JPH08266455A - Mop made of polyamide - Google Patents
Mop made of polyamideInfo
- Publication number
- JPH08266455A JPH08266455A JP7285095A JP7285095A JPH08266455A JP H08266455 A JPH08266455 A JP H08266455A JP 7285095 A JP7285095 A JP 7285095A JP 7285095 A JP7285095 A JP 7285095A JP H08266455 A JPH08266455 A JP H08266455A
- Authority
- JP
- Japan
- Prior art keywords
- nylon
- mop
- polyamide
- support
- yarn
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業用の利用分野】本発明は、遊び毛が少なく清掃性
能および耐久性にすぐれ、かつ再循環可能なポリアミド
製モップに関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a recyclable polyamide mop having less idle hair, excellent cleaning performance and durability.
【０００２】なお、本発明でいう再循環可能とは、ナイ
ロン６製モップを解重合反応によりナイロン６のモノマ
ーであるε−カプロラクタムに戻すことが可能であるこ
と、つまり、いわゆるケミカルリサイクル性を有するこ
とを意味する。The term "recyclable" in the present invention means that a nylon 6 mop can be returned to ε-caprolactam, which is a monomer of nylon 6, by a depolymerization reaction, that is, it has a so-called chemical recycling property. Means that.
【０００３】[0003]
【従来の技術】従来の清掃用モップは、綿糸空なる表糸
を、綿布、合繊織物、プラスチックフィルムまたは人工
皮革などからなる支持体に、縫製または縫製により結合
させて構成した雑巾部分と、プラスチック、金属または
木製の柄部と、雑巾部分と柄とを結合させる部位とから
構成されている。2. Description of the Related Art A conventional cleaning mop comprises a cotton cloth, an empty surface thread, and a rag portion formed by joining the support made of cotton cloth, synthetic fiber cloth, plastic film, artificial leather, or the like by sewing or sewing, and a plastic cloth. , A metal or wooden handle, and a portion for connecting the rag and the handle.
【０００４】しかしながら、綿糸を表糸として利用した
従来のモップは、使用回数が増すにしたがって、遊び毛
と呼ばれる単繊維の抜けが発生したり、耐久性不足のた
め糸切れが発生するという問題があった。However, the conventional mop using cotton yarn as the surface yarn has a problem that as the number of times of use increases, a single fiber called play hair comes off or yarn breakage occurs due to lack of durability. there were.
【０００５】また、使用限度がきた雑巾部分は、焼却ま
たは産業廃棄物として処理され、再循環またはリサイク
ル使用することはできなかった。Further, the rag portion whose usage limit has been reached is incinerated or treated as industrial waste and cannot be recycled or recycled.
【０００６】一方、特開昭６１−１００２２２号公報お
よび特開平６−１２３０３４号公報などには、ポリアミ
ド製の表糸を使用することにより、遊び毛や耐久性を改
良したモップが提案されているが、このモップは清掃性
能が劣り、しかも表糸として主にナイロン６６を用いて
いることから、再循環またはリサイクル使用することが
不可能であった。On the other hand, Japanese Unexamined Patent Publication No. 6100222 and Japanese Unexamined Patent Publication No. 6-123034 propose a mop in which play yarn and durability are improved by using a polyamide surface yarn. However, this mop has poor cleaning performance, and since nylon 66 is mainly used as the surface yarn, it cannot be recycled or recycled.
【０００７】[0007]
【発明が解決しようとする課題】本発明は、上述した従
来技術における問題点の解消を課題として検討した結果
達成されたものである。SUMMARY OF THE INVENTION The present invention has been achieved as a result of studying how to solve the above-mentioned problems in the prior art.
【０００８】したがって本発明の目的は、遊び毛が少な
く清掃性能および耐久性にすぐれ、かつ再循環可能なポ
リアミド製モップを提供することにある。[0008] Therefore, an object of the present invention is to provide a recyclable polyamide mop which has a small amount of idle hair and is excellent in cleaning performance and durability.
【０００９】[0009]
【課題を解決するための手段】上記の目的を達成するた
めに、本発明のポリアミド製モップは、ナイロン６製捲
縮繊維からなる表糸を、ナイロン６製支持体に結合させ
てなる雑巾部を有することを特徴とする。In order to achieve the above object, the polyamide mop of the present invention comprises a rag portion formed by binding a surface yarn made of nylon 6 crimped fiber to a nylon 6 support. It is characterized by having.
