JPH08318602A - Propylene resin laminated foamed sheet for molding - Google Patents
Propylene resin laminated foamed sheet for moldingInfo
- Publication number
- JPH08318602A JPH08318602A JP7090276A JP9027695A JPH08318602A JP H08318602 A JPH08318602 A JP H08318602A JP 7090276 A JP7090276 A JP 7090276A JP 9027695 A JP9027695 A JP 9027695A JP H08318602 A JPH08318602 A JP H08318602A
- Authority
- JP
- Japan
- Prior art keywords
- propylene
- molding
- resin
- sheet
- foamed sheet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、容器等の成形品を製造
する際の熱成形に用いられる成形用プロピレン系樹脂積
層発泡シートに関し、詳しくは、連続成形において、成
形不良を防止し強度及び外観の優れた成形品を得るのに
好適な、プロピレン系樹脂発泡シートにプロピレン系樹
脂延伸フィルムを積層して複合化された、成形用発泡シ
ートに関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a propylene-based resin laminated foam sheet for molding, which is used for thermoforming when producing a molded article such as a container. The present invention relates to a foaming sheet for molding, which is suitable for obtaining a molded article having an excellent appearance, and is made into a composite by laminating a propylene-based resin stretched film on a propylene-based resin foaming sheet.
【０００２】[0002]
【従来の技術】従来から容器等を成形するための成形用
発泡シートとして、プロピレン系樹脂発泡シートが公知
である。例えば、このような発泡シートとして本出願人
は先に特定の構造とドローダウン性を持つプロピレン系
樹脂を使用してなる発泡シートを出願している（特開平
５−２３０２５５号公報）。2. Description of the Related Art A propylene-based resin foam sheet has been conventionally known as a foam sheet for molding for molding a container or the like. For example, as such a foamed sheet, the present applicant previously applied for a foamed sheet using a propylene-based resin having a specific structure and drawdown property (Japanese Patent Laid-Open No. 5-230255).
【０００３】この発泡シートは、長鎖分岐を有すると共
に特定のドローダウン性を持つプロピレン系樹脂を基材
樹脂として用い、該樹脂を押出機内て発泡剤等と溶融混
練した後、低圧下に押出して発泡せしめてなる、密度
０．３〜０．０６ｇ／ｃｍ3 、厚み１〜３ｍｍを有し、
表面スキン層の厚みと気泡の平均膜厚との間に、表面ス
キン層の厚み／気泡の平均膜厚≦２なる関係を満たすと
共に、厚み方向の気泡膜数が２〜１５であることを特徴
とするものである。This foamed sheet uses a propylene resin having a long chain branch and a specific drawdown property as a base resin, and melts and kneads the resin with a foaming agent in an extruder and then extrudes it under a low pressure. Has a density of 0.3 to 0.06 g / cm 3 and a thickness of 1 to 3 mm,
The thickness of the surface skin layer and the average film thickness of the bubbles satisfy the relationship of the thickness of the surface skin layer / the average film thickness of the bubbles ≦ 2, and the number of bubble films in the thickness direction is 2 to 15. It is what
【０００４】上記の発明は、特定の構造とドローダウン
性を持つプロピレン系樹脂を基材樹脂として用いたこと
により、それ以前の無架橋プロピレン系樹脂の押出発泡
シートが、密度０．２ｇ／ｃｍ3 を超える低発泡倍率の
ものか或いは密度０．０１３ｇ／ｃｍ3 未満の高発泡倍
率のものしか得られなかったのが、密度が０．４５〜
０．０６ｇ／ｃｍ3 の押出発泡シートが容易に得られる
ものである。又、上記の発泡シートは、密度及び厚みを
特定の範囲に規定し、表面スキン層の厚みと気泡の平均
膜厚との間に特定の関係が成り立つ範囲とし、厚み方向
の気泡膜数を２〜１５としたことにより、断熱性、成形
品の保形性、及び成形性等のバランスのとれたものが得
られる。In the above invention, the propylene resin having a specific structure and drawdown property is used as the base resin, so that the extruded foamed sheet of the non-crosslinked propylene resin before that has a density of 0.2 g / cm. Only a low expansion ratio of more than 3 or a high expansion ratio of less than 0.013 g / cm 3 was obtained.
An extruded foam sheet of 0.06 g / cm 3 can be easily obtained. Further, in the above-mentioned foamed sheet, the density and the thickness are defined in a specific range, and the specific relationship is established between the thickness of the surface skin layer and the average film thickness of the bubbles, and the number of bubble films in the thickness direction is 2 By setting it to 15 or less, a product having a well-balanced heat insulating property, shape retaining property of the molded product, and moldability can be obtained.
【０００５】上記の成形用発泡シートは、耐熱性、耐水
性、耐薬品性、断熱性、保形性、剛性等に優れているた
め、例えば食品を収納したままで電子レンジ内で直接加
熱する用途に利用される、電子レンジ用食品容器等の成
形用シートとして好適なものであった。またこれらの成
形用発泡シートは、深絞り成形性にも優れているため、
底の深い容器を成形した場合でも、容器が部分的（特に
底部と側壁との境界部分）に極端に薄くなって穴が開い
たりすることがない優れたものであった。Since the above foam sheet for molding has excellent heat resistance, water resistance, chemical resistance, heat insulation, shape retention, rigidity, etc., for example, it is directly heated in a microwave oven while containing food. It was suitable as a sheet for molding such as a food container for microwave oven, which is used for various purposes. In addition, since these foamed sheets for molding are also excellent in deep drawability,
Even when a container having a deep bottom was formed, the container was excellent in that it did not become extremely thin locally (particularly at the boundary between the bottom and the side wall) and no holes were formed.
【０００６】また本出願人は、上記のプロピレン系樹脂
発泡シートを改良して、過酷な深絞り成形や複雑な成形
等を可能とするために、プロピレン系樹脂発泡シートに
特定の厚みのプロピレン系樹脂フィルムを積層して複合
化してなる成形用積層発泡シートを提案している（特開
平６−９０６号公報）。しかしながら、上記の成形用発
泡シートを用い連続成形機により成形を行う場合、下記
の如き問題があった。[0006] The present applicant has further improved the above-mentioned propylene-based resin foamed sheet to make it possible to perform severe deep-drawing molding and complicated molding. A laminated foam sheet for molding, which is formed by laminating resin films to form a composite, has been proposed (JP-A-6-906). However, when molding is performed by a continuous molding machine using the foaming sheet for molding described above, there are the following problems.
【０００７】[0007]
【発明が解決しようとする課題】従来のプロピレン系樹
脂発泡シートを用いた容器等の連続成形方法は、例えば
特開平６−２７８２００号公報の〔従来の技術〕の欄に
も記載されているように、長尺な発泡シートの両端をク
ランプした搬送手段にて発泡シートを次々に搬送し、加
熱ゾーンでオーブンによって予め加熱し成形可能な状態
に軟化させた後、該発泡シートを成形ゾーンに移送し、
上記の軟化した発泡シートを所定形状に成形することで
成形品が得られる。A conventional method for continuously molding a container or the like using a propylene-based resin foamed sheet is described in, for example, Japanese Patent Application Laid-Open No. 6-278200, [Prior Art]. In addition, the foamed sheets are conveyed one after another by a conveying means that clamps both ends of a long foamed sheet, preheated by an oven in a heating zone to soften the foamable sheet, and then the foamed sheet is transferred to a molding zone. Then
A molded product is obtained by molding the softened foamed sheet into a predetermined shape.
