JPH09110663A - Gel capsule blended with oil soluble component, its production and composition for oral cavity - Google Patents
Gel capsule blended with oil soluble component, its production and composition for oral cavityInfo
- Publication number
- JPH09110663A JPH09110663A JP29757395A JP29757395A JPH09110663A JP H09110663 A JPH09110663 A JP H09110663A JP 29757395 A JP29757395 A JP 29757395A JP 29757395 A JP29757395 A JP 29757395A JP H09110663 A JPH09110663 A JP H09110663A
- Authority
- JP
- Japan
- Prior art keywords
- soluble component
- oil
- gel capsule
- oil soluble
- soluble
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、油溶性成分が安定
に配合されたゲルカプセル及びこの油溶性成分配合ゲル
カプセルの製造方法並びにこのゲルカプセルを配合して
なる口腔用組成物に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a gel capsule containing an oil-soluble component stably mixed therein, a method for producing the oil-soluble component-containing gel capsule, and an oral composition containing the gel capsule.
【０００２】[0002]
【従来の技術及び発明が解決しようとする課題】従来、
芯材にアルギン酸塩水溶液、凝固剤に塩化カルシウム水
溶液を用いてゲルカプセルを製造することはよく知られ
ており、このようなゲルカプセルに水溶性薬剤を封入す
ることは容易に行われる。しかし、脂溶性薬剤は、芯材
水溶液に分散しないので、ゲルカプセルに封入すること
は困難である。この場合、脂溶性薬剤の水溶性を高める
ため、芯材水溶液に界面活性剤を添加して脂溶性薬剤を
乳化又は可溶化することが知られているが、界面活性剤
を添加すると芯材のゲル化能に影響し、良好なゲルカプ
セルが調製できないものであった。2. Description of the Related Art
It is well known to manufacture a gel capsule using an alginate aqueous solution as a core material and a calcium chloride aqueous solution as a coagulant, and encapsulating a water-soluble drug in such a gel capsule is easily performed. However, since the fat-soluble drug is not dispersed in the aqueous core material solution, it is difficult to encapsulate it in a gel capsule. In this case, in order to increase the water solubility of the fat-soluble drug, it is known that a surfactant is added to the aqueous core material solution to emulsify or solubilize the fat-soluble drug. The gelling ability was affected, and good gel capsules could not be prepared.
【０００３】ところで、歯磨等の口腔用組成物には、香
料や各種有効成分（薬剤）が配合される。これら香料及
び有効成分の多くは油溶性であるが、従来より口腔用組
成物においては、香料や有効成分の徐放性が望まれてい
ると共に、特に配合安定性、保存安定性が望まれてい
た。By the way, a fragrance and various active ingredients (medicines) are blended with oral compositions such as toothpaste. Although many of these fragrances and active ingredients are oil-soluble, conventionally, in oral compositions, sustained release of fragrances and active ingredients is desired, and especially formulation stability and storage stability are desired. It was
【０００４】本発明は上記事情に鑑みなされたもので、
油溶性成分が安定に保持された油溶性成分配合ゲルカプ
セル及びその製造方法並びにこのゲルカプセルが配合さ
れた口腔用組成物を提供することを目的とする。[0004] The present invention has been made in view of the above circumstances,
An object of the present invention is to provide an oil-soluble component-containing gel capsule in which an oil-soluble component is stably retained, a method for producing the same, and an oral composition containing the gel capsule.
