JPH09292514A - Color filter and liquid crystal display device - Google Patents
Color filter and liquid crystal display deviceInfo
- Publication number
- JPH09292514A JPH09292514A JP10742496A JP10742496A JPH09292514A JP H09292514 A JPH09292514 A JP H09292514A JP 10742496 A JP10742496 A JP 10742496A JP 10742496 A JP10742496 A JP 10742496A JP H09292514 A JPH09292514 A JP H09292514A
- Authority
- JP
- Japan
- Prior art keywords
- film
- liquid crystal
- color filter
- color
- display device
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、基板に平行な向き
を持つ電界により駆動される液晶表示装置に使用される
カラーフィルター関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a color filter used in a liquid crystal display device driven by an electric field having a direction parallel to a substrate.
【０００２】[0002]
【従来の技術】基板に平行な向きの電界で駆動される液
晶表示装置に使用されるカラーフィルターについては、
基板に平行な向きに有効に電界をかけるためにカラーフ
ィルターを液晶より低い比誘電率の材料、好ましくは半
分以下の比誘電率の材料で構成することが重要である
が、従来使用されていたカラーフィルターにおいては、
金属ブラックマトリックス等の高比誘電率の材料が使わ
れていたため液晶中に有効な横電界をかけることが困難
であった。2. Description of the Related Art A color filter used in a liquid crystal display device driven by an electric field parallel to a substrate is
In order to effectively apply an electric field in the direction parallel to the substrate, it is important that the color filter is composed of a material having a relative dielectric constant lower than that of the liquid crystal, preferably a material having a relative dielectric constant of less than half, but it has been conventionally used In the color filter,
Since a material having a high relative dielectric constant such as a metal black matrix is used, it is difficult to apply an effective lateral electric field in the liquid crystal.
【０００３】[0003]
【発明が解決しようとする課題】本発明の課題は、基板
に平行な向きの電界にて駆動される液晶表示装置におい
て、液晶中に有効かつ安定に電界をかけられるカラーフ
ィルター及びそれを有する液晶表示装置を提供すること
にある。SUMMARY OF THE INVENTION An object of the present invention is to provide a color filter capable of effectively and stably applying an electric field in a liquid crystal in a liquid crystal display device driven by an electric field in a direction parallel to a substrate, and a liquid crystal having the color filter. It is to provide a display device.
【０００４】[0004]
【課題を解決するための手段】上記課題を解決するため
に本発明は次の構成を有する。In order to solve the above problems, the present invention has the following constitution.
【０００５】透明基板上に着色膜を形成してなるカラー
フィルターにおいて、該着色膜の比誘電率が４．５以下
であることを特徴とするカラーフィルター。A color filter having a colored film formed on a transparent substrate, wherein the colored film has a relative dielectric constant of 4.5 or less.
【０００６】[0006]
【発明の実施の形態】本発明で言うところのカラーフィ
ルターとは、任意の色数で各色別に所望のパタ−ン状に
設けられた着色層からなる画素を有し、図１で示すとこ
ろの層構成、つまり透明基板上に着色層が形成されたカ
ラーフィルターであり、主に透明基板に対して平行な向
きの電界（横電界）により駆動されるカラ−液晶表示装
置に用いられる。BEST MODE FOR CARRYING OUT THE INVENTION A color filter as referred to in the present invention has a pixel composed of a colored layer provided in a desired pattern for each color with an arbitrary number of colors, as shown in FIG. It is a color filter having a layer structure, that is, a colored layer formed on a transparent substrate, and is mainly used in a color liquid crystal display device driven by an electric field (horizontal electric field) in a direction parallel to the transparent substrate.
【０００７】本発明で言うところの着色膜とは任意の色
の光を透過する性能を有する膜であり、その比誘電率が
４．５以下、より好ましくは３．６以下であることが好
ましい。The colored film as referred to in the present invention is a film having a property of transmitting light of an arbitrary color, and its relative dielectric constant is preferably 4.5 or less, more preferably 3.6 or less. .