【０００８】ところが、上記従来の連続成形方法におい
て、特開平６−２７８２００号公報にも記載されている
ように、発泡シートを加熱ゾーンにおいて加熱すると、
加熱軟化したシートは両端がクランプによって固定され
ているため、熱膨張（二次発泡）により波打ち現象（コ
ルゲート）が発生する。このコルゲートは加熱ムラの原
因となり、加熱の不均一な状態の発泡シートが成形ゾー
ンに移送され成形されると、得られた成形品は、加熱ム
ラのため、場所によって成形品の状態が異なったり、肉
厚が不均一で強度に劣るものであった。However, in the conventional continuous molding method described above, when the foamed sheet is heated in the heating zone as described in JP-A-6-278200,
Since both ends of the heat-softened sheet are fixed by the clamps, a corrugation phenomenon occurs due to thermal expansion (secondary foaming). This corrugation causes uneven heating, and when a foamed sheet with uneven heating is transferred to the molding zone and molded, the resulting molded product may have different heating conditions due to uneven heating. The thickness was uneven and the strength was poor.
【０００９】又、発泡シートにコルゲートが生じた状態
で成形されると、成形品ににシワ（ブリッジ）の発生が
見られることもあり、外観的にも満足しうるものではな
かった。尚、単発成形の場合にも、成形用発泡シートが
固定されているため、加熱した際に連続成形の場合と同
様にコルゲートが発生するが、成形面積が小さく、１ケ
取りのため、加熱ムラが発生したり、ブリッジが発生す
ることはなく、大きな問題とはならなかった。Further, if the foamed sheet is molded in a state where corrugations are formed, wrinkles (bridges) may be observed in the molded product, which is not satisfactory in appearance. Even in the case of single-shot molding, since the foaming sheet for molding is fixed, corrugates are generated when heated, similar to the case of continuous molding, but the molding area is small, and the heating unevenness is caused by one piece. It did not cause any problems or bridges, and it was not a big problem.
【００１０】上記の問題に対し、特開平６−２７８２０
０号公報の発明では、成形用発泡シートを加熱ゾーンで
成形可能な状態に加熱軟化した後に、発泡シートの搬送
方向と直交する幅方向に発泡シートを拡張した後、成形
ゾーンで所望形状に成形する方法を採用している。その
結果、上記発明では、発泡シートが成形される前に波打
った部分が引き延ばされるので、肉厚が均一で強度を有
し、外観のきれいな、強度、品質ともに優れた発泡ポリ
プロピレンの成形品が得られるとされている。To solve the above problem, Japanese Patent Laid-Open No. 6-27820
In the invention of Japanese Patent No. 0, the foamed sheet for molding is heated and softened in a heating zone to a moldable state, and then the foamed sheet is expanded in the width direction orthogonal to the conveying direction of the foamed sheet, and then molded into a desired shape in the molding zone. Is adopted. As a result, in the above invention, since the corrugated portion is stretched before the foamed sheet is molded, the molded product of foamed polypropylene having a uniform thickness and strength, a clean appearance, strength and excellent quality. Is said to be obtained.
【００１１】しかしながら、上記の発明のように、軟化
した発泡シートを拡張して成形ゾーンで成形するには、
公報に記載されているように特殊な装置を必要とするも
のである。即ち、上記の発明では、シートをクランプす
るレール状の搬送手段として、加熱ゾーンから成形ゾー
ンに移る間に搬送方向に進むに連れてシートの拡張幅に
拡がるような連続した搬送チェーンを設置する必要があ
り、従来の成形設備を使用して成形を行うことはできな
い。一般に、容器等の成形において、品質及び外観の良
好な成形品が得られるとしても、製造設備を改良しなけ
ればならないのでは、設備投資に莫大な経費がかかって
しまい、成形品のコストアップとなるため、あまり実用
的ではない。However, in order to expand the softened foam sheet and mold it in the molding zone as in the above invention,
It requires a special device as described in the publication. That is, in the above invention, it is necessary to install, as the rail-shaped conveying means for clamping the sheet, a continuous conveying chain that expands to the expanded width of the sheet as it advances in the conveying direction while moving from the heating zone to the forming zone. Therefore, molding cannot be performed using conventional molding equipment. Generally, in molding a container or the like, even if a molded product with good quality and appearance can be obtained, if the manufacturing equipment must be improved, a huge cost will be required for the equipment investment, and the cost of the molded product will increase. Therefore, it is not very practical.
【００１２】本発明者らは、上記のような製造設備の改
良を行わずに、従来の成形装置を利用して物性及び外観
の優れたプロピレン系樹脂発泡シートの成形品を得るこ
とを可能とするために、成形に用いるプロピレン系樹脂
発泡シートに着目した。本発明は、連続成形時における
コルゲートの発生を防止し、加熱ムラやブリッジ等をな
くし、物性及び外観の優れた成形品を得ることを可能と
する、成形用プロピレン系樹脂発泡シートを提供するこ
とを目的としている。The inventors of the present invention can obtain a molded product of a propylene-based resin foam sheet having excellent physical properties and appearance by using a conventional molding apparatus without improving the manufacturing equipment as described above. In order to do so, attention was paid to the propylene-based resin foam sheet used for molding. The present invention provides a propylene-based resin foam sheet for molding, which prevents generation of corrugations during continuous molding, eliminates uneven heating and bridges, and makes it possible to obtain a molded article having excellent physical properties and appearance. It is an object.
【００１３】[0013]
【課題を解決するための手段】即ち本発明は、（１）ド
ローダウン性が６０ｍ／分以下である無架橋プロピレン
系樹脂を基材樹脂とするプロピレン系樹脂発泡シート
と、該発泡シートの少なくとも片面に積層された厚さ１
０〜２００μｍのプロピレン系樹脂延伸フィルムとから
なることを特徴とする成形用プロピレン系樹脂積層発泡
シート、（２）プロピレン系樹脂発泡シートが、厚さ１
〜５ｍｍ、密度０．０６ｇ／ｃｍ3 以上〜０．４５ｇ／
ｃｍ3 未満である上記（１）の成形用プロピレン系樹脂
積層発泡シート、（３）プロピレン系樹脂延伸フィルム
が、少なくとも一方向の収縮応力が１０〜２００ｇ／５
ｍｍである上記（１）又は（２）記載の成形用プロピレ
ン系樹脂積層発泡シート、（３）プロピレン系樹脂延伸
フィルムが、発泡フィルムである上記（１）、（２）又
は（３）記載の成形用プロピレン系樹脂積層発泡シー
ト、を要旨とするものである。Means for Solving the Problems That is, according to the present invention, (1) a propylene-based resin foamed sheet using a non-crosslinked propylene-based resin having a drawdown property of 60 m / min or less as a base resin, and at least the foamed sheet Thickness 1 laminated on one side
A propylene-based resin laminated foam sheet for molding, comprising (2) a propylene-based resin foamed sheet having a thickness of 1
~ 5 mm, density 0.06 g / cm 3 or more ~ 0.45 g /
The propylene-based resin laminated foam sheet for molding of (1) and the stretched propylene-based resin film (3) of less than cm 3 have a shrinkage stress of at least one direction of 10 to 200 g / 5.
