JPH0875918A - Colored composition for forming transparent fine pattern and method for producing substrate having transparent colored fine pattern by using the same - Google Patents
Colored composition for forming transparent fine pattern and method for producing substrate having transparent colored fine pattern by using the sameInfo
- Publication number
- JPH0875918A JPH0875918A JP15104095A JP15104095A JPH0875918A JP H0875918 A JPH0875918 A JP H0875918A JP 15104095 A JP15104095 A JP 15104095A JP 15104095 A JP15104095 A JP 15104095A JP H0875918 A JPH0875918 A JP H0875918A
- Authority
- JP
- Japan
- Prior art keywords
- transparent
- fine pattern
- colored
- pattern
- composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は透明微細パターン形成用
着色組成物およびその応用に関する。更に詳しくは、特
に表示素子や撮像素子などのカラーフィルターの製造に
有用な透明微細パターン形成用着色組成物およびその応
用に関する。FIELD OF THE INVENTION The present invention relates to a coloring composition for forming transparent fine patterns and its application. More specifically, the present invention relates to a colored composition for forming a transparent fine pattern, which is particularly useful for producing a color filter for a display device, an image pickup device and the like, and its application.
【０００２】[0002]
【従来の技術と発明が解決しようとする課題】表示素子
や撮像素子などのカラーフィルターは、染料、顔料など
の着色剤および熱硬化性または感光性樹脂材料を含有し
てなる組成物を用い、ガラスなどの透明基板上に印刷
法、顔料分散法あるいは電着法などの方法によって透明
着色微細パターンを形成して製造されている。印刷法
は、印刷インキを用いて文字どおり印刷により直接透明
基板上に着色パターンを形成する方法である。顔料分散
法は、例えば、顔料および感光性樹脂材料を含有するフ
ォトレジスト組成物を用いて透明基板上にフォトレジス
ト層を形成し、次いでフォトリソグラフィ法によってパ
ターン化して着色パターンを形成する方法である。電着
法は、例えば、特開昭５９−１１４５７２号公報に記載
されているように、透明基板上に互に絶縁された複数の
導電回路を設け、染料または顔料と高分子材料とを含有
してなる電着浴を用い電着によって該導電回路上に選択
的に着色パターンを形成する方法である。また、電着法
は、例えば、特開昭６４−２２３７９号公報に記載され
ているように、導電層が回路状ではなくその全面に形成
された透明基板を用いても実施されている。2. Description of the Related Art A color filter such as a display device or an imaging device uses a composition containing a colorant such as a dye or a pigment and a thermosetting or photosensitive resin material. It is manufactured by forming a transparent colored fine pattern on a transparent substrate such as glass by a method such as a printing method, a pigment dispersion method or an electrodeposition method. The printing method is a method of forming a colored pattern directly on a transparent substrate by printing literally using a printing ink. The pigment dispersion method is, for example, a method of forming a photoresist layer on a transparent substrate using a photoresist composition containing a pigment and a photosensitive resin material, and then patterning the photoresist layer by a photolithography method to form a colored pattern. . The electrodeposition method is, for example, as described in JP-A-59-114572, in which a plurality of electrically conductive circuits insulated from each other are provided on a transparent substrate, and a dye or pigment and a polymer material are contained. Is a method for selectively forming a colored pattern on the conductive circuit by electrodeposition using the electrodeposition bath described above. The electrodeposition method is also carried out by using a transparent substrate having a conductive layer formed on the entire surface thereof instead of a circuit shape, as described in JP-A No. 64-22379.
【０００３】これらの透明着色微細パターンが表示素子
などのカラーフィルターとして使用されるためには、基
板の全面にわたって着色塗膜の膜厚の変動が少なく平坦
性に優れ、色の均一性とパターンの境界の鮮明性がよい
こと、更には色が鮮明で透明性がよく明るいことなどが
要求される。平坦性をよくするために、例えば、上記し
た公知の方法で透明着色微細パターンを形成し、次いで
パターン上に熱ローラーをかけて表面をならす方法や、
微細な研磨剤を用いて表面を研磨する方法などが知られ
ているが、これらの方法はカラーフィルターの生産性を
低下させるものであり、その改善が望まれている。In order for these transparent colored fine patterns to be used as a color filter for a display device or the like, there is little variation in the thickness of the colored coating film over the entire surface of the substrate and the flatness is excellent, and the uniformity of the color and the pattern are excellent. It is required that the boundary has good sharpness, and that the color is clear, has good transparency, and is bright. In order to improve the flatness, for example, a method of forming a transparent colored fine pattern by the above-described known method, and then smoothing the surface by applying a heat roller on the pattern,
There are known methods for polishing the surface using a fine abrasive, but these methods reduce the productivity of color filters, and their improvement is desired.
