JPH0871797A - Production of hollow strut parts made of fiber reinforced metal - Google Patents
Production of hollow strut parts made of fiber reinforced metalInfo
- Publication number
- JPH0871797A JPH0871797A JP23936294A JP23936294A JPH0871797A JP H0871797 A JPH0871797 A JP H0871797A JP 23936294 A JP23936294 A JP 23936294A JP 23936294 A JP23936294 A JP 23936294A JP H0871797 A JPH0871797 A JP H0871797A
- Authority
- JP
- Japan
- Prior art keywords
- fiber
- capsule
- reinforced metal
- hollow strut
- metal material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【0001】[0001]
【産業上の利用分野】本発明は、航空機の脚構造材やエ
ンジン支持部材,宇宙機器の構造材,例えば宇宙ステー
ションの構造材,宇宙ロボットのアーム等に用いる為の
繊維強化金属製中空ストラット部品の製造方法に関す
る。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a hollow strut component made of fiber reinforced metal for use in aircraft leg structure materials, engine support members, space equipment structure materials, such as space station structure materials, space robot arms, and the like. Manufacturing method.
【0002】[0002]
【従来の技術】従来の繊維強化金属製中空ストラット部
品の製造方法として、特公平3−13943号公報に記
載の繊維強化金属製品の成形方法がある。この成形方法
は、図6及び図7に示すように内側カプセル2と外側カ
プセル1で形成される成形用カプセル装置6の内部に、
繊維強化金属素材3を封入し、加熱条件下で前記カプセ
ル装置6の外部から加圧して成形を行う静水圧成形(等
方圧成形)による繊維強化金属製品の成形方法におい
て、前記カプセル装置6内で、前記外側カプセル1と前
記内側カプセル2のいずれか一方に隣接して、成形温度
条件で前記カプセルの材料より高い剛性を有する材料の
変形防止部材(中子)4を配置し、前記外側カプセル1
と前記内側カプセル2との間に前記繊維強化金属素材3
を封入して、静水圧成形(等方圧成形)を行うものであ
る。2. Description of the Related Art As a conventional method for producing a fiber-reinforced metal hollow strut component, there is a method for forming a fiber-reinforced metal product described in Japanese Patent Publication No. 3-13943. As shown in FIGS. 6 and 7, this molding method is performed inside the molding capsule device 6 formed of the inner capsule 2 and the outer capsule 1,
In the method of molding a fiber-reinforced metal product by isostatic molding, in which the fiber-reinforced metal material 3 is encapsulated and pressure is applied from outside the capsule device 6 under heating conditions, Then, a deformation preventing member (core) 4 made of a material having a rigidity higher than that of the material of the capsule under a molding temperature condition is arranged adjacent to one of the outer capsule 1 and the inner capsule 2, and the outer capsule 1
And the fiber-reinforced metal material 3 between the inner capsule 2 and the inner capsule 2.
And is subjected to isostatic molding (isostatic molding).
【0003】ところで、等方圧成形による中空ストラッ
ト部品の製造では、任意の方向に負荷される圧力を繊維
強化金属素材3の複合化に必要な所定の圧力方向に制御
する必要がある。上記従来の成形方法では、圧力媒体と
なる均厚のカプセル装置6の内部に、内外側のカプセル
2,1よりも剛性の大きい変形防止部材(中子)4を挿
入し、外側カプセル1の変形を防止しているが、この成
形方法ではカプセル構成が複雑になると共に、所定の外
形寸法を得ることが困難であった。By the way, in the production of hollow strut parts by isotropic molding, it is necessary to control the pressure applied in an arbitrary direction to a predetermined pressure direction required for compounding the fiber-reinforced metal material 3. In the conventional molding method described above, the deformation preventing member (core) 4 having a higher rigidity than the inner and outer capsules 2 and 1 is inserted into the uniform thickness capsule device 6 serving as a pressure medium to deform the outer capsule 1. However, this molding method complicates the capsule structure and makes it difficult to obtain a predetermined external dimension.
【0004】また、従来の繊維強化金属製中空ストラッ
ト部品は、繊維の配向方向がストラットの長手方向と平
行方向のみであったが、中空ストラット部品の使用時の
複雑な応力伝達には不十分であった。通常の繊維の積層
法は、繊維の中間素材と金属箔を所定の大きさに切断し
た後、中空ストラット部品の長手方向と繊維方向が一致
するように内側カプセル2に巻き付けて積層する。この
方向で繊維を中空ストラット部品の長手方向以外の方向
に積層(角度積層)した場合には、繊維の拘束によって
内側カプセル2の拡管方向への変形が妨げられ、カプセ
ル装置6の内部の繊維強化金属素材3に成形圧力が伝達
されず、繊維強化金属素材3の成形不良が起こる。さら
に、従来の成形方法で成形した繊維強化金属製中空スト
ラット部品は、機械加工により外側カプセル1を削り取
って、取り出していたが、中空ストラット部品の内面の
内側カプセル2の除去には高精度の特殊加工が必要であ
り、製造工程の複雑化、高コスト化につながっていた。Further, in the conventional fiber-reinforced metal hollow strut component, the orientation direction of the fiber is only parallel to the longitudinal direction of the strut, but it is not sufficient for complicated stress transmission when the hollow strut component is used. there were. In a usual fiber laminating method, an intermediate material of fibers and a metal foil are cut into a predetermined size, and then wound and laminated on the inner capsule 2 so that the longitudinal direction of the hollow strut part and the fiber direction coincide with each other. When fibers are laminated in this direction in a direction other than the longitudinal direction of the hollow strut part (angle lamination), the constraint of the fibers prevents the inner capsule 2 from being deformed in the tube expanding direction, and the fiber reinforcement inside the capsule device 6 is prevented. The molding pressure is not transmitted to the metal material 3, and the fiber-reinforced metal material 3 is defectively molded. Further, in the fiber-reinforced metal hollow strut parts molded by the conventional molding method, the outer capsule 1 was scraped off by machining to be taken out, but the inner capsule 2 on the inner surface of the hollow strut part is removed with high precision. Processing was required, which led to complicated manufacturing processes and higher costs.
