る裏移りの生じない孔版印刷用エマルジョンインキを提
供することを目的とする。The present invention has been made in view of such a situation, and the ink on the plate surface of a printing press is held in a stable state without being changed even after being left for a long time, and the ink is not dried after printing. It is an object of the present invention to provide an emulsion ink for stencil printing which does not transfer to the next non-printing surface, that is, so-called set-off does not occur.

【０００９】[0009]

【課題を解決するための手段】本発明によれば、第一
に、油中水滴型エマルジョンインキにおいて、少なくと
も不揮発性油または難揮発性油、着色剤、乳化剤および
樹脂からなる油相中にシリコーンワックスを含有させる
ことを特徴とする孔版印刷用エマルジョンインキが提供
される。According to the present invention, firstly, in a water-in-oil emulsion ink, silicone is contained in an oil phase composed of at least a nonvolatile oil or a hardly volatile oil, a colorant, an emulsifier and a resin. Provided is an emulsion ink for stencil printing, which is characterized by containing a wax.

【００１０】第二に、上記第一に記載した孔版印刷用エ
マルジョンインキにおいて、前記シリコーンワックスが
シリコーンエステルワックスであることを特徴とする孔
版印刷用エマルジョンインキが提供される。Secondly, in the emulsion ink for stencil printing described in the above-mentioned first, there is provided an emulsion ink for stencil printing, wherein the silicone wax is a silicone ester wax.

【００１１】第三に、上記第一に記載した孔版印刷用エ
マルジョンインキにおいて、前記シリコーンワックスが
アルコール変性シリコーンワックスであることを特徴と
する孔版印刷用エマルジョンインキが提供される。Thirdly, there is provided an emulsion ink for stencil printing, wherein the silicone wax is an alcohol-modified silicone wax in the emulsion ink for stencil printing described in the above first.

【００１２】第四に、上記第一、第二または第三に記載
した孔版印刷用エマルジョンインキにおいて、前記シリ
コーンワックスが４０〜１２０℃の範囲の融点を有する
ことを特徴とする孔版印刷用エマルジョンインキが提供
される。Fourthly, in the emulsion ink for stencil printing described in the above first, second or third, the silicone wax has a melting point in the range of 40 to 120 ° C., the emulsion ink for stencil printing. Will be provided.

【００１３】第五に、上記第一、第二、第三または第四
に記載した孔版印刷用エマルジョンインキにおいて、前
記シリコーンワックスを全インキ中０．５〜５重量％含
有させることを特徴とする孔版印刷用エマルジョンイン
キが提供される。Fifth, in the emulsion ink for stencil printing described in the above first, second, third or fourth, the silicone wax is contained in an amount of 0.5 to 5% by weight in all inks. An emulsion ink for stencil printing is provided.

【００１４】以下に本発明を詳細に説明する。上記のよ
うに、本発明は着色剤、不揮発性油または難揮発性油、
界面活性剤、樹脂等を含む油相中に水相を分散した油中
水滴型孔版印刷用エマルジョンインキにおいて、油相中
にさらにシリコーンワックスを含有させることを特徴と
するものである。The present invention will be described in detail below. As noted above, the present invention is a colorant, non-volatile oil or sparingly volatile oil,
In a water-in-oil type emulsion ink for stencil printing in which an aqueous phase is dispersed in an oil phase containing a surfactant, a resin and the like, a silicone wax is further contained in the oil phase.

