JPH082690B2 - recoding media - Google Patents
recoding mediaInfo
- Publication number
- JPH082690B2 JPH082690B2 JP61122746A JP12274686A JPH082690B2 JP H082690 B2 JPH082690 B2 JP H082690B2 JP 61122746 A JP61122746 A JP 61122746A JP 12274686 A JP12274686 A JP 12274686A JP H082690 B2 JPH082690 B2 JP H082690B2
- Authority
- JP
- Japan
- Prior art keywords
- layer
- recording medium
- resin
- thermosensitive coloring
- thermosensitive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【発明の詳細な説明】 （産業上の利用分野） 本発明は、情報の記録再生が可能な記録媒体に関す
る。TECHNICAL FIELD The present invention relates to a recording medium capable of recording and reproducing information.
（従来の技術） ロイコ染料、ジアゾ化合物等よりなる感熱発色層を基
材に設けた感熱記録媒体はサーマルヘッド等による加熱
により情報が容易に感熱発色層に記録され、その記録方
法の簡便性により広く用いられている。しかしながら、
これらに記録される情報は、目視不可能に記録できない
ため、第三者に見られても差し支えのない内容のものに
限られ、一般の磁気カードに記録されるような第三者に
知られると不都合の生じる重要な情報は記録することが
できなかった。すなわち、記録方法の簡便さにかかわら
ず目視で判別できない情報を有することができる偽造防
止性にすぐれた記録媒体として感熱記録媒体を利用する
ことができなかった。(Prior art) A thermosensitive recording medium having a thermosensitive coloring layer composed of a leuco dye, a diazo compound or the like provided on a base material, information is easily recorded on the thermosensitive coloring layer by heating with a thermal head or the like. Widely used. However,
The information recorded on these is not visible and cannot be recorded, so it is limited to the contents that can be seen by a third party, and is known to third parties like those recorded on general magnetic cards. And important information that causes inconvenience could not be recorded. That is, it was not possible to use a heat-sensitive recording medium as a recording medium having excellent anti-counterfeit property that can have information that cannot be visually identified regardless of the simplicity of the recording method.
（発明が解決しようとする問題点） 本発明は上記の点に鑑みてなされたものである。(Problems to be Solved by the Invention) The present invention has been made in view of the above points.
本発明者は、従来公知のロイコ染料またはジアゾ化合
物からなる感熱発色層はインキ顔料を含む樹脂層からな
る隠蔽層をその層上に設けても、サーマルヘッドによ
り、良好に発色することに注目し、この現象を光学的記
録手段に利用することを考えて種々研究を行った。その
結果、感熱発色層、隠蔽層からなる積層体を形成して、
サーマルヘッドで情報パターンを印字すれば、感熱発色
層に発色により形成される情報パターンは隠蔽層により
目視できないが、赤外線を照射すると発色した部分は赤
外線の反射率が低く、未発色の部分とでは赤外線の反射
率が異なり、この反射率の差を利用して印字された情報
パターンを読み取ることができることを見出して本発明
に達し得たものである。The present inventor has noticed that the conventionally known thermosensitive coloring layer made of a leuco dye or a diazo compound provides good color development by a thermal head even if a concealing layer made of a resin layer containing an ink pigment is provided on the layer. , We have conducted various studies in consideration of utilizing this phenomenon for optical recording means. As a result, a laminate comprising a thermosensitive coloring layer and a hiding layer is formed,
When an information pattern is printed with a thermal head, the information pattern formed by coloring on the thermosensitive coloring layer cannot be visually observed due to the concealing layer, but the infrared-irradiated portion has a low infrared reflectance, and the uncolored portion is different from the uncolored portion. The present invention has been accomplished by finding out that the reflectance of infrared rays is different and the printed information pattern can be read by utilizing this difference in reflectance.
（問題点を解決するための手段） 本発明の記録媒体は、基材上に、ロイコ染料系感熱材
料またはジアゾ系感熱材料からなる感熱発色層および隠
蔽層が順次積層される記録媒体であって、該感熱発色層
には、加熱手段により、目視不可能な任意の情報パター
ンが記録され、赤外線照射により読み取り可能であるこ
とを特徴とするものである。(Means for Solving Problems) The recording medium of the present invention is a recording medium in which a thermosensitive coloring layer and a hiding layer made of a leuco dye-based thermosensitive material or a diazo-based thermosensitive material are sequentially laminated on a substrate. The thermosensitive coloring layer is characterized in that an arbitrary information pattern that cannot be visually observed is recorded by the heating means and can be read by infrared irradiation.
以下、実施例に基づいて本発明を詳細に説明する。 Hereinafter, the present invention will be described in detail based on examples.