【0005】[0005]
【発明が解決しようとする課題】そこで本発明は、成形
用カプセル装置のカプセル構成の簡素化と共に成形され
る繊維強化金属製中空ストラット部品の品質の向上及び
外形寸法精度の向上を図ることができ、また内側カプセ
ルの拡管方向への変形が妨げられず、成形用カプセル装
置の内部の繊維強化金属素材に成形圧力を伝達できて、
成形不良が生ぜず、さらに成形した繊維強化金属製中空
ストラット部品の取り出し時の内面加工などの機械加工
を大幅に減少し、工程の簡素化,低コスト化を達成でき
る繊維強化金属製中空ストラット部品の製造方法を提供
しようとするものである。SUMMARY OF THE INVENTION Therefore, the present invention can simplify the capsule structure of the molding capsule device and improve the quality and the accuracy of the external dimension of the fiber-reinforced metal hollow strut parts to be molded. Also, the deformation of the inner capsule in the tube expanding direction is not hindered, and the molding pressure can be transmitted to the fiber-reinforced metal material inside the molding capsule device,
Fiber reinforced metal hollow strut parts that do not cause molding defects and can significantly reduce machining such as inner surface processing when taking out the molded fiber reinforced metal hollow strut parts, simplifying the process and reducing cost The present invention is intended to provide a manufacturing method of.
【0006】[0006]
【課題を解決するための手段】上記課題を解決するため
の本発明の繊維強化金属製中空ストラット部品の製造方
法は、内側カプセルと外側カプセルで形成される成形用
カプセル装置の内部に、繊維強化金属素材を充填,封塞
し、加熱条件下で前記カプセル装置の外部から加圧して
熱間等方圧成形を行い、然る後カプセルの除去及び中空
ストラットの取り出しを行う繊維強化金属製中空ストラ
ット部品の製造方法に於いて、前記カプセル装置の外側
カプセルを内側カプセルよりも肉厚を厚くすると共に内
外側カプセルの材質を軟鋼となして、熱間等方圧成形を
行うことを特徴とするものである。A method for manufacturing a fiber-reinforced metal hollow strut component according to the present invention for solving the above-mentioned problems includes a fiber-reinforced inside a molding capsule device formed of an inner capsule and an outer capsule. A fiber-reinforced metal hollow strut that is filled and sealed with a metal material and subjected to hot isostatic pressing by applying pressure from the outside of the capsule device under heating conditions, and then removing the capsule and taking out the hollow strut. In the method of manufacturing a component, the outer capsule of the capsule device is made thicker than the inner capsule and the material of the inner and outer capsules is made of mild steel, and hot isostatic pressing is performed. Is.
【0007】上記本発明の繊維強化金属製中空ストラッ
ト部品の製造方法に於いて、成形用カプセル装置の内部
への繊維強化金属素材の充填の一手段としては、シート
状の繊維強化金属素材中の繊維を隣り合った繊維と夫々
一定間隔ずらして切断の上、内側カプセルに繊維が斜向
するようにシート状の繊維強化金属素材を巻き付けて積
層し、外側カプセルの内部に挿入することであることが
好ましい。In the method for producing a hollow fiber-reinforced metal strut part of the present invention, one means for filling the inside of the molding capsule device with the fiber-reinforced metal material is a sheet-shaped fiber-reinforced metal material. It is to insert the fiber inside the outer capsule by slicing the sheet-shaped fiber reinforced metal material so that the fiber is diagonally inclined to the inner capsule after cutting the fiber with a certain gap between adjacent fibers. Is preferred.
【0008】他の手段としては、シート状の繊維強化金
属素材中の一部の繊維を外側カプセルの内面に接する位
置に斜向して巻くように積層して配し、その内面に残り
のシート状の繊維強化金属素材中の繊維をストラットの
長手方向と繊維方向が一致した方向に巻きつけた内側カ
プセルを嵌合することであることが好ましい。As another means, a part of the fibers in the sheet-shaped fiber-reinforced metal material is laminated so as to be obliquely wound at a position in contact with the inner surface of the outer capsule, and the remaining sheet is placed on the inner surface. It is preferable to fit an inner capsule formed by winding the fibers in the fiber-shaped metal material in the shape of a fiber in a direction in which the longitudinal direction of the struts and the fiber direction coincide with each other.
【0009】以上の本発明の繊維強化金属製中空ストラ
ット部品の製造方法に於いて、熱間等方圧成形は、繊維
強化金属素材の金属マトリックスの拡散接合可能な温度
領域で、100〜200MPaのガス圧を30分〜60
分間負荷する条件で行うことが好ましい。In the above-mentioned method for producing a fiber-reinforced metal hollow strut component of the present invention, hot isostatic pressing is performed at 100 to 200 MPa in a temperature range in which the metal matrix of the fiber-reinforced metal material can be diffusion-bonded. Gas pressure 30 minutes to 60
It is preferable to carry out under the condition of loading for a minute.