【０００８】液晶中に基板に平行な向きに有効に電界を
かけるためには、カラーフィルター構成材料の比誘電率
が、液晶の比誘電率の短軸成分、若しくは長軸成分のい
ずれかより小さいこと、より好ましくは１／２以下であ
ることが望ましい。カラーフィルター構成材料の比誘電
率が大きくなるにつれ、液晶とカラーフィルターとの界
面において電界の向きが基板に平行な向きからのずれが
大きくなり実効電界が低下するため、液晶のスイッチン
グ効率が低下するからである。着色膜は、オーバーコー
トレスカラーフィルターの場合は、液晶に直接接する、
若しくは配向膜を介して接する部分であるため、より低
比誘電率の材料であることが好ましい。In order to effectively apply an electric field in the liquid crystal in a direction parallel to the substrate, the relative permittivity of the color filter constituent material is smaller than either the short axis component or the long axis component of the relative permittivity of the liquid crystal. It is desirable that it is 1/2 or less. As the relative permittivity of the color filter constituent material increases, the switching efficiency of the liquid crystal decreases because the direction of the electric field at the interface between the liquid crystal and the color filter deviates from the direction parallel to the substrate and the effective electric field decreases. Because. In the case of an overcoatless color filter, the colored film is in direct contact with the liquid crystal,
Alternatively, since it is a portion that contacts through the alignment film, a material having a lower relative dielectric constant is preferable.
【０００９】又、オーバーコート膜を有する場合でもカ
ラーフィルター全体の比誘電率を下げるという点から、
より低比誘電率の材料であることが好ましい。Further, even when the overcoat film is provided, the relative dielectric constant of the entire color filter is lowered,
A material having a lower relative dielectric constant is preferable.
【００１０】薄膜トランジスタにて駆動される液晶表示
装置に使用される液晶の比誘電率の最大成分は通常８〜
１２程度、少なくとも４．５以上である。従って、該着
色膜の比誘電率は４．５以下、より好ましくは３．６以
下であることが好ましい。ここで言う比誘電率は２０
℃、周波数１００〜１００ｋＨｚでの測定値を指す。The maximum component of the relative permittivity of liquid crystal used in a liquid crystal display device driven by thin film transistors is usually 8 to
It is about 12, at least 4.5 or more. Therefore, the relative permittivity of the colored film is preferably 4.5 or less, more preferably 3.6 or less. The relative permittivity here is 20
It indicates a measured value at a temperature of 100 to 100 kHz.
【００１１】着色膜の具体的材質としては、顔料及び染
料分散されたポリイミド膜、若しくはアクリル膜、染色
処理されたＰＶＡ（ポリビニルアルコール）、任意の光
のみを透過するように膜厚制御されたＳｉＯ２膜等があ
るが、顔料分散されたポリイミド膜である事がより好ま
しい。耐熱性、耐加工性、耐薬品性、プロセスの簡便
さ、という点では顔料分散されたポリイミド膜、アクリ
ル膜が好ましく、比誘電率の点からはポリイミド膜がア
クリル膜より低比誘電率であるためより好ましいからで
ある。又、ポリイミド膜を使用した場合は着色膜を直接
ラビング処理することにより、着色膜に液晶の配向規制
力を持たせることも可能であるからである。Specific materials of the colored film include a polyimide film in which a pigment and a dye are dispersed, an acrylic film, a dyed PVA (polyvinyl alcohol), and a SiO2 film whose thickness is controlled so that only arbitrary light is transmitted. Although there is a film or the like, a polyimide film in which a pigment is dispersed is more preferable. From the viewpoint of heat resistance, process resistance, chemical resistance, and process simplicity, a pigment-dispersed polyimide film or acrylic film is preferable. From the viewpoint of relative dielectric constant, the polyimide film has a lower relative dielectric constant than the acrylic film. Therefore, it is more preferable. Further, when a polyimide film is used, it is possible to give the colored film a liquid crystal alignment regulating force by directly rubbing the colored film.
【００１２】本発明で用いられるカラーフィルターはブ
ラックマトリクスと呼ばれる、各画素間に配列された遮
光領域を有することが望ましい。液晶表示装置のコント
ラストを向上させることができるからである。The color filter used in the present invention preferably has a light-shielding area called a black matrix arranged between pixels. This is because the contrast of the liquid crystal display device can be improved.