第１図は、本発明の一実施例を示す断面図であり、基
材10上に、感熱発色層１、隠蔽層２および必要に応じて
設けられる保護層３が順次積層されている。FIG. 1 is a cross-sectional view showing an embodiment of the present invention, in which a thermosensitive coloring layer 1, a hiding layer 2 and a protective layer 3 provided as needed are sequentially laminated on a substrate 10.
基材10は基本的には、積層される各層を支持する働き
をするものであるが、その使用用途により種々の形状を
とることができ、例えば、他の物品等に本発明の記録媒
体を設けることを目的とした場合、又は磁気テープのよ
うな記録媒体を目的とした場合には薄いフィルム形状の
ものが適するし、それ自体で手軽な取扱いのできる記録
媒体として使用される場合にはカード形状すなわち一般
的なプラスチックカード用の形状、紙カード用の形状、
通帳用の形状、その他一般に使用されている記録媒体の
形状のものが適する。The base material 10 basically functions to support each layer to be laminated, but can have various shapes depending on the intended use, and for example, the recording medium of the present invention can be applied to other articles or the like. If it is intended to be provided, or if it is intended for a recording medium such as a magnetic tape, a thin film shape is suitable, and if it is used as a recording medium that can be easily handled by itself, a card Shape, that is, general plastic card shape, paper card shape,
A passbook shape or other generally used recording medium shape is suitable.
このような基材10の材質としては上記の理由から、様
々なものが使用できるが、例えば、ポリ塩化ビニル、ポ
リ塩化ビニリデン、ナイロン、セルロースジアセテー
ト、エチレンビニルアセテート、セルローストリアセテ
ート、ポリスチレン、ポリプロピレン、ポリエステル、
ポリイミド、ポリアミド、ポリメチルメタクリレート、
ポリアクリレート、ポリウレタン、アイオノマー、ポリ
カーボネート等のプラスチック類、銅、アルミニウム等
の金属、紙、含浸紙等を単独であるいは組合せて複合体
として用いることができる。基材として要求される物性
例えば強度、剛性等を考慮して、上記の材料の中から好
ましいものを適宜選択すればよい。Various materials can be used as the material of the base material 10 for the above reasons, and examples thereof include polyvinyl chloride, polyvinylidene chloride, nylon, cellulose diacetate, ethylene vinyl acetate, cellulose triacetate, polystyrene, and polypropylene. polyester,
Polyimide, polyamide, polymethylmethacrylate,
Plastics such as polyacrylate, polyurethane, ionomer and polycarbonate, metals such as copper and aluminum, paper, impregnated paper and the like can be used alone or in combination to form a composite. Considering the physical properties required for the base material, such as strength and rigidity, preferred materials may be appropriately selected from the above materials.
上記基材10上には、感熱発色層１が設けられている。
感熱発色層１はサーマルヘッドの加熱により発色して情
報が記録される情報記録層の働きをなすものであり、ロ
イコ染料系感熱材料またはジアゾ染料系感熱発色材料の
感熱発色材料および必要な添加剤を包合させたバインダ
ーから形成されている。The thermosensitive coloring layer 1 is provided on the base material 10.
The thermosensitive coloring layer 1 functions as an information recording layer that develops color by heating a thermal head to record information. The thermosensitive coloring material of a leuco dye-based thermosensitive material or a diazo dye-based thermosensitive coloring material and necessary additives. Is formed from a binder that has been incorporated.
