JPH0827372A - Water-absorbing resin composition - Google Patents
Water-absorbing resin compositionInfo
- Publication number
- JPH0827372A JPH0827372A JP6164268A JP16426894A JPH0827372A JP H0827372 A JPH0827372 A JP H0827372A JP 6164268 A JP6164268 A JP 6164268A JP 16426894 A JP16426894 A JP 16426894A JP H0827372 A JPH0827372 A JP H0827372A
- Authority
- JP
- Japan
- Prior art keywords
- water
- polydioxolane
- resin composition
- polymer
- absorbent resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、吸水性樹脂組成物に関
するものである。詳しく述べると、取り扱いが良好でか
つ吸水性能に優れた吸水性樹脂組成物に関するものであ
る。FIELD OF THE INVENTION The present invention relates to a water absorbent resin composition. More specifically, the present invention relates to a water absorbent resin composition which is easily handled and has excellent water absorbing performance.
【０００２】[0002]
【従来の技術】近年、自重の数百倍の水を吸収すること
のできる吸水性重合体が開発され、紙おむつ、ナプキン
等の衛生材料やケーブル用止水テープに用いられてい
る。しかしながら、多くの吸水性重合体は、粉末状であ
るためにそのままでは扱いにくく、このため、パルプ等
と混合したり、ゴム中に分散したり、あるいは接着剤や
疎水性のあるバインダーで基材に固定したりして用いら
れている。2. Description of the Related Art In recent years, water-absorbent polymers capable of absorbing hundreds of times their own weight of water have been developed and used for sanitary materials such as diapers and napkins, and waterproof tape for cables. However, since many water-absorbent polymers are powdery, they are difficult to handle as they are. Therefore, they are mixed with pulp, dispersed in rubber, or used as a base material with an adhesive or a hydrophobic binder. It is used by fixing to.
【０００３】しかしながら、ゴムや接着剤は疎水性であ
るため、吸水性ポリマーの吸水性能が損なわれてしまう
という問題があった。However, since the rubber and the adhesive are hydrophobic, there is a problem that the water absorbing performance of the water absorbing polymer is impaired.
【０００４】また、水溶性重合体であるポリエチレンオ
キサイド中に吸水性重合体を配合してなる被覆組成物も
知られている（特開昭５７−１６８９２１号および特開
平１−１８２３６２号）。さらに、ポリエチレンオキサ
イドをバインダーとして吸水性重合体を基材に付着させ
てなるケーブル用止水材も知られている（特開昭６３−
７５７１３号）。Further, coating compositions prepared by blending a water-absorbing polymer in polyethylene oxide, which is a water-soluble polymer, are also known (JP-A-57-168921 and JP-A-1-182362). Further, a waterproof material for cables is known, in which a water-absorbing polymer is attached to a substrate by using polyethylene oxide as a binder (Japanese Patent Laid-Open No. 63-63).
75713).
【０００５】しかしながら、ポリエチレンオキサイド
は、吸水性重合体の吸水性能を阻害するため、吸水速度
が遅くなったりして、十分には吸水性能を発揮できるも
のではなかった。However, since polyethylene oxide hinders the water absorption performance of the water-absorbent polymer, the water absorption speed is slowed down, and the water absorption performance has not been sufficiently exhibited.
【０００６】[0006]
【発明が解決しようとする課題】したがって、本発明の
目的は、新規な吸水性樹脂組成物を提供することにあ
る。Therefore, an object of the present invention is to provide a novel water absorbent resin composition.
【０００７】本発明の他の目的は、取り扱いが良好でか
つ吸水性能に優れた吸水性樹脂組成物を提供することに
ある。Another object of the present invention is to provide a water-absorbent resin composition which is easy to handle and has excellent water absorption performance.
【０００８】[0008]
【課題を解決するための手段】上記諸目的は、ポリジオ
キソランおよび吸水性重合体を含んでなる吸水性樹脂組
成物により達成される。The above objects are achieved by a water-absorbent resin composition containing polydioxolane and a water-absorbent polymer.
【０００９】本発明はまた、ポリジオキソランのマトリ
ックス内に吸水性重合体が分散されてなる前記吸水性樹
脂組成物である。本発明はさらに、ポリジオキソランの
マトリックス表面に吸水性重合体が分散して固着されて
なる前記吸水性樹脂組成物である。本発明は、該組成物
の形状がシート状ないしフィルム状または繊維状である
前記吸水性樹脂組成物である。本発明はまた、吸水性重
合体の表面にポリジオキソランが被覆されてなる前記吸
水性樹脂組成物である。本発明はさらに、ポリジオキソ
ランをバインダーとして吸水性重合体が凝集体ないし造
粒体を形成してなる前記吸水性樹脂組成物である。The present invention is also the above water-absorbent resin composition comprising a water-absorbing polymer dispersed in a polydioxolane matrix. The present invention is the water absorbent resin composition, further comprising a water absorbent polymer dispersed and fixed on the surface of the polydioxolane matrix. The present invention is the water-absorbent resin composition, wherein the composition is in the form of a sheet, a film or a fiber. The present invention is also the above water-absorbent resin composition in which the surface of the water-absorbent polymer is coated with polydioxolane. The present invention further provides the above water-absorbent resin composition, wherein the water-absorbent polymer forms an aggregate or a granule using polydioxolane as a binder.
【００１０】[0010]
【作用】本発明による吸水性樹脂組成物は、ポリジオキ
ソランおよび吸水性重合体を含んでなるものである。The water absorbent resin composition according to the present invention comprises polydioxolane and a water absorbent polymer.
【００１１】該吸水性樹脂組成物の形態としては、ポリ
ジオキソランと吸水性重合体の単なる混合物でもよい
し、例えば、以下に示す形態のものでもよい。The form of the water absorbent resin composition may be a simple mixture of polydioxolane and a water absorbent polymer, or may be, for example, the form shown below.
【００１２】（１）ポリジオキソランのマトリックス内
に吸水性重合体が分散してなる吸水性樹脂組成物。(1) A water-absorbent resin composition in which a water-absorbent polymer is dispersed in a polydioxolane matrix.
【００１３】（２）ポリジオキソランのマトリックス表
面に吸水性重合体が分散して固着してなる吸水性樹脂組
成物。(2) A water absorbent resin composition in which a water absorbent polymer is dispersed and fixed on the surface of a polydioxolane matrix.
【００１４】（３）吸水性重合体の表面にポリジオキソ
ランが被覆されてなる吸水性樹脂組成物。(3) A water absorbent resin composition obtained by coating the surface of a water absorbent polymer with polydioxolane.
【００１５】（４）吸水性重合体がポリジオキソランを
バインダーとして凝集体ないし造粒体を形成してなる吸
水性樹脂組成物。(4) A water-absorbent resin composition comprising a water-absorbent polymer as an aggregate or granules using polydioxolane as a binder.
【００１６】しかしながら、本発明による吸水性樹脂組
成物の形態は、これらの形態に限定されるものではな
い。However, the form of the water absorbent resin composition according to the present invention is not limited to these forms.
【００１７】本発明で用いられるポリジオキソランを得
る方法としては、例えば、１，３−ジオキソラン、２−
メチル−１，３−ジオキソラン、４−メチル−１，３−
ジオキソラン、２−２´−ジエチル−１，３−ジオキソ
ランなどの単量体から選ばれる少なくとも１種の単量体
をカチオン重合すればよい。またこれらの単量体と共重
合な他の単量体を共重合させてもよい。共重合可能な単
量体としては、例えばスチレン；（メタ）アクリル酸；
エチレン、プロピレン等の不飽和炭化水素；トリオキサ
ン、エチレンオキシド、プロピレンオキシド、テトラヒ
ドロフラン等の環状エーテル類；γ−ブチロラクトン、
グリコリド、ラクチド、ε−カプロラクトン、ε−カプ
ロラクタム等のラクトンまたはラクタムを挙げることが
できる。As the method for obtaining the polydioxolane used in the present invention, for example, 1,3-dioxolane, 2-
Methyl-1,3-dioxolane, 4-methyl-1,3-
At least one monomer selected from monomers such as dioxolane and 2-2′-diethyl-1,3-dioxolane may be cationically polymerized. Further, other monomers copolymerizable with these monomers may be copolymerized. Examples of the copolymerizable monomer include styrene; (meth) acrylic acid;
Unsaturated hydrocarbons such as ethylene and propylene; cyclic ethers such as trioxane, ethylene oxide, propylene oxide and tetrahydrofuran; γ-butyrolactone,
Lactones or lactams such as glycolide, lactide, ε-caprolactone, ε-caprolactam can be mentioned.
【００１８】ポリジオキソランは、ホルムアルデヒドと
エチレングリコールとの重縮合によっても得ることがで
きる。Polydioxolane can also be obtained by polycondensation of formaldehyde and ethylene glycol.
【００１９】本発明で用いられるポリジオキソランがこ
れらの方法により得られるものに限定されるものではな
いが、代表的なものとしては、例えば、つぎの一般式
（Ｉ）で示されるオキシメチレン−オキシエチレンの繰
り返し単位を有するものがある。The polydioxolane used in the present invention is not limited to those obtained by these methods, but a typical example thereof is oxymethylene-oxy represented by the following general formula (I). Some have repeating units of ethylene.