【００１３】ブラックマトリックスとしては通常Ｃｒ、
Ａｌ、Ｎｉなどの金属薄膜（厚さ約０．１〜０．２μ
ｍ）や樹脂中に遮光剤を分散させてなる樹脂ブラックマ
トリクスが用いられる。本発明においては金属薄膜のブ
ラックマトリクスも使用可能であるが、ポリイミド膜中
に黒色顔料を分散させてなる樹脂ブラックマトリクスを
用いることがより好ましい。低反射、耐熱性, 、耐溶剤
性に優れるという特徴を持つうえ、画素上と同様にラビ
ング処理により液晶の配向規制力を持たせることも可能
であるからである。又、樹脂を用いることによりカラー
フィルターの誘電率を低くすることができる。The black matrix is usually Cr,
Metal thin films such as Al and Ni (thickness of about 0.1 to 0.2μ
m) or a resin black matrix in which a light shielding agent is dispersed in a resin is used. Although a black matrix of a metal thin film can be used in the present invention, it is more preferable to use a resin black matrix in which a black pigment is dispersed in a polyimide film. This is because, in addition to having the characteristics of low reflection, heat resistance, and excellent solvent resistance, it is also possible to give a liquid crystal alignment regulating force by rubbing treatment as in the case of pixels. In addition, the use of resin can reduce the dielectric constant of the color filter.
【００１４】本発明で用いられる顔料には特に制限はな
いが、顔料の中でも耐光性、耐熱性、耐薬品性に優れた
物が望ましい。代表的な顔料の具体的な例をカラーイン
デックス（ＣＩ）ナンバ−で示す。黄色顔料の例として
はピグメントイエロー２０、２４、８３、８６、９３、
９４、１０９、１１０、１１７、１２５、１３７、１３
８、１３９、１４７、１４８、１５３、１５４、１６
６、１７３などがあげられる。橙色顔料の例としてはピ
グメントオレンジ１３、３１、３６、３８、４０、４
２、４３、５１、５５、５９、６１、６４、６５などが
挙げられる。赤色顔料の例としてはピグメントレッド
９、９７、１２２、１２３、１４４、１４９、１６６、
１６８、１７７、１８０、１９２、２１５、２１６、２
２４などが挙げられる。紫色顔料の例としてはピグメン
トバイオレット１９、２３、２９、３２、３３、３６、
３７、３８などが挙げられる。青色顔料の例としてはピ
グメントブルー１５（１５：３、１５：４、１５：６な
ど）、２１，２２、６０、６４などが挙げられる。緑色
顔料の例としてはピグメントグリーン７、１０、３６、
４７などが挙げられる。黒色顔料の例としてはピグメン
トブラック７などが挙げられる。本発明ではこれらに限
定されず種々の顔料を使用する事ができる。なお、顔料
は必要に応じて、ロジン処理，酸性基処理，塩基性基処
理などの表面処理が施されている物を使用してもよい。The pigment used in the present invention is not particularly limited, but among the pigments, those having excellent light resistance, heat resistance and chemical resistance are desirable. Specific examples of typical pigments are shown by color index (CI) numbers. Examples of yellow pigments include Pigment Yellow 20, 24, 83, 86, 93,
94, 109, 110, 117, 125, 137, 13
8, 139, 147, 148, 153, 154, 16
6, 173 and the like. Pigment oranges 13, 31, 36, 38, 40, 4 are examples of orange pigments.
2, 43, 51, 55, 59, 61, 64, 65 and the like. Examples of red pigments include Pigment Red 9, 97, 122, 123, 144, 149, 166,
168, 177, 180, 192, 215, 216, 2
24 and the like. Examples of violet pigments include Pigment Violet 19, 23, 29, 32, 33, 36,
37, 38 and the like. Examples of blue pigments include Pigment Blue 15 (15: 3, 15: 4, 15: 6, etc.), 21, 22, 60, 64 and the like. Examples of green pigments include Pigment Green 7, 10, 36,
47 and the like. Pigment Black 7 and the like are examples of the black pigment. The present invention is not limited to these, and various pigments can be used. The pigment may be subjected to surface treatment such as rosin treatment, acidic group treatment and basic group treatment, if necessary.