感熱発色層１に用いられるロイコ染料系感熱発色材料
はロイコ染料と酸性物質からなるものが使用でき、例え
ば、ロイコ染料としては、トリフェニルメタン系染料
のロイコ体ベース;3,3′−ビス（ｐジメチルアミノフェ
ニル）フタリド、3,3′−ビス（ｐ−ジメチルアミノフ
ェニル）−６−ジメチルアミノフタリド、3,3′−ビス
（ｐ−ジメチルアミノフェニル）−６−ジエチルアミノ
フタリド、3,3′−ビス（ｐ−ジメチルアミノフェニ
ル）−６−クロルフタリド、3,3′−ビス（ｐ−ジブチ
ルアミノフェニル）フタリド等、フルオラン系染料の
ロイコ体ベース;6−シクロヘキシルアミノ−６−クロル
フルオラン、３−（N,N−ジメチルアミノ）−５−メチ
ル−７−（N,N−ジベンジルアミノ）フルオラン、３−
ジエチルアミノ−5,7−ジメチルフルオラン、３−ジエ
チルアミノ−７−メチルフルオラン、３−ジエチルアミ
ノ−7,8−ベンズフルオラン等、フルオラン系染料;3
−ジエチルアミノ−６−メチル−７−クロルフルオラ
ン、３−ピロリジノ−６−メチル−７−アニリノフルオ
ラン、２−〔Ｎ−（３′−トリフルオロメチルフエニ
ル）アミノ〕−６−ジエチルアミノフルオラン、２−3,
6−ビス（ジエチルアミノ）−９−（ｏ−クロルアリニ
ノ）キサンチル安息香酸ラクタム等、ラクトン化合
物;3−（２′−ヒドロキシ−４′−ジメチルアミノフェ
ニル）−３−（２′−メトキシ−５′−クロルフェニ
ル）フタリド、３−（２′−ヒドロキシ−４′−ジメチ
ルアミノフェニル）−３−（２′−メトキシ−５′−ニ
トロフェニル）フタリド、３−（２′−ヒドロキシ−
４′−ジメチルアミノフェニル）−３−（２′−メトキ
シ−５′−メチルフェニル）フタリド、３−（２′−メ
トキシ−４′−ジメチルアミノフェニル）−３−（２′
−ヒドロキシ−４′−クロル−５′−メチルフェニル）
フタリド等が使用できる。又、発色助剤である酸性物質
としては、ホウ酸、シュウ酸、マレイン酸、酒石酸、ク
エン酸、コハク酸、安息香酸、ステアリン酸、没食子
酸、サリチル酸、１−ヒドロキシ−２−ナフトエ酸、ｏ
−ヒドロキシ安息香酸、ｍ−ヒドロキシ安息香酸、2,4
ジヒドロキシ安息香酸、２−ヒドロキシ−Ｐ−トルイル
酸、3,5−キシレノール、チモール、ｐ−ｔ−ブチルフ
ェノール、４−ヒドロキシフェノキシド、メチル−４−
ヒドロキシベンゾエート、４−ヒドロキシアセトフェノ
ン、α−テフトール、β−ナフトール、カテコール、レ
ゾルシン、ヒドロキシノン、４−ｔ−オクチルカテコー
ル、4,4′−sec−ブチリデンフェノール、2,2′−ヒド
ロキシジフェニル、2,2′−メチレンビス（４−メチル
−６−ｔ−ブチルフェノール）、2,2′−ビス（４′−
ヒドロキシフェニル）プロパン、4,4′−sec−ブチリデ
ンジフェノール、ピロガロール、フロログリシン、フロ
ログリシンカルボン酸等が使用できる。The leuco dye-based thermosensitive coloring material used in the thermosensitive coloring layer 1 may be a leuco dye and an acidic substance. For example, the leuco dye may be a leuco base of a triphenylmethane dye: 3,3'-bis ( p dimethylaminophenyl) phthalide, 3,3′-bis (p-dimethylaminophenyl) -6-dimethylaminophthalide, 3,3′-bis (p-dimethylaminophenyl) -6-diethylaminophthalide, 3, Leuco base of fluorane dyes such as 3'-bis (p-dimethylaminophenyl) -6-chlorophthalide and 3,3'-bis (p-dibutylaminophenyl) phthalide; 6-cyclohexylamino-6-chlorofluorane , 3- (N, N-dimethylamino) -5-methyl-7- (N, N-dibenzylamino) fluorane, 3-
Fluoran dyes such as diethylamino-5,7-dimethylfluorane, 3-diethylamino-7-methylfluorane, 3-diethylamino-7,8-benzfluorane, etc .; 3
-Diethylamino-6-methyl-7-chlorofluorane, 3-pyrrolidino-6-methyl-7-anilinofluorane, 2- [N- (3'-trifluoromethylphenyl) amino] -6-diethylaminofluor Oran, 2-3,
Lactam compounds such as 6-bis (diethylamino) -9- (o-chloralinino) xanthyl benzoate lactam; 3- (2'-hydroxy-4'-dimethylaminophenyl) -3- (2'-methoxy-5'- Chlorphenyl) phthalide, 3- (2'-hydroxy-4'-dimethylaminophenyl) -3- (2'-methoxy-5'-nitrophenyl) phthalide, 3- (2'-hydroxy-
4'-Dimethylaminophenyl) -3- (2'-methoxy-5'-methylphenyl) phthalide, 3- (2'-methoxy-4'-dimethylaminophenyl) -3- (2 '
-Hydroxy-4'-chloro-5'-methylphenyl)
Phthalide can be used. Further, as an acidic substance which is a color forming aid, boric acid, oxalic acid, maleic acid, tartaric acid, citric acid, succinic acid, benzoic acid, stearic acid, gallic acid, salicylic acid, 1-hydroxy-2-naphthoic acid, o
-Hydroxybenzoic acid, m-hydroxybenzoic acid, 2,4
Dihydroxybenzoic acid, 2-hydroxy-P-toluic acid, 3,5-xylenol, thymol, p-t-butylphenol, 4-hydroxyphenoxide, methyl-4-
Hydroxybenzoate, 4-hydroxyacetophenone, α-tephthol, β-naphthol, catechol, resorcin, hydroxynone, 4-t-octylcatechol, 4,4′-sec-butylidenephenol, 2,2′-hydroxydiphenyl, 2 2,2'-methylenebis (4-methyl-6-t-butylphenol), 2,2'-bis (4'-
Hydroxyphenyl) propane, 4,4'-sec-butylidene diphenol, pyrogallol, phloroglysin, phloroglysin carboxylic acid and the like can be used.
