JPH09157827A - Process roll for carrying cold steel strip excellent in foreign matter sticking resistance - Google Patents
Process roll for carrying cold steel strip excellent in foreign matter sticking resistanceInfo
- Publication number
- JPH09157827A JPH09157827A JP7312522A JP31252295A JPH09157827A JP H09157827 A JPH09157827 A JP H09157827A JP 7312522 A JP7312522 A JP 7312522A JP 31252295 A JP31252295 A JP 31252295A JP H09157827 A JPH09157827 A JP H09157827A
- Authority
- JP
- Japan
- Prior art keywords
- steel strip
- roll
- foreign matter
- carrying
- ceramics
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、耐異物付着性に優
れた冷間鋼帯搬送用プロセスロールに関するものであ
る。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a process roll for transporting cold steel strip which is excellent in foreign matter adhesion resistance.
【０００２】[0002]
【従来の技術】冷間鋼帯の搬送用プロセスロールとして
例えば、デフレクターロール、ピンチロール、ブライド
ルロール、ステアリングロール等においては、鋼帯に張
力を加えて、搬送または形状矯正等を施しつつ搬送する
ことから、搬送用プロセスロールの摩耗によるロール寿
命が短命になることが知られている。また、ロールの耐
久性を向上させるために、ロール表面にセラミックスを
被覆し、その表面を水ガラスにより封孔処理して電気め
っき液がセラミックス膜に浸透することを防止する高耐
食性ロールが特開平３−４４４５５号公報に開示されて
いる。2. Description of the Related Art As process rolls for transporting cold steel strips, such as deflector rolls, pinch rolls, bridle rolls, steering rolls, etc., the steel strips are transported while being subjected to tensioning or straightening. Therefore, it is known that the life of the roll due to the abrasion of the transport process roll becomes short. Further, in order to improve the durability of the roll, there is provided a high corrosion-resistant roll that coats the roll surface with ceramics and seals the surface with water glass to prevent the electroplating solution from penetrating into the ceramic film. It is disclosed in Japanese Patent Publication No. 3-44455.
【０００３】[0003]
【発明が解決しようとする課題】上記のごとく、水ガラ
スによるセラミックス膜表面を封孔処理したロールは、
セラミックス膜への電気めっき液の浸透を阻止する機能
としては十分であるが、鋼帯に高張力を加えて矯正しつ
つ搬送するブライドルロールまたは、鋼帯を方向変換し
つつ搬送するデフレクターロール等の上記搬送用プロセ
スロールにおいては、鋼帯に高張力を加え、しかも高速
搬送（通板）することから亀裂、摩耗等により封孔処理
した水ガラスが脱落し、その脱落した凹部に鉄粉等の異
物が噛み込み付着堆積して凝着する。このようなことか
ら異物によって搬送鋼帯に疵を発生させ品質を劣化させ
る等の課題がある。本発明は、このような課題を有利に
解決するためなされたものであり、セラミックス膜表面
の気孔等凹部を樹脂によって封孔処理し、鋼帯を高速、
高張力搬送においても異物の付着を確実に防止する冷間
鋼帯の搬送用プロセスロールを提供することを目的とす
るものである。As described above, the roll obtained by sealing the surface of the ceramic film with water glass is
Although it is sufficient as a function to prevent the penetration of the electroplating solution into the ceramics film, it does not function as a bridle roll that conveys the steel strip while correcting it by applying high tension, or a deflector roll that conveys the steel strip while changing its direction. In the above-mentioned process roll for conveyance, high tension is applied to the steel strip, and since the high-speed conveyance (passing) is performed, the sealed water glass drops off due to cracking, abrasion, etc. Foreign matter is caught, adheres, accumulates, and adheres. For this reason, there is a problem that a foreign material causes a flaw in the conveyed steel strip to deteriorate the quality. The present invention has been made in order to advantageously solve such a problem, the recesses such as pores on the ceramic film surface is sealed with a resin, the steel strip at high speed,
It is an object of the present invention to provide a process roll for transporting cold steel strips, which reliably prevents foreign matter from adhering even in high tension transport.