The propylene-based resin laminated foam sheet for molding according to the above (1) or (2), which is mm, and the (3) propylene-based resin stretched film is a foamed film, according to the above (1), (2) or (3). The gist is a propylene-based resin laminated foam sheet for molding.
【００１４】以下、本発明を図面を用いて詳細に説明す
る。図１は本発明の成形用プロピレン系樹脂積層発泡シ
ートの１例を示す断面図である。図１に示すように本発
明の成形用プロピレン系樹脂積層発泡シート１（以下、
積層発泡シート１と略記することもある）は、プロピレ
ン系樹脂発泡シート２（以下、発泡シート２と略記する
こともある）と、該発泡シート２の片面に積層されたプ
ロピレン系樹脂延伸フィルム３（以下、延伸フィルム３
と略記することもある）とからなる。本発明において、
プロピレン系樹脂延伸フィルム３は発泡シート２の両面
に積層されていてもよい。The present invention will be described in detail below with reference to the drawings. FIG. 1 is a sectional view showing an example of a propylene-based resin laminated foam sheet for molding of the present invention. As shown in FIG. 1, a propylene-based resin laminated foam sheet for molding 1 (hereinafter,
The laminated foam sheet 1 may be abbreviated), the propylene resin foam sheet 2 (hereinafter also abbreviated as the foam sheet 2), and the propylene resin stretched film 3 laminated on one side of the foam sheet 2. (Hereinafter, stretched film 3
Sometimes abbreviated) and consists. In the present invention,
The propylene-based resin stretched film 3 may be laminated on both sides of the foamed sheet 2.
【００１５】本発明の積層発泡シート１は、プロピレン
系樹脂延伸フィルム３が積層されている構成を採用した
ことで、積層発泡シート１が連続成形時の熱膨張によっ
てコルゲートが発生しようとしても、プロピレン系樹脂
延伸フィルム３の収縮応力によって引っ張られるため、
積層発泡シート１全体が波うつことがなく、加熱ムラや
ブリッジが発生せず、強度、品質及び外観とも優れた成
形品が得られる。The laminated foamed sheet 1 of the present invention adopts a constitution in which the propylene-based resin stretched film 3 is laminated, so that even if the laminated foamed sheet 1 is subjected to thermal expansion during continuous molding, corrugates are likely to occur. Since it is pulled by the contraction stress of the stretched resin film 3,
The entire laminated foamed sheet 1 does not undulate, heating unevenness and bridges do not occur, and a molded product excellent in strength, quality and appearance can be obtained.
【００１６】プロピレン系樹脂発泡シート２は、厚さ１
〜５ｍｍのものを用いるのが好ましく、又、密度０．０
６ｇ／ｃｍ3 以上、０．４５ｇ／ｃｍ3 未満であるのが
好ましい。また、プロピレン系樹脂延伸フィルム３は、
厚さ１０〜２００μｍのものが用いられ、好ましくは２
０〜１５０μｍである。その理由は、以下の通りであ
る。発泡シート２の厚さが５ｍｍを超えると、成形の際
の均一加熱が難しくなって、成形性に悪影響を及ぼす。
また、発泡シート２の密度が０．４５ｇ／ｃｍ3以上の
場合には柔軟性が不足し、一方密度が０．０６ｃｍ3 未
満であると、積層発泡シート１から得られる成形品は、
例えば成形品としてラップフィルムで包装する魚肉用の
トレー等としては、保形性及び剛性等が不足する。また
延伸フィルム２の厚さが２００μｍを超えると、延伸フ
ィルム２をプロピレン系樹脂発泡シート２に積層するの
が困難になり、製造効率の点で問題がある。The propylene resin foam sheet 2 has a thickness of 1
It is preferable to use one having a diameter of ~ 5 mm and a density of 0.0
6 g / cm 3 or more, preferably less than 0.45 g / cm 3. In addition, the propylene-based resin stretched film 3
A film having a thickness of 10 to 200 μm is used, preferably 2
It is 0 to 150 μm. The reason is as follows. When the thickness of the foamed sheet 2 exceeds 5 mm, uniform heating during molding becomes difficult, which adversely affects the moldability.
When the density of the foamed sheet 2 is 0.45 g / cm 3 or more, flexibility is insufficient, while when the density is less than 0.06 cm 3 , the molded product obtained from the laminated foamed sheet 1 is
For example, as a tray for fish meat that is wrapped with a wrap film as a molded product, shape retention and rigidity are insufficient. If the thickness of the stretched film 2 exceeds 200 μm, it becomes difficult to laminate the stretched film 2 on the propylene-based resin foam sheet 2, which causes a problem in production efficiency.
【００１７】延伸フィルム３の収縮応力が１０ｇ／５ｍ
ｍ未満の場合は、収縮応力が小さすぎて、熱膨張して発
生するコルゲートを充分防止できない虞れがあり、又、
収縮応力が２００ｇ／５ｍｍを超えると、収縮応力が大
きすぎて延伸フィルムの伸びが悪く、成形品が裂けたり
する虞れがある。尚、延伸フィルム３は、無発泡のフィ
ルムであっても発泡フィルムであってもいずれでもよ
い。延伸フィルム３として発泡フィルムを用いた場合に
は、その発泡倍率は、１．１〜３倍が好ましく、更に好
ましくは１．１〜２倍であり、延伸フィルムの収縮応力
は発泡フィルムであっても未発泡フィルムであっても上
記の範囲が好ましい範囲である。延伸フィルム３の発泡
倍率が３倍を越える高い発泡倍率になると外観が低下す
る虞れがある。又、延伸フィルムとして上記発泡フィル
ムを用いた場合には、未発泡のフィルムを用いた場合と
比較して、フィルムを貼ったという感じがなくなって意
匠性が向上し、伸びが良好となって深絞り性が向上し、
外観の更に良好な成形品が得られる。The shrinkage stress of the stretched film 3 is 10 g / 5 m
If it is less than m, the shrinkage stress may be too small to sufficiently prevent the corrugation caused by thermal expansion.
When the shrinkage stress exceeds 200 g / 5 mm, the shrinkage stress is too large and the stretched film is poor in elongation, and the molded product may be torn. The stretched film 3 may be a non-foamed film or a foamed film. When a foamed film is used as the stretched film 3, the expansion ratio thereof is preferably 1.1 to 3 times, more preferably 1.1 to 2 times, and the contraction stress of the stretched film is that of the foamed film. The above range is a preferable range even for an unfoamed film. When the stretched film 3 has a high expansion ratio exceeding 3 times, the appearance may be deteriorated. In addition, when the above foamed film is used as the stretched film, compared to the case where an unfoamed film is used, the feeling of sticking the film disappears, the designability is improved, and the elongation becomes good and the depth is improved. Drawability is improved,
A molded product having a better appearance can be obtained.
