JPH0915119A - Method for fixing and measuring surface profile measuring sample of filmy strip - Google Patents
Method for fixing and measuring surface profile measuring sample of filmy stripInfo
- Publication number
- JPH0915119A JPH0915119A JP16250595A JP16250595A JPH0915119A JP H0915119 A JPH0915119 A JP H0915119A JP 16250595 A JP16250595 A JP 16250595A JP 16250595 A JP16250595 A JP 16250595A JP H0915119 A JPH0915119 A JP H0915119A
- Authority
- JP
- Japan
- Prior art keywords
- sample
- shape
- measuring
- film
- slide glass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【0001】[0001]
【産業上の利用分野】本発明は、長尺のフィルム状帯状
物の、特に磁気記録媒体の表面形状の良否を良好に測定
することができるフィルム状帯状物の表面形状測定用サ
ンプルの固定方法及びその測定方法に関するものであ
る。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for fixing a sample for measuring the surface shape of a long film-shaped strip, particularly a film-shaped strip capable of satisfactorily measuring the surface shape of a magnetic recording medium. And the measuring method thereof.
【0002】[0002]
【従来の技術】前記長尺の帯状物としては、ベースフィ
ルムの表面に磁性材を塗布し、または蒸着して磁性層が
形成された磁気記録媒体とかベースフィルムの表面に感
光性乳剤が塗布された写真フィルムなどがある。以下、
図を用いて本発明を説明するが、その説明においては、
ベースフィルムの表面に磁性層が形成された磁気テープ
状の磁気記録媒体を採り挙げ、その表面形状の良否を測
定する場合を例示して説明する。図1はサンプルとして
採取しようとするビデオ用磁気テープを示していて、同
図Aはパンケーキ状に巻かれたビデオ用磁気テープの平
面図、同図Bは同図Aの矢印で示したリール部付近の一
部拡大図、同図Cは同図Bのリール付近から切り取った
ビデオ用磁気テープのサンプルの平面図である。2. Description of the Related Art As the long strip, a magnetic recording medium having a magnetic layer formed by coating or vapor-depositing a magnetic material on the surface of a base film or a photosensitive emulsion is coated on the surface of the base film. Photographic film. Less than,
The present invention will be described with reference to the drawings.
A magnetic tape-shaped magnetic recording medium having a magnetic layer formed on the surface of a base film will be taken as an example to explain the case of measuring the quality of the surface shape. FIG. 1 shows a video magnetic tape to be taken as a sample. FIG. 1A is a plan view of a video magnetic tape wound in a pancake shape, and FIG. B is a reel indicated by an arrow in FIG. FIG. 3C is a plan view of a sample of a magnetic tape for video taken from the vicinity of the reel in FIG.
【0003】従来、磁気記録媒体を製造した場合、その
磁気記録媒体の表面の粗さや形状が良好であるか否かの
一つの検査を行って、品質管理が行われている。例え
ば、図1Aに示したように、ビデオ用磁気テープTがリ
ールRにパンケーキ状に巻かれた場合、同図Bに拡大し
て示したように、ビデオ用磁気テープTのリールRへの
巻き始めに段差が生じ、この段差によりその上層に巻か
れたビデオ用磁気テープTに形状不良Pの押し跡が付
く。Conventionally, when a magnetic recording medium is manufactured, quality control is performed by conducting one inspection as to whether or not the surface roughness or shape of the magnetic recording medium is good. For example, when the video magnetic tape T is wound in a pancake shape on the reel R as shown in FIG. 1A, as shown in the enlarged view of FIG. A step is generated at the beginning of winding, and the step causes a mark of the defective shape P to be attached to the video magnetic tape T wound on the upper layer.
