JPH09285569A - Tennis racket - Google Patents
Tennis racketInfo
- Publication number
- JPH09285569A JPH09285569A JP8101289A JP10128996A JPH09285569A JP H09285569 A JPH09285569 A JP H09285569A JP 8101289 A JP8101289 A JP 8101289A JP 10128996 A JP10128996 A JP 10128996A JP H09285569 A JPH09285569 A JP H09285569A
- Authority
- JP
- Japan
- Prior art keywords
- tennis racket
- face portion
- rigidity
- face part
- rigidity material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明はテニスラケットに係
り、特に反発性能が良好なテニスラケットに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a tennis racket, and more particularly to a tennis racket having good resilience performance.
【０００２】[0002]
【従来の技術】テニスラケットは、周知の通り、ガット
（ストリング）が張られるフェース部と、プレーヤーに
よって握られるグリップ部と、これらをつなぐシャフト
部とからなる。2. Description of the Related Art As is well known, a tennis racket comprises a face portion on which a gut (string) is stretched, a grip portion grasped by a player, and a shaft portion connecting them.
【０００３】従来のテニスラケットの多くは、繊維強化
合成樹脂、アルミニウム等の軽量な金属で構成されてい
る。なお、チタン又はチタン合金製のテニスラケットも
公知である（特公昭５９−１８１３８号公報）。また、
フェース部のスィートスポットを広げるためにフェース
部に鉛を取り付けることもある。Most conventional tennis rackets are made of lightweight metal such as fiber reinforced synthetic resin and aluminum. A tennis racket made of titanium or titanium alloy is also known (Japanese Patent Publication No. 59-18138). Also,
Lead may be attached to the face part to widen the sweet spot on the face part.
【０００４】[0004]
【発明が解決しようとする課題】本発明者がテニスラケ
ットについてひずみゲージを利用してボールヒット時の
変形挙動を動的応答解析実験したところ、第３図
（Ａ）、（Ｂ）のように、ボール１０の慣性力によって
テニスラケット１１がフェース部幅方向の線分に沿って
中折れする如く変形することが分った。このようなボー
ルヒット時のテニスラケットの変形が大きいと、エネル
ギーロスも多くなり、反発特性がそれだけ低くなる。The present inventor conducted a dynamic response analysis experiment on the deformation behavior of a tennis racket at the time of a ball hit using a strain gauge, and as shown in FIGS. 3 (A) and 3 (B). It was found that the tennis racket 11 was deformed by the inertial force of the ball 10 such that the tennis racket 11 was bent along the line segment in the width direction of the face portion. If the deformation of the tennis racket at the time of such a ball hit is large, the energy loss is also increased, and the repulsion characteristic is reduced accordingly.
【０００５】本発明はボールヒット時のフェース部の変
形を小さくし、テニスラケットの反発性能を高めること
を目的とする。An object of the present invention is to reduce the deformation of the face portion at the time of hitting a ball and to improve the resilience performance of a tennis racket.
【０００６】[0006]
【課題を解決するための手段】本発明のテニスラケット
は、ガットが張られるフェース部を有するテニスラケッ
トにおいて、該フェース部のサイド部分に、該フェース
部の構成母材よりも剛性が高い高剛性材をフェース部の
延在方向に延設したことを特徴とするものである。この
高剛性材は高剛性金属プレートであり、フェース部の外
面に設けられるのが好ましい。The tennis racket of the present invention is a tennis racket having a face portion on which a gut is stretched, and the side rack portion of the face portion has high rigidity higher than that of the constituent base material of the face portion. It is characterized in that the material is extended in the extending direction of the face portion. The high-rigidity material is a high-rigidity metal plate and is preferably provided on the outer surface of the face portion.
【０００７】かかるテニスラケットにあっては、高剛性
材によってフェース部サイド部分の曲げ剛性が高めら
れ、ボールヒット時のフェース部の変形が小さくなり、
テニスラケットの反発性能が向上する。In such a tennis racket, the bending rigidity of the side portion of the face portion is increased by the high-rigidity material, and the deformation of the face portion at the time of a ball hit is reduced,
The resilience performance of the tennis racket is improved.