【００１８】上記延伸フィルムを構成するポリプロピレ
ン系樹脂としては、ホモポリプロピレンや、プロピレン
を主成分とする（プロピレン成分を６０モル％以上含有
するもの。）プロピレン系ランダム共重合体、又、プロ
ピレン系ブロック共重合体、プロピレン系グラフト共重
合体が例示される。尚、本発明における延伸フィルム３
の収縮応力とは、下記の測定方法に基づくものである。
発泡シートへの積層に使用する延伸フィルムから、長さ
１０ｍｍ、幅５ｍｍのサンプルを切り出し、熱機械的分
析装置（ＴＭＡ）を使用し、フィルムサンプルの長さ方
向の両端を固定し、フィルムを１０℃／分の速度で昇温
して加熱する。加熱していくとフィルムは収縮しようと
するが、その収縮を妨げるに必要な荷重が前記装置によ
り測定される。この時の荷重の最大値を本発明における
収縮応力（ｇ／５ｍｍ）と称する。延伸フィルムの長手
方向の収縮応力を測定する場合には、フィルムサンプル
の長さ方向と延伸フィルムの長手方向を一致させ、ま
た、延伸フィルムの長手方向と直交する方向の収縮応力
を測定する場合には、フィルムサンプルの長さ方向と、
延伸フィルムの長手方向と直交する方向を一致させるよ
うにする。The polypropylene resin constituting the stretched film is homopolypropylene, a propylene-based random copolymer containing propylene as a main component (containing 60% by mole or more of propylene component), or a propylene-based block. Examples include copolymers and propylene-based graft copolymers. In addition, the stretched film 3 in the present invention
The shrinkage stress of is based on the following measuring method.
A sample with a length of 10 mm and a width of 5 mm was cut out from the stretched film used for laminating on the foamed sheet, and both ends in the length direction of the film sample were fixed using a thermomechanical analyzer (TMA) to make the film 10 The temperature is raised at a rate of ° C / min to heat. The film tries to shrink as it is heated, but the load necessary to prevent the shrinkage is measured by the device. The maximum value of the load at this time is called the shrinkage stress (g / 5 mm) in the present invention. When measuring the contraction stress in the longitudinal direction of the stretched film, the length direction of the film sample and the longitudinal direction of the stretched film are matched, and when measuring the contraction stress in the direction orthogonal to the longitudinal direction of the stretched film. Is the length direction of the film sample,
The direction orthogonal to the longitudinal direction of the stretched film is made to match.
【００１９】発泡シート２と延伸フィルム３の積層は、
エクストルージョンラミネート法（接着剤としての使
用）、又はサーマルラミネート法（接着剤なしの熱ラミ
ネート）、ホットメルト接着剤によるラミネート等の一
般的な方法により行うことができる。尚、上記の延伸フ
ィルム３の厚みは、エクストルージョンラミネート法及
びホットメルト接着剤等によるラミネートの接着剤の厚
みは含まない。The laminated structure of the foamed sheet 2 and the stretched film 3 is
It can be carried out by a general method such as an extrusion laminating method (use as an adhesive), a thermal laminating method (thermal laminating without an adhesive), laminating with a hot melt adhesive or the like. The thickness of the stretched film 3 does not include the thickness of the adhesive for lamination by the extrusion laminating method or hot melt adhesive.
【００２０】プロピレン系樹脂延伸フィルム３の基材樹
脂は、発泡シート１の基材樹脂として用いられる、後述
する特定のドローダウン性を有するプロピレン系樹脂と
同種の樹脂、又はそれ以外の通常のプロピレン系樹脂の
いずれを用いてもよい。通常のプロピレン系樹脂は、プ
ロピレン単独重合体、又はプロピレンと共重合可能な不
飽和結合を有するモノマーとの共重合体のいずれでもよ
く、共重合体の場合には、ブロック共重合体、ランダム
共重合体のいずれでもよい。上記のプロピレンと共重合
可能な不飽和結合を有するモノマーとしては、エチレ
ン、或いは１−ブテン、イソブチレン、１−ペンテン、
３−メチル−１−ブテン、１−ヘキセン、４−メチル−
１−ペンテン、３，４−ジメチル−１−ブテン、１−ヘ
プテン、３−メチル−１−ヘキセン等の炭素数４〜１０
のα−オレフィン等が挙げられる。The base resin of the propylene-based resin stretched film 3 is the same type of resin as the base resin of the foamed sheet 1 and having a specific drawdown property described later, or other usual propylene. Any of the system resins may be used. The usual propylene-based resin may be either a propylene homopolymer or a copolymer with a monomer having an unsaturated bond capable of copolymerizing with propylene, and in the case of a copolymer, a block copolymer or a random copolymer. Any of polymers may be used. The above-mentioned monomer having an unsaturated bond copolymerizable with propylene, ethylene, 1-butene, isobutylene, 1-pentene,
3-methyl-1-butene, 1-hexene, 4-methyl-
4-10 carbon atoms such as 1-pentene, 3,4-dimethyl-1-butene, 1-heptene, 3-methyl-1-hexene
.Alpha.-olefin and the like.
【００２１】発泡シート２は、ドローダウン性が６０ｍ
／分以下である無架橋プロピレン系樹脂を基材樹脂とす
るものであり、ドローダウン性は、好ましくは３０ｍ／
分以下であり、更に好ましくは１５ｍ／分以下である。
また、無架橋ポロピレン系樹脂の主鎖に長鎖分岐を有す
るものは、ドローダウン性を上記範囲に調整することが
容易であり好ましい。The foam sheet 2 has a drawdown property of 60 m.
/ Min or less is used as the base resin, and the drawdown property is preferably 30 m / min.
Min or less, more preferably 15 m / min or less.
In addition, a non-crosslinked polypropylene resin having a long chain branch in the main chain is preferable because it is easy to adjust the drawdown property within the above range.
【００２２】尚、上記のドローダウン性とは、２３０℃
に加熱した溶融ポリプロピレン系樹脂をノズル（口径
２．０９５ｍｍ、長さ８ｍｍ）より、一定速度（１０ｍ
ｍ／分）で紐状に押出し、次いで該紐状物を上記ノズル
の下方の張力検出プーリーの上方に位置する送りロール
を通過させた後、巻取りロールで巻取る一方で、巻取り
ロールの巻取り速度を徐々に増加させていって紐状物が
切断した時の紐状物の巻取り速度を言う。The above-mentioned drawdown property means 230 ° C.
The molten polypropylene resin heated to the nozzle (nozzle diameter 2.095 mm, length 8 mm) is fed at a constant speed (10 m
m / min), and then the string-shaped material is passed through a feed roll located above the tension detection pulley below the nozzle and then wound up by a winding roll, while The winding speed of the string-shaped material when the string-shaped material is cut while gradually increasing the winding speed.