【0010】さらに、以上の本発明の繊維強化金属製中
空ストラット部品の製造方法に於いて、カプセルの除去
は、内側カプセルと同程度の厚さになるまでの機械加工
による外側カプセルの余肉切除と処理液中への浸漬によ
るカプセルの溶解除去であることが好ましい。さらにま
た、以上の本発明の繊維強化金属製中空ストラット部品
の製造方法に於いては、成形用カプセル装置の内部に繊
維強化金属素材を充填すると共に、その両端に端末金具
を嵌着して封塞し、熱間等方圧成形を行って繊維強化金
属素材の複合化成形と同時に端末金具を拡散接合するこ
とが好ましい。Further, in the above-described method for manufacturing a fiber-reinforced metal hollow strut component according to the present invention, the removal of the capsule is performed by removing the excess thickness of the outer capsule by machining until the thickness is about the same as the inner capsule. It is preferable that the capsules are dissolved and removed by immersion in the treatment liquid. Furthermore, in the above-described method for producing a fiber-reinforced metal hollow strut component of the present invention, the inside of the molding capsule device is filled with the fiber-reinforced metal material, and both ends thereof are fitted with terminal fittings for sealing. It is preferable that the terminal metal fittings are diffusion-bonded simultaneously with the composite molding of the fiber-reinforced metal material by closing and hot isostatic pressing.
【0011】[0011]
【作用】本発明の繊維強化金属製中空ストラット部品の
製造方法に於いては、前述のようにカプセル装置の外側
カプセルを内側カプセルよりも肉厚を厚くすると共に、
内外側カプセルの材質を軟鋼としたので、カプセル装置
の外部から加圧して熱間等方圧成形を行った際、外側カ
プセルの変形が防止されて、所定の外形寸法の中空スト
ラット部品を得ることができ、寸法精度が向上する。ま
た外側カプセルの肉厚を厚くしたことにより、従来の変
形防止部材(中子)を無くすることができて、カプセル
構成が簡素化する。そしてカプセルの材質を軟鋼とした
ことにより、カプセルと繊維強化金属素材との間の反応
や焼き付きが防止され、品質の良い繊維強化金属製中空
ストラット部品が得られる。In the method of manufacturing the fiber-reinforced metal hollow strut component of the present invention, the outer capsule of the capsule device is made thicker than the inner capsule as described above, and
As the material of the inner and outer capsules is mild steel, the deformation of the outer capsule is prevented when hot isostatic pressing is performed by applying pressure from the outside of the capsule device, and a hollow strut part with a predetermined external dimension is obtained. The dimensional accuracy is improved. Further, by increasing the thickness of the outer capsule, the conventional deformation preventing member (core) can be eliminated, and the capsule structure is simplified. Since the capsule is made of mild steel, reaction and seizure between the capsule and the fiber-reinforced metal material are prevented, and a good quality fiber-reinforced metal hollow strut component can be obtained.
【0012】また、本発明の繊維強化金属製中空ストラ
ット部品の製造方法に於いて、成形用カプセル装置の内
部への繊維強化金属素材の充填の一手段として、シート
状の繊維強化金属素材中の繊維を隣り合った繊維と夫々
一定間隔ずらして切断の上、内側カプセルに繊維が斜向
するようにシート状の繊維強化金属素材を巻き付けて積
層し、外側カプセルの内部へ挿入する方法を採用した場
合は、カプセル装置の外部から加圧して熱間等方圧成形
を行った際、内側カプセルの拡管方向への変形が、巻き
付け積層した繊維強化金属素材により拘束されず、従っ
て、カプセル装置内の繊維強化金属素材に成形圧力が十
分に伝達され、繊維強化金属素材の中空ストラット部品
への成形が良好に行われる。Further, in the method for producing a fiber-reinforced metal hollow strut part of the present invention, as a means for filling the inside of the molding capsule device with the fiber-reinforced metal material, a sheet-shaped fiber-reinforced metal material is used. We adopted a method in which the fibers were cut at a certain distance from the adjacent fibers, cut, wrapped with a sheet-shaped fiber-reinforced metal material so that the fibers were diagonally wrapped around the inner capsule, and laminated into the outer capsule. In the case, when hot isostatic pressing is performed by applying pressure from the outside of the capsule device, the deformation of the inner capsule in the tube expanding direction is not restricted by the wound and laminated fiber reinforced metal material, and therefore The molding pressure is sufficiently transmitted to the fiber reinforced metal material, and the fiber reinforced metal material is satisfactorily molded into the hollow strut component.
【0013】また、成形用カプセル装置の内部への繊維
強化金属素材の充填の他の手段として、シート状の繊維
強化金属素材中の一部の繊維を、外側カプセルの内面に
接する位置に斜向して巻くように積層して配し、その内
面に残りのシート状の繊維強化金属素材中の繊維をスト
ラットの長手方向と繊維方向が一致した方向に巻きつけ
た内側カプセルを嵌合する方法を採用した場合は、カプ
セル装置の外部から加圧して熱間等方圧成形を行った
際、内側カプセルの内面近くに斜向して配した繊維が無
いので、内側カプセルの拡管方向への変形が拘束され
ず、従って、カプセル装置内の繊維強化金属素材に成形
圧力が十分に伝達され、繊維強化金属素材の中空ストラ
ット部品への成形が良好に行われる。As another means for filling the inside of the molding capsule device with the fiber-reinforced metal material, a part of the fibers in the sheet-shaped fiber-reinforced metal material is inclined to a position in contact with the inner surface of the outer capsule. Then, the inner capsule is formed by winding the remaining fibers in the sheet-shaped fiber-reinforced metal material in the direction in which the longitudinal direction of the struts and the direction of the fibers match each other. When adopted, when hot isostatic pressing is performed by applying pressure from the outside of the capsule device, there is no fiber obliquely arranged near the inner surface of the inner capsule, so deformation of the inner capsule in the tube expansion direction does not occur. It is not restrained, and therefore, the molding pressure is sufficiently transmitted to the fiber-reinforced metal material in the capsule device, and the fiber-reinforced metal material is well molded into the hollow strut part.
