JPH0947500A - Deodorization filter - Google Patents
Deodorization filterInfo
- Publication number
- JPH0947500A JPH0947500A JP7201193A JP20119395A JPH0947500A JP H0947500 A JPH0947500 A JP H0947500A JP 7201193 A JP7201193 A JP 7201193A JP 20119395 A JP20119395 A JP 20119395A JP H0947500 A JPH0947500 A JP H0947500A
- Authority
- JP
- Japan
- Prior art keywords
- deodorant
- zeolite
- deodorizing
- transition metal
- metal oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は密閉空間内の悪臭を除去
するためにエアコン及び空気清浄機等に使用され、脱臭
性能が高く、たばこ臭も除去することができる脱臭フィ
ルタに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a deodorizing filter which is used in an air conditioner, an air purifier or the like to remove a bad odor in a closed space, has a high deodorizing performance and is capable of removing a cigarette odor.
【０００２】[0002]
【従来の技術】一般的に、エアコン及び空気清浄機等に
使用されている脱臭フィルタの脱臭剤は、その主原料が
活性炭であり、粉末活性炭又は粒状活性炭がフィルタの
表面に添着されている。このフィルタ面を、密閉空間内
の悪臭を含む空気が通過することにより、密閉空間内の
悪臭が除去される。2. Description of the Related Art Generally, a deodorizing agent for a deodorizing filter used in an air conditioner, an air purifier or the like is mainly composed of activated carbon, and powdered activated carbon or granular activated carbon is attached to the surface of the filter. The bad odor in the closed space is removed by passing the air containing the bad odor in the closed space through the filter surface.
【０００３】[0003]
【発明が解決しようとする課題】しかしながら、従来の
脱臭フィルタに添着されている脱臭剤の主原料である活
性炭には、タバコ臭を除去する効果が十分ではないとい
う問題点がある。これは、活性炭の脱臭機構は、悪臭の
もとである分子が活性炭の表面にある細孔内に物理吸着
することによるものであり、タバコ臭の主成分であるア
ンモニア、アセトアルデヒド及び酢酸等の中で、極性分
子であるアンモニア及びアセトアルデヒドは活性炭に吸
着されにくいからである。However, activated carbon, which is the main raw material of the deodorant attached to the conventional deodorizing filter, has a problem that the effect of removing tobacco odor is not sufficient. This is because the deodorizing mechanism of activated carbon is due to the physical adsorption of molecules that are the source of malodor into the pores on the surface of activated carbon, among the main components of tobacco odor, such as ammonia, acetaldehyde and acetic acid. The polar molecules, ammonia and acetaldehyde, are not easily adsorbed on the activated carbon.
【０００４】また、活性炭は比重が小さいため、フィル
タ表面の活性炭への悪臭分子の吸着重量を増加させるた
めに、多量の活性炭が必要となる。そして、この多量の
活性炭を含む脱臭剤をフィルタ表面に脱落しないように
添着するためには、多量のバインダーを使用しなければ
ならない。その結果、活性炭の表面がバインダーで覆わ
れて、本来の活性炭が有する脱臭能力が著しく低下す
る。Since activated carbon has a low specific gravity, a large amount of activated carbon is required to increase the weight of the malodorous molecules adsorbed on the activated carbon on the filter surface. Then, in order to attach the deodorant containing a large amount of activated carbon to the filter surface so as not to drop off, a large amount of binder must be used. As a result, the surface of the activated carbon is covered with the binder, and the deodorizing ability of the original activated carbon is significantly reduced.
【０００５】本発明はかかる問題点に鑑みてなされたも
のであって、製造コストが低く、厚さを薄くすることが
できると共に、脱臭性能が高く、タバコ臭をも除去する
ことができる脱臭フィルタを提供することを目的とす
る。The present invention has been made in view of the above problems, and has a low manufacturing cost, a reduced thickness, a high deodorizing performance, and a deodorizing filter capable of removing tobacco odor. The purpose is to provide.
【０００６】[0006]
【課題を解決するための手段】本発明に係る脱臭フィル
タは、ゼオライト及び遷移金属酸化物を含有する脱臭剤
が多孔性基材に添着されていることを特徴とする。The deodorizing filter according to the present invention is characterized in that a deodorizing agent containing zeolite and a transition metal oxide is attached to a porous substrate.