【００１５】本発明で言うところの顔料分散されたポリ
イミド膜とは、該顔料を分散したポリアミック酸溶液を
基板上に塗布する事により形成される一般式（１）で表
わされる構造単位を主成分とするポリイミド前駆体着色
被膜を加熱処理し，イミド環やその他の環状構造を有す
るポリマ（ポリイミド、ポリアミドイミド）となすこと
によって得られる着色被膜のことである。The term "pigment-dispersed polyimide film" as used in the present invention means that the structural unit represented by the general formula (1) is formed by applying a polyamic acid solution in which the pigment is dispersed onto a substrate. Is a colored film obtained by heat-treating the polyimide precursor colored film to obtain a polymer (polyimide, polyamide-imide) having an imide ring or other cyclic structure.
【００１６】[0016]
【化１】 ここで一般式（１）のｎは１〜２である。Ｒ１は少なく
とも２個の炭素原子を有する３価または４価の有機基で
ある。耐熱性の面から、Ｒ１は環状炭化水素、芳香族環
または芳香族複素環を含有し、かつ炭素数６から３０の
３価または４価の基が好ましい。Ｒ１の例として、フェ
ニル基、ビフェニル基、ターフェニル基、ナフタレン
基、ペリレン基、ジフェニルエーテル基、ジフェニルス
ルフォン基、ジフェニルプロパン基、ベンゾフェノン
基、ビフェニルトリフルオロプロパン基、シクロブチル
基、シクロペンチル基などが挙げられるがこれらに限定
されるものではない。またＲ２は少なくとも２個の炭素
原子を有する２価の有機基である。Embedded image Here, n in the general formula (1) is 1-2. R1 is a trivalent or tetravalent organic group having at least two carbon atoms. From the viewpoint of heat resistance, R1 is preferably a trivalent or tetravalent group containing a cyclic hydrocarbon, an aromatic ring or an aromatic heterocyclic ring and having 6 to 30 carbon atoms. Examples of R1 include a phenyl group, a biphenyl group, a terphenyl group, a naphthalene group, a perylene group, a diphenylether group, a diphenylsulfone group, a diphenylpropane group, a benzophenone group, a biphenyltrifluoropropane group, a cyclobutyl group, a cyclopentyl group, and the like. Is not limited to these. R2 is a divalent organic group having at least two carbon atoms.
【００１７】耐熱性の面から、Ｒ２は環状炭化水素、芳
香族環または芳香族複素環を含有し、かつ炭素数６から
３０の２価の基が好ましい。Ｒ２の例として、フェニル
基、ビフェニル基、ターフェニル基、ナフタレン基、ペ
リレン基、ジフェニルエーテル基、ジフェニルスルフォ
ン基、ジフェニルプロパン基、ベンゾフェノン基、ビフ
ェニルトリフルオロプロパン基、ジフェニルメタン基、
シクロヘキシルメタン基などが挙げられるがこれらに限
定されるものではない。一般式（１）で表わされる構造
単位を主成分とするポリマはＲ１、Ｒ２がこれらの内各
々１個から構成されていても良いし、各々２種以上から
構成される共重合体であっても良い。 基板との接着力
を向上させるため耐熱性を低下させない範囲でジアミン
成分として、シロキサン構造を有するビス（３−アミノ
プロピル）テトラメチルジシロキサンなどを共重合させ
ても良い。またアミン末端の封止剤として無水マレイン
酸などの無水物をポリイミド前駆体の重合終了後に末端
濃度に応じて加え、反応させても良い。ポリイミド膜の
力学的特性は、分子量が大きいほど良好である。このた
め、ポリイミド前駆体の分子量も大きい事が望まれる。
一方、ポリイミド前駆体を湿式エッチングによりパタ−
ン加工を行う場合、ポリイミド前駆体の分子量が大き過
ぎると、現像に要する時間が長くなり過ぎるという問題
がある。このため通常重合度は、５から１０００の範囲
にする事が望ましい。From the viewpoint of heat resistance, R2 is preferably a divalent group containing a cyclic hydrocarbon, an aromatic ring or an aromatic heterocycle and having 6 to 30 carbon atoms. Examples of R2 are phenyl group, biphenyl group, terphenyl group, naphthalene group, perylene group, diphenyl ether group, diphenyl sulfone group, diphenylpropane group, benzophenone group, biphenyltrifluoropropane group, diphenylmethane group,