【００２０】[0020]
【化１】 Embedded image
【００２１】（ただし、式中、Ｒ1 〜Ｒ6 はそれぞれ別
個に水素原子、メチル基またはエチル基である。） 開始剤としては、例えば、リンタングステン酸やリンモ
リブデン酸等のヘテロポリ酸やトリエチルアルミニウ
ム、アルミニウムイソプロポキシド、チタンイソプロポ
キシド等の有機金属化合物を用いることができる。ま
た、ホルムアルデヒドとエチレングリコールの重縮合に
より得ることもできる。本発明でマトリックスとして使
用されるポリジオキソランの平均数分子量は、５，００
０〜１０００万、好ましくは１万〜１００万である。(In the formula, R 1 to R 6 are each independently a hydrogen atom, a methyl group or an ethyl group.) Examples of the initiator include heteropolyacids such as phosphotungstic acid and phosphomolybdic acid, and triethyl. Organometallic compounds such as aluminum, aluminum isopropoxide, and titanium isopropoxide can be used. It can also be obtained by polycondensation of formaldehyde and ethylene glycol. The polydioxolane used as a matrix in the present invention has an average number molecular weight of 5,000.
It is 0 to 10,000,000, preferably 10,000 to 1,000,000.
【００２２】この発明で用いられるポリジオキソランが
これらの方法により得られるものに限定されるものでな
い。The polydioxolane used in the present invention is not limited to those obtained by these methods.
【００２３】本発明で用いられる吸水性重合体は、従来
公知のものを用いることができ、例えば、ポリアクリル
酸部分中和物架橋体、澱粉−アクリル酸グラフト重合
体、澱粉−アクリロニトリルグラフト重合体の加水分解
物、酢酸ビニル−アクリル酸エステル共重合体の鹸化
物、アクリロニトリル共重合体もしくはアクリルアミド
共重合体の加水分解物またはこれらの架橋体、イソブチ
レン−無水マレイン酸共重合架橋体、（メタ）アクリル
酸塩−（メタ）アクリルアミド共重合架橋体、（メタ）
アクリルアミド−２−メチルプロパンスルホン酸塩共重
合架橋体、アルコキシポリエチレングリコール（メタ）
アクリレート共重合架橋体、ポリビニルアルコール架橋
体、変性ポリエチレンオキサイド架橋体等が挙げられ、
これら重合体の１種または２種以上を挙げることができ
る。これらのうちポリアクリル酸部分中和物架橋体が最
も好ましい。吸水性重合体の形状は特に制限なく、一般
に不定形、球状、鱗片状、塊状、繊維状等が挙げられ
る。その平均粒径は、例えば１μｍ〜１０ｍｍ、好まし
くは１０μｍ〜１ｍｍである。吸水性重合体は、その一
次粒子が集合した造粒物を用いることもできる。また、
吸水性重合体は、その表面が表面架橋されたものを用い
ることもできる。表面架橋は、カルボキシル基等の吸水
性重合体の官能基と共有結合やイオン結合を生成するこ
とのできる多価アルコール、多価エポキシ化合物、多価
アミン、多価金属塩等と吸水性重合体とを吸水性重合体
の表面近傍で反応させることによりなされる。なお、本
発明で用いることができる吸水性重合体が上記重合体に
限定されるものではない。As the water-absorbent polymer used in the present invention, conventionally known ones can be used, and examples thereof include cross-linked polyacrylic acid partially neutralized products, starch-acrylic acid graft polymers, starch-acrylonitrile graft polymers. , A hydrolyzate of vinyl acetate-acrylic acid ester copolymer, a hydrolyzate of an acrylonitrile copolymer or an acrylamide copolymer or a crosslinked product thereof, an isobutylene-maleic anhydride copolymer crosslinked product, (meth) Acrylate- (meth) acrylamide copolymer cross-linked product, (meth)
Acrylamide-2-methylpropane sulfonate copolymer cross-linked product, alkoxy polyethylene glycol (meth)
Examples include acrylate copolymer crosslinked products, polyvinyl alcohol crosslinked products, modified polyethylene oxide crosslinked products,
One or more of these polymers may be mentioned. Among these, a crosslinked polyacrylic acid partially neutralized product is most preferable. The shape of the water-absorbent polymer is not particularly limited, and generally includes an amorphous shape, a spherical shape, a scaly shape, a lump shape, a fibrous shape and the like. The average particle size is, for example, 1 μm to 10 mm, preferably 10 μm to 1 mm. As the water-absorbent polymer, a granulated product in which the primary particles are aggregated can also be used. Also,
As the water-absorbent polymer, a surface-crosslinked one may be used. Surface cross-linking is a water-absorbing polymer such as a polyhydric alcohol, a polyvalent epoxy compound, a polyvalent amine, or a polyvalent metal salt capable of forming a covalent bond or an ionic bond with a functional group of a water-absorbing polymer such as a carboxyl group. It is made by reacting with and near the surface of the water-absorbent polymer. The water-absorbent polymer that can be used in the present invention is not limited to the above polymers.
【００２４】表面架橋させる際の吸水性重合体の平均粒
径は１〜１０００μｍ、好ましくは１０〜８５０μｍで
あり、表面処理により一次粒子が集合したりして、平均
粒径が２０〜１０００μｍ、好ましくは３０〜８５０μ
ｍとなる。The average particle diameter of the water-absorbent polymer at the time of surface cross-linking is 1 to 1000 μm, preferably 10 to 850 μm, and the average particle diameter is 20 to 1000 μm, preferably primary particles aggregated by the surface treatment. Is 30-850μ
m.
【００２５】表面架橋に用いられる架橋剤としては、例
えばエチレングリコール、ジエチレングリコール、トリ
エチレングリコール、ポリエチレングリコール、グリセ
リン、ポリグリセリン、プロピレングリコール、ジエタ
ノールアミン、トリエタノールアミン、ポリプロピレン
グリコール、ポリビニルアルコール、ペンタエリスリト
ール、１，４−ブタンジオール、１，５−ペンタンジオ
ール、１，６−ヘキサンジオール、ソルビット、ソルビ
タン、グルコース、マンニット、マンニタン、ショ糖、
ブドウ糖等の多価アルコール；エチレングリコールジグ
リシジルエーテル、ポリエチレングリコールジグリシジ
ルエーテル、グリセリントリグリシジルエーテル等の多
価グリシジル化合物；エピクロルヒドリン、α−メチル
クロルヒドリン等のハロエポキシ化合物；グルタールア
ルデヒド、グリオキザール等のポリアルデヒド；エチレ
ンジアミン、ポリエチレンイミン等の多価アミン化合
物；水酸化カルシウム、塩化カルシウム、炭酸カルシウ
ム、酸化カルシウム、塩化硼砂マグネシウム、酸化マグ
ネシウム、塩化アルミニウム、塩化亜鉛および塩化ニッ
ケル等の周期律表２Ａ族、３Ｂ族、８族の金属の水酸化
物、ハロゲン化物、炭酸塩、酸化物、硼砂等の硼酸塩、
アルミニウムイソプロピラート等の多価金属化合物等が
挙げられ、これらの１種または２種以上を、反応性を考
慮した上で適宜選んで用いることができる。これらの中
でも、その得られる粒子表面近傍が架橋された吸水性重
合体の粒子構造の強さから、該吸水性重合体がカルボキ
シル基を有する場合には、架橋剤としては、多価アルコ
ール化合物、多価グリシジル化合物等を用いることが好
ましい。As the cross-linking agent used for surface cross-linking, for example, ethylene glycol, diethylene glycol, triethylene glycol, polyethylene glycol, glycerin, polyglycerin, propylene glycol, diethanolamine, triethanolamine, polypropylene glycol, polyvinyl alcohol, pentaerythritol, 1 , 4-butanediol, 1,5-pentanediol, 1,6-hexanediol, sorbit, sorbitan, glucose, mannitol, mannitane, sucrose,
Polyhydric alcohols such as glucose; polyhydric glycidyl compounds such as ethylene glycol diglycidyl ether, polyethylene glycol diglycidyl ether, glycerin triglycidyl ether; haloepoxy compounds such as epichlorohydrin, α-methylchlorohydrin; glutaraldehyde, glyoxal, etc. Polyaldehydes; polyvalent amine compounds such as ethylenediamine and polyethyleneimine; calcium hydroxide, calcium chloride, calcium carbonate, calcium oxide, magnesium borax magnesium, magnesium oxide, aluminum chloride, zinc chloride and nickel chloride, etc. Hydroxides, halides, carbonates, oxides, borax, etc. of Group 3B and Group 8 metals,
Examples thereof include polyvalent metal compounds such as aluminum isopropylate, and one or more of these can be appropriately selected and used in consideration of reactivity. Among these, from the strength of the particle structure of the water-absorbent polymer crosslinked near the surface of the particles obtained, when the water-absorbent polymer has a carboxyl group, as a crosslinking agent, a polyhydric alcohol compound, It is preferable to use a polyvalent glycidyl compound or the like.
【００２６】本発明で使用される吸水性重合体の吸水倍
率（ｇ／ｇ）は５〜１０００、好ましくは１０〜５００
である。The water absorbing polymer used in the present invention has a water absorption capacity (g / g) of 5 to 1000, preferably 10 to 500.
Is.
【００２７】ポリジオキソランのマトリックス内に吸水
性重合体が分散した吸水性樹脂組成物の形状としては、
特に制限なく、例えばフィルム状、シート状、繊維状、
塊状、液状等が挙げられる。吸水性重合体はマトリック
ス内に分散しているが、その一部は表面に露出したもの
でもよい。ポリジオキソランは水溶性であるが、室温で
は溶解しにくく５０〜６０℃の温水には易溶である。し
たがって、吸水性樹脂組成物が吸水した際、他の水溶性
重合体、例えばポリエチレンオキサイド等は吸水性重合
体の吸水を阻害するのに対し、吸水性重合体の吸水特性
を阻害しないものである。したがって、こうした吸水性
組成物は吸水性および取り扱い性の良好な吸水性樹脂組
成物となる。The shape of the water absorbent resin composition in which the water absorbent polymer is dispersed in the polydioxolane matrix is as follows:
Without particular limitation, for example, film-like, sheet-like, fiber-like,
Examples include lumps and liquids. The water-absorbent polymer is dispersed in the matrix, but a part of it may be exposed on the surface. Although polydioxolane is water-soluble, it hardly dissolves at room temperature and easily dissolves in warm water of 50 to 60 ° C. Therefore, when the water-absorbent resin composition absorbs water, other water-soluble polymers such as polyethylene oxide inhibit water absorption of the water-absorbent polymer, but do not inhibit the water-absorbent property of the water-absorbent polymer. . Therefore, such a water-absorbent composition becomes a water-absorbent resin composition having good water absorbability and handleability.