【００１０】また、本発明のポリアミド製モップは、ナ
イロン６製捲縮繊維からなる表糸を、ナイロン６製支持
体に結合させてなる雑巾部と、ナイロン６製柄部から構
成されており、モップの構成要素全体が再循環可能であ
ることを特徴とする。The polyamide mop of the present invention comprises a nylon 6 handle and a nylon 6 crimped fiber, and a nylon 6 handle. Characterized by the fact that the entire mop components are recyclable.
【００１１】そして、上記表糸は、繊度３００デニール
〜２００００デニール、捲縮伸長率５パーセント以上の
ナイロン６製捲縮マルチフィラメントから構成されるこ
とが、さらにはこのナイロン６製捲縮マルチフィラメン
トと、同様の繊度および捲縮伸長率を有する炭素繊維含
有ナイロン６マルチフィラメントとを混繊してなり、後
者を全体の５％以下の割合で含むことが好ましい。The surface yarn is composed of a nylon 6 crimped multifilament having a fineness of 300 denier to 20000 denier and a crimp extension ratio of 5% or more. It is preferable that the carbon fiber-containing nylon 6 multifilament having the same fineness and crimp elongation is mixed and the latter is contained in a proportion of 5% or less of the whole.
【００１２】以下に、本発明を図面にしたがって詳細に
説明する。The present invention will be described in detail below with reference to the drawings.
【００１３】図１は本発明のポリアミド製モップの一実
施例を示す説明図である。FIG. 1 is an explanatory view showing one embodiment of the polyamide mop of the present invention.
【００１４】図１に示した実施例において、本発明のポ
リアミド製モップは、ナイロン６製捲縮繊維からなる表
糸１をナイロン６製支持体２に結合させてなる雑巾部３
と、柄部４と、前記雑巾部３と柄部４とを連結する紐状
の連結部５とから構成されており、モップの構成要素全
体を際循環可能な点では、前記柄部４および連結部６も
またナイロン６から形成されていることが望ましい。In the embodiment shown in FIG. 1, the polyamide mop of the present invention has a rag 3 formed by binding a surface yarn 1 made of nylon 6 crimped fiber to a nylon 6 support 2.
And a handle portion 4 and a string-like connecting portion 5 that connects the dust cloth portion 3 and the handle portion 4, and the handle portion 4 and the handle portion 4 are The connecting portion 6 is also preferably made of nylon 6.
【００１５】本発明で表糸１として用いるナイロン６捲
縮繊維は、図２に例示したようなＹ型、田型および長方
型などの異形断面を有するナイロン６紡出糸を、延伸、
捲縮加工して得られた嵩高加工糸を原糸とし、撚糸また
は合糸撚糸、撚糸ヒートセット加工、または合糸撚糸ヒ
ートセット加工した後、染色加工して製造されたマルチ
フィラメントである。The nylon 6 crimped fiber used as the surface yarn 1 in the present invention is obtained by drawing a nylon 6 spun yarn having a modified cross section such as Y type, tabular type and rectangular type as illustrated in FIG.
It is a multifilament produced by using a bulky processed yarn obtained by crimping as a raw yarn, twisting or plied yarn twisted yarn, plied yarn heat set process, or plied yarn twisted yarn heat set process and then dyeing process.
【００１６】このナイロン６捲縮マルチフィラメント
は、その繊度が３００デニール〜２００００デニール、
とくに１０００〜１５０００デニール、捲縮伸長率が５
パーセント以上、とくに７パーセント以上に規制された
ものである。This nylon 6 crimped multifilament has a fineness of 300 denier to 20,000 denier,
Especially 1000 ~ 15000 denier, crimp elongation 5
It is regulated to a percentage or more, especially 7% or more.