【０００８】[0008]
【発明の実施の形態】第１図（Ａ）は実施の形態に係る
テニスラケットの正面図、同（Ｂ）は同（Ａ）のＢ部分
の拡大斜視図、同（Ｃ）は同（Ｂ）のＣ−Ｃ線に沿う断
面図である。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS FIG. 1A is a front view of a tennis racket according to an embodiment, FIG. 1B is an enlarged perspective view of a portion B of FIG. 1A, and FIG. 7 is a cross-sectional view taken along line CC of FIG.
【０００９】このテニスラケット１は、フェース部２、
シャフト３及びグリップ４よりなる。フェース部２は略
々長円形であり、そのサイド部分に高剛性材４がフェー
ス部２の延在方向に延設されている。This tennis racket 1 has a face portion 2,
It consists of a shaft 3 and a grip 4. The face portion 2 has a substantially oval shape, and a high-rigidity material 4 is provided on the side portion of the face portion 2 in the extending direction of the face portion 2.
【００１０】この実施の形態にあっては、高剛性材５は
高剛性の金属のプレートよりなり、フェース部２の表裏
両側に設けられている。In this embodiment, the high-rigidity material 5 is made of a high-rigidity metal plate and is provided on both sides of the face portion 2.
【００１１】この実施の形態にあっては、テニスラケッ
トの高剛性材５以外の部分は繊維強化合成樹脂にて構成
されている。フェース部２にあっては、ガット（ストリ
ング）を通すための孔６が設けられている。In this embodiment, the portion of the tennis racket other than the high-rigidity material 5 is made of fiber reinforced synthetic resin. The face portion 2 is provided with a hole 6 for passing a gut (string).
【００１２】このように高剛性材５を設けたことによ
り、ボールヒット時のフェース部２の変形が小さくな
り、高反発性能を得ることができるようになる。By providing the high-rigidity material 5 in this way, the deformation of the face portion 2 at the time of a ball hit becomes small, and high resilience performance can be obtained.
【００１３】高剛性材を金属製とする場合、金属として
はチタン又はチタン合金、ジュラルミン、ステンレス、
超硬スチール等が好適であるが、軽量であることからチ
タン又はチタン合金が最も好ましい。なお、常温におけ
るチタンの弾性率は１．１４２×１０-12 ｄｙｎ／ｃｍ
2 であり、これとほぼ同等又はそれ以上の弾性率の金属
又は合金が好ましい。ちなみに、鉛の常温における弾性
率は０．１５７×１０-12 ｄｙｎ／ｃｍ2 ときわめて低
く、鉛プレートを取り付けても反発性能は向上しない。When the high-rigidity material is made of metal, the metal is titanium or titanium alloy, duralumin, stainless steel,
Carbide steel and the like are preferable, but titanium or titanium alloy is most preferable because it is lightweight. The elastic modulus of titanium at room temperature is 1.142 × 10 −12 dyn / cm.
A metal or alloy having a modulus of elasticity of about 2 or about the same or higher is preferable. Incidentally, the elastic modulus of lead at room temperature is as low as 0.157 × 10 −12 dyn / cm 2, and even if a lead plate is attached, the resilience performance is not improved.
【００１４】このような金属製の高剛性材の場合、その
厚みは０．３〜２．５ｍｍとりわけ０．５〜２ｍｍとく
に０．７〜１．５ｍｍが好ましい。この高剛性材５を設
ける範囲は、フェース部２のテニスラケットの長手方向
の長さをＬとした場合、フェーストップから高剛性材５
の先端（フェーストップ側の端部）までの距離Ｌ1 と、
高剛性材４の後端までの距離Ｌ2 とがそれぞれ次の範囲
となるように定めるのが好ましい。In the case of such a metal high-rigidity material, its thickness is preferably 0.3 to 2.5 mm, particularly 0.5 to 2 mm, and particularly 0.7 to 1.5 mm. When the length of the tennis racket of the face portion 2 in the longitudinal direction is L, the range of the high rigidity material 5 is from the face top to the high rigidity material 5.
The distance L 1 to the tip (end on the face top side) of
It is preferable to set the distance L 2 to the rear end of the high-rigidity material 4 to be in the following ranges.