【００２８】こうした組成物は、例えば、吸水性重合体
の存在下にジオキソランを重合したり、ポリジオキソラ
ンと吸水性重合体とを混合した後に、所望の形状に成形
することにより得られる。好ましくはポリジオキソラン
と吸水性重合体とを混合し成型する方法である。具体的
にはポリジオキソランと吸水性重合体とを加熱下に溶融
混練し、インフレーション法やＴダイ法によりフィルム
やシート状に成形したり、紡糸して繊維状に成形したり
する方法や、あるいはポリジオキソランを水やクロロホ
ルム等の溶媒に溶解した後に吸水性重合体を分散し、こ
のものを塗工したり紡糸する方法等が挙げられる。得ら
れるフィルムやシートや繊維は、延伸することにより強
靭なフィルムやシートや繊維が得られる。また、２枚の
ポリジオキソランのフィルムやシートの間に吸水性重合
体を散布し熱プレスすることも可能である。得られるフ
ィルムやシートの厚さは一般に１μｍ〜１０ｍｍの範囲
である。厚さが１μｍより薄いと強度の乏しいものとな
り、１０ｍｍより厚いと吸水速度が非常に遅くなること
がある。また繊維の径は一般に１μｍ〜２ｍｍ、好まし
くは１０〜１０００μｍの範囲である。フィルムやシー
トの厚さや繊維の径がこれらの範囲に限定されるもので
はない。Such a composition can be obtained, for example, by polymerizing dioxolane in the presence of a water-absorbing polymer, mixing polydioxolane and the water-absorbing polymer, and then molding the mixture into a desired shape. Preferred is a method in which polydioxolane and a water-absorbent polymer are mixed and molded. Specifically, a method of melt-kneading polydioxolane and a water-absorbent polymer under heating, forming into a film or sheet by an inflation method or a T-die method, or spinning to form a fiber, or Examples thereof include a method in which polydioxolane is dissolved in a solvent such as water or chloroform, and then a water-absorbent polymer is dispersed, and this is applied or spun. By stretching the obtained film, sheet or fiber, a tough film, sheet or fiber can be obtained. It is also possible to spray a water-absorbing polymer between two polydioxolane films or sheets and heat press. The thickness of the obtained film or sheet is generally in the range of 1 μm to 10 mm. When the thickness is less than 1 μm, the strength is poor, and when it is more than 10 mm, the water absorption speed may be very slow. The fiber diameter is generally in the range of 1 μm to 2 mm, preferably 10 to 1000 μm. The thickness of the film or sheet and the diameter of the fiber are not limited to these ranges.
【００２９】この組成物中のポリジオキソランと吸水性
重合体の割合は、目的や用途に応じて適宜設定できる
が、一般にポリジオキソラン１００重量部に対し吸水性
重合体１〜２０００重量部の範囲であり、好ましくは５
〜１０００重量部の範囲である。吸水性重合体が１重量
部未満では、充分な吸水性能を発揮することができなく
なることがあり、一方、２０００重量部を越えると強度
が脆くなることがある。The ratio of the polydioxolane to the water-absorbing polymer in this composition can be appropriately set depending on the purpose and application, but generally it is within the range of 1 to 2000 parts by weight of the water-absorbing polymer with respect to 100 parts by weight of polydioxolane. Yes, preferably 5
The range is up to 1000 parts by weight. If the amount of the water-absorbent polymer is less than 1 part by weight, sufficient water absorption performance may not be exhibited, while if it exceeds 2000 parts by weight, the strength may be weakened.
【００３０】この吸水性重合体がポリジオキソランのマ
トリックス内に分散した組成物には、その吸水速度を向
上させるため無機微粒子、パルプ繊維、界面活性剤等が
添加されていてもよい。これらの添加剤は、ポリジオキ
ソランマトリックスあるいは吸水性重合体のいずれに添
加されてもよい。吸水性重合体の形状は特に制限ない
が、形状が球状であれば、不定形の重合体を用いた場合
に比べ表面のより平滑な組成物が得られる。Inorganic particles, pulp fibers, surfactants, etc. may be added to the composition in which the water-absorbent polymer is dispersed in the polydioxolane matrix in order to improve the water absorption rate. These additives may be added to either the polydioxolane matrix or the water absorbing polymer. The shape of the water-absorbent polymer is not particularly limited, but if the shape is spherical, a composition having a smoother surface can be obtained as compared with the case of using an amorphous polymer.
【００３１】添加剤としては使用される無機粒子として
は、平均粒径０．００１〜１０μｍ、好ましくは０．０
１〜１μｍのものであり、例えばシリカ微粉末、タル
ク、酸化チタン、酸化亜鉛、酸化マグネシウム、炭酸カ
ルシウム、けい藻土、鉄粉等がある。該組成物に対して
０．０００１〜５０重量％、好ましくは０．００１〜２
０重量％使用される。The inorganic particles used as an additive have an average particle size of 0.001 to 10 μm, preferably 0.0
The particle size is 1 to 1 μm, and examples thereof include fine silica powder, talc, titanium oxide, zinc oxide, magnesium oxide, calcium carbonate, diatomaceous earth, and iron powder. 0.0001 to 50% by weight relative to the composition, preferably 0.001 to 2
0% by weight is used.
【００３２】また、パルプとしては、平均粒径１０〜５
００μｍ、好ましくは１０〜３００μｍのものであり、
例えばリンターパルプ、木材パルプ、合成パルプ等があ
る。該組成物に対して０．１〜５０重量％、好ましくは
１〜２０重量％使用される。The pulp has an average particle size of 10 to 5
00 μm, preferably 10 to 300 μm,
Examples include linter pulp, wood pulp, synthetic pulp and the like. It is used in an amount of 0.1 to 50% by weight, preferably 1 to 20% by weight, based on the composition.
【００３３】界面活性剤としては、例えばポリオキシア
ルキレンアルキルエーテル、ポリオキシアルキレンアシ
ルエーテル等に代表される非イオン性界面活性剤や、ア
ルキルベンゼンスルホン酸塩に代表されるアニオン性界
面活性剤やアルキルアンモニウム塩に代表されるカチオ
ン性界面活性剤等があり、該組成物に対して０．０１〜
１０重量％、好ましくは０．１〜５重量％使用される。Examples of the surfactant include nonionic surfactants represented by polyoxyalkylene alkyl ethers and polyoxyalkylene acyl ethers, anionic surfactants represented by alkylbenzene sulfonates, and alkylammonium. There are cationic surfactants typified by salts and the like.
10% by weight, preferably 0.1-5% by weight is used.
【００３４】上記のようにして得られるポリジオキソラ
ンのマトリックス内に吸水性重合体の分散した吸水性樹
脂組成物は、吸水性重合体が水溶性液体と接触すると、
ポリジオキソランが吸水性重合体の吸水性を阻害しない
ので、膨潤した重合体により組成物が水壊し、水性液体
が全体に拡散し該液体はすばやく吸収される。また、ポ
リジオキソランは高湿度雰囲気下においても吸湿性が低
いので、こうした吸水性樹脂組成物は、表面のべたつき
や粘着性がなく、取り扱い易いものとなる。この吸水性
樹脂組成物は、フィルム、シート、繊維、袋等の形状に
加工が容易であり、そうした形状のものは取り扱い性が
良好である。また、他の熱可塑性樹脂との複合化も容易
に行なうことができる。また熱加工により他の基材との
複合化も容易に行うことができる。このものは吸水性に
優れ、加工性も良好であるので、衛生材料の吸収剤や拡
散材、通信ケーブル用止水材等に好適に用いることがで
きる。また、水壊性にも優れるので、医薬品・農薬・肥
料・界面活性剤・洗剤・顔料等の水溶性基質や水分散基
質の包装に好適に用いることができる。The water-absorbent resin composition obtained by dispersing the water-absorbent polymer in the polydioxolane matrix obtained as described above, when the water-absorbent polymer comes into contact with the water-soluble liquid,
Since the polydioxolane does not hinder the water absorption of the water-absorbing polymer, the swollen polymer causes the composition to break down, the aqueous liquid diffuses throughout, and the liquid is quickly absorbed. Further, since polydioxolane has low hygroscopicity even in a high humidity atmosphere, such a water-absorbent resin composition has no stickiness or tackiness on the surface and is easy to handle. This water-absorbent resin composition can be easily processed into a shape such as a film, a sheet, a fiber, and a bag, and such a shape has good handleability. Further, it is possible to easily form a composite with another thermoplastic resin. Further, it can be easily formed into a composite with another substrate by thermal processing. Since it has excellent water absorbency and good workability, it can be suitably used as an absorbent or diffusing material for sanitary materials, a water blocking material for communication cables, and the like. Further, since it is also excellent in water-disintegrating property, it can be suitably used for packaging water-soluble substrates or water-dispersed substrates such as pharmaceuticals, agricultural chemicals, fertilizers, surfactants, detergents and pigments.
【００３５】また、このポリジオキソランのマトリック
ス内に吸水性重合体が分散してなる吸水性樹脂組成物
は、加熱あるいは溶媒等によって液状にすることによ
り、この吸水性樹脂組成物を、不織布やフィルム等の他
の基材に施し複合体とすることもできる。The water-absorbent resin composition in which the water-absorbent polymer is dispersed in the polydioxolane matrix is heated or liquefied by a solvent or the like to give the water-absorbent resin composition a nonwoven fabric or a film. It can also be applied to other base materials such as to form a composite.