【００１７】そして、ナイロン６捲縮マルチフィラメン
トは、捲縮糸製造時に、全体の５パーセント以下、とく
に２〜４パーセントの比率で、炭素含有ナイロン６マル
チフィラメントを紡糸混繊するか、または後加工工程で
混繊していることが望ましく、これによりモップの使用
時にナイロン６捲縮繊維から発生する静電気発生が抑制
されて、埃を捕集した後に除塵する際、埃が繊維にから
容易に離れることが可能で、清掃性能が一層すぐれたも
のになるという特徴をモップに具備せしめることができ
る。The nylon 6 crimped multifilament is spun and mixed with the carbon-containing nylon 6 multifilament at a ratio of 5% or less, especially 2 to 4% of the total amount when the crimped yarn is manufactured. It is desirable to mix fibers in the process, which suppresses the generation of static electricity generated from nylon 6 crimped fibers when using a mop, and when dust is removed after collecting dust, dust easily separates from the fibers It is possible to provide the mop with a feature that cleaning performance is further improved.
【００１８】この炭素含有ナイロン６マルチフィラメン
トは、その単糸断面を図３に示したように、たとえばナ
イロン６マルチフィラメントの中に炭素粒子Ｃを分散さ
せたもの（ａ）、またはナイロン６マルチフィラメント
の内部に、２層構造（ｂ）または三層構造（ｃ）で炭素
繊維層Ｃ´を形成したものが挙げられるが、なかでもナ
イロン６マルチフィラメントの内部に炭素繊維層を形成
したものが好ましく用いられる。This carbon-containing nylon 6 multifilament has, for example, a nylon 6 multifilament in which carbon particles C are dispersed as shown in FIG. The carbon fiber layer C'having a two-layer structure (b) or a three-layer structure (c) is formed inside, and among them, a carbon fiber layer formed inside a nylon 6 multifilament is preferable. Used.
【００１９】なお、上記のナイロン６捲縮マルチフィラ
メントおよび炭素含有ナイロン６捲縮マルチフィラメン
トは、染色加工工程またはその後工程において、抗菌加
工、防臭加工、およびはっ水加工などを付与されたもの
であっても良い。The nylon 6 crimped multifilament and the carbon-containing nylon 6 crimped multifilament have been subjected to antibacterial treatment, deodorizing treatment, water repellent treatment and the like in the dyeing process or the subsequent process. It may be.
【００２０】ここで、上記各捲縮マルチフィラメントの
繊度が３００デニール以下では、雑巾部を構成するのに
多数の表糸が必要荷なり、コストアップになる。また大
きい埃の捕集性能が落ちるため好ましくない。また２０
０００デニール以上では、雑巾部の表糸の目付が少ない
ため、全体の表糸の表面積が小さくなり埃の捕集性能低
下するため好ましくない。When the fineness of each crimped multifilament is 300 denier or less, a large number of surface yarns are required to form the rag portion, resulting in an increase in cost. In addition, the performance of collecting large dust is deteriorated, which is not preferable. 20
When the denier is 000 denier or more, the surface weight of the surface yarn in the rag portion is small, so that the surface area of the entire surface yarn is small and the dust collecting performance is deteriorated, which is not preferable.
【００２１】また、上記各捲縮マルチフィラメントの捲
縮伸長率が５パーセント未満の場合には、嵩高性能が低
すぎて埃の捕集性能が落ち、清掃性能が低下するため好
ましくない。If the crimp extension ratio of each crimped multifilament is less than 5%, the bulk performance is too low, the dust collection performance is deteriorated, and the cleaning performance is deteriorated, which is not preferable.
【００２２】さらに、炭素含有ナイロン６捲縮マルチフ
ィラメントの含有率が、全体の５パーセントを越える場
合は、埃の捕集性能が低下し、清掃性能が阻害される傾
向になるため好ましくない。Further, if the content of the carbon-containing nylon 6 crimped multifilament exceeds 5% of the whole, the dust collection performance is lowered and the cleaning performance tends to be impaired, which is not preferable.
【００２３】本発明で使用する支持体２は、ナイロン６
製織物、ナイロン６製不織布またはナイロン６製フィル
ムであるが、ナイロン６製表糸１を確実に結合し得るこ
と、支持体自体の耐久性が良いこと、およびコストが安
いことなどから、ナイロン６織物またはナイロン６不織
布がより好ましく、これら支持体２は通常袋形状に形成
される。The support 2 used in the present invention is nylon 6
Although it is a woven fabric, a non-woven fabric made of nylon 6, or a film made of nylon 6, nylon 6 can be reliably bonded to the surface yarn 1 made of nylon 6, the durability of the support itself is good, and the cost is low. A woven fabric or a nylon 6 non-woven fabric is more preferable, and these supports 2 are usually formed in a bag shape.