【0014】本発明の繊維強化金属製中空ストラット部
品の製造方法に於いて、熱間等方圧成形を、繊維強化金
属素材の金属マトリックスの拡散接合可能な温度領域で
100〜200MPaのガス圧を、30分〜60分間負
荷する条件で行った場合、繊維強化金属素材の複合化に
よる中空ストラット部品の製造が精度良く円滑に行われ
る。In the method for producing a fiber-reinforced metal hollow strut component of the present invention, hot isostatic pressing is performed by applying a gas pressure of 100 to 200 MPa in a temperature range in which the metal matrix of the fiber-reinforced metal material can be diffusion-bonded. When carried out under the condition of being loaded for 30 to 60 minutes, the manufacture of the hollow strut component by the composite of the fiber-reinforced metal material is carried out accurately and smoothly.
【0015】本発明の繊維強化金属製中空ストラット部
品の製造方法に於いて、カプセルの除去を、内側カプセ
ルと同程度の厚さになるまで機械加工による外側カプセ
ルの余肉切除と、処理液中への浸漬によるカプセルの溶
解除去とした場合、内面加工などの機械加工の比率が大
幅に減少し、工程の簡素化や低コスト化を達成できる。In the method for producing a fiber-reinforced metal hollow strut component according to the present invention, the removal of the capsule is carried out by cutting the excess thickness of the outer capsule by machining until the thickness is about the same as that of the inner capsule and in the treatment liquid. When the capsule is dissolved and removed by dipping in, the ratio of machining such as inner surface processing is significantly reduced, and the process can be simplified and the cost can be reduced.
【0016】このように外側カプセルを全部機械加工し
ないのは、旋盤加工時の偏心や熱歪み等の発生によって
繊維強化金属製中空ストラット部品の一部が加工されて
しまうのを防止するためであり、逆に、繊維強化金属製
中空ストラット部品を傷付けずに機械加工のみで外側カ
プセル全部を除去するには、非常に厳密な加工精度が要
求されるとともに、非常なコストアップとなるためであ
る。また、溶解処理だけでカプセル全体を除去するため
には、外側カプセルが厚いため長時間を要し、溶解液に
より繊維強化金属製中空ストラット部品に悪影響を及ぼ
すことが懸念される。そこで、外側カプセルを内側カプ
セルと同じ程度の厚みまでラフに機械加工した後、溶解
処理をすることによって、機械加工のコストダウン、溶
解処理時間の短縮、及び中空ストラット部品の品質の向
上が達成できるものである。[0016] The reason why the outer capsule is not entirely machined in this way is to prevent a part of the fiber-reinforced metal hollow strut component from being machined due to the occurrence of eccentricity or thermal strain during lathe machining. On the contrary, in order to remove all the outer capsules only by machining without damaging the fiber-reinforced metal hollow strut parts, very strict processing accuracy is required and the cost is greatly increased. Further, in order to remove the entire capsule only by the dissolution treatment, it takes a long time because the outer capsule is thick, and there is a concern that the dissolution liquid may adversely affect the fiber-reinforced metal hollow strut component. Therefore, by roughly machining the outer capsule to the same thickness as the inner capsule and then performing the melting treatment, it is possible to reduce the machining cost, shorten the melting treatment time, and improve the quality of the hollow strut parts. It is a thing.
【0017】本発明の繊維強化金属製中空ストラット部
品の製造方法に於いて、成形用カプセル装置の内部に繊
維強化金属素材を充填すると共に、その両端部に端末金
具を嵌着して封塞し、熱間等方圧成形を行って、繊維強
化金属素材の複合化成形と同時に端末金具を拡散接合し
た場合、端末金具の取付工程が簡略化されると共に、繊
維強化金属素材の特性劣化を抑制できる。即ち、従来法
だと中空ストラット管と端末金具をろう付けを用いて取
り付けていた為、繊維強化金属素材に2回の熱履歴が加
わり、繊維強化金属素材の特性劣化が懸念され、また工
程が2工程となり、コストアップの要因となっていたも
のが解消される。In the method of manufacturing a fiber-reinforced metal hollow strut component of the present invention, the inside of the molding capsule device is filled with the fiber-reinforced metal material, and both ends are fitted with terminal fittings for sealing. , When hot isostatic pressing is performed and the end fittings are diffusion-bonded at the same time as the composite forming of the fiber reinforced metal material, the mounting process of the end fittings is simplified and the deterioration of the characteristics of the fiber reinforced metal material is suppressed. it can. That is, in the conventional method, since the hollow strut tube and the terminal fitting are attached by brazing, heat history is added twice to the fiber reinforced metal material, and there is a concern that the characteristics of the fiber reinforced metal material may deteriorate, and the process The number of processes is two, which eliminates the factor that increased the cost.
【0018】[0018]
【実施例】本発明の繊維強化金属製中空ストラット部品
の製造方法の実施例を図によって説明する。EXAMPLE An example of the method for producing a fiber-reinforced metal hollow strut component according to the present invention will be described with reference to the drawings.