又、ジアゾ染料系感熱発色材料はジアゾ化合物、カッ
プラー剤および塩基剤からなるものが使用でき、例え
ば、ジアゾ化合物としては、一般式Ar−Ｎ＝Ｎ＝Ｘ−Ｍ
で表され、該式において、Arは、置換または未置換のフ
ェニル、ビフェニル、ナフチル、ベンゾカルバゾール、
ジフェニルスルファイド基であり、Ｘはハロゲン又はHS
O4の如き酸残基であり、Ｍは塩化亜鉛、塩化カドミウム
あるいは四フッ化硼基であるものが使用できる。Further, the diazo dye-based thermosensitive coloring material may be composed of a diazo compound, a coupler agent and a base agent. For example, the diazo compound may be represented by the general formula Ar-N = N = X-M.
In the formula, Ar is a substituted or unsubstituted phenyl, biphenyl, naphthyl, benzocarbazole,
Diphenyl sulfide group, X is halogen or HS
An acid residue such as O 4 can be used, and M can be zinc chloride, cadmium chloride or a boron tetrafluoride group.
又、カップラー剤としては、置換または未置換のフェ
ノール、ナフトール、レゾルシン、カテコール等が使用
できる。Further, as the coupler agent, substituted or unsubstituted phenol, naphthol, resorcin, catechol and the like can be used.
又、塩基剤としては、尿素、チオ尿素、グアニジン等
が使用できる。Further, as the base agent, urea, thiourea, guanidine, etc. can be used.
上記の感熱発色材料に加える添加剤としては、炭酸カ
ルシウム、シリカ、酸化マグネシウム、タルク、硫酸バ
リウム、アルミナ、パラフィンワックス、マイクロクリ
スタリンワックス、ポリエチレンワックス、密ろう、白
ろう、カルナバワックス、ステアリン酸、ステアリン酸
アミド、ステアリン酸金属物等を使用でき、又、バイン
ダーとしては、ポリビニルアルコール、メトキシセルロ
ース、ヒドロキシエチルセルロース、カルボキシメチル
セルロース、ポリビニルピロリドン、ポリアクリルアミ
ド、ポリアクリル酸、デンプン、ゼラチン等の水溶性樹
脂、ポリスチレン、酢酸ビニル−塩化ビニル共重合体、
ポリブチルメタクリレート等の水性エマルジョン樹脂等
が使用できる。Additives to be added to the above heat-sensitive color developing material include calcium carbonate, silica, magnesium oxide, talc, barium sulfate, alumina, paraffin wax, microcrystalline wax, polyethylene wax, beeswax, white wax, carnauba wax, stearic acid, stearin. Acid amides, metal stearates, etc. can be used, and as the binder, polyvinyl alcohol, methoxycellulose, hydroxyethyl cellulose, carboxymethyl cellulose, polyvinylpyrrolidone, polyacrylamide, polyacrylic acid, starch, water-soluble resins such as gelatin, polystyrene. , Vinyl acetate-vinyl chloride copolymer,
An aqueous emulsion resin such as polybutyl methacrylate can be used.
感熱発色層１は上記の材料を用いて適宜な塗布方法、
例えば、ロールコート法、エアナイフコート法、グラビ
アコート法により塗布厚１〜20μｍで基剤の全面または
一部に形成される。The thermosensitive coloring layer 1 is formed by using the above-mentioned materials by an appropriate coating method,
For example, it is formed on the whole surface or a part of the base material by a roll coating method, an air knife coating method or a gravure coating method with a coating thickness of 1 to 20 μm.