【０００４】また、色の均一性とパターンの境界の鮮明
性をよくするために、着色パターンを極めて精度よく導
電回路上にのみ選択的に塗着することができる電着法に
着目した方法が特開昭６２−２４７３３１号公報に記載
されている。この方法は着色パターンの間隙に遮光性塗
膜を形成してパターンの境界の鮮明性をよくしようとす
る方法であり、前記特開昭５９−１１４５７２号公報な
どに記載されている電着法によって着色パターンを形成
し、形成した着色パターン上の全面に遮光性ネガ型フォ
トレジスト組成物を塗布して塗膜を形成し、次いで着色
パターンを有する基板の裏面から該着色パターンをマス
クとして露光した後、未露光部分を現像除去する方法で
ある。この方法によれば、色の均一性とパターンの境界
の鮮明性は改善されるが、尚一層の改善が望まれてい
る。Further, in order to improve the color uniformity and the sharpness of the boundary of the pattern, a method focused on an electrodeposition method capable of selectively applying a colored pattern only on a conductive circuit with extremely high accuracy is known. It is described in JP-A-62-247331. This method is a method in which a light-shielding coating film is formed in the gap between the colored patterns to improve the sharpness of the boundary of the pattern, and the electrodeposition method described in JP-A-59-114572 is used. After forming a colored pattern, applying a light-shielding negative photoresist composition on the entire surface of the formed colored pattern to form a coating film, and then exposing the back surface of the substrate having the colored pattern using the colored pattern as a mask In this method, the unexposed portion is developed and removed. According to this method, the color uniformity and the sharpness of the boundary of the pattern are improved, but further improvement is desired.
【０００５】更には、印刷法による均一性や透明性の問
題、あるいはパターン位置からのずれの問題、顔料分散
法による工程が非常に複雑であるという問題、電着法に
よる着色パターンからの色落ちの問題などを解決するこ
とを目的に、特開昭６０−１８４６９６号公報には、電
着法によって形成さた着色パターン中で着色剤と高分子
材料とが化学的に結合していることを特徴とする方法、
すなわち、着色剤として高分子材料と化学的に結合しう
る反応性染料を用いる方法が提案されている。しかしな
がら、この方法も上記の各要求を満足するには至ってい
ない。Furthermore, there are problems of uniformity and transparency by the printing method, problems of deviation from the pattern position, problems of the pigment dispersion method being very complicated, and color fading from colored patterns by the electrodeposition method. For the purpose of solving the above-mentioned problems, JP-A-60-184696 discloses that a coloring agent and a polymer material are chemically bonded in a coloring pattern formed by an electrodeposition method. How to characterize,
That is, a method using a reactive dye that can be chemically bound to a polymer material as a colorant has been proposed. However, this method has not yet satisfied the above requirements.
【０００６】本発明者らは、上述の種々の問題を解決
し、とりわけ表示素子などのカラーフィルターの製造に
有用な諸特性に優れた着色組成物を見出すことを目的に
鋭意検討した結果、特定の体質顔料を用いることによっ
て目的が達成されることを見出して本発明を完成するに
至った。The present inventors have made extensive studies as a result of solving the above-mentioned various problems and finding a coloring composition excellent in various properties useful for manufacturing a color filter such as a display device. The present invention has been completed by finding that the object can be achieved by using the extender pigment.
【０００７】[0007]
【課題を解決するための手段】本発明は、着色剤、体質
顔料および熱硬化性または感光性樹脂材料を含有してな
る組成物にして、体質顔料が３００ｎｍ以下の平均粒径
を有する透明微細パターン形成用着色組成物、およびそ
の組成物を用いることを特徴とする透明着色微細パター
ンを有する基板の製造方法を提供する。The present invention provides a composition comprising a colorant, an extender pigment and a thermosetting or photosensitive resin material, wherein the extender pigment has a transparent fine particle size of 300 nm or less. Provided are a colored composition for pattern formation and a method for producing a substrate having a transparent colored fine pattern, which is characterized by using the composition.