【０００５】[0005]
【課題を解決するための手段及び発明の実施の形態】本
発明者は上記目的を達成するため鋭意検討を行った結
果、無機又は有機粉粒状担体に油溶性成分を含浸又は付
着させ、これをアルギン酸塩、硫酸化セルロース、カル
ボキシメチルセルロース、キサンタンガム、ジェランガ
ム及びヒアルロン酸から選ばれる水溶性高分子物質の水
溶液に添加、分散して芯液を調製し、これをアルカリ金
属又はアルカリ土類金属の水溶性塩を含む凝固液に滴下
することにより、油溶性成分を簡単かつ確実にゲルカプ
セル中に封入し得ると共に、このゲルカプセルは油溶性
成分が安定に保持され、油溶性の香料や有効成分を油溶
性成分としたゲルカプセルを歯磨等の口腔用組成物に配
合した場合、香料や有効成分がゲルカプセル中に安定に
保持されているので、口腔用組成物の他成分と混合した
場合や口腔用組成物を長期間保存した場合などに失活し
難く、配合安定性、保存安定性に優れていると共に、徐
放性を与えることができることを知見し、本発明をなす
に至った。Means for Solving the Problems and Modes for Carrying Out the Invention As a result of intensive studies for achieving the above-mentioned object, the present inventor impregnated or adhered an oil-soluble component to an inorganic or organic powdery granular carrier, Add and disperse an aqueous solution of a water-soluble polymer selected from alginate, sulfated cellulose, carboxymethyl cellulose, xanthan gum, gellan gum and hyaluronic acid to prepare a core liquid, which is soluble in alkali metal or alkaline earth metal. The oil-soluble component can be easily and surely encapsulated in the gel capsule by dropping it into the coagulating liquid containing salt, and the gel-capsule retains the oil-soluble component in a stable manner. When a gel capsule that is a soluble component is mixed with an oral composition such as toothpaste, the fragrance and the active ingredient are stably retained in the gel capsule. It is difficult to deactivate when mixed with other components of the oral composition or when the oral composition is stored for a long period of time, and it is possible to give sustained release while being excellent in formulation stability and storage stability. That is, the present invention has been completed.
【０００６】従って、本発明は、（１）油溶性成分が含
浸又は付着した無機又は有機粉粒状担体を芯材とし、こ
れをアルギン酸塩、硫酸化セルロース、カルボキシメチ
ルセルロース、キサンタンガム、ジェランガム及びヒア
ルロン酸から選ばれる水溶性高分子物質のゲル膜で被覆
してなることを特徴とする油溶性成分配合ゲルカプセ
ル、（２）油溶性成分を無機又は有機粉粒状担体に含浸
又は付着させた後、これをアルギン酸塩、硫酸化セルロ
ース、カルボキシメチルセルロース、キサンタンガム、
ジェランガム及びヒアルロン酸から選ばれる水溶性高分
子物質の水溶液に添加、分散して芯液を調製し、次いで
これをアルカリ金属又はアルカリ土類金属の水溶性塩を
含有する凝固液に滴下することを特徴とする上記油溶性
成分配合ゲルカプセルの製造方法、及び、（３）上記油
溶性成分配合ゲルカプセルを配合してなる口腔用組成物
を提供する。Therefore, according to the present invention, (1) an inorganic or organic powdery or granular carrier impregnated with or adhering an oil-soluble component is used as a core material, which is prepared from alginate, sulfated cellulose, carboxymethyl cellulose, xanthan gum, gellan gum and hyaluronic acid. An oil-soluble component-containing gel capsule characterized by being coated with a gel film of a selected water-soluble polymer substance, (2) after impregnating or adhering the oil-soluble component onto an inorganic or organic powdery granular carrier, Alginate, sulfated cellulose, carboxymethyl cellulose, xanthan gum,
It is added to an aqueous solution of a water-soluble polymer substance selected from gellan gum and hyaluronic acid to prepare a core liquid, which is then added dropwise to a coagulating liquid containing a water-soluble salt of an alkali metal or an alkaline earth metal. A method for producing the above-mentioned gel capsule containing the oil-soluble component, and (3) a composition for oral cavity obtained by blending the gel capsule containing the oil-soluble component.
【０００７】以下、本発明につき更に詳述すると、本発
明のゲルカプセルの製造に用いる油溶性成分は特に制限
されないが、このゲルカプセルを口腔用組成物に用いる
場合は、ｌ−メントール、スペアミント油、ペパーミン
ト油等の油溶性香料、ビタミンＡ、ビタミンＥ、ビオゾ
ール、トリクロサン等のビタミン類、殺菌剤、その他の
油溶性有効成分（薬効成分）などが挙げられる。The present invention will be described in more detail below. The oil-soluble component used for producing the gel capsule of the present invention is not particularly limited, but when this gel capsule is used in an oral composition, l-menthol and spearmint oil are used. , Oil-soluble flavors such as peppermint oil, vitamins such as vitamin A, vitamin E, biosol and triclosan, fungicides, and other oil-soluble active ingredients (medicinal ingredients).