【００２３】発泡シート２の基材樹脂として用いられる
無架橋ポリプロピレン系樹脂は、単独重合体、ブロック
共重合体、又はランダム共重合体のいずれであってもよ
いが、共重合体の場合には、プロピレン以外のオレフィ
ンを共重合体中に０．５〜３０重量％、特に好ましくは
１〜１０重量％の割合で含有せしめるのが好ましい。こ
の場合のオレフィンとしては、エチレン、或いは延伸フ
ィルムの基材樹脂として例示した炭素数４〜１０のα−
オレフィンを挙げることができ、これらは１種、又は２
種以上を組み合わせて使用することができる。The non-crosslinked polypropylene resin used as the base resin of the foamed sheet 2 may be a homopolymer, a block copolymer or a random copolymer. In the case of a copolymer, It is preferable that the olefin other than propylene is contained in the copolymer in an amount of 0.5 to 30% by weight, particularly preferably 1 to 10% by weight. In this case, as the olefin, ethylene or α- having 4 to 10 carbon atoms exemplified as the base resin of the stretched film is used.
There may be mentioned olefins, which may be one kind or two.
Combinations of more than one species can be used.
【００２４】上記の無架橋ポリプロピレン系樹脂は、ブ
ロック共重合体が好ましく、特にプロピレン−エチレン
ブロック共重合体が好ましい。このようなプロピレン−
エチレンブロック共重合体からなる発泡シートは最も熱
成形性が良好である。The above-mentioned non-crosslinked polypropylene resin is preferably a block copolymer, particularly preferably a propylene-ethylene block copolymer. Such propylene-
A foamed sheet made of an ethylene block copolymer has the best thermoformability.
【００２５】発泡シート２の基材樹脂として用いる無架
橋ポリプロピレン系樹脂は、例えば結晶性線状ポリプロ
ピレン系樹脂に低温分解型の過酸化物（分解温度：室温
〜１２０℃程度）を混合して１２０℃以下に加熱し、ア
タクチック又は／及び結晶していないアイソタクチック
成分の分岐鎖を主鎖に再結合せしめる方法により得るこ
とができ、主として端部に長鎖分岐を有する枝別れ構造
を有する。The non-crosslinked polypropylene resin used as the base resin for the foamed sheet 2 is, for example, a crystalline linear polypropylene resin mixed with a low temperature decomposable peroxide (decomposition temperature: room temperature to about 120 ° C.). It can be obtained by a method in which the branched chain of the atactic or / and non-crystalline isotactic component is recombined with the main chain by heating to a temperature of not higher than 0 ° C., and it has a branched structure mainly having long chain branches at the ends.
【００２６】上記低温分解型の過酸化物としては、ジ
（ｓ−ブチル）ペルオキシジカーボネート、ビス（２−
エトキシ）ペルオキシジカーボネート、シシクロヘキシ
ペルオキシジカーボネート、ジ−ｎ−プロピルペルオキ
シジカーボネート、ジ−ｎ−ブチルペルオキシジカーボ
ネート、ジイソプロピルペルオキシジカーボネート、ｔ
−ブチルペルオキシネオデカノアート、ｔ−アミノペル
オキシネオデカノアート及びｔ−ブチルペルオキシピバ
ラート等が例示される。Examples of the low temperature decomposition type peroxide include di (s-butyl) peroxydicarbonate and bis (2-
(Ethoxy) peroxydicarbonate, cyclohexylperoxydicarbonate, di-n-propylperoxydicarbonate, di-n-butylperoxydicarbonate, diisopropylperoxydicarbonate, t
-Butylperoxy neodecanoate, t-aminoperoxy neodecanoate, t-butylperoxypivalate and the like are exemplified.
【００２７】ドローダウン性が６０ｍ／分以下の無架橋
ポリプロピレン系樹脂は、例えば下記の方法によって得
られる。通常のプロピレン系樹脂を、かくはん機を備え
た反応器中でかくはんしながらアルゴン等の不活性ガス
で反応容器内を置換し、次いで上記過酸化物を樹脂１ｋ
ｇ当たり５〜５０ミリモル添加し、かくはんを続けなが
ら１２０℃程度まで、好ましくは７０〜１０５℃程度に
加熱して３０〜１２０分間程度反応させ、しかる後メチ
ルメルカプタンなどの反応停止剤を反応容器に導入した
り、あるいは反応生成物を１３０℃〜１５０℃程度で２
０〜４０分間加熱する方法により、反応を停止すること
で得られる。ドローダウン性は、長鎖分岐の数や長さに
より調整することができる。一般に長鎖分岐の数が多い
程、また分岐の長さが長い程、ドローダウン性は低下す
る（数値が小さくなる）傾向にある。The non-crosslinked polypropylene resin having a drawdown property of 60 m / min or less can be obtained, for example, by the following method. An ordinary propylene-based resin was replaced in the reaction vessel with an inert gas such as argon while stirring in a reactor equipped with a stirrer, and then the above-mentioned peroxide was added to the resin 1k.
Add 5 to 50 millimoles per g and heat to about 120 ° C., preferably about 70 to 105 ° C. for 30 to 120 minutes while stirring, and then react with a reaction terminator such as methyl mercaptan in a reaction vessel. Or by introducing the reaction product at about 130 ° C to 150 ° C.
It can be obtained by stopping the reaction by a method of heating for 0 to 40 minutes. The drawdown property can be adjusted by the number and length of long chain branches. In general, the larger the number of long chain branches and the longer the branch length, the lower the drawdown property (the smaller the numerical value).
【００２８】通常、長鎖分岐を持たないプロピレン系樹
脂や、分岐を有していても短い分岐しか持たないプロピ
レン系樹脂等は、ドローダウン性が６０ｍ／分を上回っ
てしまう。ドローダウン性が６０ｍ／分を超えるプロピ
レン系樹脂を基材樹脂として用い押出発泡を行った場
合、密度０．０６ｇ／ｃｍ3 以上〜０．４５ｇ／ｃｍ3
未満の発泡シートは、コルゲートや表面凹凸が多く、商
品価値のないものである。Usually, a propylene-based resin having no long-chain branch, a propylene-based resin having a branch but only a short branch, etc. has a drawdown property of more than 60 m / min. When extrusion foaming is performed using a propylene-based resin having a drawdown property of more than 60 m / min as a base resin, a density of 0.06 g / cm 3 or more to 0.45 g / cm 3
Foamed sheets of less than 1 have many corrugations and surface irregularities, and have no commercial value.