【００２４】また、本発明で用いる柄４は、プラスチッ
ク、金属および木などで形成可能であるが、柄本体もふ
くめて再循環（ケミカルリサイクル）させるためには、
ナイロン６樹脂製であることがより好ましい。The handle 4 used in the present invention can be formed of plastic, metal, wood, etc., but in order to recycle (chemical recycle) including the handle body,
More preferably, it is made of nylon 6 resin.
【００２５】支持体２と柄４の結合方法としては、図１
に示したナイロン６製の紐からなる連結部５の使用以外
にも、両者を融着または接着剤を介して接合する方法な
どが挙げられる。As a method of connecting the support 2 and the handle 4, FIG.
In addition to the use of the connecting portion 5 made of the nylon 6 string shown in (2), a method of fusing them or joining them via an adhesive may be used.
【００２６】表糸１の支持体２に対する結合態様として
は、製織および縫製が採用される。Weaving and sewing are adopted as the manner of connecting the surface thread 1 to the support 2.
【００２７】すなわち、製織の場合には、図４に示した
ように、袋形状の支持体２を畳んだ状態において、その
袋表皮に対し表糸１がループ状製織によって直接係合さ
れ、この場合には図６の（ｂ）〜（ｄ）に示したループ
（ｃ）、カット（ｂ）またはループ・カット（ｄ）など
の毛足の短い形態のモップに適している。That is, in the case of weaving, as shown in FIG. 4, when the bag-shaped support 2 is folded, the surface yarn 1 is directly engaged with the bag skin by the loop-shaped weaving. In some cases, it is suitable for mops having short hairs such as loop (c), cut (b) or loop cut (d) shown in FIGS. 6 (b) to 6 (d).
【００２８】また、縫製の場合には、図５に示したよう
に、袋形状の支持体２を畳んだ状態において、その袋表
皮に対し表糸１が縫糸６で縫製結合され、この場合には
図６の（ａ）に示したように、毛足の長いカットすなわ
ち紐状の形態のモップに適している。Further, in the case of sewing, as shown in FIG. 5, when the bag-shaped support 2 is folded, the surface thread 1 is sewn and joined to the bag skin by the sewing thread 6, and in this case, Is suitable for a long-haired cut, that is, a mop in the form of a string, as shown in FIG. 6 (a).
【００２９】そして、上記毛足の短いカットを持つモッ
プは、机上、および車内など狭い場所の埃を除去する目
的に好ましく使用される。The mop having the short cut hair is preferably used for the purpose of removing dust on a narrow place such as a desk or a car.
【００３０】また、毛足の短いループまたはループ・カ
ットを持つモップは、主としてカバン、靴、および衣服
など身の回り品の埃を除去する目的に好ましく使用され
る。A mop having short loops or loop cuts on the hair is preferably used mainly for the purpose of removing dust from personal belongings such as bags, shoes, and clothes.
【００３１】さらに、毛足の長いカットを持つモップ
は、主として床面、天井、および壁などの広い場所の埃
を除去する目的に好ましく使用される。Further, the mop having a long-haired cut is preferably used mainly for removing dust in a wide area such as a floor surface, a ceiling, and a wall.
【００３２】以上の構成からなる本発明のポリアミド製
モップは、表糸をナイロン６製捲縮繊維、またはこのナ
イロン６製捲縮繊維と炭素含有ナイロン６製捲縮繊維と
の混繊糸で形成したため、長時間使用後も遊び毛が少な
く、清掃性能および耐久性がきわめてすぐれている。In the polyamide mop of the present invention having the above-mentioned constitution, the surface yarn is formed by the nylon 6 crimped fiber or the mixed fiber of the nylon 6 crimped fiber and the carbon-containing nylon 6 crimped fiber. As a result, there is little idle hair even after long-term use, and cleaning performance and durability are extremely superior.