【０００７】前記ゼオライトは脱臭剤中に４０乃至９５
重量％含有され、前記遷移金属酸化物は脱臭剤中に５乃
至６０重量％含有されていることが好ましい。The zeolite is contained in the deodorant in an amount of 40 to 95.
It is preferable that the transition metal oxide is contained in an amount of 5 to 60% by weight in the deodorant.
【０００８】このゼオライトは例えばハイシリカゼオラ
イトであり、遷移金属酸化物は、例えば、Ｃｕ、Ｍｎ及
びＦｅからなる群から選択された１又は２以上の金属元
素の酸化物である。The zeolite is, for example, a high silica zeolite, and the transition metal oxide is, for example, an oxide of one or more metal elements selected from the group consisting of Cu, Mn and Fe.
【０００９】また、この脱臭剤には、化学吸着型消臭剤
又は活性炭を添加することができる。A chemical adsorption type deodorant or activated carbon can be added to the deodorant.
【００１０】多孔性基材としては、例えば、ネット状合
成樹脂、ポリウレタンフォーム又は不織布がある。Examples of the porous substrate include net synthetic resin, polyurethane foam and non-woven fabric.
【００１１】[0011]
【作用】本願発明者等が前記課題を解決するために鋭意
実験研究を重ねた結果、ゼオライト及び遷移金属酸化物
を含有する脱臭剤を多孔性基材に添着することにより、
従来の脱臭フィルタでは脱臭効果が不十分であったタバ
コ臭を除去することができることを見い出した。As a result of the inventors of the present invention having conducted extensive studies in order to solve the above-mentioned problems, by attaching a deodorant containing zeolite and a transition metal oxide to the porous substrate,
It has been found that the conventional deodorizing filter can remove the tobacco odor, which was insufficient in deodorizing effect.
【００１２】本発明においては、脱臭フィルタ用の脱臭
剤として、ゼオライト及び遷移金属酸化物を使用する
が、このゼオライトはアンモニア及びアセトアルデヒド
等の極性分子を除去する効果が優れている。また、遷移
金属酸化物はメチルメルカプタン及び硫化水素等の硫黄
性の悪臭分子を除去する効果が優れている。従って、こ
れらの脱臭剤を組み合わせることにより、脱臭性能が優
れた脱臭フィルタを得ることができる。その結果、従来
の活性炭を使用した脱臭フィルタの性能と比較して、脱
臭性能が同等のものであれば、本発明は多孔性基材上に
添着する脱臭剤の量を少なくすることが可能となるた
め、従来の脱臭フィルタよりも薄くすることができる。In the present invention, a zeolite and a transition metal oxide are used as a deodorant for a deodorizing filter, and this zeolite has an excellent effect of removing polar molecules such as ammonia and acetaldehyde. Further, the transition metal oxide has an excellent effect of removing sulfur malodorous molecules such as methyl mercaptan and hydrogen sulfide. Therefore, by combining these deodorizing agents, a deodorizing filter having excellent deodorizing performance can be obtained. As a result, as compared with the performance of the conventional deodorizing filter using activated carbon, if the deodorizing performance is equivalent, the present invention can reduce the amount of deodorant attached to the porous substrate. Therefore, it can be made thinner than the conventional deodorizing filter.
【００１３】この脱臭剤中におけるゼオライトの比率が
４０重量％未満であると、アンモニア及びアセトアルデ
ヒド等の極性分子を除去する効果が低下する。一方、脱
臭剤中におけるゼオライトの比率が９５重量％を超える
と、メチルメルカプタン及び硫化水素等の硫黄性の悪臭
分子を除去する効果が低下する。従って、脱臭剤中のゼ
オライト及び遷移金属酸化物の各比率は、ゼオライトが
４０乃至９５重量％、遷移金属酸化物が５乃至６０重量
％であることが望ましい。When the proportion of zeolite in the deodorant is less than 40% by weight, the effect of removing polar molecules such as ammonia and acetaldehyde decreases. On the other hand, when the proportion of zeolite in the deodorant exceeds 95% by weight, the effect of removing sulfurous malodorous molecules such as methyl mercaptan and hydrogen sulfide decreases. Therefore, the respective proportions of zeolite and transition metal oxide in the deodorant are preferably 40 to 95% by weight of zeolite and 5 to 60% by weight of transition metal oxide.