【００３６】こうした複合体は、ポリジオキソランをバ
インダーとして吸水性重合体が基材に固着したものであ
り、従来の疎水性の接着剤やバインダーを用いたものと
比較して、吸水性の優れたものとなる。Such a composite has a water-absorbing polymer fixed to a substrate by using polydioxolane as a binder, and has excellent water-absorbing property as compared with a conventional one using a hydrophobic adhesive or binder. Will be things.
【００３７】本発明において、ポリジオキソランのマト
リックス表面に吸水性重合体が固着した吸水性組成物
も、好ましい形態である。この吸水性樹脂組成物は、ポ
リジオキソランの存在下吸水性重合体となる単量体を重
合したり、ポリジオキソランを所望の形状に成形した
後、そのマトリックス表面に吸水性重合体を接触せし
め、吸水性重合体をポリジオキソランのマトリックス表
面に埋め込んだり、あるいは接着剤などのバインダーを
介して固着する方法等により得られる。好ましくは、バ
インダー等を用いることなく吸水性重合体がポリジオキ
ソランのマトリックス表面に埋め込まれるなどして固着
したものである。このものは、例えばポリジオキソラン
をフィルムやシートや繊維に成形した後、吸水性重合体
をその上に散布したり吸水性重合体と混合したりして、
ポリジオキソランと吸水性重合体とを接触せしめ、つい
で加熱してポリジオキソランを軟化してマトリックス表
面に吸水性重合体を埋め込み、表面に固着せしめる。ま
た、ポリジオキソランを溶媒により軟化したのち、吸水
性重合体と接触せしめ表面に固着させることもできる。
吸水性重合体は、その一部が完全にマトリックス内に埋
め込まれたものでもよい。In the present invention, a water absorbing composition having a water absorbing polymer fixed on the surface of a polydioxolane matrix is also a preferred form. This water-absorbent resin composition is obtained by polymerizing a monomer to be a water-absorbent polymer in the presence of polydioxolane, or molding polydioxolane into a desired shape, and then contacting the water-absorbent polymer with the matrix surface thereof, It can be obtained by a method of embedding the water-absorbing polymer on the surface of the polydioxolane matrix, or by fixing it through a binder such as an adhesive. Preferably, the water-absorbing polymer is fixed by being embedded in the surface of the polydioxolane matrix without using a binder or the like. This is obtained by, for example, molding polydioxolane into a film, sheet or fiber, and then spraying a water-absorbent polymer thereon or mixing it with a water-absorbent polymer,
The polydioxolane and the water-absorbent polymer are brought into contact with each other, and then heated to soften the polydioxolane to embed the water-absorbent polymer on the matrix surface and fix it to the surface. It is also possible to soften the polydioxolane with a solvent and then bring it into contact with the water-absorbing polymer to fix it on the surface.
The water-absorbent polymer may be partially embedded in the matrix.
【００３８】ポリジオキソランと吸水性重合体の割合
は、目的や用途に応じ適宜設定できるが、一般にポリジ
オキソラン１００重量部に対し吸水性重合体が１〜２０
００重量部の範囲であり、好ましくは５〜１０００重量
部の範囲である。吸水性重合体の粒径や形状は特に制限
なく、粒径は一般に１〜１０００μｍの範囲であり、好
ましくは１０〜８５０μｍである。形状も不定形、球
状、鱗片状、繊維状等種々の形状の重合体を用いること
ができる。吸水性重合体は、表面架橋のなされたものを
用いることもできる。また、吸水速度や拡散性を向上さ
せるため、無機微粒子や界面活性剤、パルプ繊維等の添
加剤が加えられてもよい。The ratio of the polydioxolane to the water-absorbing polymer can be appropriately set depending on the purpose and application, but generally 1 to 20 parts by weight of the water-absorbing polymer are used per 100 parts by weight of polydioxolane.
It is in the range of 00 parts by weight, preferably in the range of 5 to 1000 parts by weight. The particle size and shape of the water-absorbent polymer are not particularly limited, and the particle size is generally in the range of 1 to 1000 μm, preferably 10 to 850 μm. Polymers having various shapes such as an amorphous shape, a spherical shape, a scaly shape, and a fibrous shape can be used. The water-absorbent polymer may be surface-crosslinked. Further, in order to improve the water absorption rate and diffusibility, additives such as inorganic fine particles, surfactants, pulp fibers and the like may be added.
【００３９】こうして得られる吸水性樹脂組成物は、吸
水性重合体がマトリックス表面に固着しているので、そ
の吸水速度が速く、またままこ等が生じにくく拡散性も
良好であるので、水性液体と接触すると全体にすばやく
拡散し該液体はすばやく吸収される。また、フィルムや
シートや繊維に成形することにより、取り扱い性や加工
性も良好なものとなる。そして、ポリジオキソランが熱
可塑性を有するので他の熱可塑性樹脂との複合化も容易
に行えるようになる。また、吸水性樹脂組成物そのもの
の加工も容易となる。In the water-absorbent resin composition thus obtained, since the water-absorbent polymer is fixed on the surface of the matrix, the water-absorbing speed is high, and the dampness is less likely to occur, and the diffusibility is good. When it comes into contact with the liquid, it quickly diffuses throughout and the liquid is absorbed quickly. Further, by forming it into a film, a sheet, or a fiber, the handleability and processability are improved. Further, since polydioxolane has thermoplasticity, it becomes easy to form a composite with another thermoplastic resin. Further, the water absorbent resin composition itself can be easily processed.
【００４０】本発明の別の好ましい形態として、吸水性
重合体の表面にポリジオキソランが被覆された吸水性樹
脂組成物が挙げられる。このものはポリジオキソランと
吸水性重合体を溶融混練したり、ポリジオキソランをク
ロロホルムや水などに溶解した後吸水性重合体を分散し
溶媒を除去したり、あるいは溶融したポリジオキソラン
や溶媒に分散したポリジオキソランを吸水性重合体に吹
き付けたりして得られる。また、吸水性重合体の存在下
に１，３−ジオキソランを重合したり、あるいはポリジ
オキソランの存在下に吸水性重合体の出発原料を重合す
ることによって得ることもできる。吸水性重合体とポリ
ジオキソランとの割合は、一般に吸水性重合体１００重
量部に対しポリジオキソラン０．０１〜５０重量部好ま
しくは０．１〜２０重量部の範囲である。吸水性重合体
の粒径や形状は特に制限なく、粒径は一般に１〜１００
０μｍの範囲であり、好ましくは１０〜８５０μｍの範
囲である。形状は不定形、球状、鱗片状、繊維状等種々
の形状の重合体を用いることができる。また、吸水性重
合体は表面架橋のなされたものを用いることもできる。
更に吸水速度や拡散性を向上させるため、無機微粒子や
界面活性剤、パルプ繊維等の添加剤が吸水性組成物に加
えられてもよい。Another preferred embodiment of the present invention is a water absorbent resin composition in which the surface of a water absorbent polymer is coated with polydioxolane. This product is obtained by melt-kneading polydioxolane and a water-absorbing polymer, dissolving polydioxolane in chloroform or water and then dispersing the water-absorbing polymer to remove the solvent, or dispersing in a melted polydioxolane or solvent. It can be obtained by spraying polydioxolane on a water-absorbing polymer. It can also be obtained by polymerizing 1,3-dioxolane in the presence of a water-absorbing polymer, or by polymerizing a starting material of the water-absorbing polymer in the presence of polydioxolane. The ratio of the water absorbent polymer to the polydioxolane is generally 0.01 to 50 parts by weight, preferably 0.1 to 20 parts by weight, based on 100 parts by weight of the water absorbent polymer. The particle size and shape of the water-absorbent polymer are not particularly limited, and the particle size is generally 1 to 100.
It is in the range of 0 μm, preferably in the range of 10 to 850 μm. Polymers having various shapes such as amorphous, spherical, scale-like, and fibrous can be used. Further, the water-absorbent polymer may be surface-crosslinked.
Further, in order to improve the water absorption rate and diffusibility, inorganic fine particles, additives such as surfactants and pulp fibers may be added to the water absorbing composition.
【００４１】吸水性重合体の表面にポリジオキソランが
被覆されていると、ポリジオキソランは吸湿した時にも
粘着性を有さないので、吸水性重合体が吸湿したときに
ケーティングを起こしたりすることがない。また、吸湿
したときの流動性も良好で取り扱い性も良いものとな
る。さらに水性液体と接触したときにもままこ現象やゲ
ルブロッキングが起こりにくくなり、ゲル化剤用吸収剤
や衛生材用吸収剤等に好適に用いることができる。When the surface of the water-absorbent polymer is coated with polydioxolane, the polydioxolane does not have tackiness even when it absorbs moisture, so that the water-absorbent polymer may cause coating when it absorbs moisture. There is no. In addition, when it absorbs moisture, the fluidity is good and the handleability is good. Further, when it comes into contact with an aqueous liquid, the residue or gel blocking hardly occurs, and it can be suitably used as an absorbent for gelling agents, absorbent for sanitary materials, and the like.