【００２９】プロピレン系樹脂発泡シート２の基材樹脂
として用いる無架橋ポリプロピレン系樹脂は、その結晶
化温度＋１５℃における半結晶化時間が８００秒以上で
あることが好ましく、特に１０００秒以上であるのが押
出発泡温度範囲をより拡大することができることから更
に好ましい。上記の半結晶化時間の測定には結晶化速度
測定機を用いる。半結晶化時間の測定方法は、フィルム
状の試料が保持された支持体を結晶化速度測定機のエア
バス内に入れて試料を完全に溶融させ、次いで溶融試料
を支持体ごと試料の結晶化温度＋１５℃の温度に保持さ
れたオイルバス中に、光源と光センサーとの間の光路を
遮るように浸漬し、溶けた試料が再度固化するまでの
間、光センサーにおいて常に一定の光量が検出されるよ
うに光源の電圧を調整し、電圧〜時間曲線を得る。半結
晶化時間は、上記の電圧〜時間曲線において電圧が一定
値となった時の電圧をＶ0 とした場合、電圧が１／２Ｖ
0 となるまでの時間である。The non-crosslinked polypropylene resin used as the base resin of the propylene resin foam sheet 2 preferably has a half crystallization time of 800 seconds or longer at the crystallization temperature of + 15 ° C., and particularly 1000 seconds or longer. Is more preferable because the extrusion foaming temperature range can be further expanded. A crystallization rate measuring device is used for the measurement of the half-crystallization time. The method of measuring the semi-crystallization time is to put the support holding the film-like sample in the air bath of the crystallization rate measuring machine to completely melt the sample, and then melt the sample together with the support to the crystallization temperature of the sample. Immerse in an oil bath maintained at a temperature of + 15 ° C so as to block the optical path between the light source and the optical sensor, and a constant amount of light is constantly detected by the optical sensor until the melted sample solidifies again. The voltage of the light source is adjusted so that a voltage-time curve is obtained. The half crystallization time is 1/2 V when the voltage when the voltage has a constant value in the above voltage-time curve is V 0.
It is the time to reach 0 .
【００３０】また、プロピレン系樹脂発泡シート２の基
材樹脂として用いられる無架橋ポリプロピレン系樹脂
は、上記の無架橋ポリプロピレン系樹脂を単独で用いる
のみならず、ドローダウン性が６０ｍ／分を超えない範
囲であれば、他の樹脂を混合して用いることもできる。
混合する樹脂は、例えば上記以外のプロピレン系樹脂、
或いは高密度ポリエチレン、低密度ポリエチレン、直鎖
状低密度ポリエチレン、直鎖状超低密度ポリエチレン、
エチレン−ブテン共重合体、エチレン−無水マレイン酸
共重合体等のエチレン系樹脂、ブテン系樹脂、ポリ塩化
ビニル、塩化ビニル−酢酸ビニル共重合体等の塩化ビニ
ル系樹脂、スチレン系樹脂等が挙げられる。これらの樹
脂を混合する際、混合する樹脂の量は、混合後の樹脂中
の含有量で４０重量％以下が好ましい。As the non-crosslinked polypropylene resin used as the base resin for the propylene resin foam sheet 2, not only the above noncrosslinked polypropylene resin is used alone, but also the drawdown property does not exceed 60 m / min. Within the range, other resins can be mixed and used.
The resin to be mixed is, for example, a propylene resin other than the above,
Or high density polyethylene, low density polyethylene, linear low density polyethylene, linear ultra low density polyethylene,
Ethylene-butene copolymers, ethylene-based resins such as ethylene-maleic anhydride copolymers, butene-based resins, polyvinyl chloride, vinyl chloride-based resins such as vinyl chloride-vinyl acetate copolymers, styrene-based resins, etc. To be When these resins are mixed, the amount of the resin to be mixed is preferably 40% by weight or less based on the content in the resin after mixing.
【００３１】上記の無架橋ポリプロピレン系樹脂（基材
樹脂）から発泡シート２を得る方法として、例えば下記
の方法が挙げられる。押出機内で基材樹脂と発泡剤とを
溶融混練した後、押出機先端に取り付けられた環状のリ
ップを有するサーキュラーダイスを用い、このリップよ
り溶融混練物を押出発泡させてチューブ状の発泡体を
得、次いでこのチューブを切り開いてシート状として発
泡シートを得る方法。As a method of obtaining the foamed sheet 2 from the above-mentioned non-crosslinked polypropylene resin (base resin), for example, the following method can be mentioned. After melt-kneading the base resin and the foaming agent in the extruder, a circular die having an annular lip attached to the tip of the extruder is used to extrude and foam the melt-kneaded product from this lip to form a tubular foam. Then, the tube is cut open to obtain a foamed sheet as a sheet.
【００３２】上記の発泡シート２を得る方法において用
いられる発泡剤は、無機発泡剤、揮発性発泡剤、分解型
発泡剤等が挙げられる。揮発性発泡剤としては、プロパ
ン、ｎ−ブタン、ｉ−ブタン、ペンタン、ヘキサン等の
脂肪族炭化水素、シクロブタン、シクロペンタン等の環
式脂肪族炭化水素、トリクロロフロロメタン、ジクロロ
ジフロロメタン、ジクロロテトラフロロエタン、メチル
クロライド、エチルクロライド、メチレンクロライド等
のハロゲン化炭化水素等が挙げられる。また、分解型発
泡剤としては、アゾジカルボンアミド、ジニトロソペン
タメチレンテトラミン、アゾイソブチロニトリル、重炭
酸ナトリウム等が挙げられる。これらの発泡剤は適宜混
合して用いることができる。発泡剤の使用量は、発泡剤
の種類、所望する発泡倍率等によっても異なるが、密度
０．０６ｇ／ｃｍ3 以上〜０．４５ｇ／ｃｍ3 未満の発
泡シート２を得るための目安は、樹脂１００重量部当た
り、揮発性発泡剤で０．３〜８．０重量部（ブタン換
算）程度、無機発泡剤で０．１〜５．０重量部（二酸化
炭素換算）程度、分解型発泡剤で０．１〜１５重量部程
度である。Examples of the foaming agent used in the method for obtaining the foamed sheet 2 include an inorganic foaming agent, a volatile foaming agent, and a decomposable foaming agent. Examples of the volatile blowing agent include aliphatic hydrocarbons such as propane, n-butane, i-butane, pentane and hexane, cycloaliphatic hydrocarbons such as cyclobutane and cyclopentane, trichlorofluoromethane, dichlorodifluoromethane and dichloro. Examples thereof include halogenated hydrocarbons such as tetrafluoroethane, methyl chloride, ethyl chloride and methylene chloride. Examples of the decomposing type foaming agent include azodicarbonamide, dinitrosopentamethylenetetramine, azoisobutyronitrile, sodium bicarbonate and the like. These foaming agents can be appropriately mixed and used. The amount of blowing agent, the kind of the foaming agent varies depending desired expansion ratio and the like, a guideline for obtaining a foamed sheet 2 a density of less than 0.06 g / cm 3 or more ~0.45g / cm 3, the resin Per 100 parts by weight, about 0.3 to 8.0 parts by weight of volatile foaming agent (converted to butane), about 0.1 to 5.0 parts by weight of inorganic foaming agent (converted to carbon dioxide), and decomposition type blowing agent It is about 0.1 to 15 parts by weight.