【０００８】以下、本発明について詳細に説明する。本
発明で使用する着色剤は、染料類および有機または無機
顔料類から選ばれる少なくとも１種である。染料類およ
び顔料類は、所望の分光吸光特性を有し、透明で実用上
十分な堅牢性を有する限り特に制限されることはなく、
公知のいずれのものも使用することができる。染料類と
しては酸性染料、反応性染料、直接染料、塩基性染料、
分散染料、油溶性染料などがあげられ、顔料類としては
アゾレーキ系、不溶性アゾ系、縮合アゾ系、フタロシア
ニン系、キナクリドン系、ジオキサジン系、イソインド
リノン系、イソインドリン系、アントラキノン系、ペリ
レン系、チオインジゴ系顔料、酸性または塩基性染料の
レーキ、および各種無機顔料などをあげることができ
る。これらの着色剤中、耐熱性などの観点から顔料類が
好適に用いられる。The present invention will be described in detail below. The colorant used in the present invention is at least one selected from dyes and organic or inorganic pigments. Dyes and pigments are not particularly limited as long as they have desired spectral absorption characteristics, are transparent and have practically sufficient fastness,
Any known one can be used. As dyes, acid dyes, reactive dyes, direct dyes, basic dyes,
Disperse dyes, oil-soluble dyes, and the like, and as pigments, azo lake type, insoluble azo type, condensed azo type, phthalocyanine type, quinacridone type, dioxazine type, isoindolinone type, isoindoline type, anthraquinone type, perylene type, Examples thereof include thioindigo-based pigments, lakes of acidic or basic dyes, and various inorganic pigments. Among these colorants, pigments are preferably used from the viewpoint of heat resistance and the like.
【０００９】本発明における熱硬化性または感光性樹脂
材料も特に制限されることはなく、本技術分野で通常用
いられているいずれのものも使用することができる。熱
硬化性樹脂材料としては、前出の特開昭６０−１８４６
９６号公報に記載されているようなマレイン化油系、ア
クリル系、ポリエステル系、ポリブタジエン系、ポリオ
レフィン系などの樹脂や、フェノールノボラック、ポリ
イミド、ポリビニールアルコール、変成アクリル樹脂、
変成エポキシ樹脂、変成シリコーン樹脂などを例示する
ことができる。The thermosetting or photosensitive resin material in the present invention is also not particularly limited, and any of those commonly used in this technical field can be used. As the thermosetting resin material, the above-mentioned JP-A-60-1846 is used.
Maleized oil-based, acrylic-based, polyester-based, polybutadiene-based, polyolefin-based resins, phenol novolac, polyimide, polyvinyl alcohol, modified acrylic resin, etc.
Examples thereof include modified epoxy resin and modified silicone resin.
【００１０】感光性樹脂材料としては、上記各種樹脂
に、例えばトリメチロールプロパントリ（メタ）アクリ
レート、ジトリメチロールプロパンヘキサ（メタ）アク
リレートなどの多官能（メタ）アクリレートやウレタン
（メタ）アクリレート、ポリエステル（メタ）アクリレ
ートなどのオリゴマーなどの光硬化性材料を混合したも
の、あるいは、アマニ油、ポリブタジエンなどに、２−
ヒドロキシエチル（メタ）アクリレートなどの（メタ）
アクリロイル基を有する水酸基含有モノマーを半エステ
ル付加させて得られる光硬化性樹脂、エポキシ樹脂に
（メタ）アクリル酸を付加させ、次いで多塩基酸をエス
テル付加させて得られる光硬化性樹脂、高酸価ポリマー
にグリシジル（メタ）アクリレートなどを作用させて得
られる光硬化性樹脂、水溶性ポリエステル樹脂にジイソ
シアネートの存在下にヒドロキシエチルアクリレートな
どの水酸基含有モノマーを付加させて得られる光硬化性
樹脂などを例示することができる。また、顔料分散法な
どで通常使用されているフォトレジスト組成物なども例
示することができる。これらの材料は、それぞれ単独
で、または２種以上を混合して使用することができる。As the photosensitive resin material, in addition to the above various resins, for example, polyfunctional (meth) acrylates such as trimethylolpropane tri (meth) acrylate and ditrimethylolpropane hexa (meth) acrylate, urethane (meth) acrylate, polyester ( A mixture of photo-curable materials such as oligomers such as (meth) acrylate, linseed oil, polybutadiene, etc.