Examples thereof include, but are not limited to, a cyclohexylmethane group. In the polymer having the structural unit represented by the general formula (1) as a main component, R1 and R2 may be each composed of one of these, or a copolymer composed of two or more of each. Is also good. Bis (3-aminopropyl) tetramethyldisiloxane having a siloxane structure may be copolymerized as a diamine component as long as the heat resistance is not reduced in order to improve the adhesion to the substrate. In addition, an anhydride such as maleic anhydride may be added as a blocking agent for the amine terminal, depending on the terminal concentration, after the completion of the polymerization of the polyimide precursor, and reacted. The higher the molecular weight, the better the mechanical properties of the polyimide film. For this reason, it is desired that the molecular weight of the polyimide precursor is also large.
On the other hand, the polyimide precursor is patterned by wet etching.
When the polyimide processing is performed, if the molecular weight of the polyimide precursor is too large, there is a problem that the time required for development becomes too long. For this reason, it is usually desirable that the degree of polymerization be in the range of 5 to 1,000.
【００１８】本発明で言うところのカラーフィルターは
該着色膜上にオーバーコート膜を有していてもかまわな
い。オーバーコート膜とは、該着色被膜が耐熱性、耐薬
品性、硬度、段差平坦性等の点で実用上問題を有する場
合に、該着色被膜の保護、カラーフィルター表面の平坦
化のため形成される膜であり。本発明においては、オー
バーコート膜を有する場合には、着色膜と同様にその比
誘電率が４．５未満、より好ましくは３．６以下である
ことが望ましい。The color filter in the present invention may have an overcoat film on the colored film. The overcoat film is formed for the purpose of protecting the colored coating and flattening the surface of the color filter when the colored coating has practical problems in terms of heat resistance, chemical resistance, hardness, step flatness, etc. It is a membrane. In the present invention, in the case of having an overcoat film, it is desirable that its relative dielectric constant is less than 4.5, more preferably 3.6 or less, like the colored film.
【００１９】具体的には、エポキシ膜、アクリルエポキ
シ膜、アクリル膜、シロキサンポリマ系の膜、ポリイミ
ド膜、ケイ素含有ポリイミド膜、ポリイミドシロキサン
膜等があげられるが、ポリイミド膜、ケイ素含有ポリイ
ミド膜、ポリイミドシロキサン膜等のポリイミド系高分
子膜であることがより好ましい、平坦性、塗布性、耐熱
性の点でよりすぐれていることに加え、これらポリイミ
ド系の膜はアクリル系の膜と比較して低比誘電率である
からである。Specific examples include an epoxy film, an acrylic epoxy film, an acrylic film, a siloxane polymer film, a polyimide film, a silicon-containing polyimide film, a polyimide siloxane film, and the like. A polyimide film, a silicon-containing polyimide film, and a polyimide film. A polyimide-based polymer film such as a siloxane film is more preferable. In addition to being superior in flatness, coatability, and heat resistance, these polyimide-based films have a lower performance than acrylic-based films. This is because it has a relative dielectric constant.
【００２０】本発明のカラーフィルタを用いて、基板と
平行な向きの電界により液晶を駆動する液晶表示装置を
作成する事により、液晶成分より着色膜の比誘電率が低
いという理由で、液晶中において基板に平行な向きに、
有効かつ安定に電界を印加することができるので、応答
速度が速く表示品位のよい液晶表示装置を提供すること
ができる。By using the color filter of the present invention to prepare a liquid crystal display device in which liquid crystal is driven by an electric field in a direction parallel to the substrate, the relative dielectric constant of the colored film is lower than that of the liquid crystal component. In a direction parallel to the substrate at
Since the electric field can be applied effectively and stably, it is possible to provide a liquid crystal display device having a fast response speed and good display quality.