【0004】このような形状不良Pが発生したビデオ用
磁気テープTに映像信号を記録し、これを再生した場合
に、形状不良Pの大きさにより再生画面に筋状の線が流
れ、好ましくない再生画面になる。従って、従来からこ
の押し跡を含む近傍のビデオ用磁気テープTを長さ方向
に切り取ったサンプルSを切り取り、その表面形状を測
定、検査して、どの程度の大きさ(深さ)の形状不良ま
でなら、前記のような不良な再生画面が発生しない許容
範囲に入るかという測定を行っている。図1Cに前記形
状不良PがあるサンプルSを示した。When a video signal is recorded on the video magnetic tape T having such a defective shape P and reproduced, a streak line flows on the reproduction screen depending on the size of the defective shape P, which is not preferable. The playback screen will appear. Therefore, conventionally, a sample S obtained by cutting the video magnetic tape T in the vicinity including the pushing mark in the length direction is cut, and the surface shape is measured and inspected to find out how large (depth) the shape defect is. Up to this point, measurement is performed to determine whether or not the defective reproduction screen as described above falls within the allowable range. FIG. 1C shows a sample S having the shape defect P.
【0005】従来、ビデオ用磁気テープTなどの磁気記
録媒体の表面の粗さや、前記押し跡、折れ、しわ等の形
状を測定する場合には、測定しようとする磁気記録媒体
の一部を前記のように切り取り、サンプルSとし、スラ
イドガラスの表面に固定し、二次元粗度計を用いて、そ
の表面形状を測定している。その測定用サンプルを固定
する固定方法としては次のような方法が採られている。Conventionally, in the case of measuring the surface roughness of a magnetic recording medium such as a magnetic tape T for video and the shape of the above-mentioned imprints, folds, wrinkles, a part of the magnetic recording medium to be measured is referred to above. Sample S is cut out as described above, fixed on the surface of the slide glass, and the surface shape is measured using a two-dimensional roughness meter. The following method is adopted as a fixing method for fixing the measurement sample.
【0006】1.磁気記録媒体の測定しようとする部分
を裁断してサンプルを採り、そのサンプルを平面基板で
あるスライドガラスの表面にシリコンオイルを用いて固
定する方法 2.スライドガラスの表面に水を垂らし、その上にサン
プルを載せ、余分な水分を取り除いた後、そのサンプル
の四辺を接着テープで固定する方法 である。[0006] 1. 1. A method of cutting a portion of a magnetic recording medium to be measured, taking a sample, and fixing the sample on the surface of a slide glass, which is a flat substrate, using silicon oil. This is a method in which water is dripped onto the surface of the slide glass, the sample is placed on it, excess water is removed, and then the four sides of the sample are fixed with adhesive tape.
【0007】[0007]
【発明が解決しようとする課題】ところが、これらシリ
コンオイルや水によるスライドガラスへのサンプルSの
固定方法では、シリコンオイルや水により、サンプルS
がスライドガラスの表面に密着したような状態になり、
前記押し跡、折れ、しわ等の平坦化され、形状不良が不
明確になって、二次元粗度計の触針でなぞっても、その
形状不良を検出することができないという問題を抱えて
いた。However, in the method of fixing the sample S to the slide glass with these silicone oil and water, the sample S is fixed with the silicone oil and water.
Becomes in close contact with the surface of the slide glass,
There was a problem that the imperfections in shape were unclear due to the flattening of the pushing marks, folds, wrinkles, etc., and the imperfections in shape could not be detected even by tracing with the stylus of the two-dimensional roughness meter. .
【0008】本発明は、前記のような欠点を無くするこ
とを課題とするものであって、前記ビデオ用磁気テープ
などの磁気記録媒体の表面の粗さや、前記押し跡、折
れ、しわ等の形状不良が確実に測定できるフィルム状帯
状物の表面形状測定用サンプルの固定方法及びその測定
方法を得ることを目的とするものである。An object of the present invention is to eliminate the above-mentioned drawbacks, and to solve the problems such as the roughness of the surface of a magnetic recording medium such as the above-mentioned magnetic tape for video, the above-mentioned dents, creases and wrinkles. It is an object of the present invention to provide a method for fixing a sample for measuring the surface shape of a film-shaped strip that can reliably measure shape defects, and a method for measuring the same.
【0009】[0009]
【課題を解決するための手段】従って、本発明のフィル
ム状帯状物の表面形状測定用サンプルの固定方法は、磁
気テープの長さ方向の測定方向に、その形状不良を含む
磁気テープを切り出して短片のサンプルを作成し、その
測定方向の一辺のみを平面基板であるスライドガラスの
表面に接着テープで固定して、前記課題を解決した。Therefore, the method for fixing the sample for measuring the surface shape of the film-shaped strip according to the present invention is to cut out a magnetic tape containing a defective shape in the measuring direction in the length direction of the magnetic tape. The above problem was solved by preparing a short sample and fixing only one side in the measurement direction to the surface of a slide glass, which is a flat substrate, with an adhesive tape.