(Meth) such as hydroxyethyl (meth) acrylate
A photocurable resin obtained by half-esterifying a hydroxyl group-containing monomer having an acryloyl group, a photocurable resin obtained by adding (meth) acrylic acid to an epoxy resin, and then esterifying a polybasic acid, a high acid A photocurable resin obtained by allowing glycidyl (meth) acrylate to act on a valent polymer, and a photocurable resin obtained by adding a hydroxyl group-containing monomer such as hydroxyethyl acrylate to a water-soluble polyester resin in the presence of diisocyanate. It can be illustrated. Moreover, the photoresist composition etc. normally used by the pigment dispersion method etc. can be illustrated. These materials can be used alone or in admixture of two or more.
【００１１】本発明で使用する体質顔料（エキステンダ
ー）は、実質的に無色または白色であれば、その種類に
ついては特に制限されることなく、公知のいずれのもの
も使用することができる。好ましくは、亜鉛華、リトポ
ン、炭酸カルシウム、（白艶華、炭酸石灰粉、重質炭カ
ル、白亜、チョーク、Ｐａｒｉｓ Ｗｈｉｔｅ）、硫酸
バリウム（沈降性硫酸バリウム、バライト）、炭酸バリ
ウム、石膏（Ｇｙｐｓｕｍ、Ｌｉｇｈｔ Ｓｐａｒ）、
アスベスト（石綿）、クレー（Ｃｈｉｎａ Ｃｌａｙ、
カオリン、白土）、シリカ粉（珪石粉、微粉ケイ酸、Ｗ
ｈｉｔｅ Ｃａｒｂｏｎ）、珪藻土、タルク（滑石
粉）、塩基性炭酸マグネシウム、アルミナホワイト（水
酸化アルミニウム）、グロスホワイト（Ａｌｕｍｉｎａ
−ＢｌａｎｃＦｉｘ）、サチン白や酸化セリウムなどを
例示することができる。これらの体質顔料はそれぞれ単
独で、または２種以上を混合して使用することができ
る。The extender pigment used in the present invention is not particularly limited in its kind as long as it is substantially colorless or white, and any known one can be used. Preferred are zinc white, lithopone, calcium carbonate, (white luster, lime carbonate powder, heavy carbon, calcite, chalk, Paris White), barium sulfate (precipitable barium sulfate, barite), barium carbonate, gypsum (Gypsum, Light). Spar),
Asbestos (asbestos), clay (China Clay,
Kaolin, clay, silica powder (silica powder, fine silicic acid, W)
white carbon), diatomaceous earth, talc (talc powder), basic magnesium carbonate, alumina white (aluminum hydroxide), gloss white (Alumina)
-BlancFix), satin white, cerium oxide, and the like. These extender pigments can be used alone or in admixture of two or more.
【００１２】本発明で使用する体質顔料は、３００ｎｍ
以下、好ましくは１００ｎｍ以下の平均粒径を有する。
粒径分布は狭い方が好ましく、とりわけ、粗大粒子の混
入は好ましくなく、特に粒径が５００ｎｍ以上の粒子
は、体質顔料中、好ましくは７重量％以下で可能な限り
無くしておくことが望ましい。一方、平均粒径が非常に
小さい場合、例えば、５ｎｍより小さい場合には所望の
効果が得難いことがある。このようなことから、本発明
で使用する体質顔料の平均粒径は３００ｎｍ以下で好ま
しくは５ｎｍ以上、より好ましくは１００ｎｍ以下で７
ｎｍ以上の範囲である。The extender pigment used in the present invention is 300 nm.
Below, preferably it has an average particle size of 100 nm or less.