【００３３】発泡シート２を製造する際に、樹脂と発泡
剤の溶融混練物中に、必要に応じて気泡調整剤を添加す
ることができる。気泡調整剤としては、タルク、シリカ
等の無機粉末や、多価カルボン酸の酸性塩、多価カルボ
ン酸と炭酸ナトリウム或いは重炭酸ナトリウムとの反応
混合物等が挙げられる。気泡調整剤は樹脂１００重量部
当たり１３重量部程度以下添加するのが好ましい。但
し、下記のように無機充填剤を樹脂に多量に添加する場
合は、この限りではない。更に必要に応じ熱安定剤、紫
外線吸収剤、酸化防止剤、着色剤等の添加剤を添加する
こともできる。When the foamed sheet 2 is manufactured, a cell regulator may be added to the melt-kneaded product of the resin and the foaming agent, if necessary. Examples of the bubble regulator include inorganic powders such as talc and silica, acidic salts of polyvalent carboxylic acids, and reaction mixtures of polyvalent carboxylic acids with sodium carbonate or sodium bicarbonate. It is preferable to add about 13 parts by weight or less of the cell regulator to 100 parts by weight of the resin. However, this is not the case when a large amount of inorganic filler is added to the resin as described below. Further, if necessary, additives such as a heat stabilizer, an ultraviolet absorber, an antioxidant and a colorant can be added.
【００３４】また発泡シート２を製造する際に、総重量
の４０％を限度として、無機充填剤を基材樹脂に添加し
て、発泡シート２に無機充填剤を含有せしめることもで
きる。無機充填剤としては、例えばタルク、シリカ、炭
酸カルシウム、クレー、ゼオライト、アルミナ、硫酸バ
リウム等が挙げられる。これらの無機充填剤の平均粒径
は１〜７０μｍが好ましい。発泡シート２に無機充填剤
を含有せしめた場合、得られる発泡シートの耐熱性が向
上するとともに、焼却処理の際の燃焼カロリーを低下さ
せる。When the foamed sheet 2 is manufactured, an inorganic filler may be added to the base resin so that the foamed sheet 2 contains the inorganic filler up to 40% of the total weight. Examples of the inorganic filler include talc, silica, calcium carbonate, clay, zeolite, alumina, barium sulfate and the like. The average particle size of these inorganic fillers is preferably 1 to 70 μm. When the foamed sheet 2 contains an inorganic filler, the heat resistance of the foamed sheet obtained is improved and the calories burned during the incineration treatment are reduced.
【００３５】本発明の積層発泡シート１を用いて成形品
を製造する際の成形方法としては、真空成形、圧空成形
や、これらの応用として、フリードローイング成形、プ
ラグ・アンド・リッジ成形、リッジ成形、マッチド・モ
ールド成形、ストレート成形、ドレープ成形、リバース
ドロー成形、エアスリップ成形、プラグアシスト成形、
プラグアシストリバースロード成形等やこれらを組み合
わせた方法等が挙げられる。As a molding method for manufacturing a molded product using the laminated foam sheet 1 of the present invention, vacuum molding, pressure molding, and applications of these include free drawing molding, plug and ridge molding, and ridge molding. , Matched molding, straight molding, drape molding, reverse draw molding, air slip molding, plug assist molding,
Examples include plug-assisted reverse road molding and the like, and methods combining these.
【００３６】本発明の積層発泡シート１は、各種容器の
成形用として好適であるが、特に連続成形に用いられる
成形用発泡シートとして最適である。本発明の積層発泡
シート１より得られた成形品（容器）は、耐熱性、耐水
性、耐薬品性、断熱性、保形性、剛性等に優れる。その
ため、本発明の積層発泡シート１は、電子レンジでその
まま調理したり再加熱したりする用途に用いる食品用容
器や弁当容器等の連続成形用として好適である。The laminated foam sheet 1 of the present invention is suitable for molding various containers, but is most suitable as a foam sheet for molding used in continuous molding. The molded product (container) obtained from the laminated foam sheet 1 of the present invention is excellent in heat resistance, water resistance, chemical resistance, heat insulation, shape retention, rigidity and the like. Therefore, the laminated foam sheet 1 of the present invention is suitable for continuous molding of food containers, bento containers and the like used for the purpose of cooking or reheating in a microwave oven as it is.
【００３７】以下、実施例を挙げて本発明を更に詳細に
説明する。Hereinafter, the present invention will be described in more detail with reference to Examples.
【００３８】実施例１〜６、比較例１〜２ 表１に示すロール状に巻かれた長尺状の押出発泡シート
（環状ダイスから押出発泡させた後、マンドレル上で冷
却しつつ切り開いてシート状にしたもの。幅６３０ｍ
ｍ。）とロール状に巻かれた長尺状のフィルムとを連続
的に繰出し、両者を圧着ロールに導くと共に、当該圧着
部に、押出機から溶融状態のプロピレン系ブロック共重
合体（エチレン成分６．７重量％）を垂れ流し、これを
接着剤層（厚み約１００μｍ）として三者を一体化し、
成形用プロピレン系樹脂積層発泡シートを得、ロール状
に巻き取った。次にこの積層発泡シートを使用して熱成
形試験を行った。その結果を表１に示す。Examples 1 to 6 and Comparative Examples 1 to 2 A long extruded foamed sheet wound in a roll shape shown in Table 1 (extruded and foamed from an annular die and then cut open while cooling on a mandrel. 630m wide
m. ) And a long film wound in a roll form are continuously fed out, and both are guided to a pressure bonding roll, and a propylene block copolymer in a molten state (ethylene component 6. 7% by weight), and this is used as an adhesive layer (thickness of about 100 μm) to integrate the three,
A propylene-based resin laminated foam sheet for molding was obtained and wound into a roll. Next, a thermoforming test was conducted using this laminated foam sheet. Table 1 shows the results.
【００３９】[0039]
【表１】 [Table 1]
【００４０】表１において使用した発泡シートの基材樹
脂は、下記の表２に示した通りである。The base resin of the foamed sheet used in Table 1 is as shown in Table 2 below.
【表２】 [Table 2]
【００４１】又、各例で使用されたフィルムの種類は表
３の通りである。The types of film used in each example are shown in Table 3.
【００４２】[0042]
【表３】 [Table 3]
【００４３】尚、使用した基材樹脂のドローダウン性の
測定には、（株）東洋精機製作所製のメルトテンション
テスターII型を用い、半結晶化時間の測定にはコタキ商
事（株）製の結晶化速度測定器ＭＫ−８０１型を使用
し、フィルムの収縮応力の測定には、（株）島津製作所
製の熱機械的分析装置ＴＭＡ−５０を使用した。A melt tension tester type II manufactured by Toyo Seiki Seisaku-sho, Ltd. was used for measuring the drawdown property of the base resin used, and a half-crystallization time was measured by Kotaki Corporation. A crystallization rate meter MK-801 type was used, and a thermomechanical analyzer TMA-50 manufactured by Shimadzu Corporation was used for measuring the shrinkage stress of the film.