【００１４】使用するゼオライトは、Ａ型、Ｘ型、Ｙ型
若しくはハイシリカゼオライト等の合成ゼオライト又は
各種天然ゼオライトから任意に選択することができる
が、ハイシリカゼオライトを使用すると最も優れた脱臭
性能が得られる。なお、ハイシリカゼオライトとは、ゼ
オライト中におけるＳｉ成分及びＡｌ成分の重量比（Ｓ
ｉ成分：Ａｌ成分）が１０：１乃至５０：１のものを示
すが、特にこの重量比が４０：１乃至５０：１のハイシ
リカゼオライトを使用することが好ましい。The zeolite to be used can be arbitrarily selected from synthetic zeolites such as A-type, X-type, Y-type or high-silica zeolite or various natural zeolites, but the use of high-silica zeolite gives the best deodorizing performance. can get. The high-silica zeolite is a weight ratio of the Si component and the Al component in the zeolite (S
The i component: Al component) is 10: 1 to 50: 1, and it is particularly preferable to use a high silica zeolite having a weight ratio of 40: 1 to 50: 1.
【００１５】また、使用する遷移金属酸化物は、Ｃｕ、
Ｍｎ又はＦｅ等の各種酸化物の中から任意に選択するこ
とができるが、脱臭性能面ではＣｕ−Ｍｎ系複合酸化
物、Ｆｅ−Ｍｎ系複合酸化物又はＭｎ酸化物を使用する
ことが望ましい。The transition metal oxide used is Cu,
It can be arbitrarily selected from various oxides such as Mn or Fe, but in terms of deodorizing performance, it is desirable to use Cu—Mn-based composite oxide, Fe—Mn-based composite oxide or Mn oxide.
【００１６】更に、本発明における脱臭剤に化学吸着型
消臭剤を添加することにより、アンモニア分子及び酢酸
分子の除去効果がより一層優れたものとなる。一方、活
性炭を添加すると、より優れた酢酸分子の除去効果を示
す。Furthermore, by adding the chemisorption type deodorant to the deodorant in the present invention, the effect of removing ammonia molecules and acetic acid molecules becomes more excellent. On the other hand, the addition of activated carbon shows a more excellent effect of removing acetic acid molecules.
【００１７】本発明においては、脱臭剤を多孔性基材に
添着させる。一般に多孔性基材とは、その表面をガスが
通過することができる穴を多量に有する基材を総称して
おり、例えば、多孔性合成樹脂、ポリウレタンフォー
ム、不織布、ループ状積層体、又はセラミックス、金
属、紙若しくは樹脂製の各種ハニカムから任意に選択す
ることができるが、ネット状合成樹脂、ポリウレタンフ
ォーム又は不織布を多孔性基材に使用すると、脱臭フィ
ルターを薄くすると共に、経済性の点で望ましい。In the present invention, a deodorant is attached to the porous substrate. Generally, a porous substrate is a generic name for substrates having a large number of holes through which gas can pass, and examples thereof include porous synthetic resin, polyurethane foam, nonwoven fabric, looped laminate, or ceramics. , It can be arbitrarily selected from various honeycombs made of metal, paper or resin. However, when net-like synthetic resin, polyurethane foam or non-woven fabric is used as the porous base material, the deodorizing filter becomes thin and economically advantageous. desirable.
【００１８】これらの多孔性基材に添着する脱臭剤の添
着量が１０ｇ／ｍ2 未満であると脱臭性能が不十分であ
り、脱臭剤の添着量が１０００ｇ／ｍ2 を超えると優れ
た脱臭性能を示すものの、通気抵抗が１０ｍｍＡｑ以上
となるため、フィルタとしての使用に適さない。従っ
て、多孔性基材に添着する脱臭剤の添着量は、１０乃至
１０００ｇ／ｍ2 の範囲で、使用する脱臭フィルタに要
求される脱臭性能、通気抵抗及び経済性によって任意に
選択できる。If the amount of the deodorant attached to these porous substrates is less than 10 g / m 2 , the deodorizing performance is insufficient, and if the amount of the deodorant attached exceeds 1000 g / m 2 , excellent deodorization is achieved. Although it shows performance, it has a ventilation resistance of 10 mmAq or more and is not suitable for use as a filter. Therefore, the amount of the deodorant attached to the porous substrate is 10 to 1000 g / m 2 Within the range, it can be arbitrarily selected depending on the deodorizing performance, ventilation resistance and economy required for the deodorizing filter to be used.