【０００８】本発明においては、これらの油溶性成分を
無機又は有機粉粒状担体に含浸又は付着させて用いる
が、かかる担体としては、水溶液中で網目構造を形成
し、懸濁安定性、乳化安定性が良好なものが好ましい。In the present invention, these oil-soluble components are used by impregnating or adhering to an inorganic or organic powdery or granular carrier. As such a carrier, a network structure is formed in an aqueous solution, and suspension stability and emulsion stability are obtained. Those having good properties are preferable.
【０００９】具体的に無機担体としては、シリカ等のケ
イ酸系、カオリナイト、ベントナイト、セリサイト等の
アルミノケイ酸系、ベリクレース、マグネサイト、タル
ク等のマグネシウム系、炭酸カルシウム、石膏等の石灰
質系、酸化バリウム、酸化錫、酸化チタン、酸化マグネ
シウム、硫酸バリウム等のピグメント系担体を使用する
ことができ、また、有機担体としては、商品名「アビセ
ル」、「セルファイア」（共に旭化成工業製）等の結晶
セルロース、ナイロン粉末、ポリエチレン粉末、ポリプ
ロピレン粉末、ポリビニル塩化粉末、ポリスチレン粉末
等の合成品、部分アルファー化デンプン、クルミ粉末、
アプリコット粉末、ミルクパウダー等の天然品を使用す
ることができる。なお、これら担体の平均粒径は、５〜
２０μｍ、特に１０〜１５μｍとすることが好ましい。Specific examples of the inorganic carrier include silicic acid type such as silica, aluminosilicate type such as kaolinite, bentonite and sericite, magnesium type such as beliclase, magnesite and talc, and calcareous type such as calcium carbonate and gypsum. , Pigment-based carriers such as barium oxide, tin oxide, titanium oxide, magnesium oxide, and barium sulfate can be used, and as organic carriers, trade names “Avicel” and “Cellfire” (both manufactured by Asahi Kasei Kogyo) Synthetic products such as crystalline cellulose, nylon powder, polyethylene powder, polypropylene powder, polyvinyl chloride powder, polystyrene powder, partially pregelatinized starch, walnut powder, etc.
Natural products such as apricot powder and milk powder can be used. The average particle size of these carriers is 5 to
The thickness is preferably 20 μm, particularly preferably 10 to 15 μm.
【００１０】これらの担体に対する油溶性成分の含浸又
は付着量は適宜選定されるが、通常担体１００重量部に
対して１〜２００重量部、特に１〜１００重量部であ
る。The amount of the oil-soluble component impregnated or adhered to these carriers is appropriately selected, but is usually 1 to 200 parts by weight, particularly 1 to 100 parts by weight, relative to 100 parts by weight of the carrier.
【００１１】本発明のゲルカプセルは、上記油溶性成分
を付着又は含浸させた担体を、アルギン酸ナトリウム等
のアルギン酸塩、硫酸化セルロース、カルボキシメチル
セルロース、キサンタンガム、ジェランガム、ヒアルロ
ン酸から選ばれる１種又は２種以上の水溶性高分子物質
を含有する水溶液に添加、分散し、芯液を得た後、これ
をアルカリ金属又はアルカリ土類金属の水溶性塩を含む
凝固液に滴下する。In the gel capsule of the present invention, the carrier having the oil-soluble component adhered or impregnated therein is selected from one or two selected from alginates such as sodium alginate, sulfated cellulose, carboxymethyl cellulose, xanthan gum, gellan gum and hyaluronic acid. After adding and dispersing to an aqueous solution containing one or more water-soluble polymer substances to obtain a core liquid, this is added dropwise to a coagulating liquid containing a water-soluble salt of an alkali metal or an alkaline earth metal.
【００１２】ここで、上記水溶性高分子物質の水溶液の
濃度は、０．１〜５％（重量％、以下同じ）、特に０．
１〜３％とすることが好ましい。また、この水溶性高分
子物質水溶液に対する上記油溶性成分の含浸又は付着担
体の添加量は、１〜７０％、好ましくは１〜２５％であ
る。Here, the concentration of the aqueous solution of the water-soluble polymer substance is 0.1 to 5% (% by weight, the same applies hereinafter), particularly 0.
It is preferably set to 1 to 3%. The amount of the oil-soluble component impregnated or adhered carrier added to the aqueous solution of the water-soluble polymer is 1 to 70%, preferably 1 to 25%.