【００１５】油相中の油成分（溶媒）としては、不揮発
性油または難揮発性油が用いられ、例えばマシン油、ス
ピンドル油、モーター油、ギヤ油、流動パラフィン等の
鉱油、ひまし油、大豆油、トール油等の植物油、フタル
酸ジオクチル（ＤＯＰ）、リン酸トリクレジル（ＴＣ
Ｐ）等の可塑剤および合成油等が使用でき、水より蒸発
速度の遅い高沸点溶剤、特に沸点２００℃以上のものが
好ましく用いられる。溶剤の使用比率は全インキ中５〜
３０重量％である。As the oil component (solvent) in the oil phase, a non-volatile oil or a hardly volatile oil is used. For example, machine oil, spindle oil, motor oil, gear oil, mineral oil such as liquid paraffin, castor oil, soybean oil. , Vegetable oils such as tall oil, dioctyl phthalate (DOP), tricresyl phosphate (TC)
A plasticizer such as P) and a synthetic oil can be used, and a high boiling point solvent having a slower evaporation rate than water, particularly one having a boiling point of 200 ° C. or higher is preferably used. The ratio of solvent used is 5 to all inks
30% by weight.

【００１６】樹脂はロジン、ロジンエステル、ロジン変
性フェノール樹脂、アルキッド樹脂、マレイン酸樹脂等
が用いられ、樹脂使用比率は全インキ中０〜２０重量％
を含有させる。着色剤は、従来より周知の無機または有
機顔料あるいは染料が使用され、特に、顔料としてカー
ボンブラック、群青、紺青、フタロシアニン顔料、アゾ
顔料、キナクリドン顔料等を使用することができる。着
色剤のの使用比率は、全インキ中０．５〜１５重量％、
好ましくは２〜６重量％含有させる。As the resin, rosin, rosin ester, rosin-modified phenol resin, alkyd resin, maleic acid resin, etc. are used, and the resin usage ratio is 0 to 20% by weight in all inks.
Is contained. As the colorant, conventionally known inorganic or organic pigments or dyes are used, and in particular, carbon black, ultramarine blue, dark blue, phthalocyanine pigments, azo pigments, quinacridone pigments and the like can be used as pigments. The use ratio of the colorant is 0.5 to 15% by weight in all inks,
It is preferably contained in an amount of 2 to 6% by weight.

【００１７】界面活性剤は、油中水滴型エマルジョンを
形成し、エマルジョン安定性の高い界面活性剤が用いら
れ、好ましくは、非イオン界面活性剤であり、ＨＬＢが
７以下のものである。界面活性剤は、単独または二種以
上を組み合わせて使用することができる。例えば、ソル
ビタンモノラウレート、ソルビタンモノパルミテート、
ソルビタンセスキオレート、ソルビタンセスキイソステ
アレート等のソルビタン高級脂肪酸エステル、ポリオキ
シエチレンソルビタン高級脂肪酸エステル、オレイン酸
モノグリセリド、オレイン酸ジグリセリド等の脂肪酸モ
ノまたはグリセリド、高級アルコール、アルキルフェノ
ール，脂肪酸等の酸化エチレン付加物などが挙げられ
る。界面活性剤の使用比率は、ソルビタン高級脂肪酸エ
ステル系の場合、全インキ中０．５〜５重量％を含有さ
せる。As the surfactant, a surfactant that forms a water-in-oil emulsion and has high emulsion stability is used, preferably a nonionic surfactant and having an HLB of 7 or less. The surfactants may be used alone or in combination of two or more. For example, sorbitan monolaurate, sorbitan monopalmitate,
Sorbitan higher fatty acid ester such as sorbitan sesquioleate and sorbitan sesquiisostearate, polyoxyethylene sorbitan higher fatty acid ester, fatty acid mono- or glyceride such as oleic acid monoglyceride, oleic acid diglyceride, higher alcohol, alkylphenol, ethylene oxide adduct such as fatty acid And so on. When the sorbitan higher fatty acid ester type is used, the surfactant is used in an amount of 0.5 to 5% by weight based on the total ink.

【００１８】本発明では油相中にさらにシリコーンワッ
クスを含有させる。本発明のシリコーンワックスとは、
常温で固体状のものを指し、中でもシリコーンエステル
ワックスまたはアルコール変性シリコーンワックスが好
ましく用いられる。In the present invention, a silicone wax is further contained in the oil phase. The silicone wax of the present invention is
It means a solid at room temperature, and among them, silicone ester wax or alcohol-modified silicone wax is preferably used.