【0019】図1及び図2は本発明の第1の実施例を示
すもので、繊維強化金属製中空ストラット部品の製造方
法に使用されるカプセル装置6′は、外側カプセル1′
と内側カプセル2′とから成る。外側カプセル1′と内
側カプセル2′は、共に円筒形で、互いに同軸に配置さ
れている。外側カプセル1′は、内側カプセル2′より
も肉厚を厚く、本例の場合3倍程度に厚くしてあり、両
カプセル1′,2′の材質は軟鋼となしてある。繊維強
化金属素材3′は、図3に示すように直径75〜150
μmのセラミックス製連続繊維,本例の場合140μm
のSiC繊維7と厚さ100μmのTi−15V−3C
r−3Al−3Snよりなる合金箔8を組合せた複合材
料である。この複合材料の詳細について述べると、大型
ドラム上に、一方向にフィラメント・ワイデングして整
列させたSiC繊維を、接着剤などを用いて繊維間を固
定した後、一端を切断して展開し、SiC繊維シートと
する。このSiC繊維シート一層と前記Ti合金箔一枚
を重ね、必要ならば適宜接着剤を用いて固定したもので
ある。このシート状の繊維強化金属素材3′を成形用カ
プセル装置6′の内部に充填するには、図3に示すよう
にSiC繊維7を隣り合ったSiC繊維7と夫々一定間
隔ずらして、本例の場合内側カプセル2′を1周乃至2
周する間に不連続となるように20〜30mmずつずら
して切断の上、内側カプセル2′にSiC繊維7が斜向
するようにカプセルの長手方向に対して30〜60度の
角度を付けてシート状の繊維強化金属素材3′を巻き付
けて積層し、外側カプセル1′の内部に挿入する。前記
シート状の繊維強化金属素材3′を成形用カプセル装置
6′の内部に充填する他の方法としては、シート状の繊
維強化金属素材3′中の一部のSiC繊維7を外側カプ
セル1′の内面に接する位置に斜向するように角度を付
けて巻いて積層して配し、その内面に残りのシート状の
繊維強化金属素材3′中のSiC繊維7をストラットの
長手方向と繊維方向が一致した方向に巻きつけた内側カ
プセル2′を嵌合する。1 and 2 show a first embodiment of the present invention, in which a capsule device 6'used in a method for manufacturing a fiber-reinforced metal hollow strut component comprises an outer capsule 1 '.
And the inner capsule 2 '. The outer capsule 1'and the inner capsule 2'are both cylindrical and are arranged coaxially with each other. The outer capsule 1'is thicker than the inner capsule 2 ', which is about three times thicker in this example, and the materials of both capsules 1', 2'are made of mild steel. The fiber-reinforced metal material 3'has a diameter of 75 to 150 as shown in FIG.
μm ceramic continuous fiber, 140 μm in this example
SiC fiber 7 and Ti-15V-3C with a thickness of 100 μm
It is a composite material in which an alloy foil 8 made of r-3Al-3Sn is combined. Explaining the details of this composite material, SiC fibers aligned by filament-widing in one direction on a large drum are fixed between the fibers with an adhesive or the like, and then one end is cut and expanded. It is a SiC fiber sheet. One layer of this SiC fiber sheet and one sheet of the above Ti alloy foil are superposed, and if necessary, they are fixed by using an adhesive. In order to fill the sheet-shaped fiber-reinforced metal material 3 ′ into the molding capsule device 6 ′, as shown in FIG. 3, the SiC fibers 7 are displaced from the adjacent SiC fibers 7 by a constant distance, respectively, and this embodiment is used. In the case of 1 to 2 rounds of the inner capsule 2 '
The cutting is performed by shifting by 20 to 30 mm so as to be discontinuous during the circumference, and the inner capsule 2'is inclined at an angle of 30 to 60 degrees with respect to the longitudinal direction of the capsule so that the SiC fiber 7 is obliquely inclined. The sheet-shaped fiber-reinforced metal material 3'is wound and laminated, and is inserted into the outer capsule 1 '. As another method of filling the sheet-shaped fiber-reinforced metal material 3'into the molding capsule device 6 ', a part of the SiC fibers 7 in the sheet-shaped fiber-reinforced metal material 3'is filled in the outer capsule 1'. Of the sheet-like fiber-reinforced metal material 3 ', and the SiC fibers 7 in the remaining sheet-shaped fiber-reinforced metal material 3'are arranged on the inner surface of the struts in the longitudinal direction and the fiber direction. The inner capsule 2'wound in the same direction is fitted.
【0020】このように成形用カプセル装置6′内に繊
維強化金属素材3′を充填した後、成形用カプセル装置
6′の端部に図1に示すように端板9を溶接して成形用
カプセル装置6を封塞する。端板9はカプセル1′,
2′と同一の金属材料により構成されている。この端板
9には排気口10が形成されており、この排気口10か
ら成形用カプセル装置6′の内部の空気を排除して、該
成形用カプセル装置6′内を真空状態にする。次いで、
成形用カプセル6′を加熱しながら該カプセル装置6′
の周囲を高圧状態にする。加熱温度及び圧力は繊維の種
類及びマトリックス金属により異なるが、本実施例の場
合、Ti−15V−3Cr−3Al−3Snマトリック
スの拡散接合可能な温度領域、即ち900℃〜950℃
で、ガス圧100〜200MPaを、30〜60分間負
荷する。加熱により外側カプセル1′及び内側カプセル
2′の剛性が低下し、変形が容易な状態となる。成形用
カプセル6′の周囲に与えられる圧力により、内側カプ
セル2′が半径方向外向きに膨らむように変形し、内部
の繊維強化金属素材3′に成形圧力を与える。外側カプ
セル1′は内側カプセル2′よりも肉厚を3倍程度厚く
してあるので、該外側カプセル2′はほとんど変形せ
ず、変形は主として内側カプセル2′のみに生じること
になる。従って、成形品である繊維強化金属製中空スト
ラット部品の外周面は、外側カプセル1′の内面により
精度良く成形される。After filling the fiber-reinforced metal material 3'in the molding capsule device 6'in this manner, the end plate 9 is welded to the end portion of the molding capsule device 6'as shown in FIG. 1 for molding. The capsule device 6 is closed. The end plate 9 is a capsule 1 ',
It is made of the same metal material as 2 '. An exhaust port 10 is formed in the end plate 9, and the air in the molding capsule device 6'is removed from the exhaust port 10 to make the inside of the molding capsule device 6'a vacuum state. Then
The capsule device 6'while heating the molding capsule 6 '.