【０００４】[0004]
【課題を解決するための手段】本発明の特徴とするとこ
ろは、ロール表面に形成したサーメットまたはセラミッ
クス溶射膜表面の凹部を樹脂により、封孔したことを特
徴とする耐異物付着性に優れた冷間鋼帯搬送用プロセス
ロールである。A feature of the present invention is that a cermet formed on a roll surface or a concave portion on the surface of a ceramic sprayed film is sealed with a resin, which is excellent in foreign matter adhesion resistance. This is a process roll for transporting cold steel strips.
【０００５】[0005]
【発明の実施の形態】搬送用プロセスロール表面に溶射
形成するサーメットとしては、例えばＮｉ、Ｎｉ−Ｃ
ｒ、Ｃｏ、Ｃｒ、Ａｌ、Ｙ、Ｍｏ、Ｗ、Ｔｉ、Ｖ、Ｔａ
系等の金属とＷＣ、ＴｉＣ、ＮｂＣ、Ｃｒ3 Ｃ2 、Ａｌ
2 Ｏ3 、Ｃｒ2 Ｏ3 、ＺｒＯ2 等のセラミックスからな
るサーメット、またセラミックスとしては、上記のごと
きセラミックスを溶射形成することができる。このよう
なサーメットまたはセラミックスは、一般に行われてい
るガスフレーム溶射、プラズマ溶射等により溶射膜を形
成するこができる。BEST MODE FOR CARRYING OUT THE INVENTION Examples of cermets formed by thermal spraying on the surface of a process roll for conveyance include Ni and Ni-C.
r, Co, Cr, Al, Y, Mo, W, Ti, V, Ta
Metals such as WC, TiC, NbC, Cr 3 C 2 , Al
As the cermet made of ceramics such as 2 O 3 , Cr 2 O 3 and ZrO 2 , and as the ceramics, the above ceramics can be formed by thermal spraying. Such a cermet or ceramics can form a sprayed film by gas flame spraying, plasma spraying or the like which is generally performed.
【０００６】このように溶射したサーメットまたはセラ
ミックスは、図３に示すごとくロール１の表面に溶射膜
２として溶射後、その表面を研摩して平坦化することが
あり、この研摩により溶射膜２表面に位置している溶射
膜２中の粒子が剥離して凹部３となり、また気孔が露出
して凹部３となることもあり、これらの凹部３に鉄粉等
の異物が噛み込み堆積する。The cermet or ceramics thus sprayed may be sprayed as a sprayed film 2 on the surface of the roll 1 as shown in FIG. 3, and then the surface may be polished and flattened. By this polishing, the surface of the sprayed film 2 may be polished. Particles in the sprayed film 2 located on the side may be peeled off to form the recesses 3 and the pores may be exposed to form the recesses 3, and foreign matters such as iron powder are caught and deposited in the recesses 3.
【０００７】また本発明者等は、前記のごとき冷間鋼帯
搬送用プロセスロールとして、サーメットまたはセラミ
ックスを図４のようにロール１表面に粗度（凹４、凸
５）を有する溶射膜２として形成することにより、鋼帯
の蛇行を確実に防止することを開発した。即ち、溶射し
た溶射膜表面粗度は、Ｒａ０．５〜１０に形成すること
によって、鋼帯の蛇行を確実に抑制して搬送速度を高速
に維持し、生産性を高めることができ、Ｒａ０．５未満
であると、高速搬送時に鋼帯の蛇行が発生し易く、また
表面粗度がＲａ１０超になると、搬送鋼帯表面に疵が発
生したり、粗度マークが転写することがあり好ましくな
い。このような表面粗度の溶射膜を形成するには、例え
ば溶射後の表面がＲａ０．５〜１０になるように、予め
搬送用プロセスロール表面にショットブラスト等によっ
てダル加工を施した後、上記のごとく溶射膜を形成する
ことにより、確実に表面粗度を調整することができる。As a process roll for transporting the cold steel strip as described above, the inventors of the present invention have used a cermet or a ceramic as shown in FIG. It was developed to prevent the meandering of the steel strip with certainty. That is, when the surface roughness of the sprayed sprayed film is Ra 0.5 to 10, it is possible to reliably suppress the meandering of the steel strip, maintain the conveying speed at a high speed, and improve the productivity. If it is less than 5, meandering of the steel strip is likely to occur during high-speed transportation, and if the surface roughness exceeds Ra10, flaws may occur on the surface of the transported steel strip or the roughness mark may be transferred, which is not preferable. . In order to form a sprayed film having such a surface roughness, for example, after carrying out dull processing by shot blasting or the like on the surface of the process roll for transportation so that the surface after spraying is Ra 0.5 to 10, By forming a sprayed film as described above, the surface roughness can be reliably adjusted.