【００１９】シリコーンエステルワックスとしては、例
えば、ポリラウリルトリメチロールプロパンシロキサ
ン、ポリイソステアリルトリメチロールプロパンシロキ
サン、アルコール変性シリコーンワックスとしては信越
化学工業社製Ｘ−２２−８０１Ｂなどがある。Examples of the silicone ester wax include polylauryl trimethylolpropane siloxane and polyisostearyl trimethylolpropane siloxane, and examples of the alcohol-modified silicone wax include X-22-801B manufactured by Shin-Etsu Chemical Co., Ltd.

【００２０】ワックスは融点が４０〜１２０℃の範囲の
ものを使用するのが好ましい。融点が４０℃未満のワッ
クスを使用した場合には，裏移り防止の効果が小さく，
逆に融点が１２０℃を越えると裏移り防止の効果は良い
が、定着性が悪くなる。The wax having a melting point in the range of 40 to 120 ° C. is preferably used. When wax with a melting point of less than 40 ° C is used, the effect of set-off prevention is small,
On the other hand, when the melting point exceeds 120 ° C., the effect of preventing set-off is good, but the fixability is poor.

【００２１】ワックスの使用比率は全インキ中０．５〜
５重量％とするのが好ましい。比率が０．５重量％未満
では裏移り防止に対する効果が小さく，逆に５重量％を
越えると画像の定着性が低下する傾向が出て好ましくな
い。The use ratio of wax is 0.5 to 0.5 in all inks.
It is preferably 5% by weight. If the ratio is less than 0.5% by weight, the effect of preventing set-off is small, and if it exceeds 5% by weight, the fixing property of the image tends to deteriorate, which is not preferable.

【００２２】水相の成分は、水が主成分であるが、水以
外に蒸発抑制、凍結防止剤としてエチレングリコール、
プロピレングリコール、グリセリンなどの多価アルコー
ルやポリエチレングリコール、防腐、防かび剤、水溶性
高分子物質等の増粘剤、電解質等のエマルジョン安定性
向上剤その他添加剤を添加することができる。水相は全
インキ中で油相の約１０〜６０重量％に対して約９０〜
４０重量％の比率である。The main component of the water phase is water, but in addition to water, ethylene glycol is used as an anti-evaporation and anti-freezing agent.
Polyhydric alcohols such as propylene glycol and glycerin, polyethylene glycol, preservatives, fungicides, thickeners such as water-soluble polymer substances, emulsion stability improvers such as electrolytes and other additives can be added. The water phase is about 90 to 60% by weight of the oil phase in all inks.
The ratio is 40% by weight.

【００２３】油中水滴型エマルジョンからなる孔版印刷
用インキの調製例を示すと、別々に油相は通常の三本ロ
ールミル、サンドミル等の分散機で顔料を練肉、分散
し、水相は通常の撹拌機により混合した後、油相中に水
相を徐々に添加しながら各種の乳化機を使用して油相中
に微分散された水相からなる油中水滴型エマルジョンを
容易に調製することができる。A preparation example of a stencil printing ink comprising a water-in-oil emulsion will be described. Separately, the oil phase is prepared by dispersing and dispersing the pigment in a conventional disperser such as a three-roll mill or a sand mill. After being mixed with the stirrer described above, a water-in-oil emulsion consisting of the water phase finely dispersed in the oil phase is easily prepared by using various emulsifiers while gradually adding the water phase to the oil phase. be able to.