【0010】また、本発明のサンプルの表面形状測定方
法は、磁気テープの長さ方向に、その形状不良を含む磁
気テープを切り出して短片のサンプルを作成し、その測
定方向の一辺のみを平面基板であるスライドガラスの表
面に接着テープで固定し、その固定側からフリー状態の
他端に向けて触針を所定の圧力の下で接触させながら走
査し、前記サンプルの表面形状を測定する方法を採っ
て、前記課題を解決した。Further, according to the method of measuring the surface shape of a sample of the present invention, a short piece of sample is prepared by cutting out a magnetic tape having a defective shape in the lengthwise direction of the magnetic tape, and only one side of the measuring direction is a flat substrate. Is fixed on the surface of the slide glass with an adhesive tape, and scanning is performed from the fixed side toward the other end in the free state while contacting the stylus under a predetermined pressure, and the surface shape of the sample is measured. The problem was solved by taking the above.
【0011】[0011]
【作用】従って、本発明によれば、スライドガラスの表
面上でサンプルの表面に形成された形状不良を殆どその
ままの形状状態で保持でき、その形状を確実かつ忠実に
検出、測定することができる。Therefore, according to the present invention, the shape defect formed on the surface of the sample on the surface of the slide glass can be maintained in almost the same shape state, and the shape can be detected and measured surely and faithfully. .
【0012】[0012]
【実施例】次に、図2乃至図4を参照しながら、本発明
のフィルム状帯状物の表面形状測定用サンプルの固定方
法及びその測定方法を説明する。図2は本発明のフィル
ム状帯状物の表面形状測定用サンプルの固定方法を説明
するための図であって、同図Aはスライドガラスの表面
にサンプルを固定した状態を示した平面図、同図Bは同
図AのA−A線上における断面図であり、図3は本発明
のフィルム状帯状物の表面形状測定方法を用いて、図2
に示した本発明のフィルム状帯状物の表面形状測定用サ
ンプルの固定方法を用いて固定してリールに巻かれた複
数層の磁気テープから採ったサンプルを測定した場合の
グラフであり、そして図4は異なる形状不良のサンプル
を示した平面図である。EXAMPLES Next, with reference to FIGS. 2 to 4, a method for fixing a sample for measuring the surface shape of a film-shaped strip of the present invention and a measuring method therefor will be described. FIG. 2 is a diagram for explaining a method for fixing the sample for measuring the surface shape of the film-shaped strip of the present invention, and FIG. 2A is a plan view showing a state in which the sample is fixed on the surface of the slide glass. 2B is a cross-sectional view taken along the line AA of FIG. 2A, and FIG.
FIG. 4 is a graph of a case where a sample taken from a plurality of layers of magnetic tape which is fixed and wound using the method for fixing the surface shape measuring sample of the film-shaped strip of the present invention shown in FIG. 4 is a plan view showing samples with different shape defects.
【0013】先ず、図1を参照して本発明のフィルム状
帯状物の表面形状測定用サンプルの固定方法を説明す
る。前記のようにビデオ用磁気テープTから前記のよう
な押し跡、折れ、しわ等がある磁気テープ部分を所定の
長さでサンプルSとして切り取り、そのサンプルSをス
ライドガラスGの表面に載置し、サンプルSの一端部分
を接着テープADでスライドガラスGの表面に接着、固
定する。First, with reference to FIG. 1, a method for fixing the sample for measuring the surface shape of the film-shaped strip of the present invention will be described. As described above, the magnetic tape portion having the above-mentioned imprints, folds, and wrinkles is cut out as a sample S from the magnetic tape T for video with a predetermined length, and the sample S is placed on the surface of the slide glass G. , One end of the sample S is adhered and fixed to the surface of the slide glass G with an adhesive tape AD.
【0014】このような固定方法でサンプルSをスライ
ドガラスG上に固定すると、そのサンプルSの形状不良
Pの部分が、図2Bに示したように、スライドガラスG
の表面から浮上した元々の形状不良状態を保ったまま、
保持することができる。When the sample S is fixed on the slide glass G by such a fixing method, the portion of the sample S having the defective shape P is slide glass G as shown in FIG. 2B.