【００１３】一方、上記凝固液を得るためのアルカリ金
属又はアルカリ土類金属の水溶性塩は適宜選定される
が、上記水溶性高分子物質の種類に応じて選択使用する
ことが好ましい。例えば、使用する高分子物質がアルギ
ン酸ナトリウムの場合にはカルシウム系、硫酸化セルロ
ースにはナトリウム系、カルボキシメチルセルロースに
はリチウム、ナトリウム、カリウム、セシウム、マグネ
シウム、カルシウム系、キサンタンガムにはナトリウム
系、ジェランガムにはナトリウム、カルシウム、マグネ
シウム系、ヒアルロン酸にはナトリウム系の凝固剤を使
用することができる。なお、これらアルカリ金属又はア
ルカリ土類金属の水溶性塩の水溶液（凝固液）濃度は
０．１〜２５％、特に１〜２０％とすることが好まし
い。On the other hand, a water-soluble salt of an alkali metal or an alkaline earth metal for obtaining the coagulating liquid is appropriately selected, but it is preferably selected and used according to the kind of the water-soluble polymer substance. For example, when the polymeric substance used is sodium alginate, it is calcium-based, sulfated cellulose is sodium-based, carboxymethylcellulose is lithium, sodium, potassium, cesium, magnesium, calcium-based, xanthan gum is sodium-based, and gellan gum is A sodium-based coagulant can be used for sodium, calcium, magnesium and hyaluronic acid. The concentration of the aqueous solution (coagulating liquid) of these water-soluble salts of alkali metals or alkaline earth metals is preferably 0.1 to 25%, particularly 1 to 20%.
【００１４】上記のように凝固液中に上記芯液を滴下す
ることにより、芯液中の水溶性高分子物質がゲル化し、
上記芯材（油溶性成分が含浸又は付着した担体）をこの
水溶性高分子物質のゲル膜が被覆するもので、これによ
って本発明のゲルカプセルが得られるが、本発明のゲル
カプセルは油溶性成分がカプセル中に安定に保持されて
いると共に、徐放性を有するので、種々の用途に使用さ
れ、特に口腔用組成物、例えば歯磨類、洗口剤などや、
トローチ、チューインガム、更に各種化粧料などに配合
することができ、とりわけ洗口剤等の水性製剤に好適に
用いられる。なお、本発明のゲルカプセルが配合される
口腔用組成物等の製剤の処方は公知の処方とすることが
できる。By dropping the above core liquid into the coagulating liquid as described above, the water-soluble polymer substance in the core liquid gels,
The above-mentioned core material (carrier impregnated with or adhered to an oil-soluble component) is coated with a gel film of this water-soluble polymer substance, whereby the gel capsule of the present invention is obtained. The gel capsule of the present invention is oil-soluble. While the components are stably retained in the capsule and have sustained release properties, they are used in various applications, especially oral compositions, such as dentifrice, mouthwash, and the like,
It can be blended in troches, chewing gum, and various cosmetics, and is particularly preferably used for an aqueous preparation such as a mouthwash. It should be noted that the formulation of the preparation such as the oral composition containing the gel capsule of the present invention can be a known formulation.
【００１５】[0015]
【発明の効果】本発明の油溶性成分を配合したゲルカプ
セルは、油溶性成分を分散性良く、安定に保持したゲル
カプセルであり、各種口腔用組成物に良好に配合されて
良好な油溶性成分徐放効果を付与することができると共
に、かかる油溶性成分を安定配合し得、かつ優れた保存
安定性を与える。また、本発明のゲルカプセルの製造方
法によれば、上述した油溶性成分を保持した優れたゲル
カプセルを簡単かつ確実に得ることができる。EFFECT OF THE INVENTION The gel capsule containing the oil-soluble component of the present invention is a gel capsule in which the oil-soluble component has good dispersibility and is stably retained, and is well blended in various oral compositions and has good oil solubility. It is possible to impart a sustained-release effect to the components, to stably mix such oil-soluble components, and to provide excellent storage stability. Further, according to the method for producing a gel capsule of the present invention, it is possible to easily and reliably obtain the excellent gel capsule holding the oil-soluble component described above.