【０００８】上記のごとき、表面粗度を有する溶射膜厚
としては、５〜２０μで確実に耐摩耗性を向上すること
ができ、５μ未満であると、早期に摩耗が発生して耐久
性が劣ることになり、また２０μ超になるとコスト的に
不利であり、しかも溶射後の表面粗度を確保するため
に、ロール表面の粗度を大きくすることが必要となり好
ましくない。このような溶射膜厚で数年の耐久性（メン
テナンスフリー）を維持することができ、搬送用プロセ
スロールの取替えによる設備停止での生産性の低下を防
止し、かつ、搬送用プロセスロールの耐久性の向上によ
りコストを著しく軽減することができる。このような溶
射膜２においても表面に気孔等の凹部３が露出している
ことがあり、この凹部３に異物が堆積することになる。[0008] As described above, the sprayed coating thickness having a surface roughness of 5 to 20 µm can surely improve the wear resistance, and if it is less than 5 µm, abrasion occurs at an early stage and durability is increased. In addition, if it exceeds 20 μ, it is disadvantageous in terms of cost, and it is not preferable because it is necessary to increase the roughness of the roll surface in order to secure the surface roughness after thermal spraying. With such a sprayed film thickness, it is possible to maintain durability for several years (maintenance-free), prevent productivity deterioration due to equipment stoppage due to replacement of the transport process roll, and durability of the transport process roll. The cost can be remarkably reduced by improving the property. Even in such a sprayed film 2, recesses 3 such as pores may be exposed on the surface, and foreign matter is deposited in the recesses 3.
【０００９】しかして、この凹部を樹脂により封孔処理
するものであり、その樹脂としては、例えばテフロン
系、エポキシ系、シリコン系の樹脂等化学的に安定した
樹脂が好ましく、封孔処理方法としては、塗布、浸漬等
により処理することができる。However, this recess is subjected to a sealing treatment with a resin. As the resin, for example, a chemically stable resin such as Teflon-based, epoxy-based or silicon-based resin is preferable. Can be treated by coating, dipping and the like.
【００１０】[0010]
【実施例】次に、本発明の実施例を挙げる。図１におい
て、搬送用プロセスロール１の表面にサーメットまたは
セラミックスの溶射膜２を形成後、研摩した溶射膜２の
凹部３を樹脂６で封孔する。また図４のごとく、搬送用
プロセスロール１の表面に粗度（凹４、凸５）を有する
サーメットまたはセラミックスの溶射膜２を形成後、発
生した溶射膜２の凹部３に、図２に示すごとく、その表
面の凹部３を樹脂６で封孔するものである。EXAMPLES Next, examples of the present invention will be described. In FIG. 1, after forming a sprayed film 2 of cermet or ceramics on the surface of the transport process roll 1, the recess 3 of the polished sprayed film 2 is sealed with a resin 6. Further, as shown in FIG. 4, after forming a sprayed film 2 of cermet or ceramics having roughness (concave 4, convex 5) on the surface of the process roll 1 for conveyance, the recessed part 3 of the sprayed film 2 generated is shown in FIG. As described above, the concave portion 3 on the surface is sealed with the resin 6.
【００１１】次に、本発明の搬送用プロセスロールを用
いた操業例を挙げる。Next, an operation example using the carrying process roll of the present invention will be described.