【００１５】Ｌ×２０％≦Ｌ1 ≦Ｌ×３５％ Ｌ×６５％≦Ｌ2 ≦Ｌ×８０％ とりわけ Ｌ×２５％≦Ｌ1 ≦Ｌ×３０％ Ｌ×７０％≦Ｌ2 ≦Ｌ×７５％ この高剛性材５の存在範囲は、多くのプレーヤーのヒッ
ティングエリアＨの側方部位であり、ボールヒット時の
フェース部２の変形を十分に小さくすることができる。L × 20% ≦ L 1 ≦ L × 35% L × 65% ≦ L 2 ≦ L × 80% Especially L × 25% ≦ L 1 ≦ L × 30% L × 70% ≦ L 2 ≦ L × 75% The existence range of the high-rigidity material 5 is a side part of the hitting area H of many players, and the deformation of the face portion 2 at the time of a ball hit can be sufficiently reduced.
【００１６】なお、この高剛性材５がフェース部２の母
材（この実施の形態では繊維強化合成樹脂）よりも比重
が大きい場合、高剛性材５を設けることによりフェース
部２の慣性モーメントが大きくなり、スィートスポット
が大きくなると共にボールヒット時の面安定性も良くな
る。When the high-rigidity material 5 has a larger specific gravity than the base material of the face portion 2 (fiber-reinforced synthetic resin in this embodiment), the high-rigidity material 5 is provided so that the moment of inertia of the face portion 2 is increased. The larger the sweet spot, the better the surface stability on a ball hit.
【００１７】上記実施の形態では高剛性材５をフェース
部２の表裏に設けているが、第２図（Ａ）、（Ｆ）のよ
うにフェース部２Ａ、２Ｆの内周面と外周面に高剛性材
５Ａ、５Ｆを設けても良い。（この場合内周面と外周面
との一方にのみ高剛性材を設けても良い。）また、第２
図（Ｂ）、（Ｅ）のようにフェース部２Ｂ、２Ｅの全周
に高剛性材５Ｂ、５Ｅを設けても良く、第２図（Ｃ）の
ようにフェース部２Ｃの角縁を図り込むように高剛性材
５Ｃを設けても良い。更に、図示はしないが、高剛性材
を表裏の一方にのみ設けても良い。高剛性材を表裏の一
方のみ、あるいは内・外周面の一方にのみ設けた場合に
は、両方に設ける場合に比べてラケット重量を軽くする
ことができる。In the above embodiment, the high-rigidity material 5 is provided on the front and back surfaces of the face portion 2. However, as shown in FIGS. 2A and 2F, the inner and outer peripheral surfaces of the face portions 2A and 2F are arranged. High rigidity materials 5A and 5F may be provided. (In this case, the high-rigidity material may be provided on only one of the inner peripheral surface and the outer peripheral surface.)
High rigidity materials 5B and 5E may be provided all around the face portions 2B and 2E as shown in FIGS. 2B and 2E, and the corner edges of the face portion 2C are embedded as shown in FIG. 2C. Thus, the high rigidity material 5C may be provided. Further, although not shown, the high-rigidity material may be provided on only one of the front and back sides. When the high-rigidity material is provided on only one of the front and back surfaces, or only on one of the inner and outer peripheral surfaces, the racket weight can be made lighter than when it is provided on both.
【００１８】高剛性材は均一厚みのものに限られず、第
２図（Ｄ）の高剛性材５Ｄのように部分的に厚みが大き
くなっていても良い。The high-rigidity material is not limited to having a uniform thickness, but may be partially thickened as in the high-rigidity material 5D of FIG. 2 (D).
【００１９】フェース部の断面形状も、角形に限らず、
第２図（Ｅ）、（Ｆ）のように各種形状としうる。The sectional shape of the face portion is not limited to the rectangular shape,
It may have various shapes as shown in FIGS. 2 (E) and (F).
【００２０】高剛性材をフェース部の母材部分に固定す
る手段は、特に限定されるものではなく、接着、ねじ留
め、インサート成形など各種手段を採用できる。この高
剛性材と母材との一体性を高めるために、高剛性材の母
材との接触面に細かな凹凸をつけたり、高剛性材を粗面
化処理しても良い。The means for fixing the high-rigidity material to the base material portion of the face portion is not particularly limited, and various means such as adhesion, screwing, insert molding and the like can be adopted. In order to enhance the integrity of the high-rigidity material and the base material, the contact surface of the high-rigidity material with the base material may be finely roughened or the high-rigidity material may be roughened.