【００４２】また本発明の好ましい形態の一つとして、
吸水性重合体がポリジオキソランをバインダーとして凝
集あるいは造粒体を形成した吸水性組成物が挙げられ
る。このものは、例えばポリジオキソランと吸水性重合
体とを加熱下に溶融混練し、所望とする大きさまで解砕
したり、あるいはポリジオキソランをクロロホルムや水
等の溶媒に溶解し吸水性重合体と混合し、溶媒を除去
し、所望とする大きさまで解砕して得られる。また、吸
水性重合体の存在下に１，３−ジオキソランを重合した
り、あるいはポリジオキソランの存在下に吸水性重合体
の出発原料を重合することによって得ることもできる。
吸水性重合体とポリジオキソランとの割合は、一般に吸
水性重合体１００重量部に対しポリジオキソラン０．０
１〜５０重量部好ましくは１〜２０重量部の範囲であ
る。得られる凝集体や造粒体の大きさは特に制限なく、
用いる吸水性重合体の粒径や形状やその用途や目的によ
り適宜設定できるが、造粒体の場合１０〜１０００μ
ｍ、好ましくは２０〜８５０μｍの範囲であり、凝集体
の場合、厚さは０．１〜５ｍｍ、好ましくは０．１〜２
ｍｍの範囲である。形状も不定形、球状、鱗片状、繊維
状等種々の形状の重合体を用いることができる。As one of the preferred embodiments of the present invention,
An example is a water-absorbent composition in which the water-absorbent polymer is aggregated or formed into granules using polydioxolane as a binder. For example, polydioxolane and a water-absorbing polymer are melt-kneaded under heating and crushed to a desired size, or polydioxolane is dissolved in a solvent such as chloroform or water and mixed with the water-absorbing polymer. Then, the solvent is removed, and the product is crushed to a desired size. It can also be obtained by polymerizing 1,3-dioxolane in the presence of a water-absorbing polymer, or by polymerizing a starting material of the water-absorbing polymer in the presence of polydioxolane.
The ratio of the water-absorbent polymer and the polydioxolane is generally 0.09% of the polydioxolane based on 100 parts by weight of the water-absorbent polymer.
1 to 50 parts by weight, preferably 1 to 20 parts by weight. The size of the obtained aggregate or granule is not particularly limited,
It can be appropriately set depending on the particle size and shape of the water-absorbing polymer to be used and its use and purpose, but in the case of a granulated product, 10 to 1000 μ
m, preferably 20 to 850 μm, and in the case of agglomerates, the thickness is 0.1 to 5 mm, preferably 0.1 to 2 mm.
The range is mm. Polymers having various shapes such as an amorphous shape, a spherical shape, a scaly shape, and a fibrous shape can be used.
【００４３】また、吸水性重合体は、表面架橋のなされ
たものを用いることもできる。そして吸水速度や拡散性
を向上させるため、前記のごとき無機微粒子や界面活性
剤、パルプ繊維等の添加剤が吸水性組成物に加えられて
もよい。The water-absorbent polymer may be surface-crosslinked. Then, in order to improve the water absorption rate and the diffusibility, the above-mentioned inorganic fine particles, an additive such as a surfactant and pulp fiber may be added to the water absorbing composition.
【００４４】この吸水性樹脂組成物は、バインダーであ
るポリジオキソランが吸水性重合体の吸水性を阻害しな
いので、吸水時にままこ現象を生じたりすることがなく
優れた吸水特性を有するものである。また、比較的細か
い粒径の吸水性重合体が集合していると、同じ大きさの
吸水性重合体と比較して吸水速度が速いものとなる。This water-absorbent resin composition has excellent water-absorbing properties, because polydioxolane, which is a binder, does not impair the water-absorbing property of the water-absorbing polymer, and thus does not cause a trapping phenomenon during water absorption. . In addition, when water-absorbing polymers having a relatively small particle size are aggregated, the water-absorbing rate is higher than that of water-absorbing polymers having the same size.
【００４５】また、粒径の細かい吸水性重合体を造粒す
れば、吸水性重合体の微粉を取り扱わずにすむので、作
業性や取り扱い性が向上する。また、粉塵の浮遊を抑止
することもできる。また、他の水溶性重合体、例えばポ
リエチレンオキサイド等とは異なり、ポリジオキソラン
が吸湿時にタックを示さないので、吸湿流動性も良好と
なる。そして、ポリジオキソランは熱可塑性を有するの
で加熱による他の材料との複合化も容易に行えるように
なる。When the water-absorbent polymer having a small particle size is granulated, fine powder of the water-absorbent polymer is not required to be handled, so that workability and handleability are improved. It is also possible to prevent the dust from floating. Further, unlike other water-soluble polymers such as polyethylene oxide, polydioxolane does not exhibit tack at the time of moisture absorption, so that the hygroscopic fluidity becomes good. Since polydioxolane has thermoplasticity, it can be easily combined with another material by heating.
【００４６】この発明の吸水性樹脂組成物には種々の添
加剤を加えることができる。添加剤としては、シリカ微
粒子、酸化チタン、酸化亜鉛、酸化マグネシウム、炭酸
カルシウム、タルク、けい藻土等、鉄粉に代表される無
機微粒子、有機微粒子、フィラー、ソルビタン脂肪エス
テル、しょ糖脂肪酸エステル、ポリオキシアルキレンア
ルキルエーテル、ポリオキシアルキレンアシルエステル
等に代表される界面活性剤、テトラクロロイソフタロニ
トリル、チアベンダゾール、ジンクピリチオン等に代表
される防かび剤や抗菌剤、防腐剤、金属フタロシアニン
等に代表される消臭剤、グリセリン、ポリエチレングリ
コール、ジオクチルフタレート等に代表される可塑剤、
スルファミン酸グアニジンおよびその誘導体、リン酸グ
アニジンおよびその誘導体、トリエチルフォスフェート
およびトリスクロロエチルフォスフェート等のリン酸エ
ステルに代表される難燃剤、塩化リチウムや塩化マグネ
シウムや塩化カルシウム等の潮解性無機塩や乳酸ナトリ
ウム等に代表される吸湿剤、ヒドロキシエチルセルロー
ス、カルボキシメチルセルロース、ポリビニルアルコー
ル、ポリアクリル酸塩等の合成高分子、各種医薬品、農
薬、肥料、着色剤、パルプ、活性炭、ガス吸着剤等が挙
げられる。これら添加剤の添加量は特にに制限ないが、
一般に吸水性組成物１重量部に対し、０．０００１〜１
００重量部の範囲であり、好ましくは０．００１〜１０
重量部の範囲である。Various additives can be added to the water absorbent resin composition of the present invention. As the additive, silica fine particles, titanium oxide, zinc oxide, magnesium oxide, calcium carbonate, talc, diatomaceous earth, etc., inorganic fine particles represented by iron powder, organic fine particles, filler, sorbitan fatty ester, sucrose fatty acid ester, poly Surfactants represented by oxyalkylene alkyl ethers, polyoxyalkylene acyl esters, etc., fungicides represented by tetrachloroisophthalonitrile, thiabendazole, zinc pyrithione, etc., antibacterial agents, preservatives, represented by metal phthalocyanines, etc. Deodorant, plasticizer represented by glycerin, polyethylene glycol, dioctyl phthalate, etc.,
Guanidine sulfamate and its derivatives, guanidine phosphate and its derivatives, flame retardants typified by phosphoric acid esters such as triethyl phosphate and trischloroethyl phosphate, deliquescent inorganic salts such as lithium chloride, magnesium chloride and calcium chloride, Hygroscopic agents represented by sodium lactate, synthetic polymers such as hydroxyethyl cellulose, carboxymethyl cellulose, polyvinyl alcohol, polyacrylic acid salts, various pharmaceuticals, agricultural chemicals, fertilizers, coloring agents, pulp, activated carbon, gas adsorbents and the like. . The amount of these additives added is not particularly limited,
Generally, 0.0001 to 1 to 1 part by weight of the water absorbing composition
It is in the range of 00 parts by weight, preferably 0.001 to 10
The range is parts by weight.
【００４７】[0047]
【実施例】以下、実施例により本発明をさらに説明する
が本発明がこれら実施例に限定されるものではない。The present invention will be further described below with reference to examples, but the present invention is not limited to these examples.
【００４８】参考例１ 攪拌機、温度計、窒素導入管および冷却管を備えた四つ
口フラスコを窒素置換し、１，３−ジオキソラン６０ｇ
を導入し、系を０℃に保持した。次に５％のリンタング
ステン酸／アセトン溶液０．３ｍｌを窒素雰囲気下攪拌
下添加し、重合を開始した。重合による発熱がピークを
迎えた後トリエチルアミン１ｍｌを添加して反応を停止
した。Reference Example 1 A four-necked flask equipped with a stirrer, a thermometer, a nitrogen introducing tube and a cooling tube was purged with nitrogen to obtain 60 g of 1,3-dioxolane.
Was introduced and the system was kept at 0 ° C. Next, 0.3 ml of a 5% phosphotungstic acid / acetone solution was added with stirring under a nitrogen atmosphere to initiate polymerization. After the heat generated by the polymerization reached a peak, 1 ml of triethylamine was added to stop the reaction.
【００４９】得られたポリジオキソランのジオキソラン
溶液を減圧乾燥機中１００℃にて５時間乾燥することに
よりポリジオキソラン（１）を得た。The obtained dioxolane solution of polydioxolane was dried in a vacuum dryer at 100 ° C. for 5 hours to obtain polydioxolane (1).
【００５０】得られたポリジオキソラン（１）のポリス
チレン換算数平均分子量は１０万であった。The polystyrene equivalent number average molecular weight of the obtained polydioxolane (1) was 100,000.
【００５１】参考例２ ７５％が水酸化ナトリウムにより中和された部分中和ア
クリル酸ナトリウムの単量体水溶液（単量体濃度３７重
量％）にＮ，Ｎ´−メチレンビスアクリルアミド０．１
モル％（対アクリル酸ナトリウム単量体）および過硫酸
ナトリウム１ｇ／モル（対アクリル酸ナトリウム単量
体）を添加し、次いで窒素ガスでモノマー水溶液中の溶
存酸素を除去した。この単量体水溶液を、窒素雰囲気
下、１２０℃に加熱されたステンレス製のスチールベル
ト上に滴下して薄膜重合した。重合後の重合体をベルト
からかきとって乾燥してから粉砕し、吸水性重合体
（Ａ）を得た。このものの生理食塩水の吸水倍率は４０
（ｇ／ｇ）、純水の吸水倍率は３００（ｇ／ｇ）であっ
た。Reference Example 2 N, N'-methylenebisacrylamide 0.1% was added to a monomer aqueous solution (monomer concentration 37% by weight) of partially neutralized sodium acrylate in which 75% was neutralized with sodium hydroxide.