High pressure around. The heating temperature and pressure differ depending on the type of fiber and the matrix metal, but in the case of this example, the temperature range in which the diffusion bonding of the Ti-15V-3Cr-3Al-3Sn matrix is possible, that is, 900 ° C to 950 ° C.
Then, a gas pressure of 100 to 200 MPa is applied for 30 to 60 minutes. The heating lowers the rigidity of the outer capsule 1'and the inner capsule 2 ', so that the outer capsule 1'and the inner capsule 2'are easily deformed. By the pressure applied around the molding capsule 6 ', the inner capsule 2'deforms so as to expand outward in the radial direction, and the molding pressure is applied to the fiber-reinforced metal material 3'inside. Since the outer capsule 1'is three times thicker than the inner capsule 2 ', the outer capsule 2'is hardly deformed, and the deformation mainly occurs only in the inner capsule 2'. Therefore, the outer peripheral surface of the fiber-reinforced metal hollow strut component, which is a molded product, is more accurately molded by the inner surface of the outer capsule 1 '.
【0021】成形後、繊維強化金属製中空ストラット部
品を取り出す為にカプセル1′,2′の除去が行われる
が、本例の場合は、内側カプセル2′と同程度の厚さに
なるまでの機械加工による外側カプセル1′の余肉切除
と処理液中への浸漬によるカプセル1′,2′の溶解除
去が行われる。処理液の一例を下記の表1に示す。After the molding, the capsules 1'and 2'are removed to take out the fiber-reinforced metal hollow strut parts. In the case of this example, the capsules 1'and 2'are removed to the same thickness as the inner capsule 2 '. The outer capsule 1'is excised by machining and the capsules 1 ', 2'are dissolved and removed by immersion in the treatment liquid. An example of the treatment liquid is shown in Table 1 below.
【0022】[0022]
【表1】 *:ミーリング速度調整の為適量添加する[Table 1] *: Add an appropriate amount to adjust the milling speed
【0023】こうしてカプセル1′,2′を除去して取
り出した繊維強化金属製中空ストラット部品は、カプセ
ル1′,2′と繊維強化金属素材3′との反応や焼き付
きが無いので品質が良く、また外形寸法の精度が高かっ
た。この中空ストラット部品の肉厚方向の断面組織を図
4に示す。The hollow fiber-reinforced metal strut parts obtained by removing the capsules 1'and 2'in this manner are of good quality because there is no reaction or seizure between the capsules 1'and 2'and the fiber-reinforced metal material 3 '. Moreover, the accuracy of the external dimensions was high. The cross-sectional structure in the wall thickness direction of this hollow strut part is shown in FIG.
【0024】前記Ti合金マトリックスの繊維強化金属
素材3′に端末金具を取り付けるには、繊維強化金属素
材3′の複合化時の熱間等方圧成形の高温、高圧を利用
して、複合化成形と同時に拡散接合する。複合化でもT
i合金箔同士の拡散接合を利用している為、Ti合金マ
トリックスの繊維強化金属素材3′の複合化条件と端末
金具の接合条件は一致している。この接合では繊維強化
金属素材3′の表面マトリックスと端末金具の接合とな
る為、両者の間の応力伝達はせん断力が支配的になる。
このせん断力を伝達する具体的な接合様式の例を図5の
a,b,cに示す。図中、3′は繊維強化金属素材、1
1は端末金具である。これらの接合様式は、中空ストラ
ットの使用条件によって選択、または組み合わせて用い
ることが可能である。このように繊維強化金属素材3′
の複合化成形と端末金具11の拡散接合をすることによ
り、端末金具11の取付工程が簡略化されると共に、繊
維強化金属素材3′の特性劣化が抑制できた。In order to attach the terminal fitting to the fiber-reinforced metal material 3'of the Ti alloy matrix, the high temperature and high pressure of the hot isostatic pressing at the time of compounding the fiber-reinforced metal material 3'are used to carry out the compounding. Diffusion bonding is performed simultaneously with molding. Even in compounding T
Since the diffusion bonding of the i alloy foils is used, the compounding conditions of the Ti alloy matrix fiber reinforced metal material 3 ′ and the bonding conditions of the terminal fittings are the same. In this joining, since the surface matrix of the fiber reinforced metal material 3'and the end fitting are joined, the shear force is dominant in the stress transmission between the two.
Examples of specific joining modes for transmitting this shearing force are shown in a, b, c of FIG. In the figure, 3'is a fiber-reinforced metal material, 1
1 is a terminal fitting. These joining modes can be selected or used in combination depending on the usage conditions of the hollow strut. Fiber-reinforced metal material 3 '
By performing the composite molding of 1 and the diffusion joining of the end fitting 11, the mounting process of the end fitting 11 was simplified, and the characteristic deterioration of the fiber-reinforced metal material 3'was suppressed.