【００２１】本発明のラケットフレームは、高剛性材以
外のフレーム母材が繊維強化合成樹脂製とされるのが好
ましい。この補強繊維としては、引張弾性率が１６〜４
０ｔｏｎ／ｍｍ2 とりわけ２４〜３０ｔｏｎ／ｍｍ2 の
ものが好適であり、カーボン繊維、ボロン繊維、アルミ
ナ繊維、超極細鉄線、Ｔｉ−Ｓｉ−Ｃ−Ｏ系繊維（商品
名チラノ繊維）、芳香族ポリアミド繊維、芳香族ポリエ
ステル繊維、超高分子ポリエチレン繊維などを用い得る
が、コストの面からもカーボン繊維が好適である。In the racket frame of the present invention, the frame base material other than the high rigidity material is preferably made of fiber reinforced synthetic resin. This reinforcing fiber has a tensile modulus of 16 to 4
0 ton / mm 2 and especially 24 to 30 ton / mm 2 are suitable, and carbon fiber, boron fiber, alumina fiber, ultrafine iron wire, Ti—Si—C—O fiber (trade name Tyranno fiber), aromatic polyamide Although fibers, aromatic polyester fibers, ultra-high molecular weight polyethylene fibers, etc. may be used, carbon fibers are preferable in terms of cost.
【００２２】合成樹脂としては、エポキシ樹脂、ナイロ
ンなどが好適であるが、強度、耐久性及び価格の点でエ
ポキシ樹脂が好適である。As the synthetic resin, epoxy resin, nylon and the like are preferable, but epoxy resin is preferable in terms of strength, durability and cost.
【００２３】本発明のラケットフレームの母材部分を合
成樹脂にて製造するには、例えば、複数のプリプレグシ
ートを芯材の回りに積層し、これを金型のフレーム形状
としたキャビティ内に配置し加熱するという繊維強化合
成樹脂製ラケットフレームの通常の製造法によれば良
い。In order to manufacture the base material portion of the racket frame of the present invention with synthetic resin, for example, a plurality of prepreg sheets are laminated around a core material, and the prepreg sheets are placed in a cavity having a frame shape of a mold. Then, a conventional method for manufacturing a racket frame made of a fiber-reinforced synthetic resin, in which heating is performed, may be performed.
【００２４】[0024]
【発明の効果】以上の通り、本発明によると、テニスラ
ケットのボールヒット時の変形を小さくすることにより
エネルギーロスを小さくし、反発性を高めることができ
る。なお、フェース部の慣性モーメントを大きくし、面
安定性を高めることも可能である。As described above, according to the present invention, the energy loss can be reduced and the resilience can be enhanced by reducing the deformation of the tennis racket when the ball is hit. It is also possible to increase the surface moment by increasing the moment of inertia of the face portion.
【図１】実施の形態に係るテニスラケットの正面図、フ
ェース部拡大斜視図及びフェース部断面図である。FIG. 1 is a front view of a tennis racket according to an embodiment, an enlarged perspective view of a face portion, and a sectional view of the face portion.
【図２】別の実施の形態に係るテニスラケットのフェー
ス部の断面図である。FIG. 2 is a cross-sectional view of a face portion of a tennis racket according to another embodiment.
【図３】従来のテニスラケットを示す模式的な側面図で
ある。FIG. 3 is a schematic side view showing a conventional tennis racket.
１，１１ テニスラケット ２，２Ａ，２Ｂ，２Ｃ，２Ｄ，２Ｅ，２Ｆ フェース部 ３ シャフト部 ４ グリップ部 ５，５Ａ，５Ｂ，５Ｃ，５Ｄ，５Ｅ，５Ｆ 高剛性材 1,11 Tennis racket 2,2A, 2B, 2C, 2D, 2E, 2F Face part 3 Shaft part 4 Grip part 5,5A, 5B, 5C, 5D, 5E, 5F High rigidity material
Claims (2)
ニスラケットにおいて、該フェース部のサイド部分に、
該フェース部の構成母材よりも剛性が高い高剛性材をフ
ェース部の延在方向に延設したことを特徴とするテニス
ラケット。1. A tennis racket having a face portion on which a gut is stretched, the side portion of the face portion being
A tennis racket characterized in that a high-rigidity material having higher rigidity than the constituent base material of the face portion is extended in the extending direction of the face portion.
性金属プレートであり、フェース部の外面に設けられて
いることを特徴とするテニスラケット。2. The tennis racket according to claim 1, wherein the high-rigidity material is a high-rigidity metal plate and is provided on the outer surface of the face portion.