Mol% (to sodium acrylate monomer) and sodium persulfate 1 g / mol (to sodium acrylate monomer) were added, and then dissolved oxygen was removed from the aqueous monomer solution with nitrogen gas. This monomer aqueous solution was dropped onto a stainless steel belt heated to 120 ° C. under a nitrogen atmosphere to perform thin film polymerization. The polymer after polymerization was scraped off from the belt, dried and then pulverized to obtain a water-absorbent polymer (A). This product has a water absorption capacity of 40
(G / g), the water absorption capacity of pure water was 300 (g / g).
【００５２】引き続きこのものを２００メッシュの篩で
篩い吸水性重合体（Ａ−１）を得た。Subsequently, this was sieved with a 200-mesh sieve to obtain a water-absorbent polymer (A-1).
【００５３】参考例３ 参考例２で得た吸水性重合体（Ａ）１００部にエチレン
グリコールジグリシジルエーテル０．１部、水５部、イ
ソプロピルアルコール１部を混合し、得られた混合物を
乾燥機中に１００℃、３０分間加熱処理を行ない、吸水
性重合体（Ｂ）を得た。このものの生理食塩水の吸水倍
率は３８（ｇ／ｇ）、純水の吸水倍率は２８０（ｇ／
ｇ）であった。Reference Example 3 100 parts of the water-absorbent polymer (A) obtained in Reference Example 2 was mixed with 0.1 part of ethylene glycol diglycidyl ether, 5 parts of water and 1 part of isopropyl alcohol, and the resulting mixture was dried. Heat treatment was carried out in the machine at 100 ° C. for 30 minutes to obtain a water absorbent polymer (B). The water absorption capacity of this product is 38 (g / g), and the water absorption capacity of pure water is 280 (g / g).
g).
【００５４】引き続きこのものを２００メッシュ、１４
０メッシュ、１００メッシュの篩いで篩い、吸水性重合
体（Ｂ−１）、（Ｂ−２）、（Ｂ−３）を得た。Subsequently, this product was treated with 200 mesh, 14
Sieving with a 0 mesh or 100 mesh sieve gave water-absorbent polymers (B-1), (B-2) and (B-3).
【００５５】参考例４ ７５％が水酸化ナトリウムにより中和された部分中和ア
クリル酸ナトリウムの単量体水溶液（単量体濃度３７重
量％）にポリエチレングリコールジアクリレート（平均
エチレンオキサイド鎖数８）０．１モル％（対アクリル
酸ナトリウム単量体）および過硫酸ナトリウム０．０２
ｇ／モル（対アクリル酸ナトリウム単量体）を添加し、
次いで窒素ガスでモノマー水溶液中の溶存酸素を除去し
た。Reference Example 4 Polyethylene glycol diacrylate (average ethylene oxide chain number: 8) was added to an aqueous monomer solution of partially neutralized sodium acrylate 75% neutralized with sodium hydroxide (monomer concentration 37% by weight). 0.1 mol% (to sodium acrylate monomer) and sodium persulfate 0.02
g / mol (to sodium acrylate monomer) was added,
Then, dissolved oxygen in the monomer aqueous solution was removed with nitrogen gas.
【００５６】攪拌機、還流冷却器、温度計、窒素ガス導
入管および滴下ロートを備えた２リットルの四つ口セパ
ラブルフラスコにシクロヘキサン１リットルをとり、分
散剤としてソルビタンモノステアレート４ｇを加えて、
窒素ガスを吹き込み溶存酸素を追いだした。1 liter of cyclohexane was placed in a 2-liter four-necked separable flask equipped with a stirrer, a reflux condenser, a thermometer, a nitrogen gas introducing tube and a dropping funnel, and 4 g of sorbitan monostearate was added as a dispersant.
Nitrogen gas was blown in to drive out the dissolved oxygen.
【００５７】次いで、シクロヘキサンの温度を、５５℃
に昇温し前記単量体水溶液を滴下し、２００ｒｐｍで攪
拌することにより分散させた。その後浴温を５５℃に保
ち重合反応を開始させた後１時間この温度に保ち重合を
完結させた。重合終了後、共沸脱水により大部分の水分
を取り除いた後、濾過し、さらに８０℃で減圧乾燥さ
せ、吸収性重合体（Ｃ）を得た。このものの生理食塩水
の吸水倍率は４５（ｇ／ｇ）であり、純水の吸水倍率は
３５０（ｇ／ｇ）であった。Then, the temperature of cyclohexane is set to 55.degree.
The temperature was raised to 1, the above aqueous monomer solution was added dropwise, and the mixture was dispersed by stirring at 200 rpm. After that, the bath temperature was kept at 55 ° C. to start the polymerization reaction, and then this temperature was kept for 1 hour to complete the polymerization. After completion of the polymerization, most of the water was removed by azeotropic dehydration, followed by filtration and further drying under reduced pressure at 80 ° C. to obtain an absorbent polymer (C). The water absorption capacity of this product was 45 (g / g), and the water absorption capacity of pure water was 350 (g / g).
【００５８】引き続きこのものを２００メッシュの篩で
篩い吸水性ポリマー（Ｃ−１）を得た。Subsequently, this was sieved with a 200-mesh sieve to obtain a water-absorbent polymer (C-1).
【００５９】実施例１ 参考例１で得たポリジオキソラン（１）１０重量部をク
ロロホルム４０重量部に加え溶解した後、参考例２で得
た吸水性重合体（Ａ−１）を１０重量部加え均一に分散
した。このものを離型紙上にバーコーターで塗工した後
クロロホルムを除去し、離型紙から剥がし本発明の吸水
性樹脂組成物（１）を得た。得られた吸水性樹脂組成物
の厚さは１００μｍであった。得られた吸水性組成物の
吸収速度を表１に示す。Example 1 10 parts by weight of the polydioxolane (1) obtained in Reference Example 1 was added to 40 parts by weight of chloroform and dissolved, and then 10 parts by weight of the water-absorbent polymer (A-1) obtained in Reference Example 2 was added. The mixture was uniformly dispersed. This was coated on a release paper with a bar coater, chloroform was removed, and the release paper was peeled off to obtain a water absorbent resin composition (1) of the present invention. The thickness of the obtained water absorbent resin composition was 100 μm. The absorption rate of the resulting water absorbent composition is shown in Table 1.
【００６０】なお、表１に示した吸収速度は次の方法に
より行なった。The absorption rates shown in Table 1 were measured by the following method.
【００６１】（吸収速度）直径４５ｍｍに切り取った吸
水性組成物に生理食塩水（０．９重量％塩化ナトリウム
水溶液）１ｍｌを加え、吸水性組成物に生理食塩水が吸
収される時間を測定し、吸収速度を求めた。(Absorption rate) 1 ml of physiological saline (0.9 wt% sodium chloride aqueous solution) was added to the water absorbing composition cut into a diameter of 45 mm, and the time taken for the physiological saline to be absorbed by the water absorbing composition was measured. , The absorption rate was determined.
【００６２】実施例２〜４ 実施例１において吸水性重合体（Ａ−１）に代えて参考
例３で得た吸水性重合体（Ｂ−１）、（Ｂ−２）および
（Ｂ−３）、をそれぞれ用いた以外は、実施例１と同様
にして本発明の吸水性樹脂組成物（２）〜（４）を得
た。得られた吸水性樹脂組成物（２）〜（４）の厚さは
それぞれ１００，２１０、および２５０μｍであった。
得られた吸水性樹脂組成物の吸収速度を表１に示す。Examples 2 to 4 In place of the water absorbent polymer (A-1) in Example 1, the water absorbent polymers (B-1), (B-2) and (B-3) obtained in Reference Example 3 were used. ) And were used in the same manner as in Example 1 to obtain water-absorbent resin compositions (2) to (4) of the present invention. The water-absorbent resin compositions (2) to (4) obtained had thicknesses of 100, 210, and 250 μm, respectively.
The absorption rate of the resulting water absorbent resin composition is shown in Table 1.
【００６３】実施例５ 実施例１において吸水性重合体（Ａ−１）に代えて、参
考例４で得た吸水性重合体（Ｃ−１）を用いた以外は、
実施例１と同様にして本発明の吸水性樹脂組成物（５）
を得た。得られた吸水性樹脂組成物（５）の厚さは１１
０μｍであった。このものは表面が平滑で風合いの良好
なフィルムであった。得られた吸水性樹脂組成物の吸収
速度を表１に示す。Example 5 Except that the water absorbent polymer (A-1) in Example 1 was replaced by the water absorbent polymer (C-1) obtained in Reference Example 4,
Similar to Example 1, the water absorbent resin composition (5) of the present invention
I got The thickness of the resulting water absorbent resin composition (5) was 11
It was 0 μm. This film was a film having a smooth surface and a good texture. The absorption rate of the resulting water absorbent resin composition is shown in Table 1.
【００６４】実施例６ 実施例１において吸水性重合体（Ａ−１）に対しシリカ
微粒子（商品名Ａ−２００：日本アエロジル株式会社
製）を０．５重量％添加した以外は、実施例１と同様に
して本発明の吸水性樹脂組成物（６）を得た。得られた
吸水性樹脂組成物（６）の厚さは９０μｍであった。得
られた吸水性樹脂組成物の吸収速度を表１に示す。Example 6 Example 1 was repeated except that 0.5% by weight of silica fine particles (trade name A-200: manufactured by Nippon Aerosil Co., Ltd.) was added to the water absorbent polymer (A-1). A water-absorbent resin composition (6) of the present invention was obtained in the same manner as in. The thickness of the resulting water absorbent resin composition (6) was 90 μm. The absorption rate of the resulting water absorbent resin composition is shown in Table 1.