【００４４】熱成形性の試験方法及び評価は次の通りで
ある。ロール状の各積層シートを順次繰出し、上下から
ヒーターで加熱し、次いで容器状に熱成形する連続成形
を行った。この熱成形で得られた容器は、上面開口部の
寸法が１０１ｍｍ×１０１ｍｍ、底部の寸法が７７ｍｍ
×７７ｍｍ（底部のアールは３５Ｒ）、高さが３２ｍｍ
の平面形状がほぼ正方形の惣菜用の容器であった。熱成
形の１ショットあたりの容器の取り数は、積層シートの
長手方向に４個、幅方向に７個の計２８個であった。
尚、使用した連続成形機は、浅野研究所製の４３１型で
ある。この熱成形により得られた成形容器を観察し、ブ
リッジの発生のないものを『良好』と評価した。ブリッ
ジの発生が見られたものに対しては、『ブリッジ発生』
と評価した。The test method and evaluation of thermoformability are as follows. Roll-shaped laminated sheets were sequentially fed out, heated from above and below with a heater, and then thermoformed into a container for continuous molding. The container obtained by this thermoforming has a top opening size of 101 mm x 101 mm and a bottom size of 77 mm.
× 77mm (R on the bottom is 35R), height is 32mm
It was a container for prepared foods having a substantially square plan shape. The number of containers taken per one shot of thermoforming was 28 in total, four in the longitudinal direction of the laminated sheet and seven in the width direction.
The continuous molding machine used was a Model 431 manufactured by Asano Laboratory. The molded container obtained by this thermoforming was observed, and those having no occurrence of bridge were evaluated as "good". For those in which the occurrence of bridge was seen, "Bridge occurrence"
It was evaluated.
【００４５】次に、成形容器の厚みむらを比較するため
に、実施例１で得られた容器と比較例１で得られた容器
に対し、次の測定を行った。実施例１で得られた無数の
容器から無作為に２８個取り出し、各容器の側壁の中央
部の厚みを測定（容器１枚あたり４つの側壁があるので
４箇所測定。総計１１２箇所測定。）すると共に底部中
央部の厚みを測定した（容器１枚あたり１箇所測定。総
計２８箇所測定。）。その結果、側壁部の厚みの相加平
均値は１．８５ｍｍであった。一方、底部の厚みの相加
平均値は１．９２ｍｍであった。この差は０．０７ｍｍ
であった。比較例１で得られた容器に対しても、上記と
同様にして測定した結果、側壁部の厚みの相加平均値は
１．５２ｍｍであった。一方、底部の厚みの相加平均値
は２．０６ｍｍであった。この差は０．５４ｍｍであっ
た。以上の結果より、本発明の積層シートから得られる
容器の厚みむらはわずかであることが分かる。Next, in order to compare the thickness unevenness of the molded containers, the following measurements were performed on the container obtained in Example 1 and the container obtained in Comparative Example 1. Twenty-eight randomly picked out from the innumerable containers obtained in Example 1 and measuring the thickness of the central part of the side wall of each container (four containers have four side walls, total of 112 positions are measured.). At the same time, the thickness of the central portion of the bottom was measured (1 measurement per container, 28 total measurements). As a result, the arithmetic mean value of the thickness of the side wall was 1.85 mm. On the other hand, the arithmetic average value of the thickness of the bottom was 1.92 mm. This difference is 0.07mm
Met. The container obtained in Comparative Example 1 was also measured in the same manner as above, and as a result, the arithmetic mean value of the thickness of the side wall was 1.52 mm. On the other hand, the arithmetic average value of the thickness of the bottom was 2.06 mm. This difference was 0.54 mm. From the above results, it can be seen that the thickness unevenness of the container obtained from the laminated sheet of the present invention is slight.
【００４６】[0046]
【発明の効果】以上説明したように本発明の成形用プロ
ピレン系樹脂積層発泡シートは、特定のドローダウン製
を有するプロピレン系樹脂発泡シートにプロピレン系樹
脂延伸フィルムが積層された構成を採用したことによ
り、本発明の成形用プロピレン系樹脂積層発泡シートを
用いて連続成形機において成形する際、該発泡シートの
両端がクランプされた状態で加熱されると、延伸フィル
ムがその収縮力によって発泡シートを引っ張って、発泡
シートが熱膨張により波打つのを防ぎ、コルゲートの発
生を防止することができる。その結果、成形用プロピレ
ン系樹脂積層発泡シートに加熱ムラやブリッジ等が発生
することなく成形が行われる為、物性及び外観に優れた
成形品が得られる。更に、本発明の成形用プロピレン系
樹脂積層発泡シートを使用することで、従来の成形装置
をそのまま利用することができるため、成形装置を改良
することなく、実用的である。As described above, the propylene resin laminated foam sheet for molding of the present invention has a constitution in which a propylene resin stretched film is laminated on a propylene resin foam sheet having a specific drawdown. Thus, when the propylene-based resin laminated foam sheet for molding of the present invention is molded in a continuous molding machine, when the foamed sheet is heated in a state in which both ends are clamped, the stretched film causes the foamed sheet to shrink due to its contracting force. By pulling, the foamed sheet can be prevented from waviness due to thermal expansion, and corrugation can be prevented from occurring. As a result, the propylene-based resin laminated foam sheet for molding can be molded without causing uneven heating and bridges, so that a molded product having excellent physical properties and appearance can be obtained. Further, by using the propylene-based resin laminated foam sheet for molding of the present invention, the conventional molding device can be used as it is, which is practical without improving the molding device.
【図１】本発明の成形用プロピレン系樹脂積層発泡シー
トの１例を示す断面図である。FIG. 1 is a cross-sectional view showing an example of a propylene-based resin laminated foam sheet for molding of the present invention.
１ 成形用プロピレン系樹脂積層発泡シート ２ プロピレン系樹脂発泡シート ３ プロピレン系樹脂延伸フィルム 1 Propylene resin laminated foam sheet for molding 2 Propylene resin foam sheet 3 Propylene resin stretched film
Claims (4)
無架橋プロピレン系樹脂を基材樹脂とするプロピレン系
樹脂発泡シートと、該発泡シートの少なくとも片面に積
層された厚さ１０〜２００μｍのプロピレン系樹脂延伸
フィルムとからなることを特徴とする成形用プロピレン
系樹脂積層発泡シート。1. A propylene-based resin foamed sheet using a non-crosslinked propylene-based resin as a base resin having a drawdown property of 60 m / min or less, and propylene having a thickness of 10 to 200 μm laminated on at least one side of the foamed sheet. A propylene-based resin laminated foam sheet for molding, which comprises a stretched resin-based film.
〜５ｍｍ、密度０．０６ｇ／ｃｍ3 以上〜０．４５ｇ／
ｃｍ3 未満である請求項１記載の成形用プロピレン系樹
脂積層発泡シート。2. A propylene-based resin foam sheet having a thickness of 1
~ 5 mm, density 0.06 g / cm 3 or more ~ 0.45 g /
The propylene-based resin laminated foam sheet for molding according to claim 1, which is less than cm 3 .
くとも一方向の収縮応力が１０〜２００ｇ／５ｍｍであ
る請求項１又は２記載の成形用プロピレン系樹脂積層発
泡シート。3. The propylene resin laminated foam sheet for molding according to claim 1, wherein the stretched propylene resin film has a shrinkage stress in at least one direction of 10 to 200 g / 5 mm.
フィルムである請求項１、２又は３記載の成形用プロピ
レン系樹脂積層発泡シート。4. The propylene-based resin laminated foam sheet for molding according to claim 1, 2 or 3, wherein the propylene-based resin stretched film is a foamed film.