【0025】前記実施例は、繊維強化金属素材3′のマ
トリックス金属としてTi合金を使用したが、これに限
るものではなく、Ti−Al系金属間化合物でも良い。
また、上記マトリックス金属は、Ti合金箔8である
が、強化繊維に対するマトリックス金属の溶射や強化繊
維に対するマトリックス金属粉末の充填を行った後シー
ト状に成形したものでも良い。さらに、強化繊維として
SiC繊維7を用いているが、Al203繊維やボロン
系の繊維の他、金属繊維でも良い。また、上記実施例は
円筒形の中空ストラット部品の製造の場合であるが、多
角形の中空ストラット部品の製造にも応用できる。In the above embodiment, the Ti alloy was used as the matrix metal of the fiber-reinforced metal material 3 ', but the present invention is not limited to this, and a Ti-Al intermetallic compound may be used.
Further, although the above-mentioned matrix metal is the Ti alloy foil 8, it may be formed into a sheet after the thermal spraying of the matrix metal on the reinforcing fibers and the filling of the matrix metal powder on the reinforcing fibers. Furthermore, although SiC fiber 7 is used as the reinforcing fiber, metal fiber other than Al203 fiber, boron fiber, and the like may be used. Further, although the above-mentioned embodiment is a case of manufacturing a cylindrical hollow strut part, it can be applied to manufacture of a polygonal hollow strut part.
【0026】[0026]
【発明の効果】以上の通り本発明の繊維強化金属製中空
ストラット部品の製造方法によれば、成形用カプセル装
置のカプセル構成の簡素化と共に、品質が良く外形寸法
精度の高い繊維強化金属製中空ストラット部品を得るこ
とができる。また、内側カプセルの拡管方向への変形が
妨げられず、成形用カプセル装置内の繊維強化金属素材
に成形圧力を伝達できて成形不良が生じることがない。
さらに成形した繊維強化金属製中空ストラット部品の取
り出し時の内面加工などの機械加工が大幅に減少し、工
程の簡素化,低コスト化を達成できる。さらにまた繊維
強化金属素材の複合成形化と同時に端末金具の取付けを
行うことができて、端末金具の取付工程が簡略化され、
繊維強化金属素材の特性劣化が抑制される。As described above, according to the method for producing a fiber-reinforced metal hollow strut component of the present invention, the fiber-reinforced metal hollow having a good quality and a high external dimension accuracy can be realized while simplifying the capsule structure of the molding capsule device. Strut parts can be obtained. Further, the deformation of the inner capsule in the tube expanding direction is not hindered, the molding pressure can be transmitted to the fiber-reinforced metal material in the molding capsule device, and the molding failure does not occur.
Further, machining such as inner surface machining at the time of taking out the molded fiber-reinforced metal hollow strut part is significantly reduced, and the process can be simplified and the cost can be reduced. Furthermore, it is possible to attach the terminal metal fittings simultaneously with the composite molding of the fiber reinforced metal material, which simplifies the mounting process of the terminal metal fittings.
Characteristic deterioration of the fiber reinforced metal material is suppressed.
【図1】本発明の繊維強化金属製中空ストラット部品の
製造方法を示す図である。FIG. 1 is a diagram showing a method for manufacturing a fiber-reinforced metal hollow strut component of the present invention.
【図2】図1のA−A線断面図である。FIG. 2 is a sectional view taken along the line AA of FIG.
【図3】本発明の製造方法に於いて使用する繊維強化金
属素材と、これを成形用カプセル装置内に充填する為に
内側カプセルに巻き付けて積層する状態を示す図であ
る。FIG. 3 is a diagram showing a fiber-reinforced metal material used in the manufacturing method of the present invention and a state in which the fiber-reinforced metal material is wrapped around an inner capsule to be stacked so as to be filled in a molding capsule device.
【図4】本発明の製造方法により製造された繊維強化金
属製中空ストラット部品の肉厚方向の断面組織を示す図
である。FIG. 4 is a view showing a cross-sectional structure in the thickness direction of a fiber-reinforced metal hollow strut component manufactured by the manufacturing method of the present invention.
【図5】a,b,c共に繊維強化金属素材と端末金具の
接合様式を示す図である。FIG. 5 is a diagram showing a joining mode of a fiber-reinforced metal material and a terminal fitting for all of a, b, and c.
【図6】従来の繊維強化金属製中空ストラット部品の製
造方法を示す図である。FIG. 6 is a diagram showing a method for manufacturing a conventional fiber-reinforced metal hollow strut component.
【図7】図6のB−B線断面図である。7 is a cross-sectional view taken along the line BB of FIG.