【００２１】[0021]
実施例１ 無アルカリガラス基板上に、真空蒸着装置を用いてアル
ミニウム膜１０００〓を蒸着し共通電極を作製した。Example 1 A common electrode was prepared by depositing an aluminum film of 1000 liters on a non-alkali glass substrate using a vacuum vapor deposition apparatus.
【００２２】アルミニウム膜上に、ポリアミック酸溶液
に顔料が分散された、赤、青、緑、各色のカラーペース
トをスピンコートし、クリーンオーブン中において１１
０℃で２０分、引き続いて２９０℃で４０分加熱処理
し、膜厚１μｍのポリイミド着色被膜を形成した。On the aluminum film, color pastes of red, blue, green, and various colors in which pigments were dispersed in a polyamic acid solution were spin-coated, and the paste was applied in a clean oven at 11
Heat treatment was performed at 0 ° C. for 20 minutes and subsequently at 290 ° C. for 40 minutes to form a polyimide colored coating film having a film thickness of 1 μm.
【００２３】着色膜膜面に１ｃｍ角の穴が複数個あいた
ＳＵＳマスクを重ね再びアルミニウムを真空蒸着し対向
電極を作製した。A SUS mask having a plurality of 1 cm square holes was formed on the surface of the colored film, and aluminum was vacuum-deposited again to form a counter electrode.
【００２４】着色膜を一部はがして電極取り出し部を作
製した後、対向電極と、共通電極に銀ペーストを用いて
導線をとりつけた。After the colored film was partly peeled off to form an electrode lead-out portion, a conductive wire was attached to the counter electrode and the common electrode using silver paste.
【００２５】ＬＣＲメーターで共通電極と対向電極間の
容量を周波数領域１００Ｈｚ〜１００ｋＨｚの範囲で測
定した。別途ポリイミドの膜厚と対向電極面積を測定
し、比誘電率を計算した。図３に示す測定結果の通り、
比誘電率は該周波数領域において４．３以下であった。The capacitance between the common electrode and the counter electrode was measured with an LCR meter in the frequency range of 100 Hz to 100 kHz. Separately, the polyimide film thickness and the counter electrode area were measured, and the relative permittivity was calculated. As the measurement result shown in FIG.
The relative permittivity was 4.3 or less in the frequency region.
【００２６】実施例２ 無アルカリガラス上に、ポリアミック酸溶液中に黒色顔
料を分散した黒色ペーストを該ガラス基板上にスピンコ
ートし、５０℃で１０分間、９０℃で１０分間，１１０
℃で２０分間オ−ブンを用いて空気中で加熱乾燥して、
膜厚１．６μｍのポリイミド前駆体着色膜を得た。この
膜上にポジ型フォトレジスト（東京応化社製ＯＦＰＲ−
８００）を塗布し８０℃で２０分加熱乾燥して膜厚１μ
ｍのレジスト膜を得た。キャノン社製紫外線露光機ＰＬ
Ａ−５０１Ｆを用い、クロム製のフォトマスクを介し
て、波長３６５ｎｍでの強度が５０ｍＪ／ｃｍ２の紫外
線を照射した。露光後、テトラメチルアンモニウムハイ
ドロオキサイドの２．３８ｗｔ％の水溶液からなる現像
液に浸漬し、フォトレジスト及びポリイミド前駆体の現
像を同時に行った。エッチング後、不要となったフォト
レジスト層をメチルセロソルブアセテートで剥離した。
さらにこのようにして得られたポリイミド前駆体着色被
膜を窒素雰囲気中で３００℃で３０分間熱処理し、膜厚
１．２μｍのポリイミド着色被膜によりブラックマトリ
クスパターンを得た。Example 2 On a non-alkali glass, a black paste prepared by dispersing a black pigment in a polyamic acid solution was spin-coated on the glass substrate and heated at 50 ° C. for 10 minutes and 90 ° C. for 10 minutes.