【００１６】[0016]
【実施例】以下、実施例及び配合例を示し、本発明を具
体的に説明するが、本発明は下記実施例に制限されるも
のでない。EXAMPLES The present invention will be specifically described below with reference to examples and formulation examples, but the present invention is not limited to the following examples.
【００１７】［実施例１］ｌ−メントール１０ｇ、結晶
セルロース粉末１０ｇを共に乳鉢に入れ、良く混合した
後、１％アルギン酸ソーダ水溶液８０ｇ中に添加し、良
く撹拌した。この溶液を２０％塩化カルシウム水溶液１
００ｇに滴下し、凝固させて、瀘過、水洗後、ゲルカプ
セルを得、調製したゲルカプセルを水中に入れて保存し
た。Example 1 10 g of l-menthol and 10 g of crystalline cellulose powder were placed in a mortar, mixed well, then added to 80 g of a 1% sodium alginate aqueous solution, and stirred well. This solution is 20% calcium chloride aqueous solution 1
It was added dropwise to 00 g, solidified, filtered and washed with water to obtain a gel capsule, and the prepared gel capsule was put in water and stored.
【００１８】［実施例２］結晶セルロース粉末の代わり
にリン酸カルシウム１０ｇを使用した以外は、実施例１
と同様の方法でゲルカプセルを調製した。Example 2 Example 1 except that 10 g of calcium phosphate was used instead of crystalline cellulose powder.
A gel capsule was prepared in the same manner as in.
【００１９】上記ゲルカプセルは、ｌ−メントールの放
出量が初期にかなり多く、時間の経過と共に急激に低下
するようなことがなく、経時的にほぼ同じで、良好な徐
放効果を有しているものであり、これは担体（結晶セル
ロース粉末、リン酸カルシウム）に油溶性成分（ｌ−メ
ントール）が均一に担持され、それを水溶性高分子物質
（アルギン酸ソーダ）のゲル膜が被覆しているためと考
えられた。The above-mentioned gel capsule has a considerably large amount of l-menthol released in the beginning, does not decrease sharply with the passage of time, is almost the same over time, and has a good sustained release effect. This is because the oil-soluble component (l-menthol) is uniformly supported on the carrier (crystalline cellulose powder, calcium phosphate), and the gel film of the water-soluble polymer (sodium alginate) coats it. It was considered.
【００２０】次に、ゲルカプセルの配合例を示す。 ［配合例１］洗口剤 エタノール １０．０ ％ グリセリン（８５％） １０．０ プロピレングリコール ２．０ クエン酸 ３．０ クエン酸ナトリウム ６．０ キシリット ３．０ ポリ（オキシエチレン）（２０）セチルエーテル ２．０ フッ化ナトリウム ０．２ サッカリンナトリウム ０．１ 安息香酸ナトリウム ０．２ 香料 ０．７ ゲルカプセル（実施例１） ２．０ 色素 微量 精製水 バランス 計 １００．０Next, a formulation example of the gel capsule will be shown. [Formulation Example 1] Mouthwash Ethanol 10.0% Glycerin (85%) 10.0 Propylene glycol 2.0 Citric acid 3.0 Sodium citrate 6.0 Xylit 3.0 Poly (oxyethylene) (20) cetyl Ether 2.0 Sodium Fluoride 0.2 Sodium Saccharin 0.1 Sodium Benzoate 0.2 Perfume 0.7 Gel Capsule (Example 1) 2.0 Pigment Micro Purified Water Balance Meter 100.0