隠蔽層２は感熱発色層１上に、感熱発色層の発色部分
と未発色の部分とを目視不可能に隠蔽するために設けら
れる層であり、着色層の一層で形成されてもよいし、
又、積層構成、例えば、着色層上に意匠的外観性をもた
せるための模様層を設けてなる複数層で形成されてもよ
い。又、隠蔽層２はサーマルヘッドと接触するため、あ
る程度の耐熱性、耐摩擦性を有することが必要である。The concealing layer 2 is a layer provided on the thermosensitive coloring layer 1 so as to conceal the colored portion and the uncolored portion of the thermosensitive coloring layer invisible, and may be formed of one layer of the coloring layer.
Further, it may be formed of a laminated structure, for example, a plurality of layers in which a patterned layer for providing a design appearance is provided on the colored layer. Further, since the hiding layer 2 comes into contact with the thermal head, it is necessary to have heat resistance and abrasion resistance to some extent.
隠蔽層２において、着色剤としては耐熱性の点から顔
料を使用することが望ましく、又その顔料その光学的特
性としては、可視光領域での反射率が高く、赤外領域で
の透過が高いものが望ましい。又、染料であっても上記
の特性を備えていれば使用できうる。In the concealing layer 2, it is desirable to use a pigment as a coloring agent from the viewpoint of heat resistance, and the optical characteristics of the pigment are high reflectance in the visible light region and high transmission in the infrared region. Things are desirable. Further, even a dye can be used as long as it has the above characteristics.
このような隠蔽層２は、上記の特性を有する顔料もし
くは染料を、含弗素系樹脂、含珪素系樹脂に混練してな
るインキ組成物、又は、エチルセルロース、エチルヒド
ロキシセルロース、セルロースアセテートプロピオネー
ト、酢酸セルロース等のセルロース誘導体、ポリスチレ
ン、ポリ−α−メチルスチレン等のスチレン樹脂または
スチレン共重合樹脂、ポリメタクリル酸メチル、ポリメ
タクリル酸エチル、ポリアクリル酸エチル、ポリメタク
リル酸ブチル等のアクリル樹脂またはメタクリル酸樹脂
の単独あるいは共重合樹脂に混練してなるインキ組成
物、又は、ロジン、ロジン変成フェノール樹脂、重合ロ
ジン等のロジンエステル樹脂、ポリ酢酸ビニル樹脂、ク
マロン樹脂、ビニルトルエン樹脂、塩化ビニル樹脂、ポ
リエステル樹脂、ポリウレタン樹脂、ビニルブチラール
樹脂、ブチラール樹脂等に混練してなるインキ組成物、
あるいは、上記の樹脂に弗素樹脂および珪素樹脂を混合
させた混合物に混練してなるインキ組成物に可塑剤、安
定剤、ワックス、グリース、乾燥剤、乾燥補助剤、硬化
剤、増粘剤、分散剤等を添加した後、溶剤あるいは希釈
剤で充分に混練して作成したインキを用いて、適宜な印
刷手段、例えば、オフセット印刷法、シルクスクリーン
印刷法、活版印刷法、静電印刷法、凹版印刷法、グラビ
アコート法、ロールコート法、ナイフコート法等の印刷
方法または塗布方法により層厚１〜20μｍで形成され
る。Such a hiding layer 2 is an ink composition obtained by kneading a pigment or dye having the above-mentioned properties with a fluorine-containing resin or a silicon-containing resin, or ethyl cellulose, ethyl hydroxycellulose, cellulose acetate propionate, Cellulose derivatives such as cellulose acetate, polystyrene, styrene resins such as poly-α-methylstyrene or styrene copolymer resins, acrylic resins such as polymethylmethacrylate, polyethylmethacrylate, polyethylacrylate, polybutylmethacrylate and methacrylic resins. An ink composition obtained by kneading an acid resin alone or with a copolymer resin, or rosin, rosin-modified phenol resin, rosin ester resin such as polymerized rosin, polyvinyl acetate resin, coumarone resin, vinyltoluene resin, vinyl chloride resin, Polyester resin, poly Urethane resins, polyvinyl butyral resins, ink composition obtained by kneading the butyral resin or the like,
Alternatively, a plasticizer, a stabilizer, a wax, a grease, a desiccant, a drying auxiliary agent, a curing agent, a thickener, and a dispersion are added to an ink composition obtained by kneading a mixture obtained by mixing the above resin with a fluorine resin and a silicon resin. Using an ink prepared by sufficiently kneading with a solvent or a diluent after adding an agent or the like, an appropriate printing means, for example, an offset printing method, a silk screen printing method, a letterpress printing method, an electrostatic printing method, an intaglio plate. It is formed with a layer thickness of 1 to 20 μm by a printing method such as a printing method, a gravure coating method, a roll coating method, a knife coating method or a coating method.