【００３３】また、ナイロン６製捲縮繊維からなる表糸
をナイロン６製支持体に結合させてなる雑巾部を有する
か、またはこれに加えて柄部をもナイロン６で形成した
ため、雑巾部のみを取り外して解重合に供するか、また
はモップの構成要素全体をそのまま解重合に供すること
により、ε−カプロラクタムに戻す再循環が可能であ
り、資源の有効活用を図ることができる。Also, since the surface thread made of the crimped fiber made of nylon 6 is bonded to the nylon 6 support, or the handle portion is made of nylon 6 in addition to this, only the cloth portion is formed. Is removed and subjected to depolymerization, or the entire constituents of the mop are subjected to depolymerization as they are, so that recirculation to return to ε-caprolactam is possible and effective utilization of resources can be achieved.
【００３４】以下に実施例を挙げて、本発明の構成およ
び効果をさらに詳しく説明する。The constitution and effects of the present invention will be described in more detail with reference to the following examples.
【００３５】[0035]
【実施例】なお、上述および以下の実施例中の物性値
は、次のようにして求めた。EXAMPLES The physical property values in the above and the following examples were determined as follows.
【００３６】［捲縮伸長率］繊維に無荷重下で９８℃×
５分間の沸騰水処理を与えた後、風乾し、初荷重（２ｍ
ｍｇ／ｄ）をかけて長さ（Ｌ１）を測定し、次いで定荷
重（１００ｍｍｇ／ｄ）をかけて長さ（Ｌ２）を測定し
て、下記の式により求めたものである。◎ 捲縮伸長率（％）＝１００×（Ｌ２−Ｌ１）／（Ｌ１） ［集塵性能および除塵性能］モップを用いて床掃除を行
う場合の集塵性能および除塵性能をフィーリング評価
し、この結果を下記の基準で判定した。 ◎……きわめて良好 ○……良好 ×……不良。[Crimp elongation ratio] 98 ° C. under no load on the fiber
After boiling water treatment for 5 minutes, air-dry, and first load (2m
mg / d) was applied to measure the length (L1), then a constant load (100 mmg / d) was applied to measure the length (L2), and the length was determined by the following formula. ◎ Crimping elongation rate (%) = 100 × (L2-L1) / (L1) [Dust collection performance and dust removal performance] Feeling evaluation of dust collection performance and dust removal performance when floor cleaning is performed using a mop, The result was judged according to the following criteria. ◎ ... very good ○ …… good × …… bad.
【００３７】［遊び毛］モップを用いて、１日あたり１
０ｍ平方の床を１０分間掃除、毎日、手で１０回表糸を
叩いて除塵、５日に一度水洗・乾燥の条件で毎日掃除を
行った場合に、遊び毛が発生するまでの日数を判定し、
下記の基準で評価した。 ◎……１００日間後でも遊び毛発生せず ×……２０日間で遊び毛発生。[Play hair] 1 per day using mop
Clean the floor of 0m square for 10 minutes, remove dust by hitting the surface thread 10 times with your hand every day, and determine the number of days until play hair occurs when cleaning is performed daily under the condition of washing and drying once every 5 days. Then
The following criteria evaluated. ◎ …… No play hair occurs after 100 days × …… Play hair occurs after 20 days.
【００３８】［耐久性能］モップを用いて、上記遊び毛
の評価と同様の掃除を毎日行い、表毛形成繊維に清掃性
能を低下させるような捲縮の低下、および繊維のへたり
が発生するまでの日数を判定し、下記の基準で評価し
た。 ◎……１００日間後でも捲縮低下およびへたりが発生せ
ず ×……３０日間で捲縮低下およびへたりが発生。[Durability] A mop is used to carry out the same cleaning as in the above evaluation of the idle hair every day, and the crimps and the sagging of the fibers, which deteriorate the cleaning performance, are generated in the surface hair forming fibers. The number of days until was determined and evaluated according to the following criteria. ∘: No crimp reduction and sag occurred even after 100 days. ×: Crimping decline and sag occurred after 30 days.
【００３９】［解重合ラクタム回収率］モップを用い
て、上記遊び毛の評価と同様の掃除を１００日間続けて
行った後、モップの全体を投入して解重合し、出発原料
としての規定の純度を持つε−カプロラクタムの回収率
（％）を測定した。[Depolymerization lactam recovery rate] A mop was used for 100 days of cleaning similar to the evaluation of the above-mentioned play hair, and then the entire mop was charged and depolymerized to obtain a prescribed starting material. The recovery rate (%) of pure ε-caprolactam was measured.