While maintaining the original shape defect state that floated from the surface of
Can be held.
【0015】従って、本発明のフィルム状帯状物の表面
形状測定方法は、二次元粗度計の触針Nを、前記サンプ
ルSの接着テープADによる固定側からフリー状態の他
端に向けて(矢印Xの方向)、所定の軽い圧力の下で接
触させながら走査し、サンプルSの表面形状を測定する
方法を採った。このような方法で触針NをサンプルSの
幅方向の異なる位置に沿って、例えば、両端部と中心部
などを走査、測定する。Therefore, in the method for measuring the surface shape of the film-shaped strip according to the present invention, the stylus N of the two-dimensional roughness meter is directed from the fixed side of the sample S with the adhesive tape AD to the other end in the free state ( In the direction of arrow X), the surface shape of the sample S was measured by scanning while contacting under a predetermined light pressure. With such a method, the stylus N is scanned and measured along different positions in the width direction of the sample S, for example, both end portions and the central portion.
【0016】「押し跡」があるサンプルSの表面を、本
発明の表面形状測定方法を用いて測定し、数値化、グラ
フ化した場合、図3に示したように、その「押し跡」の
形状不良Pをグラフで明確に測定することができる。同
図Aのグラフは、リールRに巻かれた一層目の磁気テー
プのサンプルSの形状変化を示したものであり、同図B
のグラフはリールRに巻かれた二層目の磁気テープのサ
ンプルSの形状変化を示したものであり、そして同図C
のグラフはリールRに巻かれた三層目の磁気テープのサ
ンプルSの形状変化を示したものであって、いずれの場
合のグラフも、形状不良Pが明確に現れている。When the surface of the sample S having a "push mark" is measured using the surface shape measuring method of the present invention and is numerically expressed and graphed, as shown in FIG. The shape defect P can be clearly measured by a graph. The graph of FIG. A shows the shape change of the sample S of the first-layer magnetic tape wound on the reel R, and FIG.
Is a graph showing the shape change of the sample S of the second-layer magnetic tape wound on the reel R, and FIG.
Shows the change in shape of the sample S of the magnetic tape of the third layer wound on the reel R, and in any case, the shape defect P clearly appears.
【0017】本発明のフィルム状帯状物の表面形状測定
方法は、形状不良の発生が、図4Aに示したような、サ
ンプルSaの長手方向に対して斜め方向に生じている形
状不良Paがある場合にも、また、図4Bに示したよう
に、サンプルSbの長手方向の中心線上に生じている形
状不良Sbがある場合にも用いて測定することができ
る。ただし、図4Bに示した形状不良Pがあるサンプル
Sbを測定する場合は、そのサンプルSbの長手方向の
一端を接着テープADでスライドガラスGの表面に接
着、固定するのではなく、サンプルSbの幅方向におけ
るいずれかの一端を接着、固定して、触針Nを形状不良
Pに対して直角な方向に走査させて測定を行う。In the method for measuring the surface shape of a film-shaped strip according to the present invention, there is a shape defect Pa in which a defect in the shape occurs obliquely with respect to the longitudinal direction of the sample Sa as shown in FIG. 4A. In any case, as shown in FIG. 4B, the measurement can be performed also when there is a defective shape Sb occurring on the longitudinal centerline of the sample Sb. However, when measuring the sample Sb having the shape defect P shown in FIG. 4B, one end of the sample Sb in the longitudinal direction is not adhered and fixed to the surface of the slide glass G with the adhesive tape AD, but the sample Sb of the sample Sb is fixed. One end in the width direction is adhered and fixed, and the stylus N is scanned in a direction perpendicular to the shape defect P for measurement.