隠蔽層２上には必要に応じて耐摩擦性向上のための保
護層３を設けることができる。A protective layer 3 for improving abrasion resistance can be provided on the concealing layer 2 if necessary.
このような保護層３は、隠蔽層に用いられる樹脂を使
用するか、あるいは、さらに弗素系樹脂、珪素系樹脂を
混入させた樹脂を使用して隠蔽層形成方法と同様の印刷
方法または塗布方法により厚さ0.5〜10μｍで形成され
る。For such a protective layer 3, the same printing method or coating method as the method for forming the concealing layer is used, using the resin used for the concealing layer, or using a resin further mixed with a fluorine resin or a silicon resin. To have a thickness of 0.5 to 10 μm.
又、本発明では第２図にその断面図を示すように感熱
発色層１と基剤10の間に赤外線反射層４を設けることが
できる。Further, in the present invention, as shown in the sectional view of FIG. 2, an infrared reflection layer 4 can be provided between the thermosensitive coloring layer 1 and the base material 10.
赤外線反射層４は感熱発色層の発色部分と未発色部分
における赤外線の反射率の差を増幅させる働きをなすも
のであり、その材質は赤外線を反射するものであれば広
く使用でき、例えば、金属薄膜層、チタンホワイト層、
金属粉末を含有するプラスチックフィルム、顔料含有率
の高いプラスチックフィルム等が使用できる。The infrared reflective layer 4 has a function of amplifying a difference in infrared reflectance between a colored portion and a non-colored portion of the thermosensitive coloring layer, and its material can be widely used as long as it reflects infrared rays. Thin film layer, titanium white layer,
A plastic film containing metal powder, a plastic film having a high pigment content, and the like can be used.
赤外線反射層４は上記の材料を用いて適宜な形成法、
例えば、真空蒸着法、印刷法、塗布法、積層法により形
成されるがその厚みは特に限定されるものではない。The infrared reflective layer 4 is formed using the above-mentioned material by an appropriate method,
For example, it is formed by a vacuum vapor deposition method, a printing method, a coating method, or a lamination method, but the thickness thereof is not particularly limited.
又、本発明では第３図にその断面図を示すような感熱
発色層の反対面の基剤上に接着剤層５を設ける態様もと
ることができる。Further, in the present invention, an embodiment in which the adhesive layer 5 is provided on the base material on the surface opposite to the thermosensitive color developing layer as shown in the sectional view of FIG.
接着剤層５は本発明の記録媒体を他の物品等に貼り合
わせする場合のものであり、感熱接着剤を含む接着剤ま
たは粘着剤により形成される。The adhesive layer 5 is used when the recording medium of the present invention is bonded to another article or the like, and is formed of an adhesive containing a heat-sensitive adhesive or an adhesive.
接着剤としては、一般的に使用されているものが広く
使用でき、例えば、ポリイソプレンゴム、ポリイソブチ
ルゴム、スチレングタジエンゴム、ブタジエンアクリロ
ニトリルゴム等のゴム系樹脂、ポリアクリル系樹脂、ポ
リアクリル酸エステル系樹脂、ポリメタアクリル酸系樹
脂、ポリビニル系樹脂、ポリビニルエーテル系樹脂、ポ
リ酢酸ビニル系樹脂、塩化ビニル酢酸ビニル共重合体系
樹脂、ポリスチレン系樹脂、ポリエステル系樹脂、ポリ
アミド系樹脂、ポリ塩素化オレフィン系樹脂、ポリビニ
ルブチラール系樹脂等からなる任意の接着剤が使用で
き、また、粘着剤としては、一般的な粘着剤が使用で
き、例えば、ポリアクリル系樹脂、ゴム系樹脂等からな
る粘着剤が使用できる。As the adhesive, generally used ones can be widely used, and examples thereof include rubber resins such as polyisoprene rubber, polyisobutyl rubber, styrene butadiene rubber, and butadiene acrylonitrile rubber, polyacrylic resins, polyacrylic acid. Ester resin, polymethacrylic acid resin, polyvinyl resin, polyvinyl ether resin, polyvinyl acetate resin, vinyl chloride vinyl acetate copolymer resin, polystyrene resin, polyester resin, polyamide resin, polychlorination Any adhesive made of olefin-based resin, polyvinyl butyral-based resin or the like can be used, and as the pressure-sensitive adhesive, a general pressure-sensitive adhesive can be used, for example, a pressure-sensitive adhesive made of polyacrylic resin, rubber-based resin or the like. Can be used.