1′ 外側カプセル 2′ 内側カプセル 3′ 繊維強化金属素材 6′ 成形用カプセル装置 7 SiC繊維 8 Ti合金箔 9 端板 10 排気口 11 端末金具 1'Outer capsule 2'Inner capsule 3'Fiber reinforced metal material 6'Molding capsule device 7 SiC fiber 8 Ti alloy foil 9 End plate 10 Exhaust port 11 Terminal fitting
───────────────────────────────────────────────────── フロントページの続き (72)発明者 中谷 浩 岐阜県各務原市川崎町1番地 川崎重工業 株式会社岐阜工場内 (72)発明者 青木 敏幸 岐阜県各務原市川崎町1番地 川崎重工業 株式会社岐阜工場内 ─────────────────────────────────────────────────── ─── Continuation of the front page (72) Inventor Hiroshi Nakatani 1 Kawasaki-cho, Kakamigahara-shi, Gifu Kawasaki Heavy Industries, Ltd. Gifu factory (72) Inventor Toshiyuki Aoki Kawasaki-cho, Kakamigahara, Gifu Kawasaki Heavy Industries, Ltd. Gifu factory Within
Claims (6)
る成形用カプセル装置の内部に、繊維強化金属素材を充
填,封塞し、加熱条件下で前記カプセル装置の外部から
加圧して熱間等方圧成形を行い、然る後カプセルの除去
及び中空ストラットの取り出しを行う繊維強化金属製中
空ストラット部品の製造方法に於いて、前記カプセル装
置の外側カプセルを内側カプセルよりも肉厚を厚くする
と共に内外側カプセルの材質を軟鋼となして、熱間等方
圧成形を行うことを特徴とする繊維強化金属製中空スト
ラット部品の製造方法。1. A hot-molding encapsulation device formed of an inner capsule and an outer capsule is filled and sealed with a fiber-reinforced metal material and pressurized from outside the encapsulation device under heating conditions. In the method of manufacturing a fiber-reinforced metal hollow strut component in which pressure molding is performed and then the capsule is removed and the hollow strut is taken out, the outer capsule of the capsule device is made thicker than the inner capsule and A method of manufacturing a fiber-reinforced metal hollow strut component, characterized in that the outer capsule is made of mild steel and hot isostatic pressing is performed.
ラット部品の製造方法に於いて、成形用カプセル装置の
内部への繊維強化金属素材の充填が、シート状の繊維強
化金属素材中の繊維を隣り合った繊維と夫々一定間隔ず
らして切断の上、内側カプセルに繊維が斜向するように
シート状の繊維強化金属素材を巻き付けて積層し、外側
カプセルの内部に挿入することを特徴とする繊維強化金
属製中空ストラット部品の製造方法。2. The method for producing a fiber-reinforced metal hollow strut component according to claim 1, wherein the fiber-reinforced metal material is filled in the molding capsule device by a fiber in the sheet-shaped fiber-reinforced metal material. Are separated from adjacent fibers by a certain distance, cut, and then wrapped in a sheet-shaped fiber-reinforced metal material so that the fibers are obliquely wrapped around the inner capsule, laminated, and inserted into the outer capsule. A method for manufacturing a fiber-reinforced metal hollow strut component.
ラット部品の製造方法に於いて、成形用カプセル装置の
内部への繊維強化金属素材の充填が、シート状の繊維強
化金属素材中の一部の繊維を外側カプセルの内面に接す
る位置に斜向して巻くように積層して配し、その内面に
残りのシート状の繊維強化金属素材中の繊維をストラッ
トの長手方向と繊維方向が一致した方向に巻きつけた内
側カプセルを嵌合することを特徴とする繊維強化金属製
中空ストラット部品の製造方法。3. The method of manufacturing a fiber-reinforced metal hollow strut component according to claim 1, wherein the filling of the fiber-reinforced metal material into the molding capsule device is performed by using one of the sheet-shaped fiber-reinforced metal materials. The fibers of the part are laminated so as to be wound obliquely at the position where they contact the inner surface of the outer capsule, and the fibers in the remaining sheet-shaped fiber-reinforced metal material are aligned on the inner surface in the longitudinal direction of the strut and the fiber direction. A method for manufacturing a fiber-reinforced metal hollow strut component, which comprises fitting an inner capsule wound in a predetermined direction.
化金属製中空ストラット部品の製造方法に於いて、熱間
等方圧成形が、繊維強化金属素材の金属マトリックスの
拡散接合可能な温度領域で、100〜200MPaのガ
ス圧を、30分〜60分間負荷する条件で行われること
を特徴とする繊維強化金属製中空ストラット部品の製造
方法。4. The method for producing a fiber-reinforced metal hollow strut component according to any one of claims 1 to 3, wherein hot isostatic pressing enables diffusion bonding of a metal matrix of a fiber-reinforced metal material. A method for producing a fiber-reinforced metal hollow strut component, characterized in that the gas pressure of 100 to 200 MPa is applied in a temperature region for 30 to 60 minutes.
化金属製中空ストラット部品の製造方法に於いて、カプ
セルの除去が、内側カプセルと同程度の厚さになるまで
の機械加工による外側カプセルの余肉切除と処理液中へ
の浸漬によるカプセルの溶解除去であることを特徴とす
る繊維強化金属製中空ストラット部品の製造方法。5. The method for manufacturing a fiber-reinforced metal hollow strut component according to claim 1, wherein the removal of the capsule is performed by machining until the thickness of the capsule is about the same as that of the inner capsule. A method for producing a fiber-reinforced metal hollow strut component, which comprises removing the excess thickness of the outer capsule and dissolving and removing the capsule by immersion in a treatment liquid.
化金属製中空ストラット部品の製造方法に於いて、成形
用カプセル装置の内部に繊維強化金属素材を充填すると
共に、その両端部に端末金具を嵌着して封塞し、熱間等
方圧成形を行って、繊維強化金属素材の複合化成形と同
時に端末金具を拡散接合することを特徴とする繊維強化
金属製中空ストラット部品の製造方法。6. The method for manufacturing a fiber-reinforced metal hollow strut component according to claim 1, wherein the fiber-reinforced metal material is filled inside the molding capsule device and both ends of the device are filled. A fiber-reinforced metal hollow strut part characterized by fitting and sealing a terminal metal fitting, performing hot isostatic pressing, and simultaneously diffusion-bonding the terminal metal fitting at the same time as composite molding of a fiber-reinforced metal material. Production method.