【００２４】本発明では、ワックスの分散を良くするた
めに、あらかじめ樹脂および溶媒とワックスを加熱溶解
してワニスを作成し、該ワニスを残りの油相成分と一緒
に分散機で練肉、分散することにより均一な油相を形成
させた後、水相を徐々に添加して油中水滴型エマルジョ
ンを調製することが好ましい。In the present invention, in order to improve the dispersion of the wax, a resin, a solvent and the wax are heated and melted to prepare a varnish, and the varnish is kneaded and dispersed with a remaining oil phase component in a disperser. It is preferable to form a uniform oil phase by doing so and then gradually add the water phase to prepare a water-in-oil emulsion.

【００２５】[0025]

【実施例】以下、本発明を実施例によりさらに具体的に
説明する。なお、文中の部および％はいすれも重量基準
である。EXAMPLES Hereinafter, the present invention will be described more specifically with reference to examples. All parts and% in the text are based on weight.

【００２６】〔実施例１〕 〈ワニスの調製〉 ロジン変性フェノール樹脂 ２５部 Ｃマシン油（日本石油社製） ７０部 イソステアリルトリメチロールプロパンシロキサン ５部 上記組成で２００℃にて加熱溶解してワニスを調製し
た。[Example 1] <Preparation of varnish> Rosin-modified phenolic resin 25 parts C machine oil (manufactured by Nippon Oil Co., Ltd.) 70 parts Isostearyl trimethylolpropane siloxane 5 parts Varnish by heating with the above composition at 200 ° C Was prepared.

【００２７】 〈油相の調製〉 カーボンブラック １２部 ソルビタンセスキオレート １２部 アイソパールＬ（エクソン社製溶剤） １０部 ワニス ６６部 上記配合で二本ロールミルで十分に混練りして油相を調
製した。<Preparation of Oil Phase> Carbon black 12 parts Sorbitan sesquioleate 12 parts Isopar L (solvent manufactured by Exxon Co.) 10 parts Varnish 66 parts The oil phase was prepared by thoroughly kneading with the above-mentioned composition using a two-roll mill. .

【００２８】 〈水相の調製〉 水 ９０部 エチレングリコール １０部 上記配合で混合して水相を調製した。<Preparation of Aqueous Phase> Water 90 parts Ethylene glycol 10 parts Mixing with the above formulation, an aqueous phase was prepared.

【００２９】〈インキの作製〉油相３０部に撹洋機で撹
拌しながら水相７０部を徐々に加えて乳化させることに
より油中水滴型エマルジョンインキを作製した。<Preparation of Ink> A water-in-oil type emulsion ink was prepared by gradually adding 70 parts of an aqueous phase to 30 parts of an oil phase while stirring with a stirrer and emulsifying.

【００３０】印刷による評価は、得られたエマルジョン
インキを用いて、孔版印刷機（リコー社製：プリポート
ＶＴ−３８２０）により実施した。その結果、裏移りは
印刷物裏面の汚れ度合いを肉眼により判定したところ、
裏移りのない鮮明な印刷物を得ることができた。また、
印刷終了後１週間印刷機を使用せずに放置した後に印刷
を行ったところ、ドラムメッシュの目詰まりもなく、裏
移りのない鮮明な印刷物が得られた。The evaluation by printing was carried out using a stencil printing machine (manufactured by Ricoh Co .: Preport VT-3820) using the obtained emulsion ink. As a result, the set-off is the degree of smearing on the back side of the printed matter, which is determined by the naked eye.
It was possible to obtain a clear printed material without set-off. Also,
When printing was carried out after leaving the printing machine for 1 week without using the printing machine after completion of printing, a clear printed matter without settling of the drum mesh was obtained.