【００１９】[0019]
【実施例】以下、本発明に係る脱臭フィルタの実施例に
ついてその比較例と比較して具体的に説明する。EXAMPLES Examples of the deodorizing filter according to the present invention will be specifically described below in comparison with comparative examples.
【００２０】本発明に係る脱臭フィルタは、バインダー
としては例えばカルボキシルメチルセルロース（ＣＭ
Ｃ）及び酢酸ビニルが使用され、脱臭剤とバインダーと
の比率を例えば１７対１として、配合液中の総固形物量
を２５％に調整したスラリーを多孔性基材に含浸させ
て、目詰まりをとばした後に乾燥させて作製する。In the deodorizing filter according to the present invention, as a binder, for example, carboxymethyl cellulose (CM) is used.
C) and vinyl acetate are used, the ratio of the deodorant to the binder is set to, for example, 17: 1, and the porous base material is impregnated with the slurry in which the total solid content in the compounding liquid is adjusted to 25% to prevent clogging. It is produced by skipping and then drying.
【００２１】先ず、脱臭剤中の各種遷移金属酸化物に対
する脱臭性能を比較するために、下記表１に示す遷移金
属酸化物を使用した実施例に関して、悪臭分子の除去率
を脱臭性能として評価した。但し、ゼオライトはハイシ
リカゼオライト（Ｓｉ成分：Ａｌ成分＝４０：１乃至５
０：１）を使用して、これと遷移金属酸化物との重量比
を６０対４０とし、多孔性基材としてポリエステル製ネ
ットを使用した。比較例としては、脱臭剤の原料に活性
炭を使用して脱臭フィルタを作製した。これらの脱臭性
能の評価結果を下記表１に併せて示す。なお、悪臭分子
の濃度は測定を開始してから５分後の値を採用し、下記
数式１に示す方法で除去率を計算した。First, in order to compare the deodorizing performance with respect to various transition metal oxides in the deodorant, with respect to the examples using the transition metal oxides shown in Table 1 below, the removal ratio of malodorous molecules was evaluated as the deodorizing performance. . However, the zeolite is high silica zeolite (Si component: Al component = 40: 1 to 5).
0: 1) was used and the weight ratio of the transition metal oxide to the transition metal oxide was 60:40, and a polyester net was used as the porous substrate. As a comparative example, a deodorizing filter was produced by using activated carbon as a raw material of the deodorizing agent. The evaluation results of these deodorizing performances are also shown in Table 1 below. As the concentration of the malodorous molecule, a value 5 minutes after the measurement was started was adopted, and the removal rate was calculated by the method shown in the following mathematical formula 1.
【００２２】[0022]
【数１】除去率（％）＝｛（入口濃度−出口濃度）／入
口濃度｝×１００[Equation 1] Removal rate (%) = {(inlet concentration−outlet concentration) / inlet concentration} × 100
【００２３】また、悪臭分子としては、タバコ臭の主成
分であるアンモニア、アセトアルデヒド、酢酸及び硫化
水素の４成分を選定して測定した。但し、アセトアルデ
ヒドについては、製造した脱臭フィルタのサンプルを４
枚重ねて測定した。As the malodorous molecule, four components, which are the main components of tobacco odor, ammonia, acetaldehyde, acetic acid and hydrogen sulfide were selected and measured. However, regarding acetaldehyde, 4
The measurement was performed by stacking one sheet.
【００２４】[0024]
【表１】 [Table 1]
【００２５】上記表１に示すように、比較例１の従来の
活性炭フィルタと比較して、実施例１乃至３は悪臭分子
となる４成分全てについて、脱臭性能が向上した。その
中でも、特に、脱臭剤として有効な遷移金属酸化物はＣ
ｕ−Ｍｎ系酸化物であり、以下、Ｍｎ酸化物、Ｆｅ−Ｍ
ｎ系酸化物の順である。As shown in Table 1 above, in comparison with the conventional activated carbon filter of Comparative Example 1, Examples 1 to 3 have improved deodorizing performance with respect to all four components which are malodorous molecules. Among them, the transition metal oxide particularly effective as a deodorant is C
u-Mn-based oxide, hereinafter Mn oxide, Fe-M
The order is n-type oxides.