【表１】 [Table 1]
【００１２】注１：プロセスロールは、ＤＲ：デフレク
ターロール、ＢＲ：ブライドルロール、ＰＲ：ピンチロ
ール、ＳＲ：スタアリングロール。 注２：溶射膜成分は、Ａ：セラミックス（ＺｒＯ2 ）、
Ｂ：セラミックス（Ａｌ 2 Ｏ3 ）、Ｃ：サーメット（Ａ
ｌ2 Ｏ3 系）、Ｄ：サーメット（ＷＣ系）。 注３：封孔樹脂は、Ａ：テフロン系、Ｂ：エポキシ系、
Ｃ：シリコン系、Ｅ：水ガラス。 注４：鋼帯搬送量は、鋼帯搬送によりロール溶射膜表面
に異物が付着し、取替えるまでの搬送量。 注５：鋼帯蛇行回数は、鋼帯搬送量１０００ｔ毎の鋼帯
蛇行により搬送速度を大幅に低下させた回数。 注６：冷間圧延後の鋼帯熱処理設備で、鋼帯搬送用プロ
セスロールに適用した。Note 1: Process roll is DR: deflection
Tarroll, BR: Bridle roll, PR: Pinchiro
, SR: Staring roll. Note 2: Thermal spray coating components are A: ceramics (ZrOTwo),
B: Ceramics (Al TwoOThree), C: Cermet (A
lTwoOThreeSystem), D: cermet (WC system). Note 3: Sealing resin: A: Teflon type, B: Epoxy type,
C: Silicon type, E: Water glass. Note 4: The amount of steel strip transported is the surface of the roll sprayed film due to steel strip transportation.
The amount of conveyance until foreign matter adheres to and is replaced. Note 5: The number of meandering steel strips is the number of steel strips transported per 1000 tons of steel strip.
The number of times the transport speed has been significantly reduced due to meandering. * 6: Steel strip heat treatment equipment after cold rolling.
Applied to the set roll.
【００１３】[0013]
【発明の効果】本発明の搬送用プロセスロールよれば、
鉄粉等の異物付着を防止してロールの耐久性を向上し、
ロール取替えによる設備の停止が少なくなり、生産性を
高めることができる。また、ロールコストを著しく低下
させることができる。更に、搬送鋼帯の異物による疵発
生も減少して品質、歩留りを向上することができる等の
優れた効果が得られるものである。According to the transporting process roll of the present invention,
Prevents foreign substances such as iron powder from adhering to improve roll durability,
It is possible to improve productivity by reducing the stoppage of equipment due to roll replacement. In addition, the roll cost can be significantly reduced. Further, the occurrence of flaws due to foreign matter on the conveyed steel strip is reduced, and excellent effects such as improvement in quality and yield can be obtained.
【図１】本発明の実施例を示す搬送用プロセスロールの
要部側断面図である。FIG. 1 is a side sectional view of a main part of a carrying process roll showing an embodiment of the present invention.
【図２】本発明の実施例を示す搬送用プロセスロールの
要部側断面図である。FIG. 2 is a side sectional view of a main part of a carrying process roll showing an embodiment of the present invention.
【図３】溶射後の搬送用プロセスロールの要部側断面図
である。FIG. 3 is a side sectional view of a main part of a carrying process roll after thermal spraying.
【図４】溶射後の搬送用プロセスロールの要部側断面図
である。FIG. 4 is a side cross-sectional view of a main part of a transporting process roll after thermal spraying.
１ 搬送用プロセスロール ２ 溶射膜 ３ 凹部 ４ 表面粗度（凹部） ５ 表面粗度（凸部） ６ 樹脂 1 Transport Process Roll 2 Sprayed Film 3 Recess 4 Surface Roughness (Concave) 5 Surface Roughness (Convex) 6 Resin
───────────────────────────────────────────────────── フロントページの続き (72)発明者 津村 康浩 愛知県東海市東海町５−３ 新日本製鐵株 式会社名古屋製鐵所内 ─────────────────────────────────────────────────── ─── Continuation of the front page (72) Inventor Yasuhiro Tsumura 5-3 Tokai-cho, Tokai-shi, Aichi Nippon Steel Stock Company Nagoya Works
Claims (2)
セラミックス溶射膜表面の凹部を樹脂により、封孔した
ことを特徴とする耐異物付着性に優れた冷間鋼帯搬送用
プロセスロール。1. A process roll for transporting cold steel strips, which is excellent in foreign matter adhesion resistance, characterized in that a cermet formed on the roll surface or a recess on the surface of a ceramic sprayed film is sealed with a resin.
０μのサーメットまたはセラミックス溶射膜を形成せし
めたことを特徴とする請求項１に記載の耐異物付着性に
優れた冷間鋼帯搬送用プロセスロール。2. A surface roughness Ra of 0.5 to 10 and a film thickness of 5 to 2.
The process roll for transporting cold steel strip having excellent foreign matter adhesion resistance according to claim 1, wherein a 0 μm cermet or ceramic sprayed film is formed.