接着剤層５は、上記の接着剤または粘着剤を用いて慣
用の印刷方法または塗布方法により、適宜な厚さ１〜10
0μｍで形成される。The adhesive layer 5 has an appropriate thickness of 1 to 10 by a conventional printing method or coating method using the above adhesive or pressure-sensitive adhesive.
It is formed with a thickness of 0 μm.
次に、上記のようにして構成される本発明の記録媒体
を使用する方法を説明する。Next, a method of using the recording medium of the present invention configured as described above will be described.
まず、所望する情報をパターン、例えば、1,0を表す
ドット、バーコード、OCR文字、一般文字、記号に変換
してサーマルヘッドで隠蔽層場上から印字する。この際
記録された情報は目視できないが、感熱発色層の発色と
いう形で感熱発色層上に記録される。First, desired information is converted into a pattern, for example, dots representing 1,0, a bar code, an OCR character, a general character, and a symbol, and printed from above the concealing layer with a thermal head. The information recorded at this time is not visible, but is recorded on the thermosensitive coloring layer in the form of coloring of the thermosensitive coloring layer.
次に、赤外線投光機（700nm以上の波長、好ましくは9
00nm以上の赤外線を発するもの）により記録媒体に情報
の読みだしのスキャンが行われ、その後、隠蔽層を通っ
て感熱発色層で反射した赤外線が受光機で検出されて、
その受光量から記録された情報が読み取られる。Next, an infrared projector (wavelength above 700 nm, preferably 9 nm
The recording medium is scanned for reading information by means of one that emits infrared rays of 00 nm or more), and then the infrared rays reflected by the thermosensitive coloring layer through the concealment layer are detected by the receiver,
The recorded information is read from the received light amount.
（発明の効果） 本発明の記録媒体は、情報が目視不可能に記録できる
ため、一般の磁気テープと同様の使い方ができ、且つ、
磁気テープのように、市販の磁気ビュアー等の器具、装
置で情報が容易に読み取られることはなく極めて高い偽
造防止性を有する。(Effects of the Invention) The recording medium of the present invention can record information invisible, and thus can be used in the same manner as a general magnetic tape, and
Like magnetic tape, information is not easily read by instruments and devices such as commercially available magnetic viewers, and it has extremely high anti-counterfeiting properties.
更に、本発明の基材としてカード基板を用いれば、一
般の磁気カードと同様な使用ができる情報記録カードと
して使用できる。Furthermore, if a card substrate is used as the base material of the present invention, it can be used as an information recording card that can be used in the same manner as a general magnetic card.
又、記録される情報の変換パターンも多く、1,0を表
すドットから文字まで任意に選択でき、その記録方法も
サーマルヘッドにより容易に行うことができる。Also, there are many conversion patterns of information to be recorded, and dots from 1,0 to characters can be arbitrarily selected, and the recording method can be easily performed by a thermal head.
更に又、本発明の一態様の接着剤を有するものを使用
して、例えば、磁気カード、ICカード、光カード、磁気
通帳等の記録媒体に本発明の記録媒体を設ければ更に情
報が付加できると共に、その偽造防止性も高まる。Furthermore, by using the adhesive having the adhesive of one embodiment of the present invention, if the recording medium of the present invention is provided to a recording medium such as a magnetic card, an IC card, an optical card, or a magnetic passbook, further information is added. In addition to being able to do so, the anti-counterfeit property is also enhanced.
本発明を具体的実施例を挙げ更に詳細に説明する。 The present invention will be described in more detail with reference to specific examples.
実施例１ 基材としての厚さ250μｍのポリエチレンテレフタレー
トフィルム上に下記組成のインキＡインキＢを1:2にな
るように混合撹拌して得られたインキを用いて、グラビ
アコート法により厚み５μｍで感熱発色層を形成した。Example 1 An ink obtained by mixing and stirring Ink A Ink B having the following composition in a ratio of 1: 2 on a polyethylene terephthalate film having a thickness of 250 μm as a base material was prepared by a gravure coating method with a thickness of 5 μm. A thermosensitive coloring layer was formed.
次いで、感熱発色層上に下記組成のインキを用いグラ
ビアコート法により厚み３μｍで隠蔽層を形成した。Then, a concealing layer having a thickness of 3 μm was formed on the thermosensitive coloring layer by an gravure coating method using an ink having the following composition.
次いで、隠蔽層上に下記組成のインキを用いてグラビ
アコート法により厚み１μｍで保護層を形成して本発明
の記録媒体を得た。Then, a protective layer having a thickness of 1 μm was formed on the concealing layer by an gravure coating method using an ink having the following composition to obtain a recording medium of the present invention.