【0018】[0018]
【発明の効果】以上、説明したように、本発明のフィル
ム状帯状物の表面形状測定用サンプルの固定方法及びそ
の測定方法によれば、形状不良が存在する磁気テープな
どのフィルム状帯状物のサンプルを極めて容易に作成す
ることができ、そしてフィルム状帯状物の表面の形状不
良を二次元粗度計を用いて明確に数値化、グラフ化する
ことができるので、どの程度までの形状不良であれば、
再生画面に乱れが生ぜず、許容できるかを明確に判断す
ることができる。更にまた、フィルム状帯状物の形状不
良の限界見本などを簡単に作成することができる。As described above, according to the method of fixing the sample for measuring the surface shape of the film-shaped strip of the present invention and the measuring method thereof, the film-shaped strip such as a magnetic tape having a defective shape is present. Samples can be created very easily, and the shape defects on the surface of film-shaped strips can be clearly quantified and graphed using a two-dimensional roughness meter. if there is,
There is no disturbance on the playback screen, and it is possible to clearly judge whether it is acceptable. Furthermore, it is possible to easily create a limit sample of the defective shape of the film-shaped strip.
【図1】 サンプルとして採取しようとするビデオ用磁
気テープを示していて、同図Aはパンケーキ状に巻かれ
たビデオ用磁気テープの平面図、同図Bは同図Aの矢印
で示したリール部付近の一部拡大図、同図Cは同図Bの
リール付近から切り取ったビデオ用磁気テープのサンプ
ルの平面図である。FIG. 1 shows a magnetic tape for video to be collected as a sample, FIG. 1A is a plan view of a magnetic tape for video wound in a pancake shape, and FIG. 1B is an arrow shown in FIG. FIG. 7C is a partially enlarged view of the vicinity of the reel portion, and FIG. 10C is a plan view of a sample of the magnetic tape for video taken from the vicinity of the reel of FIG.
【図2】 本発明のフィルム状帯状物の表面形状測定用
サンプルの固定方法を説明するための図であって、同図
Aはスライドガラスの表面にサンプルを固定した状態を
示した平面図、同図Bは同図AのA−A線上における断
面図である。FIG. 2 is a view for explaining a method for fixing the sample for measuring the surface shape of the film-shaped strip of the present invention, FIG. 2A is a plan view showing a state where the sample is fixed on the surface of the slide glass, FIG. 2B is a sectional view taken along the line AA of FIG.
【図3】 本発明のフィルム状帯状物の表面形状測定方
法を用いて、図2に示した本発明のフィルム状帯状物の
表面形状測定用サンプルの固定方法を用いて固定してリ
ールに巻かれた複数層の磁気テープから採ったサンプル
を測定した場合のグラフである。FIG. 3 is a view showing a method for measuring the surface shape of a film-shaped strip according to the present invention, and a method for fixing the surface shape measurement sample for a film-shaped strip according to the present invention shown in FIG. It is a graph at the time of measuring the sample taken from the magnetic tape of several layers burned.
【図4】 異なる形状不良のサンプルを示した平面図で
ある。FIG. 4 is a plan view showing samples having different shape defects.
AD 接着テープ G スライドガラス N 触針 P 形状不良 R リール S サンプル Sa サンプル Sb サンプル T ビデオ用磁気テープ AD Adhesive tape G Slide glass N Stylus P Bad shape R Reel S Sample Sa sample Sb sample T Video magnetic tape
Claims (2)
ルム状帯状物を切り出して短片のサンプルを作成し、そ
の測定方向の一辺のみを平面基板の表面に接着テープで
固定したことを特徴とするフィルム状帯状物の表面形状
測定用サンプルの固定方法。1. A short strip sample is produced by cutting out the film-shaped strip in the measuring direction of the film-shaped strip, and only one side of the measuring direction is fixed to the surface of the flat substrate with an adhesive tape. A method for fixing a sample for measuring the surface shape of a film-shaped strip.
ルム状帯状物を切り出して短片のサンプルを作成し、そ
の測定方向の一辺のみを平面基板の表面に接着テープで
固定し、該固定側からフリー状態の他端に向けて触針を
所定の圧力の下で接触させながら走査し、前記フィルム
状帯状物のサンプルの表面形状を測定することを特徴と
するフィルム状帯状物の表面形状測定方法。2. A short piece sample is prepared by cutting out the film-shaped strip in the measuring direction of the film-shaped strip, and only one side in the measuring direction is fixed to the surface of a flat substrate with an adhesive tape, and the fixed side From the free state to the other end of the free state, scanning while contacting the stylus under a predetermined pressure, to measure the surface shape of the sample of the film belt Method.