【００４０】［実施例１〜４］規定の純度を持つε−カ
プロラクタムを重合することにより、相対粘度が２．８
のナイロン６ポリマーを得た。[Examples 1 to 4] The relative viscosity is 2.8 by polymerizing ε-caprolactam having a specified purity.
Nylon 6 polymer was obtained.
【００４１】次に、上記ナイロン６ポリマーを溶融紡糸
法にて得た糸条に対し、油剤を付着せしめ、続いて引取
りロールで引取り、加熱延伸ロールにて延伸した後、連
続して特公昭５８−１２１４号公報の捲縮加工装置にて
２５０℃以上での加熱蒸気処理を行い捲縮付与した後、
巻取ることにより、表１に示した繊度を有するナイロン
６原糸（嵩高糸）を得た。Next, an oil agent is attached to the yarn obtained by melt spinning the above-mentioned nylon 6 polymer, and then it is taken up by a take-up roll and drawn by a heat-drawing roll, and then continuously treated. After crimping by heating and steaming at 250 ° C. or higher with the crimping machine disclosed in Japanese Kokoku No. 58-1214,
By winding, nylon 6 raw yarn (bulk yarn) having the fineness shown in Table 1 was obtained.
【００４２】なお、実施例２、４では上記ナイロン６原
糸に、さらに炭素粒子を４０重量％含有するナイロン６
繊維を５０デニールの割合で混繊させて巻取った静電気
防止原糸を製造した。In Examples 2 and 4, the nylon 6 raw yarn further contains 40% by weight of carbon particles.
An antistatic raw yarn was manufactured by mixing fibers at a ratio of 50 denier and winding them.
【００４３】次に上記原糸をそれぞれ３本合糸し、スチ
ームでヒートセットし、それぞれ表１に示した繊度を有
するヒートセット糸（表糸）を得た。Next, three of each of the above-mentioned raw yarns were combined and heat-set with steam to obtain heat-set yarns (front yarns) each having the fineness shown in Table 1.
【００４４】これらヒートセット糸を綛にして染色、乾
燥処理することにより得られたナイロン６捲縮繊維を表
糸として用い、ナイロン６オックスフォード織物をナイ
ロン６糸で縫製して製造した袋形状のナイロン支持体の
袋表皮の片面に、表糸長１０ｃｍ、２０本／ｃｍ2 にな
るように、ナイロン６縫糸による縫製によって結合させ
ることにより、表糸２０００本の雑巾部分を得た。A bag-shaped nylon produced by sewing nylon 6 oxford fabric with nylon 6 thread, using nylon 6 crimped fiber obtained by dyeing and heat treating these heat set threads as a surface thread. By sewn with nylon 6 sewing thread on one surface of the bag outer skin of the support so that the surface thread length was 10 cm and 20 threads / cm 2 , a rag portion of 2000 surface threads was obtained.
【００４５】次いで、ナイロン６樹脂製の柄を、上記袋
形状のナイロン６支持体の袋部分に差し入れたのち、ナ
イロン６糸で両者を結びつけて結合さることにより、ナ
イロン６製モップを得た。Then, a nylon 6 resin handle was inserted into the bag portion of the bag-shaped nylon 6 support, and the nylon 6 thread was tied together to obtain a nylon 6 mop.
【００４６】これら各ナイロン６製モップについて、集
塵性能、除塵性能、遊び毛、耐久制能および解重合ラク
タム回収率を評価した結果を表１に併せて示す。Table 1 also shows the results of evaluating the dust collection performance, dust removal performance, idle hair, durability control and depolymerization lactam recovery rate of each of these nylon 6 mops.
【００４７】[0047]
【表１】 この結果、使用間、使用後において遊び毛が出ることは
なかった。また１００日間使用後も掃除性能を低下させ
るような嵩高性能の低下、繊維のへたりは観察されなか
った。[Table 1] As a result, play hair did not appear during use and after use. In addition, even after 100 days of use, deterioration of bulk performance and deterioration of fiber performance such as deterioration of cleaning performance were not observed.