It is preferable that the particle size distribution is narrow, and in particular, it is not preferable to mix coarse particles, and it is particularly preferable that particles having a particle size of 500 nm or more in the extender pigment are preferably 7% by weight or less as much as possible. On the other hand, when the average particle diameter is very small, for example, when it is smaller than 5 nm, it may be difficult to obtain a desired effect. Therefore, the average particle size of the extender pigment used in the present invention is 300 nm or less, preferably 5 nm or more, and more preferably 100 nm or less.
It is in the range of nm or more.
【００１３】体質顔料の平均粒径は常法により、光散乱
法、Ｘ線散乱法、比表面積測定法または電子顕微鏡など
によって測定することができる。また、本発明で使用す
る体質顔料の粒子の形状は、球または球に近似のものの
みならず、板状、棒状、針状などであってもよい。球ま
たは球に近似でない形状のものの粒径は、その体積が等
しい球（等価球）の直径を代用することができる。この
場合、光散乱法、Ｘ線散乱法または電子顕微鏡によって
等価球の直径で代替した平均粒径を測定することができ
る。The average particle size of the extender pigment can be measured by a conventional method such as a light scattering method, an X-ray scattering method, a specific surface area measuring method or an electron microscope. Further, the shape of the particles of the extender pigment used in the present invention is not limited to spheres or spheres, and may be plate-like, rod-like, needle-like, or the like. For the particle size of a sphere or a shape not approximate to a sphere, the diameter of a sphere having the same volume (equivalent sphere) can be substituted. In this case, a light scattering method, an X-ray scattering method, or an electron microscope can be used to measure the average particle diameter, which is replaced by the diameter of the equivalent sphere.
【００１４】本発明の透明微細パターン形成用着色組成
物を製造するに当たり、着色剤と熱硬化性または感光性
樹脂材料との混合割合は公知の範囲内で適宜決定するこ
とができる。例えば、着色組成物を電着法による透明微
細パターンの形成に使用する場合、着色剤と熱硬化性ま
たは感光性樹脂材料との混合重量割合は約１／２〜１／
２０である。体質顔料の使用量は、その種類および平均
粒径により、また着色剤の種類および使用量によって異
なるが、本発明の着色組成物を用い後述する方法に従っ
て透明基板上に透明着色微細パターンを形成したとき、
該パターン中の体質顔料の含量がパターンの重量に対し
て、好ましくは０．０３〜１５重量％、より好ましくは
０．１〜５重量％になるように調整する。体質顔料の使
用量が少なすぎると所望の効果が得られない場合があ
り、一方、多すぎると透明性や平坦性を損なう場合があ
る。In producing the transparent fine pattern forming colored composition of the present invention, the mixing ratio of the colorant and the thermosetting or photosensitive resin material can be appropriately determined within a known range. For example, when the colored composition is used for forming a transparent fine pattern by the electrodeposition method, the mixing weight ratio of the colorant and the thermosetting or photosensitive resin material is about 1/2 to 1 /.
Twenty. The amount of the extender pigment used varies depending on the type and average particle size of the extender pigment and the type and amount of the colorant used, but a transparent colored fine pattern was formed on the transparent substrate according to the method described below using the coloring composition of the present invention. When
The content of the extender pigment in the pattern is adjusted to preferably 0.03 to 15% by weight, more preferably 0.1 to 5% by weight, based on the weight of the pattern. If the amount of the extender pigment used is too small, the desired effect may not be obtained, while if it is too large, the transparency and flatness may be impaired.
【００１５】本発明の透明微細パターン形成用着色組成
物は、上記した着色剤、体質顔料、および熱硬化性また
は感光性樹脂材料に所望によりそれらの溶剤、更に所望
により印刷インキや塗料などに通常用いられている添加
剤を適宜混合し、常法に従いロールミル、ボールミル、
サンドミル、ビーズミルなどを用いて容易に製造するこ
とができる。溶剤としては、水の他に、アルコール類、
セロソルブ類、エステル類、炭化水素類などの有機溶剤
が、また、添加剤としては、分散剤、ｐＨ調整剤、消泡
剤、塗膜流展剤などが例示され、これらの使用量は、公
知の範囲内で適宜決定することができる。The transparent fine pattern-forming coloring composition of the present invention is usually used in the above-mentioned coloring agents, extender pigments, thermosetting or photosensitive resin materials, if desired, in their solvents, and if desired, in printing inks and paints. Appropriately mixing the additives used, roll mill, ball mill,
It can be easily manufactured using a sand mill, a bead mill, or the like. As the solvent, in addition to water, alcohols,
Organic solvents such as cellosolves, esters, and hydrocarbons, and examples of the additives include dispersants, pH adjusters, defoamers, coating leveling agents, and the like. It can be appropriately determined within the range.