【００２６】次に、脱臭剤中のゼオライトに対する脱臭
性能を比較するために、下記表２に示すゼオライトを使
用した実施例に関して、悪臭分子の除去率を脱臭性能と
して評価した。但し、遷移金属酸化物は前記表１の評価
で最も優れた脱臭効果を示したＣｕ−Ｍｎ系酸化物を使
用して、その他の条件は表１と同様に設定した。これら
の脱臭性能の評価結果を下記表２に併せて示す。Next, in order to compare the deodorizing performance with respect to the zeolite in the deodorizing agent, the removal rate of the malodorous molecules was evaluated as the deodorizing performance in the examples using the zeolites shown in Table 2 below. However, as the transition metal oxide, a Cu-Mn-based oxide showing the most excellent deodorizing effect in the evaluation of Table 1 was used, and the other conditions were set in the same manner as in Table 1. The evaluation results of these deodorizing performances are also shown in Table 2 below.
【００２７】[0027]
【表２】 [Table 2]
【００２８】上記表２に示すように、比較例１の従来の
活性炭フィルタと比較して、実施例１及び６については
悪臭分子となる４成分全てについて、脱臭性能が向上
し、特に、脱臭剤として有効なゼオライトはハイシリカ
ゼオライトであった。また、実施例４及び５について
も、酢酸を除く３成分について、良好な脱臭効果を示し
た。As shown in Table 2 above, in comparison with the conventional activated carbon filter of Comparative Example 1, in Examples 1 and 6, the deodorizing performance was improved with respect to all four components which are malodorous molecules, and in particular, the deodorizing agent was used. The effective zeolite was high silica zeolite. In addition, Examples 4 and 5 also showed a good deodorizing effect for the three components except acetic acid.
【００２９】また、脱臭剤中におけるゼオライト及び遷
移金属酸化物の重量比に対する脱臭性能を比較するため
に、下記表３に示す重量比である脱臭剤原料を使用した
実施例及び比較例について、悪臭分子の除去率を脱臭性
能として評価した。但し、ゼオライト及び遷移金属酸化
物は前記表１及び２の評価で最も優れた脱臭効果を示し
たハイシリカゼオライト及びＣｕ−Ｍｎ系酸化物を使用
して、その他の条件は表１と同様に設定した。なお、多
孔性基材に添着する脱臭剤の添着量は２５０ｇ／ｍ2 と
した。これらの脱臭性能の評価結果を下記表３に併せて
示す。Further, in order to compare the deodorizing performance with respect to the weight ratio of the zeolite and the transition metal oxide in the deodorant, the bad odor was obtained in Examples and Comparative Examples in which the deodorant raw materials having the weight ratios shown in Table 3 below were used. The removal rate of molecules was evaluated as the deodorizing performance. However, as the zeolite and the transition metal oxide, high silica zeolite and Cu-Mn-based oxide which showed the most excellent deodorizing effect in the evaluations of Tables 1 and 2 were used, and other conditions were set in the same manner as in Table 1. did. The amount of the deodorant attached to the porous substrate was 250 g / m 2 . The evaluation results of these deodorizing performances are also shown in Table 3 below.
【００３０】[0030]
【表３】 [Table 3]
【００３１】上記表３に示すように、比較例２及び３は
脱臭剤中におけるゼオライトの重量比が本発明の範囲か
ら外れ、４０重量％未満であるので、アンモニア、アセ
トアルデヒド及び酢酸に対する脱臭効果が低い。また、
比較例４は脱臭剤が全てゼオライトからなっているの
で、硫化水素に対する除去効果がない。一方、実施例１
及び７乃至１２は脱臭剤中におけるゼオライト及び遷移
金属酸化物の重量比が本発明の範囲内であるので、全て
の悪臭分子について良好な脱臭性能を示した。As shown in Table 3 above, in Comparative Examples 2 and 3, the weight ratio of the zeolite in the deodorant is outside the range of the present invention and is less than 40% by weight, so that the deodorizing effect on ammonia, acetaldehyde and acetic acid is not high. Low. Also,
Since the deodorant of Comparative Example 4 is entirely made of zeolite, it has no effect of removing hydrogen sulfide. On the other hand, Example 1
And Nos. 7 to 12 exhibited good deodorizing performance for all malodorous molecules, because the weight ratio of zeolite and transition metal oxide in the deodorant was within the range of the present invention.