フルオラン系ロイコ染料 20部 ポリメチルメタクリレート樹脂 20部 パラフィンワックス ４部 トルエン 56部 〔感熱発色層インキＢ〕 2,4ジヒドロキシ安息香酸 20部 ポリメチルメタクリレート 20部 パラフィンワックス ４部 トルエン 56部 〔隠蔽層〕 テトラフルオロエチレンパウダー ５部 ウレタン樹脂 20部 イソシアネート硬化剤 １部 顔料 10部 メチルエチルケトン 30部 トルエン 30部 〔保護層〕 テトラフルオロエチレンパウダー 10部 ポリビニルブチラール樹脂 10部 湿気硬化型ウレタン樹脂 10部 メチルエチルケトン 30部 トルエン 30部 酢酸エチル 30部 実施例２ 基材としての厚さ250μｍのポリエチレンテレフタレ
ートに真空蒸着法によりスズを1000Aで形成して、赤外
線反射層を形成した。Fluoran-based leuco dye 20 parts Polymethylmethacrylate resin 20 parts Paraffin wax 4 parts Toluene 56 parts [Thermal coloring layer ink B] 2,4 Dihydroxybenzoic acid 20 parts Polymethylmethacrylate 20 parts Paraffin wax 4 parts Toluene 56 parts [Hiding layer] Tetrafluoroethylene powder 5 parts Urethane resin 20 parts Isocyanate curing agent 1 part Pigment 10 parts Methyl ethyl ketone 30 parts Toluene 30 parts [Protective layer] Tetrafluoroethylene powder 10 parts Polyvinyl butyral resin 10 parts Moisture curing urethane resin 10 parts Methyl ethyl ketone 30 parts Toluene 30 parts Ethyl acetate 30 parts Example 2 Tin was formed at 1000 A on a polyethylene terephthalate film having a thickness of 250 μm as a base material by a vacuum deposition method to form an infrared reflective layer.
次いで、上記赤外線反射層上に実施例１と同様にして
保護層まで形成して本発明の記録媒体を得た。Then, a protective layer was formed on the infrared reflective layer in the same manner as in Example 1 to obtain the recording medium of the present invention.
実施例３ 基材としての厚さ250μｍのポリエチレンテレフタレ
ートに保護層まで実施例２と同様に形成した。Example 3 A protective layer was formed in the same manner as in Example 2 on a polyethylene terephthalate film having a thickness of 250 μm as a substrate.
次に、基材の反対面に下記の組成からなるインキを用
いてグラビアコート法により厚み10μｍで接着剤層を形
成して本発明の記録媒体を得た。Next, an adhesive layer having a thickness of 10 μm was formed on the opposite surface of the substrate by the gravure coating method using an ink having the following composition to obtain the recording medium of the present invention.
塩化ビニル酢酸ビニル共重合体 20部 ポリアクリル樹脂 10部 酢酸エチル 20部 トルエン 50部 Vinyl chloride Vinyl acetate copolymer 20 parts Polyacrylic resin 10 parts Ethyl acetate 20 parts Toluene 50 parts
第１図、第２図および第３図は本発明の記録媒体の断面
図である。 １……感熱発色層 ２……隠蔽層 ３……保護層 ４……赤外線反射層 ５……接着剤層 10……基材1, 2 and 3 are sectional views of the recording medium of the present invention. 1 ... Thermosensitive coloring layer 2 ... Concealing layer 3 ... Protecting layer 4 ... Infrared reflecting layer 5 ... Adhesive layer 10 ... Base material
Claims (4)
アゾ系感熱材料からなる感熱発色層および隠蔽層が順次
積層される記録媒体であって、該感熱発色層には、加熱
手段により、目視不可能な任意の情報パターンが記録さ
れ、赤外線照射により読み取り可能であることを特徴と
する記録媒体。1. A recording medium in which a thermosensitive coloring layer and a hiding layer made of a leuco dye thermosensitive material or a diazo thermosensitive material are sequentially laminated on a substrate, and the thermosensitive coloring layer is heated by a heating means. A recording medium on which an invisible information pattern is recorded and which can be read by infrared irradiation.
とを特徴とする特許請求の範囲第１項記載の記録媒体。2. The recording medium according to claim 1, wherein a protective layer is provided on the concealing layer.
層が設けられていることを特徴とする特許請求の範囲第
１項または第２項記載の記録媒体。3. The recording medium according to claim 1 or 2, wherein an infrared reflecting layer is provided between the base material and the thermosensitive coloring layer.
が設けられていることを特徴とする特許請求の範囲第１
項〜第３項いずれかに記載の記録媒体。4. An adhesive layer is provided on the surface of the base material opposite to the thermosensitive coloring layer.
The recording medium according to any one of items 3 to 3.