【００４８】また実施例２および４では炭素含有ナイロ
ン６繊維を混繊させた結果、埃を捕集した後の除塵率を
高めることができた。Further, in Examples 2 and 4, as a result of mixing the carbon-containing nylon 6 fiber, the dust removal rate after collecting dust could be increased.
【００４９】さらに、各モップは、出発原料である規定
の純度を持つε−カプロラクタムを９０パーセント以上
の収率で回収することができた。Furthermore, each mop was able to recover ε-caprolactam having a specified purity as a starting material in a yield of 90% or more.
【００５０】［比較例１〜４］比較例１では表糸に捲縮
伸長率が３パーセントと低いナイロン６糸を用い、比較
例２では炭素含有ナイロン６繊維の混繊量を１３０デニ
ール（７％）とした。[Comparative Examples 1 to 4] In Comparative Example 1, nylon 6 yarn having a low crimp elongation of 3% was used as the surface yarn, and in Comparative Example 2, the carbon-containing nylon 6 fiber was mixed with 130 denier (7). %).
【００５１】また、比較例３、４では、表糸としてそれ
ぞれ表２に示した繊度を有するポリエステル捲縮繊維お
よび綿糸をそれぞれ用いた。In Comparative Examples 3 and 4, polyester crimped fibers and cotton yarns having the fineness shown in Table 2 were used as the surface yarns.
【００５２】その他の条件は、すべて上記実施例と同一
条件とした。All other conditions were the same as those in the above-mentioned embodiment.
【００５３】得られた各モップについて、集塵性能、除
塵性能、遊び毛、耐久制能および解重合ラクタム回収率
を評価した結果を表２に併せて示す。Table 2 also shows the results of evaluating the dust collection performance, dust removal performance, idle hair, durability control and depolymerization lactam recovery rate of each of the obtained mops.
【００５４】[0054]
【表２】 結果は表２に示したとおり、比較例１、２では集塵性能
が不良であった。[Table 2] As shown in Table 2, the dust collection performance was poor in Comparative Examples 1 and 2.
【００５５】また、比較例３では３０日間使用後ですで
に掃除性能を低下させるような嵩高性能の低下、繊維の
へたりが観察され、耐久性能が不良であった。Further, in Comparative Example 3, after 30 days of use, deterioration of bulk performance and deterioration of cleaning performance, fiber sag were observed, and durability performance was poor.
【００５６】さらに、比較例４では２０日間使用後から
遊び毛の発生が問題となり、３０日間使用後では繊維が
へたり、部分的に糸切れ現象がみられた。Further, in Comparative Example 4, the occurrence of idle hair became a problem after 20 days of use, and after 30 days of use, the fibers were sagging and a partial yarn breakage phenomenon was observed.
【００５７】[0057]
【発明の効果】以上説明したように、本発明のポリアミ
ド製モップは、表糸をナイロン６製捲縮繊維、またはこ
のナイロン６製捲縮繊維と炭素含有ナイロン６製捲縮繊
維との混繊糸で形成したため、長時間使用後も遊び毛が
少なく、清掃性能および耐久性がきわめてすぐれてい
る。As described above, in the polyamide mop of the present invention, the nylon 6 crimped fiber is used as the surface yarn, or a mixed fiber of the nylon 6 crimped fiber and the carbon-containing nylon 6 crimped fiber. Since it is made of thread, it has less idle hair even after long-term use and has excellent cleaning performance and durability.
【００５８】また、ナイロン６製捲縮繊維からなる表糸
をナイロン６製支持体に結合させてなる雑巾部を有する
か、またはこれに加えて柄部をもナイロン６で形成した
ため、雑巾部のみを取り外して解重合に供するか、また
はモップの構成要素全体をそのまま解重合に供すること
により、ε−カプロラクタムに戻す再循環が可能であ
り、資源の有効活用を図ることができる。Also, since the surface thread made of the crimped fiber made of nylon 6 is bonded to the support made of nylon 6 or in addition to this, the handle portion is also made of nylon 6, only the cloth portion is formed. Is removed and subjected to depolymerization, or the entire constituents of the mop are subjected to depolymerization as they are, so that recirculation to return to ε-caprolactam is possible and effective utilization of resources can be achieved.
【図１】図１は本発明のポリアミド製モップの一実施例
を示す説明図である。FIG. 1 is an explanatory view showing an embodiment of a polyamide mop of the present invention.