【００３２】次に、脱臭剤として最も有効なゼオライト
及び遷移金属酸化物を使用した実施例１に、下記表４に
示す消臭剤を２５％の割合で添加した脱臭剤に関して、
前記表１乃至３に示す評価と同様に、悪臭分子の除去率
を脱臭性能として評価した。但し、活性炭は１００メッ
シュ以下の粉末活性炭を使用した。これらの脱臭性能の
評価結果を下記表４に併せて示す。Next, with respect to the deodorant obtained by adding 25% of the deodorant shown in Table 4 below to Example 1 using the most effective zeolite and transition metal oxide as the deodorant,
Similar to the evaluations shown in Tables 1 to 3, the removal rate of malodorous molecules was evaluated as the deodorizing performance. However, the activated carbon used was powdered activated carbon of 100 mesh or less. The evaluation results of these deodorizing performances are also shown in Table 4 below.
【００３３】[0033]
【表４】 [Table 4]
【００３４】上記表４に示すように、実施例１の消臭剤
の添加がないものと比較して、実施例１３は特にアンモ
ニアに関して、脱臭性能が向上した。実施例１４はアン
モニア及び酢酸に関して高い脱臭効果を示し、実施例１
５は酢酸に関して脱臭性能が向上した。As shown in Table 4 above, the deodorizing performance of Example 13 was improved especially with respect to ammonia, as compared with Example 1 in which the deodorant was not added. Example 14 shows a high deodorizing effect with respect to ammonia and acetic acid.
No. 5 had improved deodorizing performance with respect to acetic acid.
【００３５】更に、比較例１、実施例１乃至３及び１３
乃至１５について、たばこの処理本数試験を行った。但
し、たばこの処理本数試験は、（社）日本電気工業会の
空気清浄機脱臭性能試験に関する自主基準における性能
試験方法に準拠して評価した。これらの評価結果を下記
表５に示す。Further, Comparative Example 1, Examples 1 to 3 and 13
The number of cigarettes processed was tested for Nos. 15 to 15. However, the cigarette treatment number test was evaluated in accordance with the performance test method based on the voluntary standard for the air purifier deodorizing performance test of the Japan Electrical Manufacturers' Association. The results of these evaluations are shown in Table 5 below.
【００３６】[0036]
【表５】 [Table 5]
【００３７】上記表５に示すように、実施例１乃至３及
び１３乃至１５は比較例１に対して、たばこの処理本数
が著しく向上した。As shown in Table 5 above, in Examples 1 to 3 and 13 to 15, the number of treated cigarettes was remarkably improved as compared with Comparative Example 1.
【００３８】また、多孔性基材の種類に対する脱臭フィ
ルタの性能を比較するために、下記表６に示す多孔性基
材に、脱臭剤原料として実施例１と同様に、ハイシリカ
ゼオライト及びＣｕ−Ｍｎ系酸化物を６０対４０の重量
比で混合したものを２５０ｇ／ｍ2 添着した各種多孔性
基材に関して、通気抵抗、素材厚さ、たばこ処理本数を
測定した。更に、それらの多孔性基材の経済性も考慮し
て総合的に評価した。これらの測定結果及び評価結果を
下記表６に併せて示す。但し、通気抵抗の測定条件は、
面風速を１ｍ／ｓｅｃとした。Further, in order to compare the performance of the deodorizing filter with respect to the kind of the porous base material, the porous base material shown in Table 6 below was used as the deodorant raw material in the same manner as in Example 1, such as high silica zeolite and Cu-. 250 g / m 2 of a mixture of Mn-based oxides at a weight ratio of 60:40 With respect to each of the various porous substrates attached, the ventilation resistance, the material thickness, and the number of cigarettes treated were measured. Furthermore, comprehensive evaluation was performed in consideration of the economical efficiency of those porous substrates. The measurement results and evaluation results are also shown in Table 6 below. However, the measurement conditions of ventilation resistance are
The surface wind speed was 1 m / sec.