【００２１】 ［配合例２］洗口剤 エタノール １．０ ％ ソルビット（６０％） ７．５ グリセリン（８５％） ７．５ プロピレングリコール １．５ カルボキシメチルセルロース ０．４ ポリソルベート（８０） １．５ クエン酸 ２．５ クエン酸ナトリウム ５．０ グリチルリチン酸ジカリウム ０．０５ トラネキサム酸 ０．０５ ステビアエキス ０．１ ゲルカプセル（実施例２） ２．０ 香料 ０．３ 精製水 バランス 計 １００．０[Formulation Example 2] Mouthwash Ethanol 1.0% Solbit (60%) 7.5 Glycerin (85%) 7.5 Propylene glycol 1.5 Carboxymethylcellulose 0.4 Polysorbate (80) 1.5 Quent Acid 2.5 Sodium citrate 5.0 Dipotassium glycyrrhizinate 0.05 Tranexamic acid 0.05 Stevia extract 0.1 Gel capsule (Example 2) 2.0 Perfume 0.3 Purified water Balance meter 100.0
【００２２】 ［配合例３］洗口剤 エタノール １０．０ ％ グリセリン（８５％） １０．０ プロピレングリコール ２．０ アルギン酸ナトリウム ０．２ ヒドロキシエチルセルロース ０．３ リン酸１水素ナトリウム ３．０ リン酸２水素ナトリウム ６．０ ポリ（オキシエチレン）（２０）セチルエーテル ２．０ 炭酸水素ナトリウム ３．０ サッカリンナトリウム ０．１ 安息香酸ナトリウム ０．２ ゲルカプセル（実施例１） ２．０ 色素 微量 精製水 バランス 計 １００．０[Formulation Example 3] Mouthwash Ethanol 10.0% Glycerin (85%) 10.0 Propylene glycol 2.0 Sodium alginate 0.2 Hydroxyethylcellulose 0.3 Phosphorus monohydrogen sodium 3.0 Phosphoric acid 2 Sodium hydrogen 6.0 Poly (oxyethylene) (20) cetyl ether 2.0 Sodium hydrogencarbonate 3.0 Sodium saccharin 0.1 Sodium benzoate 0.2 Gel capsule (Example 1) 2.0 Dye micro- purified water balance meter 100.0
【００２３】 ［配合例４］洗口剤 エタノール １．０ ％ ソルビット（６０％） ７．５ グリセリン（８５％） ７．５ プロピレングリコール １．５ アルギン酸ナトリウム ０．４ ポリソルベート（８０） １．５ クエン酸 ２．５ リン酸２水素ナトリウム ２．５ トリクロサン ０．１ ステビアエキス ０．１ ゲルカプセル（実施例１） ２．０ 香料 ０．３ 精製水 バランス 計 １００．０[Formulation Example 4] Mouthwash 1.0% Ethanol 1.0% Solbit (60%) 7.5 Glycerin (85%) 7.5 Propylene glycol 1.5 Sodium alginate 0.4 Polysorbate (80) 1.5 Quent Acid 2.5 Sodium dihydrogen phosphate 2.5 Triclosan 0.1 Stevia extract 0.1 Gel capsule (Example 1) 2.0 Perfume 0.3 Purified water Balance meter 100.0
【００２４】 ［配合例５］洗口剤 エタノール １０．０ ％ ソルビット（６０％） １０．０ プロピレングリコール １．５ カルボキシメチルセルロース ０．４ クエン酸 ２．５ クエン酸ナトリウム ５．０ 塩化セチルピリジニウム ０．０５ ステビアエキス ０．１ ゲルカプセル（実施例１） ２．０ 香料 ０．３ 精製水 バランス 計 １００．０[Formulation Example 5] Mouthwash Ethanol 10.0% Solbit (60%) 10.0 Propylene glycol 1.5 Carboxymethylcellulose 0.4 Citric acid 2.5 Sodium citrate 5.0 Cetylpyridinium chloride 0. 05 Stevia extract 0.1 Gel capsule (Example 1) 2.0 Fragrance 0.3 Purified water Balance meter 100.0
【００２５】 ［配合例６］液状歯磨 沈降性シリカ ２０．０ ％ キサンタンガム ０．２５ ポリアクリル酸ナトリウム ０．２５ プロピレングリコール ２．０ ソルビット ３０．０ グリセリン １０．０ 塩化ベンゼトニウム ０．０５ ポリ（オキシエチレン）（１０）オレイルエーテル １．０ サッカリンナトリウム ０．１ ゲルカプセル（実施例１） ２．０ 香料 １．０ 精製水 バランス 計 １００．０[Formulation Example 6] Liquid toothpaste Precipitable silica 20.0% Xanthan gum 0.25 Sodium polyacrylate 0.25 Propylene glycol 2.0 Sorbit 30.0 Glycerin 10.0 Benzethonium chloride 0.05 Poly (oxyethylene) ) (10) Oleyl ether 1.0 Sodium saccharin 0.1 Gel capsule (Example 1) 2.0 Fragrance 1.0 Purified water Balance meter 100.0