【図２】図２は表糸を形成するナイロン６捲縮繊維の断
面図である。FIG. 2 is a cross-sectional view of nylon 6 crimped fiber forming a face yarn.
【図３】図３（ａ）〜（ｃ）は表糸に含まれる炭素含有
ナイロン６捲縮繊維の断面図である。3 (a) to 3 (c) are cross-sectional views of carbon-containing nylon 6 crimped fibers contained in a surface yarn.
【図４】図４は表糸を支持体に対し製織結合した状態を
示す断面図である。FIG. 4 is a cross-sectional view showing a state in which a surface yarn is woven and bonded to a support.
【図５】図５は表糸を支持体に対し縫製結合した状態を
示す断面図である。FIG. 5 is a cross-sectional view showing a state in which a front thread is sewn to a support body.
【図６】図６（ａ）〜（ｄ）は表糸と支持体Ｋ結合状態
を示す断面図である。6 (a) to 6 (d) are cross-sectional views showing a binding state of a surface yarn and a support K.
１ 表糸 ２ 支持体 ３ 雑巾部 ４ 柄部 ５ 結合部（紐） ６ 縫糸 1 surface thread 2 support 3 rag section 4 handle section 5 connecting section (string) 6 sewing thread
Claims (8)
アミド製支持体に結合させてなる雑巾部を有することを
特徴とするポリアミド製モップ。1. A polyamide mop, characterized in that it has a rag formed by binding a surface yarn made of polyamide fiber to a polyamide support.
を、ナイロン６製支持体に結合させてなる雑巾部を有す
ることを特徴とするポリアミド製モップ。2. A polyamide mop, characterized in that it has a rag formed by binding a surface yarn made of nylon 6 crimped fiber to a nylon 6 support.
を、ナイロン６製支持体に結合させてなる雑巾部と、ナ
イロン６製柄部とから構成されたことを特徴とするポリ
アミド製モップ。3. A polyamide mop comprising a nylon 6 crimped fiber surface yarn bonded to a nylon 6 support and a nylon 6 handle.
が、繊度３００デニール〜２００００デニール、捲縮伸
長率５パーセント以上のナイロン６マルチフィラメント
から構成されることを特徴とする請求項１、２または３
に記載のポリアミド製モップ。4. The nylon 6 crimped fiber forming the surface yarn is composed of nylon 6 multifilament having a fineness of 300 denier to 20000 denier and a crimp elongation of 5% or more. 2 or 3
Polyamide mop described in.
が、繊度３００デニール〜２００００デニール、捲縮伸
長率５パ−セント以上のナイロン６マルチフィラメント
と、同様の繊度および捲縮伸長率を有する炭素繊維含有
ナイロン６マルチフィラメントとを混繊してなり、後者
を全体の５％以下の割合で含むことを特徴とする請求項
１、２、３または４に記載のポリアミド製モップ。5. The nylon 6 crimped fiber forming the surface yarn has the same fineness and crimp elongation as nylon 6 multifilament having a fineness of 300 denier to 20,000 denier and a crimp elongation of 5 percent or more. The polyamide mop according to claim 1, wherein the polyamide mop is formed by mixing the carbon fiber-containing nylon 6 multifilament, and the latter is contained in a ratio of 5% or less of the whole.
物、不織布またはフィルムからなることを特徴とする請
求項１、２、３、４または５に記載のポリアミド製モッ
プ。6. The polyamide mop according to claim 1, 2, 3, 4 or 5, wherein the support is made of a nylon 6 woven fabric, an assemblage, a nonwoven fabric or a film.
態において袋表皮に表糸をナイロン６繊維の縫糸で縫製
結合させたことを特徴とする請求項１、２、、３、４、
５または６に記載のポリアミド製モップ。7. The support has a bag shape, and in a folded state of the bag, a surface thread is sewn and bonded to a bag skin by a nylon 6 fiber sewing thread. ,
The mop made of polyamide according to 5 or 6.
態において袋表皮に表糸を製織によって結合させたこと
を特徴とする請求項１、２、、３、４、５または６に記
載のポリアミド製モップ。8. The support according to claim 1, wherein the support has a bag shape, and a surface yarn is bonded to the bag skin by weaving in a folded state of the bag. Polyamide mop described.