Heat dry in air using an oven for 20 minutes at ℃,
A polyimide precursor colored film having a thickness of 1.6 μm was obtained. A positive photoresist (OFPR- manufactured by Tokyo Ohka Co., Ltd.) is formed on this film.
800) is applied and dried by heating at 80 ° C for 20 minutes to give a film thickness of 1μ.
m was obtained. Canon UV exposure machine PL
Using A-501F, an ultraviolet ray having an intensity of 50 mJ / cm 2 at a wavelength of 365 nm was irradiated through a photomask made of chromium. After the exposure, the photoresist and the polyimide precursor were developed at the same time by immersing in a developing solution composed of a 2.38 wt% aqueous solution of tetramethylammonium hydroxide. After the etching, the unnecessary photoresist layer was stripped with methyl cellosolve acetate.
Further, the thus obtained polyimide precursor colored film was heat-treated at 300 ° C. for 30 minutes in a nitrogen atmosphere to obtain a black matrix pattern with a 1.2 μm-thick polyimide colored film.
【００２７】同様に、実施例１で使用したポリアミック
酸溶液中に顔料分散してなる青、赤、緑のペーストにつ
いても各色につき順次同様のプロセスによりパターン化
されたポリイミド着色被膜を作製した。該着色膜をラビ
ング処理機にてラビング処理した。Similarly, with respect to the blue, red, and green pastes obtained by dispersing the pigment in the polyamic acid solution used in Example 1, patterned polyimide colored coating films were sequentially produced for each color by the same process. The colored film was rubbed with a rubbing machine.
【００２８】ついで薄膜トランジスタ素子を備えた対向
基板を次の手順で作製した。まず、無アルカリガラス上
にクロムを用いてフォトエッチングの手法によりゲート
電極とコモン電極をパターニングした後、これらの電極
を覆うように窒化シリコン（ＳｉＮ）膜からなる絶縁膜
を形成した。ゲート絶縁膜上に非晶質シリコン（ａ―Ｓ
ｉ）膜を形成し、この膜上にアルミニウムを用いて、ソ
ース電極とドレイン電極を形成した。その際、コモン電
極とドレイン電極の間に基板に平行な向きに電界がかか
るよう電極をパターニングした。これらの電極上にＳｉ
Ｎ膜で保護膜を形成した。最後にポリイミド系の配向膜
を最上層に設け、ラビング処理して薄膜トランジスタを
備えた電極付き対向基板を得た。Then, a counter substrate provided with thin film transistor elements was manufactured by the following procedure. First, a gate electrode and a common electrode were patterned on a non-alkali glass by a photoetching method using chromium, and then an insulating film made of a silicon nitride (SiN) film was formed so as to cover these electrodes. Amorphous silicon (a-S) is formed on the gate insulating film.
i) A film was formed, and a source electrode and a drain electrode were formed on this film using aluminum. At that time, the electrodes were patterned so that an electric field was applied between the common electrode and the drain electrode in a direction parallel to the substrate. Si on these electrodes
A protective film was formed with the N film. Finally, a polyimide-based alignment film was provided on the uppermost layer and rubbed to obtain a counter substrate with electrodes provided with thin film transistors.
【００２９】電極付き対向基板とカラーフィルタとを貼
り合わせ、ツイストネマチック型液晶ＺＬＩー４７９２
（ε〓＝３．１、ε‖＝８．３）を注入し液晶表示装置
を作製したところ、応答時間５０ｍｓの良好なスイッチ
ング特性が得られた。A counter substrate with electrodes and a color filter are bonded together to form a twisted nematic liquid crystal ZLI-4792.
When a liquid crystal display device was manufactured by injecting (ε = 3.1, ε∥ = 8.3), good switching characteristics with a response time of 50 ms were obtained.