【００３１】〔実施例２〕 〈ワニスの調製〉 アルキッド樹脂 ２５部 Ｃマシン油（日本石油社製） ６０部 ポリラウリルトリメチロールプロパンシロキサン １５部 上記組成で実施例１と同様にしてワニスを調製した。上
記ワニスを使用した以外は実施例１と同様の方法でエマ
ルジョンイキを作製し、孔版印刷を行ない同様の評価を
したところ、実施例１と同様に裏移り防止性、経時安定
性ともに良好な結果が得られた。[Example 2] <Preparation of varnish> Alkyd resin 25 parts C Machine oil (manufactured by Nippon Oil Co., Ltd.) 60 parts Polylauryl trimethylolpropane siloxane 15 parts A varnish was prepared in the same manner as in Example 1 with the above composition. . Emulsion ink was prepared in the same manner as in Example 1 except that the above varnish was used, and stencil printing was performed and the same evaluation was performed. As with Example 1, settling prevention properties and stability over time were excellent. was gotten.

【００３２】〔実施例３〕 〈ワニスの調製〉 ロジン変性フェノール樹脂 ２５部 Ｃマシン油（日本石油社製） ６０部 アルコール変性シリコーンワックス （信越化学工業社製：Ｘ−２２−８０１Ｂ） １５部 上記配合で実施例１と同様にしてワニスを調製した。上
記ワニスを使用した以外は実施例１と同様の方法でエマ
ルジョンインキを作製し、孔版印刷を行ない評価したと
ころ、実施例１と同様に裏移り防止性、経時安定性とも
に良好な結果が得られた。[Example 3] <Preparation of varnish> Rosin-modified phenol resin 25 parts C machine oil (manufactured by Nippon Oil Co., Ltd.) 60 parts Alcohol-modified silicone wax (Shin-Etsu Chemical Co., Ltd .: X-22-801B) 15 parts A varnish was prepared in the same manner as in Example 1 by blending. An emulsion ink was prepared in the same manner as in Example 1 except that the above varnish was used, and stencil printing was performed and evaluated. As with Example 1, good results were obtained in both anti-setoff property and stability over time. It was

【００３３】〔比較例１〕 〈ワニスの調製〉 ロジン変性フェノール樹脂 ２５部 Ｃマシン油（日本石油社製） ７５部 上記のようにワックス成分を含有しない配合にした以外
は実施例１と同様の方法でワニスを調製した。また、上
記ワニスを使用した以外は全て実施例１と同様にしてエ
マルジョンインキを作製し、孔版印刷を行ない同様の評
価を行ったところ、経時安定性は良好であったが、印刷
時の裏移りによる汚れのが発生した。Comparative Example 1 <Preparation of Varnish> Rosin-modified phenolic resin 25 parts C Machine oil (manufactured by Nippon Oil Co., Ltd.) 75 parts Same as Example 1 except that the wax component was not included as described above. A varnish was prepared by the method. Further, an emulsion ink was prepared in the same manner as in Example 1 except that the above-mentioned varnish was used, and stencil printing was carried out, and the same evaluation was carried out. Dirt caused by.

【００３４】〔参考例１〕 〈ワニスの調製〉 ロジン変性フェノール樹脂 ２５部 Ｃマシン油（日本石油社製） ４５部 ポリイソステアリルトリメチロールプロパンシロキサン３０部 ワックス成分をやや過剰に含有した上記配合で実施例１
と同様の方法でワニスを調製した。[Reference Example 1] <Preparation of varnish> Rosin-modified phenol resin 25 parts C Machine oil (manufactured by Nippon Oil Co., Ltd.) 45 parts Polyisostearyl trimethylolpropane siloxane 30 parts With the above composition containing a slight excess of the wax component. Example 1
A varnish was prepared in the same manner as in.

【００３５】上記ワニスを使用した以外は、全て実施例
１と同様にしてエマルジョンインキを作製し、孔版印刷
を行ない同様の評価を行ったところ、裏移りのない鮮明
な印刷物を得ることができたが、印刷５分後の触指試験
による印刷用紙への固着状態の評価を行ったところ、画
像の定着性が若干低下した。An emulsion ink was prepared in the same manner as in Example 1 except that the above-mentioned varnish was used, and stencil printing was carried out, and the same evaluation was carried out. As a result, clear printed matter without set-off was obtained. However, when the state of sticking to the printing paper was evaluated by a finger touch test 5 minutes after printing, the fixability of the image was slightly lowered.