【００６５】実施例７ 実施例１において吸水性重合体（Ａ−１）５０重量部を
加えた以外は、実施例１と同様にして本発明の吸水性樹
脂組成物（７）を得た。得られた吸水性樹脂組成物
（７）の厚さは２００μｍであった。得られた吸水性樹
脂組成物の吸収速度を表１に示す。Example 7 A water absorbent resin composition (7) of the present invention was obtained in the same manner as in Example 1 except that 50 parts by weight of the water absorbent polymer (A-1) was added. The water absorbent resin composition (7) obtained had a thickness of 200 μm. The absorption rate of the resulting water absorbent resin composition is shown in Table 1.
【００６６】実施例８ 実施例１において吸水性重合体（Ａ−１）に代えて吸水
性重合体（Ａ）を微粉砕し、４００メッシュの篩で篩っ
た吸水性重合体（Ａ−４、平均粒径２０μｍ）を用いた
以外は、実施例１と同様にして本発明の吸水性樹脂組成
物（８）を得た。得られた吸水性樹脂組成物（８）の厚
さは３０μｍであった。得られた吸水性樹脂組成物の吸
収速度を表１に示す。Example 8 The water absorbent polymer (A-1) in Example 1 was replaced by finely pulverized water absorbent polymer (A) and sieved with a 400 mesh sieve (A-4). , And an average particle diameter of 20 μm) were used to obtain a water absorbent resin composition (8) of the present invention in the same manner as in Example 1. The water absorbent resin composition (8) thus obtained had a thickness of 30 μm. The absorption rate of the resulting water absorbent resin composition is shown in Table 1.
【００６７】実施例９ 参考例１で得たポリジオキソラン（１）１０重量部に参
考例２で得た吸水性重合体（Ａ−１）５重量部を加え８
０℃で加熱混練した。このものを１２０℃で熱プレスし
本発明の吸水性樹脂組成物（９）を得た。得られた吸水
性樹脂組成物（９）の厚さは５０μｍであった。得られ
た吸水性樹脂組成物の吸収速度を表１に示す。Example 9 To 10 parts by weight of the polydioxolane (1) obtained in Reference Example 1 was added 5 parts by weight of the water-absorbing polymer (A-1) obtained in Reference Example 8
The mixture was kneaded by heating at 0 ° C. This was hot-pressed at 120 ° C. to obtain a water absorbent resin composition (9) of the present invention. The water absorbent resin composition (9) obtained had a thickness of 50 μm. The absorption rate of the resulting water absorbent resin composition is shown in Table 1.
【００６８】比較例１〜３ 実施例１，２および５においてポリジオキソラン（１）
の代わりのポリエチレンオキサイド（平均分子量１５〜
４０万）を用いた以外は、同様にしてそれぞれ比較吸水
性樹脂組成物（１）、（２）および（３）を得た。得ら
れた比較吸水性樹脂組成物の厚さはそれぞれ１００、１
１０および１１０μｍであった。得られた比較吸水性樹
脂組成物は、本発明の吸水性樹脂組成物（１）〜（９）
と比較して、指で触るとべとつきがあり、粘着性を有す
るものであった。得られた比較吸水性樹脂組成物の吸収
速度を表１に示す。Comparative Examples 1-3 Polydioxolane (1) in Examples 1, 2 and 5
Of polyethylene oxide (average molecular weight 15-
Comparative water-absorbent resin compositions (1), (2) and (3) were obtained in the same manner except that (400,000) was used. The thickness of the obtained comparative water absorbent resin composition was 100 and 1 respectively.
10 and 110 μm. The comparative water absorbent resin composition thus obtained is the water absorbent resin composition (1) to (9) of the present invention.
Compared with, it was tacky to the touch with fingers and had tackiness. The absorption rate of the obtained comparative water absorbent resin composition is shown in Table 1.
【００６９】実施例１０ 参考例１で得たポリジオキソラン（１）１０重量部にク
ロロホルム４０重量部を加え溶解し、バーコーダーで離
型紙上に塗工した。引き続き参考例３で得た吸水性重合
体（Ｂ−３）５重量部を散布した後乾燥し溶媒を除去
し、本発明の吸水性樹脂組成物（１０）を得た。このも
のの厚さは１４０μｍであった。得られた吸水性樹脂組
成物の吸収速度を表１に示す。Example 10 40 parts by weight of chloroform was added to 10 parts by weight of the polydioxolane (1) obtained in Reference Example 1 and dissolved, and the solution was coated on a release paper with a bar coater. Subsequently, 5 parts by weight of the water-absorbent polymer (B-3) obtained in Reference Example 3 was sprayed and dried to remove the solvent, to obtain a water-absorbent resin composition (10) of the present invention. The thickness of this product was 140 μm. The absorption rate of the resulting water absorbent resin composition is shown in Table 1.
【００７０】実施例１１ 参考例１で得たポリジオキソランをＴダイ法によりフィ
ルムに成形した。このフィルムを８０℃に加熱しフィル
ム表面を軟化した後、吸水性重合体（Ｂ−３）を散布
し、本発明の吸水性樹脂組成物（１１）を得た。このも
のの厚さは２００μｍであった。得られた吸水性樹脂組
成物の吸収速度を表１に示す。Example 11 The polydioxolane obtained in Reference Example 1 was formed into a film by the T-die method. This film was heated to 80 ° C. to soften the film surface, and then the water-absorbent polymer (B-3) was sprayed to obtain the water-absorbent resin composition (11) of the present invention. The thickness of this product was 200 μm. The absorption rate of the resulting water absorbent resin composition is shown in Table 1.
【００７１】比較例４ 実施例１１においてポリジオキソラン（１）の代わりに
ポリエチレンオキサイド（１）を用いた他は実施例１１
と同様にして比較吸水性樹脂組成物（４）を得た。この
ものの厚さは１３０μｍであった。得られた比較吸水性
樹脂組成物の吸収速度を表１に示す。Comparative Example 4 Example 11 was repeated except that polyethylene oxide (1) was used in place of polydioxolane (1) in Example 11.
A comparative water absorbent resin composition (4) was obtained in the same manner as in. This had a thickness of 130 μm. The absorption rate of the obtained comparative water absorbent resin composition is shown in Table 1.
【００７２】[0072]
【表１】 [Table 1]
【００７３】実施例１２ 参考例１で得たポリジオキソラン（１）１０重量部に参
考例３で得た吸水性重合体（Ｂ−１）５重量部を加え８
０℃で加熱混練した。このものを０．１ｍｍのダイスか
ら押し出し、繊維状の吸水性樹脂組成物（１２）を得
た。この吸水性樹脂組成物０．１ｇを１ｍｌの生理食塩
水に浸漬したところ２０秒で吸水した。Example 12 To 10 parts by weight of the polydioxolane (1) obtained in Reference Example 1 was added 5 parts by weight of the water-absorbing polymer (B-1) obtained in Reference Example 3 to give 8 parts.
The mixture was kneaded by heating at 0 ° C. This was extruded from a 0.1 mm die to obtain a fibrous water absorbent resin composition (12). When 0.1 g of this water absorbent resin composition was immersed in 1 ml of physiological saline, it absorbed water in 20 seconds.
【００７４】実施例１３ 参考例１で得たポリジオキソラン（１）１０重量部をク
ロロホルム５００重量部に加え溶解した後、参考例２で
得た吸水性重合体（Ａ）１００重量部を加え、攪拌した
後濾過した。濾物を乾燥し解砕し本発明の吸水性樹脂組
成物（１３）を得た。このものを以下に示すＶＯＲＴＥ
Ｘ吸水速度を測定したところ、吸水速度は１２秒であっ
た。Example 13 10 parts by weight of the polydioxolane (1) obtained in Reference Example 1 was added to 500 parts by weight of chloroform and dissolved, and then 100 parts by weight of the water-absorbing polymer (A) obtained in Reference Example 2 was added. After stirring, it was filtered. The residue was dried and crushed to obtain the water absorbent resin composition (13) of the present invention. This is VORTE shown below
When the X water absorption rate was measured, the water absorption rate was 12 seconds.
【００７５】（ＶＯＲＴＥＸ吸水速度）１００ｍｌのビ
ーカーに生理食塩水５０ｍｌを加え、スターラーピース
で攪拌した（攪拌速度毎分６００回転）。この中に吸水
性組成物２ｇを加え、吸水組成物が膨潤して渦が消える
までの時間を測定し、ＶＯＲＴＥＸ吸水速度を求めた。(VORTEX water absorption rate) 50 ml of physiological saline was added to a 100 ml beaker and stirred with a stirrer piece (stirring speed of 600 rpm). 2 g of the water absorbing composition was added thereto, and the time until the water absorbing composition swelled and the vortex disappeared was measured to determine the VORTEX water absorbing speed.
【００７６】比較例５ 参考例２で得た吸水性重合体（Ａ）のＶＯＲＴＥＸ吸水
速度は６６秒であった。Comparative Example 5 The VORTEX water absorption rate of the water absorbent polymer (A) obtained in Reference Example 2 was 66 seconds.
【００７７】比較例６ 実施例１３においてポリジオキソラン（１）に代えてポ
リエチレンオキサイド（１）を用いた以外は、実施例１
３と同様にして比較吸水性樹脂組成物（５）を得た。こ
のもののＶＯＲＴＥＸ吸水速度は９０秒であった。Comparative Example 6 Example 1 was repeated except that polyethylene oxide (1) was used instead of polydioxolane (1) in Example 13.