【００３０】比較例１ 着色膜として、顔料分散したアクリル膜を使用して実施
例２と同様の手法で液晶表示装置を作製した。但し、カ
ラーフィルター上に配向膜として１０００〓のポリイミ
ド膜を別途形成し、ラビング処理した。該着色膜のうち
緑の着色膜の比誘電率が最も大きくその値は１００Ｈｚ
で５．０であった。該液晶表示装置を動作したところ、
液晶の応答時間は１００ｍｓであった。Comparative Example 1 A liquid crystal display device was manufactured in the same manner as in Example 2 by using an acrylic film in which a pigment was dispersed as a colored film. However, a 1000-liter polyimide film was separately formed as an alignment film on the color filter and subjected to rubbing treatment. Among the colored films, the green colored film has the largest relative permittivity and its value is 100 Hz.
Was 5.0. When the liquid crystal display device is operated,
The response time of the liquid crystal was 100 ms.
【００３１】[0031]
【発明の効果】本発明によれば、液晶表示装置を作製し
た際、液晶中により有効かつ安定に横電界をかけうるカ
ラーフィルターを提供する事ができる。According to the present invention, it is possible to provide a color filter capable of applying a lateral electric field more effectively and stably in a liquid crystal when a liquid crystal display device is manufactured.
【図１】本発明の実施例２におけるカラーフィルター基
板の断面図。FIG. 1 is a sectional view of a color filter substrate according to a second embodiment of the present invention.
【図２】本発明の実施例２におけるカラーフィルター基
板を使用した液晶表示装置の断面図の一例。FIG. 2 is an example of a cross-sectional view of a liquid crystal display device using a color filter substrate according to a second embodiment of the present invention.
【図３】本発明で使用した着色膜の比誘電率の測定結
果。 １ 透明基板 ２ 遮光層 ３ 着色膜 ４ 配向膜 ５ 保護膜 ６ 絶縁膜 ７ ゲート電極 ８ ドレイン電極 ９ ソース電極（画素電極） １０ コモン電極 １１ 薄膜トランジスタ １２ 液晶層FIG. 3 shows the measurement results of the relative dielectric constant of the colored film used in the present invention. DESCRIPTION OF SYMBOLS 1 Transparent substrate 2 Light-shielding layer 3 Coloring film 4 Alignment film 5 Protective film 6 Insulating film 7 Gate electrode 8 Drain electrode 9 Source electrode (pixel electrode) 10 Common electrode 11 Thin film transistor 12 Liquid crystal layer
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｇ０２Ｆ 1/136 ５００ Ｇ０２Ｆ 1/136 ５００ ─────────────────────────────────────────────────── ─── Continuation of the front page (51) Int.Cl. 6 Identification code Office reference number FI technical display location G02F 1/136 500 G02F 1/136 500
Claims (7)
フィルターにおいて、該着色膜の比誘電率が４．５以下
であることを特徴とするカラーフィルター。1. A color filter in which a colored film is formed on a transparent substrate, wherein the colored film has a relative dielectric constant of 4.5 or less.
フィルターにおいて、該着色膜の比誘電率が３．６以下
であることを特徴とする請求項１記載のカラーフィルタ
ー。2. A color filter comprising a transparent substrate and a colored film formed on the transparent substrate, wherein the colored film has a relative dielectric constant of 3.6 or less.
ることを特徴とする請求項１記載のカラーフィルター。3. The color filter according to claim 1, wherein the colored film is a polyimide film in which a pigment is dispersed.
る樹脂ブラックマトリクスを有することを特徴とする請
求項１記載のカラーフィルター。4. The color filter according to claim 1, further comprising a resin black matrix in which a black pigment is dispersed in a polyimide film.
ことを特徴とする液晶表示装置。5. A liquid crystal display device comprising the color filter according to claim 1.
に平行な向きに電界をかけられるよう構成された対向基
板を有することを特徴とする液晶表示装置。6. A liquid crystal display device, comprising: the color filter according to claim 1; and a counter substrate configured to apply an electric field in a direction parallel to the substrate.
薄膜トランジスタを備えていることを特徴とする請求項
５記載の液晶表示装置。7. The liquid crystal display device according to claim 5, wherein the counter substrate with electrodes used in the liquid crystal display device comprises a thin film transistor.