【００２６】 ［配合例７］液状歯磨 炭酸水素ナトリウム ０．３ ％ 沈降性シリカ ２０．０ キサンタンガム ０．１５ ポリアクリル酸ナトリウム ０．２ プロピレングリコール ２．０ グリセリン ２０．０ ソルビット ５０．０ サッカリン ０．１ ラウリン酸デカグリセリル ０．５ ラウリル硫酸ナトリウム １．２ Ｎ−ミリストイルサルコシンナトリウム ０．１ ゲルカプセル（実施例１） ２．０ 香料 １．０ 精製水 バランス 計 １００．０[Formulation Example 7] Liquid toothpaste Sodium hydrogen carbonate 0.3% Precipitable silica 20.0 Xanthan gum 0.15 Sodium polyacrylate 0.2 Propylene glycol 2.0 Glycerin 20.0 Sorbit 50.0 Saccharin 0. 1 Decaglyceryl laurate 0.5 Sodium lauryl sulfate 1.2 N-myristoyl sarcosine sodium 0.1 Gel capsule (Example 1) 2.0 Perfume 1.0 Purified water Balance meter 100.0
【００２７】 ［配合例８］トローチ アラビアゴム ６．０ ％ ブドウ糖 ７２．０ モノフルオロリン酸ナトリウム ０．０５ リン酸１カリウム ０．１ リン酸２カリウム ０．２ ゲルカプセル（実施例１） ２．０ 香料 １．０ 精製水 バランス 計 １００．０[Formulation Example 8] Lozenge gum arabic 6.0% Glucose 72.0 Sodium monofluorophosphate 0.05 1 potassium phosphate 0.1 dipotassium phosphate 0.2 gel capsule (Example 1) 2. 0 Fragrance 1.0 Purified water Balance meter 100.0
【００２８】 ［配合例９］チューインガム ガムベース ２０．０ ％ 炭酸カルシウム ２．０ 水アメ １５．０ 粉糖 ５８．０ リン酸１カリウム ０．４ リン酸２ナトリウム ０．５ ゲルカプセル（実施例１） ２．０ 香料 １．０ 精製水 バランス 計 １００．０[Formulation Example 9] Chewing gum Gum base 20.0% Calcium carbonate 2.0 Water candy 15.0 Powdered sugar 58.0 Phosphorus 1 potassium 0.4 Disodium phosphate 0.5 Gel capsule (Example 1) 2.0 Fragrance 1.0 Purified water Balance meter 100.0
Claims (3)
有機粉粒状担体を芯材とし、これをアルギン酸塩、硫酸
化セルロース、カルボキシメチルセルロース、キサンタ
ンガム、ジェランガム及びヒアルロン酸から選ばれる水
溶性高分子物質のゲル膜で被覆してなることを特徴とす
る油溶性成分配合ゲルカプセル。1. A water-soluble polymer substance selected from alginate, sulfated cellulose, carboxymethyl cellulose, xanthan gum, gellan gum and hyaluronic acid, which is made of an inorganic or organic powdery carrier impregnated with or adhered with an oil-soluble component. A gel capsule containing an oil-soluble component, which is coated with the gel film of.
含浸又は付着させた後、これをアルギン酸塩、硫酸化セ
ルロース、カルボキシメチルセルロース、キサンタンガ
ム、ジェランガム及びヒアルロン酸から選ばれる水溶性
高分子物質の水溶液に添加、分散して芯液を調製し、次
いでこれをアルカリ金属又はアルカリ土類金属の水溶性
塩を含有する凝固液に滴下することを特徴とする請求項
１記載の油溶性成分配合ゲルカプセルの製造方法。2. After impregnating or adhering an oil-soluble component on an inorganic or organic powdery or granular carrier, it is added with a water-soluble polymer substance selected from alginate, sulfated cellulose, carboxymethyl cellulose, xanthan gum, gellan gum and hyaluronic acid. 2. A gel containing an oil-soluble component according to claim 1, which is added to and dispersed in an aqueous solution to prepare a core liquid, which is then added dropwise to a coagulating liquid containing a water-soluble salt of an alkali metal or an alkaline earth metal. Capsule manufacturing method.
セルを配合してなる口腔用組成物。3. An oral composition comprising the gel capsule containing an oil-soluble component according to claim 1.