Comparative water absorbent resin composition (5) was obtained in the same manner as in 3. This product had a VORTEX water absorption rate of 90 seconds.
【００７８】実施例１４ 参考例１で得たポリジオキソランを６０℃の温水に溶解
しポリジオキソランの１０重量％水溶液を調製した。こ
の水溶液５重量部を参考例３で得た吸水性重合体（Ｂ）
１００重量部に攪拌下添加し、９０℃で乾燥した後解砕
し、本発明の吸水性樹脂組成物（１４）を得た。このも
ののＶＯＲＴＥＸ吸水速度は１０秒であった。Example 14 The polydioxolane obtained in Reference Example 1 was dissolved in warm water at 60 ° C. to prepare a 10 wt% aqueous solution of polydioxolane. Water-absorbent polymer (B) obtained in Reference Example 3 with 5 parts by weight of this aqueous solution
100 parts by weight was added with stirring, dried at 90 ° C., and then crushed to obtain a water absorbent resin composition (14) of the present invention. The VORTEX water absorption rate of this product was 10 seconds.
【００７９】この吸水性樹脂組成物（１４）１０ｇを１
００ｍｌのビーカーにいれ、左右に振ったが発塵は全く
なかった。引き続きこのものを温度２５℃相対湿度６０
％の恒温恒湿機内に８時間放置した後、ビーカーを傾け
たところさらさらと流れ、流動性は良好であった。10 g of this water absorbent resin composition (14)
It was placed in a 00 ml beaker and shaken left and right, but no dust was generated. Continue this at a temperature of 25 ° C and a relative humidity of 60.
After being left for 8 hours in a constant temperature and humidity chamber, the beaker was tilted and flowed smoothly, and the fluidity was good.
【００８０】比較例７ 実施例１４においてポリジオキソラン（１）に代えてポ
リエチレンオキサイド（１）を用いた以外は、実施例１
４と同様にして比較吸水樹脂組成物（６）を得た。この
もののＶＯＲＴＥＸ吸水速度は７０秒であった。Comparative Example 7 Example 1 was repeated except that polyethylene oxide (1) was used instead of polydioxolane (1) in Example 14.
Comparative water absorbent resin composition (6) was obtained in the same manner as in 4. This product had a VORTEX water absorption rate of 70 seconds.
【００８１】この比較吸水性組成物（６）１０ｇを１０
０ｍｌのビーカーにいれ、左右に振ったが発塵はほとん
どなかった。引き続きこのものを温度２５℃相対湿度６
０％の恒温恒湿機内に８時間放置した後、ビーカーを傾
けたところ、重合体は一体化し固まりとなった。10 g of this comparative water absorbing composition (6)
It was placed in a 0 ml beaker and shaken to the left and right, but almost no dust was generated. Continue this at a temperature of 25 ° C and a relative humidity of 6
After being left in a 0% constant temperature and humidity chamber for 8 hours, when the beaker was tilted, the polymer was integrated and solidified.
【００８２】比較例８ 参考例３で得た吸水性重合体（Ｂ）１０ｇを１００ｍｌ
のビーカーに入れ、左右に振ったところ、重合体が中に
舞い発塵が生じた。引き続きこのものを温度２５℃相対
湿度６０％の恒温恒湿機内に８時間放置した後、ビーカ
ーを傾けたところ、重合体は一体化し固まりとなってい
た。Comparative Example 8 100 ml of 10 g of the water-absorbent polymer (B) obtained in Reference Example 3
When placed in a beaker and shaken left and right, the polymer flew in and dust was generated. Subsequently, this was left for 8 hours in a thermo-hygrostat at a temperature of 25 ° C. and a relative humidity of 60%, and the beaker was tilted. As a result, the polymer was integrated and solidified.
【００８３】[0083]
【発明の効果】本発明による吸水性樹脂組成物は、前記
のごとき構成を有しているので、つぎのごとき利点があ
る。Since the water absorbent resin composition according to the present invention has the constitution as described above, it has the following advantages.
【００８４】１．ポリジオキソランが吸水性重合体の吸
水性を阻害しないので、吸水時の拡散性が良好となり、
ままこの発生やゲルブロッキングを防止できるので、吸
水特性の優れた吸水性樹脂組成物となる。1. Since polydioxolane does not hinder the water absorption of the water-absorbing polymer, the diffusivity at the time of water absorption becomes good,
Since this generation and gel blocking can be prevented as it is, the water absorbent resin composition has excellent water absorbing properties.
【００８５】２．ポリジオキソランが熱可塑性を有する
ので、目的や用途に応じてシート状、フィルム状、繊維
状、粒状、袋状等種々の形状への加工や成形が容易に行
うことができる。2. Since polydioxolane has thermoplasticity, it can be easily processed and molded into various shapes such as a sheet shape, a film shape, a fibrous shape, a granular shape, and a bag shape depending on the purpose and application.
【００８６】３．ポリジオキソランが熱可塑性を有する
ので、他の材料特に熱可塑性樹脂からなる基材との複合
化が容易に行なうことができる。3. Since polydioxolane has thermoplasticity, it can be easily formed into a composite with another material, particularly a base material made of a thermoplastic resin.
【００８７】４．吸水性樹脂組成物の形状がシート状や
フィルム状であると、粉体等を扱わずにすみ取り扱い性
が良好となる。4. When the shape of the water-absorbent resin composition is a sheet or film, the handling property is good without handling powders and the like.
【００８８】５．ポリジオキソランが成膜性を有するの
で、フィルム化やシート化が容易となり取り扱い性が良
好となる。5. Since polydioxolane has a film forming property, it can be easily formed into a film or a sheet, and the handleability becomes good.
【００８９】６．吸水性樹脂組成物が液状であると、他
の基材に施すことにより吸水性の良好な吸水樹脂複合体
を容易に得ることができる。6. When the water-absorbent resin composition is in a liquid state, a water-absorbent resin composite having good water-absorbent property can be easily obtained by applying it to another substrate.
【００９０】７．ポリジオキソランは高湿度雰囲気下に
おいても吸湿性が低く吸湿時に粘着性を示さないので、
吸湿したときにケーキングを起こしたりすることがな
く、取り扱い性が良好となる。また、吸湿時の流動性も
良好なものとなる。7. Since polydioxolane has low hygroscopicity even in a high humidity atmosphere and does not show tackiness when it absorbs moisture,
Caking does not occur when moisture is absorbed, and the handleability is good. Further, the fluidity when absorbing moisture is also good.
【００９１】８．ポリジオキソランと吸水性重合体とか
らなるので、発塵を防止することができる。8. Since it is composed of polydioxolane and a water-absorbing polymer, it is possible to prevent dust generation.
【００９２】従って、この発明の吸水性樹脂組成物は、
紙おむつやナプキンや包帯等の衛生材料のみならず、食
品の鮮度保持やドリップ吸収、包装材料、結露防止材、
電線や通信ケーブル用止水材、シーリング材、保冷材、
人工雪、コンクリート混和・改質剤、セメントブリージ
ング水の吸収、農園芸用保水材、カイロ用保水材、油の
脱水材、バッテリーセパレーター、靴の中敷き、消臭
剤、芳香剤、人工雪、防音材、防振材、人工水晶体、人
工関節用ゲル、ドラッグデリバリー用重合体、パップ材
等各種用途に用いることができる。本発明の吸水性樹脂
組成物の用途がこれら用途に限定されるものではない。Therefore, the water absorbent resin composition of the present invention is
Not only hygiene materials such as paper diapers, napkins and bandages, but also food freshness retention, drip absorption, packaging materials, anti-condensation materials,
Water blocking materials for electric wires and communication cables, sealing materials, cold insulation materials,
Artificial snow, concrete admixture / modifier, absorption of cement breathing water, water retention material for agriculture and horticulture, water retention material for body warmers, oil dehydration material, battery separator, insole, deodorant, fragrance, artificial snow, soundproofing It can be used for various purposes such as materials, anti-vibration materials, artificial lenses, gels for artificial joints, polymers for drug delivery, and pap materials. The use of the water absorbent resin composition of the present invention is not limited to these uses.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｂ０１Ｊ 20/26 Ｄ Ｃ０８Ｊ 5/18 ＣＥＺ Ｃ０８Ｌ 101/14 ＬＴＢ ─────────────────────────────────────────────────── ─── Continuation of the front page (51) Int.Cl. 6 Identification number Office reference number FI Technical display location B01J 20/26 D C08J 5/18 CEZ C08L 101/14 LTB
Claims (6)
含んでなる吸水性樹脂組成物。1. A water absorbent resin composition comprising polydioxolane and a water absorbent polymer.
水性重合体が分散されてなる請求項１に記載の吸水性樹
脂組成物。2. The water absorbent resin composition according to claim 1, wherein the water absorbent polymer is dispersed in a polydioxolane matrix.
吸水性重合体が分散して固着されてなる請求項１に記載
の吸水性樹脂組成物。3. The water absorbent resin composition according to claim 1, wherein the water absorbent polymer is dispersed and fixed on the surface of the polydioxolane matrix.
ム状または繊維状である請求項１ないし３のいずれかに
一つに記載の吸水性樹脂組成物。4. The water absorbent resin composition according to claim 1, wherein the composition has a sheet shape, a film shape, or a fibrous shape.
が被覆されてなる請求項１に記載の吸水性樹脂組成物。5. The water absorbent resin composition according to claim 1, wherein the surface of the water absorbent polymer is coated with polydioxolane.
水性重合体が凝集体ないし造粒体を形成してなる請求項
１に記載の吸水性樹脂組成物。6. The water-absorbent resin composition according to claim 1, wherein the water-absorbent polymer forms an aggregate or a granule using polydioxolane as a binder.