【００１６】このようにして得られる着色組成物を用
い、印刷法、顔料分散法、電着法などの公知の方法に従
って、ガラスなどの透明基板上に透明着色微細パターン
を形成することができる。本発明の透明微細パターン形
成用着色組成物は、着色塗膜の膜厚の変動、平坦性、パ
ターニングの精度およびコストなどの観点から、特に電
着法による透明着色微細パターンの形成に好適に用いら
れる。The colored composition thus obtained can be used to form a transparent colored fine pattern on a transparent substrate such as glass by a known method such as a printing method, a pigment dispersion method or an electrodeposition method. The transparent fine pattern forming colored composition of the present invention is preferably used for forming a transparent fine colored pattern by the electrodeposition method, particularly from the viewpoints of variation in film thickness of a colored coating film, flatness, patterning accuracy and cost. To be
【００１７】[0017]
【実施例】以下に本発明を実施例によって更に詳細に説
明するが、本発明はこの実施例に限定されるものではな
い。EXAMPLES The present invention will be described below in more detail with reference to examples, but the present invention is not limited to these examples.
【００１８】実施例１ 着色剤としてフタロシアニンブルーＳＲ−１５０（山陽
色素社製）、フタロシアニングリーンＳＡＸ（山陽色素
社製）、ピグメントレッド４ＢＳ（山陽色素社製）およ
び透明酸化鉄（ＴＯＲ、大日精化社製）の各顔料を、体
質顔料としてアエロジル２００ＣＦ（平均粒径１２ｎｍ
のシリカ粉、日本アエロジル社製）およびファイネック
ス５０（平均粒径２０ｎｍの亜鉛華、堺化学製）を下表
の重量比で適量のメチルセロソルブと混合し、それぞれ
赤色、緑色および青色顔料組成物を調整した。尚、下表
の重量比の値は後述の方法で透明基板上に形成した透明
着色微細パターンの重量を１００としたときの値であ
る。Example 1 As colorants, phthalocyanine blue SR-150 (manufactured by Sanyo Dye Co., Ltd.), phthalocyanine green SAX (manufactured by Sanyo Dye Co., Ltd.), Pigment Red 4BS (manufactured by Sanyo Dye Co., Ltd.) and transparent iron oxide (TOR, Dainichiseika) Aerosil 200CF (average particle size 12 nm) as an extender
Silica powder, manufactured by Nippon Aerosil Co., Ltd.) and FINEX 50 (zinc flower having an average particle size of 20 nm, manufactured by Sakai Chemical Co., Ltd.) were mixed with appropriate amounts of methyl cellosolve in the weight ratios shown in the table below to give red, green and blue pigment compositions, respectively. Was adjusted. The weight ratio values in the table below are values when the weight of the transparent colored fine pattern formed on the transparent substrate by the method described below is 100.
【００１９】[0019]
【表１】 [Table 1]
【００２０】一方、エスビアＥＤ−３０００クリアー
（水溶性ポリエステル樹脂および水溶性メラミン樹脂か
らなる樹脂成分７０重量％、およびブチルセロソルブ、
エチルセロソルブおよびｎ−ブタノールからなる溶剤成
分３０重量％からなる電着用塗料、神東塗料社製）と水
との溶液（エスビアＥＤ−３０００：水重量比＝５：１
２０）を準備し、これに、上記の各色顔料組成物を混
合、分散してそれぞれの電着浴を調製した。On the other hand, Svia ED-3000 clear (70% by weight of a resin component consisting of a water-soluble polyester resin and a water-soluble melamine resin, and butyl cellosolve,
Electrodeposition paint consisting of 30% by weight of a solvent component consisting of ethyl cellosolve and n-butanol, manufactured by Shinto Paint Co., Ltd., and a solution of water (Esvia ED-3000: water weight ratio = 5: 1).