【００３６】〔参考例２〕 〈ワニスの調製〉実施例１において用いたワックス成分
ポリイソステアリルトリメチロールプロパンシロキサン
に代えて、融点２０℃のシリコーンエステルワックスを
用いた以外は、実施例１と同様にしてエマルジョンイン
キを作製し、同様に評価したところ、裏移り防止効果は
やや低下した。同様に融点１４０℃のシリコーンエステ
ルワックスを用いた結果、画像の定着性の低下が見られ
た。Reference Example 2 <Preparation of Varnish> Same as Example 1 except that the wax component polyisostearyl trimethylolpropane siloxane used in Example 1 was replaced by a silicone ester wax having a melting point of 20 ° C. When an emulsion ink was prepared as described above and evaluated in the same manner, the settling prevention effect was slightly lowered. Similarly, as a result of using a silicone ester wax having a melting point of 140 ° C., a decrease in image fixability was observed.

【００３７】[0037]

【発明の効果】以上のように、上記第一に記載した孔版
印刷用エマルジョンインキによれば、油相中にシリコー
ンワックスを含有させることにより、エマルジョンイン
キの印刷機上放置安定性を損なうことなく、良好な裏移
り防止性を得ることができる。上記第二または第三に記
載した孔版印刷用エマルジョンインキによれば、シリコ
ーンワックスのなかでも、裏移り防止性の優れた材料に
よるインキが得られる。上記第四、第五に記載した孔版
印刷用エマルジョンインキによれば、裏移り防止効果の
有効なインキが得られる。As described above, according to the emulsion ink for stencil printing described above in the first aspect, the inclusion of silicone wax in the oil phase does not impair the stability of the emulsion ink left on the printing machine. It is possible to obtain good anti-setoff property. According to the emulsion ink for stencil printing described in the above second or third, among the silicone waxes, an ink made of a material having an excellent anti-setoff property can be obtained. According to the emulsion inks for stencil printing described in the above fourth and fifth, an ink having an effective set-off prevention effect can be obtained.

Claims (5)

【特許請求の範囲】[Claims] 【請求項１】 油中水滴型エマルジョンインキにおい
て、少なくとも不揮発性油または難揮発性油、着色剤、
乳化剤および樹脂からなる油相中にシリコーンワックス
を含有させることを特徴とする孔版印刷用エマルジョン
インキ。1. A water-in-oil emulsion ink comprising at least a non-volatile oil or a hardly volatile oil, a colorant,
An emulsion ink for stencil printing, wherein a silicone wax is contained in an oil phase composed of an emulsifier and a resin. 【請求項２】 前記シリコーンワックスがシリコーンエ
ステルワックスであることを特徴とする請求項１記載の
孔版印刷用エマルジョンインキ。2. The emulsion ink for stencil printing according to claim 1, wherein the silicone wax is a silicone ester wax. 【請求項３】 前記シリコーンワックスがアルコール変
性シリコーンワックスであることを特徴とする請求項１
記載の孔版印刷用エマルジョンインキ。3. The silicone wax is an alcohol-modified silicone wax.
The emulsion ink for stencil printing described above. 【請求項４】 前記シリコーンワックスが４０〜１２０
℃の範囲の融点を有することを特徴とする請求項１乃至
３記載の孔版印刷用エマルジョンインキ。4. The silicone wax is 40-120.
The emulsion ink for stencil printing according to claim 1, which has a melting point in the range of ° C. 【請求項５】 前記シリコーンワックスを全インキ中
０．５〜５重量％含有させることを特徴とする請求項１
乃至４記載の孔版印刷用エマルジョンインキ。5. The ink according to claim 1, wherein the silicone wax is contained in an amount of 0.5 to 5% by weight.
An emulsion ink for stencil printing according to any one of 4 to 4.