【００３９】[0039]
【表６】 [Table 6]
【００４０】上記表６に示すように、実施例１、１６及
び１８は通気性が特に優れ、実施例１８及び１９は、た
ばこの処理本数が高い値を示している。しかしながら、
エアコン又は空気清浄機等への適応を素材の厚さ及び経
済性等より考慮すると、多孔性基材としてネット状合成
樹脂、ポリウレタンフォーム又は不織布が最適である。As shown in Table 6 above, Examples 1, 16 and 18 are particularly excellent in air permeability, and Examples 18 and 19 show a high number of cigarettes to be treated. However,
Considering the adaptability to an air conditioner or an air purifier, etc., from the viewpoint of the thickness and economical efficiency of the material, a net synthetic resin, polyurethane foam or nonwoven fabric is most suitable as the porous substrate.
【００４１】前記表１乃至６に示すように、本発明は従
来の活性炭による脱臭フィルタと比較して著しく良好な
性能を有する脱臭フィルタを得ることができた。As shown in Tables 1 to 6, according to the present invention, it was possible to obtain a deodorizing filter having remarkably good performance as compared with the conventional deodorizing filter using activated carbon.
【００４２】[0042]
【発明の効果】以上詳述したように本発明によれば、ゼ
オライト及び遷移金属酸化物を含有する脱臭剤が多孔性
基材に添着されているので、たばこ臭に対する脱臭効果
が向上し、ゼオライトとしてハイシリカゼオライトを使
用し、脱臭剤に化学吸着型消臭剤又は活性炭を添加する
と、脱臭効果がより一層優れたものとなる。また、多孔
性基材にネット状合成樹脂、ポリウレタンフォーム又は
不織布を使用すると、製造コストが低く、脱臭フィルタ
ーを薄くすることができる。As described in detail above, according to the present invention, since the deodorant containing zeolite and transition metal oxide is attached to the porous substrate, the deodorizing effect on the tobacco odor is improved, and the zeolite If a high-silica zeolite is used as the above and a chemical adsorption type deodorant or activated carbon is added to the deodorant, the deodorizing effect is further enhanced. When a net synthetic resin, polyurethane foam or nonwoven fabric is used for the porous substrate, the manufacturing cost is low and the deodorizing filter can be made thin.
Claims (6)
る脱臭剤が多孔性基材に添着されていることを特徴とす
る脱臭フィルタ。1. A deodorizing filter comprising a deodorant containing zeolite and a transition metal oxide attached to a porous substrate.
至９５重量％含有され、前記遷移金属酸化物は前記脱臭
剤中に５乃至６０重量％含有されていることを特徴とす
る請求項１に記載の脱臭フィルタ。2. The deodorant is contained in the deodorant in an amount of 40 to 95% by weight, and the transition metal oxide is included in the deodorant in an amount of 5 to 60% by weight. Deodorizing filter described.
であることを特徴とする請求項１又は２に記載の脱臭フ
ィルタ。3. The deodorizing filter according to claim 1, wherein the zeolite is high silica zeolite.
Ｆｅからなる群から選択された１又は２以上の遷移金属
元素の酸化物であることを特徴とする請求項１又は２に
記載の脱臭フィルタ。4. The transition metal oxide according to claim 1, wherein the transition metal oxide is an oxide of one or more transition metal elements selected from the group consisting of Cu, Mn and Fe. Deodorizing filter.
性炭からなる群から選択された少なくとも１種の消臭剤
が添加されていることを特徴とする請求項１乃至４のい
ずれか１項に記載の脱臭フィルタ。5. The deodorant according to claim 1, wherein at least one deodorant selected from the group consisting of a chemisorption type deodorant and activated carbon is added. The deodorizing filter according to item 1.
ポリウレタンフォーム及び不織布からなる群から選択さ
れた１種であることを特徴とする請求項１乃至５のいず
れか１項に記載の脱臭フィルタ。6. The net base synthetic resin,
The deodorizing filter according to claim 1, wherein the deodorizing filter is one selected from the group consisting of polyurethane foam and non-woven fabric.