20) was prepared, and the above-described pigment compositions of each color were mixed and dispersed to prepare respective electrodeposition baths.
【００２１】このように調製した電着浴中に、表面に８
０μｍ幅のＩＴＯ（６０Ω／平方）回路を２０μｍの間
隙をおいて（１００μｍピッチ）ストライプ状に形成し
てなる１．１ｍｍ厚ガラス基板を浸漬し、常法により１
０Ｖ、３分間の条件で電着を行ない、透明着色微細パタ
ーンを有する基板を作成した。次いで、前出特開昭６２
−２４７３３１号公報実施例１に記載されている方法で
上記の透明着色微細パターンの間隙に黒色の遮光性塗膜
を形成した。In the electrodeposition bath thus prepared, 8
A 1.1 mm-thick glass substrate formed by forming ITO (60 Ω / square) circuit with a width of 0 μm in stripes with a gap of 20 μm (pitch of 100 μm) was dipped, and 1
Electrodeposition was performed under conditions of 0 V for 3 minutes to prepare a substrate having a transparent colored fine pattern. Then, the above-mentioned JP-A-62
A black light-shielding coating film was formed in the gap of the transparent colored fine pattern by the method described in Example 1 of JP-A-247331.
【００２２】このようにして透明基板上に形成した透明
着色微細パターンは着色塗膜の膜厚の変動が少なく、平
坦性が優れ、色の均一性および各パターンの境界の鮮明
性がよく、光の漏れがなく、更には色が鮮明で透明性が
よく明るいものであった。The transparent colored fine pattern thus formed on the transparent substrate has little variation in the thickness of the colored coating film, is excellent in flatness, has good color uniformity and sharpness of the boundary between the patterns, and There was no leakage, and the color was clear, the transparency was good, and it was bright.
【００２３】[0023]
【発明の効果】本発明の着色組成物は透明着色微細パタ
ーンの形成に使用して、着色塗膜の膜厚の変動が少な
く、平坦性が優れ、色の均一性およびパターンの境界の
鮮明性がよく、更に色が鮮明で透明性がよく明るいパタ
ーンを形成することができ、このようなパターンが形成
された基板をカラーフィルターとして用いると高輝度、
高コントラストで高画質の液晶ディスプレーなどを製造
することができる。The colored composition of the present invention is used for forming a transparent colored fine pattern and has little variation in the thickness of a colored coating film, excellent flatness, color uniformity and sharpness of pattern boundaries. It is possible to form a bright pattern that has a good color and is clear and has good transparency. When a substrate on which such a pattern is formed is used as a color filter, high brightness,
It is possible to manufacture liquid crystal displays with high contrast and high image quality.
フロントページの続き (51)Int.Cl.6 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｃ２５Ｄ 13/06 Ｂ Continuation of the front page (51) Int.Cl. 6 Identification code Office reference number FI technical display location C25D 13/06 B
Claims (7)
感光性樹脂材料を含有してなる組成物にして、体質顔料
が３００ｎｍ以下の平均粒径を有する透明微細パターン
形成用着色組成物。1. A colored composition for forming a transparent fine pattern, comprising a colorant, an extender pigment and a thermosetting or photosensitive resin material, wherein the extender pigment has an average particle diameter of 300 nm or less.
有する請求項１に記載の組成物。2. The composition according to claim 1, wherein the extender pigment has an average particle size of 5 to 300 nm.
有する請求項１または２に記載の組成物。3. The composition according to claim 1, wherein the extender pigment has an average particle size of 7 to 100 nm.
らなる請求項１〜３のいずれかに記載の組成物。4. The composition according to claim 1, wherein the extender pigment has a particle size smaller than 500 nm.
を７重量％以下含有する請求項１〜３のいずれかに記載
の組成物。5. The composition according to claim 1, wherein the extender pigment contains 7% by weight or less of particles having a particle size of 500 nm or more.
を用いることを特徴とする透明着色微細パターンを有す
る基板を製造する方法。6. A method for producing a substrate having a transparent colored fine pattern, which comprises using the composition according to any one of claims 1 to 5.
着色微細パターンを有する基板。7. A substrate having a transparent colored fine pattern produced by the method of claim 6.